WO2007049591A1 - ふっ素樹脂成形体 - Google Patents

ふっ素樹脂成形体 Download PDF

Info

Publication number
WO2007049591A1
WO2007049591A1 PCT/JP2006/321123 JP2006321123W WO2007049591A1 WO 2007049591 A1 WO2007049591 A1 WO 2007049591A1 JP 2006321123 W JP2006321123 W JP 2006321123W WO 2007049591 A1 WO2007049591 A1 WO 2007049591A1
Authority
WO
WIPO (PCT)
Prior art keywords
carbon fiber
fiber structure
carbon
granular
diameter
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/JP2006/321123
Other languages
English (en)
French (fr)
Inventor
Koichi Handa
Subiantoro
Takayuki Tsukada
Tsuyoshi Okubo
Jiayi Shan
Akira Yamauchi
Manabu Nagashima
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Mitsui and Co Ltd
Original Assignee
Mitsui and Co Ltd
Bussan Nanotech Research Institute Inc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Mitsui and Co Ltd, Bussan Nanotech Research Institute Inc filed Critical Mitsui and Co Ltd
Priority to EP06822103A priority Critical patent/EP1950229A4/en
Publication of WO2007049591A1 publication Critical patent/WO2007049591A1/ja
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

　ふっ素樹脂粉末及び炭素繊維構造体を含む混合粉体を成形焼成してなるふっ素樹脂成形体であって、前記炭素繊維構造体を、外径１５～１００ｎｍの炭素繊維から構成される３次元ネットワーク状を呈しており、前記炭素繊維が複数延出する態様で、当該炭素繊維を互いに結合する粒状部を有しており、かつ当該粒状部は前記炭素繊維の成長過程において形成されてなるものとする。フッ素樹脂成形体に導電性を付与するための物質に着目し、新規なふっ素樹脂成形体を提供するものである。

Description

明 細 書
ふつ素樹脂成形体
技術分野
[0001] 本発明は、ふつ素榭脂粉末と炭素繊維構造体とを含む混合粉末を成形焼成してな るふつ素榭脂成形体に関する。さらに具体的には、柔軟で強度が高ぐ強靭な特殊 構造を有する微細炭素繊維構造体が配合されてなるふつ素榭脂成形体に関する。 背景技術
[0002] ポリテトラフルォロエチレン (PTFE)などのふつ素榭脂は、耐熱性、耐薬品性などに 優れており、半導体製造装置用のチューブや薬液槽などに使用されている。しかし、 ふつ素榭脂は電気絶縁性であり、容易に帯電するので静電気を嫌う用途にはそのま ま使用することが出来ない。また、帯電により雰囲気中のゴミを吸着するという問題も ある。
[0003] ふつ素榭脂の帯電を防止する方法としては、導電性の高!、フイラ一等を添加するこ とにより導電性を付与する方法が知られている。例えば、特許文献 1には、カーボン ブラックとふつ素榭脂粉末とを含む混合粉体を溶融混合して成形し、ふつ素榭脂中 にカーボンブラックが分散されたふつ素榭脂成形体などが提案されている。
特許文献 1 :特開 2003— 82187号公報
発明の開示
発明が解決しょうとする課題
[0004] し力しながら、カーボンブラックを導電性フイラ一として用いた場合、所望する導電 性を得るためには相当量のカーボンブラックを配合する必要が生じ、配合量を多くす るほど、当該カーボンブラックがふつ素榭脂成形体力 脱離する危険性が高まり、外 部を汚染することが危惧される。
[0005] 近年においては、カーボンブラックに代えて炭素繊維を導電性フイラ一として使用 することち研究されている。
[0006] し力しながら、この場合であっても、所望の導電性を得ようとすると相当量の配合が 必要となるため、ふつ素榭脂本来の物性を低下させてしまうといった問題が生じ得る 。また、炭素繊維は、現在、最終フィラメントにおいて炭素原子の異方性シートの良好 な配向が確保されるように、注意深く維持した引張り力の下で前駆物質たる有機ポリ マー、特にセルロース又はポリアクリロニトリルの連続フィラメントを制御下に熱分解す ることによって製造されており、炭化における重量損失や炭化速度が遅いなどのため 、最終的に高価になってしまうといった問題もある。
[0007] ここ数年においては、炭素繊維に関する別のものとして、カーボンナノチューブ (以 下、「CNT」とも記する。）に代表されるカーボンナノ構造体などの微細炭素繊維が注 目されている。
[0008] カーボンナノ構造体を構成するグラフアイト層は、通常では規則正 、六員環配列 構造を有し、その特異な電気的性質とともに、化学的、機械的および熱的に安定した 性質を持つ物質である。従って、例えば、各種榭脂、セラミックス、金属等の固体材 料、あるいは燃料油、潤滑剤等の液体材料中に、このような微細炭素繊維を分散配 合することにより、前記したような物性を生かすことができれば、その添加剤としての 用途が期待されることとなり、これをふつ素榭脂中に配合せしめる導電性フイラ一とし て用いることも充分に考え得る。
[0009] し力しながら、一方で、このような微細炭素繊維は、生成時点で既に塊になってしま い、これをそのまま使用すると、ふつ素榭脂中において分散が進まず性能不良をきた すおそれがある。従って、ふつ素榭脂に導電性等の所定の特性を発揮させようとする 場合には、かなりの添力卩量を必要とするものであった。
[0010] 本発明はこのような状況においてなされたものであり、フッ素榭脂成形体に導電性 を付与するための物質に着目し、当該物質を従来と同量配合した場合には、従来に 比べ優れた導電性を有し、一方、当該導電性を付与する物質を従来よりも大幅に低 減した場合であっても、充分な導電性を確保することができ、かつ当該導電性を付与 する物質がふつ素榭脂から脱落することがない、新規なふつ素榭脂成形体を提供す ることを主たる課題とする。
課題を解決するための手段
[0011] 上記課題を解決するために、本発明者らは鋭意検討の結果、その添加量が少なく ても十分な導電性を発揮させるためには、可能な限り微細な炭素繊維を用い、さらに これら炭素繊維が一本一本ばらばらになることなく互いに強固に結合し、疎な構造体 でふつ素榭脂に保持されており、また炭素繊維自体の一本一本が極力欠陥の少な いものであることが有効であることを見出し、本発明に到達したものである。
[0012] すなわち、上記課題を解決するための本発明は、ふつ素榭脂粉末及び炭素繊維 構造体を含む混合粉体を成形焼成してなるふつ素榭脂成形体であって、前記炭素 繊維構造体力 外径 15〜： LOOnmの炭素繊維力も構成される 3次元ネットワーク状を 呈しており、前記炭素繊維が複数延出する態様で、当該炭素繊維を互いに結合する 粒状部を有しており、かつ当該粒状部は前記炭素繊維の成長過程にお 、て形成さ れてなるものであることを特徴する。
