WO2013047874A1 - 発光素子用反射基板 - Google Patents

発光素子用反射基板 Download PDF

Info

Publication number
WO2013047874A1
WO2013047874A1 PCT/JP2012/075390 JP2012075390W WO2013047874A1 WO 2013047874 A1 WO2013047874 A1 WO 2013047874A1 JP 2012075390 W JP2012075390 W JP 2012075390W WO 2013047874 A1 WO2013047874 A1 WO 2013047874A1
Authority
WO
WIPO (PCT)
Prior art keywords
inorganic
substrate
emitting element
light
layer
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/JP2012/075390
Other languages
English (en)
French (fr)
Inventor
堀田　吉則
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Fujifilm Corp
Original Assignee
Fujifilm Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Fujifilm Corp filed Critical Fujifilm Corp
Publication of WO2013047874A1 publication Critical patent/WO2013047874A1/ja
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

　バルブ金属基材上の少なくとも一部に無機反射層を備え、上記無機反射層が、ビッカース硬度（Ｈｖ）１ＧＰａ以上、赤外分光法により測定した波数３０００ｃｍ－１と波数１９００ｃｍ－１の吸光度の差（ＯＨ表面構造吸収係数）が０．４０以上である、より耐熱性が高く、耐光性にも優れ、光反射率の高い発光素子用反射基板を提供する。

Description

発光素子用反射基板
　本発明は、発光素子に用いられる光反射基板、より具体的には、発光ダイオード(以下、ＬＥＤという）等の発光素子に用いられる発光素子用反射基板およびその製造方法に関する。
　特許文献１は、樹脂とシリカエアロゲルとの混合物で、樹脂が粉体塗料である塗料組成物、金属基板の表面に塗料組成物の塗膜を形成した照明器具用反射板が記載されている。粉体塗料は樹脂分１００％の固形分であり、有機溶剤等を含まないので、疎水化処理をしたシリカエアロゲルが有機溶剤等の作用で収縮して白濁するようなことがなく、塗膜の光反射率が優れていると記載されている。
特開平１１－２９７４５号公報
　しかし、発光素子用光反射基板が、樹脂バインダーを含む場合には反射層自身の耐熱性が低く、耐光性も劣るので経年変化に耐えられないという問題がある。
　本発明者は上記背景技術の問題点を検討し、より耐熱性が高く、耐光性にも優れ、光反射率の高い発光素子用反射基板を提供することを目的とする。
　発明者は、基板表面に、特定の無機反射層が存在し、この無機反射層が特定のＯＨ基に由来する表面構造を有すると、光反射率が高く、その表面に設けられる封止樹脂層または金属配線層との密着性に優れ、このＯＨ基に由来する表面構造は耐電圧への悪影響がなくむしろ耐電圧が向上することを知見して本発明を達成した。
　すなわち、本発明は、以下を提供する。    
（１）バルブ金属基材上の少なくとも一部に無機反射層を備え、上記無機反射層が、ビッカース硬度（Ｈｖ）１ＧＰａ以上、赤外分光法により測定した波数３０００ｃｍ－１と波数１９００ｃｍ－１の吸光度の差で示されるＯＨ表面構造吸収係数が０．４０以上である発光素子用反射基板。
（２）上記バルブ金属基材と上記無機反射層との間にバルブ金属基材の陽極酸化皮膜層を有する（１）に記載の発光素子用反射基板。
（３）上記無機反射層が、リン酸アルミニウム、塩化アルミニウムおよびケイ酸ナトリウムからなる群から選択される少なくとも一つの無機結着剤と、屈折率１．５以上１．８以下、平均粒子径０．１μｍ以上５μｍ以下の無機粒子とを含有する（１）または（２）に記載の発光素子用反射基板。
（４）上記無機粒子は、酸化物、水酸化物、および無機塩からなる群から選択される少なくとも一つである（１）～（３）のいずれか１項に記載の発光素子用反射基板。
（５）上記無機粒子が硫酸バリウムおよび酸化アルミニウムからなる群から選択される少なくとも一つである（１）～（４）のいずれか１項に記載の発光素子用反射基板。
（６）上記バルブ金属が、アルミニウム、タンタル、ニオブ、チタン、ハフニウム、ジルコニウム、亜鉛、タングステン、ビスマスおよびアンチモンからなる群から選択される少なくとも１種の金属である（１）～（５）のいずれか１項に記載の発光素子用反射基板。
（７）上記バルブ金属基材の厚さが、０．１～２ｍｍである（１）～（６）のいずれか１項に記載の発光素子用反射基板。
（８）上記バルブ金属が、アルミニウムである（１）～（７）のいずれか１項に記載の発光素子用反射基板。
（９）上記発光素子用反射基板の引張強度が、３０ＭＰａ以上１００ＭＰａ以下である（１）～（８）のいずれか１項に記載の発光素子用反射基板。
（１０）上記無機粒子が、２種類以上である（１）～（９）のいずれか１項に記載の発光素子用反射基板。
（１１）バルブ金属基材表面に上の少なくとも一部に設けたビッカース硬度（Ｈｖ）１ＧＰａ以上の無機反射層を加熱水蒸気処理または親水化処理して、赤外分光法により測定した波数３０００ｃｍ－１と波数１９００ｃｍ－１の吸光度の差で示されるＯＨ表面構造吸収係数が０．４０以上である無機反射層を形成する、発光素子用反射基板の製造方法。
（１２）上記無機反射層が、無機結着剤と無機粒子とを混合して前記バブル金属基材表面に塗布され、１００℃～３００℃の温度で低温焼成される（１１）に記載の発光素子用反射基板の製造方法。
（１３）上記バルブ金属基材表面を陽極酸化処理した後に上記陽極酸化処理層上に無機反射層を形成する（１１）または（１２）に記載の発光素子用反射基板の製造方法。
（１４）上記（１１）～（１３）のいずれか１項に記載の工程を経た後、以下の（ｃ）および（ｄ）工程を任意の順序で行う、（１１）～（１３）のいずれか１項に記載の発光素子用反射基板の製造方法：
　（ｃ）発光素子への電気信号伝送のための金属配線層を形成し、上記金属配線層をパターン化する工程；
　（ｄ）発光素子を実装する部分に相当する電極部に金属層を設ける工程。
（１５）上記（１）～（１０）のいずれか１項に記載の発光素子用反射基板の上に青色発光素子を有し、その周りおよび／または上部に蛍光発光体を備える白色系発光ダイオード装置。
　本発明の発光素子用反射基板は、耐熱性が高く、耐光性に優れ、光反射率が高い。また、その表面に設けられる封止樹脂層および／または金属配線層との密着性に優れる。
図１（Ａ）は，本発明の発光素子用反射基板の好適な実施態様の一例を説明する拡大断面図であり、図１（Ｂ）は、本発明の別の好適な実施態様を説明する拡大断面図である。 本発明の発光素子用反射基板の好適な実施態様の一例を説明する概略断面図である。 本発明の発光素子用反射基板の別の実施態様を用いた発光装置を説明する断面図である。 評価に用いた配線パターンを説明する概略図である。 赤外分光法による吸光度の測定結果を示すチャートである。
　［発光素子用反射基板］
　本発明の発光素子用反射基板は、バルブ金属基材表面の少なくとも一部に無機反射層を備える基板であり、上記無機反射層が、ビッカース硬度１ＧＰａ以上であり、かつ赤外分光光度計により測定した波数３０００ｃｍ－１と波数１９００ｃｍ－１の吸光度の差（以下、ＯＨ表面構造吸収係数ということがある）が０．４０以上である発光素子用反射基板である。好ましくはビッカース硬度１ＧＰａ以上１０ＧＰａ以下であり、ＯＨ表面構造吸収係数が、０．４０以上０．８以下である。
　次に、本発明の発光素子用反射基板について図１に示す好適例を用いて説明する。
　図１は、本発明の発光素子用反射基板の好適な実施態様の一例を示す概略図である。
　図１（Ａ）に示すように、本発明の発光素子用反射基板３０は、バルブ金属基材１の少なくとも一部の表面にビッカース硬度１ＧＰａ以上であり、かつ赤外分光光度計により測定した波数３０００ｃｍ－１と波数１９００ｃｍ－１の吸光度の差（ＯＨ表面構造吸収係数）が０．４０以上である無機反射層３を備える発光素子用反射基板である。
