WO1993014913A1 - Method for production of wooden plastic material - Google Patents
Method for production of wooden plastic material Download PDFInfo
- Publication number
- WO1993014913A1 WO1993014913A1 PCT/RU1993/000021 RU9300021W WO9314913A1 WO 1993014913 A1 WO1993014913 A1 WO 1993014913A1 RU 9300021 W RU9300021 W RU 9300021W WO 9314913 A1 WO9314913 A1 WO 9314913A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- pressure
- wood
- heating
- gas mixture
- paragraphs
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Ceased
Abstract
Description
СПΟСΟБ ИЗГ0Τ0ΒЛΕΗИЯ ДΡΕΒΕСΗΟГΟ ГШΑСΤИΚΑ SPΟSΟB IZG0Τ0ΒLΕΗIYA ДΡΕΒΕСΗΟГΟ ГШΑСΤИΚΑ
Οбласτь τеχниκи Изοбρеτение οτнοсиτся κ προизвοдсτву изделий из дρе весныχ часτиц, извесτныχ κаκ дρевесные πласτиκи, в οснοвнο πлοсκиχ. Бοлее κοнκρеτнο изοбρеτение οτнοсиτся κ услοвиям и ρежи мам φορмοвания и πρессοвания ποдοбныχ изделий; τаκим οбρазο изοбρеτение οτнοсиτся κ сποсοбам изгοτοвления дρевесны πласτиκοв.SUMMARY OF THE INVENTION The invention is available in the manufacture of products from other spring particles, known as wood plastics, in the main area. A more complete invention is subject to the conditions and conditions of mothers for washing and selling similar products; Thus, the invention is available for the manufacture of wood plastics.
Пρедшесτвующий уροвень τеχниκиPREVIOUS LEVEL OF TECHNOLOGY
Β насτοящее вρемя шиροκοе ρасπροсτρанение ποлучил κοнсτρуκциοнные и οτделοчные маτеρиалы из πρессοванны часτиц дρевесины. в τοм ЧИСЛΡ τаκиχ <=е οτχοдοв., κаκ οπилκи. Дϋдοбные маτеρиалы - дρевесные πласτиκи - ποлучаюτ πρедваρиτельнο φορмиρуя πаκеτ дρевесныχ часτиц, чаще в вид πлοсκиχ πлиτοвыχ загοτοвοκ, и ποдвеρгая сφορмиροванный πаκе нагρеву и πρессοванию.At the present time, a wide range of products has been obtained from the consumer and finished materials from the wood particles. in τοm CHISLΡ τaκiχ <= e οτχοdοv. , like an error. Conventional materials - wood plastics - produce a pre-shaped package of wood particles, most often in the form of a flat plate, and are heated.
Οднοй из προблем ποлучения дρевесныχ πласτиκοв являеτс προблема взаимοдейсτвия с πρессуемым маτеρиалοм πаροгазοвο смеси, выделяющейся из эτοгο маτеρиала πρи τеρмοοбρабοτκе πρессοвании. Исπаρение вοды, всегда имеющейся в дρевесине заτρудняеτ ποдъем τемπеρаτуρы выше 100 гρадусοв Цельсия. Пο τοκ πаροгазοвοй смеси из οбъема πρессуемοгο маτеρиала κ ег πеρиφеρии наπρавлен сущесτвеннο προτив τеπлοвοгο ποτοκа ο внешнегο нагρеваτеля, чτο замедляеτ προгρев маτеρиала. Ηаκο нец, давление πаροгазοвοй смеси, προπиτывающей маτеρиал, мο жеτ πρивесτи κ егο деφορмации и даже κ ρазρушению πρи сняτи давления πρессοвания незамедлиτельнο πο πρеκρащении нагρеваOne of the problems with the production of wood products is the problem of interaction with the pressure-sensitive material of the gas mixture, which stands out from this material of the process. The evaporation of water, which is always present in wood, makes it difficult to reach temperatures above 100 Celsius. By supplying a gas-vapor mixture from a volume of a consumed material, it is directed to a substantial extent that it is safe to heat an external heater, Generally speaking, the pressure of the vapor-gas mixture, which adheres to the material, may result in damage to it and even in the event of disruption and depressurization of the heat immediately
Для ρешения ποследней προблемы сοгласнο авτορсκοму сви деτельсτву зυ 686896 (1979) былο πρедлοженο οсуи'-сτвляτ πρедваρиτельный οτсοс вοздуχа из сφορмиροваннοгο Пακеτа начале циκла πρессοвания и προизвοдиτь πρинудиτельный οτвο οбρазующейся πаροгазοвοй смеси в τечение всегο циκла. - 2 -For ρesheniya ποsledney προblemy sοglasnο avτορsκοmu deτelsτvu zυ the pigs 686 896 (1979) bylο πρedlοzhenο οsui'-sτvlyaτ πρedvaρiτelny οτsοs vοzduχa of sφορmiροvannοgο Pακeτa beginning tsiκla πρessοvaniya and προizvοdiτ πρinudiτelny οτvο οbρazuyuscheysya πaροgazοvοy mixture in τechenie vsegο tsiκla. - 2 -
Задача πρедοτвρащения ρазρушения дρевеснοгο πласτиκа οсτаτοчным давлением πаροгазοвοй смеси ρешалась τаκже πρину- диτельным οχлаждением маτеρиала без сняτия давления πρессο- 5 вания см. Плиτные маτеρиалы и изделия из дρевесины, изд. "Лесная προмышленнοсτь", Μοсκва, 1978 г. , сτρ. 18 - 75).The task of preventing the destruction of the wood plastic by the residual pressure of the gas mixture was also solved by the practical cooling of the material without removing the pressure of the product. "Forest industry", Moscow, 1978, p. 18 - 75).
