WO2014123065A1 - 金属加飾板 - Google Patents

金属加飾板 Download PDF

Info

Publication number
WO2014123065A1
WO2014123065A1 PCT/JP2014/052219 JP2014052219W WO2014123065A1 WO 2014123065 A1 WO2014123065 A1 WO 2014123065A1 JP 2014052219 W JP2014052219 W JP 2014052219W WO 2014123065 A1 WO2014123065 A1 WO 2014123065A1
Authority
WO
WIPO (PCT)
Prior art keywords
layer
metal
adhesive layer
plate
metal decorative
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/JP2014/052219
Other languages
English (en)
French (fr)
Inventor
真一 北村
徳勲 瀧西
元 仲川
鉄矢 中山
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nissha Printing Co Ltd
Original Assignee
Nissha Printing Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nissha Printing Co Ltd filed Critical Nissha Printing Co Ltd
Publication of WO2014123065A1 publication Critical patent/WO2014123065A1/ja
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

【課題】金属加飾板から金属加飾成形品を作成する場合に、柄層などにクラックが発生せず、かつ金属加飾成形品の表面に凹凸形状が発生しないような金属加飾板を提供する。 【解決手段】本発明の金属加飾板１は、金属板２と熱可塑性樹脂を含む接着層３および柄層４と前記柄層の上に積層される艶消し層５とを備え、艶消し層と柄層と艶消し層の厚みの合計が５μｍ～２０μｍであり、艶消し層の表面粗さが金属板の表面粗さよりも大きい金属加飾板となるように構成した。

