WO2005104289A1 - 電池用非水電解液及びそれを備えた非水電解液電池 - Google Patents

電池用非水電解液及びそれを備えた非水電解液電池 Download PDF

Info

Publication number
WO2005104289A1
WO2005104289A1 PCT/JP2005/005920 JP2005005920W WO2005104289A1 WO 2005104289 A1 WO2005104289 A1 WO 2005104289A1 JP 2005005920 W JP2005005920 W JP 2005005920W WO 2005104289 A1 WO2005104289 A1 WO 2005104289A1
Authority
WO
WIPO (PCT)
Prior art keywords
battery
aqueous electrolyte
nonaqueous electrolyte
phosphine oxide
group
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/JP2005/005920
Other languages
English (en)
French (fr)
Inventor
Yasuo Horikawa
Shinichi Eguchi
Masashi Ohtsuki
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Bridgestone Corp
Original Assignee
Bridgestone Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Bridgestone Corp filed Critical Bridgestone Corp
Priority to US11/578,602 priority Critical patent/US7947399B2/en
Priority to EP05727866A priority patent/EP1739784B1/en
Priority to JP2006512493A priority patent/JP4785735B2/ja
Publication of WO2005104289A1 publication Critical patent/WO2005104289A1/ja
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

　本発明は、優れた安全性を有する電池用非水電解液、並びに、該非水電解液を備えた安全性の高い非水電解液電池に関し、より詳しくは、分子中にＰ－Ｆ結合及び／又はＰ－ＮＨ2結合を有するホスフィンオキサイド化合物と、支持塩とを含むことを特徴とする電池用非水電解液、並びに、該電池用非水電解液と、正極と、負極とを備えた非水電解液電池に関するものである。

Description

明 細 書
電池用非水電解液及びそれを備えた非水電解液電池
技術分野
[0001] 本発明は、電池用非水電解液及びそれを備えた非水電解液電池に関し、特に安 全性に優れた電池用非水電解液及び非水電解液電池に関するものである。
背景技術
[0002] 近年、電気自動車や燃料電池自動車の主電源若しくは補助電源として、又は小型 電子機器の電源として、軽量且つ長寿命で、高エネルギー密度の電池が求められて いる。これに対し、リチウムを負極活物質とする非水電解液電池は、リチウムの電極電 位が金属中で最も低ぐ単位体積当りの電気容量が大きいために、エネルギー密度 の高い電池の一つとして知られており、 1次電池 · 2次電池を問わず多くの種類のも のが活発に研究され、一部が実用化し市場に供給されている。例えば、非水電解液 1次電池は、カメラ、電子ウォッチ及び各種メモリーバックアップ用電源として用いられ ている。また、非水電解液 2次電池は、ノート型パソコン及び携帯電話等の駆動電源 として用レ、られており、更には、電気自動車や燃料電池自動車の主電源若しくは補 助電源として用いることが検討されている。
