TWI612065B - 接枝於金屬氧化物表面的聚合物，將聚合物接枝至金屬氧化物表面的方法，及適用於該方法的接枝聚合物 - Google Patents
接枝於金屬氧化物表面的聚合物，將聚合物接枝至金屬氧化物表面的方法，及適用於該方法的接枝聚合物 Download PDFInfo
- Publication number
- TWI612065B TWI612065B TW105117527A TW105117527A TWI612065B TW I612065 B TWI612065 B TW I612065B TW 105117527 A TW105117527 A TW 105117527A TW 105117527 A TW105117527 A TW 105117527A TW I612065 B TWI612065 B TW I612065B
- Authority
- TW
- Taiwan
- Prior art keywords
- metal oxide
- polymer
- polymers
- group
- configuration
- Prior art date
Abstract
金屬氧化物具有一表面，複數個獨立的聚合物接枝於表面上，每一聚合物包含添加聚合物以及第一部分，添加聚合物聚有第一與第二端，第一部分包含終端磷酸基，使第一部分鍵結於第一端，並且磷酸基附著於金屬氧化物表面，並且複數個接枝的聚合物包含至少一個群體之相鄰聚合物，相鄰聚合物聚有可拉伸的鍵狀構型，其中相鄰的可拉伸鍵狀構型具有幾乎平行的方向性，使存在於群體之聚合物共同形成刷子狀構型。接枝複數個獨立的聚合物至金屬氧化物表面的方法。
Description
本發明第一層面是關於一種具有多個獨立聚合物接枝於表面的金屬氧化物。每一聚合物包含添加聚合物，該添加聚合物具有第一端與第二端，以及第一部分，第一部分包含終端連接基團，使第一部分鍵結於第一端，並藉由終端連接基團接觸金屬氧化物表面使第一端與金屬氧化物表面連接。第二層面，本發明是關於一種接枝聚合物至金屬氧化物表面的方法。第三層面，本發明是關於一種適用於前述方法的接枝聚合物。
接枝聚合物於金屬氧化物表面，用以提供金屬氧化物表面，不同於金屬氧化物本身的新功能性，為本領域中常用的手段。
舉例來說，金屬氧化物表面具有強大極性的官能基團，可以被具有有機化合物特性的接枝聚合物包圍，在金屬氧化物表面形成非極性之特性。
為了拿到隔離的效果，聚合物於金屬氧化物表面的覆蓋範圍，需要達到足以使原有的金屬氧化物表面的特性不足以影響最外圍的聚合物覆蓋層之特性。
基本上，習知有兩個方法來使聚合物附著於金屬氧化物表面：「接枝至」(grafting onto)與「接枝自」(grafting from)。「接枝至」技術是先將聚合物形成好後，再將置於溶液中的聚合物套用到金屬氧化物表面，以使聚合物之終端基團能附著於金屬氧化物表面。「接枝自」技術是先形成包含終端連接基團的前驅聚合物後，將於溶液中的前驅聚合物套用於金屬氧化物表面，以使終端連接基團附著於金屬氧化物表面，接著聚合物自前驅聚合物長出，直到形成所需的長度。