Description

金属加飾板
　本発明は金属加飾板に関し、金属板の表面形状が表面に発生しにくい金属加飾板に関する。
　転写シートを用いてプラスチック部品や外装品のような物品の表面を装飾する方法が従来から知られている。転写シートは、支持体である基体シートの片面上に転写層が設けられた構成であり、この転写層が基体シートから物品の表面に転写される。物品の表面に転写された転写層は樹脂や図柄等が積層された積層体であり、物品表面に保護被覆や装飾被覆を形成する。
　上記転写シートを用いた製品として、金属加飾成形品（例えば、パソコンの筐体）が挙げられる。金属加飾成形品は、転写シートを用いて金属板上に接着層、柄層、ハードコート層が積層された金属加飾板を、プレス加工したものである（例えば、特許文献１)。
特開２００７－２４５７２５号公報
　しかし、特許文献１の方法で金属加飾板をプレス加工して金属加飾成形品を作成すると、その表面に金属板の表面形状が現れる。
　本発明は、金属加飾板をプレス加工して金属加飾成形品を作成する場合に、金属加飾成形品の表面に金属板の表面形状が現れない金属加飾板を提供する。
　上記目的を達成するために、本発明は以下のように構成する。
　本発明の第１態様の特徴は、金属板と、前記金属板の上に積層され熱可塑性樹脂を含む接着層と、前記接着層の上に積層され熱可塑性樹脂を含む柄層と、前記柄層の上に積層される艶消し層とを備え、前記接着層と、前記柄層と、前記艶消し層の厚みの合計が、５μｍ～２０μｍであり、前記艶消し層の表面粗さが前記金属板の表面粗さよりも大きい金属加飾板を提供する。
　本発明の第２態様の特徴は、前記接着層と前記柄層を構成する熱可塑性樹脂が、アクリル樹脂、ウレタン樹脂、塩酸ビニル樹脂、エポキシ樹脂、ポリエステルの一群から少なくとも選ばれる一の樹脂と酢酸ビニル樹脂との共重合体である金属加飾板を提供する。
　本発明の第３態様の特徴は、前記艶消し層の上に保護フィルムが積層され、前記保護フィルムは、全光線透過率が９０％～９５％であり、ヘイズ値が３％～２０％である金属加飾板を提供する。　
　本発明の第４態様の特徴は、前記柄層および前記接着層のガラス転移点以上であって、保護フィルムの溶融温度以下に熱し、プレス加工する金属加飾成形品の製造方法を提供する。
　本発明の第５態様の特徴は、上記方法で作成された金属加飾成形品を提供する。
本発明の金属加飾板の断面図である。 転写シートの断面図である。 本発明の金属加飾板の製造方法にかかる断面図である。 本発明の金属加飾成形品の製造方法にかかる断面図である。 本発明の金属加飾成形品にかかる断面図である。
　下記で、本発明に係る実施形態を図面に基づいてさらに詳細に説明する。なお、本発明の実施例に記載した部位や部分の寸法、材質、形状、その相対位置などは、とくに特定的な記載がない限り、この発明の範囲をそれらのみに限定する趣旨のものではなく、単なる説明例にすぎない。
［金属加飾板］
　図１は、本発明の本実施形態の金属加飾板１の構造を示す断面図である。図１に示すように、金属加飾板１は、金属板２の片面に接着層３、柄層４、艶消し層５、保護フィルム６が、この順番で積層された構成からなる。また、接着層３、柄層４、艶消し層５は、その厚みの合計が５μｍ～２０μｍとなるように構成されている。上記層の厚みの合計が５μｍ～２０μｍであれば、本発明の金属加飾板１をプレス加工して得られる金属加飾成形品を触ったとき、金属加飾成形品から金属が有する触感を得ることができる。なお、厚みの合計が５μｍ未満であると、金属板と上記層との密着力が不足するという問題や、金属加飾板の表面硬度が十分でなくなるという問題が発生し、２０μｍを超えると金属加飾板から金属の有する触感が得られないという問題が発生する。
　なお、接着層３、柄層４、艶消し層５の厚みの合計が５μｍ～２０μｍの場合、艶消し層５の表面粗さは、金属板２の表面粗さより大きいことが好ましい。艶消し層５の表面粗さが金属板２の表面粗さより大きいと、本発明の金属加飾板１をプレス加工して得られる金属加飾成形品の表面形状は艶消し層５の表面形状が支配的になり、金属加飾成形品の表面に金属板２の表面形状が現れなくなる。
　以下で、金属板２、接着層３、柄層４、艶消し層５、保護フィルム６の材質などについて詳細に説明する。
　＜金属板＞
　金属板２は、接着層３、柄層４、艶消し層５、保護フィルム６などを保持する板状の部材であり、アルミニウム、マグネシウム、ＳＵＳなどから構成される。
　＜接着層＞
　接着層３は、金属板２と柄層４、艶消し５、保護フィルム６を接着するための層である。接着層３は、熱可塑性樹脂から構成される。具体的には、アクリル樹脂、ウレタン樹脂、塩酸ビニル樹脂、エポキシ樹脂、ポリエステルの一群から少なくとも選ばれる一の樹脂と酢酸ビニル樹脂との共重合体から構成される。接着層３が上記のように構成されると、金属板２と接着層３の密着性が向上する。また接着層３が上記のように構成されると、金属加飾板１を熱すると接着層３は柔らかくなる。すなわち、金属加飾板１をプレス加工するとき、金属加飾板１を加熱しておけば接着層３が柔らかくなった状態で金属加飾板１をプレス加工することができるので、接着層３内でクラックを発生させずに金属加飾成形品を作成することができる。
　＜柄層＞
　柄層４は、金属加飾板１を装飾する層である。柄層４の材質としては、接着層３と同一の樹脂を用いることができる。接着層３と同一の樹脂を用いることにより、接着層３と柄層４との密着性が向上する。また、上記のように構成することで接着層３の場合と同様に、柄層４内でクラックを発生させずに金属加飾成形品を作成することができる。
　＜艶消し層＞
　艶消し層５は、金属加飾板１の表面に配置される層である。そのため、艶消し層５は、柄層４、接着層３、金属板２を保護するために一定以上の硬度を有している。艶消し層５の材質としては、シアノアクリレート系やウレタンアクリレートなどの電離放射線硬化性樹脂や、アクリル系やウレタン系などの熱硬化性樹脂が挙げられるが、特に限定されない。
