CN107201007A - 一种可生物降解树脂及其产品的制备方法 - Google Patents
一种可生物降解树脂及其产品的制备方法 Download PDFInfo
- Publication number
- CN107201007A CN107201007A CN201610148636.XA CN201610148636A CN107201007A CN 107201007 A CN107201007 A CN 107201007A CN 201610148636 A CN201610148636 A CN 201610148636A CN 107201007 A CN107201007 A CN 107201007A
- Authority
- CN
- China
- Prior art keywords
- biodegradable
- preparation
- packaging material
- year
- biodegradable resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种可生物降解树脂及其产品的制备方法，本发明的目的在于提供一种可吹膜的生物降解树脂及其制备方法。若采用这种方法生产的降解塑料包装膜，可从根本上解决包装材料在使用完以后，丢弃在大自然中或堆埋在垃圾中，可在3个月至半年的时间内被完全分解成二氧化碳和水等，是一种有益于植物生长的物质的可完全生物降解的包装材料。本发明的另一个目的是能够解决取代石油资源消耗的问题。所述可全生物降解材料为全生物材料，不含4P（即PE,PP,PVC,PS）是一种全新的生物降解材料，能够有效的替代石油资源。全世界每年用于包装材料上的聚烯烃材料数以亿万吨计，都是石油产品裂解制得的。我们成功地将淀粉基制造的包装材料，在石油价格不断攀升之际，每年将为国家节省大量石油资源。
Description
说明书摘要
本发明的目的在于提供一种可吹膜的生物降解树脂及其制备方法。若采用这种方法生产的降解塑料包装膜，可从根本上解决包装材料在使用完以后，丢弃在大自然中或堆埋在垃圾中，可在3个月至半年的时间内被完全分解成二氧化碳和水等，是一种有益于植物生长的物质的可完全生物降解的包装材料。本发明的另一个目的是能够解决取代石油资源消耗的问题。所述可全生物降解材料为全生物材料，不含4P（即PE, PP, PVC, PS）是一种全新的生物降解材料，能够有效的替代石油资源。全世界每年用于包装材料上的聚烯烃材料数以亿万吨计，都是石油产品裂解制得的。我们成功地将淀粉基制造的包装材料，在石油价格不断攀升之际，每年将为国家节省大量石油资源。
技术领域
本发明涉及包装材料，具体涉及一种可吹膜的生物降解树脂及其制备方法。
背景技术
众所周知，现在石油资源日益紧缺，油价不断攀升，给人们日常生活、工作带来了诸多不良影响，严重影响了社会经济的发展速度，也是地区之间资源争夺的不安定因素。
长期以来，我们所使用的塑料薄膜类制品都是用石油合成树脂，如聚氯乙烯，聚乙烯等材料制成的一次性薄膜类制成品，用完后被废弃为垃圾，这种垃圾需200年左右才能被分解，因此有的被随处丢弃，造成了危害很大的“白色污染”，有的被堆埋、或焚烧，极大的浪费了上亿年才能形成的石油资源，在处理弃置塑料薄膜类制品过程中会产生有害物质直接污染大气或水源，由于石油化工塑料不降解特性，其残留的塑料破坏了土壤结构，使许多良田减产，土壤沙漠化，河流堵塞，造成洪涝灾害。
近年来，解决“白色污染”对人类产生的危害正被许多国家政府提到日程议事上，呼声越来越高，各国相继投入了大量的财力物力，并拿出了相应的治理措施，但效果均不明显。“白色污染”正在不断地破环我们赖以生存的自然环境，全世界正在努力的想办法治理或消除“白色污染”给人们带来的危害。本申请人基于上述原因，经过研发提出过多种可降解生物树脂材料的生产方法，本发明就是本发明人基于以往方案的基础上，经过改进所提出的一种可吹膜的生物降解树脂及其制备方法。
发明内容
一种可吹膜的生物降解树脂及其制备方法，其特征在于：该材料的制备方法包括如下步骤：
一、按照下面重量百分比准备原料：
聚乳酸 30-50%
淀粉 5-25%
生物降解聚酯 40-60%
增塑剂 0.1-0.5%
填料 1-5%
相容剂 0.5-2.5%
二、将聚乳酸、淀粉、生物降解聚酯、增塑剂、填料、相容剂加入到高速混合机内，搅拌均匀；
三、将上述混合均匀的原料放入造粒机中进行混炼、熔融、挤出、冷却后切粒，制备生物降解树脂；
所述淀粉为玉米淀粉、木薯淀粉、马铃薯淀粉的一种或其混合物；
所述的生物降解聚酯为：聚丁二酸丁二醇酯、聚丁二酸-己二酸-丁二醇共聚物、聚对苯二甲酸-己二酸-丁二醇共聚物、聚己内酯、聚羟基丁酸-羟基戊酸共聚酯中的一种或其他混合物；
所述的增塑剂为甘油、山梨醇、柠檬酸三丁酯的一种或其混合物。
所述的填料为碳酸钙、滑石粉、蒙脱土的一种或其混合物。
所述的相容剂为乙烯-甲基丙烯酸共聚物、乙烯-丙烯酸共聚物、乙烯-醋酸乙烯酯共聚物的一种或其混合物。
本发明的生产方法的优点是工艺简单，采用一步法把各种原料混合，通过双螺杆挤出机造粒，所制树脂通过吹膜设备加工成薄膜。
本发明降解性能优良、可完全降解、对环境无污染、无毒性、不会土壤结构产生破坏。
另外，其生产工艺简单、成本低，综合性能较好。
以下是本发明的具体实施例：
实施例一：
聚乳酸 35%、玉米淀粉 10%、聚丁二酸丁二醇酯 50%、甘油 0.5%、碳酸钙 2.5%、乙烯-丙烯酸共聚物 2%
实施例二：
聚乳酸 40%、木薯淀粉 15%、聚对苯二甲酸-己二酸-丁二醇共聚物40%、山梨醇 1%、蒙脱土 3%、乙烯-甲基丙烯酸共聚物 1%
本发明的造粒机中采用了双螺杆挤出机，将所述的造粒机中采用水冷方式冷却挤出的熔融条料，其中，加工温度为180℃，螺杆转速为150rpm。最后生产的可生物降解树脂颗粒规格为：粒度为φ2-3mm，长度为3-4mm，圆柱形颗粒。
Claims (5)
1.所述的一种可吹膜的生物降解树脂及其制备方法，其特征在于：所述的造粒机中采用了双螺杆挤出机，加工温度为140-200℃，螺杆转速为30-300rpm。
2.按照下面重量百分比
聚乳酸 30-50%
淀粉 5-25%
生物降解聚酯 40-60%
增塑剂 0.1-0.5%
填料 1-5%
相容剂 0.5-2.5%
将聚乳酸、淀粉、生物降解聚酯、增塑剂、填料、相容剂加入到高速混合机内，搅拌均匀。
3.填料为碳酸钙、滑石粉、蒙脱土的一种或其混合物。
4.所述的增塑剂为甘油、山梨醇、柠檬酸三丁酯的一种或其混合物。
5.相容剂为乙烯-甲基丙烯酸共聚物、乙烯-丙烯酸共聚物、乙烯-醋酸乙烯酯共聚物的一种或其混合物。