當使用一種終端連接基團，例如羧基，來進行接枝，上述兩種方法可以造成不同的結果。「接枝至」技術使用先形成好的聚合物，因此在溶液中會隨機形成盤繞的線團構型，而在終端連接基團附著於金屬氧化物表面的過程中，聚合物鏈會保持盤繞的線團構型。另一方面，「接枝自」技術被發現，相鄰的兩聚合物之間能具有較小的距離，並且聚合物自連接的前驅聚合物長出，因此具有可拉伸的鍵狀構型。上述的複數個聚合物都具有自由終端，並且匹此間相互平行，共同形成刷子狀構型。
由於「接枝自」技術中產生的上述刷子狀構型，幾乎完整覆蓋、保護、隔離原有的金屬氧化物表面，因此對於增加新的功能性於金屬氧化物表面而言，刷子狀構型扮演很重要的角色。但目前遇到的課題是，「接枝自」技術相較於「接枝至」技術來的複雜，且成本相對昂貴。
因此，本發明的課題在於開發一種「接枝至」技術，能產生具有刷子狀構型的接枝聚合物於金屬氧化物表面，以使金屬氧化物表面產生效果佳的新功能性。
在本發明以下的說明中，字詞『接枝至』意義包含「由接枝至技術獲得」的表現型。
為能達到上述目的，本發明是關於一金屬氧化物，其具有複數個之獨立的聚合物接枝至金屬氧化物表面，每一聚合物包含添加聚合物以及第一部分，添加聚合物具有第一端與第二端，第一部分包含終端磷酸基，使第一部分與第一端鍵結，磷酸基附著於金屬氧化物表面，上述複數個接枝聚合物包含至少一群體之相鄰聚合物，相鄰聚合物具有可拉伸的鏈狀構型，其中相鄰之可拉伸的鏈狀構型具有實質上相互平行之方向性，使該些群體內之聚合物共同形成刷子狀構型。
本發明使用磷酸基作為接枝聚合物的終端連接基團，以完成與金屬氧化物表面的連接。利用磷酸基做為接枝聚合物的終端連接基團，已於Basuki et al. inMacromolecules, 46, 7043-7054, ACS Publications 2013
中有敘述，其中10奈米的超順磁性氧化鐵奈米粒子(super-paramagnetic iron oxide nanoparticles) 被嵌段共聚物(block copolymer) 接枝。在接枝聚合物的自由終端之間，存在的大的間隔空間，可以用來包覆、封裝離子染料。這些特別的奈米粒子被應用於生物醫學的相關研究。由於他們相對小的尺寸以及相對小的球體構型，本案所包含與應用的上述奈米粒子，在習知技術中被認為本質上不適合用來形成刷子狀構型。
更明確的來說，本發明之金屬氧化物具有，一群體之聚合物形成刷子狀構型，並被接枝至非球面的金屬氧化物表面，的技術特徵。因相鄰之接枝聚合物的自由終端彼此間有限的距離，或多或少相等於連接磷酸基團之間的距離，因此此種表面(如平面或是近似平面的表面)可促使可拉伸的鏈狀構型形成。
本案之金屬氧化物包含多種不同之金屬，如鈦、鐵、釩、鈰、鎢、銅或銻。
較佳地，本發明之金屬氧化物具有反磁性的特性(diamagnetic)。以接枝金屬氧化物表面之應用領域來看，此特徵是具有優勢的，如同一般習知會避免使表面具有順磁性的特性。更佳地，本發明之金屬氧化物為二氧化鈦。
依據本發明之一較佳實施例之金屬氧化物，上述群體之聚合物形成一刷子狀構型，並且於金屬氧化物表面的任兩相鄰之聚合物之間具有平均距離D，其中D/2小於獨立的接枝聚合物可以隨機形成的盤繞線團構型的平均旋轉半徑Rg。本案發明人還發現，上述限定之數值範圍可進一步促進接枝聚合物之上述可拉伸的鏈狀構型的形成。
