WO1999006199A1 - Procede de preparation de lentilles de contact a base d'alcool polyvinylique - Google Patents

Procede de preparation de lentilles de contact a base d'alcool polyvinylique Download PDF

Info

Publication number
WO1999006199A1
WO1999006199A1 PCT/JP1998/003084 JP9803084W WO9906199A1 WO 1999006199 A1 WO1999006199 A1 WO 1999006199A1 JP 9803084 W JP9803084 W JP 9803084W WO 9906199 A1 WO9906199 A1 WO 9906199A1
Authority
WO
WIPO (PCT)
Prior art keywords
lens
mold
mixture
polyvinyl alcohol
polymer
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/JP1998/003084
Other languages
English (en)
French (fr)
Inventor
Hiroki Degawa
Yuki Ikeda
Kenji Uno
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Seed Co Ltd
Original Assignee
Seed Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority to US09/463,835 priority Critical patent/US6402995B1/en
Application filed by Seed Co Ltd filed Critical Seed Co Ltd
Priority to AU81277/98A priority patent/AU739519B2/en
Priority to EP98931028A priority patent/EP1000726B1/en
Priority to DE69834191T priority patent/DE69834191T2/de
Publication of WO1999006199A1 publication Critical patent/WO1999006199A1/ja
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Description

明 細 書
\
ポリビュルアルコール製コンタク卜レンズの製造方法 技術分野
本発明は、 コンタクトレンズの製造方法に関するものである。 より詳 しくは、 新規な架橋ポリビュルアルコール製コンタクトレンズの製造方 法に関するものである。 背景技術
一般に、 ポリビュルアルコールはポリ酢酸ビュル等のポリビュルエス テルを加水分解して得られるが、 そのポリビュルアルコールを架橋する ことは簡単なことではない。
従来、 ポリビュルアルコールの架橋には、 ポリ酢酸ビュルを加水分解 してポリビュルアルコールとしてから、 アルデヒ ド等により後から架橋 する方法がとられていた。 しかし、 この方法では、 ポリビュルアルコ一 ルの架橋の程度を厳密にコントロールすることは容易ではなかった。 また、 ポリビュルアルコール自体も、 その特異な性質からレンズ形状 に成形することが難しいため、 ポリビュルアルコールを素材としたコン タクトレンズは実用化に至らなかった。
これに対し、 特開平 9— 4 0 7 1 9号公報には、 酢酸ビュルと トリア リルイソシァヌレ一卜からなる共重合体を、 冷却下でレンズ状に加工し た後に加水分解する架橋ポリビュルアルコール製コンタクトレンズが開 示されている。
特開平 9一 4 0 7 1 9号公報では、 架橋剤としてのトリァリルイソシ ァヌレートと酢酸ビュルを試験管等の容器中で塊状重合した後、 その重 合物を冷却下で切削、 研磨等の機械加工によりレンズ状物としてから加 水分解しており、 得られたレンズ状物は高含水率の架橋ポリビュルアル コール製コンタク 卜レンズとして有用なものである。