　＜保護フィルム＞
　保護フィルム６は、金属加飾板１をプレス加工するときに、金属加飾板１に傷や汚れが入らないよう、金属加飾板１を保護するためものである。保護フィルム６は、全光線透過率（ＪＩＳ Ｋ ７３６１－１）が９０％～９５％であり、ヘイズ値が３％～２０％であることが好ましい。全光線透過率とグロス値が上記範囲内にあると、保護フィルム６と艶消し層５との間に塵やゴミが入ったときに、目視による検査が容易になる。なお、保護フィルム６は、アクリル、ウレタン、ＰＥＴ、ＰＥ、オレフィンからなり、厚みは２０μｍ～６０μｍからなる。
　＜その他の構成＞
　図示しないが、艶消し層５と保護フィルム６との間には、感圧接着層が積層されていてもよい。この場合、感圧接着層と保護フィルム６との剥離重さは、感圧接着層と艶消し層５の剥離重さより大きいことが好ましい。上記のようであれば、保護フィルム６を金属加飾板１から剥離するとき、感圧接着層は保護フィルム６に残り、艶消し層５には残らない。その結果、意匠性の高い金属加飾成形品４０を作成できる。また、感圧接着層の剥離重さは、３．５Ｎ／２０ｍｍ～５．０Ｎ／２０ｍｍであることが好ましい。剥離重さが３．５Ｎ／２０ｍｍ未満であると、感圧接着層自身が軟弱となり、保護フィルム６を金属加飾板１から剥離して金属加飾成形品４０を作成するときに、感圧接着層の破壊（すなわち、感圧接着層内で層内分離）が生じる。その結果、保護フィルム６を剥離すると艶消し層５の表面に感圧接着層の一部が付着するという問題が発生する。剥離重さが５．０Ｎ／２０ｍｍを越えると、保護フィルム６を剥離する時の作業性が悪くなり、場合によっては保護フィルム６を金属加飾成形品から剥離する際に、金属加飾成形品４０自体が変形するという問題が発生する。
　次に、金属加飾板１の製造方法について説明する。
　図２は、転写シート１０の構造を示す断面図であり、図３は金属加飾板１の製造工程の一部を示す断面図である。
　金属加飾板１は、転写シート１０を使用して作成される。図２で示すように、転写シート１０は、基体シート１１の片面に転写層１２が設けられた構成からなる。基体シート１１は、ＰＥＴなどの合成樹脂から構成され、転写層１２は、基体シート１１側から順に艶消し層５、柄層４、接着層３が積層された構成からなる。艶消し層５、柄層４、接着層３の基体シート１１上への積層は、特に断らない限り、グラビアコート法、ロールコート法、コンマコート法などのコート法、またはグラビア印刷法、スクリーン印刷法などの印刷法によって行う。
　図３に示すように、転写シート１０を使用した金属加飾板１の製造方法は、まず、転写シート１０の転写層１２側の面を金属板２の表面に重ねる。そして、ロール転写機、アップダウン転写機などの転写機２０を用いて、転写シート１０の基体シート１１側から熱及び圧力をかける。このようにすることで、転写シート１０が金属板２の表面に接着する。
　転写シート１０と金属板２との接着が完了すれば、基体シート１１を金属板２から剥離する。このようにすると、転写層１２が金属板２の表面に転写されて、金属加飾板１が作成される。また、この金属加飾板１の艶消し層５の上に保護フィルム６を形成してもよい。なお、艶消し層５の上に保護フィルム６を形成する場合は、ラミネート法などの貼着方法によって、艶消し層５の上に保護フィルム６を形成する。
　次に、上記で作成した金属加飾板１を用いた金属加飾成形品の製造方法と金属加飾成形品について説明する。
　図４は、金属加飾成形品４０の製造工程を表す断面図であり、図５は、金属加飾成形品４０の断面図である。図４に示すように、金属加飾成形品４０の製造にはプレス加工機３０が用いられる。プレス加工機３０は、載置台３１と金型３２から構成され、載置台３１と金型３２の表面形状は、成形したい金属加飾成形品４０の形状に成形されている。また、載置台３１と金型３２の表面にはヒータ３３、３４が設置されている。
　図４に示すように、プレス加工機３０を用いて金属加飾成形品を製造する場合は、まずプレス加工機３０の載置台３１に金属加飾板１を設置する。載置台３１に金属加飾板１が設置されると、載置台３１内に設置されたヒータ３３によって、金属加飾板１が温められる。このとき金属加飾板１は、金属加飾板１を構成する接着層３や柄層４のガラス転移点以上であって、保護フィルムの溶融温度以下の範囲で温められる。金属加飾板１が上記温度まで温められることで、接着層３や柄層４が柔らかくなり、金属加飾板１をプレスする際に接着層３や柄層４にクラックが発生するのを防止できる。
　なお、金属加飾板１が上記温度まで温められると、次に金型３２を降下させて載置台３１と金型３２を型閉めし、金属加飾板１をプレス加工する。プレス加工する際の圧力と時間については、例えば、圧力が１ＭＰａ～３ＭＰａ、時間が２秒間程度である。
　プレス加工が終了すると、載置台３１から金型３２を分離させて載置台３１から成形された金属加飾板１を取り出す。最後に、取り出した金属加飾板１から保護フィルム６を剥離して金属加飾成形品４０を得る。図５に示すように、このようにして得られた金属加飾成形品４０は、接着層３や柄層４にクラックがなく、かつ金属加飾成形品４０の表面に金属板２の表面形状が表現されていない意匠性の高い金属加飾成形品４０となっている。
　なお、上記では載置台３１と金型３２にヒータ３３、３４が設置されたプレス加工機３０を用いて金属加飾成形品４０を作成する場合について説明した。しかし、載置台３１と金型３２にヒータ３３、３４が設置されていない場合には、あらかじめ金属加飾板１を室温以上であって、接着層３や柄層４のガラス転移点以下の範囲で温めておき、温めた金属加飾板１を載置台３１に設置してプレス加工すればよい。
　１：金属加飾板
　２：金属板
　３：接着層
　４：柄層
　５：艶消し層
　６：保護フィルム
　１０：転写シート
　１１：基体シート
　１２：転写層
　２０：金属板
　２１：ロール転写機
　３０：プレス加工機
　３１：載置台
　３２：金型
　３３：ヒータ
　３４：ヒータ
　４０：金属加飾成形品