再者，較佳地，本發明之金屬氧化物中的接枝聚合物，其具有較小的多分散性指數 (或稱聚合度分佈性指數，polydispersity index，簡稱PDI)，多分散性指數是重量平均分子量(Mw)之比值，同時也是數目平均分子量(Mn)。本發明之金屬氧化物中的接枝聚合物的PDI值介於1與2之間，且較佳為介於1與1.5之間。此種接枝聚合物具有相對一致大小的自由終端，能提升所形成的刷子狀構型的品質。
更佳地，本案的金屬氧化物中，每一接枝聚合物具有第二部分，其包含一脂肪族終端基團，第二部分藉由硫羰基(-SC(=S)-)與第二端鍵結，並且較佳藉由三硫代碳酸基(-SC(=S)S-)。上述的硫代基(thio-group)是通稱的RAFT (reversible addition fragmentation chain transfer)反應物的主要特徵，RAFT反應物可以促使可逆加成斷裂鏈轉移(reversible addition fragmentation chain transfer)反應的進行。RAFT反應物可以做為一個前驅聚合物分子，使硫代基旁的得以形成、長出聚合物鏈。進一步而言，RAFT反應物能控制聚合反應的程度，因此所形成的聚合物鏈可以具有相對小的多分散性。具體來說，上述脂肪族終端基團較佳為選自正丁基~十二烷基的直線狀基團。
更佳地，本發明的金屬氧化物中，上述添加聚合物包含：一直鏈狀碳原子，較佳包含10~50個碳原子。此碳鏈長度可以使該添加聚合物，在形成相對於金屬氧化物表面新的功能性時，可以有效的適應成為可拉伸的構型。
在本發明的金屬氧化物中，較佳地，添加聚合物為聚苯乙烯、聚異戊二烯、聚丙烯腈、聚丙烯酸酯、聚甲基丙烯酸酯、ABS、SAN或其組合。ABS與SAN皆為共聚物，分別代表丙烯腈-丁二烯-苯乙烯共聚物 (acrylonitrile butadiene styrene)與苯乙烯-丙烯晴共聚物(styrene acrylonitrile)。
本發明中，其他適合作為添加聚合物的聚合物為：聚乙烯、聚丙烯、聚氯乙烯、聚醋酸乙烯酯、丙烯酸聚合物、聚甲基丙烯酸甲酯、HEMA與氰基丙烯酸聚合物、聚甲基丙烯酸酯與聚乙烯丙烯酸酯、氟化聚合物(如聚四氟乙烯、氟橡膠(fluoroelastomers)、聚氟乙烯與聚偏二氟乙烯)、二烯聚合物(如聚丁二烯與聚異戊二烯)、聚氯丁烯。上述化合物的任一組合同樣也包含於本發明的實施例中，做為添加聚合物。
於較佳實施例中，本發明的金屬氧化物中，磷酸基團中的磷原子P藉由羧基與第一端鍵結，且較佳藉由亞甲基羧基團(P-CH2
-O(O=)C-)。具體地，羧基較佳藉由-C(CH3
)(CH3
)- 來與第一端鍵結。此種磷酸基與第一端的共價鍵被發現能使本發明成功獲得所欲之功能。
具體來說，本發明較佳實施例中，該金屬氧化物為顆粒型態，並且較佳介於20~200奈米。落在這範圍內的尺寸大小可具有足夠的表面積，使刷子狀構形的接枝聚合物形成至金屬氧化物表面。本發明揭示的尺寸範圍，部分落在IUPAC定義的奈米粒子(100奈米以下)的範圍中，同時有部分範圍是大於奈米粒子定義。本發明之奈米粒子較佳為金紅石(二氧化鈦結晶)，其具有四角形的(tetragonal)、複正方的(ditetragonal)或雙椎面的(dipyramidal) 結晶對稱性。
本發明的另一實施例是關於一金屬氧化物，其中金屬氧化物為肉眼可見之片狀構型，而接枝聚合物可做為覆蓋層。接枝聚合物接枝至金屬氧化物表面，覆蓋並提供保護，抵擋環境對金屬氧化物產生的不良影響，包含抵擋侵蝕的發生。另一方面，聚合物接枝至金屬氧化物表面，可做為底層，以使塗層可以形成於其上。相較於沒有接枝聚合物底層、直接進行塗層於金屬氧化物表面的情況，塗層能較好的附著於金屬氧化物表面。
