US20190137675A1 - Laminated resin film, method for producing same, laminated optical film, image display device, and adhesion improvement-treated resin film - Google Patents

Laminated resin film, method for producing same, laminated optical film, image display device, and adhesion improvement-treated resin film Download PDF

Info

Publication number
US20190137675A1
US20190137675A1 US16/301,207 US201716301207A US2019137675A1 US 20190137675 A1 US20190137675 A1 US 20190137675A1 US 201716301207 A US201716301207 A US 201716301207A US 2019137675 A1 US2019137675 A1 US 2019137675A1
Authority
US
United States
Prior art keywords
resin film
film
group
meth
adhesion
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US16/301,207
Other languages
English (en)
Inventor
Ryo KANNO
Takeshi Saito
Tatsuya Yamasaki
Keisuke Kimura
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nitto Denko Corp
Original Assignee
Nitto Denko Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nitto Denko Corp filed Critical Nitto Denko Corp
Assigned to NITTO DENKO CORPORATION reassignment NITTO DENKO CORPORATION ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: SAITO, TAKESHI, KANNO, RYO, KIMURA, KEISUKE, YAMASAKI, TATSUYA
Publication of US20190137675A1 publication Critical patent/US20190137675A1/en
Abandoned legal-status Critical Current

Links

Classifications

    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
    • C08K5/00—Use of organic ingredients
    • C08K5/55—Boron-containing compounds
    • G—PHYSICS
    • G02—OPTICS
    • G02B—OPTICAL ELEMENTS, SYSTEMS OR APPARATUS
    • G02B5/00—Optical elements other than lenses
    • G02B5/30—Polarising elements
    • G02B5/3025—Polarisers, i.e. arrangements capable of producing a definite output polarisation state from an unpolarised input state
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B27/00—Layered products comprising a layer of synthetic resin
    • B32B27/06—Layered products comprising a layer of synthetic resin as the main or only constituent of a layer, which is next to another layer of the same or of a different material
    • B32B27/08—Layered products comprising a layer of synthetic resin as the main or only constituent of a layer, which is next to another layer of the same or of a different material of synthetic resin
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B27/00—Layered products comprising a layer of synthetic resin
    • B32B27/18—Layered products comprising a layer of synthetic resin characterised by the use of special additives
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B27/00—Layered products comprising a layer of synthetic resin
    • B32B27/28—Layered products comprising a layer of synthetic resin comprising synthetic resins not wholly covered by any one of the sub-groups B32B27/30 - B32B27/42
    • B32B27/285—Layered products comprising a layer of synthetic resin comprising synthetic resins not wholly covered by any one of the sub-groups B32B27/30 - B32B27/42 comprising polyethers
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B27/00—Layered products comprising a layer of synthetic resin
    • B32B27/30—Layered products comprising a layer of synthetic resin comprising vinyl (co)polymers; comprising acrylic (co)polymers
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B27/00—Layered products comprising a layer of synthetic resin
    • B32B27/38—Layered products comprising a layer of synthetic resin comprising epoxy resins
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B37/00—Methods or apparatus for laminating, e.g. by curing or by ultrasonic bonding
    • B32B37/12—Methods or apparatus for laminating, e.g. by curing or by ultrasonic bonding characterised by using adhesives
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B7/00—Layered products characterised by the relation between layers; Layered products characterised by the relative orientation of features between layers, or by the relative values of a measurable parameter between layers, i.e. products comprising layers having different physical, chemical or physicochemical properties; Layered products characterised by the interconnection of layers
    • B32B7/04—Interconnection of layers
    • B32B7/12—Interconnection of layers using interposed adhesives or interposed materials with bonding properties
    • C—CHEMISTRY; METALLURGY
    • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
    • C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
    • C09D163/00—Coating compositions based on epoxy resins; Coating compositions based on derivatives of epoxy resins
    • C—CHEMISTRY; METALLURGY
    • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
    • C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
    • C09D183/00—Coating compositions based on macromolecular compounds obtained by reactions forming in the main chain of the macromolecule a linkage containing silicon, with or without sulfur, nitrogen, oxygen, or carbon only; Coating compositions based on derivatives of such polymers
    • C—CHEMISTRY; METALLURGY
    • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
    • C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
    • C09D185/00—Coating compositions based on macromolecular compounds obtained by reactions forming in the main chain of the macromolecule a linkage containing atoms other than silicon, sulfur, nitrogen, oxygen, and carbon; Coating compositions based on derivatives of such polymers
    • C—CHEMISTRY; METALLURGY
    • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
    • C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
    • C09D4/00—Coating compositions, e.g. paints, varnishes or lacquers, based on organic non-macromolecular compounds having at least one polymerisable carbon-to-carbon unsaturated bond ; Coating compositions, based on monomers of macromolecular compounds of groups C09D183/00 - C09D183/16
    • C—CHEMISTRY; METALLURGY
    • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
    • C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
    • C09D5/00—Coating compositions, e.g. paints, varnishes or lacquers, characterised by their physical nature or the effects produced; Filling pastes
    • C—CHEMISTRY; METALLURGY
    • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
    • C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
    • C09D7/00—Features of coating compositions, not provided for in group C09D5/00; Processes for incorporating ingredients in coating compositions
    • C09D7/40—Additives
    • C09D7/60—Additives non-macromolecular
    • C09D7/63—Additives non-macromolecular organic
    • C—CHEMISTRY; METALLURGY
    • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
    • C09J—ADHESIVES; NON-MECHANICAL ASPECTS OF ADHESIVE PROCESSES IN GENERAL; ADHESIVE PROCESSES NOT PROVIDED FOR ELSEWHERE; USE OF MATERIALS AS ADHESIVES
    • C09J11/00—Features of adhesives not provided for in group C09J9/00, e.g. additives
    • C09J11/02—Non-macromolecular additives
    • C09J11/06—Non-macromolecular additives organic
    • C—CHEMISTRY; METALLURGY
    • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
    • C09J—ADHESIVES; NON-MECHANICAL ASPECTS OF ADHESIVE PROCESSES IN GENERAL; ADHESIVE PROCESSES NOT PROVIDED FOR ELSEWHERE; USE OF MATERIALS AS ADHESIVES
    • C09J201/00—Adhesives based on unspecified macromolecular compounds
    • C—CHEMISTRY; METALLURGY
    • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
    • C09J—ADHESIVES; NON-MECHANICAL ASPECTS OF ADHESIVE PROCESSES IN GENERAL; ADHESIVE PROCESSES NOT PROVIDED FOR ELSEWHERE; USE OF MATERIALS AS ADHESIVES
    • C09J201/00—Adhesives based on unspecified macromolecular compounds
    • C09J201/02—Adhesives based on unspecified macromolecular compounds characterised by the presence of specified groups, e.g. terminal or pendant functional groups
    • C—CHEMISTRY; METALLURGY
    • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
    • C09J—ADHESIVES; NON-MECHANICAL ASPECTS OF ADHESIVE PROCESSES IN GENERAL; ADHESIVE PROCESSES NOT PROVIDED FOR ELSEWHERE; USE OF MATERIALS AS ADHESIVES
    • C09J7/00—Adhesives in the form of films or foils
    • C09J7/30—Adhesives in the form of films or foils characterised by the adhesive composition
    • G—PHYSICS
    • G02—OPTICS
    • G02B—OPTICAL ELEMENTS, SYSTEMS OR APPARATUS
    • G02B1/00—Optical elements characterised by the material of which they are made; Optical coatings for optical elements
    • G02B1/10—Optical coatings produced by application to, or surface treatment of, optical elements
    • G02B1/14—Protective coatings, e.g. hard coatings
    • G—PHYSICS
    • G02—OPTICS
    • G02B—OPTICAL ELEMENTS, SYSTEMS OR APPARATUS
    • G02B5/00—Optical elements other than lenses
    • G02B5/30—Polarising elements
    • G—PHYSICS
    • G02—OPTICS
    • G02B—OPTICAL ELEMENTS, SYSTEMS OR APPARATUS
    • G02B5/00—Optical elements other than lenses
    • G02B5/30—Polarising elements
    • G02B5/3025—Polarisers, i.e. arrangements capable of producing a definite output polarisation state from an unpolarised input state
    • G02B5/3033—Polarisers, i.e. arrangements capable of producing a definite output polarisation state from an unpolarised input state in the form of a thin sheet or foil, e.g. Polaroid
    • G—PHYSICS
    • G02—OPTICS
    • G02B—OPTICAL ELEMENTS, SYSTEMS OR APPARATUS
    • G02B5/00—Optical elements other than lenses
    • G02B5/30—Polarising elements
    • G02B5/3025—Polarisers, i.e. arrangements capable of producing a definite output polarisation state from an unpolarised input state
    • G02B5/3033—Polarisers, i.e. arrangements capable of producing a definite output polarisation state from an unpolarised input state in the form of a thin sheet or foil, e.g. Polaroid
    • G02B5/3041—Polarisers, i.e. arrangements capable of producing a definite output polarisation state from an unpolarised input state in the form of a thin sheet or foil, e.g. Polaroid comprising multiple thin layers, e.g. multilayer stacks
    • G02B5/305—Polarisers, i.e. arrangements capable of producing a definite output polarisation state from an unpolarised input state in the form of a thin sheet or foil, e.g. Polaroid comprising multiple thin layers, e.g. multilayer stacks including organic materials, e.g. polymeric layers
    • G—PHYSICS
    • G02—OPTICS
    • G02F—OPTICAL DEVICES OR ARRANGEMENTS FOR THE CONTROL OF LIGHT BY MODIFICATION OF THE OPTICAL PROPERTIES OF THE MEDIA OF THE ELEMENTS INVOLVED THEREIN; NON-LINEAR OPTICS; FREQUENCY-CHANGING OF LIGHT; OPTICAL LOGIC ELEMENTS; OPTICAL ANALOGUE/DIGITAL CONVERTERS
    • G02F1/00—Devices or arrangements for the control of the intensity, colour, phase, polarisation or direction of light arriving from an independent light source, e.g. switching, gating or modulating; Non-linear optics
    • G02F1/01—Devices or arrangements for the control of the intensity, colour, phase, polarisation or direction of light arriving from an independent light source, e.g. switching, gating or modulating; Non-linear optics for the control of the intensity, phase, polarisation or colour 
    • G02F1/13—Devices or arrangements for the control of the intensity, colour, phase, polarisation or direction of light arriving from an independent light source, e.g. switching, gating or modulating; Non-linear optics for the control of the intensity, phase, polarisation or colour  based on liquid crystals, e.g. single liquid crystal display cells
    • G02F1/133—Constructional arrangements; Operation of liquid crystal cells; Circuit arrangements
    • G02F1/1333—Constructional arrangements; Manufacturing methods
    • G02F1/1335—Structural association of cells with optical devices, e.g. polarisers or reflectors
    • G—PHYSICS
    • G02—OPTICS
    • G02F—OPTICAL DEVICES OR ARRANGEMENTS FOR THE CONTROL OF LIGHT BY MODIFICATION OF THE OPTICAL PROPERTIES OF THE MEDIA OF THE ELEMENTS INVOLVED THEREIN; NON-LINEAR OPTICS; FREQUENCY-CHANGING OF LIGHT; OPTICAL LOGIC ELEMENTS; OPTICAL ANALOGUE/DIGITAL CONVERTERS
    • G02F1/00—Devices or arrangements for the control of the intensity, colour, phase, polarisation or direction of light arriving from an independent light source, e.g. switching, gating or modulating; Non-linear optics
    • G02F1/01—Devices or arrangements for the control of the intensity, colour, phase, polarisation or direction of light arriving from an independent light source, e.g. switching, gating or modulating; Non-linear optics for the control of the intensity, phase, polarisation or colour 