[0013] また、前記炭素繊維構造体は、面積基準の円相当平均径が 50〜： LOO /z mであるこ とが好ましい。
[0014] また、前記炭素繊維構造体は、嵩密度が、 0. 0001〜0. 05gZcm3であることが好 ましい。
[0015] また、前記炭素繊維構造体は、ラマン分光分析法で測定される I Λ 1S 0. 2
D G 以下 であることが好ましい。
[0016] また、前記炭素繊維構造体は、空気中での燃焼開始温度が 750°C以上であること が好ましい。
[0017] また、前記炭素繊維の結合箇所にお!、て、前記粒状部の粒径が、前記炭素繊維 の外径よりも大き 、ことが好ま 、。
[0018] また、前記炭素繊維構造体は、炭素源として、分解温度の異なる少なくとも 2っ以 上の炭素化合物を用いて、生成されたものであるが好まし 、。
[0019] また、前記炭素繊維構造体を 0. 01〜30. 0質量％の割合で含有することが好まし い。
[0020] さらに、前記ふつ素榭脂粉末は、粒径 100 IX m以上の大径粒体を全ふつ素榭脂粉 末の 5〜： LOO質量％、残部が粒子径 100 m未満の小径粒体で構成されていること が好ましい。
[0021] さらに、前記大径粒体が、粒子径 100〜1000 μ mであることが好ましい。
[0022] さらに、前記ふつ素榭脂粉末が、ポリテトラフルォロエチレン、パーフルォロアルコキ シビュルエーテルを共重合させて変性したポリテトラフルォロエチレン及びへキサフ ルォロプロピレンを共重合させて変性したポリテトラフルォロエチレン力もなる群から 選ばれたの少なくとも 1種力もなる粉末であることが好ましい。
発明の効果
[0023] 本発明のふつ素榭脂成形体は、これに導電性を付与する物質として、炭素繊維構 造体を用いており、かつ当該炭素繊維構造体が、上記したような 3次元ネットワーク 状に配された微細径の炭素繊維が、前記炭素繊維の成長過程にお!ヽて形成された 粒状部によって互いに強固に結合され、該粒状部力 前記炭素繊維が複数延出す る形状を有するものであるため、ふつ素榭中に配合した場合に、当該炭素繊維構造 体は、疎な構造を残したまま容易に分散し、少量の添加量においても、ふつ素榭脂 中に、微細な炭素繊維を均一な広がりをもって配置することができる。このため、ふつ 素榭脂全体に当該炭素繊維構造体による良好な導電性パスを形成することができ、 その結果、導電性を向上させることができる。また機械的特性、熱特性等に関しても 、ふつ素榭脂全体に微細炭素繊維力もなるフィラーが満遍なく配されることで、特性 向上を図ることができる。
[0024] さらにまた、本発明のふつ素榭脂成形体は、前述した炭素繊維構造体を配合する に際し、粒径 100 m以上の大径粒体を 5〜： LOO質量％含むふつ素榭脂粉末を用 いることにより、大径粒子同士の接合界面に前述の炭素繊維構造体が多く存在する ようになり、その結果、炭素繊維構造体同士の接触による導電性パスがより形成され 易くなり、従来に比べ導電性をより向上することができる。
図面の簡単な説明
[0025] [図 1]本発明のふつ素榭脂成形体に用いる炭素繊維構造体の中間体の SEM写真で ある。
[図 2]本発明のふつ素榭脂成形体に用いる炭素繊維構造体の中間体の TEM写真で ある。
[図 3]本発明のふつ素榭脂成形体に用いる炭素繊維構造体の SEM写真である。 圆 4A]、
[図 4B]は、それぞれ本発明のふつ素榭脂成形体に用いる炭素繊維構造体の TEM 写真である。
[図 5]本発明のふつ素榭脂成形体に用いる炭素繊維構造体の SEM写真である。
[図 6]本発明のふつ素榭脂成形体に用いる炭素繊維構造体および該炭素繊維構造 体の中間体の X線回折チャートである。
[図 7]本発明のふつ素榭脂成形体に用いる炭素繊維構造体および該炭素繊維構造 体の中間体のラマン分光分析チャートである。
[図 8]本発明の実施例において炭素繊維構造体の製造に用いた生成炉の概略構成 を示す図面である。
符号の説明
[0026] 1 生成炉
2 導入ノズル
3 衝突部
4 原料ガス供給口
a 導入ノズルの内径
b 生成炉の内径
c 衝突部の内径
d 生成炉の上端から原料混合ガス導入口までの距離
e 原料混合ガス導入ロカ 衝突部の下端までの距離
f 原料混合ガス導入口から生成炉の下端までの距離
発明を実施するための最良の形態
[0027] 以下、本発明を好ましい実施形態に基づき詳細に説明する。
本発明のふつ素榭脂成形体は、ふつ素榭脂粉末及び炭素繊維構造体を含む混合 粉体を成形焼成してなる。
[0028] (1)炭素繊維構造体
先ず、本発明のふつ素榭脂成形体を構成する炭素繊維構造体について詳細に説 明する。
本発明において用いられる炭素繊維構造体は、例えば、図 3に示す SEM写真また は図 4Aおよび図 4Bに示す TEM写真に見られるように、外径 15〜100nmの炭素繊 維力も構成される 3次元ネットワーク状の炭素繊維構造体であって、前記炭素繊維構 造体は、前記炭素繊維が複数延出する態様で、当該炭素繊維を互いに結合する粒 状部を有することを特徴とする炭素繊維構造体である。
[0029] 炭素繊維構造体を構成する炭素繊維の外径を、 15〜： LOOnmの範囲のものとする のは、外径が 15nm未満であると、後述するように炭素繊維の断面が多角形状となら ず、一方、炭素繊維の物性上直径が小さいほど単位量あたりの本数が増えるとともに 、炭素繊維の軸方向への長さも長くなり、高い導電性が得られるため、 lOOnmを越 える外径を有することは、ふつ素榭脂へ導電性を付与する物質として配合される炭素 繊維構造体として適当でないためである。なお、炭素繊維の外径としては特に、 20 〜70nmの範囲内にあること力 より望ましい。この外径範囲のもので、筒状のグラフ エンシートが軸直角方向に積層したもの、すなわち多層であるものは、曲がりにくぐ 弾性、すなわち変形後も元の形状に戻ろうとする性質が付与されるため、炭素繊維 構造体がー且圧縮された後においても、ふつ素榭脂に配合された後において、疎な 構造を採りやすくなる。
[0030] なお、 2400°C以上でァニール処理すると、積層したグラフエンシートの面間隔が狭 まり真密度が 1. 89g/cm3から 2. lg/cm3に増加するとともに、炭素繊維の軸直交 断面が多角形状となり、この構造の炭素繊維は、積層方向および炭素繊維を構成す る筒状のグラフエンシートの面方向の両方において緻密で欠陥の少ないものとなるた め、曲げ剛性 (EI)が向上する。
[0031] カロえて、該微細炭素繊維は、その外径が軸方向に沿って変化するものであることが 望ましい。このように炭素繊維の外径が軸方向に沿って一定でなぐ変化するもので あると、ふつ素榭脂中において当該炭素繊維に一種のアンカー効果が生じるものと 思われ、当該榭脂中における移動が生じにくく分散安定性が高まるものとなる。
[0032] そして本発明において用いられる炭素繊維構造体においては、このような所定外 径を有する微細炭素繊維が 3次元ネットワーク状に存在する力 これら炭素繊維は、 当該炭素繊維の成長過程にお 、て形成された粒状部にぉ 、て互いに結合され、該 粒状部から前記炭素繊維が複数延出する形状を呈して!/ヽるものである。このように、 微細炭素繊維同士が単に絡合しているものではなぐ粒状部において相互に強固に 結合されているものであることから、ふつ素榭脂中に配合した場合に当該構造体が炭 素繊維単体として分散されることなぐ嵩高な構造体のまま当該榭脂中に分散配合さ れることができる。また、この炭素繊維構造体においては、当該炭素繊維の成長過程 にお 、て形成された粒状部によって炭素繊維同士が互 、に結合されて 、ることから 、その構造体自体の電気的特性等も非常に優れたものであり、例えば、一定圧縮密 度において測定した電気抵抗値は、微細炭素繊維の単なる絡合体、あるいは微細 炭素繊維同士の接合点を当該炭素繊維合成後に炭素質物質ないしその炭化物に よって付着させてなる構造体等の値と比較して、非常に低い値を示し、フッ素榭脂中 に分散配合された場合に、良好な導電性パスを形成できることができる。