因此，第一層面而言，本發明係是關於一種聚合物材料，包含聚合物介質，使大量之本發明較佳實施例之上述金屬氧化物粒子分散，其中較佳地，聚合物介質與接枝至金屬氧化物的聚合物相容、共存，並且更佳地，聚合物介質與接枝聚合物中的聚合物相同。
本發明較佳實施例為關於一種介電物質，其包含如同上第一層面所述的聚合物材料，並且具有相對介電常數(relative permittivity) εr
大於或等於3，較佳介於5~30之間，或更佳介於10~20之間。本發明之介電物質具有實質上相較於聚合物介質本身較高的介電常數，因此能用以製作較小尺寸之介電物質以用於電子設備(例如天線)中之優勢。
舉例來說，該介電物質之製作方法，是藉由直接混合金屬氧化物粒子與聚合物介質於複合機(compounding machine)中，或著藉由將粒子懸浮於包含聚合物介質的溶液中而來。
第二層面來說，本發明是關於一種接枝方法，用於接枝複數個獨立的聚合物至金屬氧化物表面，其中每一聚合物包含添加聚合物與第一部分，添加聚合物具有第一端與第二端，第一部分包含磷酸終端基團，藉以使第一終端鍵結於第一端，上述方法包含：溶解上述獨立的聚合物於適合溶劑中；將所形成之溶液套用於金屬氧化物表面；使獨立的聚合物附著金屬氧化物表面，其中磷酸終端基團附著於金屬氧化物表面，以形成複數個接枝聚合物於金屬氧化物表面，並且複數個接枝聚合物包含至少一個群體且彼此相鄰的相鄰聚合物，相鄰聚合物具有可拉伸的鏈狀構型，其中可拉伸的鏈狀構型彼此相鄰且具有實質上相互平行的方向性，使於上述群體中之接枝聚合物共同形成刷子狀構型。在接枝聚合物附著於金屬氧化物表面後，將溶劑蒸發以乾燥金屬氧化物表面。當金屬氧化物為粒子的狀況下，可以利用離心機加以乾燥金屬氧化物粒子表面。
如同上說明，以本發明的第一層面來說，習知之接枝聚合物於金屬氧化物表面之方法所產生的接枝聚合物，由於會隨機形成盤繞的線圈構型之缺點，因此無法得到如本發明中，由相鄰的接枝聚合物共同形成的刷子狀構型。而本發明藉由各獨立的聚合物所包含的磷酸終端基團，藉由基團附著於金屬氧化物表面，因此可以獲得具有可拉伸的構型，使這些彼此相鄰的接枝聚合物，共同形成刷子狀構型。
較佳的實施例中，本發明提供的方法除包含如上第一層面所述之特性，尤其還包含：形成刷子狀結構之上述群體族群之聚合物被接枝至非球型之金屬氧化物表面；金屬氧化物為反磁性，且較佳為二氧化鈦。
依據本發明提供的方法，較佳的實施例中，在金屬氧化物表面形成刷子狀構型的聚合物群體中，相鄰之聚合物之間具有平均距離D，其中D/2小於獨立的接枝聚合物隨機形成的盤繞線圈狀構型的平均旋轉半徑Rg。
於本發明之更佳實施例中，上述方法包含下列任一或其組合之特徵：接枝聚合物具有小的多分散性指數，多分散性指數是重量平均分子量(Mw)之比值，也是數目平均分子量(Mn)，此PDI值較佳介於1與2之間，且更佳為介於1與1.5之間；每一接枝聚合物包含第二部分，第二部分包含脂肪族終端基團，第二部分藉由硫羰基(-SC(=S)-)與第二端鍵結，並且較佳藉由三硫代碳酸基(-SC(=S)S-)來與第二端鍵結；添加聚合物包含直鏈狀碳鏈，較佳包含10~50個碳原子；脂肪族終端基團為線狀烷基基團，選自正丁基~正十二烷基；添加聚合物為聚苯乙烯、聚異戊二烯、聚丙烯腈、聚丙烯酸酯、聚甲基丙烯酸酯、ABS、SAN或其組合，其他適合作為添加聚合物的聚合物或聚合物組合如同上，於本案第一層面之內容所述；磷酸基團中的磷原子P藉由羧基與第一端鍵結，較佳地藉由亞甲基羧基團(P-CH2