    • G02F1/13—Devices or arrangements for the control of the intensity, colour, phase, polarisation or direction of light arriving from an independent light source, e.g. switching, gating or modulating; Non-linear optics for the control of the intensity, phase, polarisation or colour  based on liquid crystals, e.g. single liquid crystal display cells
    • G02F1/133—Constructional arrangements; Operation of liquid crystal cells; Circuit arrangements
    • G02F1/1333—Constructional arrangements; Manufacturing methods
    • G02F1/1335—Structural association of cells with optical devices, e.g. polarisers or reflectors
    • G02F1/133528—Polarisers
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B37/00—Methods or apparatus for laminating, e.g. by curing or by ultrasonic bonding
    • B32B37/12—Methods or apparatus for laminating, e.g. by curing or by ultrasonic bonding characterised by using adhesives
    • B32B2037/1253—Methods or apparatus for laminating, e.g. by curing or by ultrasonic bonding characterised by using adhesives curable adhesive
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2255/00—Coating on the layer surface
    • B32B2255/10—Coating on the layer surface on synthetic resin layer or on natural or synthetic rubber layer
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2255/00—Coating on the layer surface
    • B32B2255/24—Organic non-macromolecular coating
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2307/00—Properties of the layers or laminate
    • B32B2307/40—Properties of the layers or laminate having particular optical properties
    • B32B2307/412—Transparent
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2307/00—Properties of the layers or laminate
    • B32B2307/40—Properties of the layers or laminate having particular optical properties
    • B32B2307/42—Polarizing, birefringent, filtering
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2310/00—Treatment by energy or chemical effects
    • B32B2310/08—Treatment by energy or chemical effects by wave energy or particle radiation
    • B32B2310/0806—Treatment by energy or chemical effects by wave energy or particle radiation using electromagnetic radiation
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2457/00—Electrical equipment
    • B32B2457/20—Displays, e.g. liquid crystal displays, plasma displays
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2551/00—Optical elements
    • C—CHEMISTRY; METALLURGY
    • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
    • C09J—ADHESIVES; NON-MECHANICAL ASPECTS OF ADHESIVE PROCESSES IN GENERAL; ADHESIVE PROCESSES NOT PROVIDED FOR ELSEWHERE; USE OF MATERIALS AS ADHESIVES
    • C09J2301/00—Additional features of adhesives in the form of films or foils
    • C09J2301/40—Additional features of adhesives in the form of films or foils characterized by the presence of essential components
    • C09J2301/416—Additional features of adhesives in the form of films or foils characterized by the presence of essential components use of irradiation
    • G—PHYSICS
    • G02—OPTICS
    • G02F—OPTICAL DEVICES OR ARRANGEMENTS FOR THE CONTROL OF LIGHT BY MODIFICATION OF THE OPTICAL PROPERTIES OF THE MEDIA OF THE ELEMENTS INVOLVED THEREIN; NON-LINEAR OPTICS; FREQUENCY-CHANGING OF LIGHT; OPTICAL LOGIC ELEMENTS; OPTICAL ANALOGUE/DIGITAL CONVERTERS
    • G02F2202/00—Materials and properties
    • G02F2202/02—Materials and properties organic material
    • G02F2202/022—Materials and properties organic material polymeric
    • G—PHYSICS
    • G02—OPTICS
    • G02F—OPTICAL DEVICES OR ARRANGEMENTS FOR THE CONTROL OF LIGHT BY MODIFICATION OF THE OPTICAL PROPERTIES OF THE MEDIA OF THE ELEMENTS INVOLVED THEREIN; NON-LINEAR OPTICS; FREQUENCY-CHANGING OF LIGHT; OPTICAL LOGIC ELEMENTS; OPTICAL ANALOGUE/DIGITAL CONVERTERS
    • G02F2202/00—Materials and properties
    • G02F2202/28—Adhesive materials or arrangements

Definitions

  • the present invention relates to a laminated resin film including a first resin film and a second resin film laminated on/over the first resin film to interpose an adhesive layer therebetween.
  • This laminated resin film is usable singly or in a form of a laminated optical film to form an image display device such as a liquid crystal display device (LCD), an organic EL display device, a CRT or a PDP.
  • LCD liquid crystal display device
  • organic EL display device a CRT or a PDP.
  • a liquid crystal display device is a device making the state of polarized light visible by switching of a liquid crystal.
  • a polarizer is used.
  • TVs and other articles have been increasingly required to be higher in brightness and contrast, and wider in viewing angle.
  • Their polarizing film has also beers increasingly required to be higher in transmittance, polarizations degree, color reproducibility, and others.
  • an iodine-based polarizer As a polarizer, an iodine-based polarizer has been most popularly and widely used, which has a structure obtained by adsorbing iodine onto, for example, a polyvinyl alcohol (hereinafter also referred to merely as a “PVA”), and then stretching the resultant.
  • a generally used polarizing film is a polarizing film in which transparent protective films are bonded, respectively, onto both surfaces of a polarizer through the so-called water-based adhesive, in which a polyvinyl alcohol-based material is dissolved in water (Patent Document 1 listed below).
  • the transparent protective films for example, triacetylcellulose is used, which has a high moisture permeability.
  • the water-based adhesive the so-called wet lamination
  • a drying step is required after the transparent, protective films are bonded to the polarizer.
  • an active-energy-ray-curable adhesive is suggested.
  • the active-energy-ray-curable adhesive is used to produce polarizing films, no drying step is required.
  • the polarizing films can be improved in producibility.
  • the inventors have suggested a radical-polymerizing type active-energy-ray-curable adhesive, using an substituted amide-based monomer as a curable component (Patent Document 2 listed below).
  • Patent Document 1 JP-A-2001-296427
  • Patent Document 2 JP-A-2012-052000
  • An adhesive layer formed by using the active-energy-ray-curable adhesive described in Patent Document 2 can sufficiently pass a water resistance test of immersing the adhesive layer into, for example, hot water of 60° C. temperature for 6 hours, and subsequently evaluating whether or not the layer undergoes discoloration or exfoliation.
  • an adhesive for polarizing films has been required to be further improved in water resistance to such a degree that the resultant adhesive layer can pass a severer water resistance test, for example, in which at the time of immersing this layer in water (or saturating the layer with water) and then peeling off ends of the layer with nails, whether or not the layer undergoes exfoliation is evaluated.
  • a severer water resistance test for example, in which at the time of immersing this layer in water (or saturating the layer with water) and then peeling off ends of the layer with nails, whether or not the layer undergoes exfoliation is evaluated.
  • An object thereof is to provide a laminated resin film that has a first resin film and a second resin film good in adhesion to an adhesive layer, and further that can sustain adhering strength even in a dew condensation environment or under a severe condition such that the laminated resin film is immersed in water.
  • An object of the present invention is, particularly, to provide a polarizing film and a laminated optical film that are each a film in which when a first resin film is a polarizer, and a second resin film is a transparent film such as a transparent protective film or a retardation film, the polarizer and the transparent film are good in adhesion to an adhesive layer, and that can each sustain adhering strength even in a dew condensation environment or under a severe condition such that the film is immersed in water.
  • Another object of the present invention is to provide a laminated optical film using a laminated resin film including a polarizing film; and an image display device using a laminated resin film or optical film including a polarizing film.
  • the inventors have repeatedly made eager investigations to find out that the objects can be attained by adept the following structure: a structure in which an adhesion-improving layer including a specified boron compound is formed on/over at least one adhesion surface of a first resin film and a second resin film, and these first and second resin films are laminated to each other to interpose an adhesive layer therebetween.
  • an adhesion-improving layer including a specified boron compound is formed on/over at least one adhesion surface of a first resin film and a second resin film, and these first and second resin films are laminated to each other to interpose an adhesive layer therebetween.
  • the present invention relates to a laminated resin film including a first resin film, and a second resin film laminated on/over at least one surface of the first resin film to interpose an adhesive layer between the surface and the second resin film, and in this laminated resin film, the adhesion surface of at least one of the first resin film and the second resin film includes a compound represented by the following general formula (1):
  • X is a functional group containing a reactive group
  • R 1 and R 2 each independently represent a hydrogen atom, or an aliphatic hydrocarbon group, aryl group or heterocyclic group that may have a substituent
  • the compound represented by the general formula (1) is interposed at either one or both of a position between the first resin film and the adhesive layer, and a position between the second resin film and the adhesive layer.
  • the compound represented by the general formula (1) is a compound represented by the following general formula (1′):
  • the first resin film is a polarizer
  • the second resin film is a transparent film.
  • the compound represented by the general formula (1) is interposed at both of the position between the first resin film and the adhesive layer, and the position between the second resin film and the adhesive layer.
  • the reactive group that the compound represented by the general formula (1) has is at least one reactive group selected from the group consisting of ⁇ , ⁇ -unsaturated carbonyl, vinyl, vinyl ether, epoxy, oxetane, amino, aldehyde, mercapto, and halogen groups.
  • the present invention also relates to a method for producing a laminated resin film including a first resin film, and a second resin film laminated on/over at least one surface of the first resin film to interpose an adhesive layer between the surface and the second resin film; the method including an adhesion improvement-treating step of causing a compound represented by the following general formula (1):
  • X is a functional group containing a reactive group
  • R 1 and R 2 each independently represent a hydrogen atom, or an aliphatic hydrocarbon group, aryl group or heterocyclic group that may have a substituent to adhere to the adhesion surface of at least one of the first resin film and the second resin film
  • an applying step of applying a curable resin composition to the adhesion surface of at least one of the first resin film and the second resin film a bonding step of causing the first resin film and the second resin film to each other; and an adhering step of radiating an active energy ray to the resultant laminate from a first resin film side of the laminate, or a second resin film side of the laminate to cure the curable resin composition to yield the adhesive layer, and adhering the first resin film and the second resin film to adhere to each other through the yielded adhesive layer.
  • the compound represented by the general formula (1) is a compound represented by the following general formula (1′):
  • the present invention also relates to a laminated optical film, in which at least one laminated resin film as defined in any one of the paragraphs concerned is laminated; or an image display device, using a laminated resin film as defined in any one of the paragraphs concerned, or a laminated optical film as defined herein.