[0033] 当該粒状部は、上述するように炭素繊維の成長過程において形成されるものであ るため、当該粒状部における炭素間結合は十分に発達したものとなり、正確には明ら かではないが、 sp2結合および sp3結合の混合状態を含むと思われる。そして、生成 後 (後述する中間体および第一中間体)においては、粒状部と繊維部とが、炭素原 子力もなるパッチ状のシート片を貼り合せたような構造をもって連続しており、その後 の高温熱処理後においては、図 4Aおよび図 4Bに示されるように、粒状部を構成す るグラフェン層の少なくとも一部は、当該粒状部より延出する微細炭素繊維を構成す るグラフェン層に連続するものとなる。本発明に係る炭素繊維構造体において、粒状 部と微細炭素繊維との間は、上記したような粒状部を構成するグラフ ン層が微細炭 素繊維を構成するグラフ ン層と連続していることに象徴されるように、炭素結晶構造 的な結合によって (少なくともその一部カ 繋がっているものであって、これによつて粒 状部と微細炭素繊維との間の強固な結合が形成されているものである。
[0034] なお、本願明細書において、粒状部から炭素繊維力 ^延出する」するとは、粒状部 と炭素繊維とが他の結着剤 (炭素質のものを含む）によって、単に見かけ上で繋がつ ているような状態をさすものではなぐ上記したように炭素結晶構造的な結合によって 繋がって!/、る状態を主として意味するものである。
[0035] また、当該粒状部は、上述するように炭素繊維の成長過程において形成される力 その痕跡として粒状部の内部には、少なくとも 1つの触媒粒子、あるいはその触媒粒 子がその後の熱処理工程にぉ 、て揮発除去されて生じる空孔を有して 、る。この空 孔 (ないし触媒粒子）は、粒状部より延出している各微細炭素繊維の内部に形成され る中空部とは、本質的に独立したものである（なお、ごく一部に、偶発的に中空部と連 続してしまったものも観察される。；)。
[0036] この触媒粒子ないし空孔の数としては特に限定されるものではないが、粒状部 1つ 当りに 1〜： LOOO個程度、より望ましくは 3〜500個程度存在する。このような範囲の数 の触媒粒子の存在下で粒状部が形成されたことによって、後述するような所望の大き さの粒状部とすることができる。
[0037] また、この粒状部中に存在する触媒粒子ないし空孔の 1つ当りの大きさとしては、例 えば、 1〜： LOOnm、より好ましくは 2〜40nm、さらに好ましくは 3〜15nmである。
[0038] さらに、特に限定されるわけではないが、この粒状部の粒径は、図 2に示すように、 前記微細炭素繊維の外径よりも大きいことが望ましい。具体的には、例えば、前記微 細炭素繊維の外径の 1. 3〜250倍、より好ましくは 1. 5〜： LOO倍、さらに好ましくは 2 . 0〜25倍である。なお、前記値は平均値である。このように炭素繊維相互の結合点 である粒状部の粒径が微細炭素繊維外径の 1. 3倍以上と十分に大きなものであると 、当該粒状部より延出する炭素繊維に対して高い結合力がもたらされ、ふつ素榭脂 中に当該炭素繊維構造体を配した場合に、ある程度のせん弾力を加えた場合であ つても、 3次元ネットワーク構造を保持したままマトリックス中に分散させることができる 。一方、粒状部の大きさが微細炭素繊維の外径の 250倍を超える極端に大きなもの となると、炭素繊維構造体の繊維状の特性が損なわれる虞れがあり、例えば、フッ素 榭脂へ配合するに際し適当なものとならない虞れがあるために望ましくない。なお、 本明細書でいう「粒状部の粒径」とは、炭素繊維相互の結合点である粒状部を 1つの 粒子とみなして測定した値である。
[0039] その粒状部の具体的な粒径は、炭素繊維構造体の大きさ、炭素繊維構造体中の 微細炭素繊維の外径にも左右される力 例えば、平均値で 20〜5000nm、より好ま しくは 25〜2000nm、さらに好ましくは 30〜500nm程度である。
[0040] さらにこの粒状部は、前記したように炭素繊維の成長過程において形成されるもの であるため、比較的球状に近い形状を有しており、その円形度は、平均値で 0. 2〜 < 1、好ましく ίま 0. 5〜0. 99、より好ましく ίま 0. 7〜0. 98程度である。 [0041] カロえて、この粒状部は、前記したように炭素繊維の成長過程において形成されるも のであって、例えば、微細炭素繊維同士の接合点を当該炭素繊維合成後に炭素質 物質ないしその炭化物によって付着させてなる構造体等と比較して、当該粒状部に おける、炭素繊維同士の結合は非常に強固なものであり、炭素繊維構造体における 炭素繊維の破断が生じるような条件下においても、この粒状部 (結合部）は安定に保 持される。具体的には、例えば、後述する合成例において示すように、当該炭素繊維 構造体を液状媒体中に分散させ、これに一定出力で所定周波数の超音波をかけて 、炭素繊維の平均長がほぼ半減する程度の負荷条件としても、該粒状部の平均粒 径の変化率は、 10%未満、より好ましくは 5%未満であって、粒状部、すなわち、繊 維同士の結合部は、安定に保持されているものである。
[0042] また、本発明において用いられる炭素繊維構造体は、面積基準の円相当平均径が 50-100 μ m、より好ましくは 60〜90 μ m程度程度であることが望ましい。ここで面 積基準の円相当平均径とは、炭素繊維構造体の外形を電子顕微鏡などを用いて撮 影し、この撮影画像において、各炭素繊維構造体の輪郭を、適当な画像解析ソフト ウェア、例えば WinRoof (商品名、三谷商事株式会社製)を用いてなぞり、輪郭内の 面積を求め、各繊維構造体の円相当径を計算し、これを平均化したものである。
[0043] この円相当平均径は、ふつ素榭脂中に配合された場合における当該炭素繊維構 造体の最長の長さを決める要因となるものであり、概して、円相当平均径が 未 満であると、導電性が十分に発揮されないおそれがあり、一方、 100 /z mを越えるも のであると、例えば、ふつ素榭脂中に混練等によって配合する際に大きな粘度上昇 が起こり混合分散が困難あるいは成形性が劣化する虞れがあるためである。
[0044] また、本発明に用いられる炭素繊維構造体は、上記したように、 3次元ネットワーク 状に存在する炭素繊維が粒状部にお 、て互 ヽに結合され、該粒状部から前記炭素 繊維が複数延出する形状を呈しているが、 1つの炭素繊維構造体において、炭素繊 維を結合する粒状部が複数個存在して 3次元ネットワークを形成して 、る場合、隣接 する粒状部間の平均距離は、例えば、 0. 5 m〜300 μ m、より好ましくは 0. 5〜10 O ^ m,さらに好ましくは 1〜50 /ζ πι程度となる。なお、この隣接する粒状部間の距離 は、 1つの粒状体の中心部力 これに隣接する粒状部の中心部までの距離を測定し たものである。粒状体間の平均距離が、 0. 5 m未満であると、炭素繊維が 3次元ネ ットワーク状に十分に発展した形態とならないため、フッ素榭脂中に分散配合された 場合に、良好な導電パスを形成し得ないものとなる虞れがあり、一方、平均距離が 30 O /z mを越えるものであると、ふつ素榭脂中に分散配合させる際に、粘性を高くさせる 要因となり、炭素繊維構造体のふつ素榭脂に対する分散性が低下する虞れがあるた めである。