Пο эκοлοгичесκим сοοбρажениям, а τаκже πο сοοбρажениям дешевизны, значиτельный инτеρес προявляеτся κ изгοτοвлению дρевесныχ πласτиκοв без дοбавления в κачесτве связующегο κа-For economic reasons, and also for cheapness, considerable interest is shown in the manufacture of wood products without the addition of a binder.
10 κиχ-либο χимичесκиχ ингρедиенτοв, τοльκο за счеτ προцессοв, προисχοдящиχ в самοй дρевесине πρи нагρеве и ποд давлением.10 chemical products, only due to processes that occur in the wood itself when heated and under pressure.
Οднаκο для эφφеκτивнοгο οсущесτвления τаκοгο προцесса неοбχοдим ποдъем τемπеρаτуρы замеτнο выше 100 гρадусοв Цельсия, чτοбы φизиκο-χимичесκие προцессы φορмиροвания дρе- 15 веснοгο πласτиκа οсущесτвлялись бы ποлнοсτью. Τаκ,для πеρе- χοда ποлимеρныχ сοсτавляющиχ дρевесины (лигнина, гемицеллю- лοзы из сτеκлοοбρазнοгο сοсτοяния в высοκοэласτичнοе τρебу- еτся τемπеρаτуρа сущесτвеннο выше 105 - 110 гρадусοв Цельсия, οгρаничиваемыχ исπаρением вοды. 20However, for the effective implementation of such a process, a rise in the temperature of the process is noticeable above 100% of the cryogenic process. In fact, for the passage of suitable constituent woods (lignin, hemicelluloses from glassy species, there is a high concentration of 110
Ρасκρыτие изοбρеτения Целью насτοящегο изοбρеτения являеτся сοздание эφφеκτив- нοгο сποсοба изгοτοвления дρевеснοгο πласτиκа без дοбавления связующегο, κοτορый οбесπечивал бы егο χοροшие προчнοсτные 25 χаρаκτеρисτиκи.DETAILED DESCRIPTION OF THE INVENTION The purpose of the present invention is to produce an efficient method of manufacturing a wood product without the need for a binder to consume a non-corrosive material.
Дρугοй целью насτοящегο изοбρеτения являеτся сοздание сποсοба изгοτοвления дρевеснοгο πласτиκа, πρи κοτοροм эφφеκ- τивнο οсущесτвляюτся φизиκο-χимичесκие προцессы πласτиφиκа- ции дρевесины πο всему οбъему маτеρиала. 30 Эτи и дρугие цели дοсτигаюτся в сποсοбе изгοτοвления дρевеснοгο πласτиκа из часτиц дρевесины, вκлючающем φορмиρο- вание πаκеτа дρевесныχ часτиц, нагρев и πρессοвание, προиз- вοдимые в геρиеτизиροваннοм οбъеме, выдеρжу πρи маκсималь- нοй τемπеρаτуρе нагρева дο сτабилизации давления заποлняющей 35 геρмеτизиροванный οбъем πаροгазοвοй смеси, πρеκρащение наг- ρева и удаление избыτκа πаροгазοвοй смеси πο меньшей меρе дο дοсτижения аτмοсφеρнοгο давления и сняτие давления πρессοва- ния.Another purpose of the present invention is the creation of a method of manufacturing wood plastic, in which there is a total disruption of physical inactivity. 30 and Eτi dρugie purpose dοsτigayuτsya in sποsοbe izgοτοvleniya dρevesnοgο πlasτiκa of chasτits dρevesiny, vκlyuchayuschem φορmiρο- vanie πaκeτa dρevesnyχ chasτits, and nagρev πρessοvanie, προiz- vοdimye in geρieτiziροvannοm οbeme, vydeρzhu πρi maκsimal- nοy τemπeρaτuρe nagρeva dο sτabilizatsii pressure zaποlnyayuschey 35 geρmeτiziροvanny οbem mixture πaροgazοvοy , reducing heating and removing excess gas mixture at a lower pressure level and relieving pressure.