  • the present invention relates to an adhesion improvement-treated resin film, including: a resin film having surfaces each including at least a reactive functional group; and a compound included on/over at least one of the surfaces of the resin film, and represented by the following general formula (1):
  • R 1 and R 2 each independently represent a hydrogen atom, or an aliphatic hydrocarbon group, aryl group or heterocyclic group that may have a substituent.
  • an adhesion-improving composition including a compound represented by the following general formula (1):
  • R 1 and R 2 each independently represent a hydrogen atom, or an aliphatic hydrocarbon group, aryl group or heterocyclic group that may have a substituent.
  • the first resin film and the second resin film are good in adhesion to the adhesive layer, and further this laminated resin film can sustain adhering strength even in a dew condensation environment or under a severe condition such that the laminated resin film is immersed in water.
  • the first resin film is a polarizer and the second resin film is a transparent film such as a transparent protective film or a retardation film
  • a polarizing film and a laminated optical film that are each a film in which the polarizer and the transparent film are good in adhesion to the adhesive layer, and that can each sustain adhering strength even in a dew condensation environment or under a severe condition such that the laminated resin film is immersed in water.
  • Reasons why such advantageous effects are gained are unclear.
  • the reasons would be as follows:
  • a mechanism that, adhesion peeling is generated between the polarizer and the transparent protective film, and the adhesive layer can be presumed as follows: Water initially diffuses into the adhesive layer, and then the water diffuses to the polarizer interfacial side or the transparent protective film side of this adhesive layer.
  • hydrogen bonding and/or ion bonding contribute(s) largely to adhering strength between its polarizer and transparent protective film, and its adhesive layer; however, the water that has diffused to the polarizer interfacial side or the transparent protective film interfacial side, causes dissociation of the hydrogen bonding and the ion bonding in the interface. As a result, the adhering strength between the polarizer and transparent, protective film, and the adhesive layer is lowered. This lowering may cause interlayer exfoliation between the polarizer and transparent protective film, and the adhesive layer in a dew condensation environment.
  • the polarizing film includes, in the adhesion surface of at least, one of the polarizer and the transparent, protective film, the compound having a boric acid group and/or a borate group (the compound of the general formula (1).
  • the boric acid group and/or the borate group is/are easily combined with hydroxyl groups and others which the polarizer, particularly, of a polyvinyl alcohol type and the transparent protective film have, so as to form covalent bonding.
  • the compound represented by the general formula (1) further has X containing a reactive group, and reacts through the reactive group, which X contains, with a curable component included in the adhesive layer.
  • the boric acid group and/or the borate group, which the compound represented by the general formula (1) has is/are strongly bonded to the hydroxyl groups and the others, which the polarizer and transparent protective film have, through covalent bonding.
  • the reactive group which the compound represented by the general formula (1) has is strongly bonded through covalent bonding to the adhesion surface of the adhesive layer. In this way, even when water is present in the interfaces between the polarizer and transparent protective film, and the adhesive layer, these interact strongly with each other not only through the hydrogen bonding and/or ion bonding but also through the covalent bonding, so that the polarizer and transparent protective film, and the adhesive layer are dramatically improved in adhesion water-resistance therebetween.
  • the adhering strength between the polarizer and the adhesive layer is improved so that the polarizing film is favorably improved, particularly, in adhesion water-resistance.
  • a reason therefor would be as follows: it has been pointed out in the prior art that the adhering strength between a polarizer and an adhesive layer is weak; however, when an adhesion surface of a polarizer has the compound represented by the general formula (1), an improvement is especially made in adhering strength between the polarizer and the adhesive layer by aid of the compound of the general formula (1).
  • the compound represented by the general formula (1) contains a reactive group through its phenylene or alkylene group bonded to its boric acid atom, adhesion water-resistance is more dramatically improved between the polarizer and the transparent protective film each having, on the surface thereof, this reactive group, and the adhesive layer.
  • a reason therefor can be presumed as follows: As described above, in the compound represented by the general formula (1), its boric acid group and/or borate group react (s) with hydroxyl groups and others which the polyvinyl alcohol type polarizer and the transparent protective film each have, so that these groups are strongly bonded to each other.
  • the reactive group which the compound represented by the general formula (1) has is strongly bonded through covalent bonding to the reactive group naked to the adhesion surface of the adhesive layer. In this way, these interact strongly with each other through not only the hydrogen bonding and/or ion bonding but also the covalent bonding even when water is present at the interface between the polarizer or the transparent protective film, and the adhesive layer. Thus, adhesion water-resistance is dramatically improved between the polarizer or the transparent protective film, and the adhesive layer. However, unless the reactive group which the compound represented by the general formula (1) has reacts with any curable component included in the adhesive layer, in the end a sufficient improvement is not made in adhesion water-resistance between the polarizer and the adhesive layer, and the adhesive layer.
  • the boric acid group and/or borate group, which the compound represented by the general formula (1) has, and further the polarizer and others show hydrophilicity; thus, affinity is not very high between the compound represented by the general formula (1) and the curable component included in the adhesive layer.
  • the compound represented by the general formula (1) contains a reactive group to interpose, therebetween, its phenylene or alkylene group bonded to a boron atom (the case of the general formula (1))
  • the phenylene or alkylene group shows affinity with the curable component, so that the reactive group which the compound represented by the general formula (1) has, this reactive group having reacted with the polarizer and others, reacts very effectively with the curable component included in the adhesive layer. Consequently, adhesion water-resistance is in particular dramatically improved between the polarizer and the adhesive layer.
  • the compound having a boric acid group and/or a borate group and having a reactive group there is a compound containing a reactive group to interpose, therebetween, an oxygen atom bonded to a boron atom (hereinafter referred to also as a “B—O bond containing compound”).
  • this compound is largely different in adhesion water-resistance improvement-degree from the compound containing a reactive group to interpose, therebetween, its phenylene or alkylene group bonded to a boron atom (hereinafter referred to also as a “B—C bond containing compound”) when the surface of at least one of the polarizer and the transparent protective film has each of these compounds.
  • the laminated resin film according to the present invention includes a first resin film, and a second resin film laminated on/over at least one surface of the first resin film to interpose an adhesive layer between the surface and the second resin film.
  • the adhesion surface of at least one of the first resin film and the second resin film includes a compound represented by the following general formula (1):
  • X is a functional group containing a reactive group
  • R 1 and R 2 each independently represent a hydrogen atom, or an aliphatic hydrocarbon group, aryl group or heterocyclic group that may have a substituent.
  • the compound represented by the general formula (1) is interposed at either one or both of a position between the first resin film and the adhesive layer, and a position between the second resin film and the adhesive layer.
  • the compound represented by the general formula (1) may be interposed in an reacted state or in a state that its individual functional groups have reacted between the first resin film and the adhesive layer, and/or between the second resin film and the adhesive layer.
  • the adhesion surface of at least one of the first resin film and the second resin film includes a compound represented by the general formula (1)
  • the adhesion surface of at least one of the first resin film and the second resin film includes a compound represented by the general formula (1)
  • the wording “the adhesion surface of at least one of the first resin film and the second resin film includes a compound represented by the general formula (1)” means that, for example, at least one molecule of the compound represented by the general formula (1) is present on the adhesion surface described herein.
  • an adhesion-improving composition including the compound represented by the general formula (1) to form an adhesion-improving layer on at least one portion of the adhesion surface described just above. It is more preferred to form the adhesion-improving layer on the entire surface of the adhesion surface.
  • the laminated resin film an example is given in which the first resin film is a polarizer, and the second resin film is a transparent protective film, and further an adhesion-improving layer is formed on at least one portion of the above-mentioned adhesion surface, that is,
  • a polarizing film in which a transparent protective film is laminated on at least one surface of a polarizer to interpose an adhesive layer therebetween, and the adhesion surface of at least one of the polarizer and the transparent protective film includes thereon an adhesion-improving layer formed, using an adhesion-improving composition including a compound represented by the general formula (1) wherein X is a functional group containing a reactive group, and R 1 and R 2 each independently represent a hydrogen atom, or an aliphatic hydrocarbons group, aryl group or heterocyclic group that may have a substituent.
  • the aliphatic hydrocarbon group is, for example, a linear or branched alkyl group which has 1 to 20 carbon atoms and may have a substituent, a cyclic alkyl group which has 3 to 20 carbon atoms and may have a substituent, or an alkenyl group which has 2 to 20 carbon atoms.
  • the aryl group is, for example, a phenyl group which has 6 to 20 carbon atoms and may have a substituent, or a naphthyl group which has 10 to 20 carbon atoms and may have a substituent.
  • the heterocyclic group is, for example, a 5-membered or 6-membered group which contains at least one heteroatom, and may have a substituent.
  • R 1 and R 4 are each preferably a hydrogen atom, or a linear or branched alkyl group having 1 to 3 carbon atoms, most preferably a hydrogen atom.
  • the group X which the compound represented by the general formula (1) has, is a functional group including a reactive group, and is a functional group that can react with a curable component contained in the adhesive layer.
  • the reactive group, which X includes, include hydroxyl, amino, aldehyde, carboxyl, vinyl, (meth)acryl, styryl, (meth)acrylamide, vinyl ether, epoxy, oxetane, ⁇ , ⁇ -unsaturated carbonyl, mercapto, and halogen groups.
  • the reactive group, which X includes is preferably at least one reactive group selected from the group consisting of vinyl, (meth)acryl, styryl, (meth)acrylamide, vinyl ether, epoxy, oxetane, and mercapto groups.
  • the reactive group, which X includes is preferably at least one reactive group selected from the group consisting of (meth)acryl, styryl, and (meth)acrylamide groups.
  • the compound represented by the general formula (1) has a (meth)acrylamide group since the compound is high in reactivity to be increased in copolymerization rate in the active-energy-ray-curable adhesive composition. This case is preferred also since the (meth)acrylamide group is high in polarity so that the resultant adhesive is excellent in adhesion to produce the advantageous effects of the present invention effectively.
  • the reactive group, which X includes has preferably at least one functional group selected from the group consisting of hydroxyl, amino, aldehyde, carboxyl, vinyl ether, epoxy, oxetane, and mercapto groups.
  • the reactive group has, in particular, an epoxy group, close adhesion between the resultant adhesive layer and an adherend is favorably excellent.
  • the reactive group has a vinyl ether group
  • the curable resin composition is favorably excellent in curability.
  • a preferred and specific, example of the compound represented by the general formula (I) is a compound represented by the following general formula (1′):
  • Y is an organic group
  • X, R 1 and R 2 are the same as described above. More preferred examples thereof include the following compounds (1a) to (1d):
  • the compound represented by the general formula (1) may be a compound in which a reactive group is bonded directly to a boron atom.
  • the compound represented by the general formula (1) is a compound in which a reactive group and a boron atom are bonded to each other to interpose, therebetween, an organic group, that is, a compound represented by the general formula (1′).
  • the compound represented by the general formula (I) is, for example, a compound in which an organic group is bonded to a reactive group to interpose, therebetween, an oxygen atom bonded to a boron atom, the polarizing film tends to be deteriorated in adhesion water-resistance.