[0045] さらに、本発明において用いられる炭素繊維構造体は、上記したように、 3次元ネッ トワーク状に存在する炭素繊維が粒状部にお 、て互 ヽに結合され、該粒状部から前 記炭素繊維が複数延出する形状を呈しており、このため当該構造体は炭素繊維が 疎に存在した嵩高な構造を有するが、具体的には、例えば、その嵩密度が 0. 0001 〜0. 05g/cm3、より好ましくは 0. 001-0. 02g/cm3であることが望ましい。嵩密 度が 0. 05gZcm3を超えるものであると、少量添加によって、ふつ素榭脂に導電性を 付与することが難しくなるためである。
[0046] また、本発明に用いられる炭素繊維構造体は、 3次元ネットワーク状に存在する炭 素繊維がその成長過程にお 、て形成された粒状部にお 、て互 、に結合されて 、る ことから、上記したように構造体自体の電気的特性等も非常に優れたものであるが、 例えば、一定圧縮密度 0. 8g/cm3において測定した粉体抵抗値力 0. 02 Ω 'cm 以下、より望ましくは、 0. 001-0. 010 Ω 'cmであることが好ましい。粉体抵抗値が 0. 02 Ω 'cmを超えるものであると、ふつ素榭脂に配合された際に、良好な導電パス を形成することが難しくなるためである。
[0047] また、本発明にお 、て用いられる炭素繊維構造体は、高 、強度および導電性を有 することから、炭素繊維を構成するグラフエンシート中における欠陥が少な ヽことが望 ましぐ具体的には、例えば、ラマン分光分析法で測定される I
D Λ G比が、 0. 2以下、 より好ましくは 0. 1以下であることが望ましい。ここで、ラマン分光分析では、大きな単 結晶の黒鉛では 1580cm_1付近のピーク (Gバンド)しか現れない。結晶が有限の微 小サイズであることや格子欠陥により、 1360cm_1付近にピーク (Dバンド）が出現す る。このため、 Dバンドと Gバンドの強度比 (R=I /\ =I ZI )が上記したよう
1360 1580 D G
に所定値以下であると、グラフエンシート中における欠陥量が少ないことが認められる ためである。
[0048] また、本発明において用いられる前記炭素繊維構造体は、空気中での燃焼開始温 度が 750°C以上、より好ましくは 800〜900°Cであることが望ましい。前記したように 炭素繊維構造体が欠陥が少なぐかつ炭素繊維が所期の外径を有するものであるこ とから、このような高 、熱的安定性を有するものとなる。
[0049] 上記したような所期の形状を有する炭素繊維構造体は、特に限定されるものではな いが、例えば、次のようにして調製することができる。
[0050] 基本的には、遷移金属超微粒子を触媒として炭化水素等の有機化合物を CVD法 で化学熱分解して繊維構造体 (以下、中間体という）を得、これをさらに高温熱処理 する。
[0051] 原料有機化合物としては、ベンゼン、トルエン、キシレンなどの炭化水素、一酸化炭 素（CO)、エタノール等のアルコール類などが使用できる。特に限定されるわけでは ないが、本発明において用いられる炭素繊維構造体を得る上においては、炭素源と して、分解温度の異なる少なくとも 2つ以上の炭素化合物を用いることが好ましい。な お、本明細書において述べる「少なくとも 2つ以上の炭素化合物」とは、必ずしも原料 有機化合物として 2種以上のものを使用するというものではなぐ原料有機化合物とし ては 1種のものを使用した場合であっても、繊維構造体の合成反応過程において、 例えば、トルエンゃキシレンの水素脱アルキル化（hydrodealkylation)などのような反 応を生じて、その後の熱分解反応系にお 、ては分解温度の異なる 2つ以上の炭素 化合物となって 、るような態様も含むものである。
[0052] なお、熱分解反応系にお 、て炭素源としてこのように 2種以上の炭素化合物を存在 させた場合、それぞれの炭素化合物の分解温度は、炭素化合物の種類のみでなぐ 原料ガス中の各炭素化合物のガス分圧ないしモル比によっても変動するものである ため、原料ガス中における 2種以上の炭素化合物の組成比を調整することにより、炭 素化合物として比較的多くの組み合わせを用いることができる。
[0053] 例えば、メタン、ェタン、プロパン類、ブタン類、ペンタン類、へキサン類、ヘプタン 類、シクロプロパン、シクロへキサンなどといったアルカンないしシクロアルカン、特に 炭素数 1〜7程度のアルカン；エチレン、プロピレン、ブチレン類、ペンテン類、ヘプテ ン類、シクロペンテンなどといったアルケンないしシクロォレフイン、特に炭素数 1〜7 程度のアルケン;アセチレン、プロピン等のアルキン、特に炭素数 1〜7程度のアルキ ン；ベンゼン、トノレェン、スチレン、キシレン、ナフタレン、メチノレナフタレン、インデン、 フ ナントレン等の芳香族ないし複素芳香族炭化水素、特に炭素数 6〜18程度の芳 香族ないし複素芳香族炭化水素、メタノール、エタノール等のアルコール類、特に炭 素数 1〜7程度のアルコール類;その他、一酸化炭素、ケトン類、エーテル類等の中 力も選択した 2種以上の炭素化合物を、所期の熱分解反応温度域にぉ 、て異なる分 解温度を発揮できるようにガス分圧を調整し、組み合わせて用いること、および Zま たは、所定の温度領域における滞留時間を調整することで可能であり、その混合比 を最適化することで効率よく本発明に係る炭素繊維構造体を製造することができる。
[0054] このような 2種以上の炭素化合物の組み合わせのうち、例えば、メタンとベンゼンと の組み合わせにおいては、メタン/ベンゼンのモル比力 1〜600、より好ましくは 1. 1〜200、さらに好ましくは 3〜： LOOとすることが望ましい。なお、この値は、反応炉の 入り口におけるガス組成比であり、例えば、炭素源の 1つとしてトルエンを使用する場 合には、反応炉内でトルエンが 100%分解して、メタンおよびベンゼンが 1： 1で生じ ることを考慮して、不足分のメタンを別途供給するようにすれば良い。例えば、メタン Zベンゼンのモル比を 3とする場合には、トルエン 1モルに対し、メタン 2モルを添カロ すれば良い。なお、このようなトルエンに対して添加するメタンとしては、必ずしも新鮮 なメタンを別途用意する方法のみならず、当該反応炉より排出される排ガス中に含ま れる未反応のメタンを循環使用することにより用いることも可能である。
[0055] このような範囲内の組成比とすることで、炭素繊維部および粒状部のいずれもが十 分を発達した構造を有する炭素繊維構造体を得ることが可能となる。
[0056] なお、雰囲気ガスには、アルゴン、ヘリウム、キセノン等の不活性ガスや水素を用い ることがでさる。
[0057] また、触媒としては、鉄、コバルト、モリブデンなどの遷移金属あるいはフエ口セン、 酢酸金属塩などの遷移金属化合物と硫黄あるいはチォフェン、硫化鉄などの硫黄化 合物の混合物を使用する。
[0058] 中間体の合成は、通常行われている炭化水素等の CVD法を用い、原料となる炭 化水素および触媒の混合液を蒸発させ、水素ガス等をキャリアガスとして反応炉内に 導入し、 800〜1300°Cの温度で熱分解する。これにより、外径が 15〜： LOOnmの繊 維相互が、前記触媒の粒子を核として成長した粒状体によって結合した疎な三次元 構造を有する炭素繊維構造体（中間体)が複数集まった数 cm力 数十センチの大き さの集合体を合成する。