　また、図１（Ｂ）に示すように、本発明の発光素子用反射基板３０は、基板の耐電圧が良好となり、無機反射層と基板との密着性も良好となる理由からバルブ金属基材１の少なくとも一部の表面に陽極酸化皮膜層２等の絶縁層が設けられ、その上層にビッカース硬度１ＧＰａ以上であり、かつ赤外分光光度計により測定した波数３０００ｃｍ－１と波数１９００ｃｍ－１の吸光度の差（ＯＨ表面構造吸収係数）が０．４０以上である無機反射層３を備える発光素子用反射基板であるのが好ましい。
〔無機反射層〕
　１）無機反射層は構成材料が無機成分であり、ビッカース硬度１ＧＰａ以上である。好ましくはビッカース硬度１ＧＰａ以上１０ＧＰａ以下である。ビッカース硬度の試験法は、ダイヤモンド圧子を材料表面に押し込み、荷重を除いたあとに残ったへこみの対角線の長さｄ（ｍｍ）から表面積Ｓ（ｍｍ２）を算出する。試験荷重Ｆ（Ｎ）を算出した表面積Ｓ（ｍｍ２）で割った値の０．１０２倍の値がビッカース硬さ（Ｈｖ）であり、以下の式で求められる。
　　Ｈｖ＝０．１０２（Ｆ／Ｓ）
　２）無機反射層の表面を赤外分光光度計により測定した波数３０００ｃｍ－１と波数１９００ｃｍ－１の吸光度の差が０．４０以上である。赤外分光法（infrared spectroscopy、略称ＩＲ）は、測定対象の物質に赤外線を照射し、透過（あるいは反射）光を分光することでスペクトルを得て、対象物の特性を知る方法で、対象物の分子構造や状態を示す値であり、対象物の表面構造によっても、赤外スペクトルは微妙に変化する。これより、特定の物質の表面構造などについても知ることができる。
　後に説明する実施例１および比較例３の無機反射層表面の赤外吸収スペクトルを測定した結果を図５に示す。
　図５の結果が示すように、実施例１と比較例３との表面状態の差は、３０００～４０００ｃｍ－１の波数範囲に示される。この波数範囲は、水などに起因するＯＨ基の伸縮振動に対応する。実施例１と比較例３との３０００～４０００ｃｍ－１の波数範囲に示される表面状態の差を表す指標として、本発明者は、以下のＯＨ表面構造吸収係数を設定すると表面状態の差が示せることを発見した。
［ＯＨ表面構造吸収係数］＝［波数３０００ｃｍ－１の吸光度］‐［波数１９００ｃｍ－１の吸光度］
　例えば、実施例１と比較例３との図５に示す測定値から以下のＯＨ表面構造吸収係数が得られる。
Figure JPOXMLDOC01-appb-T000001
　参考例は、以下の条件で調整した。
　参考例：粒子径　０．５２μｍ　純度９９．９％　のアルミナ（ＡＬ-１６０ＳＧ-３）粉体を１ｇ秤量し、ハンドプレス装置で荷重１ｔでプレスして直径２０ｍｍのタブレットに成形し、タブレットを１６００℃、２時間焼結した。
　本発明の無機反射層は、上記１）および２）の条件を満たしていて、構成材料が無機成分であれば、特に限定されない。有機成分を含まないことが好ましい。無機反射層は無機材料であるので、耐熱性、耐光性が高く、経年変化にも強い。
　無機反射層は、本発明の発光素子用反射基板において、バルブ金属基材上に設けられる。絶縁性がより良好となる理由から、上記金属基材上に絶縁層を有する基板であるのが好ましい。具体的には、バルブ金属基材１上の一部に陽極酸化皮膜層２と無機反射層３とを有していてもよく、陽極酸化皮膜層２だけの部分が存在してもよい。実装する素子の形や配線の位置によって陽極酸化皮膜層である絶縁層や、無機反射層の必要な位置が異なり、各種のデザインで配置される必要があるからである。
　本発明においては、上記無機反射層の厚さは、１０μｍ以上であり、１０～６０μｍであるのが好ましく、２０～５０μｍであるのがより好ましい。
　上記無機反射層の厚さが１０μｍ以上であると、耐電圧が良好となる。また、上記無機反射層の厚さが６０μｍ以下であると、可撓性が保持され、加工性、取扱性等が良好になる。
　本発明に用いられるバルブ金属基材の板の厚みは、０．１～２．０ｍｍが好ましい。特にアルミニウム板の厚みは、０．１～２．０ｍｍ程度であり、０．１５～１．５ｍｍであるのが好ましく、０．２～１．０ｍｍであるのがより好ましい。この厚さは、ユーザーの希望等により適宜変更することができる。
　バルブ金属基材に陽極酸化皮膜層を設ける場合は、陽極酸化皮膜層の厚さは１～２００μｍであるのが好ましい。１μｍ未満であると耐電圧に乏しく耐電圧が低下し、一方、２００μｍを超えると製造に多大な電力が必要となり、経済的に不利となる。陽極酸化皮膜層の厚さは、１０μｍ以上が好ましく、２０μｍ以上がさらに好ましい。
　ここで、上記陽極酸化皮膜層、または無機反射層の膜厚の測定方法は、以下に示す通りである。
　まず、陽極酸化皮膜層または無機反射層を設けた基板を折り曲げて作製した破断面を超高分解能走査型電子顕微鏡（例えば、Ｓ－４０００、日立製作所社製）によって観察して撮影する。なお、観察倍率は、膜厚等により適宜調整して行う。具体的には、倍率１００～１００００倍であるのが好ましい。また、観察範囲は、断面長として１００μｍ以上の部分を観察するものとする。
　次いで、上記方法で得られた画像データ（写真）の多孔質部分について、観察範囲の中で最も厚くなる部分の膜厚を上記無機反射層の膜厚とする。
＜無機反射層の表面特性＞
　ＯＨ表面構造吸収係数と無機反射層の表面構造との関係を検証するために、上記でＯＨ表面構造吸収係数を測定した実施例１、比較例３および実施例１で使用したアルミナ粒子のみを１６００℃で２時間焼結して得られた表面（参考例）を１００℃～５００℃での熱重量分析を行った。ＴＧＡ　Ｑ５００（ティー・エイ・インスツルメント・ジャパン株式会社製）を用い、昇温速度５℃／ｍｉｎで測定した。３００℃における熱重量減少後の質量を初期値１００％として規格化した値を下記表２に示す。表２の結果が示すように、ＯＨ基が多いと考えられる表面構造では、表面の水分を失うことによる熱重量分析での重量減少が大きいことが確認できた。
Figure JPOXMLDOC01-appb-T000002
　＜好適な無機反射層＞
　好適な無機反射層は、無機粒子と無機結着剤とを含有し、無機結着剤によって互いの一部が結着した多数の無機粒子からなる集合体で、表面が加熱水蒸気処理または親水化処理されている無機反射層である。以下に具体的に説明する。
（無機結着剤）
　本発明では特定の無機粒子の結着剤（バインダー）として、リン酸アルミニウム、塩化アルミニウム、またはケイ酸ナトリウムを用いる。これらの２種以上の混合物を用いてもよい。
　無機結着剤は、後に説明する無機粒子同士を低温焼成によって結合し無機反射層を構成する物質である。詳細には以下が例示できる。
（リン酸アルミニウム）
　上記リン酸アルミニウムは、メタリン酸アルミニウム、オルトリン酸アルミニウム、ポリリン酸アルミニウムが例示できる。
（塩化アルミニウム）
　上記塩化アルミニウムは、塩化アルミニウム、無水塩化アルミニウム、塩化アルミニウム６水和物、ポリ塩化アルミニウム（水酸化アルミニウムを塩酸に溶解させて生成する塩基性塩化アルミニウムの重合体）が例示できる。
（ケイ酸ナトリウム）
　上記ケイ酸ナトリウムは、ケイ酸ソーダまたは水ガラスとも呼ばれるものであり、メタケイ酸のナトリウム塩であるＮａ2ＳｉＯ3が一般的だが、その他に、Ｎａ4ＳｉＯ4、Ｎａ2Ｓｉ2Ｏ5、Ｎａ2Ｓｉ4Ｏ9なども用いることができる。メタケイ酸のナトリウム塩は、二酸化ケイ素を炭酸ナトリウムまたは水酸化ナトリウムと融解して得ることができる。
（無機結着剤前駆物質）
　無機結着剤は無機結着剤前駆物質を水の存在下で反応させて得ることができる。
　無機結着剤前駆物質には、リン酸、塩酸、硫酸等の無機酸、アルミニウム、および酸化アルミニウム、硫酸アルミニウム、水酸化アルミニウム、塩化アルミニウム、リン酸アルミニウム等のアルミニウム化合物、およびこれらの混合物が挙げられる。反応物の中和が必要な場合は水酸化ナトリウム溶液を用いる。アルミニウム化合物はそれぞれの原料を無機結着剤前駆物質として反応させて製造してもよい。
　無機結着剤前駆物質には、上記アルミニウム塩のうち、水酸化アルミニウムと塩化アルミニウムの両方を添加することが好ましく、塩化アルミニウムの量が水酸化アルミニウムの量に対して５質量％～１０質量％であることが好ましい。塩化アルミニウムは水酸化アルミニウムとリン酸との反応を触媒的に進行させる役割を有すると考えられ、上記範囲の量であることが好ましい。また、塩化アルミニウムと塩酸とを用いて、リン酸アルミニウム前駆物質を用いない場合は、無機結着剤であるポリ塩化アルミニウムが着色しないので光反射率が高い。