しかし、 試験管中における熱重合方法であるため、 比重が小さく気化 し易い酢酸ビュルの取扱いが難しく、 比重が大きく気化し難いトリァリ ルイソシァヌレートとの重合のコントロールは容易ではなかった。 すな わち、 一本の棒状の塊状物から数個のレンズ状物を切り出した場合にお いては、 膨潤状態のレンズは各々のレンズ形状及び形状安定性にバラッ キが生じ、 均一の品質のレンズを得ることが難しいという問題が生じ た。
更に、 その酢酸ビ二ル共重合体は常温では十分な硬さが得られないた め冷却しながら機械加工しなければならず、 加工条件の維持等、 製造ェ 程が複雑であるので、 レンズを低コストで連続的に大量生産することが 困難であった。 その上、 冷却しながらの機械加工ではあるが、 加工中に 発生する加工熱は該酢酸ビニル共重合体に悪影響を及ぼし、 その結果、 加工後のレンズ表面が荒れてしまい光学的に満足のできるものではな かった。
そこで、 容易かつ形状安定性に優れた架橋ポリビュルアルコール製コ ンタクトレンズの製造方法の出現が強く望まれていた。
本発明は、 以上の要請に応え、 実用性のある新規な架橋ポリビュルァ ルコール製コンタク卜レンズの製造方法を提供するものである。 すなわ ち、 機械加工を経ずにレンズ状に重合できるためレンズ表面が荒れず、 完成後の膨潤状態のレンズの形状安定性に優れるため取扱い易く、 しか も一定品質で大量に製造できる架橋ポリビュルアルコール製コンタクト レンズの製造方法を提供するものである。
発明の開示
本発明の架橋ポリ ビュルアルコール製コンタクトレンズの製造方法 は、 下記構造式 （ 1 ) で示されるビュルエステル 1 0 0重量部に対し卜 リアリルイソシァヌレート 0 . 0 5〜5重量部の混合物を調製し、 次い で該混合物を雄型と雌型からなる成形型に充填し、 紫外線を照射してレ ンズ状の重合体を形成した後、 該レンズ状重合体を加水分解することを 特徴とする。
> C = C -
0— C 0— R ( 1 )
(式中、 Rは炭化水素基を示す。 ）
本発明の方法においては、 機械加工を経ずにレンズ状に重合できるた めレンズ表面が荒れず、 完成後の膨潤状態のレンズの形状安定性に優れ るため取扱い易く、 しかも一定品質で大量に製造できる。
この方法では、 短時間で成形型により始めからレンズ形状に重合でき るため、 ポリビュルエステルに対しトリァリルイソシァヌレートがレン ズ形状維持に効果的に架橋するものと考える。
発明を実施するための最良の形態
以下に本発明の具体的な実施形態の例について説明する。
本発明において、 ポリビニルアルコールの主成分となるビュルエステ ルは構造式 （ 1 ) で示され、 Rが示す炭化水素基としては d 〜C e の アルキル基、 アルケニル基、 シクロアルキル基またはァリール基が好ま しい。
具体的には、 アルキル基としてメチル基、 ェチル基、 イソプロピル 基、 へキシル基等、 アルケニル基としてビュル基、 プロぺニル基、 ブテ ニル基、 へキサジェニル基等、 シクロアルキル基としてシクロペンチ ル、 シクロへキシル基等、 ァリール基としてフヱニル基等が挙げられ る。
ビュルエステルとしては、 Rがメチル基である酢酸ビュルが特に好ま しいが、 重合速度、 モノマーの粘度、 加水分解速度等を調整するため に、 Rが d 〜C B のアルキル基、 アルケニル基、 シクロアルキル基、 ァリール基等であるビュルエステルを混合して用いることもできる。
Rが C 8 を超えるアルキル基の場合、 ビュルエステルの加水分解が困 難になり易く、 ケン化率 8 0 %以上のポリビュルアルコールを得ること が困難となる傾向があるため好ましくない。
ビニルエステルとしては、 具体的に、 酢酸ビュル、 プロピオン酸ビ二 ル、 酪酸ビュル、 ビバリン酸ビュル、 アクリル酸ビニル、 メタクリル酸 ビュル、 ソルビン酸ビュル等を挙げることができる。
