WO2007138696A1 - 発光素子実装用基板、発光素子パッケージ体、表示装置及び照明装置 - Google Patents

発光素子実装用基板、発光素子パッケージ体、表示装置及び照明装置 Download PDF

Info

Publication number
WO2007138696A1
WO2007138696A1 PCT/JP2006/310899 JP2006310899W WO2007138696A1 WO 2007138696 A1 WO2007138696 A1 WO 2007138696A1 JP 2006310899 W JP2006310899 W JP 2006310899W WO 2007138696 A1 WO2007138696 A1 WO 2007138696A1
Authority
WO
WIPO (PCT)
Prior art keywords
light
emitting element
light emitting
emitting device
phosphor
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/JP2006/310899
Other languages
English (en)
French (fr)
Inventor
Masakazu Ohashi
Ken-Ichi Uruga
Masanori Ito
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Fujikura Ltd
Original Assignee
Fujikura Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Fujikura Ltd filed Critical Fujikura Ltd
Priority to KR1020087029613A priority Critical patent/KR101026167B1/ko
Priority to PCT/JP2006/310899 priority patent/WO2007138696A1/ja
Priority to CN2006800547163A priority patent/CN101449392B/zh
Priority to EP06747053A priority patent/EP2028697A4/en
Priority to US12/303,022 priority patent/US7977696B2/en
Publication of WO2007138696A1 publication Critical patent/WO2007138696A1/ja
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

　白色ＬＥＤを製造する際に色度のばらつきが少なく、容易に高品質の発光素子パッケージ体を製造可能な発光素子実装用基板、前記基板を用いた発光素子パッケージ体、前記パッケージ体を用いた表示装置及び照明装置を提供する。前記発光素子実装用基板はコア金属の表面の少なくとも発光素子実装部分が蛍光体含有ガラスからなる蛍光ホーロー層により被覆されている。前記発光素子パッケージ体は前記発光素子実装用基板に発光素子が実装され、前記発光素子が透明な封止樹脂により封止されている。

Description

発光素子実装用基板、発光素子パッケージ体、表示装置及び照明装置 技術分野
[0001] 本発明は、発光ダイオード (以下、 LEDと記す。）などの発光素子を実装するため の発光素子実装基板、前記基板に発光素子を実装してパッケージした発光素子パ ッケージ体、この発光素子パッケージ体を用いた表示装置及び照明装置に関する。 背景技術
[0002] 発光素子は外力からの保護、発した光の指向角の制御、発光素子への電力の供 給などの観点から、パッケージ化されるのが一般的である (例えば、特許文献 1参照） 図 4は、従来の発光素子パッケージ構造の一例を示す図であり、このパッケージ構 造は、実装した発光素子 1から出射した光を前方に効率よく放射させるための傾斜面 を持つ反射凹部と発光素子通電用の一対の電極 4とを有するパッケージ 5と、このパ ッケージ 5内に実装された LEDなどの発光素子 1と、前記一方の電極 4上に固定され た前記発光素子 1と他方の電極 4とを電気的に接続している金属細線 2と、発光素子 1を外気力も封止するためにパッケージ 5の反射凹部に充填された透明な封止榭脂 3とから構成されている。