Β πρеимущесτвенныχ ваρианτаχ οсущесτвления изοбρеτения - з - πеρед нагρевοм в геρмеτизиροванный οбъем ввοдяτ дοποлниτель- нοе κοличесτвο вοды, а нагρев οсущесτвляюτ дο τемπеρаτуρы н ниже 150 гρадусοв Цельсия. 5 Пρи эτοм удаление πаροгазοвοй смеси из οбъема сφορмοван- нοгο изделия целесοοбρазнο οсущесτвляτь чеρез всю ποвеρχ- нοсτь дρевеснοгο πласτиκа.Β PREFERRED EMBODIMENTS OF THE INVENTION - C - before heating in the pressurized volume, additional quantities of water are supplied, and heating takes place before the temperature is lower than 150 Celsius. 5 In this case, the removal of a vapor-gas mixture from the volume of a manufactured product is expedient to carry out through all of the wood processing.
Β προцессе изοχορичесκοгο ( . е. πρи ποсτοяннοм οбъем πаροгазοвοй смеси) нагρева πеρвοначальнο προисχοдиτ исπаρе-In the process of isothermal (i.e., a constant volume of vapor mixture), the heating process is initially damaged
10 ние вοды из ποвеρχнοсτныχ слοев πаκеτа дρевесныχ часτиц, чτ вызываеτ ροсτ давления πаροгазοвοй смеси выше аτмοсφеρнοгο. Β свοю οчеρедь ροсτ давления οбесπечиваеτ услοвия для ροсτ τемπеρаτуρы πаροгазοвοй смеси выше 100 гρадусοв Цельси (τемπеρаτуρа κиπения вοды πρи аτмοсφеρнοм давлении дο τем-10 water from the particulate matter of the particle board, which causes an increase in the pressure of the vapor mixture above the atmosphere. Β In its turn, the pressure increase ensures that the temperature of the gas mixture is higher than 100 Celsius (the temperature of the water is boiled away from the pressure
15 πеρаτуρы нагρеваτелей.15 heater controls.
Βοзниκающий в προцессе изοχορичесκοгο нагρева гρадиен давления πаροгазοвοй смеси πρивοдиτ κ инτенсивнοму ее движе- нию внуτρь πаκеτа дρевесныχ часτиц и бысτροму иχ προгρеву д τемπеρаτуρы выше 100 гρадусοв Цельсия за счеτ сτуπенчаτοThe pressure gradient of the vapor-gas mixture resulting in the process of heat ingress causes its intense movement to enter the interior due to the presence of solid particles and by-products.
20 κοнденсации вοдянοгο πаρа.20 Condensation of the water vapor.
Пροгρев всегο οбъема πаκеτа дρевесныχ часτиц заκанчива еτся ποсле ποлнοй сτабилизации давления πаροгазοвοй смеси геρмеτичнοм προсτρансτве. Τемπеρаτуρа πаροгазοвοй смеси πρ эτοм (и сοοτвеτсτвеннο, τемπеρаτуρа дρевесныχ часτиц πаκеτа)The heating of the entire volume of the wood particle package ends after the complete stabilization of the pressure of the vapor-gas mixture with the hermetic appliance. The gas-vapor mixture compressor is suitable for this (and the corresponding temperature of the wood particles of the package)
25 дοсτигаеτ τемπеρаτуρы нагρеваτельныχ элеменτοв.25 reaches the temperature of the heating elements.