　リン酸アルミニウムにかえてまたはリン酸アルミニウムと共に、リン酸塩化合物を用いてもよく、リン酸塩化合物としては、水に不溶性であれば、特に限定する必要はない。具体例としてリン酸マグネシウム、リン酸カルシウム、リン酸亜鉛、リン酸バリウム、リン酸アルミニウム、リン酸ガリウム、リン酸ランタン、リン酸チタニウム、リン酸ジルコニウムを挙げることが出来る。リン酸アルミニウムが好ましく、他のリン酸塩と混合する場合は５０質量％以上がリン酸アルミニウムであるのが好ましい。
　ケイ酸ナトリウムを用いる場合は、水に溶かし加熱して水ガラスとして適切な粘度に調整して無機結着剤前駆物質として用いる。
　これらの無機結着剤前駆物質は目的とする無機結着剤を生成するように任意の組合せで混合して用いることができる。
　（無機粒子）
　本発明においては、上記無機粒子は特に限定されず、例えば、従来公知の金属酸化物、金属水酸化物、炭酸塩、硫酸塩などを用いることができ、中でも、金属酸化物を用いるのが好ましい。
　上記無機粒子としては、具体的には、例えば、酸化アルミニウム（アルミナ）、酸化マグネシウム、酸化イットリウム、酸化チタン、酸化亜鉛、二酸化ケイ素、酸化ジルコニウムなどの金属酸化物；水酸化アルミニウム、水酸化カルシウム、水酸化マグネシウムなどの水酸化物；炭酸カルシウム（軽質炭酸カルシウム、重質炭酸カルシウム、極微細炭酸カルシウムなど）、炭酸バリウム、炭酸マグネシウム、炭酸ストロンチウムなどの炭酸塩；硫酸カルシウム、硫酸バリウムなどの硫酸塩；また、その他に、カルシウムカーボネート、方解石、大理石、石膏、カオリンクレー、焼成クレー、タルク、セリサイト、光学ガラス、ガラスビーズなどが挙げられる。
　この中でも、後述する無機結着剤との親和性が良好となる理由から、酸化アルミニウム、二酸化ケイ素、水酸化アルミニウム、硫酸バリウムが好ましい。酸化アルミニウムがさらに好ましい。
　好適な無機反射層に用いる無機粒子は、屈折率が、１．５以上１．８以下であり、好ましくは１．５５以上１．７５以下である。屈折率がこの範囲であると得られる無機反射層の反射率が高い。この理由は、空気との反射率の差異によるものであると考えられる。
　無機粒子の平均粒子径は、好ましくは０．１μｍ以上５μｍ以下である。より好ましくは０．５～２μｍであり、さらに好ましくは０．５～１．５μｍである。平均粒子径がこの範囲の無機粒子を用いると、粒子間に適切な空隙を確保することができ、陽極酸化皮膜層との密着性も得ることができると考えられる。平均粒径が０．１μｍ未満であると反射率が劣り、粒径が６μｍ超であると陽極酸化皮膜層との密着性に劣る場合がある。ここで、平均粒子径は例えば、レーザー回折散乱法（レーザー回折／散乱式粒子径分布測定装置、Ｐａｒｔｉｃａ　ＬＡ-９１０、堀場製作所社製など）を用いて測定された５０％体積累積径（Ｄ５０）をいう。
　従来技術における１０００℃以上などの高温焼結で無機粒子を結着させ、いわゆるセラミック層を製造する工程では、層中に特定の空隙を確保するためには高温焼結の進行の制御が必要である。これに対し本発明の好ましい無機反射層は低温での加熱乾燥により高温焼結を行なわないので原料としての無機粒子の平均粒子径が無機反射層の空隙率および表面硬度を決めるため反射率に影響する重要なファクターとなる。従来技術における１０００℃以上などの高温焼結で無機粒子を結着させた、いわゆるセラミック層は、赤外分光法により測定した波数３０００ｃｍ－１と波数１９００ｃｍ－１の吸光度の差であるＯＨ表面構造吸収係数が０．１０未満である。
　上記無機粒子としては限定されないが例えば以下の無機粒子が例示できる。
　酸化アルミニウム（アルミナ）（屈折率ｎ＝１．６５～１．７６、以下、括弧内の数字は屈折率である）、水酸化アルミニウム（１．５８～１．６５～１．７６）、水酸化カルシウム（１．５７～１．６）、炭酸カルシウム（１．５８）、方解石（１．６１）、カルシウムカーボネート（１．６１）、軽質炭酸カルシウム（１．５９）、重質炭酸カルシウム（１．５６）、極微細炭酸カルシウム（１．５７）、石膏（１．５５）、硫酸カルシウム（１．５９）、大理石（１．５７）、硫酸バリウム（１．６４）、炭酸バリウム（１．６）、酸化マグネシウム（１．７２）、炭酸マグネシウム（１．５２）、水酸化マグネシウム（１．５８）、炭酸ストロンチウム（１．５２）、カオリンクレー（１．５６）、焼成クレー（１．６２）、タルク（１．５７）、セリサイト（１．５７）、光学ガラス（１．５１～１．６４）、ガラスビーズ（１．５１）。用いる粒子の素材は上記の範囲の屈折率を満たせば良く、焼結という工程が無いため、酸化物に限らず各種の無機塩を用いる事が出来る。
　また、上記特性を満たすものであれば２種類以上の粒子または２種類以上の平均粒子径を有する粒子を混合して使用してもよい。異なる粒径の粒子や異なる素材のものを組み合わせることにより、膜強度の向上や、基板との密着強度の向上を図ることが出来る。
　さらには塗布面の性状の改良で表面が滑らかになる効果も期待できる。
　更に、上記無機粒子の形状は特に限定はされず、例えば、球状、多面体状（例えば、２０面体状、１２面体状等）、立方体状、４面体状、表面に凹凸状ないし凸状の突起を複数有する形状（以下、「コンペイトウ形状」ともいう。）、板状、針状等いずれであってもよい。
　これらのうち、断熱性に優れる理由から、球状、多面体状、立方体状、４面体状、コンペイトウ形状が好ましく、入手が容易で断熱性により優れる理由から、球状であるのがより好ましい。
　＜無機反射層＞
　上記で例示する好適な無機反射層は、加熱乾燥後の単位面積当たりの質量で、２０ｇ／ｍ２～５００ｇ／ｍ２とするのが好ましい。この範囲であると、空隙をその内部に残しているために光の透過が抑制され、反射率が高い。上記の特定の無機結着剤を用いる事で高温焼結を不要とし、より低コストで無機反射層を製造することが可能である。無機反射層は無機材料であり、経年変化にも強い。更に、反射層形成時に基板の陽極酸化皮膜と反応して、基板との密着性も担保する事が可能となる。
　好適な無機反射層中の無機粒子の量と、リン酸アルミニウム、塩化アルミニウム、およびケイ酸ナトリウムからなる群から選択される少なくとも一つの無機結着剤の量とは、無機粒子１００質量部に対して無機結着剤５～１００質量部が好ましく、１０～５０質量部がより好ましい。
　好適な無機反射層には、上記無機粒子と無機結着剤以外に、他の化合物を含有してもよい。他の化合物としては、例えば、分散剤、反応促進剤等が挙げられ、また、これらと、上記無機粒子、無機結着剤前駆物質、無機粒子と無機結着剤との反応生成物等が挙げられる。
＜好適な無機反射層の製造方法＞
　以上で説明した好適な無機反射層の製造方法は、特に限定されないが、以下で説明するバインダー液として無機結着剤および／または無機結着剤前駆物質と無機粒子を混合して、この混合液を塗布膜厚が調整可能なコーターを用いて陽極酸化皮膜層上に所定量塗布し、その後１００℃～３００℃で、１０～６０分間、加熱処理（低温焼成）するのが好ましい。
　塗布方法は特に限定されず、種々の方法を用いることができるが、例えば、バーコーター塗布、回転塗布、スプレー塗布、カーテン塗布、ディップ塗布、エアーナイフ塗布、ブレード塗布、ロール塗布等を挙げることができる。
　反応式に従う化学量論組成比で無機結着剤前駆物質と無機粒子との水分散体を調整すると、反応が進むとともに液の粘度が急激に上昇する。このような現象を回避し安定的に無機反射層を形成させる目的で予め若干の水を添加しておくことが望ましい。また、陽極酸化皮膜層中にリン酸根が残存する事は基板の腐食や、ＬＥＤの封止材の劣化などをもたらす事があり望ましくない。よって化学量論比に対しリン酸以外成分の量を若干過剰に処方しておくことが望ましい。
　加熱乾燥後の皮膜中にリン酸アルミニウム、塩化アルミニウム、またはケイ酸ナトリウムが生成していることは赤外分光光度計で皮膜表面を分析すれば容易に確認する事が出来る。
　また、無機反射層を異なる組成のバインダー液を２種類以上調整して陽極酸化皮膜上に順次塗布することにより２層以上とすることもできる。２層以上の無機反射層を組み合わせることにより、無機反射層強度の向上や、基板との密着強度の向上を図ることが出来る。さらには塗布面の性状の改良で表面が滑らかになる効果も期待できる。
　無機反射層が２層以上である場合は、本発明では、最表面となる無機反射層が、ビッカース硬度１ＧＰａ以上、ＯＨ表面構造吸収係数が０．４０以上であれば、他の無機反射層はこの要件以外の無機反射層を用いることもできる。好ましくは２層以上の各無機反射層がそれぞれビッカース硬度１ＧＰａ以上、１０ＧＰａ以下、ＯＨ表面構造吸収係数が０．４０以上０．８０以下である。