-O(O=)C-)與第一端鍵結；羧基藉由-C(CH3
)(CH3
)-與第一端鍵結；以及金屬氧化物為顆粒型態，並且較佳介於20~200奈米，尤其奈米粒子較佳為金紅石(二氧化鈦結晶)，其具有四角形的(tetragonal)、複正方的(ditetragonal)、雙椎面的(dipyramidal)結晶對稱性。
於第三層面來說，本發明是關於一種接枝聚合物，適合用於如上述本發明之第二層面之方法來接枝至金屬氧化物表面，其中聚合物包含直鏈狀之聚乙烯鏈以及第一部分，聚乙烯鏈具有第一端與第二端，第一部分具有磷酸終端基團，藉以將第一部分與第一端鍵結。其中聚合物還具有第二部分，包含脂肪族終端基團，第二部分藉由硫羰基(-SC(=S)-)與第二端鍵結；其中磷酸基團中的磷原子P藉由亞甲基羧基團(P-CH2
-O(O=)C-)與第一端鍵結，並且較佳藉由-C(CH3
)(CH3
)- 來與該第一端鍵結。此特定組成之接枝聚合物被發現適合用於接枝至尺寸介於20~200奈米的粒子，並且可獲得具有至少一群體之彼此相鄰且具有可拉伸的鏈狀構型的接枝聚合物，以使群體中之聚合物共同形成刷子狀構型。磷酸終端基團可以被提供離去基團或保護基團，如磷酸或二甲基磷酸脂。
較佳地，於本發明的接枝聚合物中，添加聚合物包含直鏈狀碳原子，較佳包含10~50個碳原子。
本發明之較佳接枝聚合物包含以下特徵：添加聚合物為聚苯乙烯、聚異戊二烯、聚丙烯腈、聚丙烯酸酯、聚甲基丙烯酸酯、ABS、SAN或其組合。其他適合作為添加聚合物的聚合物或聚合物組合如同上，於本案之第一層面之內容所述。
具體地，本發明之較佳接枝聚合物中，脂肪族終端基團為線狀烷基基團，選自正丁基~正十二烷基。
如圖1所示之化學反應式，製備好前驅聚合物IV，其具有RAFT反應物之功能特性。前驅聚合物IV於AIBN和DMF中會與苯乙烯反應，由此形成聚合物V，聚合物V即為本發明前述之接枝聚合物。接枝聚合物V由三批具有不同數量的苯乙烯重複單元所製備，其中n = 18、23或42。
前驅聚合物IV的製備如下說明。使化合物I與乙二醯氯於DMF和DCM中反應，以製得化合物II。化合物II與亞磷酸二甲脂(dimethyl phosphonate) IIa反應，獲得化合物III。化合物III接著與SiMe3
Br、DCM和MeOH反應，製得化合物IV。
接枝聚合物V (具有n = 18、23或42) 溶解於適合之溶劑，如DMF，之後置入裝有金紅石奈米粒子的反應器中。包含接枝聚合物V的溶液與金紅石奈米粒子於適當之環境條件下反應24小時。接著將與接枝聚合物V接枝的粒子使用離心機分離後，於60℃減壓環境下乾燥。
圖2所示為二相鄰之接枝聚合物1之示意圖，相鄰之接枝聚合物1附著於平坦的二氧化鈦表面3。二位於二氧化鈦表面3且相鄰之接枝聚合物1之間具有距離D如圖所示，並且獨立的接枝聚合物隨機產生的盤繞線圈構型之平均旋轉半徑Rg (聚合物或許無法直觀的被判定為線圈構型，但可以簡單的以垂直於金屬氧化物表面的桿狀的方式被觀察到)同樣標示於圖式中。當D/2大於等於Rg時，則有利於隨機形成的線圈構型的熵的量度。