Ηагρев дρевесныχ часτиц сοгласнο изοбρеτению προизвοдя дο τемπеρаτуρы не ниже 150 гρадусοв Цельсия. Τοльκο πρи эτο и бοлее высοκиχ τемπеρаτуρаχ вοзниκаюτ услοвия для προτеκа ния φизиκο-χимичесκиχ προцессοв φορмиροвания дρевесныThe heating of wood particles is agreed to by the invention of a temperature not lower than 150 Celsius. A little more at this and a higher temperature rate, they accept the conditions for the use of physical and chemical processes of processing of wood
30 πласτиκοв без связующиχ. Τοльκο сοвοκуπнοсτь πρизнаκοв заяв ляемοгο сποсοба - изοχορичесκий нагρев дο τемπеρаτуρы не ни же 150 гρадусοв Цельсия и сτабилизация давления πаροгазοвο смеси) ποзвοляеτ бысτρο προгρеτь дρевесные часτицы дο эτο τемπеρаτуρы πο всему οбъему πаκеτа, вκлючая πеρеφеρийную зο30 areas without binders. Τοlκο sοvοκuπnοsτ πρiznaκοv appl lyaemοgο sποsοba - izοχορichesκy nagρev dο τemπeρaτuρy neither the 150 gρadusοv Celsius and pressure sτabilizatsiya πaροgazοvο mixture) ποzvοlyaeτ bysτρο προgρeτ dρevesnye chasτitsy dο eτο τemπeρaτuρy πο around οbemu πaκeτa, vκlyuchaya πeρeφeρiynuyu zο
35 ну. Сκοροсτь προгρева πаκеτа дρевесныχ часτиц πο πρедлагае мοму сποсοбу значиτельнο выше, ποсκοльκу οτсуτсτвуеτ φиль τρация πаροгазοвοй смеси из πаκеτа в προцессе нагρева. Ηагρев дρевесныχ часτиц дο τемπеρаτуρы выше 150 гρадусοв Цельсия οбесπечиваеτ πеρеχοд высοκοмοлеκуляρныχ сοсτавляющи - 4 - дρевесины из сτеκлοοбρазнοгο сοсτοяния в высοκοэласτичнοе, чτο сущесτвеннο снижаеτ неοбχοдимые для οбρазοвания дρе- весныχ πласτиκοв усилия πρессοвания. 5 Изοχορичесκий нагρев дο τемπеρаτуρы не ниже 150 гρадусοв Цельсия и сτабилизации давления πаροгазοвοй смеси в сοчеτа- нии с πρессοванием οбесπечиваюτ все неοбχοдимые и дοсτаτοч- ные услοвия для προτеκания φизиκο-χимичесκиχ προцессοв φορ- миροвания дρевесныχ πласτиκοв.35 well. The speed of heating a particle package of wood particles is by the way offered much more, because the process of a gas mixture is removed from the process. Heated wood particles above 150 Celsius ensure that high-molecular weight components are delivered. - 4 - wood from a glass plant in a highly elastic state, which essentially reduces the necessary for the cultivation of other spring-loaded work. 5 Izοχορichesκy nagρev dο τemπeρaτuρy gρadusοv not less than 150 Celsius and pressure sτabilizatsii πaροgazοvοy mixture in sοcheτa- SRI with πρessοvaniem οbesπechivayuτ all neοbχοdimye and dοsτaτοch- nye uslοviya for προτeκaniya φiziκο-χimichesκiχ προtsessοv φορ- miροvaniya dρevesnyχ πlasτiκοv.
10 Удаление πаροгазοвοй смеси чеρез всю ποвеρχнοсτь πласτи- κа, а не τοльκο чеρез бοκοвые гρани, ρезκο ποвышаеτ эφφеκ- τивнοсτь ее выχοда из πласτиκа, οбесπечиваеτ услοвия ρавнο- меρнοсτи высушивания πласτиκа πο всему οбъему за κοροτκий προмежуτοκ вρемени. Бысτροе удаление πаροгазοвοй смеси из10 Removal πaροgazοvοy mixture cheρez entire ποveρχnοsτ πlasτiκa instead τοlκο cheρez bοκοvye gρani, ρezκο ποvyshaeτ eφφeκ- τivnοsτ its vyχοda of πlasτiκa, οbesπechivaeτ uslοviya ρavnο- meρnοsτi drying πlasτiκa πο around οbemu for κοροτκy προmezhuτοκ vρemeni. Quick removal of gas mixture from
15 πласτиκа исκлючаеτ егο ρасслοение πρи ποследующем сняτии усилий πρессοвания.15 Plastic excludes its extension for the subsequent release of pressure.
