WO2021230005A1 - Matériau transparent présentant une couche antibuée - Google Patents

Matériau transparent présentant une couche antibuée Download PDF

Info

Publication number
WO2021230005A1
WO2021230005A1 PCT/JP2021/015780 JP2021015780W WO2021230005A1 WO 2021230005 A1 WO2021230005 A1 WO 2021230005A1 JP 2021015780 W JP2021015780 W JP 2021015780W WO 2021230005 A1 WO2021230005 A1 WO 2021230005A1
Authority
WO
WIPO (PCT)
Prior art keywords
polyvinyl alcohol
alcohol resin
mass
modified polyvinyl
transparent material
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/JP2021/015780
Other languages
English (en)
Japanese (ja)
Inventor
雄介 天野
祐貴 立花
一彦 前川
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Kuraray Co Ltd
Original Assignee
Kuraray Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Kuraray Co Ltd filed Critical Kuraray Co Ltd
Publication of WO2021230005A1 publication Critical patent/WO2021230005A1/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

L'invention concerne un matériau transparent non seulement ayant d'excellentes performances antibuée, mais présentant également une excellente durabilité dans des tests d'exposition simulant divers environnements d'utilisation. Le matériau transparent comprend un substrat transparent et une couche antibuée formée sur le substrat, la couche antibuée étant une couche formée à partir d'un produit durci d'une composition réticulable contenant : (A) une résine d'alcool polyvinylique modifiée possédant un groupe à insaturation éthylénique dans une chaîne latérale de celle-ci ; et (B) un composant d'oxyde métallique, et la teneur de la résine d'alcool polyvinylique modifiée (A) dans la composition réticulable est d'au moins 30 % en masse.
PCT/JP2021/015780 2020-05-11 2021-04-16 Matériau transparent présentant une couche antibuée Ceased WO2021230005A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2020-083523 2020-05-11
JP2020083523 2020-05-11

Publications (1)

Publication Number Publication Date
WO2021230005A1 true WO2021230005A1 (fr) 2021-11-18

Family

ID=78525799

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2021/015780 Ceased WO2021230005A1 (fr) 2020-05-11 2021-04-16 Matériau transparent présentant une couche antibuée

Country Status (1)

Country Link
WO (1) WO2021230005A1 (fr)

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN116656162A (zh) * 2022-02-18 2023-08-29 中国科学院化学研究所 超强界面粘附、抗溶胀亲水涂层及其制备方法和应用
JP2023162847A (ja) * 2022-04-27 2023-11-09 株式会社クラレ 防曇性部材の製造方法、防曇性部材、および防曇性部材の反りの発生を抑制するための方法

Citations (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS59179684A (ja) * 1983-03-31 1984-10-12 Kuraray Co Ltd 防曇性組成物
JPH09194828A (ja) * 1996-01-23 1997-07-29 Nippon Oil & Fats Co Ltd 防曇剤組成物
JP2005314495A (ja) * 2004-04-27 2005-11-10 Dainichiseika Color & Chem Mfg Co Ltd 防曇塗料、防曇性フィルムおよびその製造方法
JP2008307763A (ja) * 2007-06-13 2008-12-25 Tohcello Co Ltd セルフクリーニングフィルム
WO2018225742A1 (fr) * 2017-06-05 2018-12-13 株式会社クラレ Polymère à base d'alcool vinylique contenant une oléfine à chaîne latérale
WO2019198754A1 (fr) * 2018-04-11 2019-10-17 株式会社クラレ Composition d'alcool polyvinylique ainsi qu'application de celle-ci, et procédé de fabrication de résine à base de vinyle
JP2019202267A (ja) * 2018-05-23 2019-11-28 富士フイルム株式会社 防曇性積層体の製造方法および防曇性積層体
WO2020218459A1 (fr) * 2019-04-25 2020-10-29 株式会社クラレ Composition de revêtement et élément antibuée, élément antisalissure, stratifié et produit antibactérien mettant en œuvre une telle composition

