WO2019044716A1 - 炭素材料用分散剤、該炭素材料用分散剤を含有する分散物、全固体リチウムイオン二次電池用電極スラリー、全固体リチウムイオン二次電池用電極の製造方法、全固体リチウムイオン二次電池用電極及び全固体リチウムイオン二次電池 - Google Patents

炭素材料用分散剤、該炭素材料用分散剤を含有する分散物、全固体リチウムイオン二次電池用電極スラリー、全固体リチウムイオン二次電池用電極の製造方法、全固体リチウムイオン二次電池用電極及び全固体リチウムイオン二次電池 Download PDF

Info

Publication number
WO2019044716A1
WO2019044716A1 PCT/JP2018/031403 JP2018031403W WO2019044716A1 WO 2019044716 A1 WO2019044716 A1 WO 2019044716A1 JP 2018031403 W JP2018031403 W JP 2018031403W WO 2019044716 A1 WO2019044716 A1 WO 2019044716A1
Authority
WO
WIPO (PCT)
Prior art keywords
group
secondary battery
ion secondary
carbon
meth
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/JP2018/031403
Other languages
English (en)
French (fr)
Inventor
智信 石田
森　宏一
晃平 山本
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Sanyo Chemical Industries Ltd
Original Assignee
Sanyo Chemical Industries Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Sanyo Chemical Industries Ltd filed Critical Sanyo Chemical Industries Ltd
Priority to CN201880055177.8A priority Critical patent/CN111095632B/zh
Priority to JP2019539461A priority patent/JP7152406B2/ja
Priority to US16/641,332 priority patent/US11316163B2/en
Publication of WO2019044716A1 publication Critical patent/WO2019044716A1/ja
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

本発明は、窒素原子を含む基を有する共重合体を含有する炭素材料用分散剤であって、上記共重合体中の窒素含有量が０．０１重量％以上５重量％以下、上記共重合体のＳＰ値が８．０～１２（ｃａｌ／ｃｍ３）１／２である炭素材料用分散剤。

Description

炭素材料用分散剤、該炭素材料用分散剤を含有する分散物、全固体リチウムイオン二次電池用電極スラリー、全固体リチウムイオン二次電池用電極の製造方法、全固体リチウムイオン二次電池用電極及び全固体リチウムイオン二次電池
本発明は、炭素材料用分散剤、該炭素材料用分散剤を含有する分散物、該分散物を含有する全固体リチウムイオン二次電池用電極スラリー、該全固体リチウムイオン二次電池用電極スラリーを調製する工程を含む全固体リチウムイオン二次電池用電極の製造方法、全固体リチウムイオン電池用電極及び該全固体リチウムイオン電池用電極を用いた全固体リチウムイオン二次電池に関する。
炭素材料として、カーボンブラック（ＣＢ）、カーボンナノチューブ（ＣＮＴ）、カーボンナノファイバー（ＣＮＦ）、カーボンファイバー（ＣＦ）、アセチレンブラック（ＡＢ）及びフラーレン等は、着色顔料、遮光材料、導電材料として、印刷インキ、インクジェットインキ、筆記具用インキ、塗料、プラスチック形成材料等の幅広い分野で使用されている。一般的に、これらの用途への要求品質を満たすには、炭素材料を溶媒やフィルム、塗膜及び成型体等の中に均一に分散させることが重要となる。これらの炭素材料は、溶媒等他の分子との親和性が小さく、有機溶媒や樹脂中に均一に分散させることは容易ではなく、分散剤を用いることが一般的である。しかしながら、従来から知られているポリビニルピロリドン（ＰＶＰ）等の分散剤は、Ｎ－メチルピロリドン等の高極性溶媒中に溶解して分散性能を示すことが知られている。一方、低極性の溶媒中では溶解しないため、分散性能を示さないことが課題であり、炭素材料の分散媒や炭素材料が分散した材料の用途が限られていた。
例えば、従来のリチウムイオン二次電池に用いられる材料としては、電池製造過程において活物質や導電助剤等の材料の分散性に優れる高極性溶媒に、分散剤としてポリビニルピロリドン（ＰＶＰ）、ポリフッ化ビニリデン（ＰＶＤＦ）等を溶解させたものが用いられてきた（例えば、特許文献１）。
一方、従来のリチウムイオン二次電池は電解質として有機溶媒にリチウム塩を溶解させたものを用いるため、異常時に発火する恐れがある。そこで、近年は有機溶媒を用いない電解質として固体電解質を用いることで、発火のリスクを抑制した全固体リチウムイオン二次電池の開発が進められている。しかし、全固体リチウムイオン二次電池に用いられる固体電解質は高極性溶媒に接触すると変質して、イオン伝導性能を低下させることが知られている（例えば、特許文献２）。そのため、全固体リチウムイオン二次電池の製造には低極性溶媒を用いることが好ましい。
しかし、従来のリチウムイオン二次電池の製造で分散剤として一般的に用いられているポリビニルピロリドン（ＰＶＰ）やポリフッ化ビニリデン（ＰＶＤＦ）は低極性溶媒には溶解しないため、分散剤として使用できない点に課題がある。低極性溶媒への溶解性と分散性を両立する分散剤の開発が求められている。
特開２０１２－１７８３２７号公報 特開２０１４－０９３２６３号公報
本発明は、導電助剤等の炭素材料の低極性溶媒及び低極性媒体に対する親和性を高め、凝集を抑制して炭素材料に対する分散均一性及び分散安定性を高めることができる炭素材料用分散剤を提供することを目的とする。大電流での充電特性及び放電特性、サイクル特性及び電極の導電性に優れた全固体リチウムイオン二次電池用電極を備えた全固体リチウムイオン二次電池を提供することを目的とする。
本発明者らは、上記の目的を達成すべく検討を行った結果、本願発明をするに至った。
すなわち、本発明は、窒素原子を含む基を有する共重合体を含有する炭素材料用分散剤であって、上記共重合体中の窒素含有量が０．０１重量％以上５重量％以下、上記共重合体のＳＰ値が８．０～１２（ｃａｌ／ｃｍ３）１／２である炭素材料用分散剤；上記炭素材料用分散剤と、炭素材料と、比誘電率が１．５以上６．４以下の低極性溶媒、及び／又は、比誘電率が１．５以上６．４以下の炭化水素系樹脂である低極性媒体とを含有する分散物；上記分散物と、固体電解質と、正極活物質又は負極活物質とを含有する全固体リチウムイオン二次電池用電極スラリー；上記分散物と、導電助剤と、固体電解質と、正極活物質又は負極活物質とを混合することにより上記全固体リチウムイオン二次電池用電極スラリーを調製する工程を含む全固体リチウムイオン二次電池用電極の製造方法；上記分散物と、固体電解質と、正極活物質又は負極活物質とを含有する全固体リチウムイオン二次電池用電極；上記全固体リチウムイオン二次電池用電極を用いた全固体リチウムイオン二次電池である。