[0059] 原料となる炭化水素の熱分解反応は、主として触媒粒子な 、しこれを核として成長 した粒状体表面において生じ、分解によって生じた炭素の再結晶化が当該触媒粒 子ないし粒状体より一定方向に進むことで、繊維状に成長する。し力しながら、本発 明に係る炭素繊維構造体を得る上においては、このような熱分解速度と成長速度と のノ ランスを意図的に変化させる、例えば上記したように炭素源として分解温度の異 なる少なくとも 2つ以上の炭素化合物を用いることで、一次元的方向にのみ炭素物質 を成長させることなぐ粒状体を中心として三次元的に炭素物質を成長させる。もちろ ん、このような三次元的な炭素繊維の成長は、熱分解速度と成長速度とのバランスに のみ依存するものではなぐ触媒粒子の結晶面選択性、反応炉内における滞留時間 、炉内温度分布等によっても影響を受け、また、前記熱分解反応と成長速度とのバラ ンスは、上記したような炭素源の種類のみならず、反応温度およびガス温度等によつ ても影響を受けるが、概して、上記したような熱分解速度よりも成長速度の方が速いと 、炭素物質は繊維状に成長し、一方、成長速度よりも熱分解速度の方が速いと、炭 素物質は触媒粒子の周面方向に成長する。従って、熱分解速度と成長速度とのバラ ンスを意図的に変化させることで、上記したような炭素物質の成長方向を一定方向と することなぐ制御下に多方向として、本発明に用いられる炭素繊維構造体に係るよ うな三次元構造を形成することができるものである。なお、生成する中間体において、 繊維相互が粒状体により結合された前記したような三次元構造を容易に形成する上 では、触媒等の組成、反応炉内における滞留時間、反応温度、およびガス温度等を 最適化することが望ましい。
[0060] なお、本発明にお 、て用いられる炭素繊維構造体を効率良く製造する方法として は、上記したような分解温度の異なる 2つ以上の炭素化合物を最適な混合比にて用 いるアプローチ以外に、反応炉に供給される原料ガスに、その供給口近傍において 乱流を生じさせるアプローチを挙げることができる。ここでいう乱流とは、激しく乱れた 流れであり、渦巻いて流れるような流れをいう。
[0061] 反応炉においては、原料ガスが、その供給口より反応炉内へ導入された直後にお いて、原料混合ガス中の触媒としての遷移金属化合物の分解により金属触媒微粒子 が形成されるが、これは、次のような段階を経てもたらされる。すなわち、まず、遷移 金属化合物が分解され金属原子となり、次いで、複数個、例えば、約 100原子程度 の金属原子の衝突によりクラスター生成が起こる。この生成したクラスターの段階では 、微細炭素繊維の触媒として作用せず、生成したクラスター同士が衝突により更に集 合し、約 3ηπ！〜 lOnm程度の金属の結晶性粒子に成長して、微細炭素繊維の製造 用の金属触媒微粒子として利用されることとなる。
[0062] この触媒形成過程にお!、て、上記したように激 、乱流による渦流が存在すると、 ブラウン運動のみの金属原子又はクラスター同士の衝突と比してより激しい衝突が可 能となり、単位時間あたりの衝突回数の増加によって金属触媒微粒子が短時間に高 収率で得られ、又、渦流によって濃度、温度等が均一化されることにより粒子のサイ ズの揃った金属触媒微粒子を得ることができる。さらに、金属触媒微粒子が形成され る過程で、渦流による激しい衝突により金属の結晶性粒子が多数集合した金属触媒 微粒子の集合体を形成する。このようにして金属触媒微粒子が速やかに生成される ため、炭素化合物の分解が促進されて、十分な炭素物質が供給されることになり、前 記集合体の各々の金属触媒微粒子を核として放射状に微細炭素繊維が成長し、一 方で、前記したように一部の炭素化合物の熱分解速度が炭素物質の成長速度よりも 速いと、炭素物質は触媒粒子の周面方向にも成長し、前記集合体の周りに粒状部を 形成し、所期の三次元構造を有する炭素繊維構造体を効率よく形成する。なお、前 記金属触媒微粒子の集合体中には、他の触媒微粒子よりも活性の低 ヽな ヽしは反 応途中で失活してしまった触媒微粒子も一部に含まれていることも考えられ、集合体 として凝集するより以前にこのような触媒微粒子の表面に成長していた、あるいは集 合体となった後にこのような触媒微粒子を核として成長した非繊維状ないしはごく短 い繊維状の炭素物質層が、集合体の周縁位置に存在することで、本発明に係る炭 素繊維構造体の粒状部を形成しているものとも思われる。 [0063] 反応炉の原料ガス供給口近傍にお!、て、原料ガスの流れに乱流を生じさせる具体 的手段としては、特に限定されるものではなぐ例えば、原料ガス供給口より反応炉 内に導出される原料ガスの流れに干渉し得る位置に、何らかの衝突部を設ける等の 手段を採ることができる。前記衝突部の形状としては、何ら限定されるものではなぐ 衝突部を起点として発生した渦流によって十分な乱流が反応炉内に形成されるもの であれば良いが、例えば、各種形状の邪魔板、パドル、テーパ管、傘状体等を単独 であるいは複数組み合わせて 1な 、し複数個配置すると 、つた形態を採択することが できる。
[0064] このようにして、触媒および炭化水素の混合ガスを 800〜1300°Cの範囲の一定温 度で加熱生成して得られた中間体は、炭素原子力もなるパッチ状のシート片を貼り合 わせたような (生焼け状態の、不完全な)構造を有し、ラマン分光分析をすると、 ンドが非常に大きぐ欠陥が多い。また、生成した中間体は、未反応原料、非繊維状 炭化物、タール分および触媒金属を含んでいる。
[0065] 従って、このような中間体力 これら残留物を除去し、欠陥が少ない所期の炭素繊 維構造体を得るために、適切な方法で 2400〜3000°Cの高温熱処理する。
[0066] すなわち、例えば、この中間体を 800〜1200°Cで加熱して未反応原料やタール分 などの揮発分を除去した後、 2400〜3000°Cの高温でァニール処理することによつ て所期の構造体を調製し、同時に繊維に含まれる触媒金属を蒸発させて除去する。 なお、この際、物質構造を保護するために不活性ガス雰囲気中に還元ガスや微量の 一酸ィ匕炭素ガスを添加してもよ ヽ。
[0067] 前記中間体を 2400〜3000°Cの範囲の温度でァニール処理すると、炭素原子か らなるパッチ状のシート片は、それぞれ結合して複数のグラフエンシート状の層を形 成する。
[0068] また、このような高温熱処理前もしくは処理後において、炭素繊維構造体の円相当 平均径を数 cmに解砕処理する工程と、解砕処理された炭素繊維構造体の円相当 平均径を 50〜： LOO mに粉砕処理する工程とを経ることで、所望の円相当平均径を 有する炭素繊維構造体を得る。なお、解砕処理を経ることなぐ粉砕処理を行っても 良い。また、本発明に係る炭素繊維構造体を複数有する集合体を、使いやすい形、 大きさ、嵩密度に造粒する処理を行っても良い。さら〖こ好ましくは、反応時に形成さ れた上記構造を有効に活用するために、嵩密度が低い状態 (極力繊維が伸びきつた 状態でかつ空隙率が大きい状態)で、ァニール処理するとさらにふつ素榭脂への導 電性付与に効果的である。
[0069] (2)ふつ素榭脂粉末、およびふつ素榭脂成形体
次に本発明のふつ素榭脂成形体を構成するふつ素榭脂粉末、およびふつ素榭脂 粉末と前記で説明した炭素繊維構造体とを混合してなる混合粉体を成形焼成してな るふつ素榭脂成形体について具体的に説明する。
[0070] 本発明にお 、て用いられるふつ素榭脂粉末は、従来公知のふつ素榭脂を粉末状 にしたものであればよぐ特に限定されることはない。し力しながら特に、粒子径 100 μ m以上の大径粉末を全ふつ素榭脂粉末の 5〜： LOO質量％、残部を粒子径 100 m未満の小径粉末とする混合粉体を用いることが好ま ヽ。