圖3a與3b分別表示兩不同的聚合物4與聚合物5的構型，聚合物4跟5皆接枝至平坦的二氧化鈦表面3。依據前述說明之方法，將包含聚合物4與聚合物5的溶液套用於表面3，使兩聚合物4跟5分別接枝至金紅石奈米粒子表面3。
圖3a所示為三個相鄰之接枝聚合物，接枝聚合物4與接枝聚合物V類似，不同處在於其終端連接基團為羧基而非磷酸基。每一接枝聚合物4具有23個苯乙烯單元。相鄰之接枝聚合物4之間具有距離D，並且D/2大於Rg (接枝聚合物隨機形成的繞線構型的平均旋轉半徑Rg)。依據圖3a所示，當接枝至金屬氧化物表面的聚合物具有羧基為終端連接基團時，會隨機形成繞線結構。
圖3b所示為八個相鄰的接枝聚合物5，接枝聚合物5與接枝聚合物V完全相同。每一接枝聚合物5具有23個苯乙烯單元。相鄰之接枝聚合物5之間具有距離D，並且D/2小於Rg (接枝聚合物隨機形成之繞線構型的平均旋轉半徑Rg)。依據圖3b所示，當接枝至金屬氧化物表面的聚合物具有磷酸基為終端連接基團時，會形成可拉伸的鏈狀構型，其中相鄰之可拉伸的鏈狀構型具有大致上平行的方向性，因此聚合物組成的群體會形成刷子狀結構。
上述性質的不同可以藉由下表中所示，接枝至金屬氧化物表面的相鄰聚合物間的距離D的測量值來說明。 
從上表中可知，結果如同本發明中上述說明的接枝至金屬氧化物表面的接枝聚合物，其中相鄰之兩聚合物之間具有距離D，且D/2小於獨立的接枝聚合物隨機形成的線圈結構的平均旋轉半徑Rg。綜上所述，相鄰之聚合物因彼此間的空間障礙，被迫形成可拉伸的鏈狀構型。因此，本發明提供之接枝聚合物，彼此相鄰且共同形成刷子狀結構，以提供較佳之隔離與保護金屬氧化物表面之功能。
本發明較佳使用如圖4所示之金紅石金屬氧化物晶粒40，為一種二氧化鈦(TiO2
)結晶。粒子的長度約140~180奈米。粒子的寬度與高度大約為30~35奈米。依據本發明，較大面積之平坦表面42特別適合接枝至的聚合物。當接枝至表面42時，相鄰之接枝聚合物的自由端之間具有有限的距離，且只要符合D/2小於Rg的關係，可迫使該些聚合物形成可拉伸的鏈狀構型。
1、4、5‧‧‧聚合物
3、42‧‧‧表面
40‧‧‧晶粒
D‧‧‧距離
Rg‧‧‧平均旋轉半徑
3、42‧‧‧表面
40‧‧‧晶粒
D‧‧‧距離
Rg‧‧‧平均旋轉半徑
為讓本發明之上述和其他目的、特徵和優點能更明顯易懂，下文特舉數個較佳實施例，並配合所附圖式，作詳細說明如下： 圖1所示為依據本發明所繪製，形成接枝聚合物之反應式示意圖； 圖2所示為依據本發明所繪製，二相鄰之接枝聚合物附著於平坦的金屬氧化物表面之示意圖； 圖3a與3b所示為具有不同構型之二聚合物接枝至平坦的金屬氧化物表面之示意圖；以及 圖4所示為本發明較佳之金屬氧化物，金紅石，之示意圖。
3‧‧‧表面
5‧‧‧聚合物
Claims (19)
- 一種金屬氧化物，包含：一表面；以及複數個獨立的聚合物接枝至該表面，每一該聚合物包含：一添加聚合物，具有一第一端與一第二端；以及一第一部分，包含一終端磷酸基團，使該第一部分與該第一端鍵結，該終端磷酸基團附著於該表面，其中該複數個接枝聚合物包含至少一群體之相鄰聚合物，具有一可拉伸的鏈狀構型，其中相鄰之該可拉伸的鏈狀構型具有大致上相互平行的方向性，使該群體之相鄰聚合物共同形成一刷子狀構型。