本発明によれば、導電助剤等の炭素材料の低極性溶媒及び低極性媒体に対する親和性を高め、凝集を抑制して炭素材料に対する分散均一性及び分散安定性を高めることができる炭素材料用分散剤を提供することができる。そして、この炭素材料用分散剤を用いて作製される全固体リチウムイオン二次電池の電池性能を向上させることができる。また、大電流での充電特性及び放電特性、サイクル特性及び電極の導電性に優れた全固体リチウムイオン二次電池用電極を備えた全固体リチウムイオン二次電池を提供することができる。
＜炭素材料用分散剤＞
本発明の炭素材料用分散剤について、説明する。
本発明の炭素材料用分散剤は、窒素原子を含む基を有する共重合体を含有する。上記共重合体中の窒素含有量は０．０１重量％以上５重量％以下、上記共重合体のＳＰ値は８．０～１２（ｃａｌ／ｃｍ３）１／２である。
窒素原子を含む基を有する共重合体は、少なくとも１種類以上の共重合性モノマー（Ｘ）を構成単量体として含有する組成物であることが好ましい。共重合性モノマー（Ｘ）としては、ビニル基を有する化合物（以下、ビニル化合物）である。上記共重合性モノマーは、極性官能基を有する共重合性モノマーを重合単位としてさらに含むことができる。極性官能基を有する共重合性モノマーは、上述のビニル化合物と共重合されて重合単位として重合体に含まれる。また、上記共重合体の側鎖又は末端に極性官能基を提供することができるモノマーであることが好ましい。
ビニル化合物としては、分子中にビニル基（アクリロイル基及び／又はメタアクリロイル基を除く。）を少なくとも１個含む化合物である。このようなビニル化合物の例としては、ｎ－ブチルビニルエーテル、ドデシルビニルエーテル、シクロヘキシルビニルエーテル、ジエチレングリコールジビニルエーテル、ジメトキシメチルビニルシラン、メジチルジビニルシラン、２－メチル－１，５－ヘキサジエン、３－メチル－１－ペンテン、スチレン、２－メチルスチレン、３－メチルスチレン、４－メチルスチレン、トリフェニルビニルシラン、９－ビニルアントラセン、５－ビニルビシクロ［２．２．１］ヘプタ－２－エン、４－ビニルビフェニル、９－ビニルカルバゾール、ビニルシクロヘキサン、ビニルシクロペンタン、１－ビニルナフタレン、２－ビニロキシテトラヒドロピラン等が挙げられる。
更に極性官能基として、（メタ）アクリル酸エステル化合物［（メタ）アクリロイル基（アクリロイル基及び／又はメタアクリロイル基を意味する。）］を少なくとも１個含むビニル化合物が挙げられる。直鎖の（メタ）アクリル酸エステル化合物としては、メチル（メタ）アクリレート、エチル（メタ）アクリレート、ｎ－プロピル（メタ）アクリレート、ｎ－ブチル（メタ）アクリレート、ｎ－ペンチル（メタ）アクリレート、ｎ－ヘキシル（メタ）アクリレート、ｎ－ヘプチル（メタ）アクリレート、ｎ－オクチル（メタ）アクリレート、ｎ－ノニル（メタ）アクリレート、ｎ－デシル（メタ）アクリレート、ｎ－ドデシル（メタ）アクリレート、ｎ－トリデシル（メタ）アクリレート、ｎ－テトラデシル（メタ）アクリレート、ｎ－ペンタデシル（メタ）アクリレート、ｎ－ヘキサデシル（メタ）アクリレート、ｎ－オクタデシル（メタ）アクリレート、ｎ－イコシル（メタ）アクリレート、ｎ－テトラコシル（メタ）アクリレート、ｎ－トリアコンチル（メタ）アクリレート、ｎ－ヘキサトリアコンチル（メタ）アクリレート、ｎ－ドトリアコンチル（メタ）アクリレートが挙げられる。また、分岐の（メタ）アクリル酸エステル化合物としては、イソペンチル（メタ）アクリレート、イソヘキシル（メタ）アクリレート、イソヘプチル（メタ）アクリレート、イソオクチル（メタ）アクリレート、２－エチルヘキシル（メタ）アクリレート、３，５，５－トリメチルヘキシル（メタ）アクリレート、イソデシル（メタ）アクリレート、２，４，６－トリメチルヘプチル（メタ）アクリレート、２－エチル－ｎ－ドデシル（メタ）アクリレート、２－メチル－ｎ－テトラデシル（メタ）アクリレート、イソヘキサデシル（メタ）アクリレート、２－ｎ－オクチル－ｎ－ノニル（メタ）アクリレート、イソオクタデシル（メタ）アクリレート、１－ｎ－ヘキシル－ｎ－トリデシル、２－エチル－ｎ－ヘプタデシル、イソイコシル（メタ）アクリレート、１－ｎ－オクチル－ｎ－ペンタデシル（メタ）アクリレート、２－ｎ－デシル－ｎ－テトラデシル（メタ）アクリレート、２－ｎ－ドデシル－ｎ－ペンタデシル（メタ）アクリレート、イソトリアコンチル（メタ）アクリレート、２－ｎ－テトラデシル－ｎ－ヘプタデシル（メタ）アクリレート、２－ｎ－ヘキサデシル－ｎ－ヘプタデシル（メタ）アクリレート、２－ｎ－ヘプタデシル－ｎ－イコシル（メタ）アクリレート、２－ｎ－ヘキサデシル－ｎ－ドコシル（メタ）アクリレート、２－オクチルノニル（メタ）アクリレート、イソオクタデシル（メタ）アクリレート、１－ヘキシルトリデシル（メタ）アクリレート、２－エチル－ｎ－ヘプタデシル（メタ）アクリレート、イソトリコンチル（メタ）アクリレート、２－ｎ－テトラデシル－ｎ－ヘプタデシル（メタ）アクリレート、２－ｎ－ヘプタデシル－ｎ－イコシル（メタ）アクリレート、２－ｎ－ヘキサデシル－ｎ－ドコシル（メタ）アクリレート、２－ｎ－イコシル－ｎ－ドコシル（メタ）アクリレート、２－ｎ－テトラコシル－ｎ－ヘキサコシル（メタ）アクリレート、２－メチル－ｎ－ペンタコンチル（メタ）アクリレート、２－ｎ－テトラデシル－ｎ－テトラコンチル（メタ）アクリレート、２－ｎ－ドデシル－ｎ－ヘキサテトラコンチル（メタ）アクリレート、１－ｎ－オクタコシル－ｎ－トリコンチル（メタ）アクリレート等が挙げられる。さらにこれらのビニル化合物のアルキレンオキサイド（エチレンオキサイド、プロピレンオキサイド、ブチレンオキサイド）２～２０モル付加物等が挙げられる。
また、水酸基を少なくとも１個含むビニル化合物が挙げられ、例としては、１－ヒドロキシエチル（メタ）アクリレート、２－ヒドロキシエチル（メタ）アクリレート、３－ヒドロキシプロピル（メタ）アクリレート、４－ヒドロキシブチル（メタ）アクリレート、５－ヒドロキシペンチル（メタ）アクリレート、６－ヒドロキシヘキシル（メタ）アクリレート等が挙げられる。
また、アミド基を少なくとも１個含むビニル化合物が挙げられ、例としては、窒素原子に炭素数１～４のアルキル基が２つ結合したもの；例えばＮ，Ｎ－ジメチル（メタ）アクリルアミド、Ｎ，Ｎ－ジエチル（メタ）アクリルアミド、Ｎ，Ｎ－ジイソプロピル（メタ）アクリルアミド及びＮ，Ｎ－ジ－ｎ－ブチル（メタ）アクリルアミド等、アミノアルキル基の窒素原子に炭素数１～４のアルキル基が２つ結合したアミノアルキル基（炭素数２～６）を有するもの；例えばＮ－（Ｎ’，Ｎ’－ジメチルアミノエチル）（メタ）アクリルアミド、Ｎ－（Ｎ’，Ｎ’－ジエチルアミノエチル）（メタ）アクリルアミド、Ｎ－（Ｎ’，Ｎ’－ジメチルアミノプロピル）（メタ）アクリルアミド及びＮ－（Ｎ’，Ｎ’－ジ－ｎ－ブチルアミノブチル）（メタ）アクリルアミド等；Ｎ－ビニルカルボン酸アミド［Ｎ－ビニルホルムアミド、Ｎ－ビニルアセトアミド、Ｎ－ビニル－ｎ－又はイソプロピオン酸アミド及びＮ－ビニルヒドロキシアセトアミド等］、Ｎ－メチル（メタ）アクリルアミド、Ｎ－エチル（メタ）アクリルアミド、Ｎ－プロピル（メタ）アクリルアミド、Ｎ－イソプロピル（メタ）アクリルアミド、Ｎ－ブチル（メタ）アクリルアミド、Ｎ－イソブチル（メタ）アクリルアミド、Ｎ－ｔ－ブチル（メタ）アクリルアミド、Ｎ，Ｎ－ジメチルアミノプロピル（メタ）アクリルアミド、Ｎ，Ｎ－メチレン－ビス（メタ）アクリルアミド、Ｎ－メチロール（メタ）アクリルアミド、ヒドロキシエチル（メタ）アクリルアミド等が挙げられる。
また、アミノ基を少なくとも１個含むビニル化合物が挙げられ、例としては、ジメチルアミノエチル（メタ）アクリレート、ジエチルアミノエチル（メタ）アクリレート、Ｎ，Ｎ－ジメチルアミノエチル（メタ）アクリレート、（メタ）アクリロイルモルホリン等が挙げられる。
