WO2019189490A1 - Matériau d'emballage et poche stérilisable en autoclave ou poche pour micro-ondes pourvue d'un matériau d'emballage - Google Patents

Matériau d'emballage et poche stérilisable en autoclave ou poche pour micro-ondes pourvue d'un matériau d'emballage Download PDF

Info

Publication number
WO2019189490A1
WO2019189490A1 PCT/JP2019/013404 JP2019013404W WO2019189490A1 WO 2019189490 A1 WO2019189490 A1 WO 2019189490A1 JP 2019013404 W JP2019013404 W JP 2019013404W WO 2019189490 A1 WO2019189490 A1 WO 2019189490A1
Authority
WO
WIPO (PCT)
Prior art keywords
film
packaging material
plastic film
stretched plastic
layer
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/JP2019/013404
Other languages
English (en)
Japanese (ja)
Inventor
靖也 飯尾
有紀 龍田
紘基 阿久津
高橋　秀明
和弘 多久島
浩一 三上
戸田　清志
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Dai Nippon Printing Co Ltd
Original Assignee
Dai Nippon Printing Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Dai Nippon Printing Co Ltd filed Critical Dai Nippon Printing Co Ltd
Priority to JP2020509273A priority Critical patent/JPWO2019189490A1/ja
Publication of WO2019189490A1 publication Critical patent/WO2019189490A1/fr
Anticipated expiration legal-status Critical
Priority to JP2023218500A priority patent/JP2024041795A/ja
Ceased legal-status Critical Current

Abstract

L'invention concerne un matériau d'emballage pourvu d'au moins un premier film plastique étiré, d'un second film plastique étiré et d'une couche d'agent d'étanchéité dans cet ordre depuis le côté surface externe vers le côté surface interne. Le premier film plastique étiré et le second film plastique étiré sont les seuls films plastiques étirés inclus dans le matériau d'emballage. Un film parmi le premier film plastique étiré et le second film plastique étiré est un film de polyester à rigidité élevée et l'autre film parmi le premier film plastique étiré et le second film plastique étiré contient du polyester en tant que composant principal. La rigidité de boucle du matériau d'emballage dans une direction est de 0,16 N ou plus.
PCT/JP2019/013404 2018-03-28 2019-03-27 Matériau d'emballage et poche stérilisable en autoclave ou poche pour micro-ondes pourvue d'un matériau d'emballage Ceased WO2019189490A1 (fr)

Priority Applications (2)

Application Number Priority Date Filing Date Title
JP2020509273A JPWO2019189490A1 (ja) 2018-03-28 2019-03-27 包装材料及び包装材料を備えるレトルトパウチ又は電子レンジ用パウチ
JP2023218500A JP2024041795A (ja) 2018-03-28 2023-12-25 包装材料及び包装材料を備えるレトルトパウチ又は電子レンジ用パウチ

Applications Claiming Priority (8)

Application Number Priority Date Filing Date Title
JP2018063081 2018-03-28
JP2018-063081 2018-03-28
JP2018-150846 2018-08-09
JP2018150846 2018-08-09
JP2018186133 2018-09-28
JP2018-186119 2018-09-28
JP2018-186133 2018-09-28
JP2018186119 2018-09-28

Publications (1)

Publication Number Publication Date
WO2019189490A1 true WO2019189490A1 (fr) 2019-10-03

Family

ID=68059138

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2019/013404 Ceased WO2019189490A1 (fr) 2018-03-28 2019-03-27 Matériau d'emballage et poche stérilisable en autoclave ou poche pour micro-ondes pourvue d'un matériau d'emballage

Country Status (2)

Country Link
JP (2) JPWO2019189490A1 (fr)
WO (1) WO2019189490A1 (fr)

Cited By (11)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2020142857A (ja) * 2019-02-28 2020-09-10 大日本印刷株式会社 包装材料及び包装材料を備えるパウチ
JP2020142858A (ja) * 2019-02-28 2020-09-10 大日本印刷株式会社 包装材料及び包装材料を備えるパウチ
US20200407136A1 (en) * 2018-03-22 2020-12-31 Dai Nippon Printing Co., Ltd. Barrier laminate film, and packaging material which uses barrier laminate film
JP2021070311A (ja) * 2019-10-30 2021-05-06 大日本印刷株式会社 積層体及びこれを用いた包装体
JP2021176296A (ja) * 2020-04-30 2021-11-11 海商株式会社 包装された魚介製品およびその製造方法
JP2023010099A (ja) * 2021-07-09 2023-01-20 東洋製罐株式会社 積層フィルム及び包装袋
JP2023010098A (ja) * 2021-07-09 2023-01-20 東洋製罐株式会社 包装袋用積層フィルム
WO2023013768A1 (fr) * 2021-08-05 2023-02-09 大日本印刷株式会社 Corps barrière multicouche, matériau de revêtement et récipient d'emballage
JP2023514478A (ja) * 2019-12-20 2023-04-06 ダウ グローバル テクノロジーズ エルエルシー ラップシール用のバリア積層体フィルム
WO2023190907A1 (fr) * 2022-03-30 2023-10-05 大日本印刷株式会社 Matériau de base étiré, matériau de base d'impression, film d'étanchéité barrière, stratifié et sac d'emballage
JP7452744B1 (ja) 2023-06-19 2024-03-19 Ｔｏｐｐａｎホールディングス株式会社 積層体、包装袋及び包装体