[0003] また、白色 LEDの場合は、 InGaNのような窒化物系化合物半導体である青色発光 素子にイットリウム 'アルミニウム 'ガーネット蛍光体のような青色光励起の黄色発光蛍 光体を組み合わせて実装するのが一般的にとられる方法であり、図 4に示した構造の 場合、封止榭脂 3に前記蛍光体を分散させて実装するのが一般的である。
[0004] 一方、 LED等の発光素子の発光強度を高めるために、ノ ッケージの放熱性を高め ることが有効である。発光素子は単位消費電力あたりの発光効率が現状の技術では まだ低ぐ発光に寄与しない電力は熱に変換されて発光素子自体が発熱する。発光 素子は半導体の一種であり、温度上昇に従い発光の効率は低下する。したがって、 その発光素子を実装する基板などのパッケージの放熱性を向上させておくことにより 、さらに大きな電流を発光素子に印加することが可能となり、その結果、発光素子 1個 当たりの発光強度を高くすることができる。放熱性の高い基板としては、窒化アルミ- ゥム基板、コアに金属を用いたメタル基板などが挙げられる。
特許文献 1：特開昭 62— 224986号公報
特許文献 2：特許第 3511987号公報
発明の開示
発明が解決しょうとする課題
[0005] 青色発光素子に青色励起の黄色発光蛍光体を組み合わせる方式の白色 LEDに おいて、前述したように封止榭脂に蛍光体を添加する従来の構造の場合、実装する 蛍光体の添加量が一定でない場合、あるいは榭脂に対する添加量が一定であって も、蛍光体を含む樹脂の実装する量がばらつくことにより、発光素子から発する青色 光と、蛍光体が発する黄色光のバランスが崩れ、その結果、色度が不安定となる。さ らに蛍光体が榭脂中で沈降し、やはり発光色のばらつきが発生することがある。この ように色度がばらつくことにより、大量生産時においては目標仕様力 外れたものは 不良とするか、あるいは色度毎に分別して販売するなどの対策が必要となり、製造ェ 程の増加を招く問題があり、さらに所望の色度範囲の白色 LEDを大量に生産するこ とが困難となる問題がある。
[0006] 一方で、榭脂への蛍光体の混ぜ方を工夫する方法も提案されて!ヽる（例えば、特 許文献 2参照。 ) 0この特許文献 2では、色度のばらつきを抑えるために、ロールミル 等の装置により十分に榭脂に蛍光体を混ぜ、このことにより榭脂中の蛍光体の分散 状体が安定となり、結果として色度のばらつきは大きく低減されると記載されている。 この方法で色度のばらつきの低減は図れるものと言える力 しかし、この従来方式で は混練に要する時間が長ぐ製造時間が延長されるため、製品の製造としては加工 費の増大、また蛍光体を混ぜた榭脂を混練するための装置を購入する必要がある。
[0007] 本発明は前記事情に鑑みてなされ、白色 LEDを製造する際に色度のばらつきが 少なぐ容易に高品質の発光素子パッケージ体を製造可能な発光素子実装用基板 、前記基板に発光素子を実装してパッケージした発光素子パッケージ体、この発光 素子パッケージ体を用いた表示装置及び照明装置の提供を目的とする。 課題を解決するための手段 [0008] 前記目的を達成するため、本発明は、コア金属の表面の少なくとも発光素子実装 部分が蛍光体含有ガラスからなる蛍光ホーロー層により被覆された発光素子実装用 基板を提供する。
[0009] 本発明の発光素子実装用基板において、実装した発光素子から発する光を反射 する傾斜面を持った反射凹部が設けられて 、ることが好ま U、。
[0010] 本発明の発光素子実装用基板において、発光素子実装位置に延びる発光素子通 電用の電極が前記蛍光ホーロー層上に設けられて 、ることが好まし 、。
[0011] 本発明の発光素子実装用基板において、前記蛍光ホーロー層が、青色励起の黄 色発光蛍光体を含むものであることが好ま 、。
[0012] 本発明の発光素子実装用基板において、前記蛍光ホーロー層が、セリウム賦活し たイットリウム ·アルミニウム ·ガーネット蛍光体 15質量％〜65質量％を含有してなる ことが好ましい。
[0013] また本発明は、前述した本発明に係る発光素子実装用基板に発光素子が実装され 、前記発光素子が透明な封止榭脂により封止されている発光素子パッケージ体を提 供する。
[0014] 本発明の発光素子パッケージ体において、発光素子が青色発光ダイオードであり 、前記蛍光ホーロー層が青色励起の黄色発光蛍光体を含有し、白色光を発すること が好ましい。