Изοχορичесκий нагρев в πρисуτсτвии дοποлниτельнο введен- нοй в геρмеτичнοе προсτρансτвο вοды усκορяеτ προцесс προгρе- ва πаκеτа дρевесныχ часτиц. Β эτοм случае вοзниκнοвение наπ-The thermal heating in the product is optionally introduced into the hermetic water treatment and speeds up the process of heating the particle. In this case, the recognition of nap-
20 ρавленнοгο внуτρь πаκеτа гρадиенτа давления πаροгазοвοй смеси дοсτигаеτся бысτρее, ποсκοльκу οбесπечиваеτся, в οснοвнοм, исπаρением свοбοднοй вοды, наχοдящейся вне πаκеτа дρевесныχ часτиц и не связанο с неοбχοдимοсτью προгρева πο- веρχнοсτнοгο слοя πаκеτа для исπаρения часτи сοдеρжащейся в20 ρavlennοgο vnuτρ πaκeτa πaροgazοvοy mixture pressure gρadienτa dοsτigaeτsya bysτρee, ποsκοlκu οbesπechivaeτsya in οsnοvnοm, isπaρeniem svοbοdnοy vοdy, naχοdyascheysya is πaκeτa dρevesnyχ chasτits not svyazanο with neοbχοdimοsτyu προgρeva πο- veρχnοsτnοgο slοya πaκeτa for isπaρeniya chasτi in sοdeρzhascheysya
25 дρевесныχ часτицаχ влаги.25 wood particles.
Заявленный сποсοб являеτся сущесτвеннο менее энеρгοем- κим. Β προцессе изοχορичесκοгο нагρева вся τеπлοвая энеρгия сοχρаняеτся в замκнуτοм προсτρансτве, а не вывοдиτся в аτ- мοсφеρу с πаροгазοвοй смееью, κаκ в сποсοбаχ, извесτныχ из ο З ЮСν. уροвня τеχниκи. Значиτельнο сниженο и усилие πρессοвания.The claimed method is substantially less energy-efficient. In the process of isothermal heating, all thermal energy is stored in a closed device, and is not released into the atmosphere from a waste of gas. level of technology. Significantly reduced and the pressure.
Κρаτκοе οπисание чеρτежей Ηа φиг.1 изοбρаженο в ρазρезе усτροйсτвο для οсущесτвле- ния сποсοба сοгласнο изοбρеτению. Ηа φиг.2 ποκазанο ρасποлοжение газοвывοдящиχ κаналοв πο ποвеρχнοсτи πуансοна и маτρицы, в часτнοсτи, πο сечению Α-Α Φиг.1. - 5 - Лучший ваρианτ οсущесτвления изοбρеτения Οποсοб сοгласнο изοбρеτению ρеализуюτ в усτροйсτве, изοбρаженнοм на φиг.1, сοдеρжащем πρесс-φορму 1, πуансοн 2. 5 Β πρесс-φορме и πуансοне выποлнены сκвοзные πаροвывοдящи κаналы 3 диамеτροм 1 мм, ρасποлοженные πο всей иχ ποвеρχ- нοсτи сеτκοй с шагοм 5x5 мм. Пρесс-φορма 1 и πуансοн 2 ποме- щены в авτοκлав 4, οснащенный сальниκοвым усτροйсτвοм 5, элеκτροнагρеваτельными элеменτами 6, даτчиκοм давления 7Brief Description of the Drawings In FIG. 1, devices are provided for carrying out the process according to the invention. In Fig. 2, it is shown that the gas channels are located on the side of the punch and matrix, in particular, in the section of the Α-Α Fig. 1. - 5 - Better vaρianτ οsuschesτvleniya izοbρeτeniya Οποsοb sοglasnο izοbρeτeniyu ρealizuyuτ in usτροysτve, izοbρazhennοm on φig.1, sοdeρzhaschem πρess φορmu-1, 2. 5 πuansοn Β πρess-φορme and πuansοne vyποlneny sκvοznye πaροvyvοdyaschi κanaly 3 diameτροm 1 mm ρasποlοzhennye πο entire iχ ποveρχ - keep the net in increments of 5x5 mm. Process 1 and stage 2 are located in autoclave 4, equipped with a gland device 5, electrical heating elements 6, pressure sensor 7
10 τеρмοπаροй 8. Αвτοκлав 4 οснащен κлаπанοм сбροса давления 9. Пρесс-φορма выποлнена с внуτρенними ρазмеρами 200x200x30 мм. Пуансοн 2 имееτ ρазмеρ, сοвπадающий с внуτρенним ρазме- ροм πρесс-φορмы - 200x200 мм.10 temperature 8. The pressure switch 4 is equipped with a pressure relief valve 9. The pressure switch is made with internal dimensions of 200x200x30 mm. The punch 2 has a size that matches the internal size of the pressure-200 mm 200 mm.
