WO2013035249A1 - Procédé de fabrication de films optiques - Google Patents

Procédé de fabrication de films optiques Download PDF

Info

Publication number
WO2013035249A1
WO2013035249A1 PCT/JP2012/005175 JP2012005175W WO2013035249A1 WO 2013035249 A1 WO2013035249 A1 WO 2013035249A1 JP 2012005175 W JP2012005175 W JP 2012005175W WO 2013035249 A1 WO2013035249 A1 WO 2013035249A1
Authority
WO
WIPO (PCT)
Prior art keywords
film
dope
resin
casting
cellulose ester
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/JP2012/005175
Other languages
English (en)
Japanese (ja)
Inventor
忠浩 金子
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Konica Minolta Advanced Layers Inc
Original Assignee
Konica Minolta Advanced Layers Inc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Konica Minolta Advanced Layers Inc filed Critical Konica Minolta Advanced Layers Inc
Priority to KR1020147003742A priority Critical patent/KR101594265B1/ko
Publication of WO2013035249A1 publication Critical patent/WO2013035249A1/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

L'invention porte sur un procédé de fabrication de films optiques pour fabriquer des films optiques à l'aide d'une extrudeuse de film coulé, qui a au moins une unité de coulée à écoulement pour former le film coulé par écoulement par décharge d'un dopant de résine mixte de matériaux de départ de résine acrylique et de résine d'ester de cellulose solubilisés dans un solvant à partir d'une filière et coulée par écoulement d'un film de dopant sur un support à courroie sans fin, une unité d'étirage pour étirer le film de coulée par écoulement après qu'il a été arraché à partir du support à courroie sans fin, une unité de séchage pour le séchage, et une unité d'enroulement pour l'enroulement. Le procédé de fabrication de film optique est caractérisé en ce que l'unité de coulée à écoulement a un moyen de distribution de solution de renforcement de bords pour distribuer une solution de renforcement de bords contenant la résine d'ester de cellulose sous une proportion en masse supérieure à la proportion en masse de la résine d'ester de cellulose constituant le dopant sur les deux bords du film de dopant ou du film de coulée par écoulement, et en ce qu'il effectue une coulée à écoulement tout en distribuant la solution de renforcement de bords sur les deux bords à partir du moyen de distribution de solution de renforcement de bords.
PCT/JP2012/005175 2011-09-08 2012-08-16 Procédé de fabrication de films optiques Ceased WO2013035249A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
KR1020147003742A KR101594265B1 (ko) 2011-09-08 2012-08-16 광학 필름의 제조 방법

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2011-195753 2011-09-08
JP2011195753 2011-09-08

Publications (1)

Publication Number Publication Date
WO2013035249A1 true WO2013035249A1 (fr) 2013-03-14

Family

ID=47831726

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2012/005175 Ceased WO2013035249A1 (fr) 2011-09-08 2012-08-16 Procédé de fabrication de films optiques

Country Status (3)

Country Link
JP (1) JPWO2013035249A1 (fr)
KR (1) KR101594265B1 (fr)
WO (1) WO2013035249A1 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2018061350A1 (fr) * 2016-09-30 2018-04-05 コニカミノルタ株式会社 Procédé de fabrication de film optique

Citations (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH02208650A (ja) * 1989-02-08 1990-08-20 Konica Corp セルローストリアセテートフィルムの製造方法
JP2005199725A (ja) * 2005-03-24 2005-07-28 Fuji Photo Film Co Ltd フィルム製造方法及び装置
JP2005279956A (ja) * 2004-03-26 2005-10-13 Fuji Photo Film Co Ltd フィルムの製造方法及び製造装置
JP2008183758A (ja) * 2007-01-29 2008-08-14 Konica Minolta Opto Inc 光学用フィルムの製造方法、光学用フィルム、偏光板及び液晶表示装置
JP2009234169A (ja) * 2008-03-28 2009-10-15 Konica Minolta Opto Inc 光学フィルムの製造方法
WO2009150926A1 (fr) * 2008-06-13 2009-12-17 コニカミノルタオプト株式会社 Procédé de production de film acrylique, et film acrylique produit selon le procédé
JP2010179475A (ja) * 2009-02-03 2010-08-19 Konica Minolta Opto Inc 光学フィルムの製造方法、光学フィルム、偏光板及び表示装置
WO2011055590A1 (fr) * 2009-11-04 2011-05-12 コニカミノルタオプト株式会社 Bobine de film protecteur pour plaque de polarisation à cristaux liquides et son procédé de fabrication