Claims (5)

  1. 　金属板と、
    　前記金属板の上に積層され熱可塑性樹脂を含む接着層と、
    　前記接着層の上に積層され熱可塑性樹脂を含む柄層と、
    　前記柄層の上に積層される艶消し層とを備え、
    　前記接着層と前記柄層と前記艶消し層の厚みの合計が５μｍ～２０μｍであり、
    　前記艶消し層の表面粗さが前記金属板の表面粗さよりも大きい金属加飾板。
  2. 　前記接着層と前記柄層を構成する熱可塑性樹脂が、アクリル樹脂、ウレタン樹脂、塩酸ビニル樹脂、エポキシ樹脂、ポリエステルの一群から少なくとも選ばれる一の樹脂と酢酸ビニル樹脂との共重合体である請求項１の金属加飾板。
  3. 　前記艶消し層の上に保護フィルムが積層され、
    　前記保護フィルムは、全光線透過率が９０％～９５％であり、ヘイズ値が３％～２０％である請求項１～２の金属加飾板。　
  4. 　請求項１～３の金属加飾板を前記柄層および前記接着層のガラス転移点以上であって、
    　保護フィルムの溶融温度以下に熱し、プレス加工する金属加飾成形品の製造方法。
  5. 　請求項４の方法で作成された金属加飾成形品。
PCT/JP2014/052219 2013-02-07 2014-01-31 金属加飾板 Ceased WO2014123065A1 (ja)