（低温焼成）
　上記の低温焼成により、反応を進め無機粒子同士を反応により生成する無機結着剤により結着する。
　低温焼成温度は１００℃～３００℃であり、１５０℃～３００℃であるのが好ましく、１８０℃～２５０℃である事がより好ましい。
　１００℃未満では水分の除去が適わず、３００℃超ではアルミニウム基材の強度変化が起こるので望ましくない。また、無機結着剤前駆物質間の反応を進め、結着させるには１５０℃以上の温度が望ましく、さらに得られる無機結着剤に残存する吸着水を完全に除去するためには１８０℃以上であることが望ましい。２５０℃を超えた温度で長時間処理を行なうとバルブ金属基材の強度が変化するため、２５０℃以下で処理する事が望ましい。
　焼成時間は１０分～６０分であり、２０分～４０分が更に好ましい。短時間では反応の進捗が不十分であり、長時間になると焼成温度との関係でバルブ金属基材、特にアルミニウム金属基材の強度変化をきたす。６０分以上では製造コスト的にも望ましくない。この理由から、焼成時間は２０分～４０分がもっとも好ましい。
　このような低温での焼成処理によって得られる無機反射層の表面硬度は結着処理条件、用いる粒子サイズなどにより変化するが、高い硬度を得るには焼成温度とともに粒子サイズを選択する事が重要である。無機粒子の平均粒子径は、好ましくは０．１μｍ以上５μｍ以下である。この範囲の平均粒子径の粒子を上記範囲の温度で焼成すると得られる無機反射層の表面硬度が適切となる。
　バインダー液は水分を含む液であるため、塗布後上記低温焼成処理の前に乾燥工程を入れてもよい。リン酸アルミニウム等の無機結着剤の生成反応や無機粒子の結着反応を起こさない１００℃以下の温度で乾燥させる。
＜後処理＞
　本発明の無機反射層は構成する材料と製造方法の組合せにより、その表面が、ＯＨ表面構造吸収係数が０．４０以上とすることができる。また、上記で例示する好適な無機反射層は、低温焼成処理後、その表面を後処理されるのが好ましい。好ましい後処理は、次の加熱水蒸気処理または親水化処理が例示されるが、これらのみには限定されず、これらと同等で上記好適な無機反射層の表面を、赤外分光法により測定にして得られるＯＨ表面構造吸収係数が０．４０以上とする処理である。
　本発明の無機反射層は、本発明者の知見によれば、後処理をすることで、アルミナ水和物等またはリン酸アルミニウム等の水和物の存在により、本発明の発光素子用反射基板の熱伝導性、反射率を損なわずに耐電圧を向上させることができる。このことは予想できない顕著な効果であった。
（加熱水蒸気処理）
　本発明においては、好適な無機反射層は、上記低温焼成処理を施した後に、加熱水蒸気処理を施すのが好ましい。加熱水蒸気処理は、温度と圧力の条件から、沸騰水処理、熱水処理、蒸気処理、等を含む処理である。
　使用される水は、イオン交換水、蒸留水、天然水、水道水等のいずれでも使用できるがイオン交換水、蒸留水が好ましい。またこれらの水に対し処理の促進、水中の金属イオンの封鎖剤として、有機溶媒、アミン化合物、有機酸、リンまたは硼素の酸素酸塩等を単独または二種類以上混合してもよい。また、使用される水は、リチウム、ナトリウムあるいはマグネシウムなどのアルカリ金属アルカリ土類金属のイオンを含んでも良い。
　水蒸気を使用して連続的に表面処理することが好ましく、水蒸気処理する場合の温度は約８０℃～２００℃で、好ましくは約９０℃～１２０℃である。処理時間は３秒～３０分で、好ましくは５秒～１０分である。水素イオン濃度は約２～１１が適切で、好ましくは約３～１０である。加圧水蒸気で処理する時の圧力は約１～１５ｋｇ／ｃｍ２（絶対圧）が適切であり、好ましくは約１～５ｋｇ／ｃｍ２が好ましい。
　工業的には、処理室内に設けられた水槽内の水の温度を加熱し、それによって処理室内の温度を８０℃以上１０５℃以下にし、処理室内圧として常圧に対し－５０～３００ｍｍＡｑに保った状態の中を、加熱水蒸気処理が必要な無機反射層を通過させる方法を行ってもよい。
（親水化処理）
　本発明においては、好適な無機反射層は、上記低温焼成処理を施した後に、親水化処理を施すのが好ましい。
　上記親水化処理の方法としては、具体的には、例えば、アルカリ金属ケイ酸塩の水溶液に浸漬させる方法等が挙げられる。
　ここで、アルカリ金属ケイ酸塩の水溶液を用いた親水化処理は、米国特許第２，７１４，０６６号明細書および米国特許第３，１８１，４６１号明細書に記載されている方法および手順に従って行うことができる。
　上記アルカリ金属ケイ酸塩としては、具体的には、例えば、ケイ酸ナトリウム、ケイ酸カリウム、ケイ酸リチウム等が挙げられる。
　また、上記アルカリ金属ケイ酸塩の水溶液は、更に、水酸化ナトリウム、水酸化カリウム、水酸化リチウム等を含有してもよい。
　更に、上記アルカリ金属ケイ酸塩の水溶液は、更に、アルカリ土類金属塩または４族（第ＩＶＡ族）金属塩を含有してもよい。
　ここで、上記アルカリ土類金属塩としては、具体的には、例えば、硝酸カルシウム、硝酸ストロンチウム、硝酸マグネシウム、硝酸バリウム等の硝酸塩；硫酸塩；塩酸塩；リン酸塩；酢酸塩；シュウ酸塩；ホウ酸塩；等が挙げられる。
　また、上記４族（第ＩＶＡ族）金属塩としては、具体的には、例えば、四塩化チタン、三塩化チタン、フッ化チタンカリウム、シュウ酸チタンカリウム、硫酸チタン、四ヨウ化チタン、塩化酸化ジルコニウム、二酸化ジルコニウム、オキシ塩化ジルコニウム、四塩化ジルコニウム等が挙げられる。
　これらのアルカリ土類金属塩および４族（第ＩＶＡ族）金属塩は、一種単独で用いてもよく、２種以上を併用してもよい。
　上記親水化処理は、上記アルカリ金属ケイ酸塩の水溶液を用いた場合、アルカリ金属ケイ酸塩の水溶液は、ケイ酸塩の成分である酸化ケイ素ＳｉＯ2とアルカリ金属酸化物Ｍ2Ｏの比率（一般に〔ＳｉＯ2〕／〔Ｍ2Ｏ〕のモル比で表す。）と濃度によって保護膜厚の調節が可能である。
　ここで、Ｍとしては、特にナトリウム、カリウムが好適に用いられる。
　また、モル比は、〔ＳｉＯ2〕／〔Ｍ2Ｏ〕が０．１～５．０が好ましく、０．５～３．０がより好ましい。　更に、ＳｉＯ2の含有量は、０．１～２０質量％が好ましく、０．５～１０質量％がより好ましい。
　また、上記アルカリ金属ケイ酸塩の水溶液の温度は、１～７０℃であるのが好ましく、２～５０℃であるのがより好ましく、３～３５℃であるのが更に好ましい。
　また、上記アルカリ金属ケイ酸塩の水溶液を用いた場合の処理時間は、５秒～９０分であるのが好ましく、８秒～６０分であるのが好ましく、１２秒～３０分であるのが更に好ましい。
〔バルブ金属基材〕
　バルブ金属としては、具体的には、例えば、アルミニウム、タンタル、ニオブ、チタン、ハフニウム、ジルコニウム、亜鉛、タングステン、ビスマス、アンチモン等が挙げられる。
　バルブ金属の陽極酸化皮膜層は、電気抵抗率（１０14Ω・ｃｍ程度）を有する耐熱性の高い絶縁被膜である。
　これらのうち、寸法安定性がよく、比較的安価であることからアルミニウムの陽極酸化皮膜層であるのが好ましい。
　バルブ金属基材は、単独の板で本発明の反射基板に用いてもよい。
　バルブ金属基材は、必要な場合は鋼板等の他の金属板、ガラス板、セラミック板、樹脂製板等に積層して本発明の反射基板に設けられる。陽極酸化皮膜を形成し耐電圧を担保するためにはバブル金属基材は、厚さ１０μｍ以上の板状の部分があればよい。他の板材とバルブ金属基材とを積層して用いる場合には、可撓性があり、耐熱性の高い鋼板や金属板との積層板が好ましい。
（アルミニウム板）
　本発明の反射基板の製造には、公知のアルミニウム板を用いることができる。本発明に用いられるアルミニウム板は、寸度的に安定なアルミニウムを主成分とする金属であり、アルミニウムまたはアルミニウム合金からなる。純アルミニウム板のほか、アルミニウムを主成分とし微量の異元素を含む合金板を用いることもできる。
　本明細書においては、上述したアルミニウムまたはアルミニウム合金からなる各種の基板をアルミニウム板と総称して用いる。上記アルミニウム合金に含まれてもよい異元素には、ケイ素、鉄、銅、マンガン、マグネシウム、クロム、亜鉛、ビスマス、ニッケル、チタン等があり、合金中の異元素の含有量は１０質量％以下である。
　このように本発明に用いられるアルミニウム板は、その組成が特定されるものではなく、アルミニウムの純度は特に問わないが、通常板材として用いられる１０００系、３０００系、５０００系の合金を用いることができる。しかし発光素子用反射基板として用いる場合に耐電圧に優れる事が求められ、素材中の金属間化合物などの粒子を出来るだけ少なくする事が望ましい。熱処理条件で回避できない場合には、９９．９％以上の高純度のアルミニウムを用いる事も有用である。