さらに窒素原子を有する脂環式（メタ）アクリレート［Ｎ－ビニル－モルホリン、モルホリノエチル（メタ）アクリレート、２，２，６，６－テトラメチル－４－ピペリジル（メタ）アクリレート、Ｎ－ビニル－２，２，６，６－テトラメチルピペリジル等］、芳香族系単量体［Ｎ－（Ｎ’，Ｎ’－ジフェニルアミノエチル）（メタ）アクリルアミド、Ｎ，Ｎ－ジメチルアミノスチレン、４－ビニルピリジン、２－ビニルピリジン、Ｎ－ビニルピロール、Ｎ－ビニルイミダゾール、Ｎ－ビニルピロリドン及びＮ－ビニルチオピロリドン等］及びこれらの塩酸塩、硫酸塩、リン酸塩又は低級アルキル（炭素数１～８）モノカルボン酸（酢酸及びプロピオン酸等）塩等が挙げられる。
窒素原子を含む基を有する共重合体は、上記ビニル化合物の中でも、炭素材料の分散性の観点から、下記一般式（１）で示される（メタ）アクリル酸エステルモノマー（ａ）（以下、モノマー（ａ）ともいう）と、窒素原子含有ビニルモノマー（ｂ）（以下、モノマー（ｂ）ともいう）との共重合体（Ａ）（以下、単に共重合体（Ａ）ともいう）を含有する化合物が好ましく、窒素原子含有ビニルモノマー（ｂ）が、下記一般式（２）で示されるモノマー（ｂ１）であることがより好ましい。
Figure JPOXMLDOC01-appb-C000003
一般式（１）は、下記を満足することが好ましい。
一般式（１）中、Ｒ１は水素原子又はメチル基；Ｘ１は炭素数２～４のオキシアルキレン基；Ｒ２は、ｐ＝０のとき炭素数８～３２のアルキル基であり、ｐ＝１～２０のとき炭素数１～３２のアルキル基；ｐは０～２０の整数であり、ｐが２以上の場合、複数のＸ１は同一でも異なっていてもよく、（Ｘ１）ｐ部分の結合はランダムでもブロックでもよい。
一般式（１）におけるＲ１は、水素原子又はメチル基である。これらのうち本発明の炭素材料用分散剤の後述する低極性溶媒及び低極性媒体に対する溶解性（以下、単に本発明の炭素材料用分散剤の溶解性ともいう）の観点からメチル基であることが好ましい。
一般式（１）におけるＸ１は、炭素数２～４のオキシアルキレン基である。炭素数２～４のオキシアルキレン基としては、例えばオキシエチレン基、オキシプロピレン基、オキシブチレン基、あるいは、これらの基の水素原子の一部をハロゲン原子又は水酸基等で置換した基等を挙げることができる。
また、一般式（１）におけるＸ１における、炭素数２～４のオキシアルキレン基を構成する炭素数２～４のアルキレン基としては、本発明の炭素材料用分散剤の物性に影響を与えない限り、直鎖状及び分岐状のいずれであってもよいが、本発明の炭素材料用分散剤の溶解性の観点から直鎖状であることが好ましい。　
ｐが２以上の場合のＸ１は、同一種類でも異なる種類の炭素数２～４のオキシアルキレン基であってもよい。
一般式（１）におけるｐは０～２０の整数であり、本発明の炭素材料用分散剤の溶解性の観点から、０～１０の整数であることが好ましく、０～５の整数であることがより好ましい。ｐが２以上の場合、（Ｘ１）ｐの部分はランダム結合でもブロック結合でもよい。
一般式（１）におけるＲ２は、ｐ＝０のとき炭素数８～３２のアルキル基であり、ｐ＝１～２０のとき炭素数１～３２のアルキル基である。
ｐ＝０のときにおけるＲ２は、炭素数８～３２のアルキル基である。炭素数８～３２の直鎖アルキル基としては、例えばオクチル基、ノニル基、デシル基、ウンデシル基、ドデシル基、トリデシル基、テトラデシル基、ペンタデシル基、ヘキサデシル基、ヘプタデシル基、オクタデシル基、ノナデシル基、イコシル基、エイコシル基、ヘンイコシル基、ヘンエイコシル基、ドコシル基、トリコシル基、テトラコシル基、ペンタコシル基、ヘキサコシル基、ヘプタコシル基、オクタコシル基、ノナコシル基、トリアコンチル基、ヘントリアコンチル基、ドトリアコンチル基、分岐アルキル基としては、イソペンチル基、イソヘキシル基、イソヘプチル基、イソオクチル基、２－エチルヘキシル基、３，５，５－トリメチルヘキシル基、イソデシル基、２，４，６－トリメチルヘプチル基、２－エチル－ｎ－ドデシル基、２－メチル－ｎ－テトラデシル基、イソヘキサデシル基、２－オクチルノニル基、２－ヘキシルウンデシル基、２－エチルペンタデシル基、２－（３－メチルヘキシル）－７－メチル－ノニル基、イソオクタデシル基、１－ヘキシルトリデシル基、２－エチルヘプタデシル基、２－オクチルウンデシル基、イソイコシル基、１－ウンデシルドデシル基、１－オクチルペンタデシル基、２－デシルトリデシル基、２－デシルテトラデシル基、２－（１，４，４－トリメチルブチル）－５，７，７－トリメチル－ヘプチル基、２－ドデシルペンタデシル基、イソトリコンチル基、２－テトラデシルヘプタデシル基、２－ヘキサデシルヘプタデシル基、１－ヘプチルトリコンチル基、２－ヘプタデシルイコシル基、１－オクタデシルイコシル基、２－ヘキサデシルドコシル基、２－（１，４，４－トリメチルブチル）－５，７，７－トリメチル－トリコンチル基、２－イコシルドコシル基、１－イコシルテトラコシル基等が挙げられ、これら単量体のアルキル基は直鎖のもの側鎖を有するものいずれでも良い。これらの中でも、本発明の炭素材料用分散剤の溶解性の観点から炭素数１０～２４のアルキル基が好ましい。
また、ｐ＝１～２０のときにおけるＲ２は、炭素数１～３２のアルキル基である。上述した炭素数８～３２のアルキル基以外のアルキル基としては、メチル基、エチル基、プロピル基、ブチル基、ペンチル基、ヘキシル基、ノニル基が挙げられる。
一般式（１）で示される化合物として、炭素材料の分散性の観点から、ｎ－オクチル（メタ）アクリレート、ｎ－ノニル（メタ）アクリレート、ｎ－デシル（メタ）アクリレート、ｎ－ドデシル（メタ）アクリレート、ｎ－トリデシル（メタ）アクリレート、ｎ－テトラデシル（メタ）アクリレート、ｎ－ペンタデシル（メタ）アクリレート、ｎ－ヘキサデシル（メタ）アクリレート、ｎ－オクタデシル（メタ）アクリレート、ｎ－イコシル（メタ）アクリレート、ｎ－イコシル（メタ）アクリレート、ｎ－テトラコシル（メタ）アクリレート、ｎ－トリアコンチル（メタ）アクリレート、ｎ－ドトリアコンチル（メタ）アクリレート、２－メトキシエチル（メタ）アクリレート、ジエチレングリコールモノメチルエーテル（メタ）アクリレートであることが好ましい。
Figure JPOXMLDOC01-appb-C000004
一般式（２）は、以下を満足することが好ましい。
一般式（２）におけるＲ３は、水素原子又はメチル基である。；Ｘ２は、エステル基、アミド基、カルボニル基及び脂肪族炭化水素基からなる群から選ばれる少なくとも１種類の基であり、ｑは０又は１の整数である。；Ｘ３は、炭素数２～４のアルキレン基であり、ｒは０又は１の整数である。；一般式（２）におけるアミノ基に含まれるＲ４及びＲ５は、同一でも異なっていてもよい炭素数１～４である炭化水素基であって、結合して環を形成してもよい。一般式（２）におけるアミノ基がＲ４とＲ５を結合してなる環状アミノ基である場合、上記環状アミノ基は、炭素数４若しくは５の炭化水素基及び０～２個のカルボニル基を含有する。 
一般式（２）におけるＲ３は、水素原子又はメチル基である。これらのうち本発明の炭素材料用分散剤の溶解性の観点からメチル基であることが好ましい。
一般式（２）におけるＸ２は、エステル基、アミド基、カルボニル基及び脂肪族炭化水素基からなる群から選ばれる少なくとも１種類の基であり、ｑは０又は１の整数である。Ｘ２は、電気化学的安定性の観点からエステル基又はアミド基又はカルボニル基であることが好ましい。
一般式（２）におけるＸ３は、炭素数２～４のアルキレン基であり、ｒは０又は１の整数である。炭素数２～４のアルキレン基としては、例えば