  • the compound represented by the general formula (1) is not a compound having a boron-oxygen bond, but a compound in which a boron atom is bonded to an organic group so that while this compound has a boron-carbon bond, the compound contains a reactive group (in the case of the general formula (1)), the polarizing film is favorably improved in adhesion water-resistance.
  • the organic group specifically denotes an organic group that has 1 to 20 carbon atoms and may have a substituent. More specific examples thereof include any linear or branched alkylene group that has 1 to 20 carbon atoms and may have a substituent, any cyclic alkylene group that has 3 to 20 carbon atoms and may have a substituent, any phenylene group that has 6 to 20 carbon atoms and may have a substituent, and any naphthylene group that has 10 to 20 carbon atoms and may have a substituent.
  • Examples of the compound represented by the general formula (1) include, besides the compounds given above as the examples thereof, an ester made from hydroxyethylacrylamide and boric acid, an ester made from methylolacrylamide and boric acid, an ester made from hydroxyethyl, acrylate and boric acid, an ester made from hydroxybutyl acrylate and boric acid, and any other ester made from a (meth)acrylate and boric acid.
  • the method for using an adhesion-improving composition including a compound represented by the general formula (1) to form an adhesion-improving layer onto an adhesion surface of at least one of a polarizer and a transparent protective film is, for example, a method of producing the adhesion-improving composition (A) including the compound represented by the general formula (1), and then forming this composition into a layer on the adhesion surface of at least one of the polarizer and the transparent protective film by, for example, applying.
  • Substances that are other than the compound represented by the general formula (1) and may be included in the adhesion-improving composition (A) are, for example, a solvent and additives.
  • the adhesion-improving composition (A) includes a solvent
  • the solvent which may be included in the adhesion-improving composition (A), is preferably a solvent capable of stabilizing a compound represented by the general formula (1) to dissolve or disperse the compound.
  • the solvent may be an organic solvent, water, or a mixed solvent of these solvents.
  • the solvent is selected from, for example, the following: ethyl acetate, butyl acetate, 2-hydroxyethyl acetate, and other esters; methyl ethyl ketone, acetone, cyclohexanone, methyl isobutyl ketone, diethyl ketone, methyl-n-propyl ketone, acetylacetone, and other ketones; tetrahydrofuran (THF), dioxane, and other cyclic ethers; n-hexane, cyclohexane, and other aliphatic or alicyclic hydrocarbons; toluene, xylene, and other aromatic hydrocarbons; methanol, ethanol, n-propanol, isopropanol, cyclohexanol, and other aliphatic or alicyclic alcohols; ethylene glycol monomethyl ether, ethylene glycol monoethyl ether, diethylene glyco
  • Examples of the additive which may be included in the adhesion-improving composition (A), include a binder resin, a surfactant, a plasticizer, a tackifier, a low molecular weight polymer, a polymerizable monomer, a surface lubricant, a leveling agent, an antioxidant, a corrosion inhibitor, a light stabilizer, an ultraviolet absorber, a polymerization inhibitor, a silane coupling agent, a titanium coupling agent, an inorganic or organic filler, a metal powder, and a particulate or foil material.
  • a binder resin a surfactant, a plasticizer, a tackifier, a low molecular weight polymer, a polymerizable monomer, a surface lubricant, a leveling agent, an antioxidant, a corrosion inhibitor, a light stabilizer, an ultraviolet absorber, a polymerization inhibitor, a silane coupling agent, a titanium coupling agent, an inorganic or organic filler, a metal
  • the binder resin is sufficient to be transparent, and examples thereof include acrylic resins, styrene-based resins, polyvinyl alcohol-based resins, urethane resins, polyester resins, polypropylene resins, polyethylene resins, epoxy resins, polycarbonate resins, and other polymers.
  • the adhesion-improving composition (A) includes a binder resin
  • the content thereof is preferably 1 part or more, preferably 5 parts or more by weight for 100 parts by weight of the compound represented by the general formula (1).
  • the content is preferably 300 parts or less, more preferably 200 parts or less, even more preferably 150 parts or less, in particular preferably 100 parts or less by weight therefor.
  • the adhesion-improving composition (A) includes a levelling agent
  • the content thereof is 1 part or more, preferably 5 parts by weight or more for 100 parts by weight of the compound represented by the general formula (1).
  • the content is preferably 35 parts or less, more preferably 20 parts or less, even more preferably 10 parts or less by weight therefor.
  • adhesion-improving composition (A) includes any other additive, the content thereof is preferably 1 part or more for 100 parts by weight of the compound represented by the general formula (1). In the meantime, the content is preferably 30 parts or less therefor.
  • the adhesion-improving composition (A) includes a polymerization initiator
  • the compound represented by the general formula (1) may react in the adhesion-improving layer before the adhesive layer is laminated thereonto.
  • the polarizing film may not sufficiently gain an adhesion water-resistance improving effect, which is a primary purpose.
  • the content of the polymerization initiator in the adhesion-improving layer is preferably less than 2%, preferably less than 0.5% by weight.
  • the composition in particular preferably contains no polymerization initiator.
  • the content of the compound represented by the general formula (1) in the adhesion-improving layer is preferably 1% or more, more preferably 20% or more, even more preferably 40% or more by weight.
  • the adhesion-improving layer formed on the adhesion surface of at least one of the polarizer and the transparent protective, film may include, besides the compound represented by the general formula (1), a compound having a structural formula having an M—O bond wherein M is silicon, titanium, aluminum or zirconium, and O represents an oxygen atom.
  • the compound having the M—O bond is at least one organometallic compound selected from the group consisting of organic silicon compounds, metal alkoxides and metal chelates.
  • any one of the organic silicon compounds a compound having a Si—O bond is usable without any especial limitation.
  • a specific example thereof is an active-energy-ray-curable organic silicon compound or an organic silicon compound having no active-energy-ray curability.
  • the organic group which the organic silicon compound has in particular preferably has 3 or more carbon atoms.
  • Examples of the active-energy-ray-curable compound include vinyltrichlorosilane, vinyltrimethoxysilane, vinyltriethoxysilane, 2-(3,4 epoxycyclohexyl) ethyltrimethoxysilane, 3-glycidoxypropyltrimethoxysilane, 3-glycidoxypropylmethyldiethoxysilane, 3-glycidoxypropyltriethoxysilane, p-styryltrimethoxysilane, 3-methacryloxypropylmethyldimethoxysilane, 3-methacryloxypropyltrimethoxysilane, 3-methacryloxypropylmethyldiethoxysilane, 3-methacryloxypropyltriethoxysilane, and 3-acryloxypropyltrimethoxysilane.
  • a specific example of the compound having no active-energy-ray curability is preferably a compound having an amino group.
  • Specific examples of the compound having an amino group include ⁇ -aminopropyltrimethoxysilane, ⁇ -aminopropyltriethoxysilane, ⁇ -aminopropyltriisopropoxysilane, ⁇ -aminopropylmethyldimethoxysilane, ⁇ -aminopropylmethyldiethoxysilane, ⁇ -(2-aminoethyl)aminopropyltrimethoxysilane, ⁇ -(2-aminoethyl)aminopropylmethyldimethoxysilane, ⁇ -(2-aminoethyl)aminopropyltriethoxysilane, ⁇ -(2-aminoethyl)aminopropylmethyldiethoxysilane, ⁇ -(2-aminoethyl)aminopropyltri
  • Such compounds each having an amino group may be used singly or in any combination of two or more thereof. Out of the compounds, the following are preferred in order that the adhesive layer can ensure a good adhesion:
  • ⁇ -aminopropyltrimethoxysilane ⁇ -(2-aminoethyl)aminopropyltrimethoxysilane, ⁇ -(2-aminoethyl)aminopropylmethyldimethoxysilane, ⁇ -(2-aminoethyl)aminopropyltriethoxysilane, ⁇ -(2-aminoethyl)aminopropylmethyldiethoxysilane, and N-(1,3-dimethylbutylidene)-3-(triethoxysilyl)-1-propanamine.
  • the compound having no active-energy-ray curability include, besides the above-mentioned examples, 3-ureidapropyltriethoxysilane, 3-chloropropyltrimethoxysilane, 3-mercaptopropylmethyldimethoxysilane, 3-mercaptopropyltrimethoxysilane, bis(triethoxysilylpropyl)tetrasulfide, 3-isocyanatopropyltriethoxysilane, and imidazole silane.
  • the metal alkoxides are each a compound in which at least one alkoxy group, which is an organic group, is bonded to a metal.
  • the metal chelates are each a compound in which an organic group is bonded or coordinated through an oxygen atom to a metal.
  • Their metal is preferably titanium, aluminum or zirconium. Out of these metals, aluminum and zirconium are speedier in reactivity than titanium, and may make the pot life of the adhesion-improving composition (A) for forming the adhesion-improving layer shorter and make the adhesion water-resistance improving effect smaller.
  • the metal of the organometallic compounds is more preferably titanium from the viewpoint of an improvement of the adhesion-improving layer-in adhesion water-resistance.
  • the adhesion-improving composition (A) for forming the adhesion-improving layer includes, as the organometallic compound, a metal alkoxide, it is preferred to use a metal alkoxide having an organic group having 3 or more carbon atoms.
  • the organic group more preferably contains 6 or more carbon atoms. If the number of the carbon atoms therein is 2 or less, the composition: (A) may become short in pot life and further the adhesion water-resistance improving effect may be lowered.
  • the organic group having 6 or more carbon atoms is, for example, an octoxy group. This group is preferably usable.
  • Preferred examples of the metal alkoxide include tetraisopropyl titanate, tetra-n-butyl titanate, a butyl titanate dimer, tetraoctyl titanate, tert-amyl titanate, tetra-tert-butyl titanate, tetrastearyl titanate, zirconium tetraisopropoxide, zirconium tetra-n-butoxide, zirconium tetraoctoxide, zirconium tetra-tert-butoxide, zirconium tetrapropoxide, aluminum sec-butylate, aluminum ethylate, aluminum isopropylate, aluminum butylate, aluminum diisopropylate mono-sec-butyrate, and mono-sec-butoxyaluminum diisopropylate. Out of these examples, tetra-octyl titanate is preferred.
  • the composition (A) for forming the adhesion-improving layer includes, as the organometallic compound, a metal chelate, it is preferred that the composition includes a metal chelate having an organic group having 3 or more carbon atoms. If the number of the carbon atoms therein is 2 or less, the adhesion-improving composition (A) may become short in pot life and further the adhesion water-resistance improving effect may be lowered.
  • the organic group having 3 or more carbon atoms is, for example, an acetylacetonate, ethylacetoacetate, isostearate, or octyleneglycolate group.
  • the organic group is preferably an acetylacetonate or ethylacetoacetate from the viewpoint of an improvement of the adhesion-improving layer in adhesion water-resistance.
