WO2010113907A1 - Corps moulé composite, son procédé de fabrication et d'utilisation - Google Patents

Corps moulé composite, son procédé de fabrication et d'utilisation Download PDF

Info

Publication number
WO2010113907A1
WO2010113907A1 PCT/JP2010/055623 JP2010055623W WO2010113907A1 WO 2010113907 A1 WO2010113907 A1 WO 2010113907A1 JP 2010055623 W JP2010055623 W JP 2010055623W WO 2010113907 A1 WO2010113907 A1 WO 2010113907A1
Authority
WO
WIPO (PCT)
Prior art keywords
polyurethane
composite molded
acid units
molded body
silicone
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/JP2010/055623
Other languages
English (en)
Japanese (ja)
Inventor
秀和 齋藤
和正 服部
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Kuraray Co Ltd
Original Assignee
Kuraray Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Kuraray Co Ltd filed Critical Kuraray Co Ltd
Priority to JP2011507196A priority Critical patent/JPWO2010113907A1/ja
Publication of WO2010113907A1 publication Critical patent/WO2010113907A1/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

L'invention concerne un corps moulé composite ayant une excellente adhésion et comprenant un élément qui est constitué uniquement d'un polyuréthane ou principalement d'une composition de polyuréthane contenant un polyuréthane, et un élément qui est constitué uniquement d'un silicone ou principalement d'une composition de silicone contenant un silicone. Pour obtenir le polyuréthane, on met à réagir un polyol de poids moléculaire élevé, un polyisocyanate organique et un allongeur de chaîne, et le polyol de poids moléculaire élevé principalement contient un polyol de polyester. Le rapport de la totalité des unités d'acide dicarboxylique aromatiques et des unités d'acide hydroxycarboxylique aromatiques de toutes les unités d'acide dicarboxylique et de toutes les unités d'acide hydroxycarboxylique aromatiques constituant le polyol de polyester est compris entre 30 et 100 % par mol. L'invention concerne également un procédé de production du corps moulé composite.
PCT/JP2010/055623 2009-03-31 2010-03-30 Corps moulé composite, son procédé de fabrication et d'utilisation Ceased WO2010113907A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
JP2011507196A JPWO2010113907A1 (ja) 2009-03-31 2010-03-30 複合成形体及びその製造方法、並びに、該複合成形体の用途

Applications Claiming Priority (4)

Application Number Priority Date Filing Date Title
JP2009083951 2009-03-31
JP2009-083950 2009-03-31
JP2009083950 2009-03-31
JP2009-083951 2009-03-31

Publications (1)

Publication Number Publication Date
WO2010113907A1 true WO2010113907A1 (fr) 2010-10-07

Family

ID=42828197

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2010/055623 Ceased WO2010113907A1 (fr) 2009-03-31 2010-03-30 Corps moulé composite, son procédé de fabrication et d'utilisation

Country Status (3)

Country Link
JP (1) JPWO2010113907A1 (fr)
TW (1) TW201100253A (fr)
WO (1) WO2010113907A1 (fr)

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2017519052A (ja) * 2015-04-01 2017-07-13 サムヤン コーポレイション ポリウレタン、その製造方法及び用途
EP4365217A1 (fr) * 2022-11-07 2024-05-08 Sunko Ink Co., Ltd. Utilisation de polyuréthane thermoplastique et stratifié composite résistant aux chocs
US11981811B2 (en) 2021-09-30 2024-05-14 Sunko Ink Co., Ltd. Use of thermoplastic polyurethane and impact resistant composite laminate

Citations (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS6126682A (ja) * 1984-07-13 1986-02-05 Kuraray Co Ltd 複合フイルム用ポリウレタン系接着剤
JPS62181376A (ja) * 1985-10-14 1987-08-08 Kuraray Co Ltd ポリウレタン接着剤組成物
JPH01297419A (ja) * 1988-05-25 1989-11-30 Kuraray Co Ltd ポリウレタン樹脂の製造法
JPH10218978A (ja) * 1997-02-03 1998-08-18 Sekisui Chem Co Ltd ポリエステル樹脂、ポリウレタン樹脂及び接着剤組成物
JPH1150036A (ja) * 1997-07-30 1999-02-23 Sanyo Chem Ind Ltd 二液型ドライラミネート用接着剤組成物
JP2003342344A (ja) * 2002-05-30 2003-12-03 Mitsubishi Chemicals Corp ポリウレタン樹脂
WO2007055157A1 (fr) * 2005-11-08 2007-05-18 Shin-Etsu Polymer Co., Ltd. Element de recouvrement pour interrupteur a bouton-poussoir

