WO2012073977A1 - Composition de caoutchouc fluoré pouvant être réticulée et article de caoutchouc réticulé - Google Patents

Composition de caoutchouc fluoré pouvant être réticulée et article de caoutchouc réticulé Download PDF

Info

Publication number
WO2012073977A1
WO2012073977A1 PCT/JP2011/077579 JP2011077579W WO2012073977A1 WO 2012073977 A1 WO2012073977 A1 WO 2012073977A1 JP 2011077579 W JP2011077579 W JP 2011077579W WO 2012073977 A1 WO2012073977 A1 WO 2012073977A1
Authority
WO
WIPO (PCT)
Prior art keywords
fluoropolymer
fluororubber composition
carbon atoms
crosslinkable fluororubber
group
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/JP2011/077579
Other languages
English (en)
Japanese (ja)
Inventor
宏樹 長井
武志 山田
杉山　徳英
雅博 大倉
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
AGC Inc
Original Assignee
Asahi Glass Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Asahi Glass Co Ltd filed Critical Asahi Glass Co Ltd
Priority to JP2012546896A priority Critical patent/JPWO2012073977A1/ja
Publication of WO2012073977A1 publication Critical patent/WO2012073977A1/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

La présente invention concerne une composition de caoutchouc fluoré pouvant être réticulée qui permet la fabrication d'un article de caoutchouc réticulé présentant d'excellentes caractéristiques en termes de résistance aux agents chimiques et à la chaleur, ainsi qu'un article de caoutchouc réticulé fabriqué à l'aide de la composition de caoutchouc fluoré pouvant être réticulée. L'invention concerne une composition de caoutchouc fluoré pouvant être réticulée qui comporte un caoutchouc fluoré et un polymère fluoré (P) qui possède une unité répétitive issue d'un diène fluoré (b), ayant une efficacité résiduelle de chaîne latérale insaturée, et de multiples doubles liaisons polymérisables, ainsi qu'un article de caoutchouc réticulé obtenu par réticulation de la composition de caoutchouc fluoré pouvant être réticulée.
PCT/JP2011/077579 2010-11-30 2011-11-29 Composition de caoutchouc fluoré pouvant être réticulée et article de caoutchouc réticulé Ceased WO2012073977A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
JP2012546896A JPWO2012073977A1 (ja) 2010-11-30 2011-11-29 架橋性フッ素ゴム組成物および架橋ゴム物品

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2010266864 2010-11-30
JP2010-266864 2010-11-30

Publications (1)

Publication Number Publication Date
WO2012073977A1 true WO2012073977A1 (fr) 2012-06-07

Family

ID=46171906

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2011/077579 Ceased WO2012073977A1 (fr) 2010-11-30 2011-11-29 Composition de caoutchouc fluoré pouvant être réticulée et article de caoutchouc réticulé

Country Status (3)

Country Link
JP (1) JPWO2012073977A1 (fr)
TW (1) TW201229072A (fr)
WO (1) WO2012073977A1 (fr)

Cited By (13)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2014030586A1 (fr) * 2012-08-21 2014-02-27 旭硝子株式会社 Polymère contenant du fluor durcissable, son procédé de fabrication, et produit durci de polymère contenant du fluor
WO2015146851A1 (fr) * 2014-03-25 2015-10-01 旭硝子株式会社 Article en caoutchouc fluoré moulé
JPWO2014084082A1 (ja) * 2012-11-29 2017-01-05 旭硝子株式会社 フッ素ゴム組成物およびこれを用いた架橋ゴム物品
WO2017086323A1 (fr) * 2015-11-19 2017-05-26 旭硝子株式会社 Composition réticulable contenant un copolymère fluoré, objet réticulé, et matériau d'étanchéité pour dispositif de production de semi-conducteurs
US9982091B2 (en) 2014-03-06 2018-05-29 3M Innovative Properties Company Highly fluorinated elastomers
WO2019054293A1 (fr) * 2017-09-14 2019-03-21 三菱電線工業株式会社 Composition de caoutchouc non réticulé et produit en caoutchouc fabriqué à l'aide de celle-ci et procédé de fabrication associé
JP2019214743A (ja) * 2019-09-19 2019-12-19 三菱電線工業株式会社 ゴム製品及びその製造方法
JP2020070326A (ja) * 2018-10-30 2020-05-07 三菱電線工業株式会社 未架橋フッ素ゴム組成物及びそれを用いて製造されるゴム製品
JP2021105179A (ja) * 2018-03-29 2021-07-26 三菱電線工業株式会社 未架橋ゴム組成物並びにそれを用いて製造されるゴム製品及びその製造方法
CN115605540A (zh) * 2020-05-14 2023-01-13 霓佳斯株式会社（Jp） 橡胶组合物、含氟弹性体和密封材料
CN116507651A (zh) * 2020-11-25 2023-07-28 大金工业株式会社 含氟聚合物、水性分散液、组合物和交联物
WO2024046494A1 (fr) * 2022-10-12 2024-03-07 嘉兴富瑞邦新材料科技有限公司 Film étirable en polytétrafluoroéthylène perméable à l'air et son procédé de préparation
WO2024254906A1 (fr) * 2023-06-14 2024-12-19 上海森桓新材料科技有限公司 Procédé de passivation d'un groupe terminal de fluoroélastomère

