WO2010032715A1 - Tampon à polir - Google Patents

Tampon à polir Download PDF

Info

Publication number
WO2010032715A1
WO2010032715A1 PCT/JP2009/066046 JP2009066046W WO2010032715A1 WO 2010032715 A1 WO2010032715 A1 WO 2010032715A1 JP 2009066046 W JP2009066046 W JP 2009066046W WO 2010032715 A1 WO2010032715 A1 WO 2010032715A1
Authority
WO
WIPO (PCT)
Prior art keywords
polishing
depth
layer
groove
polishing pad
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/JP2009/066046
Other languages
English (en)
Japanese (ja)
Inventor
加藤　充
菊池　博文
知大 岡本
晋哉 加藤
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Kuraray Co Ltd
Original Assignee
Kuraray Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Kuraray Co Ltd filed Critical Kuraray Co Ltd
Publication of WO2010032715A1 publication Critical patent/WO2010032715A1/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

L'invention porte sur un tampon à polir comprenant au moins une couche de polissage. Le tampon à polir est caractérisé en ce que le tampon à polir possède des stries ouvertes vers la surface du côté de polissage de la couche de polissage et des trous ouverts vers la surface du côté de polissage de la couche de polissage, la surface de l'ouverture des trous n'étant pas inférieure à 0,05 mm2, et la profondeur des stries, la profondeur des trous et l'épaisseur de la couche de polissage satisfaisant à la formule (1) : (1) Z > X > Y dans laquelle X représente la profondeur des stries ; Y représente la profondeur des trous ; et Z représente l'épaisseur de la couche de polissage. Le tampon à polir est particulièrement utile, par exemple, pour le polissage chimico-mécanique, par exemple d'un film isolant tel qu'un film d'oxyde ou un film métallique formé sur une tranche de semi-conducteurs, il peut réaliser une vitesse de polissage élevée, une uniformité de polissage élevée et des propriétés d'aplatissement ; il est moins probable qu'il provoque un éraflement, et il ne provoque aucun changement significatif sur le plan des propriétés de polissage même lorsque le polissage est poursuivi pendant une longue période de temps.
PCT/JP2009/066046 2008-09-17 2009-09-14 Tampon à polir Ceased WO2010032715A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2008238476 2008-09-17
JP2008-238476 2008-09-17

Publications (1)

Publication Number Publication Date
WO2010032715A1 true WO2010032715A1 (fr) 2010-03-25

Family

ID=42039539

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2009/066046 Ceased WO2010032715A1 (fr) 2008-09-17 2009-09-14 Tampon à polir

Country Status (2)

Country Link
TW (1) TW201021972A (fr)
WO (1) WO2010032715A1 (fr)

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US10071461B2 (en) 2014-04-03 2018-09-11 3M Innovative Properties Company Polishing pads and systems and methods of making and using the same
TWI829909B (zh) * 2019-04-03 2024-01-21 日商可樂麗股份有限公司 研磨墊

Families Citing this family (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP5620465B2 (ja) * 2012-12-28 2014-11-05 東洋ゴム工業株式会社 円形状研磨パッド
JP6822840B2 (ja) * 2014-09-26 2021-01-27 バンドー化学株式会社 研磨パッド及び研磨パッドの製造方法

Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2001138212A (ja) * 1999-11-15 2001-05-22 Toshiro Doi 精密研磨装置
JP2003289056A (ja) * 2002-03-28 2003-10-10 Toray Ind Inc 研磨パッド、研磨装置および半導体デバイスの製造方法
JP2004167605A (ja) * 2002-11-15 2004-06-17 Rodel Nitta Co 研磨パッドおよび研磨装置

Patent Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2001138212A (ja) * 1999-11-15 2001-05-22 Toshiro Doi 精密研磨装置
JP2003289056A (ja) * 2002-03-28 2003-10-10 Toray Ind Inc 研磨パッド、研磨装置および半導体デバイスの製造方法
JP2004167605A (ja) * 2002-11-15 2004-06-17 Rodel Nitta Co 研磨パッドおよび研磨装置

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US10071461B2 (en) 2014-04-03 2018-09-11 3M Innovative Properties Company Polishing pads and systems and methods of making and using the same
US10252396B2 (en) 2014-04-03 2019-04-09 3M Innovative Properties Company Polishing pads and systems and methods of making and using the same
TWI829909B (zh) * 2019-04-03 2024-01-21 日商可樂麗股份有限公司 研磨墊

Also Published As

Publication number Publication date
TW201021972A (en) 2010-06-16

Similar Documents

Publication Publication Date Title
JP5706178B2 (ja) 研磨パッド
JP5143528B2 (ja) 研磨パッド
KR101084808B1 (ko) 금속 막 연마용 패드 및 그것을 이용하는 금속 막의 연마 방법
KR102398128B1 (ko) 연마층용 성형체 및 연마 패드
US10625391B2 (en) Non-porous molded article for polishing layer, polishing pad, and polishing method
JP2010045306A (ja) 研磨パッド
WO2018021428A1 (fr) Tampon de polissage et procédé de polissage l'utilisant
JP5997973B2 (ja) 金属膜研磨用パッドおよびそれを用いた研磨方法
JP4994894B2 (ja) 樹脂発泡体およびそれからなる研磨パッド
JP2008235508A (ja) 研磨パッド、それを用いた研磨方法および半導体デバイスの製造方法
JP5318756B2 (ja) 研磨パッドの製造方法
JP7514234B2 (ja) 研磨パッド、研磨パッドの製造方法及び研磨方法
EP4382250A1 (fr) Tampon à polir
WO2010032715A1 (fr) Tampon à polir
JP6184856B2 (ja) 研磨パッドの製造方法および該研磨パッドを用いる研磨方法
US20240383097A1 (en) Polishing pad
JP7431807B2 (ja) 研磨パッド
US20250153304A1 (en) Polishing layer, polishing pad, method for manufacturing polishing pad, and polishing method
US20240375239A1 (en) Polishing pad
WO2024257742A1 (fr) Tampon de polissage, procédé de polissage et procédé de fabrication de semi-conducteur

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 09814560

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

NENP Non-entry into the national phase

Ref country code: JP

122 Ep: pct application non-entry in european phase

Ref document number: 09814560

Country of ref document: EP

Kind code of ref document: A1