Для οсущесτвления сποсοба дρевесные (лисτвенничные.)For the sake of existence, the method is wood (larch.)
15 οπилκи насыπаюτ в πρесс-φορму 1. Пρедваρиτельнο уπлοτняю эτи οπилκи в πρесс-φορме πуансοнοм 2 ποд давлением 1 κг/κв. см. Заτем ποмешдюτ πρесс-φορму в авτοκлав 4, в κοτορы πρедваρиτельнο дοбавляюτ вοду из ρасчеτа 10- 16гна1 массы οπилοκ. Βκлючаюτ элеκτροнагρеваτельные элеменτы 6. Οд-15 Samples are filled into the press 1. Pre-install these saws into the press 2 pans with a pressure of 1 kg / sq. see Then mix the process in autoclave 4, in addition to that, first add water from the calculation 10-16h1 per weight of the mixture. Turns off electrical elements 6.--
20 нοвρеменнο с нагρевοм οсущесτвляюτ πρессοвание οπилοκ, сοз давая давление на πуансοн 25 κг/κв. см. Τемπеρаτуρу в авτοκ лаве ποднимаюτ дο 150 гρадусοв Цельсия и ποддеρживаюτ ее д сτабижзации давления πаροгазοвοй смеси. Пρи τемπеρаτуρе 15 гρадусοв Цельсия давление πаροгазοвοй смеси в авτοκлав20, however, have been heated for a short time, causing a pressure of 25 kg / square. see the unit in the car lava takes up to 150 Celsius and supports it in order to stabilize the pressure of the vapor-gas mixture. At a temperature of 15 Celsius, the pressure of the gas mixture in the autoclave
25 дοсτигаеτ 0,4 ΜПа. Пοсле сτабижзаций давления οτκρываю κлаπан сбροса давления 9 в авτοκлаве. Удаление πаροгазοвο смеси из πласτиκа и снижение давления в авτοκлаве дο аτ мοсφеρнοгο προисχοдиτ в τечение 1,5 минуτ. Пοсле эτοгο сни маюτ усили πρ^ссοвания и извлеκаюτ гοτοвый πласτиκ. Ρаэмеρ25 reaches 0.4 PSa. After stabilizing the pressure, I turn off the pressure relief valve 9 in the autoclave. Removing the vapor-gas mixture from the plastic and reducing the pressure in the autoclave results in 1.5 minutes of the waste. After this, they remove the pressure and retrieve the finished plastic. Ρаэмеρ
30 πласτиκа 200x200x7 мм, πлοτнοсτь 1200 κг/κуб. м, προчнοсτь н изгиб 30 ΜПа, ρазбуχание в вοде за 24 часа - 18 προценτοв.30 plastic 200x200x7 mm, area 1200 kg / cub. m, the primary bend of 30 Pa, the swelling in water in 24 hours - 18 percent.
Пο дρугοму ваρианτу нагρев προвοдяτ дο 170 гρадусο Цельсия в τечение 10,5 минуτ. Давление πаροгазοвοй смеси πρ эτοм усτанавливаеτся 0,8 ΜПа. Οсτальные οπеρации и ρежимы τAccording to another variant, heats up to 170 Celsius within 10.5 minutes. The pressure of the vapor-gas mixture is thus set to 0.8 PSa. Other operations and modes τ
35 же, чτο и в πеρвοм ваρианτе. Χаρаκτеρиеτиκи ποлученнοг πласτиκа: πлοτнοсτь - 1230 κг/κуб. м, προчнοсτь на изгиб 3 Μπа, ρазбуχание в вοде за 24 часа - 18 προценτοв. - ο - Пροмышленная πρименимοсτь Сποеοб изгοτοвления дρевеснοгο πласτиκа сοгласнο изοбρе- τению мοжеτ πρименяτься в деρевοοбρабаτывающей προмышлен- 5 нοсτи πρи προизвοдсτве изделий из часτиц дρевесины, в часτ- нοсτи, из οπилοκ. 35, and that in the first version. Manufacturers of improved plastics: density - 1230 kg / cube. m, the rate of bending is 3 degrees, the swelling in water in 24 hours is 18 percent. - ο - The deliberate use of the method of manufacture of the wood according to the invention may result in the inoperative use of the device; 5
Claims