DE1291505B - Process for the production of molded bodies, in particular plates made from vegetables

Info

Publication number: DE1291505B
Application number: DEB79013A
Authority: DE
Original assignee: Individual
Current assignee: Individual
Priority date: 1964-10-22
Filing date: 1964-10-22
Publication date: 1969-03-27

Description

Die Erfindung betrifft ein Verfahren zur Herstellung von Formkörpern, insbesondere von Platten, aus Vegetabilien, wobei die Platten zur Dämmung gegen Wärme, Kälte und Schall sowie als Zwischenlagen dienen sollen. The invention relates to a method for the production of moldings, in particular from panels, from vegetables, the panels for insulation against Heat, cold and sound as well as serve as intermediate layers.

Zur Herstellung von Platten oder anderen Formkörpern aus Holzstoffen oder ähnlichen faserhaltigen Vegetabilien sind seit langem die verschiedensten Verfahren bekannt. Am gebräuchlichsten sind die Verfahren zur Herstellung von Holzfaserplatten und Spanplatten. For the production of panels or other molded bodies made of wood pulp or similar fibrous vegetables have long been the most varied of processes known. The most common are the processes for the production of wood fiber boards and chipboard.

Bei der Herstellung von Holzfaserplatten muß der Rohstoff, vorwiegend Holzabfälle oder Einjahrespflanzen, mechanisch zerkleinert, thermochemisch behandelt und danach nochmals gemahlen werden. In the manufacture of fibreboard, the raw material must be predominantly Wood waste or annual plants, mechanically shredded, thermochemically treated and then ground again.

Darauf wird bei den meisten Verfahren dem derart aufbereiteten Rohstoff ein Bindemittel, vorwiegend Kunstharz, zugegeben, worauf dann die sogenannte Flotte, das ist der Faserbrei in großer Verdünnung, auf einer Siebanlage zu Platten geformt wird. Danach wird dem Formling soweit wie möglich das Wasser entzogen und dieser in einer Heißpresse bei einer Temperatur von etwa 2000 C und bei Drücken von 30 bis 50 kp/qcm zur fertigen Hartfaserplatte gepreßt.In most of the processes, this is then used to process the raw material a binder, mainly synthetic resin, is added, whereupon the so-called liquor, this is the fiber pulp in great dilution, formed into plates on a screening plant will. The water is then removed from the molding as much as possible and this in a hot press at a temperature of about 2000 C and at pressures of 30 Up to 50 kp / sq cm pressed to the finished hardboard.

Im Gegensatz zu diesem sogenannten Naßverfahren ist die Herstellung von Spanplatten ein Trockenverfahren, wobei der Rohstoff ebenfalls vorwiegend aus Holzabfällen oder Einjahrespfianzen besteht. In contrast to this so-called wet process, the production of chipboard a dry process, whereby the raw material is also predominantly made There is wood waste or annual plants.

Auch hierbei wird, wie in dem zuerst genannten Verfahren zur Herstellung von Faserplatten, der Rohstoff auf eine zweckmäßige Größe zerkleinert, getrocknet und mit Bindemitteln, meistens mit Kunstharzen, benetzt. Der derart vorbereitete Rohstoff wird dann zu Kuchen geformt und in einer Heißpresse zu fertigen Spanplatten gepreßt.Here too, as in the first-mentioned manufacturing process of fibreboard, the raw material shredded to an appropriate size, dried and wetted with binding agents, mostly synthetic resins. The one prepared in this way The raw material is then shaped into cakes and then made into chipboard in a hot press pressed.

All diesen Verfahren ist gemeinsam, daß der Rohstoff vorwiegend mit Bindemitteln versehen wird, damit eine gute Haltbarkeit erzielt werden kann. Darüber hinaus sind beim Preßvorgang verhältnismäßig große Drücke notwendig, wodurch aufwendige und komplizierte Preßanlagen erforderlich werden. All these processes have in common that the raw material is predominantly with Binding agents is provided so that a good shelf life can be achieved. About that In addition, relatively high pressures are necessary during the pressing process, which is expensive and complicated press equipment is required.