[0071] 但し、過大な大径粉末を用いると、成形後の外観に問題が生じる可能性があるので 、大径粉末の粒子径は 100〜 1000 mであることが好ましぐ 100〜500 mである ことが特に好ましい。また、この大径粉末が全ふつ素榭脂粉末中に 60〜100質量％ 含まれる場合に導電性の付与効果が著しい。この大径粉末の含有率は、通常用いら れる篩などによって分離する方法によって測定するものとする。
[0072] ふつ素榭脂の種類としては、例えば、ポリテトラフルォロエチレン、パーフルォロア ルコキシビュルエーテルを共重合させて変性したポリテトラフルォロエチレン、へキサ フルォロプロピレンを共重合させて変性したポリテトラフルォロエチレンなどが好適で ある。
このようなふつ素榭脂粉末に対する前述した炭素繊維構造体の配合量としては、特 に限定されることはないが、例えば成形体全体量の 0. 01〜30. 0質量％であること が好ましい。炭素繊維構造体の配合量が 0. 01質量％を下回ると導電性パスが充分 に形成されず、実用的な導電性が付与出来ない虞れがあるからである。一方で、上 記で説明した本発明特有の炭素繊維構造体を用いれば、その配合量は 30. 0質量 %で充分であり、これを超えて配合しても増分に見合う導電性の向上が見られず不 経済になるとともに、成形性に悪影響が生じる可能性がある力もである。 [0073] 次に、本発明のふつ素榭脂成形体の製造方法について説明する。
先ず、上記のふつ素榭脂からなる大径粉末と小径粉末とを所定の混合比で含有す るふつ素榭脂成混合粉末と、上記で説明した炭素繊維構造体とを混練機、例えば三 井三池化工機社製「ヘンシェルミキサー」に投入し、充分に混合して混合物を得る。 次 ヽで、所望の金型に混合物を充填してプレスにより圧縮して予備成形体を作製す る。このとき、予備成形体の圧縮条件としては 10〜70MPaが好ましぐ 30〜50MPa 力 り好ましい。そして、得られた予備成形体を 300〜450°C、好ましくは 340°C以上 で焼成することで、本発明のふつ素榭脂成形体が得られる。
実施例
[0074] 以下、実施例により本発明を更に詳しく説明するが、本発明は下記の実施例に何 ら限定されるものではない。
なお、以下において、本発明に用いられる炭素繊維構造体に関する各物性値は次 のようにして測定した。
[0075] <面積基準の円相当平均径>
まず、粉砕品の写真を SEMで撮影する。得られた SEM写真において、炭素繊維 構造体の輪郭が明瞭なもののみを対象とし、炭素繊維構造体が崩れているようなも のは輪郭が不明瞭であるために対象としな力つた。 1視野で対象とできる炭素繊維構 造体 (60〜80個程度）はすべて用い、 3視野で約 200個の炭素繊維構造体を対象と した。対象とされた各炭素繊維構造体の輪郭を、画像解析ソフトウェア WinRoof ( 商品名、三谷商事株式会社製)を用いてなぞり、輪郭内の面積を求め、各繊維構造 体の円相当径を計算し、これを平均化した。
[0076] <嵩密度の測定 >
内径 70mmで分散板付透明円筒に lg粉体を充填し、圧力 0. IMpa、容量 1. 3リツ トルの空気を分散板下部力 送り粉体を吹出し、自然沈降させる。 5回吹出した時点 で沈降後の粉体層の高さを測定する。このとき測定箇所は 6箇所とることとし、 6箇所 の平均を求めた後、嵩密度を算出した。
[0077] <ラマン分光分析 >
堀場ジョバンイボン製 LabRam800を用い、アルゴンレーザーの 514nmの波長を 用いて測定した。
[0078] <TG燃焼温度 >
マックサイエンス製 TG— DTAを用い、空気を 0. 1リットル Z分の流速で流通させ ながら、 10°CZ分の速度で昇温し、燃焼挙動を測定した。燃焼時に TGは減量を示 し、 DTAは発熱ピークを示すので、発熱ピークのトップ位置を燃焼開始温度と定義し た。
[0079] <X線回折 >
粉末 X線回折装置 CiDX3532、 日本電子製)を用いて、ァニール処理後の炭素繊 維構造体を調べた。 Cu管球で 40kV、 30mAで発生させた Κ α線を用いることとし、 面間隔の測定は学振法 (最新の炭素材料実験技術 (分析 ·解析編)、炭素材料学会 編）に従い、シリコン粉末を内部標準として用いた。
[0080] <粉体抵抗および復元性 >
CNT粉体 lgを秤取り、榭脂製ダイス（内寸 L 40mm, W 10mm, H 80mm) に充填圧縮し、変位および荷重を読み取る。 4端子法で定電流を流して、そのときの 電圧を測定し、 0. 9gZcm3の密度まで測定したら、圧力を解除し復元後の密度を測 定した。粉体抵抗については、 0. 5、 0. 8および 0. 9g/cm3に圧縮したときの抵抗 を測定することとする。
[0081] <粒状部の平均粒径、円形度、微細炭素繊維との比 >
面積基準の円相当平均径の測定と同様に、まず、炭素繊維構造体の写真を SEM で撮影する。得られた SEM写真において、炭素繊維構造体の輪郭が明瞭なものの みを対象とし、炭素繊維構造体が崩れているようなものは輪郭が不明瞭であるために 対象としな力つた。 1視野で対象とできる炭素繊維構造体 (60〜80個程度）はすべて 用い、 3視野で約 200個の炭素繊維構造体を対象とした。
[0082] 対象とされた各炭素繊維構造体にお!、て、炭素繊維相互の結合点である粒状部を 1つの粒子とみなして、その輪郭を、画像解析ソフトウェア WinRoof (商品名、三谷 商事株式会社製)を用いてなぞり、輪郭内の面積を求め、各粒状部の円相当径を計 算し、これを平均化して粒状部の平均粒径とした。また、円形度 (R)は、前記画像解 析ソフトウェアを用いて測定した輪郭内の面積 (A)と、各粒状部の実測の輪郭長さ（ ひより、次式により各粒状部の円形度を求めこれを平均化した。
[0083] [数 1]
R=A水 4 TU /L2
[0084] さらに、対象とされた各炭素繊維構造体における微細炭素繊維の外径を求め、これ と前記各炭素繊維構造体の粒状部の円相当径から、各炭素繊維構造体における粒 状部の大きさを微細炭素繊維との比として求め、これを平均化した。
[0085] <粒状部の間の平均距離 >
面積基準の円相当平均径の測定と同様に、まず、炭素繊維構造体の写真を SEM で撮影する。得られた SEM写真において、炭素繊維構造体の輪郭が明瞭なものの みを対象とし、炭素繊維構造体が崩れているようなものは輪郭が不明瞭であるために 対象としな力つた。 1視野で対象とできる炭素繊維構造体 (60〜80個程度）はすべて 用い、 3視野で約 200個の炭素繊維構造体を対象とした。
[0086] 対象とされた各炭素繊維構造体において、粒状部が微細炭素繊維によって結ばれ ている箇所を全て探し出し、このように微細炭素繊維によって結ばれる隣接する粒状 部間の距離 (一端の粒状体の中心部力 他端の粒状体の中心部までを含めた微細 炭素繊維の長さ）をそれぞれ測定し、これを平均化した。
[0087] <炭素繊維構造体の破壊試験 >
蓋付バイアル瓶中に入れられたトルエン 100mlに、 30 gZmlの割合で炭素繊維 構造体を添加し、炭素繊維構造体の分散液試料を調製した。
[0088] このようにして得られた炭素繊維構造体の分散液試料に対し、発信周波数 38kHz 、出力 150wの超音波洗浄器（(株)エスェヌディ製、商品名： USK-3)を用いて、超音 波を照射し、分散液試料中の炭素繊維構造体の変化を経時的に観察した。
[0089] まず超音波を照射し、 30分経過後において、瓶中から一定量 2mlの分散液試料を 抜き取り、この分散液中の炭素繊維構造体の写真を SEMで撮影する。得られた SE M写真の炭素繊維構造体中における微細炭素繊維 (少なくとも一端部が粒状部に 結合している微細炭素繊維）をランダムに 200本を選出し、選出された各微細炭素繊 維の長さを測定し、 D 平均値を求め、これを初期平均繊維長とした。
50
