WO2019008898A1 - Film formant un film de résine et feuille composite formant un film de résine - Google Patents

Film formant un film de résine et feuille composite formant un film de résine Download PDF

Info

Publication number
WO2019008898A1
WO2019008898A1 PCT/JP2018/018248 JP2018018248W WO2019008898A1 WO 2019008898 A1 WO2019008898 A1 WO 2019008898A1 JP 2018018248 W JP2018018248 W JP 2018018248W WO 2019008898 A1 WO2019008898 A1 WO 2019008898A1
Authority
WO
WIPO (PCT)
Prior art keywords
resin film
film
resin
forming
meth
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/JP2018/018248
Other languages
English (en)
Japanese (ja)
Inventor
啓示 布施
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Lintec Corp
Original Assignee
Lintec Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Lintec Corp filed Critical Lintec Corp
Priority to MYPI2019007673A priority Critical patent/MY194458A/en
Priority to JP2019528382A priority patent/JP7044780B2/ja
Priority to SG11201913224TA priority patent/SG11201913224TA/en
Priority to CN201880042700.3A priority patent/CN110831766B/zh
Priority to KR1020197038836A priority patent/KR102507152B1/ko
Priority to PH1/2020/500005A priority patent/PH12020500005B1/en
Publication of WO2019008898A1 publication Critical patent/WO2019008898A1/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

L'invention concerne un film formant un film de résine qui remplit les conditions suivantes (i) et (ii) : (i) lorsqu'un premier spécimen d'essai fabriqué au moyen d'un premier corps stratifié qui comprend une pluralité de films formant un film de résine stratifiés ensemble et présente une taille de 50 mm x 50 mm et une épaisseur de 200 µm est immergé dans de l'eau pure pendant deux heures, le premier spécimen d'essai présente une absorption d'eau de 0,55 % ou moins ; et (ii) lorsqu'un second spécimen d'essai fabriqué au moyen d'un second corps stratifié dans lequel le film formant un film de résine est fixé à une tranche miroir de silicium a été laissé dans un environnement de 23 °C et 50 % de RH pendant 30 minutes, et lorsque le second spécimen d'essai après l'écoulement du temps a été immergé dans de l'eau pure pendant deux heures, une force d'adhérence entre les films formant un film de résine ou un produit durci de ceux-ci et la tranche miroir de silicium mesurée avant et après l'immersion présente un taux de changement de force d'adhérence de 60 % ou moins.
PCT/JP2018/018248 2017-07-06 2018-05-11 Film formant un film de résine et feuille composite formant un film de résine Ceased WO2019008898A1 (fr)

Priority Applications (6)

Application Number Priority Date Filing Date Title
MYPI2019007673A MY194458A (en) 2017-07-06 2018-05-11 Resin film forming film and resin film forming composite sheet
JP2019528382A JP7044780B2 (ja) 2017-07-06 2018-05-11 樹脂膜形成用フィルム及び樹脂膜形成用複合シート
SG11201913224TA SG11201913224TA (en) 2017-07-06 2018-05-11 Resin film forming film and resin film forming composite sheet
CN201880042700.3A CN110831766B (zh) 2017-07-06 2018-05-11 树脂膜形成用膜及树脂膜形成用复合片
KR1020197038836A KR102507152B1 (ko) 2017-07-06 2018-05-11 수지막 형성용 필름 및 수지막 형성용 복합 시트
PH1/2020/500005A PH12020500005B1 (en) 2017-07-06 2018-05-11 Resin film forming film and resin film forming composite sheet

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2017-132980 2017-07-06
JP2017132980 2017-07-06

Publications (1)

Publication Number Publication Date
WO2019008898A1 true WO2019008898A1 (fr) 2019-01-10

Family

ID=64950807

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2018/018248 Ceased WO2019008898A1 (fr) 2017-07-06 2018-05-11 Film formant un film de résine et feuille composite formant un film de résine

Country Status (8)

Country Link
JP (1) JP7044780B2 (fr)
KR (1) KR102507152B1 (fr)
CN (1) CN110831766B (fr)
MY (1) MY194458A (fr)
PH (1) PH12020500005B1 (fr)
SG (1) SG11201913224TA (fr)
TW (1) TWI743361B (fr)
WO (1) WO2019008898A1 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2023052765A (ja) * 2019-03-08 2023-04-12 帝人株式会社 ポリマー部材－無機基材複合体、その製造方法、及びそのためのポリマー部材

Families Citing this family (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE112020003804B4 (de) * 2019-08-09 2026-01-22 Sk Microworks Co., Ltd. Folie zum verkleben
JP7471880B2 (ja) * 2020-03-18 2024-04-22 リンテック株式会社 フィルム状接着剤及びダイシングダイボンディングシート
JP7471879B2 (ja) * 2020-03-18 2024-04-22 リンテック株式会社 フィルム状接着剤及びダイシングダイボンディングシート
JP7387510B2 (ja) * 2020-03-26 2023-11-28 リンテック株式会社 保護膜形成フィルム、保護膜形成用複合シート、及び保護膜形成フィルム付きワークの搬送方法

Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2005317758A (ja) * 2004-04-28 2005-11-10 Shin Etsu Polymer Co Ltd 電子部品保持具
JP2011501233A (ja) * 2007-10-25 2011-01-06 コーロン インダストリーズ，インコーポレイテッド フィルム型感光性転写材料
WO2015046529A1 (fr) * 2013-09-30 2015-04-02 リンテック株式会社 Feuille composite pour la formation d'un film en résine

Family Cites Families (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP4732472B2 (ja) 2007-03-01 2011-07-27 日東電工株式会社 熱硬化型ダイボンドフィルム
JP5390209B2 (ja) 2009-02-04 2014-01-15 日東電工株式会社 熱硬化型ダイボンドフィルム
JP4717156B1 (ja) * 2010-11-01 2011-07-06 協和界面科学株式会社 剥離試験装置
JP6600872B2 (ja) * 2014-01-08 2019-11-06 リンテック株式会社 保護膜形成用複合シート
WO2017010385A1 (fr) * 2015-07-10 2017-01-19 日東電工株式会社 Module solaire, procédé de fabrication de module solaire, et procédé de câblage de cellule solaire

Patent Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2005317758A (ja) * 2004-04-28 2005-11-10 Shin Etsu Polymer Co Ltd 電子部品保持具
JP2011501233A (ja) * 2007-10-25 2011-01-06 コーロン インダストリーズ，インコーポレイテッド フィルム型感光性転写材料
WO2015046529A1 (fr) * 2013-09-30 2015-04-02 リンテック株式会社 Feuille composite pour la formation d'un film en résine

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2023052765A (ja) * 2019-03-08 2023-04-12 帝人株式会社 ポリマー部材－無機基材複合体、その製造方法、及びそのためのポリマー部材
JP7657246B2 (ja) 2019-03-08 2025-04-04 帝人株式会社 ポリマー部材－無機基材複合体、その製造方法、及びそのためのポリマー部材

Also Published As

Publication number Publication date
KR102507152B1 (ko) 2023-03-07
CN110831766B (zh) 2021-09-21
TWI743361B (zh) 2021-10-21
TW201907491A (zh) 2019-02-16
PH12020500005B1 (en) 2023-05-17
SG11201913224TA (en) 2020-01-30
KR20200026833A (ko) 2020-03-11
JPWO2019008898A1 (ja) 2020-05-21
MY194458A (en) 2022-11-30
JP7044780B2 (ja) 2022-03-30
CN110831766A (zh) 2020-02-21
PH12020500005A1 (en) 2021-01-11

Similar Documents

Publication Publication Date Title
JP7014875B2 (ja) 熱硬化性保護膜形成用フィルム、保護膜形成用複合シート、及びチップの製造方法
JPWO2019172438A1 (ja) 保護膜形成用複合シート及び保護膜付き半導体チップの製造方法
JP6914698B2 (ja) 樹脂膜形成用複合シート
JP7044780B2 (ja) 樹脂膜形成用フィルム及び樹脂膜形成用複合シート
CN111417513B (zh) 保护膜形成用复合片及带保护膜的半导体芯片的制造方法
JP7071916B2 (ja) 保護膜付き半導体チップの製造方法及び半導体装置の製造方法
CN112111236A (zh) 保护膜形成用复合片、及带保护膜的半导体芯片的制造方法
JPWO2020116275A1 (ja) 保護膜形成用複合シート、及び半導体チップの製造方法
JP6979081B2 (ja) 保護膜形成用フィルム、保護膜形成用複合シート、及び半導体チップの製造方法
WO2019082968A1 (fr) Feuille composite de formation de film protecteur et procédé de fabrication de puce semi-conductrice
CN115109284A (zh) 保护膜形成膜、保护膜形成用复合片及晶圆的再生方法
JP6686241B1 (ja) 保護膜形成用フィルム、保護膜形成用複合シート、検査方法及び識別方法
JP2019062108A (ja) 樹脂膜形成用複合シート
CN112447577A (zh) 支撑片、保护膜形成用膜、保护膜形成用复合片、及带保护膜的工件加工物的制造方法
JP7039460B2 (ja) 保護膜形成用複合シート
WO2019082961A1 (fr) Feuille composite pour former un film protecteur et procédé pour fabriquer une puce de semi-conductreurs
WO2019082969A1 (fr) Feuille composite formant une membrane de protection et procédé de fabrication d'une puce semi-conductrice
JP2022089876A (ja) 保護膜形成用フィルム及び保護膜形成用複合シート
CN115109370A (zh) 保护膜形成膜、保护膜形成用复合片、带保护膜的工件加工物与带保护膜的工件的制造方法
JP6938477B2 (ja) 保護膜形成用複合シート
JPWO2020116288A1 (ja) 保護膜形成用複合シート、及び半導体チップの製造方法
TWI885042B (zh) 保護膜形成用複合片、以及具保護膜之晶片的製造方法
JP2019062107A (ja) 樹脂膜形成用複合シート
JP2021040099A (ja) 保護膜形成用フィルム、保護膜形成用複合シート、及び保護膜付きワーク加工物の製造方法
JPWO2020175421A1 (ja) 熱硬化性樹脂フィルム及び第１保護膜形成用シート

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 18828396

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 2019528382

Country of ref document: JP

Kind code of ref document: A

ENP Entry into the national phase

Ref document number: 20197038836

Country of ref document: KR

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 18828396

Country of ref document: EP

Kind code of ref document: A1