Schließlich ist noch hervorzuheben, daß der Rohstoff vor der Verarbeitung erst einem umfangreichen Aufbereitungsprozeß unterworfen werden muß, der den Einsatz weiterer Maschinen zur Folge hat.Finally, it should be emphasized that the raw material before processing must first be subjected to an extensive preparation process that requires the use further machines.

Diese Nachteile werden durch das Verfahren gemäß der Erfindung beseitigt, indem Kokosmark - ohne oder mit in an sich bekannter Weise verwendeten Kokosfasern vermischt - in leicht feuchtem Zustand verformt und das Formstück bei einer Temperatur von etwa 1500 C und etwa 3 bis 15 kp/qcm je nach gewünschter Dichte fertiggepreßt wird. These disadvantages are eliminated by the method according to the invention, by coconut pulp - with or without coconut fibers used in a manner known per se mixed - deformed in a slightly damp state and the fitting at one temperature from about 1500 C and about 3 to 15 kp / sqcm depending on the desired density will.

Das Verfahren benutzt als Rohstoffe Kokosmark oder ein Gemisch aus Kokosmark und Kokosfasern. The process uses coconut pulp or a mixture of raw materials Coconut pulp and coconut fiber.

Diese beiden Materialien bilden zusammen die äußere dicke Schale der Kokosnuß, die als Isolationsschicht dient und in der das Kokosmark von den Kokosfasern durchzogen ist. Man erhält die Rohstoffe entweder durch das Aufschlagen der äußeren dicken Schale der Kokosnuß oder als Rückstände bei der Gewinnung von Kokosfasern aus der genannten Schale. Das Kokosmark fällt dabei fast durchwegs in der Form an, wie es später zur Verarbeitung gemäß der Erfindung benötigt wird. Bisher konnte das Kokosmark zu nichts weiter verwendet werden, da dieser Stoff weder verrottet oder ver- brannt werden kann noch für irgendwelche anderen Zwecke zu gebrauchen war. Durch das Verfahren wird das Kokosmark erstmals einer nutzbringenden Verwendung zugeführt, wobei die Aufbereitung des Kokosmarks oder des Gemisches aus Kokosmark und Kokosfasern überraschend einfach ist.These two materials together form the outer thick shell of the Coconut, which serves as an insulating layer and in which the coconut pulp is separated from the coconut fibers is streaked. The raw materials are obtained either by opening the outer ones thick shell of the coconut or as residues from the extraction of coconut fibers from the said shell. The coconut pulp is almost always in the form as it is later needed for processing according to the invention. So far could the coconut pulp cannot be used for anything else, as this substance does not rot or ver can be burned or used for any other purpose. Through the process, the coconut pulp becomes a beneficial use for the first time supplied, with the preparation of the coconut pulp or the mixture of coconut pulp and coconut fiber is surprisingly simple.

Darüber hinaus ist besonders bemerkenswert, daß den Rohstoffen gemäß der Erfindung keine Bindemittel, wie bei den bisher bekannten Verfahren zugesetzt werden müssen. Schließlich wäre noch hervorzuheben, daß die notwendigen Pressen wesentlich einfacher und kleiner ausgebildet sein müssen als bei den bisherigen Herstellungsmethoden und daß, im ganzen gesehen, die maschinelle Einrichtung für eine Fertigungsanlage weit billiger ist als die für die Verarbeitung von Holz oder Einjahrespflanzen notwendigen Maschinen. In addition, it is particularly noteworthy that according to the raw materials according to the invention no binders, as in the previously known processes, were added Need to become. Finally, it should be emphasized that the necessary presses must be made much simpler and smaller than the previous ones Manufacturing methods and that, on the whole, the machinery for a manufacturing plant is far cheaper than that for processing wood or Annual plants necessary machines.