Families Citing this family (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN105622871B (zh) * 2015-12-23 2018-03-16 西安交通大学 一种交联型氟聚合物基介电弹性体复合材料及其制备方法

Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH05230151A (ja) * 1991-08-06 1993-09-07 Asahi Glass Co Ltd 含フッ素ポリマーおよび硬化物
JP2004346087A (ja) * 2002-04-23 2004-12-09 Yunimatekku Kk 含フッ素エラストマーおよびその組成物
WO2006080259A1 (fr) * 2005-01-27 2006-08-03 Kureha Corporation Polymère de type coeur-écorce à base de fluorure de vinylidène et utilisation de celui-ci dans un dispositif électrochimique non aqueux

Patent Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH05230151A (ja) * 1991-08-06 1993-09-07 Asahi Glass Co Ltd 含フッ素ポリマーおよび硬化物
JP2004346087A (ja) * 2002-04-23 2004-12-09 Yunimatekku Kk 含フッ素エラストマーおよびその組成物
WO2006080259A1 (fr) * 2005-01-27 2006-08-03 Kureha Corporation Polymère de type coeur-écorce à base de fluorure de vinylidène et utilisation de celui-ci dans un dispositif électrochimique non aqueux

Cited By (20)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2014030586A1 (fr) * 2012-08-21 2014-02-27 旭硝子株式会社 Polymère contenant du fluor durcissable, son procédé de fabrication, et produit durci de polymère contenant du fluor
EP2889315A4 (fr) * 2012-08-21 2016-04-06 Asahi Glass Co Ltd Polymère contenant du fluor durcissable, son procédé de fabrication, et produit durci de polymère contenant du fluor
JPWO2014084082A1 (ja) * 2012-11-29 2017-01-05 旭硝子株式会社 フッ素ゴム組成物およびこれを用いた架橋ゴム物品
US9815972B2 (en) 2012-11-29 2017-11-14 Asahi Glass Company, Limited Fluoro-rubber composition and cross-linked rubber article using same
US9982091B2 (en) 2014-03-06 2018-05-29 3M Innovative Properties Company Highly fluorinated elastomers
WO2015146851A1 (fr) * 2014-03-25 2015-10-01 旭硝子株式会社 Article en caoutchouc fluoré moulé
US10005888B2 (en) 2014-03-25 2018-06-26 Asahi Glass Company, Limited Fluororubber molded article
WO2017086323A1 (fr) * 2015-11-19 2017-05-26 旭硝子株式会社 Composition réticulable contenant un copolymère fluoré, objet réticulé, et matériau d'étanchéité pour dispositif de production de semi-conducteurs
CN111094437B (zh) * 2017-09-14 2022-05-13 三菱电线工业株式会社 未交联橡胶组合物以及使用该未交联橡胶组合物制造的橡胶产品及其制造方法
JP2019052226A (ja) * 2017-09-14 2019-04-04 三菱電線工業株式会社 ゴム製品及びその製造方法
CN111094437A (zh) * 2017-09-14 2020-05-01 三菱电线工业株式会社 未交联橡胶组合物以及使用该未交联橡胶组合物制造的橡胶产品及其制造方法
US20200277467A1 (en) * 2017-09-14 2020-09-03 Mitsubishi Cable Industries, Ltd. Uncrosslinked rubber composition and rubber product manufactured by using same and manufacturing method therefor