[0003] これらの非水電解液電池においては、負極活物質のリチウムが水及びアルコール 等の活性プロトンを有する化合物と激しく反応するため、該電池に使用される電解液 は、エステル化合物及びエーテルィヒ合物等の非プロトン性有機溶媒に限られている
[0004] し力しながら、上記非プロトン性有機溶媒は、負極活物質のリチウムとの反応性が 低いものの、例えば、電池の短絡時等に大電流が急激に流れ、電池が異常に発熱し た際に、気化 '分解してガスを発生したり、発生したガス及び熱により電池の破裂 '発 火を引き起こしたり、短絡時に生じる火花が引火する等の危険性が高い。
[0005] このような問題に対して、電池用非水電解液を難燃化する方法が検討されており、 例えば、電解液にリン酸トリメチル等のリン酸エステル類を用いたり、非プロトン性有 機溶媒にリン酸エステル類を添加したりする方法が報告されている（特開平 4— 184 870号公報、特開平 8— 22839号公報、特開 2001 _ 182669号公報等参照）。し 力 ながら、これら一般的なリン酸トリエステル類は、不燃性が十分といはいえず、ま た、充放電を繰り返すことにより負極で徐々に還元分解され、サイクル特性等の電池 特性が大きく劣化してしまう問題がある。
発明の開示
[0006] そこで、本発明の目的は、燃焼抑制効果に優れた化合物を添加してなる、優れた 安全性を有する電池用非水電解液及び該非水電解液を備えた安全性の高い非水 電解液電池を提供することにある。
[0007] 本発明者らは、種々のホスフィンオキサイドィ匕合物を検討した結果、特に優れた燃 焼抑制効果を有する化合物が存在し、該化合物を非水電解液に添加することで、非 水電解液及び非水電解液電池の安全性を大幅に改善できることを見出し、本発明を 完成させるに至った。
[0008] 即ち、本発明の電池用非水電解液は、分子中に P— F結合及び Z又は P— NH結
2 合を有するホスフィンオキサイドィ匕合物と、支持塩とを含むことを特徴とする。
[0009] 本発明の電池用非水電解液の好適例においては、前記ホスフィンオキサイド化合 物の含有率力 S3体積％以上であり、 5体積％以上であるのが更に好ましい。
[0010] 本発明の電池用非水電解液の他の好適例においては、前記ホスフィンオキサイド 化合物が下記式 (I) :
Figure imgf000003_0001
(式中、 R1は、それぞれ独立して一価の置換基又はハロゲン元素であり、少なくとも一 つの R1はフッ素又はアミノ基である）で表される。ここで、式 (I)中の R1が、それぞれ独 立してフッ素、アミノ基、アルキル基及びアルコキシ基からなる群から選択され、且つ 少なくとも一つの R1がフッ素又はアミノ基であるのが更に好ましい。また、式 (I)中の R1 の少なくとも一つがフッ素で、且つ式 (I)中の R1の少なくとも一つがアミノ基であるホス フィンオキサイド化合物、並びに、式 (I)中の R1の二つ以上が、フッ素又はアミノ基であ るホスフィンオキサイド化合物が特に好ましレ、。
[0011] 本発明の電池用非水電解液は、更に非プロトン性有機溶媒を含むのが好ましい。
ここで、該非プロトン性有機溶媒としては、環状及び鎖状のエステル化合物並びに鎖 状のエーテル化合物が好ましレ、。
[0012] また、本発明の非水電解液電池は、上記電池用非水電解液と、正極と、負極とを備 えることを特徴とする。
[0013] 本発明によれば、分子中に P_F結合及び Z又は P_NH結合を有するホスフィン オキサイド化合物を含み、発火'引火の危険性が大幅に抑制された電池用非水電解 液を提供することができる。また、該非水電解液を備え、安全性が著しく改善された 非水電解液電池を提供することができる。
発明を実施するための最良の形態
[0014] <電池用非水電解液 >
以下に、本発明の電池用非水電解液を詳細に説明する。本発明の電池用非水電 解液は、分子中に P_F結合及び Z又は P_NH結合を有するホスフィンオキサイド 化合物と、支持塩とを含み、必要に応じて、非プロトン性有機溶媒等を含んでもょレ、 。本発明の非水電解液電池の非水電解液には、力かるホスフィンオキサイド化合物 が含まれるため、非水電解液及び該非水電解液を備えた電池の発火'引火の危険 性が大幅に抑制されている。
[0015] 本発明の電池用非水電解液に用いられるホスフィンオキサイド化合物は、分子中 に P— F結合及び/又は P— NH結合を有する限り特に制限はなレ、。力かるホスフィ ンオキサイド化合物の中でも、上記式 (I)で表されるホスフィンオキサイド化合物が好ま しい。式 (I)において、 R1は、それぞれ独立して一価の置換基又はハロゲン元素であり 、少なくとも一つの R1はフッ素又はアミノ基である。ここで、ハロゲン元素としては、フッ 素、塩素、臭素等が好適に挙げられ、これらの中でも、フッ素が特に好ましい。一方、 一価の置換基としては、アミノ基、アルコキシ基、アルキル基、カルボキシル基、ァシ ル基、ァリール基等が挙げられ、これらの中でも、電解液の発火'引火の危険性を低 減する効果に優れる点で、アミノ基及びアルコキシ基が好ましい。また、上記アルコキ シ基としては、メトキシ基、エトキシ基、メトキシエトキシ基、プロポキシ基、フエノキシ基 等が挙げられ、上記アルキル基としては、メチル基、ェチル基、プロピル基、ブチル 基、ペンチル基等が挙げられ、上記ァシル基としては、ホルミル基、ァセチル基、プロ ピオニル基、ブチリル基、イソプチリル基、バレリル基等が挙げられ、上記ァリール基 としては、フヱニル基、トリル基、ナフチル基等が挙げられる。これら一価の置換基中 の水素元素は、ハロゲン元素で置換されているのが好ましぐハロゲン元素としては、 フッ素、塩素、臭素等が好適に挙げられ、フッ素が最も好ましぐ次いで、塩素が好ま しい。
[0016] 上記ホスフィンオキサイド化合物は、分子中の 10質量％以上がハロゲン元素である のが好ましぐ分子中の 15質量％以上がハロゲン元素であるのが更に好ましい。また 、該ホスフィンオキサイド化合物は、分子中の 7質量％以上がフッ素であるのが好まし く、分子中の 10質量％以上がフッ素であるのが更に好ましい。分子中の 10質量％以 上がハロゲン元素であるホスフィンオキサイド化合物は、非水電解液の燃焼を抑制す る効果に優れ、分子中の 7質量％以上がフッ素であるホスフィンオキサイド化合物は、 非水電解液の燃焼を抑制する効果に特に優れる。
[0017] 上記ホスフィンオキサイド化合物としては、式 (I)中の R1の少なくとも一つがフッ素で 、且つ式 (I)中の R1の少なくとも一つがアミノ基であるホスフィンオキサイド化合物、並 びに、式 (I)中の R1の二つ以上がフッ素又はアミノ基であるホスフィンオキサイド化合 物が特に好ましい。これらホスフィンオキサイド化合物は、電解液の燃焼抑制に寄与 するフッ素及びアミノ基の分子中に占める割合が高いため、優れた燃焼抑制効果を 有する。
[0018] 上記式 (I)のホスフィンオキサイド化合物として、具体的には、トリフルォロホスフィン オキサイド [〇 = PF ]、トリァミノホスフィンオキサイド [0 = P(NH ) ]、アミノジフルォロ ホスフィンオキサイド [〇 = PF NH ]、ジァミノフルォロホスフィンオキサイド [〇 = PF(
NH ) ]、メチルジァミノホスフィンオキサイド [〇 = P(NH ) CH ]、メチルァミノフルォ 口ホスフィンオキサイド [〇 = PF(NH )CH ]、ジメトキシフルォロホスフィンオキサイド [
〇 = PF(〇CH ) ]、エトキシジフルォロホスフィンオキサイド [〇 = PF (OC H )]、メト キシジフルォロホスフィンオキサイド [〇 = PF (OCH )]、ジメチルフルォロホスフィン オキサイド [〇 = PF(CH ) ]、ジエトキシフルォロホスフィンオキサイド [〇 = PF(〇C H
) ]、メチルジフルォロホスフィンオキサイド [〇 = PF (CH )]等が挙げられる。
[0019] 上記ホスフィンオキサイド化合物の非水電解液中における含有率は、 3体積％以上 であるのが好ましぐ 5体積％以上であるのが更に好ましい。上記ホスフィンオキサイド 化合物の非水電解液中における含有率が 3体積％以上であれば、非水電解液の発 火'引火の危険性を充分に抑制することができる。なお、上記ホスフィンオキサイドィ匕 合物は、一種単独で用いてもよいし、二種以上を混合して用いてもよい。
[0020] 本発明の電池用非水電解液に用いられる支持塩としては、リチウムイオンのイオン 源となる支持塩が好ましい。該支持塩としては、特に制限はなレ、が、例えば、 LiCIO
、 LiBF、 LiPF、 LiCF SO LiAsF、 LiC F SO、 Li(CF SO ) N及び Li(C F SO
) N等のリチウム塩が好適に挙げられる。これら支持塩は、 1種単独で使用してもよく
、 2種以上を併用してもよい。
[0021] 上記非水電解液中の支持塩の濃度としては、 0.2〜1.5mol/L(M)が好ましぐ 0.5〜 lmol/L(M)が更に好ましレ、。支持塩の濃度力 S0.2mol/L(M)未満では、電解液の導電 性を充分に確保することができず、電池の放電特性及び充電特性に支障をきたすこ とがあり、 1.5mol/L(M)を超えると、電解液の粘度が上昇し、リチウムイオンの移動度を 充分に確保できないため、前述と同様に電解液の導電性を充分に確保できず、電池 の放電特性及び充電特性に支障をきたすことがある。
[0022] 本発明の非水電解液に用いることができる非プロトン性有機溶媒は、負極と反応す ることなく、更には非水電解液の粘度を低く抑えることができる。該非プロトン性有機 溶媒として、具体的には、ジメチルカーボネート (DMC)、ジェチルカーボネート (DE C)、ジフヱニルカーボネート、ェチルメチルカーボネート (EMC)、エチレンカーボネ ート (EC)、プロピレンカーボネート (PC)、 γ -ブチロラタトン (GBL)、 γ -バレロラタトン 、メチルフオルメート (MF)等のエステル類、 1，2-ジメトキシェタン (DME)、テトラヒドロ フラン (THF)等のエーテル類が好適に挙げられる。これらの中でも、 1次電池の非水 電解液用の非プロトン性有機溶媒としては、プロピレンカーボネート、 1,2-ジメトキシ ェタン及び T -プチ口ラタトンが好ましぐ一方、 2次電池の非水電解液用の非プロト ン性有機溶媒としては、エチレンカーボネート、プロピレンカーボネート、ジェチルカ ーボネート、ジメチルカーボネート、ェチルメチルカーボネート及びメチルフオルメート が好ましい。なお、環状のエステル類は、比誘電率が高く支持塩の溶解性に優れる 点で好適であり、一方、鎖状のエステル類及び鎖状のエーテル類は、低粘度である ため、電解液の低粘度化の点で好適である。これら非プロトン性有機溶媒は、 1種単 独で使用してもよぐ 2種以上を併用してもよい。
[0023] <非水電解液電池 >
次に、本発明の非水電解液電池を詳細に説明する。本発明の非水電解液電池は 、上述の電池用非水電解液と、正極と、負極とを備え、必要に応じて、セパレーター 等の非水電解液電池の技術分野で通常使用されている他の部材を備える。
[0024] 本発明の非水電解液電池の正極活物質は 1次電池と 2次電池で一部異なり、例え ば、非水電解液 1次電池の正極活物質としては、フッ化黒鉛 [(CF ) ]、 MnO (電気
X n 2 ィ匕学合成であっても化学合成であってもよい）、 V O、 MoO、 Ag CrO、 CuO、 Cu
2 5 3 2 4
S、 FeS、 SO、 SOC1、 TiS等が好適に挙げられ、これらの中でも、高容量で安全
2 2 2 2
性が高ぐ更には放電電位が高く電解液の濡れ性に優れる点で、 MnO、フッ化黒
2
鉛が好ましい。これら正極活物質は、 1種単独で使用してもよぐ 2種以上を併用して ちょい。
[0025] 一方、非水電解液 2次電池の正極活物質としては、 V O、 V O 、 MnO、 MnO
2 5 6 13 2 3 等の金属酸化物、 LiCoO、 LiNiO、 LiMn O、 LiFeO及び LiFePO等のリチウム
2 2 2 4 2 4
含有複合酸化物、 TiS、 MoS等の金属硫化物、ポリア二リン等の導電性ポリマー等
2 2
が好適に挙げられる。上記リチウム含有複合酸化物は、 Fe、 Mn、 Co及び Niからな る群から選択される 2種又は 3種の遷移金属を含む複合酸化物であってもよぐこの 場合、該複合酸化物は、 LiFe Co Ni O (式中、 0≤x< 1、 0≤y< 1、 0<x + y
x y (Ι -y) 2
≤l)、LiMn Fe〇 、あるいは LiNi Co Mn 〇等で表される。これらの中でも、
X y 2-x-y x y Ι -y 2
高容量で安全性が高ぐ更には電解液の濡れ性に優れる点で、 LiCoO、 LiNiO、
2 2
LiMn O、 LiNi Co Mn 〇が特に好適である。これら正極活物質は、 1種単独
2 4 1/3 1/3 1/3 2
で使用してもよぐ 2種以上を併用してもよい。
[0026] 本発明の非水電解液電池の負極活物質は 1次電池と 2次電池で一部異なり、例え ば、非水電解液 1次電池の負極活物質としては、リチウム金属自体の他、リチウム合 金等が挙げられる。リチウムと合金をつくる金属としては、 Sn、 Si、 Pb、 Al、 Au、 Pt、 I n、 Zn、 Cd、 Ag、 Mg等が挙げられる。これらの中でも、埋蔵量の多さ、毒性の観点 から Al、 Zn、 Mgが好ましい。これら負極活物質は、 1種単独で使用してもよ 2種 以上を併用してもよい。 [0027] 一方、非水電解液 2次電池の負極活物質としては、リチウム金属自体、リチウムと A1 、 In、 Sn、 Si、 Pb又は Zn等との合金、リチウムをドープした黒鉛等の炭素材料等が 好適に挙げられ、これらの中でも安全性がより高 電解液の濡れ性に優れる点で、 黒鉛等の炭素材料が好ましぐ黒鉛が特に好ましい。ここで、黒鉛としては、天然黒 鉛、人造黒鉛、メソフェーズカーボンマイクロビーズ (MCMB)等、広くは易黒鉛化力 一ボンや難黒鉛化カーボンが挙げられる。これら負極活物質は、 1種単独で使用して もよぐ 2種以上を併用してもよい。
[0028] 上記正極及び負極には、必要に応じて導電剤、結着剤を混合することができ、導 電剤としてはアセチレンブラック等が挙げられ、結着剤としてはポリフッ化ビニリデン（ PVDF)、ポリテトラフルォロエチレン (PTFE)、スチレン 'ブタジエンゴム (SBR)、カル ボキシメチルセルロース (CMC)等が挙げられる。これらの添加剤は、従来と同様の配 合割合で用いることができる。
[0029] また、上記正極及び負極の形状としては、特に制限はなぐ電極として公知の形状 の中力 適宜選択することができる。例えば、シート状、円柱形状、板状形状、スパイ ラル形状等が挙げられる。
[0030] 本発明の非水電解液電池に使用できる他の部材としては、非水電解液電池にぉレ、 て、正負極間に、両極の接触による電流の短絡を防止する役割で介在させるセパレ 一ターが挙げられる。セパレーターの材質としては、両極の接触を確実に防止し得、 且つ電解液を通したり含んだりできる材料、例えば、ポリテトラフルォロエチレン、ポリ プロピレン、ポリエチレン、セノレロース系、ポリブチレンテレフタレート、ポリエチレンテ レフタレート等の合成樹脂製の不織布、薄層フィルム等が好適に挙げられる。これら の中でも、厚さ 20〜50 μ m程度のポリプロピレン又はポリエチレン製の微孔性フィルム 、セノレロース系、ポリブチレンテレフタレート、ポリエチレンテレフタレート等のフイノレム が特に好適である。本発明では、上述のセパレーターの他にも、通常電池に使用さ れている公知の各部材が好適に使用できる。
[0031] 以上に説明した本発明の非水電解液電池の形態としては、特に制限はな コイン タイプ、ボタンタイプ、ペーパータイプ、角型又はスパイラル構造の円筒型電池等、種 々の公知の形態が好適に挙げられる。ボタンタイプの場合は、シート状の正極及び 負極を作製し、該正極及び負極でセパレーターを挟む等して、非水電解液電池を作 製することができる。また、スパイラル構造の場合は、例えば、シート状の正極を作製 して集電体を挟み、これに、シート状の負極を重ね合わせて巻き上げる等して、非水 電解液電池を作製することができる。
[0032] <実施例 >
以下に、実施例を挙げて本発明を更に詳しく説明するが、本発明は下記の実施例 に何ら限定されるものではない。
[0033] (実施例 1)
メトキシジフルォロホスフィンオキサイド [〇 = PF (OCH )] 10体積0 /0と、エチレン力 ーボネート（EC) /ェチルメチルカーボネート (EMC)混合溶液（EC/EMC体積比 = 3/7) 90体積％とを混合し、更に、 LiPFを lmol/Lになるように溶解させて、非水 電解液を調製した。得られた非水電解液の限界酸素指数を下記（1)の方法で測定し 、表 1に示す結果を得た。
[0034] (1)電解液の限界酸素指数
JIS K 7201に準じて、電解液の限界酸素指数を測定した。限界酸素指数が大き い程、電解液が燃焼し難いことを示す。具体的には、 SiOシート (石英濾紙、不燃性
) 127mm X 12.7mmを U字型のアルミ箔で補強して自立可能とし、該 SiOシートに前 記電解液 l.OmLを含浸して試験片を作製した。該試験片を試験片支持具に垂直に、 燃焼円筒（内径 75mm、高さ 450mm、直径 4mmのガラス粒を底部から 100 ± 5mmの厚さ に均等に満たし金属製の網をその上に置いたもの）の上端部から 100mm以上の距離 に位置するように取り付け、次に、燃焼円筒に酸素 CFIS K 1101又はこれと同等以 上のもの）及び窒素 tilS K 1107の 2級又はこれと同等以上のもの）を流し、試験片 を所定の酸素濃度下で点火し (熱源 ίお IS K 2240の 1種 1号)、燃焼状態を調べた 。但し、燃焼円筒内の総流量は 11.4L/minである。この試験を 3回行レ、、その平均値 を表 1に示す。なお、酸素指数とは、材料が燃焼を持続するのに必要な容量パーセ ントで表される最低酸素濃度の値をいい、本願では、試験片が 3分以上継続して燃 焼するか、着炎後の燃焼長さが 50mm以上燃えるのに必要な最低の酸素流量とその ときの窒素流量から、下記の式： 限界酸素指数 = (酸素流量) Z [ (酸素流量） + (窒素流量) ] X 100 (体積％) に従って限界酸素指数を算出した。
[0035] 次に、 LiCoO (正極活物質） 94質量部に対して、アセチレンブラック（導電剤） 3質 量部と、ポリフッ化ビニリデン (結着剤） 3質量部とを添加し、有機溶媒 (酢酸ェチルと エタノールとの 50/50質量％混合溶媒）で混練した後、該混練物を厚さ 25 μ mのアル ミニゥム箔（集電体）にドクターブレードで塗工し、更に熱風乾燥（100〜120°C)して、 厚さ 80 z mの正極シートを作製した。また、人造グラフアイト (負極活物質) 90質量部 に対して、ポリフッ化ビニリデン (結着剤） 10質量部を添加し、有機溶媒 (酢酸ェチル とエタノールとの 50/50質量％混合溶媒）で混練した後、該混練物を厚さ 25 μ mの銅 箔 (集電体）にドクターブレードで塗工し、更に熱風乾燥（100〜120°C)して、厚さ 80 μ mの負極シートを作製した。得られた正極シートに、厚さ 25 μ mのセパレーター（微 孔性フィルム：ポリプロピレン製）を介して、負極シートを重ね合わせて巻き上げ、円 筒型電極を作製した。該円筒型電極の正極長さは約 260mmであった。該円筒型電 極に、上記電解液を注入して封口し、単三型リチウム電池 (非水電解液 2次電池）を 作製した。得られた電池のサイクル特性及び低温特性を下記の方法で測定し、表 1 に示す結果を得た。
[0036] (2)電池のサイクル特性の評価
20°Cの環境下で、上限電圧 4.3V、下限電圧 3.0V、放電電流 50mA、充電電流 50mAの条件で、 50サイクルまで充放電を繰り返し、初期における放電容量と 50サイク ル後の放電容量とから、下記の式：
容量残存率 S = 50サイクル後の放電容量/初期放電容量 X 100 (%) に従って容量残存率 Sを算出し、電池のサイクル特性の指標とした。
[0037] (3)電池の低温特性の評価 (低温放電容量残存率の測定）
20°Cと- 10°Cの環境下で、上限電圧 4.3V、下限電圧 3.0V、放電電流 50mA、充電電 流 50mAの条件で充放電を 5サイクル行レ、、 20°Cと- 10°Cにおいて測定した 5サイクノレ 後の放電容量を比較し、下記の式：