[0090] 一方、得られた SEM写真の炭素繊維構造体中における炭素繊維相互の結合点で ある粒状部をランダムに 200個を選出し、選出された各粒状部をそれぞれ 1つの粒子 とみなしてその輪郭を、画像解析ソフトウェア WinRoof (商品名、三谷商事株式会 社製)を用いてなぞり、輪郭内の面積を求め、各粒状部の円相当径を計算し、この D
5 平均値を求めた。そして得られた D 平均値を粒状部の初期平均径とした。
0 50
[0091] その後、一定時間毎に、前記と同様に瓶中から一定量 2mlの分散液試料を抜き取 り、この分散液中の炭素繊維構造体の写真を SEMで撮影し、この得られた SEM写 真の炭素繊維構造体中における微細炭素繊維の D 平均長さおよび粒状部の D
50 50 平均径を前記と同様にして求めた。
[0092] そして、算出される微細炭素繊維の D 平均長さが、初期平均繊維長の約半分とな
50
つた時点 (本実施例においては超音波を照射し、 500分経過後）における、粒状部の D 平均径を、初期平均径と対比しその変動割合 (％)を調べた。
50
[0093] (1)本発明で用いる炭素繊維構造体の合成例 1
CVD法によって、トルエンを原料として本発明で用いる炭素繊維構造体を合成し た。
触媒としてフエ口セン及びチォフェンの混合物を使用し、水素ガスの還元雰囲気で 行った。トルエン、触媒を水素ガスとともに 380°Cに加熱し、生成炉に供給し、 1250 °Cで熱分解して、炭素繊維構造体 (第一中間体)を得た。
[0094] なお、この炭素繊維構造体 (第一中間体)を製造する際に用いられた生成炉の概 略構成を図 8に示す。図 8に示すように、生成炉 1は、その上端部に、上記したような トルエン、触媒および水素ガスからなる原料混合ガスを生成炉 1内へ導入する導入ノ ズル 2を有している力 さらにこの導入ノズル 2の外側方には、円筒状の衝突部 3が設 けられている。この衝突部 3は、導入ノズル 2の下端に位置する原料ガス供給口 4より 反応炉内に導出される原料ガスの流れに干渉し得るものとされている。なお、この実 施例において用いられた生成炉 1では、導入ノズル 2の内径 a、生成炉 1の内径 b、筒 状の衝突部 3の内径 c、生成炉 1の上端カゝら原料混合ガス導入口 4までの距離 d、原 料混合ガス導入口 4から衝突部 3の下端までの距離 e、原料混合ガス導入口 4から生 成炉 1の下端までの距離を fとすると、各々の寸法比は、おおよそ a :b : c : d: e :f=l . 0 : 3. 6 : 1. 8 : 3. 2 : 2. 0 : 21. 0に形成されていた。また、反応炉への原料ガス導入速 度は、 1850NLZmin、圧力は 1. 03atmとした。
[0095] 上記のようにして合成された中間体を窒素中で 900°Cで焼成して、タールなどの炭 化水素を分離し、第二中間体を得た。この第二中間体のラマン分光測定の R値は 0.
98であった。また、この第一中間体をトルエン中に分散して電子顕微鏡用試料調製 後に観察した SEMおよび TEM写真を図 1、 2に示す。
[0096] さらにこの第二中間体をアルゴン中で 2600°Cで高温熱処理し、得られた炭素繊維 構造体の集合体を気流粉砕機にて粉砕し、本発明にお ヽて用いられる炭素繊維構 造体を得た。
[0097] 得られた炭素繊維構造体をトルエン中に超音波で分散して電子顕微鏡用試料調 製後に観察した SEMおよび TEM写真を図 3、図 4Aおよび図 4Bに示す。
[0098] また、得られた炭素繊維構造体をそのまま電子顕微鏡用試料ホルダーに載置して 観察した SEM写真を図 5に、またその粒度分布を表 1に示した。
[0099] さらに高温熱処理前後において、炭素繊維構造体の X線回折およびラマン分光分 析を行い、その変化を調べた。結果を図 6および 7に示す。
[0100] また、得られた炭素繊維構造体の円相当平均径は、 72. 8 m、嵩密度は 0. 003 2g/cm3、ラマン ID/IG比値は 0. 090、 TG燃焼温度は 786°C、面間隔は 3. 383 オングストローム、粉体抵抗値は 0. 0083 Ω 'cm、復元後の密度は 0. 25gZcm3で めつに。
[0101] さらに炭素繊維構造体における粒状部の粒径は平均で、 443nm (SD207nm)で あり、炭素繊維構造体における微細炭素繊維の外径の 7. 38倍となる大きさであった 。また粒状部の円形度は、平均値で 0. 67(SD0. 14)であった。
[0102] また、前記した手順によって炭素繊維構造体の破壊試験を行ったところ、超音波印 カロ 30分後の初期平均繊維長（D )は、 12. 8 mであったが、超音波印加 500分後
50
の平均繊維長（D )は、6. 7 mとほぼ半分の長さとなり、炭素繊維構造体において
50
微細炭素繊維に多くの切断が生じたことが示された。し力しながら、超音波印加 500 分後の粒状部の平均径 (D )を、超音波印加 30分後の初期初期平均径 (D )と対
50 50 比したところ、その変動 (減少)割合は、わずか 4. 8%であり、測定誤差等を考慮する と、微細炭素繊維に多くの切断が生じた負荷条件下でも、切断粒状部自体はほとん ど破壊されることなく、繊維相互の結合点として機能して 、ることが明らカとなった。
[0103] なお、合成例 1の炭素繊維構造体を測定した各種物性値を、表 2にまとめた。
[0104] [表 1]
Figure imgf000024_0001
[0106] (2)本発明で用いる炭素繊維構造体の合成例 2
生成炉カ の排ガスの一部を循環ガスとして使用し、この循環ガス中に含まれるメタ ン等の炭素化合物を、新鮮なトルエンと共に、炭素源として使用して、 CVD法により 微細炭素繊維を合成した。
[0107] 合成は、触媒としてフエ口セン及びチォフェンの混合物を使用し、水素ガスの還元 雰囲気で行った。新鮮な原料ガスとして、トルエン、触媒を水素ガスとともに予熱炉に て 380°Cに加熱した。一方、生成炉の下端より取り出された排ガスの一部を循環ガス とし、その温度を 380°Cに調整した上で、前記した新鮮な原料ガスの供給路途中に て混合して、生成炉に供給した。
[0108] なお、使用した循環ガスにおける組成比は、体積基準のモル比で CH 7. 5%、 C H 0. 3%、 C H 0. 7%、 C H 0. 1%、 CO 0. 3%、 N 3. 5%、 H 87. 6
6 6 2 2 2 6 2 2
%であり、新鮮な原料ガスとの混合によって、生成炉へ供給される原料ガス中におけ るメタンとベンゼンとの混合モル比 CH /C H (なお、新鮮な原料ガス中のトルエン
4 6 6
は予熱炉での加熱によって、 CH ： C H = 1 : 1に 100%分解したものとして考慮した
4 6 6
。；)が、 3. 44となるように、混合流量を調整された。
[0109] なお、最終的な原料ガス中には、混合される循環ガス中に含まれて!/、た、 C H、 C
2 2
Hおよび COも炭素化合物として当然に含まれている力 これらの成分は、いずれも
2 6
ごく微量であり、実質的に炭素源としては無視できるものであった。
[0110] そして、合成例 1と同様に、生成炉において、 1250°Cで熱分解して、炭素繊維構 造体 (第一中間体)を得た。
[0111] なお、この炭素繊維構造体 (第一中間体)を製造する際に用いられた生成炉の構 成は、円筒状の衝突部 3がない以外は、図 8に示す構成と同様のものであり、また反 応炉への原料ガス導入速度は、合成例 1と同様に、 1850NLZmin、圧力は 1. 03a tmとした。