[0015] 本発明の発光素子パッケージ体において、前記発光素子実装用基板に多数の発 光素子が実装されてなることが好まし 、。
発明の効果
[0016] 本発明に係る発光素子実装用基板は、コア金属の表面の少なくとも発光素子実装 部分が蛍光体含有ガラスカゝらなる蛍光ホーロー層により被覆されたものなので、この 発光素子実装用基板に LEDなどの発光素子を実装して発光させることで、発光素 子力 発した光の一部は直接外部に照射され、残りの光は蛍光ホーロー基板に当た り、その蛍光が外部に照射されることで、発光素子から発した光と前記蛍光とが混ざり 合った光が得られる発光素子パッケージ体を簡単に構成することができる。特に、青 色 LEDと青色励起の黄色発光蛍光体を組み合わせることで白色 LEDパッケージ体 を作製する場合に好適である。
この白色 LEDパッケージ体の作製において、従来は封止榭脂に蛍光体を混ぜて 実装していたため実装ばらつきなどにより作製されたパッケージ体に色度ばらつきが 発生し易いが、本発明では、基板表面に蛍光体を含有した蛍光ホーロー層を設けた 構成としたので、蛍光体の分散が一つの蛍光体のバッチ間でばらつくことは少なぐ 従来に比較して、色度のばらつきを大幅に低減できる。
また、基板に用いるコア金属はセラミックスなどと比較して、機械加工が容易であり、 複数の発光素子を実装できるような基板構造のものも容易に作製できる。
また、発光素子を実装する反射凹部を設けることで、発光素子を実装する基板の構 造として、反射カップを構成する基材を基板に重ねて作製する必要がないので、基 板構造は単純であり、組立に係わるコストを抑制できるとともに、封止榭脂への基板と 反射カップを構成する基材との隙間から発生する気泡の混入を防ぐことができる。 図面の簡単な説明
[0017] [図 1]本発明に係る発光素子実装用基板と発光素子パッケージ体の一実施形態を示 す断面図である。
[図 2]本発明に係る発光素子実装用基板と発光素子パッケージ体の別な実施形態を 示す断面図である。
[図 3]実施例 5で作製した白色 LEDパッケージ体の波長スペクトルを示すグラフであ る。
[図 4]従来の発光素子パッケージ構造の一例を示す断面図である。
符号の説明
[0018] 10, 20…発光素子パッケージ体、 11, 21· ··発光素子実装用基板、 12, 22· ··コア 金属、 13, 23· ··蛍光ホーロー層、 14, 24· ··電極、 15, 25· ··発光素子、 16, 26· ··金 属細線、 17, 27…反射凹部、 18, 28…封止榭脂。
発明を実施するための最良の形態
[0019] 図 1は、本発明の発光素子実装用基板及びそれを用いた発光素子パッケージ体の 一実施形態を示す断面図であり、図 1中、符号 10は発光素子パッケージ体、 11は発 光素子実装用基板、 12はコア金属、 13は蛍光ホーロー層、 14は電極、 15は発光素 子、 16は金属細線、 17は反射凹部、 18は反射凹部 17に充填された透明な封止榭 脂である。
[0020] 本実施形態の発光素子実装用基板 11は、反射凹部 17となる傾斜した壁面を持つ 擂り鉢状の凹部を有するコア金属 12と、前記コア金属 12の表面を覆う蛍光ホーロー 層 13と、前記蛍光ホーロー層 13上に設けられた発光素子実装位置に延びる発光素 子通電用の電極 14とから構成されている。また、本実施形態の発光素子パッケージ 体 10は、前記発光素子実装用基板 11に発光素子 15が実装され、前記発光素子 15 が透明な封止榭脂 18により封止された構成になっている。
[0021] コア金属 12を覆う蛍光ホーロー層 13は、発光素子 15から発する光を受けて反射 する際に、含有する蛍光体が励起されて波長変換された蛍光を発する機能を有して いる。この蛍光ホーロー層 13を構成している蛍光体含有ガラスは、微細な蛍光体粉 末をガラス質 (ホーロー）によってコア金属 12表面に繋ぎ止めた構造になっており、 蛍光体粉末は、ガラス質に少なくとも一部が固溶するものでも、あるいはガラス質に固 溶せずガラス質に包囲された状態で存在しても良い。
[0022] この蛍光ホーロー層 13に含有せしめる蛍光体は、この発光素子パッケージ体 10に 求められる発光色に応じて、従来公知の各種蛍光体の中から選択して 1種又は 2種 以上を混合して用いることができる。本発明の好適な実施形態において、白色 LED ノ ッケージ体を構成する場合には、発光素子 15として青色 LEDを用い、蛍光体とし て青色励起の黄色発光蛍光体が用いられる。この黄色発光蛍光体としては、例えば 、セリウム賦活したイットリウム 'アルミニウム 'ガーネット蛍光体 (以下、 YAG : Ceと記 す。 )が挙げられる。