  • Preferred examples of the metal chelate include titanium acetylacetonate, titanium octyleneglycolate, titanium tetraacetylacetonate, titanium ethylacetoacetate, polyhydroxytitanium stearate, dipropoxy-bis(acetylacetonato)titanium, dibutoxytitanium-bis(octyleneglycolate), dipropoxytitanium-bis(ethylacetoacetate), titanium lactate, titanium diethanolaminate, titanium triethanolaminate, dipropoxytitanium-bis(lactate), dipropoxytitanium-bis(triethanolaminate), di-n-butoxytitanium-bis(triethanolaminate), tri-n-butoxytitanium monostearate
  • organometallic compound usable in the present invention examples include, besides the above-mentioned compounds, zinc octoate, zinc laurate, zinc stearate, tin octoate, and other organic carboxylic acid metal salts; and acetylacetone zinc chelate, benzoylacetone zinc chelate, dibenzoylmethane zinc chelates, ethyl acetoacetate zinc chelate, and other zinc chelate compounds.
  • the content of the compound having an M—O bond is preferably from 0 to 90%, more preferably from 1 to 70%, in particular preferably from 10 to 50% by weight.
  • thermosetting resin In a polarizing film given as an example of the laminated resin film according to the present invention, a polarizer and a transparent protective film are laminated onto each other to interpose an adhesive layer therebetween.
  • This adhesive layer is formed by curing a curable resin composition.
  • the form of curing the curable resin composition is roughly classified into a thermosetting form and an active energy ray curable form.
  • a resin in the thermosetting form include polyvinyl alcohol resin, epoxy resin, unsaturated polyester, urethane resin, acrylic resin, urea resin, melamine resin, and phenolic resin.
  • a curing agent is together used.
  • the thermosetting resin is more preferably polyvinyl alcohol resin or epoxy resin.
  • Resins in the active energy ray curable form can be roughly classified into electron beam curable, ultraviolet curable and visible ray curable forms according to classification based on an active energy ray therefor.
  • the curable resin composition can be divided, in accordance with the form of the curing thereof, into a radical polymerization curable resin composition or a cationic polymerization curable resin composition.
  • any active energy ray having a wavelength in a range of 10 nm or more and less than 380 nm is described as an ultraviolet ray; and any active energy ray having a wavelength in a range from 380 to 800 nm, as a visible ray.
  • the curable resin composition is preferably in an active energy ray curable form as described above.
  • the composition is in particular preferably in a visible ray curable form, which makes use of visible rays in a wavelength range from 380 to 450 nm.
  • a curable component included in the radical polymerization curable resin composition is, for example, a radical polymerizable compound used in any radical polymerization curable resin composition.
  • the radical polymerizable compound is, for example, a compound having a radical polymerizable functional group of a carbon-carbon double bond, such as a methacryloyl group or a vinyl group.
  • Such a curable component may be either a monofunctional radical polymerizable compound, or a bifunctional or higher polyfunctional radical polymerizable compound.
  • Such radical polymerizable compounds may be used singly, or in any combination of two or more thereof.
  • the radical polymer is able compound(s) is/are (each), for example, a compound having a (meth)acryloyl group.
  • the word “(meth)acryloyl” denotes an acryloyl group and/or a methacryloyl group.
  • the notation “(meth)a” has substantially the same meanings hereinafter.
  • the monofunctional radical polymerizable compound is, for example, a compound represented by the following general formula (2):
  • R 3 is a hydrogen atom or a methyl group
  • R 4 and R 5 are each independently a hydrogen atom, or an alkyl, hydroxyalkyl, alkoxyalkyl or cyclic ether group, and R 4 and R 5 may form a cyclic heterocycle.
  • the number of carbon atoms in the alkyl moiety of (each of) the alkyl, hydroxyalkyl, and/or alkoxyalkyl group(s) is not particularly limited, and is, for example, from 1 to 4.
  • the cyclic heterocycle, which R 4 and R 3 may form, is, for example, an N-acryloylmorpholine.
  • Specific examples of the compound represented by the general formula (2) include M-methyl(meth)acrylamide, N,N-dimethyl(meth)acrylamide, N,N-diethyl(meth)acrylamide, N-isopropyl(meth)acrylamide, N-butyl(meth)acrylamide, N-hexyl(meth)acrylamide, and other N-alkyl-group-containing (meth)acrylamide derivatives; N-methylol(meth)acrylamide, N-hydroxyethyl(meth)acrylamide, N-methylol-N-propane(meth)acrylamide, and other N-hydroxyalkyl-group-containing (meth)acrylamide derivatives; and N-methoxymethylacrylamide, N-ethoxymethylacrylamide, and other N-alkoxy-group-containing (meth)acrylamide derivatives.
  • the cyclic-ether-group-containing (meth)acrylamide derivative is, for example, a heterocycle-containing (meth)acrylamide derivative in which a nitrogen atom of a (math)acrylamide group forms a heterocycle.
  • examples thereof include N-acryloylmorpholine, N-acryloylpiperidine, N-methacryloylpiperidine, and N-acryloylpyrrolidine.
  • N-hydroxyethylacrylamide and N-acryloylmorpholine are preferred since these compounds are excellent in reactivity, can each give a cured product with a high elastic modulus, and the resultant adhesive layer is excellent in adhesion to the polarizer.
  • the content of the compound represented by the general formula (2) in the curable resin composition is preferably from 0.01 to 80%, more preferably from 5 to 40% by weight.
  • the curable resin composition used in the present invention may contain, besides the compound represented by the general formula (2), a different monofunctional radical polymerizable compound as a curable component.
  • a different monofunctional radical polymerizable compound examples include various (meth)acrylic acid derivatives each having a (meth)acryloyloxy group.
  • Specific examples thereof include methyl (meth)acrylate, ethyl (meth)acrylate, n-propyl (meth)acrylate, isopropyl (meth)acrylate, 2-methyl-2-nitropropyl (meth)acrylate, n-butyl (meth)acrylate, isobutyl (meth)acrylate, s-butyl (meth)acrylate, t-butyl (meth)acrylate, n-pentyl (meth)acrylate, t-pentyl (meth)acrylate, 3-pentyl (meth)acrylate, 2,2-dimethylbutyl (meth)acrylate, n-hexyl (meth)acrylate, cetyl (meth)acrylate, n-octyl (meth)acrylate, 2-ethylhexyl (meth)acrylate, 4-methyl-2-propylpentyl (meth)acrylate, n-octadecy
  • Examples of the above-mentioned (meth)acrylic acid derivatives include cyclohexyl (meth)acrylate, cyclopentyl (meth)acrylate, and other cycloalkyl (meth)acrylates; benzyl (meth)acrylate, and other aralkyl (meth)acrylates; 2-isobornyl (meth)acrylate, 2-norbornylmethyl (meth)acrylate, 5-norbornen-2-yl-methyl (meth)acrylate, 3-methyl-2-norbornylmethyl (meth)acrylate, dicyclopentenyl (meth)acrylate, dicyclopentenyloxyethyl (meth)acrylate, dicyclopentanyl (meth)acrylate, and other polycyclic (meth)acrylates; and 2-methoxyethyl (meth)acrylate, 2-ethoxyethyl (meth)acrylate, 2-methoxymethoxyethyl (meth)acrylate, 3-
  • Examples of the above-mentioned (meth)acrylic derivatives include 2-hydroxyethyl (meth)acrylate, 2-hydroxypropyl (meth)acrylate, 3-hydroxypropyl (meth)acrylate, 2-hydroxybutyl (meth)acrylate, 4-hydroxybutyl (meth)acrylate, 6-hydroxyhexyl (meth)acrylate, 8-hydroxyoctyl (meth)acrylate, 10-hydroxydecyl (meth)acrylate, 12-hydroxylauryl (meth)acrylate, and other hydroxyalkyl (meth)acrylates; [4-(hydroxymethyl)cyclohexyl]methyl acrylate, cyclohexanedimethanol mono(meth)acrylate, 2-hydroxy-3-phenoxypropyl (meth)acrylate, and other hydroxyl-group-containing (meth)acrylates; glycidyl (meth)acrylate, 4-hydroxybutyl (meth)acrylate glycidyl ether, and other epoxy-group-
  • Examples of the monofunctional radical polymerizable compound include (meth)acrylic acid, carboxyethyl acrylate, carboxypentyl acrylate, itaconic acid, maleic acid, fumaric acid, crotonic acid, isocrotonic acid, and other carboxyl-group-containing monomers.
  • the monofunctional radical polymerizable compound examples include N-vinylpyrrolidone, N-vinyl- ⁇ -caprolactam, methylvinylpyrrolidone, and other lactam-based vinyl monomers; vinylpyridine, vinylpiperidone, vinylpyrimidine, vinylpiperazine, vinylpyrazine, vinylpyrrole, vinylimidazole, vinyloxazole, vinylmorpholine, and other vinyl monomers each having a nitrogen-containing heterocycle.
  • the resultant cured product layer is improved in adhesion in various substrates.
  • the content of the hydroxyl-group-containing (meth)acrylate is preferably from 1 to 30% by weight of the resin composition. If the content is too large, the cured product may become high in water absorption coefficient to be deteriorated in water resistance.
  • the content of the carboxyl-group-containing (meth)acrylate is preferably from 1 to 20% by weight of the resin composition. If the content is too large, the polarizing film is unfavorably lowered in optical endurance.
  • the phosphate-group-containing (meth) acrylate is, for example, 2-(meth) acryloyloxyethyl acid phosphate.
  • the content thereof is preferably from 0.1 to 10% by weight of the resin composition. If the content is too large, the polarizing film is unfavorably lowered in optical endurance.
  • the monofunctional radical polymerizable compound may also be a radical polymerizable compound having an active methylene group.
  • the radical polymerizable compound having an active methylene group is a compound having, at a terminal thereof or in the molecule thereof, an active double bond group such as a (meth)acryl group, and further having an active methylene group.
  • Examples of the active methylene group include acetoacetyl, alkoxymalonyl, and cyanoacetyl groups.
  • the active methylene group is preferably an acetoacetyl group.
  • radical polymerizable compound having an active methylene group examples include 2-acetoacetoxyethyl (meth)acrylate, 2-acetoacetoxypropyl (meth)acrylate, 2-acetoacetoxy-1-methylethyl (meth)acrylate, and other acetoacetoxyalkyl (meth)acrylates; and 2-ethoxymalonyloxyethyl (meth)acrylate, 2-cyanoacetoxyethyl (meth)acrylate, N-(2-cyanoacetoxyethyl)acrylamide, N-(2-propionylacetoxybutyl)acrylamide, N-(4-acetoacetoxymethylbenzyl)acrylamide, and N-(2-acetoacetylaminoethyl)acrylamide.
  • the radical polymerizable compound having an active methylene group is preferably an acetoacetoxyalkyl (meth)acrylate.