エチレン基（ジメチレン基）、トリメチレン基、テトラメチレン基、あるいは、これらの基の水素原子の一部をハロゲン原子又は水酸基等で置換した基等を挙げることができる。これら中でも、炭素材料の分散性の観点から炭素数２～４のアルキレン基としては、エチレン基であることが好ましい。また、炭素数２～４のアルキレン基としては、本発明の炭素材料用分散剤の物性に影響を与えない限り、直鎖状及び分岐状のいずれであってもよい。
一般式（２）におけるアミノ基に含まれるＲ４及びＲ５は、同一でも異なっていてもよい炭素数１～４である炭化水素基であって、結合して環を形成してもよい。一般式（２）におけるアミノ基がＲ４とＲ５を結合してなる環状アミノ基である場合、上記環状アミノ基は、炭素数４若しくは５の炭化水素基及び０～２個のカルボニル基を含有する。
一般式（２）で示される化合物として、電気化学的安定性と炭素材料の分散性との観点から、Ｎ－（Ｎ’，Ｎ’－ジフェニルアミノエチル）（メタ）アクリルアミド、Ｎ－（Ｎ’，Ｎ’－ジメチルアミノエチル）（メタ）アクリルアミド、Ｎ－（Ｎ’，Ｎ’－ジエチルアミノエチル）（メタ）アクリルアミド、Ｎ－（Ｎ’，Ｎ’－ジメチルアミノプロピル）（メタ）アクリルアミド、モルホリノエチル（メタ）アクリレート、Ｎ，Ｎ－ジメチルアミノエチル（メタ）アクリレート、Ｎ，Ｎ－ジエチルアミノエチル（メタ）アクリレート及びＮ－ビニルピロリドンであることが好ましい。炭素材料の分散性の観点から、Ｎ，Ｎ－ジメチルアミノエチル（メタ）アクリレート、Ｎ，Ｎ－ジエチルアミノエチル（メタ）アクリレート、Ｎ－ビニルピロリドン、２，２，６，６－テトラメチルピペリジルエチル（メタ）アクリレート及びＮ－ビニル２，２，６，６－テトラメチルピペリジルであることがより好ましく、Ｎ－ビニルピロリドンであることがさらに好ましい。
共重合体（Ａ）は、本発明の炭素材料用分散剤の溶解性と炭素材料の分散性の観点から、窒素含有ビニルモノマー（ｂ）が少なくとも２種類のモノマー（ｂ１）を含有することが好ましい。
共重合体（Ａ）はランダム共重合体であってもブロック共重合体であってもよいが、本発明の炭素材料用分散剤の溶解性と炭素材料の分散性との両立の観点からランダム共重合体であることが好ましい。また共重合体（Ａ）は直鎖状であっても分岐状であってもよい。
共重合体（Ａ）は、本発明の炭素材料用分散剤の溶解性と炭素材料の分散性の両立の観点から、モノマー（ａ）及びモノマー（ｂ）に加え、炭素数１～４のアルキル基を有する（メタ）アクリル酸アルキルエステル（ｃ）（以下、モノマー（ｃ）ともいう）を構成単位として含有することが好ましい。
モノマー（ｃ）としては、メチル（メタ）アクリレート、エチル（メタ）アクリレート、プロピル（メタ）アクレート及びブチル（メタ）アクリレート等が挙げられる。モノマー（ｃ）のうち、本発明の炭素材料用分散剤の溶解性の観点からメチルメタクリレートであることが好ましい。
共重合体（Ａ）を構成するモノマー（ａ）の割合は、本発明の炭素材料用分散剤の溶解性の観点から、共重合体（Ａ）の重量に基づいて、７０～９０重量％であることが好ましく、８０～９０重量％であることがより好ましい。本発明の炭素材料用分散剤の溶解性又は炭素材料の分散性が向上し、これを分散物として用いた電池の電池性能を向上することができる。
共重合体（Ａ）を構成するモノマー（ｂ）の割合は、炭素材料の分散性の観点から、共重合体（Ａ）の重量に基づいて、１～３０重量％であることが好ましく、１～２０重量％であることがより好ましく、１～１５重量％であることがさらに好ましい。
共重合体（Ａ）を構成するモノマー（ｃ）の割合は、本発明の炭素材料用分散剤の溶解性の観点から、共重合体（Ａ）の重量に基づいて、５～２０重量％であることが好ましく、５～１５重量％であることがより好ましい。
窒素原子を含む基を有する共重合体は、公知の製造方法によって得ることができる。具体的には例えば、上記のモノマー（ａ）～（ｃ）を溶剤中で重合触媒存在下に溶液重合することにより共重合体（Ａ）を得る方法が挙げられる。 溶剤としては、トルエン、キシレン、炭素数９～１０のアルキルベンゼン、メチルエチルケトン及び鉱物油等が挙げられる。
重合触媒としては、アゾ系触媒（２，２’－アゾビス（２－メチルブチロニトリル）及び２，２’－アゾビス（２，４－ジメチルバレロニトリル）等）、過酸化物系触媒（ベンゾイルパーオキサイド、クミルパーオキサイド及びラウリルパーオキサイド等）及びレドックス系触媒（ベンゾイルパーオキサイドと３級アミンの混合物等）が挙げられる。更に必要により、公知の連鎖移動剤（炭素数２～２０のアルキルメルカプタン等）を使用することもできる。
重合温度は、工業化の観点から２５～１４０℃であることが好ましく、５０～１２０℃であることがより好ましい。また、上記の溶液重合の他に、塊状重合、乳化重合又は懸濁重合により窒素原子を含む基を有する共重合体を得ることができる。
窒素原子を含む基を有する共重合体の重量平均分子量（以下、Ｍｗと略記する場合がある）は、１万～３０万であることが好ましく、２．５万～２５万であることがより好ましく、分散安定性の観点から５万～２０万であることがさらに好ましい。共重合体の分子量分布曲線におけるピークトップ分子量（以下、Ｍｐと略記する場合がある）の１／４以下に相当する部分のピーク面積が全ピーク面積の１１．０％以下であることが好ましく、１０．０％以下であることがより好ましく、分散安定性の観点から９．０％以下であることがさらに好ましい。なお、分子量分布曲線におけるピーク面積は、分子量分布曲線の積分値から計算することができる。
なお、窒素原子を含む基を有する共重合体のＭｗ及びＭｐは、ゲルパーミエーションクロマトグラフィーにより、以下の条件で測定することができる。
 ＜Ｍｗ及びＭｐの測定条件＞
装置：「ＨＬＣ－８０２Ａ」［東ソー（株）製］
カラム：「ＴＳＫ ｇｅｌ ＧＭＨ６」［東ソー（株）製］２本
測定温度：４０℃
試料溶液：０．５重量％のテトラヒドロフラン溶液
溶液注入量：２００μｌ
検出装置：屈折率検出器
基準物質：標準ポリスチレン（ＴＳＫｓｔａｎｄａｒｄ ＰＯＬＹＳＴＹＲＥＮＥ）１２点（分子量：５００、１，０５０、２，８００、５，９７０、９，１００、１８，１００、３７，９００、９６，４００、１９０，０００、３５５，０００、１，０９０，０００、２，８９０，０００）［東ソー（株）製］
窒素原子を含む基を有する共重合体のＳＰ値は、溶解性の観点から８．０～１２（ｃａｌ／ｃｍ３）１／２、好ましくは８．５～１１（ｃａｌ／ｃｍ３）１／２、より好ましくは８．５～１０．５（ｃａｌ／ｃｍ３）１／２、特に好ましくは９．０～１０．０（ｃａｌ／ｃｍ３）１／２である。
ここで、本発明で示すＳＰ値とは、２５℃における溶解度パラメータ値であって、物質に固有の値であり、物質の溶解性を予測するための１つの指標である。ＳＰ値は、数値が大きいほど極性が高く、逆に数値が小さいほど極性が低いことを示す。そして、２種類の物質を混合する場合に、両者のＳＰ値の差が小さいほど、溶解度が大きくなる。
窒素原子を含む基を有する共重合体のＳＰ値（溶解度パラメーター）は、窒素原子を含む基を有する共重合体を形成する各モノマーのＳＰ値とモル比との積として算出されるものである。例えば、共重合体がＸ、Ｙの２種類のモノマーから形成されるものである場合、各モノマーのモル比をｘ、ｙ（モル％）、ＳＰ値をＳＰｘ、ＳＰｙとすると、この共重合体のＳＰ値は、下記関係式（１）で表される。
関係式（１）：ＳＰ＝［（ｘ×ＳＰｘ）＋（ｙ×ＳＰｙ）］
各モノマーのＳＰ値は、そのモノマーの分子構造中の原子又は原子団に対して、Ｆｅｄｏｒｓによって提案された［Ｐｏｌｙｍ．Ｅｎｇ．Ｓｃｉ．Ｖｏｌ．１１４．ｐ１１４（１９７４）］から蒸発エネルギー（Δｅｉ）及びモル体積（Δｖｉ）を求め、下記関係式（２）から算出される。但し、重合開裂する二重結合については、開裂した状態をその分子構造とする。
関係式（２）：σ＝（ΣΔｅｉ／ΣΔｖｉ）１／２