[0112] 上記のようにして合成された第一中間体をアルゴン中で 900°Cで焼成して、タール などの炭化水素を分離し、第二中間体を得た。この第二中間体のラマン分光測定の R値は 0. 83であった。また、第一中間体をトルエン中に分散して電子顕微鏡用試料 調製後に観察したところ、その SEMおよび TEM写真は図 1、 2に示す合成例 1のも のとほぼ同様のものであった。
[0113] さらにこの第二中間体をアルゴン中で 2600°Cで高温熱処理し、得られた炭素繊維 構造体の集合体を気流粉砕機にて粉砕し、本発明に係る炭素繊維構造体を得た。 得られた炭素繊維構造体をトルエン中に超音波で分散して電子顕微鏡用試料調 製後に観察した SEMおよび TEM写真は、図 3、図 4Aおよび図 4Bに示す合成例 1 のものとほぼ同様のものであった。
[0114] また、得られた炭素繊維構造体をそのまま電子顕微鏡用試料ホルダーに載置して 観察し粒度分布を調べた。得られた結果を表 3に示す。
[0115] さらに高温熱処理前後において、炭素繊維構造体の X線回折およびラマン分光分 析を行い、その変化を調べたところ、図 6および 7に示す合成例 1の結果とほぼ同様 のものであった。
[0116] また、得られた炭素繊維構造体の円相当平均径は、 75. 8 m、嵩密度は 0. 004 g/cm3、ラマン I /1比値は 0. 086、 TG燃焼温度は 807°C、面間隔は 3. 386オン
D G
ダストローム、粉体抵抗値は 0. 0077 Ω - cm,復元後の密度は 0. 26gZcm3であつ た。
[0117] さらに炭素繊維構造体における粒状部の粒径は平均で、 349. 5nm (SD180. In m)であり、炭素繊維構造体における微細炭素繊維の外径の 5. 8倍となる大きさであ つた。また粒状部の円形度は、平均値で 0. 69(SD0. 15)であった。
[0118] また、前記した手順によって炭素繊維構造体の破壊試験を行ったところ、超音波印 加 30分後の初期平均繊維長（D )は、 12. 4 mであったが、超音波印加 500分後
50
の平均繊維長（D )は、 6. 3 mとほぼ半分の長さとなり、炭素繊維構造体において
50
微細炭素繊維に多くの切断が生じたことが示された。し力しながら、超音波印加 500 分後の粒状部の平均径 (D )を、超音波印加 30分後の初期初期平均径 (D )と対
50 50 比したところ、その変動 (減少)割合は、わずか 4. 2%であり、測定誤差等を考慮する と、微細炭素繊維に多くの切断が生じた負荷条件下でも、切断粒状部自体はほとん ど破壊されることなぐ繊維相互の結合点として機能していることが明らかとなった。
[0119] なお、合成例 2の炭素繊維構造体を測定した各種物性値を、表 4にまとめた。
[0120] [表 3]
Figure imgf000026_0001
[0121] [表 4] 合成例 2
円相当平均径 5. 8 μ m
嵩密度 0. 0 04 g/c m3
I Ό/ I G比 0. 0 8 6
TG燃焼温度 8 0 7
(0 0 2) 顏隔 3. 3 8 6 A
粉体抵抗値 （at 0.5g/cmH) 0. 0 1 6 1 Ω · c m
粉体抵抗値 （at0.8g/cm3) 0. 0 0 8 9 Ω · c m
粉体抵抗値 (at 0.9g/cm¾ 0. 0 0 7 7 U · c m
復元後の密度 0. 2 6 g/c m3
[0122] (3)実施例 1〜8
表 5に示すように、ふつ素系榭脂粉末と、前記合成例 1、 2で合成した炭素繊維構 造体とをヘンシェルミキサー（三井三池化工機社製）に投入し、回転数 980rpm、 10 分間混合して混合物を得た。次いで、混合物を円筒状の金型に充填し、圧力 50MP aで 5分間圧縮して予備成形体を得た。そして、予備成形体を室温から 365°Cまで 50 °CZ分で昇温し、 365°Cで 4時間保持した後、 50°CZ分で室温まで冷却し、試験片 を得た。
[0123] そして、各試験片の表面電気抵抗率を、ロレスタ ·ΑΡ (三菱ィ匕学製)を使用して測
£し 7こ。
その結果を表 5に示す。
[0124] [表 5] ふつ 榭脂粉未 導¾性添加剤 J¾^粉体 成形休
100〜1麵
試料名 ψ均粒子 ½ 添加率 添加^ 電¾抵抗率 品名 ΐι名 μ m粉末量
( m) (質 (質量％) (Ω/D)
(質量％)
'鍾例 1 G340 200 99 CNT ^成 1 1 M A.20E+01 灾-歸 12 G340 200 99 CNT介成 2 1 64 3.301 01 雄例 3 3B0 250 99 成 1 1 83 5.30E101 実施例 4 G350 250 99 CNT ^成 2 J 83 3.50E+01
¾施例 5 450HP-J 300 99 成 1 1 72 4.謹 +01 雄例 6 4501IP-J 300 99 CNT合成 2 1 72 3.50E+01
¾施例 7 Μ-392 700 99 CNT ^成 1 1 91 6.90H+01
' 施例 8 -392 700 99 CNT合成 2 1 91

Claims

請求の範囲
[1] ふつ素榭脂粉末及び炭素繊維構造体を含む混合粉体を成形焼成してなるふつ素 榭脂成形体であって、
前記炭素繊維構造体が、外径 15〜： LOOnmの炭素繊維カゝら構成される 3次元ネット ワーク状を呈しており、前記炭素繊維が複数延出する態様で、当該炭素繊維を互い に結合する粒状部を有しており、かつ当該粒状部は前記炭素繊維の成長過程にお いて形成されてなるものであることを特徴するふつ素榭脂成形体。
[2] 前記炭素繊維構造体は、面積基準の円相当平均径が 50〜： LOO /z mであることを 特徴とする請求項 1に記載のふつ素榭脂成形体。
[3] 前記炭素繊維構造体は、嵩密度が、 0. 0001〜0. 05gZcm3であることを特徴と する請求項 1または 2に記載のふつ素榭脂成形体。
[4] 前記炭素繊維構造体は、ラマン分光分析法で測定される I
D Λ 0. 2
G力 以下であ ることを特徴とする請求項 1〜3のいずれか 1つに記載のふつ素榭脂成形体。
[5] 前記炭素繊維構造体は、空気中での燃焼開始温度が 750°C以上であることを特徴 とする請求項 1〜4のいずれ力 1つに記載のふつ素榭脂成形体。
[6] 前記炭素繊維の結合箇所にお!、て、前記粒状部の粒径が、前記炭素繊維の外径 よりも大きいことを特徴とする請求項 1〜5のいずれか 1つに記載のふつ素榭脂成形 体。
[7] 前記炭素繊維構造体は、炭素源として、分解温度の異なる少なくとも 2つ以上の炭 素化合物を用いて、生成されたものである請求項 1〜6のいずれか 1つに記載のふつ 素榭脂成形体。
[8] 前記炭素繊維構造体を 0. 01〜30. 0質量％の割合で含有することを特徴とする 請求項 1〜7のいずれか 1つに記載のふつ素榭脂成形体。
[9] 前記ふつ素榭脂粉末は、粒径 100 μ m以上の大径粒体を全ふつ素榭脂粉末の 5
〜： L00質量％、残部が粒子径 100 m未満の小径粒体で構成されていることを特徴 とする請求項 1〜8のいずれ力 1つに記載のふつ素榭脂成形体。
[10] 前記大径粒体力 粒子径 100〜1000 mであることを特徴とする請求項 1〜9の いずれか 1つに記載のふつ素榭脂成形体。 前記ふつ素榭脂粉末が、ポリテトラフルォロエチレン、パーフルォロアルコキシビ- ルエーテルを共重合させて変性したポリテトラフルォロエチレン及びへキサフルォロ プロピレンを共重合させて変性したポリテトラフルォロエチレン力 なる群力 選ばれ た少なくとも 1種力もなる粉末であることを特徴とする請求項 1〜： LOのいずれか 1つに 記載のふつ素榭脂成形体。
PCT/JP2006/321123 2005-10-25 2006-10-24 ふっ素樹脂成形体 Ceased WO2007049591A1 (ja)