架橋成分としてのトリァリルイソシァヌレートは、 0 . 0 5重量部未 満では加水分解完了後のポリビュルアルコールのゲルとしての架橋が不 十分となり、 コンタクトレンズとしての形状を保つことが困難となる。 また、 5重量部を超えると、 架橋密度が大きくなり過ぎ柔軟なコンタク トレンズにならないばかり力 含水率が低下する。 従って、 本発明で は、 0 . 0 5〜5重量部、 好ましくは 0 . 0 6〜2重量部で用いる。 本発明で用いる成形型は、 ボリエチレン、 ポリプロピレン、 ポリスチ レン、 A B S樹脂等のプラスチックゃガラス及びこれらと金属製の型を 組合せたもの等からなり、 光学的な精密度の高いものを使用する。 更 に、 酢酸ビュル等の Rの炭素数が少ないビニルエステルの場合、 気化し 易いために成形型の気密度に十分注意を払う必要がある。
重合方法は、 紫外線照射によるラジカル重合である。 成形型を用いた 熱重合による方法では、 重合が開始するまでに熱により酢酸ビュル等の ビニルエステルの気化が進行し、 成形型の気密度が高い場合、 成形型の 内圧が高くなり過ぎた場合には破裂等を生じることがあるからである。 この点、 紫外線による重合では熱重合方法に較べて比較的に重合熱の制 御が容易である。 本発明においては、 成形型における紫外線による重合反応をコン卜 ロールすることも重要である。 すなわち、 使用モノマ一量の少ない成形 型による重合では、 ビュルエステルの重合反応速度と架橋剤であるトリ ァリルイソシァヌレートの重合反応速度を厳密に調節することが要求さ れる。 これについては、 紫外線重合開始剤の量に相応して紫外線の照射 量を調節することにより達成できる。 すなわち、 重合反応条件として は、 紫外線重合開始剤を用いない場合、 紫外線の照射エネルギーとして は、 3 0〜3 0 0 m WZ c m 2 の範囲内で行うことが好ましく、 また紫 外線重合開始剤を 5 , 0 0 0〜2 5， 0 0 0 p p m程度用いる場合、 紫 外線の照射エネルギーとしては、 1 0〜 1 0 0 m Wノ c m 2 の範囲内で 行うことが好ましい。
重合した重合物は、 成形型ごとそのビニルエステル共重合体の軟化点 以下の温度に冷却して成形型から取り出すことができる。
紫外線重合開始剤としては、 ジェトキシァセトフヱノン、 4— ( 2— ヒ ドロキシェ卜キシ） フエニル一 （ 2—ヒ ドロキシー 2—プロピル） ケ トン、 2—ヒ ドロキシ— 2—メチル一 1 一フエニルプロパン— 1 一才 ン、 2—メチルー 2—モルホリノ （4ーチオメチルフエニル） プロパン 一 1 一オン、 1 —ヒドロキシシクロへキシル一フエ二ルケトン、 2—ベ ンジルー 2—ジメチルアミノー 1— ( 4一モルホリノフエニル） ーブ夕 ノン、 ベンジルジメチルケタール等を挙げることができる。
成形型内で重合したレンズ形状のビュルエステル共重合体は、 加水分 解を行うことで目的とするポリビニルアルコール製コンタクトレンズと なる。
加水分解の方法は特に限定されないが、 アル力リ性の水溶液に該レン ズ状成形体を浸漬して反応させる。 例えば該レンズ状成形体を予めメタ ノール等の低級アルコールで膨潤してから、 水酸化ナトリゥム水溶液と メタノール等の低級アルコールの混合溶液に浸漬し加温下で加水分解を 行うことが好ましい。 この際、 加水分解を十分に行わないと、 本発明の 特徴である高含水率を示さないばかりか、 重合物の透明度も低下しコン タク卜レンズとしての使用が困難となる傾向があるので、 加水分解の割 合は 8 0 %以上であることが好ましい。
このように本発明によれば、 柔軟性に優れ、 高含水率で、 かつ、 形状 安定性及びレンズ品質に優れた架橋ポリビュルアルコール製コンタクト レンズを容易に製造できる。
次に、 本発明の実施例について説明する。
実施例 1
酢酸ビュル 20 gに 卜 リアリルイソシァヌレート 0. 2 g及び紫外 線開始剤として 2—ヒ ドロキシ— 2—メチル— 1 —フエニルプロパ ンー 1 一オン （ D A R O C U R 1 1 73、 日本チバガイギ一社） を 20， O O O p pm添加し、 十分に攪拌した。 その後に、 該混合液をポ リプロピレン製の成形型に充填して紫外線照射装置内で、 高圧水銀灯に より紫外線照射エネルギ一 1 5 · 3 m Wノ c m 2 で 30分間照射してレ ンズ状重合物を得た。 更に、 メタノールと蒸留水を 8 ： 2の割合で混合 した水溶液に、 水酸化ナトリウムお 0モル濃度となるように添加して レンズ状成形体を浸漬し、 40°Cで 2時間以上加水分解を行った。 その 後、 レンズ状成形体を取り出し多量の水で良く洗浄して架橋ポリビニル アルコール製コンタクトレンズを得た。