窒素原子を含む基を有する共重合体の窒素含有量は、ＡＮＴＥＫ社製ＡＮＴＥＫ７０００全窒素分析計を用いる方法で、測定することができる。
試料溶液中の窒素濃度が約１００ｐｐｍとなるように試料を１００ｍＬメスフラスコに１ｍｇの桁まで精秤し、キシレン等の窒素を含まない希釈溶剤で１００ｍＬになるよう希釈する。メスフラスコをよく振り、試料を完全に溶解させる。
キノリンを検量線用標準試薬とし、窒素濃度が約５０ｐｐｍ、約１００ｐｐｍ、約１５０ｐｐｍとなるようキシレンで希釈して検量線用標準液を調製する。
調製した窒素濃度の異なる検量線用標準液３種類を全窒素分析計による測定を行い、検量線を作成する。続いて調製した試料溶液を全窒素分析計による測定を行う。
測定結果から、下記の式用いて試料の窒素含量を計算する。（Ａを検量線から求めた試料溶液中の窒素濃度（ｐｐｍ）、Ｓを資料の採取量（ｇ）とする。）
窒素含量(重量％)＝Ａ／Ｓ×１／１００
窒素原子を含む基を有する共重合体中の窒素含有量は、炭素材料の分散性の観点から共重合体の重量を基準として０．０１～５重量％、好ましくは０．０５～３重量％であり、より好ましくは０．０５～２重量％であり、さらに好ましくは０．０５～０．７重量％である。
窒素含有量が０．０１重量％未満である場合は、炭素材料の分散性が不十分になる傾向があり好ましくない。一方、窒素含有量が５重量％を超える場合は、炭素材料の分散性が不十分になる傾向があり好ましくない。
＜分散物＞
本発明は、本発明の炭素材料用分散剤と、炭素材料と、比誘電率が１．５以上６．４以下の低極性溶媒、及び／又は、比誘電率が１．５以上６．４以下の炭化水素系樹脂である低極性媒体とを含有する分散物でもある。
本発明の分散物は、本発明の炭素材料用分散剤を含有するため、低極性溶媒及び低極性媒体への分散性に優れ、低極性溶媒及び低極性媒体中の炭素材料の分散安定性にも優れる。
また、本発明の分散物は、ハンドリング性向上の観点から、以下に示す任意の低極性溶媒又は低極性媒体を含有する。
本発明で使用可能な低極性溶媒としては、２０℃において水１００ｇに対する溶解度が１ｇ未満の溶媒等が挙げられる。ここで低極性溶媒とは、一般に非極性あるいは比誘電率が１０未満の溶媒を意味する。ヘプタン等のアルカン系溶媒のほか、酪酸ブチルやブチルエーテル等の、エステル基やエーテル基の両端がＣ４以上の炭素数である溶媒を用いることができる。
これらの中でも、本発明において使用する低極性溶媒は、比誘電率が１．５以上６．４以下の溶媒を使用することが固体電解質との反応抑制の観点から好ましい。比誘電率とは、有機溶媒の極性の強さを表す指標のひとつである。比誘電率の測定では、水分含量５ｐｐｍ以下の有機溶媒を測定サンプルとして５０ｍＬ使用する。キーコム社製Ｅ４９８０ＡプレシジョンＬＣＲメータと電極としてキーコム社製ＤＰＴ－０１３－０５０を用い、周波数１ＭＨｚの交流電圧を印加して、２５℃における比誘電率を測定する。
本発明で使用可能な有機溶媒としては、乾燥によって除去できる媒体であれば特に限定されないが、例えば、好ましくは比誘電率が１．５以上６．４以下の有機溶媒であるジブチルエーテル、エステル系溶媒（酢酸エチル、プロピオン酸エチル、プロピオン酸プロピル、プロピオン酸ブチル、プロピオン酸アミル、プロピオン酸ヘキシル、プロピオン酸ヘプチル、プロピオン酸オクチル、酪酸エチル、酪酸プロピル、酪酸ブチル、酪酸アミル、酪酸ヘキシル、酪酸ヘプチル、酪酸オクチル、吉草酸エチル、吉草酸プロピル、吉草酸ブチル、吉草酸アミル、吉草酸ヘキシル、吉草酸ヘプチル、吉草酸オクチル、カプロン酸エチル、カプロン酸プロピル、カプロン酸ブチル、カプロン酸アミル、カプロン酸ヘキシル、カプロン酸ヘプチル、カプロン酸オクチル、エナント酸エチル、エナント酸プロピル、エナント酸ブチル、エナント酸アミル、エナント酸ヘキシル、エナント酸ヘプチル、エナント酸オクチル等）、アルカン系溶媒（ペンタン、シクロペンタン、ヘキサン、シクロヘキサン、ヘプタン、シクロヘプタン、オクタン、シクロオクタン、ノナン、デカン等）、トルエン、キシレン、ベンゼン、パラフィン、四塩化炭素等が挙げられ、更に好ましくは、有機溶媒と固体電解質との反応抑制と融点と沸点との観点から、ブチルエステル（酪酸ブチル、プロピオン酸ブチル、吉草酸ブチル）及びアルカン系溶媒（ヘキサン、シクロヘキサン、ヘプタン、シクロヘプタン、オクタン、シクロオクタン）が挙げられる。
本発明において使用する低極性媒体は、比誘電率が１．５以上６．４以下の炭化水素系樹脂である低極性媒体を使用することが固体電解質との反応抑制の観点から好ましい。
このような低極性媒体としては、例えば、ポリエチレン、ポリイソブチレン、ポリプロピレン及びポリブチレン等のポリオレフィン、ポリブタジエン及び天然ゴム等のポリジエン、ポリイソプレン、ポリスチレン及びポリテトラフルオロエチレン等のビニル重合体、スチレンブタジエンゴム、スチレンエチレンブチレンゴム、スチレンエチレンプロピレンゴム、スチレンエチレンブチレンゴム、スチレンエチレンプロピレンゴム等のエラストマー等が挙げられる。
本発明の分散物は、導電助剤として、炭素材料を含有する。
炭素材料としては、導電性を有する炭素材料であれば特に限定されるものではないが、グラファイト、カーボンブラック（ＣＢ）、カーボンナノチューブ（ＣＮＴ）、カーボンナノファイバー（ＣＮＦ）、カーボンファイバー（ＣＦ）、アセチレンブラック（ＡＢ）、フラーレン、天然黒鉛等を単独で、もしくは２種類以上併せて使用することができる。電極内部抵抗低減の観点から、カーボンナノチューブ（ＣＮＴ）の使用が好ましい。
＜全固体リチウムイオン二次電池用電極スラリー＞
本発明は、本発明の分散物と、固体電解質と、正極活物質又は負極活物質とを含有する全固体リチウムイオン二次電池用電極スラリーでもある。
全固体リチウムイオン二次電池用電極（正極及び負極）を作製するために、前段階として全固体リチウムイオン二次電池用電極スラリーを調製する。
全固体リチウムイオン二次電池用電極スラリーは、本発明の分散物と、固体電解質と、正極活物質又は負極活物質と、バインダーとを加え、超音波分散装置（エスエムテー社製「ＵＨ－５０」）を用いて３０秒間攪拌混合して得ることが好ましい。
全固体リチウムイオン二次電池用電極スラリー１００質量部に対して、本発明の炭素材料用分散剤の含有量は、０．１～１０質量部であることが好ましく、炭素材料の分散性と充放電特性の両立の観点から好ましくは０．１～５質量部であることがより好ましい。
全固体リチウムイオン二次電池用電極スラリー１００質量部に対して、導電助剤としての炭素材料は、０．１～１０質量部であることが好ましく、充放電における入出力特性と充放電容量の両立の観点から０．１～５質量部であることがより好ましい。炭素材料の濃度が低いと電極の内部抵抗が増大することにより充放電における入出力性能が低下するおそれがある。また、高すぎると電極の単位面積当たりの活物質量が少なくなり、充放電容量が低下してしまうおそれがある。
全固体リチウムイオン二次電池用電極スラリーは、固体電解質を含有する。
固体電解質としては、硫化物系固体電解質、チタン酸リチウムランタン、ＬＩＳＩＣＯＮ、ｔｈｉｏ－ＬＩＳＩＣＯＮ、タンタル酸リチウムランタンバリウム、ヨウ化リチウム－酸化アルミニウムコンポジット、リン酸リチウムオキシナイトライドガラスが挙げられる。
固体電解質は、硫化物系固体電解質であることが好ましく、Ｌｉ、Ｐ及びＳを含むリチウムイオン伝導性無機固体電解質（硫化物系固体電解質）であることがより好ましく、Ｌｉ、Ｐ、Ｓ及びハロゲン元素を含むリチウムイオン伝導性無機固体電解質（硫化物系固体電解質）であることがさらに好ましい。
全固体リチウムイオン二次電池用電極スラリーは、正極活物質又は負極活物質を含有する。