- 如請求項1所述之金屬氧化物，其中形成該刷子狀構型之該群體之相鄰聚合物，被接枝至一非球型之金屬氧化物表面。
- 如請求項1所述之金屬氧化物，其中該金屬氧化物為反磁性。
- 如請求項1所述之金屬氧化物，其中該群體之相鄰聚合物共同形成該刷子狀構型，位於該金屬氧化物之該表面，且兩相鄰之該聚合物之間具有一平均距離D，其中D/2小於該複數個獨立的接枝聚合物可以隨機形成的一盤繞線團構型的一平均旋轉半徑Rg。
- 如請求項1所述之金屬氧化物，其中該接枝聚合物具有小的一多分散性指數(PDI)，該多分散性指數(PDI)係指重量平均分子量(Mw)與數目平均分子量(Mn)之比值，該多分散性指數介於1~2之間。
- 如請求項1所述之金屬氧化物，其中每一該接枝聚合物還包含：一第二部分，包含一脂肪族終端基團，且藉由一硫羰基(-SC(=S)-)與第二端鍵結。
- 如請求項1所述之金屬氧化物，其中該添加聚合物包含： 一直鏈狀碳原子。
- 如請求項1所述之金屬氧化物，其中該添加聚合物選自聚苯乙烯、聚異戊二烯、聚丙烯腈、聚丙烯酸酯、聚甲基丙烯酸酯、ABS、SAN或其組合。
- 如請求項6所述之金屬氧化物，其中該脂肪族終端基團為一線狀烷基基團，選自正丁基~十二烷基。
- 如請求項1所述之金屬氧化物，其中該終端磷酸基團中的磷原子P藉由一羧基與該第一端鍵結。
- 如請求項10所述之金屬氧化物，其中該羧基藉由一-C(CH3)(CH3)-基團與該第一端鍵結。
- 如請求項1所述之金屬氧化物，其中該金屬氧化物為一顆粒。
- 如請求項1所述之金屬氧化物，其中該金屬氧化物為一片狀構型，且該接枝聚合物形成一塗層。
- 一種聚合物材料，包含一聚合物介質，使粒子狀之如請求項12中所述之該金屬氧化物分散於其中。
- 一種介電物質，包含如請求項14中所述之該聚合物材料，並且具有一相對介電常數(relative permittivity)εr大於或等於3。
- 一種接枝方法，用於接枝複數個獨立的聚合物至一金屬氧化物表面，其中每一該聚合物包含一添加聚合物與一第一部分，該添加聚合物具有一第一端與一第二端，該第一部分包含一磷酸終端基團，以使該第一部分鍵結於第一端，包含以下步驟：溶解獨立的該聚合物於一適合溶劑中；將所形成之一溶液套用於該金屬氧化物表面；以及使獨立的該聚合物附著金屬氧化物表面，其中該磷酸終端基團附著於該金屬氧化物表面，以形成複數個接枝聚合物於該金屬氧化物表面， 並且該複數個接枝聚合物包含至少一個群體且彼此相鄰的聚合物，該聚合物具有一可拉伸的鏈狀構型，其中相鄰之該可拉伸的鏈狀構型具有大致相互平行的方向性，使於該群體中之該聚合物共同形成一刷子狀構型。
- 如請求項16所述之接枝方法，其中該群體中之該聚合物形成該刷子狀構型，兩相鄰之該聚合物之間具有一平均距離D，其中D/2小於該複數個獨立的接枝聚合物可以隨機形成的一盤繞線團構型的一平均旋轉半徑Rg。
- 一種接枝聚合物，適於接枝至一金屬氧化物表面，如請求項16~17中任一項所述之該接枝方法，包含：一添加聚合物，具有一第一端與一第二端；一第一部分，包含一終端磷酸基團，使該第一部分與該第一端鍵結；一第二部分，包含一脂肪族終端基團，且藉由一三硫代碳酸基(-SC(=S)S-)與第二端鍵結，其特徵在於：該終端磷酸基團中的磷原子P藉由一亞甲基羧基團(P-CH2-O(O=)C-)與該第一端鍵結。
- 如請求項18所述之接枝聚合物，其中該添加聚合物包含一直鏈狀碳原子。