[0023] 本発明の好ましい実施形態において、蛍光体として前記 YAG : Ceを用いる場合に は、蛍光ホーロー層 13の原料（固体原料)全量に対して、前記 YAG : Ceを 15質量 %〜65質量％、好ましくは 25質量％〜60質量％、より好ましくは 35質量％〜60質 量％、最も好ましくは 45質量％〜60質量％を配合する。 ¥八0 :じ6が15質量％未満 であると、青色 LEDの色度を変えることが困難になる。 YAG : Ceが 65質量％を超え ると、蛍光ホーロー層 13が脆くなつて焼成後に割れ等を生じる恐れがある。
[0024] コア金属 12の材質は、特に限定されないが、蛍光ホーロー層 13を強固に焼結でき 、安価であり、かつ加工が容易な金属材料が好ましぐ例えば、低炭素鋼、ステンレス 鋼などが挙げられる。また、蛍光ホーロー層 13を構成している蛍光体含有ガラスの密 着性を向上させるため、金属表面を酸化処理してもよい。コア金属 12の形状も特に 限定されず、例えば円板状、角板状などの種々の形状の金属板や凹凸を有する形 状とすることができる。コア金属 12に反射凹部 17となる凹部を形成する方法も限定さ れず、ドリルなどによる切削加工法、研磨材による研磨加工などを用いて形成するこ とがでさる。
[0025] コア金属 12の表面を蛍光ホーロー層 13で覆ったホーロー基板の作製方法の一例 を説明すると、まず、低炭素鋼板などのコア金属 12にドリルなどによる切削加工ゃプ レス加工などによって反射凹部 17となる傾斜面を持った擂り鉢状の凹部を作製する 。一方、適当な分散媒にガラス粉末と蛍光体粉末を混ぜて蛍光ホーロー層形成用の 分散液を作製する。次に、その分散液を前記コア金属 12の表面に塗布し、高温で焼 結して蛍光体含有ガラスからなる蛍光ホーロー層 13を作製する。コア金属 12に形成 した凹部にも蛍光ホーロー層 13が積層され、平滑で蛍光体が含有された傾斜面を 持った反射凹部 17が形成される。
[0026] ドリル加工など機械的に切削して傾斜面を持つ反射凹部 17を作製する場合、前述 したように表面の平滑度を保つことが難しいと言えるが、低炭素鋼のような金属は加 ェがし易いことと、さらに、表面の平滑度が確保できなくても蛍光ホーロー層 13を積 層させることにより、凹凸のある部分は凹凸が補正されて、焼結後に得られる蛍光ホ 一口一層 13表面の平滑度は一般に高い。従って、反射凹部 17の傾斜面の平滑度も 高くなり、光反射率の高い反射凹部 17が容易に得られる。
[0027] 本発明において用いる発光素子 15は特に限定されないが、 LED,レーザダイォー ド (LD)などの半導体発光素子、有機 EL素子などが好適に用いられる。前述した通 り白色 LEDパッケージ体を構成する本発明の好ましい実施形態においては、窒化物 系化合物半導体力 なる青色 LEDが用いられる。
[0028] 発光素子 15に電力を供給する電極 14及び金属細線 16は、例えば以下の（1)〜（ 3)の方法により形成できる。
(1)反射凹部 17内に、厚膜銀ペースト層で電気回路を作製し、ギャップを介して対 向した一方の電極 14に発光素子 15を実装し、他方の電極 14に金ワイヤなどの金属 細線 16をボンディングする。
(2)金属箔などで電極 14を用意し、これを蛍光ホーロー層 13上に接着し、発光素子 15を前記（1)と同様に実装すると共に、電気的に接続する。
(3)反射凹部 17外に用意した電極と、反射凹部 17内の蛍光ホーロー層 13上に実装 した発光素子 15とを金ワイヤなどの金属細線 16でボンディングして電気的に接続す る。
[0029] 本実施形態の発光素子パッケージ体 10において、反射凹部 17表面に蛍光ホー口 一層 13を形成している関係上、前記電極 14は寸法的に細くすることが望ましい。こ の電極 14を銀で形成した場合、青色 LEDなどの発光素子 15から発した光はこの電 極 14で強く反射されるものの、その電極 14は蛍光体を含有していないので、見かけ 上電極 14の部分は青色光のみ発光することになり、電極 14の横幅を広くした場合、 綺麗に混色された白色が得られない。従って、電極 14の横幅は、 0. 8mm以下、より 好ましくは 0. 5mm以下であることが望ましい。