　具体的には、アルミニウムハンドブック第４版（１９９０年、軽金属協会発行）に記載されている従来公知の素材、例えば、ＪＩＳ　Ａ１０５０、ＪＩＳ　Ａ１１００、ＪＩＳ　Ａ１０７０、Ｍｎを含むＪＩＳ　Ａ３００４、国際登録合金　３１０３Ａ等のＡｌ－Ｍｎ系アルミニウム板を適宜利用することができる。また、引張強度を増す目的で、これらのアルミニウム合金に０．１質量％以上のマグネシウムを添加したＡｌ－Ｍｇ系合金、Ａｌ－Ｍｎ－Ｍｇ系合金（ＪＩＳ　Ａ３００５）を用いることもできる。更に、ＺｒやＳｉを含むＡｌ－Ｚｒ系合金やＡｌ－Ｓｉ系合金を用いることもできる。更に、Ａｌ－Ｍｇ－Ｓｉ系合金を用いることもできる。
　Ａｌ－Ｍｇ系合金、Ａｌ－Ｍｎ系合金、Ａｌ－Ｍｎ－Ｍｇ系合金、Ａｌ－Ｚｒ系合金、Ａｌ－Ｍｇ－Ｓｉ系合金に関しては、国際公開ＷＯ２０１０／１５０８１０号の段落［００３４］～［００３８］に記載の公報に記載されている。
　アルミニウム合金を板材に製造する方法、ＤＣ鋳造法、連続鋳造法、アルミニウム板の表面の結晶組織、アルミニウム板の金属間化合物については、国際公開ＷＯ２０１０／１５０８１０号の段落［００３９］～［００５０］に記載されている。
　本発明においては、上記に示されるようなアルミニウム板をその最終圧延工程等において、積層圧延、転写等により凹凸を形成させて粗面化処理して用いることもできる。基板表面を予め粗面化処理しておけば、陽極酸化皮膜層を形成した後に、その上に形成される無機反射層と基板との密着性を向上させることができる。その他の粗面化処理方法は後に説明する。
　本発明に用いられるアルミニウム板は、アルミニウムウェブであってもよく、枚葉状シートであってもよい。
〔発光素子用反射基板の製造方法〕
＜１．粗面化処理＞
　本発明の反射基板を製造する際にアルカリ脱脂したアルミニウム板を直接陽極酸化処理して陽極酸化皮膜層を形成してもよい。また、アルミニウム表面を予め粗面化処理して、陽極酸化処理すれば、陽極酸化皮膜層とアルミニウム板との密着性を向上させることができる。粗面化処理は、アルミニウム板に機械的粗面化処理、アルカリエッチング処理、酸によるデスマット処理および電解液を用いた電気化学的粗面化処理を順次施す方法、アルミニウム板に機械的粗面化処理、アルカリエッチング処理、酸によるデスマット処理および異なる電解液を用いた電気化学的粗面化処理を複数回施す方法、アルミニウム板にアルカリエッチング処理、酸によるデスマット処理および電解液を用いた電気化学的粗面化処理を順次施す方法、アルミニウム板にアルカリエッチング処理、酸によるデスマット処理および異なる電解液を用いた電気化学的粗面化処理を複数回施す方法が挙げられるが、本発明はこれらに限定されない。これらの方法において、上記電気化学的粗面化処理の後、更に、アルカリエッチング処理および酸によるデスマット処理を施してもよい。
　中でも、他の処理（アルカリエッチング処理等）の条件にもよるが、大波構造、中波構造および小波構造が重畳した表面形状を形成させるには、機械的粗面化処理、硝酸を主体とする電解液を用いた電気化学的粗面化処理および塩酸を主体とする電解液を用いた電気化学的粗面化処理を順次施す方法が好適に挙げられる。また、大波構造および小波構造が重畳した表面形状を形成させるには、塩酸を主体とする電解液を用い、アノード反応にあずかる電気量の総和を大きくした電気化学的粗面化処理のみを施す方法が好適に挙げられる。
　各粗面化処理の詳細については、国際公開ＷＯ２０１０／１５０８１０号の段落［００５５］～［００８３］に記載されている。
＜２．スルーホール加工＞
　本発明の発光素子用反射基板においては、発光素子を実装するにあたり、適宜配線部を設けるためのスルーホール加工、並びに、最終製品を想定してのチップ化を行うためのルーティング加工（最終製品に個別化するための加工）を行うこともできる。スルーホール加工は、必要な個所への穴あけ加工であるが、加工されるスルーホールの形状については、配線が必要な複数の層の間の長さで、その断面は必要な配線をその中に入れて確保できる大きさ／形状であれば特に制限されないが、最終的なチップの大きさ、及び、確実な配線の形成を考えると、円形であることが好ましく、大きさは、０．０１ｍｍφ～２ｍｍφが好ましく、０．０５ｍｍφ～１ｍｍφがより好ましく、０．１ｍｍφ～０．８ｍｍφが特に好ましい。
（ルーティング加工）
　ルーティング加工は、最終製品に個別化された発光素子用反射基板（以下チップという）の大きさに切り離す個別切り離し加工または、予めチップに切り離しやすい形状にする加工であり、パターン加工、チップ化ともいう。ルーティング加工には、ルーターと呼ばれる装置で基板の厚み方向に貫通した切込みを入れたり、ダイサーを用いて厚み方向に切断しない程度に切り込み（切り欠き）を入れるような加工を含む。
＜３．焼成処理＞
　前述のルーティング加工、スルーホール加工におけるアルミニウム板のＪＩＳ Ｚ２２４１による引張試験（引張速度：２ｍｍ／分）における引っ張り強度（以下引張強度という。）は、１００ＭＰａ以下のように軟質な基板であることは加工性が低下するため好ましくなく、本発明の発光素子用反射基板を製造するに当たってはルーティング加工、スルーホール加工等の機械加工後、アルミニウム板を軟質化するため焼成する事が望ましい。また、陽極酸化処理を施した後に焼成を施すとアルミと皮膜の間の熱膨張率差に起因するクラックなどが入る恐れがあり、望ましくない。よって機械加工後、陽極酸化処理前にアルミニウム板の強度を調整する焼成処理を行うことが望ましい。機械加工後、陽極酸化処理前の焼成処理は２５０℃～４００℃で、１分～１２０分加熱処理するのが好ましい。陽極酸化処理後の焼成処理を行う場合は、焼成温度は２００℃～２５０℃で、６０分～３００分加熱処理するのが好ましい。
＜４．陽極酸化処理＞
　以上のように表面処理され、加工されたアルミニウム板に、更に、陽極酸化処理を施すのが好ましい。陽極酸化処理により、アルミナからなる陽極酸化皮膜層がアルミニウム板の表面に形成され、多孔質、あるいは、非孔質の表面絶縁層が得られる。
　陽極酸化処理は、従来行われている方法で行うことができる。この場合、例えば、硫酸濃度５０～３００ｇ／Ｌで、アルミニウム濃度５質量％以下の水溶液中で、アルミニウム板を陽極として通電して陽極酸化皮膜層を形成させることができる。陽極酸化処理に用いられる溶液としては、硫酸、リン酸、クロム酸、シュウ酸、スルファミン酸、ベンゼンスルホン酸、アミドスルホン酸、マロン酸、クエン酸、酒石酸、ホウ酸、等を単独でまたは２種以上を組み合わせて用いることができる。
　陽極酸化処理の条件は、使用される電解液によって種々変化するので一概に決定され得ないが、一般的には電解液濃度１～８０質量％、液温５～７０℃、電流密度０．５～６０Ａ／ｄｍ2、電圧１～１００Ｖ、電解時間１５秒～５０分であるのが適当であり、所望の陽極酸化皮膜層量となるように調整される。
　硫酸を含有する電解液中で陽極酸化処理を行う場合には、アルミニウム板と対極との間に直流を印加してもよく、交流を印加してもよい。アルミニウム板に直流を印加する場合においては、電流密度は、１～６０Ａ／ｄｍ2であるのが好ましく、５～４０Ａ／ｄｍ2であるのがより好ましい。連続的に陽極酸化処理を行う場合には、アルミニウム板の一部に電流が集中していわゆる「焼け」が生じないように、陽極酸化処理の開始当初は、５～１０Ａ／ｄｍ2の低電流密度で電流を流し、陽極酸化処理が進行するにつれ、３０～５０Ａ／ｄｍ2またはそれ以上に電流密度を増加させるのが好ましい。連続的に陽極酸化処理を行う場合には、アルミニウム板への給電方式は液給電方式により行うのが好ましい。液給電方式は、コンダクタロールを用いない間接給電方式であり、電解液を介して給電する。
　陽極酸化皮膜層は、多孔質であっても無孔質であってもよい。多孔質である場合、その平均ポア径が５～１０００ｎｍ程度であり、平均ポア密度が１×１０6～１×１０10／ｍｍ2程度である。
　陽極酸化処理のその他の詳細については、国際公開ＷＯ２０１０／１５０８１０号の段落［００９１］～［００９４］に記載されている。
　アルミニウムは熱伝導率が非常に高いので放熱性に優れる点で、他の金属に勝るだけでなく、表層に陽極酸化皮膜層を形成させることで耐電圧を付与する事も可能である。