  • Examples of the bi- or higher polyfunctional radical polymerizable compound include N,N′-methylenebis(meth)acrylamide, which is a polyfunctional (meth)acrylamide derivative, tripropylene glycol di(meth)acrylate, tetraethylene glycol di(meth)acrylate, 1,6-hexanediol di(meth)acrylate, 1,9-nonanediol di(meth)acrylate, 1,10-decanediol diacrylate, 2-ethyl-2-butylpropanediol di(meth)acrylate, bisphenol A di(meth)acrylate, bisphenol A ethylene oxide adduct di(meth)acrylate, bisphenol A propylene oxide adduct di(meth)acrylate, bisphenol A diglycidyl ether di(meth)acrylate, neopentyl glycol di(meth)acrylate, tricyclodecanedimethanol di(meth)acrylate, cyclic
  • Preferred and specific examples thereof include ARONIX M-220 (manufactured by Toagosei Co., Ltd.), LIGHT ACRYLATE 1,9 ND-A (manufactured by Kyoeisha Chemical Co., Ltd.), LIGHT ACRYLATE DGE-4A (manufactured by Kyoeisha Chemical Co., Ltd.), LIGHT ACRYLATE DCP-A (manufactured by Kyoeisha Chemical Company, Ltd.), SR-531 (manufactured by a company Sartomer Co.), and CD-536 (manufactured by the company Sartomer).
  • a polyfunctional (meth)acrylamide derivative is preferably incorporated into the curable resin composition since the derivative gives a large polymerization rate to give an excellent producing performance, and further at the time of making the resin composition into a cured product the derivative gives an excellent crosslinking performance.
  • the monofunctional radical polymerizable compound and the polyfunctional radical polymerizable compound are preferably used together with each other in order to make the following compatible with each other: adhesion of the resultant layer to the polarizer and various transparent protective films; and the optical endurance of the polarizing film in a severe environment. It is usually preferred to use the monofunctional radical polymerizable compound in a proportion of 3 to 80% by weight of the radical polymerizable compounds, and the polyfunctional radical polymerizable compound in a proportion of 20 to 97% by weight thereof.
  • the curable resin composition used in the present invention is usable as an active-energy-ray-curable resin composition when the curable component of this composition is used as an active energy ray curable component.
  • the active-energy-ray-curable resin composition does not need to contain any photopolymerization initiator.
  • this composition preferably contains a photopolymerization initiator.
  • the photopolymerization initiator is appropriately selected in accordance with the active energy ray.
  • an ultraviolet or visible-ray-cleavable photopolymerization initiator is used.
  • this photopolymerization initiator examples include benzil, benzophenone, benzoyl benzoic acid, 3,3′-dimethyl-4-methoxybenzophenone, and other benzophenone compounds; 4-(2-hydroxyethoxy)phenyl (2-hydroxy-2-propyl) ketone, ⁇ -hydroxy- ⁇ , ⁇ ′-dimethylacetophenone, 2-methyl-2-hydroxypropiophenone, ⁇ -hydroxycyclohexyl phenyl ketone, and other aromatic ketone compounds; methoxyacetophenone, 2,2-dimethoxy-2-phenylacetophenone, 2,2-diethoxyacetophenone, 2-methyl-1-[4-(methylthio)-phenyl]-2-morpholinopropane-1, and other acetophenone compounds; benzoin methyl ether, benzoin ethyl ether, benzoin isopropyl ether, benzoin butyl ether, anisoin methyl ether, and other benzoin
  • the blend amount of the photopolymerization initiator is 20% or less by weight of the whole of the curable resin composition.
  • the blend amount of the photopolymerization initiator is preferably from 0.01 to 20%, more preferably from 0.05 to 10%, even more preferably from 0.1 to 5% by weight thereof.
  • the curable resin composition used in the present invention is used as a visible ray curable composition including, as a curable component thereof, a radical polymerizable compound
  • a photopolymerization initiator high in sensitivity particularly, to light rays having a wavelength of 380 nm or more.
  • a description will be made later.
  • R 6 and R 7 each represent —H, —CH 2 CH 3 , -iPr or Cl, and R 6 and R 7 may be the same as or different from each other; or use the compound represented by the general formula (3) together with a photopolymerization initiator high in sensitivity to light rays having a wavelength of 380 nm or more, which will be detailed later.
  • the compound represented by the general formula (3) is used, the cured product is better in adhesion than when the photopolymerization initiator high in sensitivity to light rays having a wavelength of 380 nm or more is used singly.
  • the composition proportion of the compound represented by the general formula (3) in the curable resin composition is preferably from 0.1 to 5%, more preferably from 0.5 to 4%, even more preferably from 0.9 to 3% by height of the whole of the curable resin composition.
  • a polymerization initiation aid is preferably added into the composition.
  • the polymerization initiation aid include triethylamine, diethylamine, N-methyldiethanolamine, ethanolamine, 4-dimethylaminobenzoic acid, methyl 4-dimethylaminobenzoate, ethyl 4-dimethylaminobenzoate, and isoamyl 4-dimethylaminobenzoate. Ethyl 4-dimethylaminobenzoate is particularly preferred.
  • the addition amount thereof is usually from 0 to 5%, preferably from 0 to 4%, most preferably from 0 to 3% by weight of the whole of the curable resin composition.
  • a known photopolymerization initiator may be together used.
  • a transparent protective film having a UV absorbing power does not transmit any light ray of 380 nm or less wavelengths.
  • Specific examples thereof include 2-methyl-1-(4-methylthiophenyl)-2-morpholinopropan-1-one, 2-benzyl-2-dimethylamino-1-(4-morpholinophenyl)-butanone-1, 2-(dimethylamino)-2-[(4-methylphenyl)methyl]-1-[4-(4-morpholinyl)phenyl]-1-butanone, 2,4,6-trimethylbenzoyl-diphenyl-phosphine oxide, bis(2,4,6-trimethylbenzoyl)-phenylphosphine-oxide, bis( ⁇ 5-2,4-cyclopentadien-1-yl)-bis(2,6-difluoro-3-(1H-pyrrol-1-yl)-phenyl)titanium.
  • R 8 , R 9 and R 10 each represent —H, —CH 3 , —CH 2 H 3 , -iPr or Cl, and R 8 , R 9 and R 10 may be the same or different.
  • a preferably usable example of the compound represented by the general formula (4) is 2-methyl-1-(4-methylthiophenyl)-2-morpholinopropan-1-one, which is also a commercially available product (trade name: IRGACURE 907, manufacturer: the company BASF).
  • 2-benzyl-2-dimethylamino-1-(4-morpholinophenyl)-butanone-1 (trade name: IRGACORE: 369, manufacturer; the BASF), 2-(dimethylamino)-2-[(4-methylphenyl)methyl]-1-[4-(4-morpholinyl)phenyl]-1-butanone (trade name: IRGACURE 379, manufacturer: the BASF).
  • radical polymerizable compound a radical polymerizable compound having an active methylene group in the active-energy-ray-curable resin composition
  • a combination of this compound with a radical polymerization initiator having hydrogen-withdrawing effect makes a remarkable improvement of the adhesive layer, which the polarizing film has, in adhesion even immediately after the polarizing film is taken out, particularly, from a high-humidity environment or water (even when the film is in a non-dry state). Reasons therefor are unclear.
  • the improvement would be based on the following causes: While the radical polymerizable compound having an active methylene group is polymerized together with the other radical polymerizable compounds that will be included in the adhesive layer, the compound is taken into a main chain and/or side chains of a base polymer in the adhesive layer to form the adhesive layer. In this polymerizing step, in the presence of the radical polymerization initiator, having hydrogen-withdrawing effect, the base polymer, which will be included in the adhesive layer, is formed and simultaneously hydrogen is withdrawn from the active-methylene-having radical polymerizable compound to generate radicals in methylene groups of molecules of the compound.
  • the methylene groups in which radicals are generated react with hydroxyl groups of the polarizer, such as ones of PVA, so that covalent bonds are formed between the adhesive layer and the polarizer. Consequently, the adhesive layer which the polarizing film has would be remarkably improved in adhesion even when the polarizing film is, particularly, in a non-dry state.
  • the radical polymerization initiator having hydrogen-withdrawing effect is, for example, a thioxanthone-based radical polymerization initiator, or a benzophenone-based radical polymerization initiator.
  • the radical polymerization initiator is preferably a thioxanthone-based radical polymerization initiator.
  • the thioxanthone-based radical polymerization initiator is, for example, a compound represented by the general formula (3). Specific examples of the compound represented by the general formula (3) include thioxanthone, dimethylthioxanthone, diethylthioxanthone, isopropylthioxanthone, and chlorothioxanthone. Out of compounds represented by the general formula (3), preferred is diethylthioxanthone, in which R 6 and R 7 are each —CH 2 CH 3 —.
  • the active-energy-ray-curable resin composition contains the radical polymerizable compound having an active methylene group and the radical polymerization initiator having hydrogen-withdrawing effect
  • the radical polymerizable compound having an active methylene group is contained in a proportion of 1 to 50% by weight of the whole of the curable components, and the radical polymerization initiator is contained in a proportion of 0.1 to 10% by weight of the whole.
  • radicals are generated in methylene groups of molecules of the active-methylene-group-having radical polymerizable compound in the presence of the radical polymerization initiator having hydrogen-withdrawing effect.
  • the methylene groups react with hydroxyl groups of the polarizer, such as ones of PVA, to form covalent bonds.
  • the active-methylene-group-having radical polymerizable compound is incorporated into the composition preferably in a proportion of 1 to 50%, more preferably in a proportion of 3 to 30% by weight of the whole of the curable components.
  • the proportion of the active-methylene-group-having radical polymerizable compound is set preferably to 1% or more by weight. In the meantime, if the proportion is more than 50% by weight, the adhesive layer may be poorly cured.
  • the radical polymerization initiator having hydrogen-withdrawing effect is contained preferably in a proportion of 0.1 to 10%, more preferably in a proportion of 0.3 to 9% by weight of the whole of the curable resin composition. In order to cause the hydrogen-withdrawing reaction sufficiently, the radical polymerization initiator is used in a proportion of 0.1% or more by weight. In the meantime, if the proportion is more than 10% by weight, the initiator may not be completely dissolved in the composition.
  • the cation polymerizable compound used in the cation polymerization curable resin composition is classified into a monofunctional cation polymerizable compound, which has in the molecule thereof a single cation polymerizable functional group, or a polyfunctional cation polymerizable compound, which has in the molecule thereof two or more cation polymerizable functional groups.
  • the mono-functional cation polymerizable compound is relatively low in liquid viscosity; thus, when this compound is incorporated into the resin composition, the resin composition can be lowered in liquid viscosity.
  • the monofunctional cation polymerizable compound has a functional group for expressing various functions.
  • the incorporation of this compound into the resin composition can cause various functions to be expressed in the resin composition and/or a cured product of the resin composition.
  • the polyfunctional cation polymerizable compound allows to crosslink the cure product of the resin composition three-dimensionally.
  • this compound is preferably incorporated into the resin composition.
  • the cation polymerizable functional group may be an epoxy, oxetanyl or vinyl ether group. Examples of a compound having this epoxy group include aliphatic epoxy compounds, alicyclic epoxy compounds, and aromatic epoxy compounds.
  • the cation polymerization curable resin composition in the present invention in particular preferably contains an alicyclic epoxy compound since the composition is excellent in curability and adhesion.