[0030] 反射凹部 17内に発光素子 15を実装後、反射凹部 17に透明な封止榭脂 18を充填 し、発光素子 15を外気から封止する。この封止榭脂 18としては、例えば熱硬化型ェ ポキシ榭脂などが用いられる。
[0031] 本実施形態の発光素子実装用基板 11は、コア金属 12の表面の少なくとも発光素 子実装部分が蛍光体含有ガラスカゝらなる蛍光ホーロー層 13により被覆されたものな ので、この発光素子実装用基板 11に発光素子 15を実装して発光させることで、発光 素子 15から発した光の一部は直接外部に照射され、残りの光は蛍光ホーロー基板 1 3に当たり、その蛍光が外部に照射されることで、発光素子 15から発した光と前記蛍 光とが混ざり合った光が得られる発光素子パッケージ体 10を簡単に構成することが できる。特に、青色 LEDと青色励起の黄色発光蛍光体を組み合わせることで白色 L EDパッケージ体を作製する場合に好適である。
[0032] この白色 LEDパッケージ体の作製にぉ 、て、従来は封止榭脂に蛍光体を混ぜて 実装していたため実装ばらつきなどにより作製されたパッケージ体に色度ばらつきが 発生し易いが、本実施形態では、基板表面に蛍光体を含有した蛍光ホーロー層 13 を設けた構成としたので、蛍光体の分散が一つの蛍光体のバッチ間でばらつくことは 少なぐ従来に比較して、白色 LEDパッケージ体の色度ばらつきを大幅に低減でき る。
また、基板に用いるコア金属 12はセラミックスなどと比較して、機械加工が容易であ り、複数の発光素子 15を実装できるような基板構造のものも容易に作製できる。 また、発光素子 15を実装する反射凹部 17を設けることで、発光素子 15を実装する 基板の構造として、反射カップを構成する基材を基板に重ねて作製する必要がな ヽ ので、基板構造は単純であり、組立に係わるコストを抑制できるとともに、封止榭脂へ の気泡の混入を防ぐことができる。
[0033] なお、前記の構造にぉ 、て、発光面側に榭脂などにより光学的なレンズ体を成型し 、指向角の制御などを行っても良い。また、前記（3)の構造の場合、金属細線 16をモ 一ルドするように榭脂を配置すると、信頼性の観点からも望ま 、構造と言える。
[0034] 図 2は、本発明に係る発光素子実装用基板及びそれを用いた発光素子パッケージ 体の別な実施形態を示す断面図であり、図 2中、符号 20は発光素子パッケージ体、 21は発光素子実装用基板、 22はコア金属、 23は蛍光ホーロー層、 24は電極、 25 は発光素子、 26は金属細線、 27は反射凹部、 28は透明な封止榭脂である。
[0035] 本実施形態では、 1つの基板上に複数の発光素子 25を実装可能とした発光素子 実装用基板 21及びその発光素子実装用基板 21に複数の発光素子 25を実装し、そ れぞれ封止榭脂 28によって封止してなる発光素子パッケージ体 20を例示している。 本実施形態において、コア金属 22、蛍光ホーロー層 23、電極 24、発光素子 25、金 属細線 26、反射凹部 27及び封止榭脂 28の各構成要素は、形状や発光素子実装 個数は異なる力 前述した図 1に示すコア金属 12、蛍光ホーロー層 13、電極 14、発 光素子 15、金属細線 16、反射凹部 17及び封止榭脂 18と同様のものを用いることが できる。
実施例
[0036] コア金属として、長さ 5mm、幅 5mm、厚さ lmmの低炭素鋼板を用いた。擂り鉢状 の反射凹部が形成されるよう、ドリルにより凹部を形成した。凹部底面の寸法は反射 凹部底面で直径 lmm、深さは 0. 5mm, 45° の角度の傾斜が形成されている。 [0037] 蛍光ホーロー層の原料として、ガラス粉末と、セリウムを賦活したイットリウム.アルミ -ゥム 'ガーネット蛍光体を用いた。この二つの粉末を十分に混ぜ、 2—プロパノール と水からなる分散媒に分散させた。これを前記コア金属の表面に塗布した。その後、 大気中 850°Cで焼成し、蛍光体含有ガラス力もなる蛍光ホーロー層を形成した。蛍 光ホーロー層の厚みは、 100 mとなることを目標として試料を作製した。電極は銅 ペーストを所定の電極パターンに塗布して焼成することにより作製した。その寸法は 厚み 0. 1mm、横幅 0. 5mmとなるように作製した。
[0038] LEDの実装について次に示す。蛍光ホーロー層原料中の蛍光体の量を変量して 表 1に示す実施例 1〜6及び比較例 1の発光素子実装用基板を作製し、それぞれの 発光素子実装用基板に発光素子として青色 LEDを実装して白色 LEDパッケージ体 を作製した。