Citations (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH10168293A (ja) * 1996-10-09 1998-06-23 Unitika Ltd 易引裂性二軸延伸ポリエステルフィルム
JPH11302405A (ja) * 1998-04-20 1999-11-02 Unitika Ltd 易引裂性ポリエステルフィルム
JP2001277408A (ja) * 2000-03-31 2001-10-09 Toppan Printing Co Ltd 腰強度と耐衝撃性に優れた樹脂積層フィルム
JP2015048081A (ja) * 2013-08-30 2015-03-16 ユニチカ株式会社 缶の内袋用ポリエステルフィルム
JP2015150807A (ja) * 2014-02-17 2015-08-24 ユニチカ株式会社 ポリエステル積層体
JP2016101721A (ja) * 2014-11-28 2016-06-02 東レフィルム加工株式会社 積層シート
WO2017170574A1 (fr) * 2016-04-01 2017-10-05 凸版印刷株式会社 Film barrière aux gaz
WO2018052042A1 (fr) * 2016-09-15 2018-03-22 大日本印刷株式会社 Sachet

Family Cites Families (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP5129417B2 (ja) * 2001-05-08 2013-01-30 大倉工業株式会社 ハイレトルト用アルミ箔積層フィルム
JP2003119303A (ja) * 2001-10-12 2003-04-23 Unitika Ltd ２軸延伸ポリエステル系フィルム、フィルム状積層体、及びこれより得られる液状物充填用袋
JP4962438B2 (ja) * 2003-02-24 2012-06-27 大日本印刷株式会社 包装袋
JP5815373B2 (ja) * 2011-11-10 2015-11-17 ユニチカ株式会社 包装材料
JP2013199280A (ja) * 2012-03-23 2013-10-03 Toppan Printing Co Ltd 包装袋
JP2015036208A (ja) * 2013-08-12 2015-02-23 大日本印刷株式会社 バリア性フィルム、ならびにそれを用いた積層フィルムおよび包装体
JP6229964B2 (ja) * 2017-05-15 2017-11-15 大日本印刷株式会社 パウチ
TW202019687A (zh) * 2018-10-16 2020-06-01 日商東洋紡股份有限公司 積層膜
JP7259353B2 (ja) * 2019-01-25 2023-04-18 凸版印刷株式会社 包装袋および包装袋の製造方法

Patent Citations (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH10168293A (ja) * 1996-10-09 1998-06-23 Unitika Ltd 易引裂性二軸延伸ポリエステルフィルム
JPH11302405A (ja) * 1998-04-20 1999-11-02 Unitika Ltd 易引裂性ポリエステルフィルム
JP2001277408A (ja) * 2000-03-31 2001-10-09 Toppan Printing Co Ltd 腰強度と耐衝撃性に優れた樹脂積層フィルム
JP2015048081A (ja) * 2013-08-30 2015-03-16 ユニチカ株式会社 缶の内袋用ポリエステルフィルム
JP2015150807A (ja) * 2014-02-17 2015-08-24 ユニチカ株式会社 ポリエステル積層体
JP2016101721A (ja) * 2014-11-28 2016-06-02 東レフィルム加工株式会社 積層シート
WO2017170574A1 (fr) * 2016-04-01 2017-10-05 凸版印刷株式会社 Film barrière aux gaz
WO2018052042A1 (fr) * 2016-09-15 2018-03-22 大日本印刷株式会社 Sachet