WO2019054293A1 (fr) * 2017-09-14 2019-03-21 三菱電線工業株式会社 Composition de caoutchouc non réticulé et produit en caoutchouc fabriqué à l'aide de celle-ci et procédé de fabrication associé
JP2021105179A (ja) * 2018-03-29 2021-07-26 三菱電線工業株式会社 未架橋ゴム組成物並びにそれを用いて製造されるゴム製品及びその製造方法
JP2020070326A (ja) * 2018-10-30 2020-05-07 三菱電線工業株式会社 未架橋フッ素ゴム組成物及びそれを用いて製造されるゴム製品
JP2019214743A (ja) * 2019-09-19 2019-12-19 三菱電線工業株式会社 ゴム製品及びその製造方法
CN115605540A (zh) * 2020-05-14 2023-01-13 霓佳斯株式会社（Jp） 橡胶组合物、含氟弹性体和密封材料
CN116507651A (zh) * 2020-11-25 2023-07-28 大金工业株式会社 含氟聚合物、水性分散液、组合物和交联物
WO2024046494A1 (fr) * 2022-10-12 2024-03-07 嘉兴富瑞邦新材料科技有限公司 Film étirable en polytétrafluoroéthylène perméable à l'air et son procédé de préparation
WO2024254906A1 (fr) * 2023-06-14 2024-12-19 上海森桓新材料科技有限公司 Procédé de passivation d'un groupe terminal de fluoroélastomère

Also Published As

Publication number Publication date
TW201229072A (en) 2012-07-16
JPWO2012073977A1 (ja) 2014-05-19

Similar Documents

Publication Publication Date Title
WO2012073977A1 (fr) Composition de caoutchouc fluoré pouvant être réticulée et article de caoutchouc réticulé
CN1827657B (zh) 氟化高弹体胶乳、其制备方法、氟化高弹体和氟橡胶模制产品
TWI672321B (zh) 高氟化彈性體
US11732073B2 (en) Fluorinated elastic copolymer, its composition and crosslinked rubber article
TWI491648B (zh) Crosslinkable fluorine rubber composition and cross-linked rubber items
JP6582991B2 (ja) ペルフルオロエラストマー、ペルフルオロエラストマー組成物、及び架橋ゴム物品
JPWO1999024484A1 (ja) 成形用材料
JP7283383B2 (ja) 架橋性含フッ素弾性共重合体の製造方法
WO2014030586A1 (fr) Polymère contenant du fluor durcissable, son procédé de fabrication, et produit durci de polymère contenant du fluor
WO2019073934A1 (fr) Composition copolymère élastique fluorée, peinture, et article peint
US5824755A (en) Process for producing fluoroelastomers
EP1808448B1 (fr) Procédé pour produire des fluorocopolymères élastiques et des fluoroélastomères réticulés
JP2005220161A (ja) 加硫用パーフルオロエラストマー組成物およびパーフルオロエラストマー成型品の製造方法
JPWO2019009250A1 (ja) 含フッ素弾性共重合体組成物および架橋ゴム物品
JP2007056215A (ja) パーオキサイド架橋可能なフッ素ゴム
WO2022260138A1 (fr) Procédé de production d'une dispersion aqueuse d'élastomère contenant du fluor, élastomère contenant du fluor et composition
JP6134293B2 (ja) 封止材
JPH07173204A (ja) 含フッ素エラストマーの製造方法
JPH06136008A (ja) 含フッ素ポリマーの製造方法
JP2013014785A (ja) パーオキサイド架橋可能なフッ素ゴム
WO2025075006A1 (fr) Composition de caoutchouc, procédé de production de composition de caoutchouc et article en caoutchouc réticulé
JP2023025678A (ja) 低粘度含フッ素エラストマーの製造方法

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 11844320

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 2012546896

Country of ref document: JP

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase