Classifications

• • C—CHEMISTRY; METALLURGY
  • C01—INORGANIC CHEMISTRY
  • C01B—NON-METALLIC ELEMENTS; COMPOUNDS THEREOF; METALLOIDS OR COMPOUNDS THEREOF NOT COVERED BY SUBCLASS C01C
  • C01B33/00—Silicon; Compounds thereof
  • C01B33/113—Silicon oxides; Hydrates thereof
  • C01B33/12—Silica; Hydrates thereof, e.g. lepidoic silicic acid
• • C—CHEMISTRY; METALLURGY
  • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
  • C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
  • C09D183/00—Coating compositions based on macromolecular compounds obtained by reactions forming in the main chain of the macromolecule a linkage containing silicon, with or without sulfur, nitrogen, oxygen, or carbon only; Coating compositions based on derivatives of such polymers
  • C09D183/16—Coating compositions based on macromolecular compounds obtained by reactions forming in the main chain of the macromolecule a linkage containing silicon, with or without sulfur, nitrogen, oxygen, or carbon only; Coating compositions based on derivatives of such polymers in which all the silicon atoms are connected by linkages other than oxygen atoms
• • H10P14/6529—
• • H10P14/6689—
• • H10P14/69215—
• • H10P14/6342—
• • H10P14/665—
• • H10P14/6922—

Definitions

• the present invention relates to a porous silica coating with a low dielectric constant, a semiconductor device comprising the porous silica coating, and a coating composition which becomes the porous silica coating.
• silica coatings are converted into silica coatings by firing in atmospheric air. These silica coatings are used as interlayer dielectrics for semiconductors because of excellent electrical insulating properties. Among these silica coatings, a completely inorganic silica coating has already been employed as an excellent interlayer dielectric for a semiconductor because it has high heat resistance and can be used in a non-etch back process. In this case, the physical properties of the silica coating are similar to those of silicon dioxide (SiO 2 ) and its dielectric constant is within a range from 3.0 to 4.7.
• an object of the present invention to provide a silica coating which makes it possible to drastically reduce the dielectric constant (especially to less than 2.5) and to substantially maintain the reduced dielectric constant under an ambient atmosphere without being subjected to a water repellent treatment.
• Another object of the present invention is to provide a semiconductor device comprising the silica coating with such a low dielectric constant as an interlayer dielectric, and a coating composition which becomes the silica coating.
• a porous silica coating having a dielectric constant of less than 2.5 which is obtained by firing a coating of a composition comprising an aluminum-containing polysilazane and a polyacrylate or polymethacrylate ester.
• a semiconductor device comprising the porous silica coating as an interlayer dielectric.
• a coating composition comprising an aluminum-containing polysilazane and a polyacrylate or polymethacrylate ester in an organic solvent.
• the porous silica coating of the present invention is obtained by firing a coating of a composition comprising an aluminum-containing polysilazane and a polyacrylate or polymethacrylate ester.
• the aluminum-containing polysilazane is obtained by mixing a polysilazane with an aluminum compound.
• the polysilazane as a material for forming the silica coating has in its molecular chain a silazane structure represented by the following general formula (1):
• R 1 , R 2 and R 3 each independently represents a hydrogen atom, a hydrocarbon group, a hydrocarbon group-containing silyl group, a hydrocarbon group-containing amino group, or a hydrocarbonoxy group. At least one of R 1 and R 2 represents a hydrogen atom.
• the hydrocarbon group may be combined with a substituent, and examples of the substituent include halogen such as chlorine, bromine and fluorine, an alkoxy group, an alkoxycarbonyl group, and an amino group.
• the hydrocarbon group includes an aliphatic hydrocarbon group and an aromatic hydrocarbon group, and the aliphatic hydrocarbon group includes a chain hydrocarbon group and a cyclic hydrocarbon group.
• the hydrocarbon group include an alkyl group, an alkenyl group, a cycloalkyl group, a cycloalkenyl group, an aryl group, and an arylalkyl group.
• the number of carbon atoms in these hydrocarbon atoms is not limited, but is usually 20 or less, and preferably 10 or less. In the present invention, preferred is an alkyl group having 1 to 8 carbon atoms, and particularly 1 to 4 carbon atoms.
• a preferable hydrocarbon group is an alkyl group having 1 to 20 carbon atoms, and particularly 1 to 6 carbon atoms.
• the number of hydrocarbon atoms to be combined with Si is within a range from 1 to 3.
• the number of carbon atoms in the hydrocarbon group is within a range from 1 to 3.
• the polysilazane having a silazane structure represented by the general formula (1) in a molecular chain may be a polysilazane having a chain, cyclic or crosslinked structure, or a mixture thereof.
• the number-average molecular weight is within a range from 100 to 100,000, and preferably from 300 to 10,000.
• Such a polysilazane includes conventional perhydropolysilazane, organopolysilazane, and a modified compound thereof.
• modified polysilazane examples include a platinum- or palladium-containing polysilazane, an alcohol residue-containing polysilazane, an HMDS (hexamethyldisilazane) residue-containing polysilazane, an amine-containing polysilazane, and an organic acid-containing polysilazane.
• the aluminum to be incorporated into the polysilazane may be an aluminum compound in the form capable of being dissolved in an organic solvent.
• a soluble aluminum compound includes an alkoxide, a chelete compound, an organoaluminum, and a halide.
• alkoxide of aluminum examples include those represented by the following general formula (2):
• R 4 , R 5 and R 6 represent a hydrocarbon group.
• the hydrocarbon group includes an aliphatic hydrocarbon group and an aromatic hydrocarbon group.
• the aliphatic hydrocarbon group includes a chain hydrocarbon group and a cyclic hydrocarbon group.
• Examples of the aliphatic hydrocarbon group include an alkyl group, an alkenyl group, a cycloalkyl group, and a cycloalkenyl group.
• the number of carbon atoms is not specifically limited, but is usually 20 or less, and preferably 8 or less.
• the aliphatic hydrocarbon group examples include methyl, ethyl, propyl, butyl, pentyl, octyl, dodecyl, octadecyl, dodecenyl, cyclohexyl, and cyclohexenyl.
• the aromatic hydrocarbon group includes an aryl group and an arylalkyl group. Specific examples of the aromatic hydrocarbon group include phenyl, tolyl, xylyl, naphthyl, benzyl, phenethyl, and naphthylmethyl.
• Examples of the chelete compound of aluminum include aluminum acetylacetonate and aluminum ethylacetonate.
• organoaluminum examples include those represented by the following general formula (3):
• R 4 , R 5 and R 6 represent a hydrocarbon group.
• the hydrocarbon group includes those described in connection with the general formula (2).
• halide of aluminum examples include those represented by the following general formula (4):
• X represents a halogen.
• the halogen includes chlorine, bromine, iodine, and fluorine.
• organic solvent-soluble aluminum compounds can be used alone or in combination.
• the amount of the aluminum compound to be added to the polysilazane varies depending on the kind, but is within a range from 0.001 to 10% by weight as aluminum, preferably from 0.01 to 10% by weight, and more preferably from 0.1 to 1% by weight, on the basis of the polysilazane.
• the amount of the aluminum compound is larger than the range described above, the density and homogeneity of the resulting silica coating are lowered. Therefore, it is not preferred.
• the amount is smaller than the range, the effect of the added aluminum compound becomes insufficient.
• a polysilazane and an aluminum compound are mixed with stirring in an organic solvent.
• they are mixed with stirring under the conditions of a temperature within a range from 0 to 200° C., preferably from 0 to 100° C., and a pressure within a range from normal pressure to 10 kg/cm 2 G, preferably normal pressure.
• the concentration of the polysilazane in the organic solvent is within a range from 0.1 to 80% by weight, and preferably from 5 to 50% by weight.
• an inert organic solvent free from active hydrogen is used.
• the organic solvent include an aromatic hydrocarbon solvent such as benzene, toluene, xylene, ethylbenzene, diethylbenzene, trimethylbenzene, or triethylbenzene; an alicyclic hydrocarbon solvent such as cyclohexane, cyclohexene, decahydronaphthalene, ethylcyclohexane, methylcyclohexane, p-menthine, or dipentene (limonene); an ether solvent such as dipropyl ether or dibutyl ether; and a ketone solvent such as methyl isobutyl ketone.
• An aluminum-containing polysilazane in which an aluminum compound is mixed or added, is formed by mixing the polysilazane and the aluminum compound with stirring in the organic solvent.
• the resulting aluminum-containing polysilazane does not have an aluminopolysilazane structure wherein aluminum and silicon are firmly combined.
• the coating composition of the present invention is obtained by adding a polyacrylate or polymethacrylate ester to an organic solvent solution containing the aluminum-containing polysilazane thus obtained.
• the polyacrylate or polymethacrylate ester which is useful in the present invention, is a homopolymer or copolymer of a polyacrylate or polymethacrylate ester, and specific examples thereof include polymethyl acrylate, polyethyl acrylate, polybutyl acrylate, polymethyl methacrylate, polyethyl methacrylate, polybutyl methacrylate, polyisobutyl methacrylate, and block copolymers and other copolymers thereof.
• the polyacrylate or polymethacrylate ester in the present invention those having a number-average molecular weight within a range from 1,000 to 800,000 are used.
• the number-average molecular weight is smaller than 1,000, a porous coating is not formed because the polyacrylate or polymethacrylate ester is sublimated at low temperature.
• the number-average molecular weight exceeds 800,000, the pore size increases to cause voids, thus reducing the coating strength. Therefore, both cases are not preferred.
• the number-average molecular weight of the-polyacrylate or polymethacrylate ester in the present invention is preferably within a range from 10,000 to 600,00, and particularly preferred results are obtained when the number-average molecular weight is within a range from 50,000 to 300,000.
• the amount of the polyacrylate or polymethacrylate ester in the present invention is controlled within a range from 5 to 150% by weight based on the polysilazane used.
• the amount of the polyacrylate or polymethacrylate ester is smaller than 5% by weight, the coating is insufficiently made porous.
• the amount is larger than 150% by weight, defects such as voids and cracks occur, thereby to reduce the coating strength. Therefore, it is not preferred.
• the amount of the polyacrylate or polymethacrylate ester in the present invention is preferably within a range from 10 to 120% by weight, and particularly preferred results are obtained when the amount is within a range from 20 to 100% by weight.
• the polyacrylate or polymethacrylate ester is generally added to an aluminum-containing polysilazane solution in the form of a solution prepared by dissolving the polyester in an organic solvent.
• the same organic solvent as that used in preparation of the aluminum-containing polysilazane solution may be used as the organic solvent.
• an inert organic solvent free from active hydrogen described above is used as the organic solvent in which the polyacrylate or polymethacrylate ester is dissolved.
• the concentration of the polyacrylate or polymethacrylate ester can be controlled within a range from 5 to 80% by weight, and preferably from 10 to 40% by weight.
• a homogeneous solution can be obtained by physically stirring after the addition of the polyacrylate or polymethacrylate ester.
• the polyacrylate or polymethacrylate ester itself can also be added and dissolved in the aluminum-containing polysilazane solution.
• the coating composition of the present invention can be prepared by combining the polysilazane with the polyacrylate or polymethacrylate ester and mixing the aluminum compound therewith, or combining the polyacrylate or polymethacrylate ester with the aluminum compound and mixing the polysilazane therewith.
• the resulting organic solvent solution containing the aluminum-containing polysilazane and the polyacrylate or polymethacrylate ester can be coated on the surface of a substrate by using it as a coating composition with or without controlling the concentration of the polysilazane.
• Examples of the method of coating the coating composition containing the aluminum-containing polysilazane and the polyacrylate or polymethacrylate ester to the surface of the substrate include conventionally known methods, for example, spin coating method, dipping method, spraying method, and transferring method.
• the aluminum-containing polysilazane coating formed on the surface of the substrate is fired in various atmospheres.
• the atmosphere includes, for example, an atmosphere which scarcely contains water vapor, such as dry air, dry nitrogen, or dry helium, or an atmosphere containing water vapor, such as atmospheric air, moistened atmospheric air, or moistened nitrogen.
• the firing temperature is within a range from 50 to 600° C., and preferably from 300 to 500° C., and the firing time is within a range from one minute to one hour.
• a silica coating having a low dielectric constant and a good coating quality is advantageously prepared by forming a polysilazane coating on the surface of a substrate, preliminary heating the coating in a water vapor-containing atmosphere and firing the coating with heating in a dry atmosphere.
• the water vapor content in the water vapor-containing atmosphere, is 0.1 volume % or more, and preferably 1 volume % or more.
• the upper limit value is the dew point. Examples of such an atmosphere include atmospheric air, moistened atmospheric air, and moistened nitrogen gas.
• the water vapor content is 0.5 volume % or less, and preferably 0.05 volume % or less.
• dry atmosphere examples include dry air, nitrogen gas, argon gas, and helium gas.
• the preliminary heating temperature is within a range from 50 to 400° C., and preferably from 100 to 350° C.
• the firing temperature is within a range from 100 to 500° C., and preferably from 300 to 500° C.
• Si—H, Si—R (R: hydrocarbon group) and Si—N bonds in the polysilazane are oxidized and converted into Si—O bonds to form a silica coating.
• a Si—OH bond is not substantially formed.
• Si—H, Si—R and Si—N bonds are oxidized nearly simultaneously, although it varies depending on the conditions of firing. This fact is confirmed from the fact that absorptions based on Si—H, Si—R and Si—N disappear nearly simultaneously when the IR spectrum of the resulting silica coating is measured.
• the present invention allows the Si—O bond formed by selectively oxidizing the Si—N bond, and the unoxidized Si—H and Si—R bonds, to exist in the formed silica coating, thereby making it possible to obtain a silica coating with a low density.
• the dielectric constant of the silica coating is reduced with the reduction of the coating density, while adsorption of water as a high dielectric substance occurs when the coating density is reduced. Therefore, there arises a problem that the dielectric constant increases when the silica coating is left to stand in an atmospheric air.
• the silica coating containing Si—H and Si—R bonds of the present invention adsorption of water can be prevented regardless of low density because these bonds have water repellency.
• the silica coating of the present invention has a large merit that the dielectric constant of the coating scarcely increases even if the silica coating is left to stand in an atmospheric air containing water vapor.
• the silica coating of the present invention also has a merit that it is less likely to cause cracking because the internal stress of the coating is small due to low density.
• micropores having a diameter of 0.5 to 30 nm are formed in the silica coating by sublimation of the polyacrylate of polymethacrylate ester in the coating.
• the existence of the micropores further reduces the density of the silica coating, and thus the dielectric constant of the silica coating is further reduced. This is because the compatibility between the aluminum-containing polysilazane and the polyacrylate of polymethacrylate ester is very good.
• the use of the polyacrylate of polymethacrylate ester prevents the Si—OH bond from forming in the polysilazane during the firing of the coating.
• the silica coating maintains the water repellency and the dielectric constant reduced due to the micropores scarcely increases even when left to stand in an atmospheric air containing water vapor.
• a porous silica coating capable of stably maintaining a very low dielectric constant of less than 2.5, preferably 2.0 or less, occasionally about 1.6, in cooperation with the reduction in density and impartation of water repellency due to the bond component (SiH, SiR) of the silica coating as well as reduction in density of the whole coating due to micropores. Therefore, since a water repellent treatment required to prevent moisture absorption in a conventional porous silica coating is not required, it becomes advantageous in view of the manufacturing cost and an inorganic material's merit is not impaired by introduction of an organic group.
• the density is within a range from 0.5 to 1.4 g/cm 3 , and preferably from 0.7 to 1.1 g/cm 3
• the cracking limitation in coating thickness is 1.0 ⁇ m or more, and preferably 10 ⁇ m or more and, furthermore, the internal stress is 2.0 ⁇ 10 4 N/cm 2 or less, and preferably 1.0 ⁇ 10 4 N/cm 2 or less.
• the content of Si, which exists in the form of a Si—H or Si—R bond (R: hydrocarbon group), in the silica coating is within a range from 10 to 100 atomic %, and preferably from 25 to 75 atomic %, based on the number of Si atoms contained in the silica porous coating.
• the content of Si, which exists in the form of a Si—N bond, is 5 atomic % or less.
• the thickness of the silica coating obtained after firing varies depending on the purposes of the substrate surface, but is usually within a range from 0.01 to 5 ⁇ m, and preferably from 0.1 to 2 ⁇ m. When using as an interlayer dielectric, the thickness is within a range from 0.1 to 2 ⁇ m.
• the present invention when using perhydropolysilazane having no hydrocarbon group as the polysilazane, it is made possible to obtain an inorganic coating with a low dielectric constant, which is composed only of elements of Si, O and H and has a Si—H bond but substantially has neither an N—H bond nor a Si—OH bond. Since this coating is superior in resistance to plasma, a so-called etch-back process of removing a coating layer on the metal wiring in a process of manufacturing a semiconductor can be omitted by applying this coating in the manufacture of the semiconductor. Therefore, the process of manufacturing the semiconductor can be markedly simplified.
• the porous silica coating of the present invention has a low density and has a merit that a cracking limitation in coating thickness, namely, a maximum coating thickness where a coating can be formed without causing cracking of the coating is 5 ⁇ m or more.
• a cracking limitation in coating thickness is within a range from about 0.5 to 1.5 ⁇ m. Therefore, the silica coating of the present invention exhibits a large technical effect as compared with a conventional silica coating.
• the method of forming the silica coating of the present invention can be carried out very easily because the aluminum-containing polysilazane, as a precursor thereof, can be converted into a silica coating at a firing temperature lower than 450° C. even in a dry atmospheric air by a catalytic action of aluminum.
• the present invention is advantageously applied as a method of forming an insulating coating to an aluminum wiring whose heat-resistant upper limit temperature is 450° C.
• the content of the Si—N bond can be substantially reduced to 0% by a catalytic action of aluminum, the coating has very high stability and is not deteriorated even when left to stand in atmospheric air.
• the silica coating of the present invention can be advantageously used as an interlayer dielectric in a semiconductor device.
• the silica coating is formed on the plane including a metal wiring, or a metal wiring with a ceramic coating.
• the semiconductor device including the silica coating of the present invention is not only superior in insulating properties, but also in electric characteristics because of small dielectric constant.
• a silica coating can be formed on the solid surface of various materials such as metal, ceramics or lumber by using the coating composition of the present invention.
• a metal substrate silicon, stainless steel (SUS), tungsten, iron, copper, zinc, brass, or aluminum
• a ceramics substrate metal oxide such as silica, alumina, magnesium oxide, titanium oxide, zinc oxide and tantalum oxide, metal nitride such as silicon nitride, boron nitride and titanium nitride, or silicon carbide
• the method of evaluating physical properties of the silica coating is as follows.
• the resulting polysilazane coating (about 3 mm ⁇ 3 mm in size) was removed by rubbing, with a rod applicator, four corners of the glass plate to form portions for taking electric signals.
• the polysilazane coating was converted into a silica coating in accordance with the method of the Examples or Comparative Examples.
• the resulting silica coating was covered with a mask of SUS and an Al coating was formed by a vacuum deposition method (18 patterns in the form of square of 2 mm ⁇ 2 mm, 2 ⁇ m in thickness).
• a capacitance was measured by an impedance analyzer 4192 ALF manufactured by YHP Inc. (100 kHz).
• the thickness of the coating was measured by a profilometer (Dektak IIA manufactured by Sloan Inc.).
• the dielectric constant was calculated by the following equation.
• Dielectric constant (Capacitance [ pF ]) ⁇ (Coating thickness [ ⁇ m ])/35.4
• the dielectric constant was determined by calculating an average of 18 measured values.
• Coating density [ g/cm 3 ] (Coating weight [ g ]) ⁇ (Coating thickness [ ⁇ m ])/0.008.
• the resulting polysilazane coating was converted into a silica coating in accordance with the method of the Examples or Comparative Examples.
• Samples having coating different thicknesses within a range from about 0.5 to 3 ⁇ were made by controlling the polysilazane concentration of the polysilazane solution or the rotational speed of a spin coater.
• the fired thin coating was observed by a microscope (magnification: ⁇ 120) and it was examined whether or not cracking occurred. A maximum coating thickness where no cracking occurs was taken as a cracking limitation in coating thickness.
• a four-necked flask having an internal volume of 2 L was equipped with a gas bubbling tube, a mechanical scaler and a Dewar condenser. After replacing the atmosphere of a reaction vessel by dry nitrogen, 1500 ml of dry pyridine was charged in the four-necked flask and then ice-cooled. 100 g of dichlorosilane was added to produce an adduct as a white solid (SiH 2 Cl 2 2C 5 H 5 N). The reaction mixture was ice-cooled and 70 g of ammonia was bubbled into the reaction mixture while stirring. Subsequently, dry nitrogen was bubbled into the aqueous layer for 30 minutes to remove excess ammonia.
• the number-average molecular weight of the resulting perhydropolysilazane was measured by GPC (developing solution: CDCl 3 ). As a result, it was 800 calibrated with polystyrene standards.
• An IR (infrared absorption) spectrum showed absorptions based on N—H at a wave number of approximately 3350 and 1200 cm ⁇ 1 , an absorption based on Si—H at 2170 cm ⁇ 1 , and an absorption based on Si—N—Si at 1020 to 820 cm
• the coating had a dielectric constant of 4.2, a density of 1.8 g/cm 3 , an internal stress of 1.2 ⁇ 10 4 N/cm 2 , and a cracking limitation in coating thickness of 2.2 ⁇ m.
• the resulting coating was left to stand in an atmospheric air under the conditions of a temperature of 23° C. and a relative humidity of 50% for a week and the dielectric constant was measured again. As a result, it was 4.8.
• the silicon plate coated with polysilazane was heated on a hot plate at 100° C., then at 200° C. in an atmospheric air (25° C., relative humidity: 40%) for each 3 minutes.
• the heated silicon plate was fired in a dry nitrogen atmosphere at 400° C. for one hour. Absorptions based on Si—O at a wave number of 1070 and 450 cm ⁇ 1 and absorptions based on Si—H at a wave number of 2250 and 880 cm ⁇ 1 were mainly observed, while absorptions based on N—H at a wave number of 3350 and 1200 cm ⁇ 1 nearly disappeared.
• the resulting coating was evaluated.
• the coating had a dielectric constant of 3.0, a density of 2.9 g/cm 3 , an internal stress of 1.2 ⁇ 10 4 N/cm 2 , and a cracking limitation in coating thickness of 1.4 ⁇ m.
• the resulting coating was left to stand in an atmospheric air under the conditions of a temperature of 23° C. and a relative humidity of 50% for a week and the dielectric constant was measured again. As a result, it was 3.2.
• the filtered solution was coated on a silicon wafer, 4 inch in diameter and 0.5 mm in thickness, using a spin coater (1500 rpm, 20 seconds), and then dried at room temperature (10 minutes).
• the silicon plate coated with polysilazane was heated on a hot plate at 150° C., then at 220° C. in an atmospheric air (25° C., relative humidity: 40%) each for 3 minutes.
• the heated silicon plate was fired in a dry nitrogen atmosphere at 400° C. for one hour.
• the mixed solution was filtered through a PTFE syringe filter having a filtration accuracy of 0.2 ⁇ m manufactured by Advantech Co., Ltd.
• the filtered solution was coated on a silicon wafer of 4 inch in diameter and 0.5 mm in thickness using a spin coater (2000 rpm, 20 seconds), and then dried at room temperature (5 minutes).
• the silicon plate coated with polysilazane was heated on a hot plate at 150° C., then at 220° C. in an atmospheric air (25° C., relative humidity: 40%) for each 3 minutes.
• the heated silicon plate was fired in a dry nitrogen atmosphere at 400° C. for 30 minutes.
• the mixed solution was filtered through a PTFE syringe filter having a filtration accuracy of 0.2 ⁇ m manufactured by Advantech Co., Ltd.
• the filtered solution was coated on a silicon wafer, 4 inch in diameter and 0.5 mm in thickness, using a spin coater (2000 rpm, 20 seconds), and then dried at room temperature (5 minutes).
• the silicon plate coated with polysilazane was heated on a hot plate at 150° C., then at 220° C. in an atmospheric air (25° C., relative humidity: 40%) for each 3 minutes.
• the heated silicon plate was fired in a dry nitrogen atmosphere at 400° C. for 30 minutes.
• the mixed solution was filtered through a PTFE syringe filter having a filtration accuracy of 0.2 ⁇ m manufactured by Advantech Co., Ltd.
• the filtered solution was coated on a silicon wafer, 4 inch in diameter and 0.5 mm in thickness, using a spin coater (2000 rpm, 20 seconds), and then dried at room temperature (5 minutes).
• the silicon plate coated with polysilazane was heated on a hot plate at 150° C., then at 220° C. in an atmospheric air (25° C., relative humidity: 40%) for each 3 minutes.
• the heated silicon plate was fired in a dry nitrogen atmosphere at 400° C. for 30 minutes.
• the mixed solution was filtered through a PTFE syringe filter having a filtration accuracy of 0.2 ⁇ m manufactured by Advantech Co., Ltd.
• the filtered solution was coated on a silicon wafer, 4 inch in diameter and 0.5 mm in thickness, using a spin coater (2000 rpm, 20 seconds), and then dried at room temperature (5 minutes).
• the silicon plate coated with polysilazane was heated on a hot plate at 150° C., 220° C., then at 300° C. in an atmospheric air (25° C., relative humidity: 40%) for each 3 minutes.
• the heated silicon plate was fired in a dry nitrogen atmosphere at 400° C. for 30 minutes.
• the mixed solution was filtered through a PTFE syringe filter having a filtration accuracy of 0.2 ⁇ m manufactured by Advantech Co., Ltd.
• the filtered solution was coated on a silicon wafer, 4 inch in diameter and 0.5 mm in thickness, using a spin coater (2000 rpm, 20 seconds), and then dried at room temperature (5 minutes).
• the silicon plate coated with polysilazane was heated on a hot plate at 150° C., then at 220° C. in an atmospheric air (25° C., relative humidity: 40%) for each 3 minutes.
• the heated silicon plate was fired in a dry nitrogen atmosphere at 400° C. for 30 minutes.
• the porous silica coating of the present invention has a low density and a low dielectric constant of less than 2.5, in addition to the chemical resistance, gas/ion barrier properties, wear resistance, heat resistance and flattening properties which are inherent in a silica coating derived from a polysilazane.
• This porous silica coating scarcely adsorbs water vapor even when left to stand in an atmospheric air because it contains a hydrophobic Si—H bond and, therefore, the dielectric constant is less likely to increase.
• the porous silica coating of the present invention has a feature that it has small coating stress and high coating thickness limitation. Accordingly, the porous silica coating of the present invention is suited for use as an interlayer dielectric in semiconductors.
• the porous silica coating of the present invention is preferably used as the interlayer dielectric in semiconductors, and is also advantageously used as an insulating coating in the electrical and electronic fields, such as under coating (insulating flattened coating) of liquid crystal glass and gas barrier coating of film liquid crystal.
• the method of forming a porous silica coating of the present invention can be applied as, for example, a hard coating onto the surface of a solid such as metal, glass, plastic or lumber, heat-resistant coating, acid-resistant coating, stainproof coating, and water repellent coating. It can also be applied as gas barrier coating onto a plastic film, UV cut coating onto a glass, plastic or lumber, and a coloring coating.
• the coating composition can be applied as UV cut coating, coloring coating and antibacterial coating because various functional fillers can be added.
• the porous silica coating of the present invention is advantageous in view of the manufacturing cost because it is not required to be subjected to a water repellent treatment for prevention of moisture absorption and, moreover, an inorganic material's merit is not impaired by the introduction of the organic group.

Landscapes

• Chemical & Material Sciences (AREA)
• Organic Chemistry (AREA)
• Chemical Kinetics & Catalysis (AREA)
• Life Sciences & Earth Sciences (AREA)
• Engineering & Computer Science (AREA)
• Materials Engineering (AREA)
• Wood Science & Technology (AREA)
• Inorganic Chemistry (AREA)
• Formation Of Insulating Films (AREA)
• Paints Or Removers (AREA)
• Silicon Compounds (AREA)

Priority Applications (1)

Applications Claiming Priority (2)

Related Parent Applications (1)

Related Child Applications (1)

Publications (1)

Family

ID=16405213

Family Applications (2)

Family Applications After (1)

Country Status (8)

Cited By (9)

Families Citing this family (14)

Family Cites Families (14)

• 1999
  • 1999-07-13 JP JP19928299A patent/JP4408994B2/ja not_active Expired - Fee Related
• 2000
  • 2000-06-20 CN CNB008102120A patent/CN1196649C/zh not_active Expired - Fee Related
  • 2000-06-20 DE DE60014694T patent/DE60014694T2/de not_active Expired - Lifetime
  • 2000-06-20 EP EP00937325A patent/EP1232998B1/en not_active Expired - Lifetime
  • 2000-06-20 WO PCT/JP2000/004021 patent/WO2001004049A1/ja not_active Ceased
  • 2000-06-20 TW TW089112096A patent/TW593139B/zh not_active IP Right Cessation
  • 2000-06-20 KR KR1020027000406A patent/KR100727277B1/ko not_active Expired - Fee Related
• 2001
  • 2001-01-19 US US10/009,735 patent/US20030099843A1/en not_active Abandoned
• 2003
  • 2003-02-24 US US10/370,588 patent/US6746714B2/en not_active Expired - Lifetime