Patent Citations (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH02208650A (ja) * 1989-02-08 1990-08-20 Konica Corp セルローストリアセテートフィルムの製造方法
JP2005279956A (ja) * 2004-03-26 2005-10-13 Fuji Photo Film Co Ltd フィルムの製造方法及び製造装置
JP2005199725A (ja) * 2005-03-24 2005-07-28 Fuji Photo Film Co Ltd フィルム製造方法及び装置
JP2008183758A (ja) * 2007-01-29 2008-08-14 Konica Minolta Opto Inc 光学用フィルムの製造方法、光学用フィルム、偏光板及び液晶表示装置
JP2009234169A (ja) * 2008-03-28 2009-10-15 Konica Minolta Opto Inc 光学フィルムの製造方法
WO2009150926A1 (fr) * 2008-06-13 2009-12-17 コニカミノルタオプト株式会社 Procédé de production de film acrylique, et film acrylique produit selon le procédé
JP2010179475A (ja) * 2009-02-03 2010-08-19 Konica Minolta Opto Inc 光学フィルムの製造方法、光学フィルム、偏光板及び表示装置
WO2011055590A1 (fr) * 2009-11-04 2011-05-12 コニカミノルタオプト株式会社 Bobine de film protecteur pour plaque de polarisation à cristaux liquides et son procédé de fabrication

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2018061350A1 (fr) * 2016-09-30 2018-04-05 コニカミノルタ株式会社 Procédé de fabrication de film optique
JPWO2018061350A1 (ja) * 2016-09-30 2019-07-11 コニカミノルタ株式会社 光学フィルムの製造方法

Also Published As

Publication number Publication date
KR101594265B1 (ko) 2016-02-15
KR20140035527A (ko) 2014-03-21
JPWO2013035249A1 (ja) 2015-03-23

Similar Documents

Publication Publication Date Title
JP4379547B2 (ja) 光学フィルムの製造方法
JP5521552B2 (ja) アクリル樹脂含有フィルム、それを用いた偏光板及び液晶表示装置
US8470448B2 (en) Acryl resin containing film, polarizing plate by use thereof and liquid crystal display
JP5333447B2 (ja) アクリルフィルムの製造方法およびその製造方法によって製造したアクリルフィルム
JP5652401B2 (ja) 光学フィルム
JP5402925B2 (ja) 偏光板及び液晶表示装置
JPWO2009081607A1 (ja) アクリル樹脂含有フィルム、それを用いた偏光板及び液晶表示装置
JP2012086433A (ja) 光学フィルムの製造方法
JPWO2013080847A1 (ja) アクリル樹脂含有フィルムの製造方法
JPWO2009119191A1 (ja) アクリル樹脂含有フィルム、それを用いた偏光板及び液晶表示装置
TWI468749B (zh) An optical film, a polarizing plate and a liquid crystal display device using the same
JP5533857B2 (ja) 光学フィルム、それを用いた偏光板及び液晶表示装置
JP5045539B2 (ja) 偏光板用保護フィルム、偏光板及び液晶表示装置
WO2013035249A1 (fr) Procédé de fabrication de films optiques
TWI544014B (zh) Optical film
JP2010242017A (ja) 光学フィルムの製造方法
JP5733066B2 (ja) 光学フィルム及び偏光板
JP5640743B2 (ja) 偏光板用光学フィルム、その製造方法、それを用いた偏光板及び液晶表示装置
JP5304591B2 (ja) 光学フィルム
JP2012016845A (ja) 光学フィルムの製造方法、光学フィルム、偏光板及び液晶表示装置
JPWO2010116822A1 (ja) 光学フィルム、光学フィルムを製造する方法、液晶パネル、及び画像表示装置
JP2012016844A (ja) 光学フィルムの製造方法、光学フィルム、偏光板及び液晶表示装置
JPWO2010116823A1 (ja) 光学フィルム、光学フィルムを製造する方法、液晶パネル、及び画像表示装置
JP2012198355A (ja) 偏光子保護フィルム、それを用いた偏光板及び液晶表示装置
JP5720458B2 (ja) 光学フィルムの製造における品種切り替え方法及び光学フィルム

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 12829286

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 2013532414

Country of ref document: JP

Kind code of ref document: A

ENP Entry into the national phase

Ref document number: 20147003742

Country of ref document: KR

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 12829286

Country of ref document: EP

Kind code of ref document: A1