Patent Citations (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS6126682A (ja) * 1984-07-13 1986-02-05 Kuraray Co Ltd 複合フイルム用ポリウレタン系接着剤
JPS62181376A (ja) * 1985-10-14 1987-08-08 Kuraray Co Ltd ポリウレタン接着剤組成物
JPH01297419A (ja) * 1988-05-25 1989-11-30 Kuraray Co Ltd ポリウレタン樹脂の製造法
JPH10218978A (ja) * 1997-02-03 1998-08-18 Sekisui Chem Co Ltd ポリエステル樹脂、ポリウレタン樹脂及び接着剤組成物
JPH1150036A (ja) * 1997-07-30 1999-02-23 Sanyo Chem Ind Ltd 二液型ドライラミネート用接着剤組成物
JP2003342344A (ja) * 2002-05-30 2003-12-03 Mitsubishi Chemicals Corp ポリウレタン樹脂
WO2007055157A1 (fr) * 2005-11-08 2007-05-18 Shin-Etsu Polymer Co., Ltd. Element de recouvrement pour interrupteur a bouton-poussoir

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2017519052A (ja) * 2015-04-01 2017-07-13 サムヤン コーポレイション ポリウレタン、その製造方法及び用途
US11981811B2 (en) 2021-09-30 2024-05-14 Sunko Ink Co., Ltd. Use of thermoplastic polyurethane and impact resistant composite laminate
EP4365217A1 (fr) * 2022-11-07 2024-05-08 Sunko Ink Co., Ltd. Utilisation de polyuréthane thermoplastique et stratifié composite résistant aux chocs

Also Published As

Publication number Publication date
JPWO2010113907A1 (ja) 2012-10-11
TW201100253A (en) 2011-01-01

Similar Documents

Publication Publication Date Title
JP4184178B2 (ja) 熱可塑性重合体組成物
CN102414240B (zh) 聚氨酯及其制造方法、母料、油墨用粘合剂、油墨组合物、成形用热塑性聚合物组合物、成形体、复合成形体及其制造方法
TWI238173B (en) Thermoplastic polymer composition
JPWO2009057497A1 (ja) ポリウレタン組成物
JP2003160727A (ja) 熱可塑性重合体組成物
WO2010113907A1 (fr) Corps moulé composite, son procédé de fabrication et d'utilisation
JPWO2009093480A1 (ja) キーパッド用フィルム、キーパッドおよびキーシート
JP2010260914A (ja) 熱可塑性重合体組成物
WO2003006552A1 (fr) Composition polymere thermoplastique
JP2011183573A (ja) 複合成形体
JP5536497B2 (ja) 熱可塑性樹脂組成物の製造方法および該熱可塑性樹脂組成物からなる部材を含む複合成形体
WO2010113908A1 (fr) Corps moulé composite
JP2002363247A (ja) 熱可塑性重合体組成物
WO2010126098A1 (fr) Copolymère bloc de polyuréthane
JPWO2011010588A1 (ja) キーパッド用ポリウレタンフィルム
JP4522313B2 (ja) 合成皮革用の積層体
JP3449877B2 (ja) 熱可塑性ポリウレタン組成物
JPH11302353A (ja) 熱可塑性ポリウレタン
JP3923385B2 (ja) 熱可塑性重合体組成物
KR20120125281A (ko) 시트상 스위치 부재
JPH11228810A (ja) 熱可塑性樹脂組成物

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 10758678

Country of ref document: EP

Kind code of ref document: A1

WWE Wipo information: entry into national phase

Ref document number: 2011507196

Country of ref document: JP

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 10758678

Country of ref document: EP

Kind code of ref document: A1