正極活物質としては特に限定はされないが、全固体リチウムイオン二次電池に用いる場合には、リチウムイオンをドーピング又はインターカレーション可能な金属酸化物、金属硫化物等の金属化合物及び導電性高分子等を使用することができる。例えば、鉄、コバルト、ニッケル、バナジウム、マンガン等の遷移金属の酸化物、リチウムとの複合酸化物、遷移金属硫化物等の無機化合物等が挙げられる。具体的には、ＭｎＯ、Ｖ２Ｏ５、Ｖ６Ｏ１３、ＴｉＯ2等の遷移金属酸化物粉末、層状構造のニッケル酸リチウム、コバルト酸リチウム、マンガン酸リチウム、スピネル構造のマンガン酸リチウム等のリチウムと遷移金属との複合酸化物粉末、オリビン構造のリン酸化合物であるリン酸鉄リチウム系材料等が挙げられる。また、コーティング装置を用いて、ＬｉＮｂＯ３で表面をコーティングした正極活物質を使用することもできる。
全固体リチウムイオン二次電池用電極スラリー１００質量部に対して、正極活物質は３０～６０質量部であることが好ましく、塗工適性の観点から、３０～５０質量部であることがより好ましい。
負極活物質としては特に限定はされないが、全固体リチウムイオン二次電池に用いる場合には、リチウムイオンをドーピング又はインターカレーション可能な金属リチウム又はその合金、スズ合金、シリコン合金、ＬｉＸＦｅ２Ｏ３、ＬｉＸＦｅ３Ｏ４、ＬｉＸＷＯ２等（Ｘは任意の正数）の金属酸化物、ポリアセチレン、ポリ－ｐ－フェニレン等の導電性高分子、ソフトカーボンやハードカーボンといった、アモルファス系炭素質材料や、黒鉛化炭素材料等の人造黒鉛、あるいは天然黒鉛系カーボン等の炭素質粉末、カーボンブラック、メソフェーズカーボンブラック、樹脂焼成炭素材料、気層成長炭素繊維、炭素繊維等の炭素系材料が用いられる。
全固体リチウムイオン二次電池用電極スラリー１００質量部に対して、負極活物質は２０～５０質量部であることが好ましく、塗工適性の観点から２０～４０質量部であることがより好ましい。
本発明の全固体リチウムイオン二次電池用電極スラリーの調製用溶媒としては、本発明の炭素材料用分散剤に任意に配合することができる、低極性溶媒を用いることができる。
このような低極性溶媒としては、比誘電率が６．０以下であることが好ましく、比誘電率が５．５以下であることがより好ましく、充放電特性保持の観点から、比誘電率が５．１以下であることがさらに好ましい。
比誘電率が６．４を上回る溶媒では、固体電解質構成成分の分解反応を生じるため良好な電池性能が得られないおそれがある。
全固体リチウムイオン二次電池用電極スラリーは、バインダーを含有することが好ましい。
バインダ－としては、特に限定されないが、結着用樹脂、例えばポリフッ化ビニリデン（ＰＶＤＦ）、ブタジエンゴム（ＢＲ）、カルボキシメチルセルロース（ＣＭＣ）及びスチレンブタジエンゴム（ＳＢＲ）を用いることができる。高温耐久性の観点から、バインダーとしては、ポリイミド、ポリアミド、ポリアミドイミド、ポリアクリル、若しくはカルボキシメチルセルロース等、又はこれらの組み合わせが好ましい。
全固体リチウムイオン二次電池用電極スラリー１００質量部に対して、バインダーは０．５～２０質量部であることが好ましく、塗工適性の観点から１～１０質量部であることがより好ましい。
＜全固体リチウムイオン二次電池用電極＞
本発明は、本発明の分散物と、固体電解質と、正極活物質又は負極活物質とを含有する全固体リチウムイオン二次電池用電極でもある。
本発明の全固体リチウムイオン二次電池用電極では、固体電解質のイオン伝導性を阻害せずに炭素材料の分散安定化を図ることができるので、電気化学的安定性に優れる。
本発明の全固体リチウムイオン二次電池用電極は、本発明の分散物と、固体電解質と、正極活物質又は負極活物質とを混合することにより、本発明の全固体リチウムイオン二次電池用電極スラリーを調製する工程を含むことにより得ることができる。このような本発明の全固体リチウムイオン二次電池用電極の製造方法も本発明の一態様である。
正極は、例えば、本発明の分散物と、固体電解質と、正極活物質とを含有し、必要に応じて、バインダー、低極性溶媒を含有する正極スラリーを集電体上に塗布し、乾燥処理させることにより得ることができる。具体的には、ブレード法によって集電体上に上記正極スラリーを塗工し、自然乾燥させた後、１００℃でのホットプレート上で３０分間乾燥させて溶媒を取り除くことで、正極を作製することができる。
 上記正極中における、正極活物質の含有量は、５０質量％～９０質量％であることが好ましく、６０質量％～８０質量％であることがより好ましい。
負極は、例えば、本発明の分散物と、固体電解質と、負極活物質とを含有し、必要に応じて、バインダー、低極性溶媒を含有する負極スラリーを集電体上に塗布し、乾燥処理させることにより得ることができる。具体的には、ブレード法によって集電体上に上記負極スラリーを塗工し、自然乾燥させた後、１００℃のホットプレート上で３０分間乾燥させて溶媒を取り除くことで、負極を作製することができる。
上記負極中における、負極活物質の含有量は、４０質量％～８０質量％であることが好ましく、５０質量％～７０質量％であることがより好ましい。
集電体としては、特に限定されず、公知の集電体を用いることができる。例えば、アルミニウム、銅、チタン、ニッケル、ステンレス鋼（ＳＵＳ）、これらの合金等が挙げられる。軽量、耐食性、高導電性の観点から、アルミニウム、銅であることが好ましい。なお、正極と負極に用いる集電体は、同一の材料が用いられてもよいし、異なる材料が用いられてもよい。
ここで、本発明の炭素材料用分散剤は、全固体リチウムイオン二次電池に限らず、非水溶液系リチウムイオン二次電池用の電極スラリーを作製する際にも用いることができ、非水溶液電解質として極性溶媒を用いた場合と同程度の性能を発揮することができる。
＜全固体リチウムイオン二次電池＞
本発明は、全固体リチウムイオン二次電池用電極を用いた全固体リチウムイオン二次電池でもある。
本発明の全固体リチウムイオン二次電池は、このような構成を有するために、電池性能に優れる。
本発明の全固体リチウムイオン二次電池の製造方法としては、例えば、上記方法により得られた負極の負極スラリーを塗布した面上に、アプリケーターを使用して、ブレード法によって固体電解質のスラリーを塗布する。その後、固体電解質のスラリーを乾燥させて固体電解質層を得る。
上記により得られる固体電解質層を有する負極を金型に入れてプレスし、固体電解質層からなるセパレート層を負極上に作製する。
このセパレート層の一方の面に上記方法により得られた正極を重ね、プレスすることにより、全固体リチウムイオン二次電池を得ることができる。
＜炭素材料用分散剤の作製＞
＜製造例１＞
温度調節装置、バキューム攪拌翼、窒素流入口及び流出口を備えた反応容器に、撹拌装置、加熱冷却装置、温度計及び窒素導入管を備えた反応容器に、反応溶媒である酪酸ブチルを加え、表１の製造例１に示す各種モノマー（ａ）としてデシルメタクリレート１０質量部、ドデシルメタクリレート４０質量部、テトラデシルメタクリレート２０質量部及びオクタデシルメタクリレート２０質量部、モノマー（ｂ）としてＮ，Ｎ－ジメチルアミノエチルメタクリレート２重量部及びＮ－ビニルピロリドン３重量部、モノマー（ｃ）としてメチルメタクリレートを５重量部加えた。続いて２，２’－アゾビス（２－メチルブチロニトリル）０．１８重量部を投入し、窒素置換（気相酸素濃度：１００ｐｐｍ以下）を行った後、密閉下、撹拌しながら７６℃に昇温し、同温度で４時間重合反応を行った。１２０～１３０℃に昇温後、３０分撹拌して固形分濃度５０重量％の共重合体（Ａ－１）を得た。
製造例１と同様の方法に従って、表１に記載の原料を配合することで、固形分濃度５０重量％の製造例２～２０に示す共重合体（Ａ－２）～（Ａ－２０）を得た。以下、特に固形分濃度に言及せず指定した共重合体（Ａ－１）～（Ａ－２０）の重量部は、固形分濃度１００％の共重合体（Ａ－１）～（Ａ－２０）の重量部と同じである。
＜比較製造例１～３＞