　予めＬＥＤを実装する基板形状に加工したもの、例えば六角形、八角形状のものやスルーホールが形成されているものを陽極酸化処理して基板として用いてもよいし、陽極酸化処理し、前述の無機反射層を形成した後に加工してもよい。
　陽極酸化皮膜層の厚さは１～２００μｍであるのが好ましい。１μｍ未満であると絶縁性に乏しく耐電圧が低下し、一方、２００μｍを超えると製造に多大な電力が必要となり、経済的に不利となる。陽極酸化皮膜層の厚さは、１０μｍ以上が好ましく、２０μｍ以上がさらに好ましい。
＜５．無機反射層の形成＞
　さらに、予めチップまたは複数のチップを含むパーツに分解できるような加工を施した基板に、各種の印刷手法例えばスクリーン印刷等によって光反射が必要な部分にのみ、前述の無機反射層を形成してもよい。この方法で無機反射層を形成すれば、無機反射層に用いる原料を節約できる。
（発光素子用反射基板）
　以上で説明した本発明の無機反射層を有する発光素子用反射基板は、他の金属板を芯材等の補強用に用いない場合でバルブ金属基材としてバルブ金属板を単独で用いる場合は、強度はＪＩＳ Ｚ２２４１による引張試験（引張速度：２ｍｍ／分）における引っ張り強度（以下引張強度という。）が、１００ＭＰa以下であるのが好ましく、３０～９０Ｍｐａであるのがより好ましい。さらに好ましくは、４０～８０ＭＰａである。この範囲未満では発光素子用反射基板としての強度が十分ではなく、この範囲超では、基板を加工して発光装置とする場合の取扱性が悪い。
（金属配線層）
　本発明の発光素子用反射基板は、さらに金属配線層を形成してもよい。金属配線層は発光素子が実装される陽極酸化皮膜層と無機反射層との上に設けられてもよいし、発光素子が実装される陽極酸化皮膜層とは反対側の裏面側に設けられて発光素子実装面とはスルーホールを介して電気的に接続されてもよい。
　本発明の無機反射層は、その上に設けられる金属配線層との密着性が高い。この理由は、本発明の無機反射層では、赤外分光法により測定したＯＨ表面構造吸収係数が０．４０以上であるのでその表面には水酸化物、水和物が存在すると考えられ、金属配線層を製造するインクとの濡れ性が高く、得られる金属配線層の無機反射層との密着性が高いと考えられる。
　上記金属配線層の材料は、電気を通す素材（以下、「金属素材」ともいう。）であれば特に限定されず、その具体例としては、金（Ａｕ）、銀（Ａｇ）、銅（Ｃｕ）、アルミニウム（Ａｌ）、マグネシウム（Ｍｇ）、ニッケル（Ｎｉ）等が挙げられ、これらを１種単独で使用してもよく２種以上を併用してもよい。これらのうち、電気抵抗が低い理由からＣｕを用いるのが好ましい。なお、Ｃｕによる配線層の表層には、ワイヤボンディングの容易性を高める観点から、Ａｕ層やＮｉ／Ａｕ層を設けていてもよい。
　また、上記金属配線層は、これらの材料を用いた多層構造であってもよく、例えば、最下層からＡｇ層、Ｎｉ層およびＡｕ層をこの順で設ける態様が好適に挙げられる。
　また、上記金属配線層の厚さは、目的や用途に応じて所望の厚さとすればよいが、導通信頼性およびパッケージのコンパクト性の観点から、０．５～１０００μｍが好ましく、１～５００μｍがより好ましく、５～２５０μｍが特に好ましい。
＜６．金属配線層の形成＞
　上記金属配線層の形成方法としては、例えば、上記金属素材および液体成分（例えば、溶媒、樹脂成分など）を含有する金属インクをインクジェット印刷法、スクリーン印刷法等により上記受容層上にパターン印刷する方法等が挙げられる。
　このような形成方法により、凹凸のある無機反射層の表面に多くの工程を必要とせずに簡易にパターンを有する金属配線層を形成することができる。
　また、その他の上記金属配線層の形成方法としては、例えば、電解めっき処理、無電解めっき処理、置換めっき処理などの種々めっき処理の他、スパッタリング処理、蒸着処理、金属箔の真空貼付処理、接着層を設けての接着処理等が挙げられる。
　このようにして形成される金属配線層は、発光素子実装の設計に応じ、公知の方法でパターン形成される。また、実際に発光素子が実装される箇所には、再度金属層（半田も含む）を設け、熱圧着や、フリップチップ、ワイヤボンディング等で、接続しやすいように適宜加工することができる。
　好適な金属層としては、半田、または、金（Ａｕ）、銀（Ａｇ）、銅（Ｃｕ）、アルミニウム（Ａｌ）、マグネシウム（Ｍｇ）、ニッケル（Ｎｉ）等の金属素材が好ましく、加熱により発光素子を実装する場合は、半田、または、Ｎｉを介してのＡｕ、Ａｇを設ける方法が接続信頼性の観点から好ましい。
　この際、反射層が硬度の低いものであると、電極にワイヤをこすり付けて接続するワイヤボンディングを行う際にワイヤがうまく溶融せず接続不良となりやすい。本発明の無機反射層を用いると表面硬度が１ＧＰａ以上であり接続不良は発生しなかった。
　金属配線層の形成方法として金属インクを用いてインクジェット印刷法またはスクリーン印刷法により無機反射層上にパターンを形成すれば、凹凸のある表面に多くの工程を必要とせずに簡易にパターンを有する金属配線層を形成することができ、無機反射層の凹凸によるアンカー効果が高いので金属配線層と無機反射層との密着性にも優れる。無電解メッキなどを組み合わせれば上記金属配線層上に再度金属層（半田も含む）を設け、熱圧着や、フリップチップ、ワイヤボンディング等で、配線間や、電極との接続がしやすいように適宜金属配線層を加工することができる。
〔白色系発光装置〕
　図３は、本発明の白色系発光装置の一構成例を示した概略図である。
　図３の例は上記バルブ金属基板が窪みを持つ形状であり、上記陽極酸化皮膜層２および無機反射層３が窪み１３を持つ形状のバルブ金属基板１１の表面に設けられている。発光素子１１０は、無機反射層３上の窪み１３の部分に実装され、バルブ金属基板１１の陽極酸化皮膜層２を介して発光素子１１０の実装される面と反対側の面には放熱のためのヒートシンク１８が設けられている。
　図３に示す白色系発光装置１００において、外部接続用の電極を有する発光素子用反射基板３０に、発光素子１１０であるＬＥＤ素子が実装され、電極とはワイヤボンディング１９で電気的に接続されている。発光素子１１０は、蛍光体（蛍光粒子）１５０を含む樹脂材料１６０により封止されている。白色系発光装置１００では、ＬＥＤ素子からの発光と、蛍光体１５０からの励起光との混色によって所望の波長光を得ることができる。白色系発光装置として用いられる場合、ＬＥＤ素子として青色発光のＬＥＤ素子を使用し、ＹＡＧ（イットリウムアルミニウムガーネット）などの蛍光体（蛍光粒子）１５０を含んだ樹脂で封止し、ＬＥＤ素子からの青色発光と、蛍光体（蛍光粒子）１５０からの黄色領域の励起光との混色によって、擬似白色光が発光面側に発光される。
　ＬＥＤ素子は、発光層として、ＧａＡｌＮ、ＺｎＳ、ＺｎＳｅ、ＳｉＣ、ＧａＰ、ＧａＡｌＡｓ、ＡｌＮ、ＩｎＮ、ＡｌＩｎＧａＰ、ＩｎＧａＮ、ＧａＮ、ＡｌＩｎＧａＮ等の半導体を用いたものを用いることができる。半導体の構造としては、ＭＩＳ接合、ＰＩＮ接合やＰＮ接合を有したホモ構造、ヘテロ構造あるいはダブルへテロ構造のものが挙げられる。半導体の材料やその混晶度によって発光波長を紫外光から赤外光まで種々選択することができる。
　本発明の白色系発光装置１００は、反射基板３０として、バルブ金属基材１１上に膜強度と基板への密着性に優れる、陽極酸化皮膜層２と無機反射層３とが設けられていて、反射層の光反射率も高い。
　本発明の無機反射層は、その上に設けられる蛍光体を含んだ樹脂層との密着性が高い。この理由は、本発明の無機反射層では、赤外分光法により測定したＯＨ表面構造吸収係数が０．４０以上であるあるのでその表面には水酸化物、水和物が存在すると考えられ、樹脂層との密着性が高いと考えられる。
　ＬＥＤ素子の使用範囲が室内外の照明、自動車ヘッドライト、ディスプレイ装置のバックライトユニットなど様々な分野に拡がることにより、高温焼結をすることなく、高光反射特性を有する本発明の発光素子用反射基板は有用である。
　以下に実施例を示して本発明を具体的に説明する。ただし、本発明はこれらに限定されない。
（実施例１～２３および比較例１～９）
　＜１．基無機反射層塗布液の作成＞
　表３、４に示す結着剤と水を混合し攪拌、混合して無機反射層用バインダー液を作成した。
　始めにバインダー液の処方を説明する。
　＜バインダー液（リン酸アルミニウム）＞
　表３、４の結着剤種類に、リン酸アルミニウムと記載するバインダー液は以下である。
　　リン酸８５％　　　　(和光純薬製)　４８ｇ
　　水酸化アルミニウム(和光純薬製)　　１１ｇ
　　水　　　　　　　　　　　　　　　　４１ｇ
　　計　　　　　　　　　　　　　　　１００ｇ
　＜バインダー液（塩化アルミニウム）＞