容量残存率 L =
5サイクル後放電容量 (_10°C) /5サイクル後放電容量 (20°C) X 100 (%) に従って容量残存率 Lを算出し、電池の低温特性の指標とした。
[0038] (実施例 2)
実施例 1の非水電解液の調製において、メトキシジフルォロホスフィンオキサイドに 代えてアミノジフルォロホスフィンオキサイド [〇 = PF NH ] 10体積0 /0とした他は、実
2 2
施例 1と同様に非水電解液を調製し、得られた非水電解液の限界酸素指数を測定し た。また、実施例 1と同様にして非水電解液 2次電池を作製し、サイクル特性及び低 温特性をそれぞれ評価した。結果を表 1に示す。
[0039] (実施例 3)
実施例 1の非水電解液の調製において、メトキシジフルォロホスフィンオキサイドに 代えてジァミノフルォロホスフィンオキサイド [0 = PF(NH ) ] 10体積0 /0とした他は、実
2 2
施例 1と同様に非水電解液を調製し、得られた非水電解液の限界酸素指数を測定し た。また、実施例 1と同様にして非水電解液 2次電池を作製し、サイクル特性及び低 温特性をそれぞれ評価した。結果を表 1に示す。
[0040] (比較例 1)
実施例 1の非水電解液の調製において、メトキシジフルォロホスフィンオキサイドに 代えてリン酸トリメチル 10体積％とした他は、実施例 1と同様に非水電解液を調製し、 得られた非水電解液の限界酸素指数を測定した。また、実施例 1と同様にして非水 電解液 2次電池を作製し、サイクル特性及び低温特性をそれぞれ評価した。結果を 表 1に示す。
[0041] 表 1
Figure imgf000011_0001
[0042] 表 1に示すように、分子中に P— F結合及び Z又は P— NH結合を有するホスフィン
2
オキサイド化合物を電解液に添加することにより、非水電解液の限界酸素指数を向 上させることができ、非水電解液の安全性を改善できることが確認された。

Claims

請求の範囲
[1] 分子中に P— F結合及び/又は P— NH結合を有するホスフィンオキサイド化合物
2
と、支持塩とを含むことを特徴とする電池用非水電解液。
[2] 前記ホスフィンオキサイド化合物の含有率が 3体積％以上であることを特徴とする請 求項 1に記載の電池用非水電解液。
[3] 前記ホスフィンオキサイド化合物の含有率が 5体積％以上であることを特徴とする請 求項 2に記載の電池用非水電解液。
[4] 前記ホスフィンオキサイド化合物が下記式 (I) :
Ο=ΡΙ^
3 … (I)
(式中、 R1は、それぞれ独立して一価の置換基又はハロゲン元素であり、少なくとも一 つの R1はフッ素又はアミノ基である）で表されることを特徴とする請求項 1に記載の電 池用非水電解液。
[5] 前記式 (I)中の R1力 それぞれ独立してフッ素、アミノ基、アルキル基及びアルコキシ 基からなる群から選択され、且つ少なくとも一つの R1がフッ素又はアミノ基であること を特徴とする請求項 4に記載の電池用非水電解液。
[6] 前記式 (I)中の R1の少なくとも一つがフッ素で、且つ式 (I)中の R1の少なくとも一つが アミノ基であることを特徴とする請求項 5に記載の電池用非水電解液。
[7] 前記式 (I)中の R1が、それぞれ独立してフッ素又はアミノ基であることを特徴とする請 求項 5に記載の電池用非水電解液。
[8] 更に非プロトン性有機溶媒を含むことを特徴とする請求項 1に記載の電池用非水 電解液。
[9] 前記非プロトン性有機溶媒が、環状若しくは鎖状のエステルイ匕合物又は鎖状のェ 一テル化合物を含むことを特徴とする請求項 8に記載の電池用非水電解液。
[10] 請求項：!〜 9のいずれかに記載の電池用非水電解液と、正極と、負極とを備えた非 水電解液電池。
PCT/JP2005/005920 2004-04-19 2005-03-29 電池用非水電解液及びそれを備えた非水電解液電池 Ceased WO2005104289A1 (ja)