製造例１と同様の方法に従って、表１に記載の原料を配合することで、固形分濃度５０重量％の比較用共重合体（Ａ’－１）～（Ａ’－３）を得た。以下、特に固形分濃度に言及せず指定した比較用共重合体（Ａ’－１）～（Ａ’－３）の重量部は、固形分濃度１００％の比較用共重合体（Ａ’－１）～（Ａ’－３）の重量部と同じである。
得られた共重合体（Ａ－１）～（Ａ－２０）及び比較用共重合体（Ａ’－１）～（Ａ’－３）の重量平均分子量は、ゲルパーミエーションクロマトグラフィーにより、以下の条件で測定した。
＜Ｍｗの測定条件＞
装置：「ＨＬＣ－８０２Ａ」［東ソー（株）製］
カラム：「ＴＳＫ ｇｅｌ ＧＭＨ６」［東ソー（株）製］２本
測定温度：４０℃
試料溶液：０．５重量％のテトラヒドロフラン溶液
溶液注入量：２００μｌ
検出装置：屈折率検出器
基準物質：標準ポリスチレン（ＴＳＫｓｔａｎｄａｒｄ ＰＯＬＹＳＴＹＲＥＮＥ）１２点（分子量：５００、１，０５０、２，８００、５，９７０、９，１００、１８，１００、３７，９００、９６，４００、１９０，０００、３５５，０００、１，０９０，０００、２，８９０，０００）［東ソー（株）製］
共重合体（Ａ）が、低極性媒体に可溶であることとは、共重合体（Ａ）の５重量％酪酸ブチル溶液の濁度が３００度（ホルマジン）以下である。
濁度は次の方法で測定できる。共立理化学研究所製デジタル濁度計５００Ｇを用い、測定波長６６０ｎｍ、液温２５℃、大気圧下で測定する。対照液として低極性溶媒を測定用ガラスセルに１０ｍＬ注液して濁度を測定し、この時の濁度を０度とする。測定サンプルは、共重合体（Ａ）および比較用共重合体（Ａ’）を固形分濃度５重量％となるように酪酸ブチルで希釈して作製する。測定サンプルは作成後、５分以内に測定する。
得られた固形分濃度５０重量％の共重合体（Ａ－１）～（Ａ－２０）及び固形分濃度５０重量％の比較用共重合体（Ａ’－１）～（Ａ’－３）について、濁度測定を行った。本願では、固形分濃度５０重量％の共重合体（Ａ－１）～（Ａ－２０）及び比較用共重合体（Ａ’－１）～（Ａ’－３）各１．０部を、低極性溶媒である酪酸ブチル９．０部で希釈し共立理化学研究所製デジタル濁度計５００Ｇ（ＴＢ－５００Ｇ）を用いて２５℃、大気圧下における濁度（ホルマジン）を測定した。表１に測定結果を示す。
Figure JPOXMLDOC01-appb-T000005
共重合体（Ａ－１）～（Ａ－２０）と比較用共重合体（Ａ’－１）～（Ａ’－３）中に含まれる窒素含有量（重量％）及びＳＰ値（ｃａｌ／ｃｍ３）１／２を下記表２に示す。
Figure JPOXMLDOC01-appb-T000006
以下、共重合体（Ａ－１）～（Ａ－２０）を含有する炭素材料用分散剤を、「分散剤」（Ａ－１）～（Ａ－２０）と、比較用共重合体（Ａ’－１）～（Ａ’－３）を含有する炭素材料用分散剤を、「比較用分散剤」（Ａ’－１）～（Ａ’－３）と記載する。
＜炭素材料の分散性評価＞
○分散性評価用スラリー
（実施例１）
上記製造方法にて得られた分散剤（Ａ－１）０．０５重量部と、カーボンナノチューブ（ＶＧＣＦ－Ｈ（昭和電工社製））（ＣＮＴ）１重量部とを分散媒である酪酸ブチル９９重量部と共にポリプロピレン製容器に投入した。
この容器を、超音波分散装置（エスエムテー社製ＵＨ－５０）を用いて１分間撹拌し、することによって、分散性評価用スラリー（Ｂ－１）を作製した。
（実施例２～４３）
実施例１と同様の方法により、表３に示す配合成分、配合部数に従って分散性評価用スラリー（Ｂ－２）～（Ｂ－４３）を得た。
なお、表３～６における共重合体（Ａ）の重量部数は固形分での重量部数である。
（比較例１～３）
実施例１と同様の方法により、表３に示す配合成分、配合部数に従って比較分散性評価用スラリー（Ｂ’－１）～（Ｂ’－３）を得た。
＜溶媒中の分散性評価＞
上記で得られた分散性評価用スラリー（Ｂ－１）～（Ｂ－４３）及び比較分散性評価用スラリー（Ｂ’－１）～（Ｂ’－３）をガラス製のサンプル缶に投入し、室温下で３０分間静置後の沈殿物の有無を目視で確認した。表３に結果を示す。
Figure JPOXMLDOC01-appb-T000007
○樹脂中における分散性評価
（実施例４４）
上記製造方法にて得られた分散剤（Ａ－１）０．０５重量部と、カーボンナノチューブ（ＶＧＣＦ－Ｈ（昭和電工社製））（ＣＮＴ）０．５重量部とを分散媒である酪酸ブチル８５重量部及びポリブタジエン１０重量部と共にポリプロピレン製容器に投入した。
この容器を、超音波分散装置（エスエムテー社製ＵＨ－５０）を用いて１分間撹拌し、することによって、分散性評価用スラリー（Ｂ－４４）を作製した。
（実施例４５～７４）
実施例４４と同様の方法により、表４に示す配合成分、配合部数に従って分散性評価用スラリー（Ｂ－４５）～（Ｂ－７４）を得た。
（比較例４～１１）
実施例４４と同様の方法により、表４に示す配合成分、配合部数に従って比較分散性評価用スラリー（Ｂ’－４）～（Ｂ’－１１）を得た。
＜分散性評価＞
上記で得られた分散性評価用スラリー（Ｂ－４４）～（Ｂ－７４）及び比較分散性評価用スラリー（Ｂ’－４）～（Ｂ’－１１）をガラス製のサンプル缶に投入し、室温下で３０分間静置後の凝集物の有無を目視で確認した。表４に結果を示す。
Figure JPOXMLDOC01-appb-T000008
＜Ｌｉ－Ｐ－Ｓ系固体電解質の作製＞
国際公開第２０１５／１１５５６１号に記載の方法に従って、Ｌｉ－Ｐ－Ｓ系固体電解質を作製した。具体的には、アルゴン雰囲気下（露点－７０℃）のグローブボックス内で、硫化リチウム（Ｌｉ２Ｓ、Ａｌｄｒｉｃｈ社製、純度＞９９．９８％）２．４２ｇ、五硫化二リン（Ｐ２Ｓ５、Ａｌｄｒｉｃｈ社製、純度＞９９％）３．９０ｇをそれぞれ秤量し、メノウ製乳鉢に投入し、メノウ製乳棒を用いて５分間混合した。なお、Ｌｉ２Ｓ及びＰ２Ｓ５はモル比でＬｉ２Ｓ：Ｐ２Ｓ５＝７５：２５とした。
ジルコニア製４５ｍＬ容器（フリッチュ社製）に、直径５ｍｍのジルコニアビーズを６６ｇ投入し、上記硫化リチウムと五硫化二リンの混合物全量を投入し、アルゴン雰囲気下で容器を完全に密閉した。フリッチュ社製遊星ボールミルＰ－７に容器をセットし、温度２５℃、回転数５１０ｒｐｍで２０時間メカニカルミリングを行い、黄色粉体の硫化物固体電解質材料（Ｌｉ－Ｐ－Ｓガラス、以下、７５Ｌｉ２Ｓ・２５Ｐ２Ｓ５ともいう）６．２０ｇを得た。
＜電池評価用、全固体リチウムイオン二次電池用正極スラリー（正極スラリーともいう）及び正極の作製＞
（実施例７５）
正極活物質として、平均粒径６μｍのＬｉＮｉ１／３Ｍｎ１／３Ｃｏ１／３Ｏ２（ＮＣＭともいう、シグマアルドリッチ社製）、硫化物系固体電解質として上記で作製した７５Ｌｉ２Ｓ・２５Ｐ２Ｓ５、バインダーとしてＰＶＤＦ、導電助剤としてカーボンナノチューブ（ＶＧＣＦ－Ｈ（昭和電工社製））（ＣＮＴ）、分散媒として酪酸ブチル及び分散剤（Ａ－１）を、表５に記載の重量部に従って、ポリプロピレン製容器内に入れた。
上記の容器を、超音波分散装置（エスエムテー社製ＵＨ－５０）を用いて３０秒間撹拌し、次いで震盪機（柴田化学社製ＴＴＭ－１）を用いて３分間震盪した。更に、この容器を、超音波分散装置を用いて３０秒間撹拌し、次いで震盪機を用いて３分間震盪することによって、正極スラリー（Ｃ－１）を得た。 
（実施例７６～９５、比較例１２～１４）
実施例７５と同様にして、正極スラリー（Ｃ－２）～（Ｃ－２１）、比較用正極スラリー（Ｃ’－１）～（Ｃ’－３）を得た。
Figure JPOXMLDOC01-appb-T000009
正極スラリー（Ｃ－１）～（Ｃ－２１）及び比較用正極スラリー（Ｃ’－１）、（Ｃ’－３）を、アプリケーターを使用して、ブレード法によって集電体としてのカーボン塗工アルミニウム箔上に塗工した。
塗工したアルミニウム箔を自然乾燥させた後、１００℃でのホットプレート上で３０分間乾燥させて、正極（Ｅ－１）～（Ｅ－２１）及び比較用正極（Ｅ’－１）、（Ｅ’－３）を作製した。