最初に、窒化物系化合物半導体からなる青色 LEDを一方の電極上に実装した。 青色 LEDは発光波長がピーク波長で 450nmのものを選択して使用した。さらにワイ ャボンディング装置を用いて青色 LEDと他方の電極とをボンディングした。さらに透 光性のエポキシ榭脂を発光素子が実装された反射凹部内に充填し、加熱硬化して サンプルを作製し、評価した。
[0039] 表 1に、実施例 1〜6及び比較例 1の各白色 LEDパッケージ体の色度、基板外観 及び熱伝導率の測定結果を示す。測定は試料数 10個の平均値で示した (表 1)。ま た、表 2に実施例 1〜6の各白色 LEDパッケージ体における色度のばらつきについ て、その実験値を示す。
表 1中、ガラス粉末添加量と蛍光体粉末添加量を表す数値は質量％である。また、 色度、基板外観及び熱伝導率は次のように測定した。
[0040] <色度 >
作製した白色 LEDパッケージ体の色度を色度計 (横河電機社製、マルチメディア ディスプレイテスタ 3298F)を用いて測定した。
[0041] く基板外観 >
実施例 1〜6及び比較例 1のそれぞれの発光素子実装用基板を目視確認し、割 れなどの異常の有無を調べた。外観に異常のない試料は良好とし、目視で確認でき る割れのあるものを一部割れ、として評価した。
[0042] <熱伝導率 >
実施例 1〜6及び比較例 1のそれぞれの発光素子実装用基板のガラスの組成でそ れぞれガラスのシートを作製してレーザーフラッシュ法で測定した（単位： W/mK)。 測定はメルバック理工社製のレーザーフラッシュ法熱定数測定装置 (TC— 7000)を 用い、ホーローガラス材料のサイズが φ 10 X 1mm厚のものを作製して真空中で測 定した。試験方法 ίお IS R1611— 1991に準拠して行っている。
[0043] [表 1]
Figure imgf000012_0001
[0044] [表 2]
Figure imgf000013_0001
[0045] 以上の試験結果から、 15質量％以上の蛍光体粉末を添加して蛍光ホーロー層を 形成すると、 LEDの色度が変わることがわかる。また実施例 4〜6の範囲のものは、 C IE (Comission Internationale de l 'Eclairage)で規定された昼白色の発光色 を示していることがわかる。また、蛍光体の添加は、基板の放熱性には影響をほとん ど与えな ヽことが確認された。
産業上の利用可能性
[0046] 本発明によれば、白色 LEDを製造する際に色度のばらつきが少なぐ容易に高品 質の発光素子パッケージ体を製造可能な発光素子実装用基板、前記基板に発光素 子を実装してパッケージした発光素子パッケージ体、この発光素子パッケージ体を用 いた表示装置及び照明装置を提供することができる。

Claims

請求の範囲
[1] コア金属の表面の少なくとも発光素子実装部分が蛍光体含有ガラスからなる蛍光 ホーロー層により被覆された発光素子実装用基板。
[2] 実装した発光素子から発する光を反射する傾斜面を持った反射凹部が設けられて
V、る請求項 1に記載の発光素子実装用基板。
[3] 発光素子実装位置に延びる発光素子通電用の電極が前記蛍光ホーロー層上に設 けられた請求項 1又は 2に記載の発光素子実装用基板。
[4] 前記蛍光ホーロー層が、青色励起の黄色発光蛍光体を含む請求項 1〜3のいずれ かに記載の発光素子実装用基板。
[5] 前記蛍光ホーロー層が、セリウム賦活したイットリウム 'アルミニウム 'ガーネット蛍光 体 15質量％〜65質量％を含有してなる請求項 1〜4のいずれかに記載の発光素子 実装用基板。
[6] 請求項 1〜5のいずれかに記載の発光素子実装用基板に発光素子が実装され、前 記発光素子が透明な封止榭脂により封止されている発光素子パッケージ体。
[7] 発光素子が青色発光ダイオードであり、前記蛍光体含有ガラスが青色励起の黄色 発光蛍光体を含有し、白色光を発する請求項 6に記載の発光素子パッケージ体。
[8] 前記発光素子実装用基板に多数の発光素子が実装されてなる請求項 6又は 7に 記載の発光素子パッケージ体。
[9] 請求項 6〜8の！、ずれかに記載の発光素子パッケージ体を有する表示装置。
[10] 請求項 6〜8のいずれかに記載の発光素子パッケージ体を有する照明装置。
PCT/JP2006/310899 2006-05-31 2006-05-31 発光素子実装用基板、発光素子パッケージ体、表示装置及び照明装置 Ceased WO2007138696A1 (ja)