  • the alicyclic epoxy compound include 3,4-epoxycyclohexylmethyl-3,4-epoxycyclohexane carboxylate, and caprolactone-modified products, trimethyl caprolactone modified products or valerolactone-modified products of 3,4-epoxycyclohexylmethyl-3,4-epoxycyclohexane carboxylate.
  • Examples of the oxetanyl-group-having compound include 3-ethyl-3-hydroxymethyloxetane, 1,4-bis[(3-ethyl-3-oxetanyl)methoxymethyl]benzene, 3-ethyl-3-(phenoxymethyl)oxetane, di[(3-ethyl-3-oxetanyl)methyl]ether, 3-ethyl-3-(2-ethylhexyloxymethyl)oxetane, and phenol novolac oxetane.
  • the compound having the above-mentioned vinyl ether group has an effect of improving the cation polymerization curable resin, composition in curability or lowering the composition in liquid viscosity; thus, this compound is preferably incorporated into the composition.
  • Examples of the vinyl-ether-group-having compound include 2-hydroxyethyl vinyl ether, diethylene glycol monovinyl ether, 4-hydroxybutyl vinyl ether, diethylene glycol monovinyl ether, triethylene glycol divinyl ether, cyclohexanedimethanol divinyl ether, cyclohexanedimethanol monovinyl ether, tricyclodecane vinyl ether, cyclohexyl vinyl ether, methoxyethyl vinyl ether, ethoxyethyl vinyl ether, and pentaerythritol type tetravinyl ether.
  • the cation polymerization curable resin composition includes, as a curable component, at least one compound selected from the above-mentioned epoxy-group-having compound, the oxetanyl-group-having compound and the vinyl-ether-group-having compound, and these compounds are each cured by cation polymerization.
  • a cation photopolymerization initiator is blended into the composition.
  • This cation photopolymerization initiator is irradiated with an active energy ray such as a visible ray, an ultraviolet ray, an X ray or an electron beam to generate a cationic species or Lewis acid to initiate the polymerization reaction of epoxy groups and oxetanyl groups.
  • the cation photopolymerization initiator is preferably an optical acid generator which will be detailed later.
  • a cation photopolymerization initiator high in sensitivity to light rays having wavelengths of 380 nm or more.
  • cation photopolymerization initiators are each a compound showing a maximum absorption near 300 nm or in the range of wavelengths shorter than 300 nm.
  • the photosensitizer by blending, into the composition, a photosensitizer showing a maximum absorption in the range of wavelengths longer than 300 nm, specifically, wavelengths longer than 380 nm, the photosensitizer sensitizes light rays each having a wavelength near this wavelength so that the generation of a cation species or acid can be promoted from the cation photopolymerization initiator.
  • the photosensitizer include anthracene compounds, pyrene compounds, carbonyl compounds, organic sulfur compounds, persulfates, redox compounds, azo and diazo compounds, halogenated compounds, and optically reducible colorants. These photosensitizers may be used in the form of a mixture of two or more thereof.
  • anthracene compounds are preferred because of an excellent photosensitizing effect thereof.
  • Specific examples thereof include products ANTHRACURE UVS-1331, and ANTHRACURE UVS-1221 (manufactured by Kawasaki Kasei Chemicals Co., Ltd.).
  • the content of the photosensitizer(s) is preferably from 0.1 to 5% by weight, more preferably from 0.5 to 3% by weight.
  • the curable resin composition used in the present invention preferably contains the following components:
  • the active-energy-ray-curable resin composition used in the present invention may contain, besides the curable component related to the above-mentioned radical polymerizable compound, an acrylic oligomer obtained by polymerizing a (meth)acrylic monomer.
  • an acrylic oligomer obtained by polymerizing a (meth)acrylic monomer.
  • the content of the acrylic oligomer in the curable resin composition is preferably 20% or less, more preferably 15% or less by weight of the whole of the composition. If the content of the acrylic oligomer in the curable resin composition is too large, the composition is intensely lowered in reaction rate when irradiated with an active energy ray. Thus, the composition may be poorly cured. In the meantime, the acrylic oligomer is contained in the curable resin composition in a proportion that is preferably 3% or more, more preferably 5% or more by weight of the whole of the curable resin composition.
  • the active-energy-ray-curable resin composition is preferably low in viscosity in a case where a consideration is made about the workability or evenness of the composition when the composition is applied.
  • the acrylic oligomer which is obtained by polymerizing a (meth)acrylic monomer, is also low in viscosity.
  • the weight-average molecular weight (Mw) thereof is preferably 15000 or less, more preferably 10000 or less, in particular preferably 5000 or less.
  • the weight-average molecular weight (Mw) of the acrylic oligomer is preferably 500 or more, more preferably 1000 or more, in particular preferably 1500 or more.
  • the (meth)acrylic monomer from which the acrylic oligomer is made, include methyl (meth) acrylate, ethyl (meth) acrylate, n-propyl (meth) acrylate, isopropyl (meth)acrylate, 2-methyl-2-nitropropyl (meth)acrylate, n-butyl (meth)acrylate, isobutyl (meth) acrylate, S-butyl (meth) acrylate, t-butyl (meth)acrylate, n-pentyl (meth)acrylate, t-pentyl (meth)acrylate, 3-pentyl (meth)acrylate, 2,2-dimethylbutyl (meth)acrylate, n-hexyl (meth)acrylate, cetyl (meth)acrylate, n-octyl (meth)acrylate, 2-ethylhexyl (meth)acrylate, 4-methyl-2-
  • acrylic oligomer examples include products “ARUFON” manufactured by Toagosei Co., Ltd., “ACTFLOW” manufactured by Soken Chemical & Engineering Co., Ltd., and “JONCRYL” manufactured by BASF Japan Ltd.
  • the active-energy-ray-curable resin composition may contain an optical acid generator.
  • the adhesive layer can be dramatically made better in water resistance and endurance when the composition does not contain any optical acid generator.
  • the optical acid generator can be represented by the following general formula (5):
  • L + represents any onium cation addition
  • X ⁇ represents a counter ion selected from the group consisting of PF 6 ⁇ , SbF 6 ⁇ , AsF 6 ⁇ , SbCl 6 ⁇ , BiCl 5 ⁇ , SnCl 6 ⁇ , ClO 4 ⁇ , a dithiocarbamate anion, and SCN ⁇ .
  • the counter anion X ⁇ in the general formula (5) is not particularly limited in principle, and is preferably a non-nucleophilic anion.
  • the counter anion X ⁇ is the non-nucleophilic anion, a nucleophilic reaction is not easily caused with a cation existing therewith in the molecule or various materials used together.
  • the optical acid generator itself which is represented by the general formula (4), and a composition using this agent can be improved in stability over time.
  • the non-nucleophilic anion referred to herein denotes an anion low in power for causing nucleophilic reaction.
  • anion examples include PF 6 ⁇ , SbF 6 ⁇ , AsF 6 ⁇ , SbCl 6 ⁇ , BiCl 5 ⁇ , SnCl 6 ⁇ , ClO 4 ⁇ , a dithiocarbamate anion, and SCN ⁇ .
  • optical acid generator in the present invention examples include products “CYRACURE DVI-6992”, and “CYRACURE UVI-6974” (manufactured by Dow Chemical Japan Ltd.), “ADEKA OPTOMER SP150”, “ADEKA OPTOMER SP152”, “ADEKA OPTOMER SP170”, and “ADEKA OPTOMER SP172” (manufactured by ADEKA corp.), “IRGACURE 250” (manufactured by Ciba Specialty Chemicals Corp.), “CI-5102”, and “CI-2855” (manufactured by Nippon Soda Co., Ltd.), “SAN-AID SI-60L”, “SAN-AID SI-80L”, “SAN-AID SI-100L”, “SAN-AID SI-110L”, and “SAN-AID SI-180L” (manufactured by Sanshin Chemical Industry Co., Ltd.), “CPI-100P”, and “CPI-100A” (manufactured by San-Apro Ltd.), “W
  • the content of the optical acid generator is 10% or less, preferably from 0.01 to 10%, more preferably from 0.05 to 5%, in particular preferably from 0.1 to 3% by weight of the whole of the curable resin composition.
  • the optical acid generator may be used together with a compound containing any one of an alkoxy group and an epoxy group in the active-energy-ray-curable resin composition.
  • a compound having in the molecule thereof one or more epoxy groups, or a polymer having in the molecule thereof two or more epoxy groups epoxy resin
  • a compound having in the molecule thereof two or more functional groups reactive with any epoxy group may be used together.
  • the functional group(s) reactive with any epoxy group include carboxyl, phenolic hydroxyl, mercapto, and primary or secondary aromatic amino groups.
  • the compound in particular preferably has in a single molecule thereof two or more of these functional groups, considering the three-dimensional curability thereof.
  • the polymer having in the molecule thereof one or more epoxy groups is, for example, an epoxy resin.
  • an epoxy resin examples thereof include bisphenol A type epoxy resin derived from bisphenol A and epichlorohydrin, bisphenol F type epoxy resin derived from bisphenol F and epichlorohydrin, bisphenol S type epoxy resin, phenol novolak type epoxy resin, cresol novolak type epoxy resin, bisphenol A novolak type epoxy resin, bisphenol F novolak type epoxy resin, alicyclic epoxy resin, diphenyl ether type epoxy resin, hydroquinone type epoxy resin, naphthalene type epoxy resin, biphenyl type epoxy resin, fluorene type epoxy resin, polyfunctional epoxy resins such as trifunctional epoxy resin and tetrafunctional epoxy resin, glycidylester type epoxy resin, glycidylamine type epoxy resin, hydantoin type epoxy resin, isocyanurate type epoxy resin, and aliphatic linear epoxy resin.
  • epoxy resins may be halogenated, and may be hydrogenated.
  • examples of a commercially available product of the epoxy resin include JER COATs 828, 1001, 801N, 806, 807, 152, 604, 630 and 871, YX8000, YX8034, and YX4000 manufactured by Japan Epoxy Resins Co., Ltd.; EPICLON 830, EXA 835LV, HP 4032D, HP 820 manufactured by DIC Corp.; EP 4100 series, EP 4000 series, and EPU series manufactured by ADEKA Corp.; CELLOXIDE series (2021, 2021P, 2083, 2085, and 3000), EPOLEAD series, and EHPE series manufactured by Daicel Corp.; YD series, YDF series, YDCN series, YDB series, and phenoxy resins (YP series and others: polyhydroxypolyethers each synthesized from a bisphenol and epichlorohydrin and having at both ends thereof epoxy groups, respectively) manufactured by N
  • the compound having in the molecule thereof an alkoxy group is not particularly limited as far as the compound is a compound having in the molecule thereof one or more alkoxy groups.
  • the compound may be any known compound. Typical examples of the compound include a melamine compound, an amino resin, and a silane coupling agent.
  • the blend amount of the compound containing any one of an alkoxy group and an epoxy group is usually 30% or less by weight of the whole of the curable resin composition. If the content of the compound in the composition is too large, the curable resin composition is lowered in adhesion, so that the impact resistance thereof may be deteriorated in a dropping test.