＜電池評価用、全固体リチウムイオン二次電池用負極スラリー（負極スラリーともいう）及び負極の作製＞
（実施例９６）
負極活物質として平均粒径１０μｍの天然黒鉛系カーボン（三菱ケミカル社製）、硫化物系固体電解質として７５Ｌｉ２Ｓ・２５Ｐ２Ｓ５、バインダー及び分散剤（Ａ－１）を表６に記載の重量部に従って、ポリプロピレン製容器内に入れた。
この容器を、超音波分散装置（エスエムテー社製ＵＨ－５０）を用いて３０秒間撹拌し、次いで震盪機（柴田化学社製ＴＴＭ－１）を用いて３０分間震盪することによって負極スラリー（Ｄ－１）を得た。
（実施例９７～１１６、比較例１５～１７）
 実施例９６と同様にして、負極スラリー（Ｄ－２）～（Ｄ－２１）、比較用負極スラリー（Ｄ’－１）～（Ｄ’－３）を得た。
Figure JPOXMLDOC01-appb-T000010
負極スラリー（Ｄ－１）～（Ｄ－２１）及び比較用負極スラリー（Ｄ’－１）～（Ｄ’－３）を、アプリケーターを使用して、ブレード法によって、集電体としての銅箔上に塗工した。
得られた塗工した銅箔を自然乾燥させた後、１００℃のホットプレート上で３０分間 乾燥させて、負極（Ｆ－１）～（Ｆ－２１）及び比較用負極（Ｆ’－１）～（Ｆ’－３）を作製した。
＜全固体リチウムイオン二次電池の作製＞
（実施例１１７）
硫化物系固体電解質として７５Ｌｉ２Ｓ・２５Ｐ２Ｓ５、バインダーとしてブタジエンゴム系バインダーの５質量％酪酸ブチル溶液、分散剤をボリプロピレン製容器内に入れた。
この容器を、超音波分散装置（エスエムテー社製ＵＨ－５０）を用いて３０秒間撹拌し、次いで震盪機（柴田化学社製ＴＴＭ－１）を用いて３０分間震盪することによってスラリーを得た。
得られたスラリーを、アプリケーターを使用して、ブレード法によって、作製した負極（Ｆ－１）の負極スラリーを塗布した面上に塗布し、分散媒を蒸発乾燥させ、固体電解質層を得た。
上記により得られた固体電解質層を有する負極（Ｆ－１）を、面積１ｃｍ２の金型に入れて、１０．０×１０７Ｐａでプレスし、固体電解質層からなるセパレート層を負極（Ｆ－１）上に作製した。このセパレート層の一方の面に、作製した正極（Ｅ－１）を重ねて１０．０×１０７Ｐａでプレスし、全固体リチウムイオン電池（Ｇ－１）を作製した。
（実施例１１８～１３７、比較例１８～２０）
実施例１３７と同様の方法により、表７に示す正極及び負極を用いて、全固体リチウムイオン電池（Ｇ－２）～（Ｇ－２１）及び比較用全固体リチウムイオン電池（Ｇ’－１）～（Ｇ’－３）を作製した。
＜電池特性評価＞
０．８ｍＡ（終止電流条件は、０．０１６ｍＡ）で４．１Ｖまでの充電と０．５ｍＡ（終止電流条件は、０．０１６ｍＡ）で３Ｖまでの放電を１サイクルとし、１サイクル目の放電容量を初期電池容量とした。その後、３．７Ｖまで充電し、４．８ｍＡで放電した際の５秒後の電圧降下量から、初期電池抵抗を求めた。 
次いで、０．８ｍＡで３．９Ｖまで充電し、１０分間の休止後、３Ｖまで０．５ｍＡで放電し、この充放電を１００サイクル繰り返し、１００サイクル目充放電時の放電容量を１００サイクル後電池容量とした。その後、３．７Ｖまで充電し、４．８ｍＡで放電した際の５秒後の電圧降下量から、１００サイクル後電池抵抗を求めた。
測定した初期電池容量及び１００サイクル後電池容量を用い、次式により容量維持率を算出した：
容量維持率（％）＝（１００サイクル後電池容量）／（初期電池容量）×１００
結果を以下の表７に示す。
Figure JPOXMLDOC01-appb-T000011
本発明の炭素材料用分散剤を使用すると、導電助剤等の炭素材料の低極性溶媒及び低極性媒体に対する親和性を高め、凝集を抑制して炭素材料に対する分散均一性及び分散安定性を高めることができる。
このため、本発明の炭素材料用分散剤を用いて作製される全固体リチウムイオン二次電池は、大電流での充電特性及び放電特性、サイクル特性及び電極の導電性に優れており、蓄電池電源用等として有用である。 

 

Claims (11)

  1. 窒素原子を含む基を有する共重合体を含有する炭素材料用分散剤であって、前記共重合体中の窒素含有量が０．０１重量％以上５重量％以下、前記共重合体のＳＰ値が８．０～１２（ｃａｌ／ｃｍ３）１／２である炭素材料用分散剤。
  2. 下記一般式（１）で示される（メタ）アクリル酸エステルモノマー（ａ）と、窒素原子含有ビニルモノマー（ｂ）との共重合体（Ａ）を含有する請求項１に記載の炭素材料用分散剤。 
    Figure JPOXMLDOC01-appb-C000001
      
    ［Ｒ１は水素原子又はメチル基；Ｘ１は炭素数２～４のオキシアルキレン基 ；Ｒ２は、ｐ＝０のとき炭素数８～３２のアルキル基であり、ｐ＝１～２０のとき炭素数１～３２のアルキル基；ｐは０～２０の整数であり、ｐが２以上の場合、複数のＸ１は同一でも異なっていてもよい。］
  3. 前記窒素原子含有ビニルモノマー（ｂ）が、下記一般式（２）で示されるモノマー（ｂ１）である請求項２に記載の炭素材料用分散剤。
    Figure JPOXMLDOC01-appb-C000002
     ［一般式（２）におけるＲ３は、水素原子又はメチル基である。；Ｘ２は、エステル基、アミド基 、カルボニル基及び脂肪族炭化水素基からなる群から選ばれる少なくとも１種類の基であり、ｑは０又は１の整数である。；Ｘ３は、炭素数２～４のアルキレン基であり、ｒは０又は１の整数である。；一般式（２）におけるアミノ基に含まれるＲ４及びＲ５は、同一でも異なっていてもよい炭素数１～４である炭化水素基であって、結合して環を形成してもよい。一般式（２）におけるアミノ基がＲ４とＲ５を結合してなる環状アミノ基である場合、前記環状アミノ基は、炭素数４若しくは５の炭化水素基及び０～２個のカルボニル基を含有する。］
  4. 前記窒素原子含有ビニルモノマー（ｂ）が、少なくとも２種類の前記モノマー（ｂ１）を含有する請求項３に記載の炭素材料用分散剤。
  5. 前記窒素原子含有ビニルモノマー（ｂ）が、Ｎ－ビニルピロリドンを含有する請求項２～４のいずれか１項に記載の炭素材料用分散剤。
  6. 請求項１～５のいずれか１項に記載の炭素材料用分散剤と、
    炭素材料と、
    比誘電率が１．５以上６．４以下の低極性溶媒、及び／又は、比誘電率が１．５以上６．４以下の炭化水素系樹脂である低極性媒体とを含有する分散物。
  7. 前記炭素材料は、グラファイト、カーボンブラック（ＣＢ）、カーボンナノチューブ（ＣＮＴ）、カーボンナノファイバー（ＣＮＦ）、カーボンファイバー（ＣＦ）、アセチレンブラック（ＡＢ）、フラーレン及び天然黒鉛からなる群から選ばれる少なくとも１種類の炭素材料である請求項６に記載の分散物。
  8. 請求項６又は７に記載の分散物と、固体電解質と、正極活物質又は負極活物質とを含有する全固体リチウムイオン二次電池用電極スラリー。
  9. 請求項６又は７に記載の分散物と、固体電解質と、正極活物質又は負極活物質とを混合することにより請求項８に記載の全固体リチウムイオン二次電池用電極スラリーを調製する工程を含む全固体リチウムイオン二次電池用電極の製造方法。
  10. 請求項６又は７に記載の分散物と、固体電解質と、正極活物質又は負極活物質とを含有する全固体リチウムイオン二次電池用電極。
  11. 請求項１０に記載の全固体リチウムイオン二次電池用電極を用いた全固体リチウムイオン二次電池。
     

     
PCT/JP2018/031403 2017-08-31 2018-08-24 炭素材料用分散剤、該炭素材料用分散剤を含有する分散物、全固体リチウムイオン二次電池用電極スラリー、全固体リチウムイオン二次電池用電極の製造方法、全固体リチウムイオン二次電池用電極及び全固体リチウムイオン二次電池 Ceased WO2019044716A1 (ja)