　表３、４の結着剤種類に、塩化アルミニウムと記載するバインダー液は以下である。
　　塩酸３５％　　　（和光純薬製）　　３１．７ｇ
　　水酸化アルミニウム　　　　　　　　７．４ｇ
　　水　　　　　　　　　　　　　　　６０．９ｇ
　　計　　　　　　　　　　　　　　　１００ｇ
　＜バインダー液（ケイ酸ナトリウム）＞
　表３、４の結着剤種類に、ケイ酸ナトリウムと記載するバインダー液は以下である。
　　ケイ酸ナトリウム（３号ケイ酸ソーダ：富士化学株式会社製）　　８０ｇ
　　水　　　　　　　　　　　　　　　　２０ｇ
　　計　　　　　　　　　　　　　　　１００ｇ
　＜バインダー液（リン酸アルミ／塩化アルミ）＞
　表３、４の結着剤種類に、リン酸アルミ／塩化アルミと記載するバインダー液は以下である。
　　リン酸８５％　　　　(和光純薬製)　４８ｇ
　　水酸化アルミニウム(和光純薬製)　　　１１ｇ
　　塩化アルミニウム(和光純薬製)　　　０．８ｇ
　　水　　　　　　　　　　　　　　　４０．２ｇ
　　計　　　　　　　　　　　　　　　１００ｇ
　＜バインダー液（エポキシ樹脂）、（ＰＤＭＳ）＞
　表３、４の結着剤種類に、エポキシ樹脂、ＰＤＭＳとそれぞれ記載するバインダー液は以下である。
　バインダー液（エポキシ樹脂）は、エポキシ樹脂（新日鐵化学社製ＢＰＡ型エポキシ樹脂ＹＤ－１２８）を用い、バインダー液（ＰＤＭＳ）は、ポリジメチルシロキサン：和光純薬製を用いた。
　上記バインダー液１００ｇ中に対し、表３，４に示す以下の無機粒子をそれぞれ１００ｇの比率で加え、無機反射層用塗布液を準備した。
　１）アルミナ
　用いたアルミナ粒子を以下に記載する。表３，４に屈折率、平均粒子径、種類、組成を記載する。
　昭和電工株式会社製　ＡＬ-１６０ＳＧ－３　平均粒子径０．５２μｍ　純度９９．９％を用い、平均粒子径の小さいものについてはボールミルを用いて、ジルコニアビーズとともに粉砕を行い粒径測定装置を用いて所望の平均粒子径になったものを取り出して使用した。
　１－１）粉砕せず、ＡＬ-１６０ＳＧ-３をそのまま使用した。
　１－２）昭和電工株式会社製　Ａ４２-２　平均粒子径４．７μｍ　純度９９．５７％を用いた。
　１－３）昭和電工株式会社製　ＣＢ－Ｐ１０　平均粒子径１０μｍ　純度９９．６４％、および平均粒子径８μｍ　純度９９．６４％を用いた。
　１－４）シーアイ化成社製NanoTekアルミナパウダー(平均粒子径０．０３μｍ)を用いた。
　２）水酸化カルシウム、宇部マテリアルズ株式会社製、ＣＳＨ，純度９９．９９％、平均粒子径１μｍを用いた。
　３）硫酸バリウム
　用いた硫酸バリウム粒子を以下に記載する。
　３－１）東新化成株式会社製　Ｂ－３０、純度９４％、平均粒子径　０．３μｍを用いた。
　３－２）竹原化学工業株式会社製　Ｗ‐１、平均粒子径１．５μｍを用いた。
　異なる２種の無機粒子の混合物は、表に示す平均粒子径の混合物を用いた。混合比率は、平均粒子径０．０１μｍ粒子を全粒子質量中２０質量％とした。
＜２．基板の準備＞
　基板はアルミニウム板（厚み０．２ｍｍ、０．８ｍｍ、１．５ｍｍ、４ｍｍ　１０５０材、日本軽金属株式会社製）を用い、以下の処理を行って基板Ａ～Ｃをそれぞれ準備した。
　基板Ａ・・・上記アルミニウム板にアルカリ脱脂処理とデスマット処理を実施した。表３、４に金属種Ａｌ、陽極酸化皮膜、無と記載する。
　基板Ｂ・・・上記アルミニウム板にアルカリ脱脂処理と陽極酸化処理とを行った。表３、４に金属種Ａｌ、陽極酸化皮膜、有と記載する。
　基板Ｃ・・・上記アルミニウム板にアルカリ脱脂処理と粗面化処理と陽極酸化処理とを行った。表３、４に金属種Ａｌ（粗面化）、陽極酸化皮膜、有と記載する。
　基板Ｔｉ・・・実施例１５は、金属種チタン板(添川理化学社製)、板厚０．８ｍｍを用い、厚さ２０μｍの陽極酸化皮膜を作成した。表３、４に金属種Ｔｉ、陽極酸化皮膜、有と記載する。
（１）基板Ａの処理条件
　ａ．アルカリ水溶液中での脱脂処理
　アルミニウム板に、水酸化ナトリウム濃度２７質量％、アルミニウムイオン濃度６．５質量％、温度７０℃の水溶液をスプレー管から２０秒間吹き付けた。その後、ニップローラで液切りし、更に、後述する水洗処理を行った後、ニップローラで液切りした。
　水洗処理は、自由落下カーテン状の液膜により水洗処理する装置を用いて水洗し、更に、扇状に噴射水が広がるスプレーチップを８０ｍｍ間隔で有する構造を有するスプレー管を用いて５秒間水洗処理した。
　ｂ．酸性水溶液中でのデスマット処理
　上記脱脂処理の後、デスマット処理を行った。デスマット処理に用いる酸性水溶液は、硫酸１質量％水溶液を用い、液温３５℃でスプレー管から５秒間吹き付けて行った。その後、ニップローラで液切りし、引き続き上述した装置を用いて水洗した。
（２）基板Ｂの処理条件
　基板Ａと同様に作成した基板を陽極とし、陽極酸化処理装置を用いて陽極酸化処理を行った。電解液としては、７０ｇ／Ｌ硫酸水溶液に硫酸アルミニウムを溶解させてアルミニウムイオン濃度を５ｇ／Ｌとした電解液（温度２０℃）を用いた。陽極酸化処理は、アルミニウム板がアノード反応する間の電圧を２５Ｖとなるように定電圧で電解を行なった。最終的な陽極酸化皮膜層厚みが２０μｍとなるようにした。
　その後、ニップローラで液切りし、更に、上記の水洗処理に用いたのと同様の構造のスプレー管を用いて水洗処理を行った後、ニップローラで液切りした。
（３）基板Ｃの処理条件
　基板Ａと同様に作成した基板を下記条件にて粗面化処理を施した後、陽極酸化処理装置を用いて基板Ｂと同一条件にて陽極酸化処理を行った。
　ａ．粗面化処理方法
　硝酸濃度１質量％、アルミニウムイオン濃度５ｇ/Ｌ、および液温６０℃の電解液を用いて、電気化学的粗面化処理を行った。アルミニウムイオン濃度は硝酸アルミニウムを加えて調整した。また、アンモニウムイオン濃度は７０ｍｇ／Ｌであった。
　ＩＧＢＴ（絶縁ゲートバイポーラトランジスタ）素子を用いたＰＷＭ（Pulse Width Modulation）制御によって電流制御する、任意波形の交流電流を発生する電源を用いてカーボン製の対極を用いサンプルと対極に交流を負荷して電気化学的な粗面化処理を行った。
　交流電流は台形波を用い、周波数は６０Ｈｚ、電流値がゼロからピークに達するまでの時間ＴＰ、０．１ｓｅｃであり、正負の電流比は０．５になるように設定した。サンプルに流れる正電流電気量が２００Ｃ／ｄｍ２となるように調整した。
　その後、ニップローラで液切りし、更に、上記の水洗処理に用いたのと同様の構造のスプレー管を用いて水洗処理を行った後、ニップローラで液切りした。
　上記電解処理の後、アルミニウム板に、水酸化ナトリウム濃度２７質量％、アルミニウムイオン濃度６．５質量％、温度７０℃の水溶液をスプレー管から２０秒間吹き付けた。
　その後、ニップローラで液切りし、更に、後述する水洗処理を行った後、ニップローラで液切りした。水洗処理は、自由落下カーテン状の液膜により水洗処理する装置を用いて水洗し、更に、扇状に噴射水が広がるスプレーチップを８０ｍｍ間隔で備える構造を有するスプレー管を用いて５秒間水洗処理した。更に上記脱脂処理の後、デスマット処理を行った。デスマット処理に用いる酸性水溶液は、硫酸１質量％水溶液を用い、液温３５℃でスプレー管から５秒間吹き付けて行った。その後、ニップローラで液切りした。この処理の後、基板Ｂと同じ条件で陽極酸化処理を施した。
＜３．基板への反射層の形成＞
　調整した塗布液を、塗布膜厚を調整可能なコーターにより、基板上に塗布した。その後、表３，４に記載の温度に昇温したオーブン内に入れ、５分間加熱乾燥した。乾燥後の無機反射層の量は、実施例、比較例とも２０ｇ／ｍ2～５００ｇ／ｍ2の範囲であった。
　比較例５，６は、エポキシ樹脂、ＰＤＭＳをそれぞれ用いて表４に記載の無機粒子を陽極酸化皮膜層に塗布し、乾燥した。比較例７は無機反射層を形成しなかった。
　表４中部材を用いないもの、測定できなかったもの、または処理しなかった場合は「－」を記載する。
＜４．後処理＞
　上記で得られた反射層付基板に以下の表５，６に示す後処理を行った。
（１）加熱水蒸気処理
　反射層付基板を１１０℃の水蒸気で１分間処理した。
（２）親水化処理
　反射層付基板を２．５質量％ケイ酸ソーダ液中に浸漬し、１８０℃、５分乾燥させて親水化処理した。
＜５．評価方法＞
　得られた反射層付基板を以下の条件で評価し結果を表３～６に示す。
（１）ＯＨ表面構造吸収係数