Patent Citations (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS59179684A (ja) * 1983-03-31 1984-10-12 Kuraray Co Ltd 防曇性組成物
JPH09194828A (ja) * 1996-01-23 1997-07-29 Nippon Oil & Fats Co Ltd 防曇剤組成物
JP2005314495A (ja) * 2004-04-27 2005-11-10 Dainichiseika Color & Chem Mfg Co Ltd 防曇塗料、防曇性フィルムおよびその製造方法
JP2008307763A (ja) * 2007-06-13 2008-12-25 Tohcello Co Ltd セルフクリーニングフィルム
WO2018225742A1 (fr) * 2017-06-05 2018-12-13 株式会社クラレ Polymère à base d'alcool vinylique contenant une oléfine à chaîne latérale
WO2019198754A1 (fr) * 2018-04-11 2019-10-17 株式会社クラレ Composition d'alcool polyvinylique ainsi qu'application de celle-ci, et procédé de fabrication de résine à base de vinyle
JP2019202267A (ja) * 2018-05-23 2019-11-28 富士フイルム株式会社 防曇性積層体の製造方法および防曇性積層体
WO2020218459A1 (fr) * 2019-04-25 2020-10-29 株式会社クラレ Composition de revêtement et élément antibuée, élément antisalissure, stratifié et produit antibactérien mettant en œuvre une telle composition

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN116656162A (zh) * 2022-02-18 2023-08-29 中国科学院化学研究所 超强界面粘附、抗溶胀亲水涂层及其制备方法和应用
JP2023162847A (ja) * 2022-04-27 2023-11-09 株式会社クラレ 防曇性部材の製造方法、防曇性部材、および防曇性部材の反りの発生を抑制するための方法

Similar Documents

Publication Publication Date Title
JP3846545B2 (ja) コーティング剤組成物、コーティング方法及び被覆物品
CN102066464B (zh) 柔性硬涂层和涂覆有该柔性硬涂层的基底
ES2491615T3 (es) Recubrimientos antireflexión / antiempañamiento
JP3841141B2 (ja) 下塗り剤組成物及びコーティング方法
JPS5989368A (ja) 熱成形性シリコ−ン樹脂被覆組成物及びポリカ−ボネ−ト用の二成分被覆系
JP2002053805A (ja) 被膜形成用組成物
US20090029179A1 (en) Two-liquid composition, hydrophilic composition and hydrophilic member
JPH036282A (ja) プライマー組成物
JP4958332B2 (ja) 硬化性耐摩耗コーティング組成物並びに該組成物を含む製品
JP3197918B2 (ja) 被覆用組成物及び合成樹脂成形品の表面改質方法
WO2021230005A1 (fr) Matériau transparent présentant une couche antibuée
JP3327207B2 (ja) 親水性塗膜を有する物品及びその製造方法
JP2003238887A (ja) 紫外線遮蔽層形成用樹脂組成物および紫外線遮蔽性積層体
US6037394A (en) Primer composition and article obtained using the same
JP2001316626A (ja) コーティング剤
JP4487770B2 (ja) 硬化性樹脂組成物及び反射防止材
JPS6153311A (ja) 親水性共重合体の製造方法
JP4164693B2 (ja) コーティング剤組成物及び被覆物品
JPH08302138A (ja) 透明成形体
JP3765839B2 (ja) 樹脂組成物
JP2008088260A (ja) 親水性膜形成用組成物および親水性部材
JP2023005856A (ja) コーティング組成物ならびにそれを用いたコーティング液および積層部材
JP2023005857A (ja) コーティング液およびそれを用いた積層部材
JP3319326B2 (ja) プライマー組成物及び透明被覆物品
JP4069498B2 (ja) 透明被覆成形品およびその製造方法

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 21805077

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 21805077

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: JP