該レンズ状成形体は、 赤外分光光度計によりビュルエステルからビニ ルアルコールへのケン化が約 90%以上進行していることを確認した。 このレンズは、 光線透過率が 95%以上の透明性を有し含水率が 84% でありレンズ表面の荒れが見られず、 完成後の膨潤状態レンズは柔軟か つ形状安定性に優れ取扱い易く品質の優れたものであった。 実施例 2
酢酸ビニル 1 8 g、 プロピオン酸ビュル 2 g、 ト リアリルイソシァヌ レート 0. 2 g、 紫外線開始剤 （DA R 0 CU R 1 1 73、 日本チバガ ィギ一社） を 20 , 000 p pm添加した以外は、 実施例 1と同様の方 法で架橋ポリビニルアルコール製コンタクトレンズを得た。 該レンズ状 成形体は、 赤外分光光度計によりビュルエステルからビュルアルコール へのケン化が約 90 %以上進行していることを確認した。 このレンズ は、 光線透過率が 95%以上の透明性を有し含水率が 76%でありレン ズ表面の荒れが見られず、 完成後の膨潤状態レンズは柔軟かつ形状安定 性に優れ取扱い易く品質の優れたものであった。
実施例 3
酢酸ビュル 20 gにトリアリルイソシァヌレート◦ . 2 gを混合して 十分に攪拌した。 その後に、 該混合液をポリプロピレン製の成形型に充 填して紫外線照射装置内で、 紫外線開始剤の不存在下高圧水銀灯により 紫外線照射ェネルギ一 1 07 m c m 2 で 1 0分間照射してレンズ状 重合物を得た。 更に、 実施例 1 と同様にして架橋ポリビニルアルコール 製コンタクトレンズを得た。
該レンズ状成形体は、 赤外分光光度計によりビュルエステルからビニ ルアルコールへのケン化が約 90%以上進行していることを確認した。 このレンズは、 光線透過率が 95%以上の透明性を有し含水率が 78% でありレンズ表面の荒れが見られず、 完成後の膨潤状態レンズは柔軟か つ形状安定性に優れ取扱い易く品質の優れたものであった。
比較例 1
酢酸ビュル 99 g、 トリァリルイソシァヌレート 1 g、 ラウリルパー オキサイ ド 0. 5 gの混合溶液を試験管に入れ熱重合により作成した 1 本の棒状の重合物から、 冷却下でレンズ状成形体を 1 0個得た。 この各 レンズの表面は荒れていて光学材料として満足のいく ものではなかつ た。 また、 1 0個の膨潤状態のレンズはその形状にバラツキがあり、 レ ンズとしての形状を維持できないものであった。
産業上の利用可能性
本発明の方法により得られるレンズは、 高含水率の架橋ポリビュルァ ルコール製コンタク卜レンズとして有用なものである。
本発明によれば、 高い透明性を有し高含水率である架橋ポリビニルァ ルコール製コンタクトレンズを、 重合条件をコントロールした成形型内 でレンズ状に短時間で重合するため、 レンズ表面の荒れが見られず、 そ の上、 完成後の膨潤状態のレンズも形状安定性に優れるため取扱い易く 実用性があり、 しかも一定品質で大量に製造することができる。

Claims

請 求 の 範 囲
1 . 下記構造式 （ 1 ) で示されるビュルエステルと トリァリルイソシァ ヌレートからなる共重合体を加水分解して得られる架橋ポリビュルァ ルコール製コンタク トレンズの製造方法において、 該ビニルエステル 1 0 0重量部に対し該トリアリルイソシァヌレート 0 . 0 5〜5重量部 の混合物を調製し、 次いで該混合物を雄型と雌型からなる成形型に充填 し、 紫外線を照射してレンズ状の重合体を形成した後、 該レンズ状重合 体を加水分解することを特徴とする架橋ポリビュルアルコール製コン夕 クトレンズの製造方法。
> C = C -
0 - C 0 - R ( 1 )
(式中、 Rは炭化水素基を示す。 ）
2 . 前記ビュルエステルの Rが、 C , 〜(： 8 のアルキル基、 アルケニル 基、 シクロアルキル基またはァリール基である請求項 1の製造方法。
3 . 前記ビュルエステルが、 2種またはそれ以上のビュルエステルの混 合物である請求項 1の製造方法。
PCT/JP1998/003084 1997-07-31 1998-07-09 Procede de preparation de lentilles de contact a base d'alcool polyvinylique Ceased WO1999006199A1 (fr)