　フーリエ変換型赤外分光（ＦＴ-ＩＲ）を用い吸光度（ＦＴ－ＩＲ）を測定し、波数３０００ｃｍ－１と波数１９００ｃｍ－１の吸光度の差をＯＨ表面構造吸収係数として算出した。島津製作所製FT-IR　8400S　に、反射測定が可能なオプションパーツ(Thermo Spectra-Tech社製　Foundation Siries 0070-154)を装備し、基板表面にＩＲ光を当て反射光との差分から吸光度を測定した。
（２）硬度、強度
　基材上に無機反射層を有する発光素子用反射基板のビッカース硬度は、ビッカース硬さ試験機（形式ＡＶＫ－ＣＯ、株式会社ミツトヨ製）で測定した。引張強度は、ＪＩＳ Ｚ２２４１に準ずる引張試験（引張速度：２ｍｍ／分）で測定した。結果を表５，６に示す。
（３）基板と無機反射層との密着性
　押し切りカッターで３０ｍｍ四角形状に切断し、剥れなかった基板については高さ３ｍからコンクリートの地面に落下させ、以下の評価とした。結果を下記表５，６に示す。
　ＡＡ：剥離しない
　Ａ：一部剥離した
　Ｂ：剥離部分がかなり見られた
　Ｃ：剥離した
　Ｄ：押し切りカッターで切断した際に剥れてしまったもの。
（４）耐電圧
　耐電圧は、絶縁抵抗試験機（ＴＯＳ９２００、キクスイ社製）を用い、耐電圧（ＤＣ）を測定し評価した。
　具体的には、作製した反射基板を金属製の基材（アルミニウム板）に載せ、無機反射層側にプローブを押し当てて測定し、耐電圧を測定した。
（５）反射率
　作製した基板について、反射濃度計（ＣＭ２６００Ｄ、コニカミノルタ社製）を用いて、４００～７００ｎｍの全反射率（ＳＰＩＮモードの全平均）を測定した。
（６）熱伝導率
　得られた絶縁基板について、アルバック理工社製ＴＣ－９０００／レーザーフラッシュ型熱拡散率測定装置を用い、ｔ１／２法に従い熱伝導率を計測した。結果を表５、６に示す。
〔金属配線層の作製〕
　得られた反射基板の表面にインクジェット装置（ＤＭＰ－２８３１、富士フイルム社製）を用いて銀ナノ粒子インク（ＸＡ－４３６、藤倉化学社製）の希釈液を図４に示す金属配線層２０のパターンで打滴することでＡｇ配線(配線幅：１００μｍ)を形成させた。
　次いで、ニッケルを含むめっき液でめっきし、Ａｇ－Ｎｉ配線を形成させた。
　最後に、金を含むめっき液でめっきし、Ａｇ－Ｎｉ－金配線を形成させた。なお、各層の厚みは、Ａｇ（２０μｍ），Ｎｉ（４μｍ），Ａｕ（０．４μｍ）であった。
　次いで、実施例、比較例の反射基板３０の表面に発光素子（ＬＥＤ）１０を実装し、金属配線層２０とワイヤボンディングで電気的に接続した。
（７）配線と無機反射層との密着性
　作製した各配線基板について、配線密着性を以下の基準で評価した。
　Ａ：３５０℃に加熱した半田ごてを配線部分に１分間押し付け、こてを離したときに配線の剥がれがないもの
　Ｂ：３５０℃に加熱した半田ごてを配線部分に１分間押し付け、こてを離したときに配線に線状のキズが見られたもの
　Ｃ：３５０℃に加熱した半田ごてを配線部分に１分間押し付け、こてを離したときに配線の剥がれあるいは「浮き」が発生したもの
Figure JPOXMLDOC01-appb-T000003
Figure JPOXMLDOC01-appb-T000004
Figure JPOXMLDOC01-appb-T000005
Figure JPOXMLDOC01-appb-T000006
〔実施例、比較例の評価〕
　実施例１～２２は、ＯＨ基表面構造吸収係数が高く、耐電圧、熱伝導性に優れ、基板と無機反射層との密着性に優れ、配線と無機反射層との密着性にも優れている。
　実施例２は、アルミニウム基板が粗面化され、陽極酸化処理されているので基板と無機反射層との密着性にとくに優れている。
　実施例１，２、５～１２、１４～２２の基板は陽極酸化処理皮膜を有するので基板と無機反射層との密着性に優れている。
　比較例１は、無機反射層の硬度が低く、加工時の取扱性に劣る。加熱水蒸気処理され、ＯＨ基表面構造吸収係数が高く、耐電圧、熱伝導性はよいが、無機反射層の無機粒子の平均粒子径が大きいので配線と無機反射層との密着性に劣る。
　比較例２は、無機反射層の後処理がされず、ＯＨ基表面構造吸収係数が低く、基板と無機反射層との密着性に劣り、配線と無機反射層との密着性にも劣っている。
　比較例３、４は、無機反射層の焼成温度が高いので、ＯＨ基表面構造吸収係数が低く、アルミ基板の熱膨張に無機反射層が追従できずクラックが入り耐電圧が低下する。基板と無機反射層との密着性に劣る。
　比較例５，６は、アルミナ粒子を結着するのに樹脂バインダーを使用しているので、耐熱性に劣り、耐光性にも劣り、経時劣化する。また、配線と反射層との密着性に劣る。
　比較例７は、バルブ金属上に陽極酸化皮膜層のみがあり、無機反射層がないが、加熱水蒸気処理され、ＯＨ基表面構造吸収係数が高く、耐電圧、熱伝導性はよいが、反射率に劣る。
　１、１１　バルブ金属基材
　２　陽極酸化皮膜層
　３　無機反射層
　４　無機粒子
　５　無機結着剤
　６　微小空隙
　１０　発光素子（ＬＥＤ）
　１３　窪み
　１８　ヒートシンク
　１９　ワイヤボンディング
　２０　金属配線層
　３０　発光素子用反射基板（反射基板）
　１００　白色系発光ダイオード装置
　１１０　発光素子
　１５０　蛍光体
　１６０　樹脂材料

Claims (15)

  1. 　バルブ金属基材上の少なくとも一部に無機反射層を備え、前記無機反射層が、ビッカース硬度（Ｈｖ）１ＧＰａ以上、赤外分光法により測定した波数３０００ｃｍ－１と波数１９００ｃｍ－１の吸光度の差で示されるＯＨ表面構造吸収係数が０．４０以上であることを特徴とする発光素子用反射基板。
  2. 　前記バルブ金属基材と上記無機反射層との間にバルブ金属基材の陽極酸化皮膜層を有する請求項１に記載の発光素子用反射基板。
  3. 　前記無機反射層が、リン酸アルミニウム、塩化アルミニウムおよびケイ酸ナトリウムからなる群から選択される少なくとも一つの無機結着剤と、屈折率１．５以上１．８以下、平均粒子径０．１μｍ以上５μｍ以下の無機粒子とを含有する請求項１または２に記載の発光素子用反射基板。
  4. 　前記無機粒子は、酸化物、水酸化物、および無機塩からなる群から選択される少なくとも一つである請求項１～３のいずれか１項に記載の発光素子用反射基板。
  5. 　前記無機粒子が硫酸バリウムおよび酸化アルミニウムからなる群から選択される少なくとも一つである請求項４のいずれか１項に記載の発光素子用反射基板。
  6. 　前記バルブ金属が、アルミニウム、タンタル、ニオブ、チタン、ハフニウム、ジルコニウム、亜鉛、タングステン、ビスマスおよびアンチモンからなる群から選択される少なくとも１種の金属である請求項１～５のいずれか１項に記載の発光素子用反射基板。
  7. 　前記バルブ金属基材の厚さが、０．１～２ｍｍである請求項１～６のいずれか１項に記載の発光素子用反射基板。
  8. 　前記バルブ金属が、アルミニウムである請求項１～７のいずれか１項に記載の発光素子用反射基板。
  9. 　前記発光素子用反射基板の引張強度が、３０ＭＰａ以上１００ＭＰａ以下である請求項１～８のいずれか１項に記載の発光素子用反射基板。
  10. 　前記無機粒子が、２種類以上である請求項１～９のいずれか１項に記載の発光素子用反射基板。
  11. 　バルブ金属基材表面に上の少なくとも一部に設けたビッカース硬度（Ｈｖ）１ＧＰａ以上の無機反射層を加熱水蒸気処理または親水化処理して、赤外分光法により測定した波数３０００ｃｍ－１と波数１９００ｃｍ－１の吸光度の差で示されるＯＨ表面構造吸収係数が０．４０以上である無機反射層を形成する、発光素子用反射基板の製造方法。
  12. 　前記無機反射層が、無機結着剤と無機粒子とを混合して前記バブル金属基材表面に塗布され、１００℃～３００℃の温度で低温焼成される請求項１１に記載の発光素子用反射基板の製造方法。
  13. 　前記バルブ金属基材表面を陽極酸化処理した後に前記陽極酸化処理層上に無機反射層を形成する請求項１１または１２に記載の発光素子用反射基板の製造方法。
  14. 　請求項１１～１３のいずれか１項に記載の工程を経た後、以下の（ｃ）および（ｄ）工程を任意の順序で行う、請求項１１～１３のいずれか１項に記載の発光素子用反射基板の製造方法：
    　（ｃ）発光素子への電気信号伝送のための金属配線層を形成し、上記金属配線層をパターン化する工程；
    　（ｄ）発光素子を実装する部分に相当する電極部に金属層を設ける工程。
  15. 　請求項１～１０のいずれか１項に記載の発光素子用反射基板の上に青色発光素子を有し、その周りおよび／または上部に蛍光発光体を備える白色系発光ダイオード装置。
PCT/JP2012/075390 2011-09-30 2012-10-01 発光素子用反射基板 Ceased WO2013047874A1 (ja)