Cited By (21)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20200407136A1 (en) * 2018-03-22 2020-12-31 Dai Nippon Printing Co., Ltd. Barrier laminate film, and packaging material which uses barrier laminate film
US12060207B2 (en) * 2018-03-22 2024-08-13 Dai Nippon Printing Co., Ltd. Barrier laminate film, and packaging material which uses barrier laminate film
JP7389959B2 (ja) 2019-02-28 2023-12-01 大日本印刷株式会社 包装材料及び包装材料を備えるパウチ
JP2020142858A (ja) * 2019-02-28 2020-09-10 大日本印刷株式会社 包装材料及び包装材料を備えるパウチ
JP7755815B2 (ja) 2019-02-28 2025-10-17 大日本印刷株式会社 包装材料及び包装材料を備えるパウチ
JP2024107327A (ja) * 2019-02-28 2024-08-08 大日本印刷株式会社 包装材料及び包装材料を備えるパウチ
JP2020142857A (ja) * 2019-02-28 2020-09-10 大日本印刷株式会社 包装材料及び包装材料を備えるパウチ
JP7494882B2 (ja) 2019-10-30 2024-06-04 大日本印刷株式会社 積層体及びこれを用いた包装体
JP2022145735A (ja) * 2019-10-30 2022-10-04 大日本印刷株式会社 積層体及びこれを用いた包装体
JP2021070311A (ja) * 2019-10-30 2021-05-06 大日本印刷株式会社 積層体及びこれを用いた包装体
JP7115504B2 (ja) 2019-10-30 2022-08-09 大日本印刷株式会社 積層体及びこれを用いた包装体
JP7628546B2 (ja) 2019-12-20 2025-02-10 ダウ グローバル テクノロジーズ エルエルシー ラップシール用のバリア積層体フィルム
JP2023514478A (ja) * 2019-12-20 2023-04-06 ダウ グローバル テクノロジーズ エルエルシー ラップシール用のバリア積層体フィルム
JP2021176296A (ja) * 2020-04-30 2021-11-11 海商株式会社 包装された魚介製品およびその製造方法
JP7241112B2 (ja) 2020-04-30 2023-03-16 海商株式会社 包装された魚介製品およびその製造方法
JP2023010099A (ja) * 2021-07-09 2023-01-20 東洋製罐株式会社 積層フィルム及び包装袋
JP2023010098A (ja) * 2021-07-09 2023-01-20 東洋製罐株式会社 包装袋用積層フィルム
WO2023013768A1 (fr) * 2021-08-05 2023-02-09 大日本印刷株式会社 Corps barrière multicouche, matériau de revêtement et récipient d'emballage
WO2023190907A1 (fr) * 2022-03-30 2023-10-05 大日本印刷株式会社 Matériau de base étiré, matériau de base d'impression, film d'étanchéité barrière, stratifié et sac d'emballage
JP7452744B1 (ja) 2023-06-19 2024-03-19 Ｔｏｐｐａｎホールディングス株式会社 積層体、包装袋及び包装体
JP2025000523A (ja) * 2023-06-19 2025-01-07 Ｔｏｐｐａｎホールディングス株式会社 積層体、包装袋及び包装体

Also Published As

Publication number Publication date
JP2024041795A (ja) 2024-03-27
JPWO2019189490A1 (ja) 2021-04-08

Similar Documents

Publication Publication Date Title
JP2024041795A (ja) 包装材料及び包装材料を備えるレトルトパウチ又は電子レンジ用パウチ
JP7180072B2 (ja) 積層フィルム及び包装袋
JP7373126B2 (ja) 紙容器用包装材料及び液体紙容器
JP2023001195A (ja) 袋
JP2019059511A (ja) 包装袋
WO2021199636A1 (fr) Stratifié, sachet, et matériau de couvercle
WO2022131264A1 (fr) Stratifié, sac d'emballage et sachet à fond plat
JP2022007964A (ja) 積層体、レトルト用またはボイル用パウチ
JP2022007962A (ja) 積層体、レトルト用またはボイル用パウチ
JP7389959B2 (ja) 包装材料及び包装材料を備えるパウチ
JP7371616B2 (ja) 包装材料及び包装材料を備えるレトルトパウチ又は電子レンジ用パウチ
JP2022007963A (ja) 積層体、該積層体を備える電子レンジパウチ
JP2019142522A (ja) 包装材料および包装袋
JP2019119132A (ja) ラミネートフィルムおよび成形品
JP2004050605A (ja) 積層体
WO2017209107A1 (fr) Feuille en couches, matériau d'emballage et article moulé
JP7755815B2 (ja) 包装材料及び包装材料を備えるパウチ
JP7604773B2 (ja) 紙容器用包装材料及び液体紙容器
JP7561331B2 (ja) バリア性積層フィルム及びバリア性積層フィルムの製造方法、並びにバリア性積層フィルムを備える包装材料
JP4857871B2 (ja) 紙容器
JP4760494B2 (ja) 紙容器
JP4946412B2 (ja) 液体紙容器
JP2002210858A (ja) レトルト用パウチ
JP7425984B2 (ja) 紙容器用包装材料及び液体紙容器
JP6763761B2 (ja) 食品包装用深絞り成形包装体

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 19774660

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 2020509273

Country of ref document: JP

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 19774660

Country of ref document: EP

Kind code of ref document: A1