Bei Verwendung eines Gemisches aus Kokosmark und Kokosfasern als Rohstoff ist es zweckmäßig, wenn der Anteil der Kokosfasern etwa 10 bis 40o beträgt, da dadurch eine gleichmäßige Dichte und Struktur der Formkörper erreicht wird. Daneben sind natürlich auch andere Mischungsverhältnisse möglich. When using a mixture of coconut pulp and coconut fibers as Raw material is useful if the proportion of coconut fibers is about 10 to 40o, because this results in a uniform density and structure of the molded bodies. Besides Of course, other mixing ratios are also possible.

Normalerweise ist es nicht notwendig, die Rohstoffe besonders aufzubereiten, wodurch sich die sonst erforderlichen Anlagen für die Zerkleinerung und entsprechende Vorbehandlung erübrigen. In manchen Fällen ist es jedoch von Vorteil, wenn die Kokosfasern vor dem Verformen auf eine Faserlänge zerkleinert werden, die ein Zusammenballen verhindert. Im allgemeinen sollte die Faserlänge höchstens 15 mm betragen. Usually it is not necessary to specially prepare the raw materials, whereby the otherwise necessary equipment for the comminution and corresponding No need for pretreatment. In some cases, however, it is advantageous if the coconut fibers Before being deformed, they must be comminuted to a length of fiber that would agglomerate prevented. In general, the fiber length should not exceed 15 mm.

Gewöhnlich werden die Rohstoffe in leicht feuchtem Zustand verformt. Um jedoch eine einheitliche Feuchte zu erhalten, ist es zweckmäßig, wenn die Rohstoffe vor dem Verformen getrocknet und danach entsprechend gleichmäßig angefeuchtet werden. Der Vorgang ist dann der gleiche wie bisher geschildert. Usually the raw materials are deformed in a slightly damp state. However, in order to obtain a uniform moisture content, it is useful if the raw materials dried before shaping and then moistened accordingly evenly. The process is then the same as previously described.

Die in dem Kokosmark und den Kokosfasern enthaltenen Rohstoffe ergeben unter Mitwirkung von Wasserdampf eine Bindung, die auch dann nicht nachläßt, wenn die nach dem erfindungsgemäßen Verfahren hergestellten Platten oder anderen Formkörpern den normalen äußeren Beanspruchungen beispielsweise einer Dämmplatte bekannter Bauart ausgesetzt werden. Die Platte aus Kokosmark ist stabil in ihrer Festigkeit und beständig in ihrer Form. Selbst nach einer Feuchtigkeitsaufnahme, durch die sie zum Quellen gebracht wird, geht sie in ihre ursprüngliche Form wieder zurück, ohne an Festigkeit verloren zu haben. Darüber hinaus ist die Platte stark feuerhemmend und brennt nicht mit einer Flamme. The raw materials contained in the coconut pulp and the coconut fibers result with the help of water vapor a bond that does not weaken even if the plates or other shaped bodies produced by the process according to the invention the normal external loads, for example an insulation board of a known type get abandoned. The coconut pulp plate is stable in its strength and durable in their form. Even after moisture absorption, which causes them to swell is brought back to its original shape without losing strength to have lost. In addition, the panel is highly fire retardant and does not burn with a flame.

Die Platte ist als dünne oder dicke Bauplatte für Dämmzwecke für Wärme, Kälte und Schall zu verwenden. The board is available as a thin or thick building board for insulation purposes To use heat, cold and sound.

Claims

Claims: 1. A process for the production of moldings, in particular from plates, from vegetables, d a - characterized in that coconut pulp - without or mixed with coconut fibers used in a known manner - in slightly damp State deformed and the fitting at a temperature of about 1500 C and about 3 to 15 kp / sqcm depending on the required density.

2. The method according to claim 1, characterized in that when using a mixture of coke pulp and coconut fibers, the proportion of coconut fibers is preferred is about 10 to 40e / o.

3. The method according to claim 1 and 2, characterized in that the Coconut fiber before Deformed to a fiber length of about 15 mm, which prevents clumping.

4. The method according to claim 1 to 3, characterized in that the Raw materials are dried before shaping and then moistened evenly.