  • the content by proportion of the compound in the composition is more preferably 20% or less by weight.
  • the composition contains the compound in a proportion that is preferably 2% or more, more preferably 5% or more by weight from the viewpoint of the water resistance of the composition.
  • the silane coupling agent is preferably an active energy ray curable compound.
  • this agent can give substantially the same water resistance to the composition.
  • silane coupling agent examples include the organic silicon compounds given as the above-mentioned examples.
  • the blend amount of the silane coupling agent is preferably from 0.01 to 20%, preferably from 0.05 to 15%, even more preferably from 0.1 to 10% by weight of the whole of the curable resin composition. If the blend amount is more than 20% by weight, the curable resin composition is deteriorated in storage stability. If the blend amount is less than 0.1% by weight, the composition does not sufficiently exhibit an adhesion water-resistance effect.
  • the curable resin composition used in the present invention may contain a compound having a vinyl ether group.
  • a compound having a vinyl ether group This case is favorable since a polarizer and the resultant adhesive layer are improved in adhesion water-resistance therebetween.
  • Reasons why this advantageous effect is gained are unclear; however, it is presumed that one of the reasons is as follows: the vinyl ether group, which the compound has, interacts with the polarizer to heighten the adhering strength between the polarizer and the adhesive layer.
  • the compound is preferably a radical polymerizable compound having a vinyl ether group.
  • the content of the compound is preferably from 0.1 to 19% by weight of the whole of the curable resin composition.
  • a compound in which keto-enol tautomerism is generable may be incorporated into the curable resin composition used in the present invention. It is preferred to use, for example, an embodiment in which this keto-enol tautomerism generable compound is contained in the curable resin composition that contains a crosslinking agent or that is usable in the state of blending a crosslinking agent into the composition. This embodiment allows to restrain the curable resin composition after the blending of the organometallic compound into the composition from being excessively raised in viscosity or gelatinized, and from undergoing the production of a micro-gelatinized product to realize an effect of prolonging the pot life of this composition.
  • the keto-enol tautomerism generable compound may be a ⁇ -dicarbonyl compound that may be of various types. Specific examples thereof include acetylacetone, 2,4-hexanedione, 3,5-heptanedione, 2-methylhexane-3,5-dione, 6-methylheptane-2,4-dione, 2,6-dimethylheptane-3,5-dione, and other ⁇ -diketones; methyl acetoacetate, ethyl acetoacetate, isopropyl acetoacetate, tert-butyl acetoacetate, and other acetoacetates; ethyl propionylacetate, ethyl propionylacetate, isopropyl propionylacetate, tert-butyl propionylacetate, and other propionylacetates; ethyl isobutyrylacetate, ethyl isobutyrylacetate
  • the use amount of the keto-enol tautomerism generable compound(s) may be, for example, from 0.05 to 10 parts, preferably from 0.2 to 3 parts (for example, from 0.3 to 2 parts) by weight per part by weight of the organometallic compound. If the use amount of the compound is less than 0.05 parts by weight per part by weight of the organometallic compound, the use effects thereof may not be sufficiently exhibited with ease. In the meantime, if the use amount of the compound is more than 10 parts by weight per part by weight of the organometallic compound, the compound interacts excessively with the organometallic compound so that a target water resistance may not be easily expressed.
  • additives may be blended, as other optional components, into the curable resin composition used in the present invention as far as the object and advantageous effects of the invention are not damaged.
  • the additives include epoxy resin, polyamide, polyamideimide, polyurethane, polybutadiene, polychloroprene, polyether, polyester, styrene-butadiene block copolymer, petroleum resin, xylene resin, ketone resin, cellulose resin, fluorine-contained oligomer, silicone-based oligomer, polysulfide-based oligomer, and other polymers or oligomers; phenothiazine, 2,6-di-t-butyl-4-methylphenol, and other polymerization inhibitors; polymerization initiation aids; leveling agents; wettability improvers; surfactants; plasticizers; ultraviolet absorbers; inorganic fillers; pigments; and dyes.
  • the amount of the additives is usually from 0 to 10%, preferably from 0 to 5%, most preferably from 0 to 3% by weight of the whole of the curable resin composition.
  • the viscosity of the curable resin composition used in the present invention is preferably 100 cp or less at 25° C. from the viewpoint of the applicability thereof.
  • the temperature of the curable resin composition may be controlled when the composition is applied, so as to adjust the viscosity thereof to 100 cp or less.
  • the thus obtained composition is usable.
  • the viscosity ranges more preferably from 1 to 80 cp, most preferably from 10 to 50 cp.
  • the viscosity is measurable, using an E-type viscometer TVE22LT manufactured by Toki Sangyo Co., Ltd.
  • the curable resin composition used in the present invention it is preferred to use, as the curable component(s), a material low in skin irritation from the viewpoint of safety.
  • the skin irritation can be judged, using an index of P.I.I.
  • the P.I.I is widely used as an index showing the degree of skin disorder, and is measured by a Draize method. The measured value thereof is represented in a range from 0 to 8. As this value is smaller, the irritation is judged to be lower. However, the measured value includes a large accidental error; thus, it is advisable to understand this index as a reference value.
  • the P.I.I is preferably 4 or less, more preferably 3 or less, most preferably 2 or less.
  • the laminated resin film according to the present invention includes a first resin film, and a second resin film laminated on/over at least one surface of the first resin film to interpose an adhesive layer between the surface and the second resin film.
  • This laminated resin film includes the following producing method: a method including an adhesion improvement-treating step of attaching a compound represented, by the general, formula (1) to the adhesion surface of at least one of the first resin film and second, resin, film; an applying step of applying a curable resin composition to the adhesion surface of at least one of the first resin film and the second resin film; a bonding step of causing the first resin film and the second resin film to each other; and an adhering step of radiating an active energy ray to the resultant laminate from a first resin film side of the laminate, or a second resin film side of the laminate to cure the curable resin composition to yield the adhesive layer, and adhering the first resin film and the second resin film to adhere to each other through the yielded adhesive layer.
  • a polarizing film given as an example of the laminated resin film according to the present invention is a polarizing film including a polarizer, and an adhesive layer that is positioned on/over at least one surface of the polarizer and yielded by curing a curable resin composition; and is a polarizing film in which a transparent protective film is laminated to the surface of the polarizer to interpose the adhesive layer between the surface and the transparent-protective film.
  • This polarizing film can be produced by the following producing method:
  • a method for producing a polarizing film including a polarizer, and a transparent protective film laminated on/over at least one surface of the polarizer to interpose an adhesive layer between the surface and the transparent protective film,
  • the method including an adhesion improvement-treating step of causing a compound represented by the general formula (1) to adhere to the adhesion surface of at least one of the polarizer and the transparent protective film; an applying step of applying a curable resin composition to the adhesion surface of at least one of the polarizer and the transparent protective film; a bonding step of causing the polarizer and the transparent protective film to each other; and an adhering step of radiating an active energy ray to the resultant laminate from a polarizer side of the laminate, or a transparent protective film side of the laminate to cure the curable resin composition to yield the adhesive layer, and adhering the polarizer and the transparent, protective film to adhere to each other through the yielded adhesive layer.
  • an adhesion improvement-treating step of causing a compound represented by the general formula (1) to adhere to the adhesion surface of at least one of the polarizer and the transparent protective film
  • an applying step of applying a curable resin composition to the adhesion surface of at least one of the polarizer and
  • the adhesion improvement-treating step of using an adhesion-improving composition including a compound represented by the general formula (1) to form an adhesion-improving layer onto the adhesion surface of at least one of the polarizer and the transparent protective film is, for example, a method of producing the adhesion-improving composition, which is an adhesion-improving composition (A) including the compound represented by the general formula (1), and forming this composition into a film onto the adhesion surface of at least one of the polarizer and the transparent protective film by, for example, applying.
  • a solvent and additives that may be included in the adhesion-improving composition (A) and are other than the compound represented by the general formula (1) are as described above.
  • the adhesion-improving composition (A) includes a solvent
  • the resultant is optionally subjected to a drying step or a curing treatment (for example, thermal treatment.).
  • the method for using the adhesion-improving composition (A) to form the adhesion-improving layer on the polarizer the following is appropriately usable: a method of immersing the polarizer directly onto a treatment bath for the composition (A), or a known applying method.
  • the applying method include roll coating, gravure coating, bar coating, reverse coating, roll brushing, spray coating, air knife coating, and curtain coating methods.
  • the method is not limited to these methods.
  • the adhesion-improving layer may be lowered in cohesive strength so that an adhesion-improving effect thereof may be lowered.
  • the thickness of the adhesion-improving layer is 300 nm or less, preferably 200 nm or less. From the viewpoint of the producibility of polarizing films, the thickness is more preferably 100 nm or less.
  • the lower limit of the thickness for causing the adhesion-improving layer to exhibit an advantageous effect sufficiently is at least the thickness of a monomolecular membrane of the compound represented by the general formula (1), and is usually 0.1 nm or more, preferably 1 nm or more, more preferably 2 nm or more.
  • adhesion-improving layer by causing the compound represented by the general formula (1) to adhere to the adhesion surfaces of both of the first resin film and the second resin film, particularly, to both surfaces of the polarizer and the transparent protective film by, for example, applying since the resultant laminated resin film, particularly, polarizing film is improved in adhesion.
  • the method for applying the curable resin composition is appropriately selected in accordance with the viscosity of the curable resin composition, or a target thickness of the resultant layer.
  • examples thereof include a reverse coater, a (direct, reverse or offset) gravure coater, a bar reverse coater, a roll coater, a die coater, a bar coater, and a rod coater.
  • the viscosity of the curable resin composition used in the present invention is preferably from 3 to 100 mPa ⁇ s, more preferably from 5 to 50 mPa ⁇ s, most preferably from 10 to 30 mPa ⁇ s.
  • the surface of the applied composition is poor in smoothness so that a poor external appearance may be unfavorably generated.
  • the curable resin composition used in the present invention can be applied in the state of heating or cooling the composition to be adjusted into a preferred viscosity range.
  • the laminated resin film according to the present invention is a polarizing film
  • a polarizer which is a constituent matter of the film, from the viewpoint of an improvement of the polarizer in adhesion to an adhesive layer, that the content by percentage in the polarizer is as low as possible before the adhesive layer is applied onto the polarizer.
  • the adhesive layer is particularly made of an acrylic adhesive
  • the water content by percentage in the polarizer is set preferably to 15% or less by weight, more preferably to 13% or less by weight, in particular preferably to 10% or less by weight, from the viewpoint of a further improvement in the adhesion, before the compound represented by the general formula (1), in particular, the composition (A) including this compound is applied onto the polarizer.
  • the polarizer and the transparent protective film may be subjected to a surface-modifying treatment before the adhesion-improving layer is formed.
  • a surface-modifying treatment before the formation or bonding of the adhesion-improving layer.
  • the surface-modifying treatment include corona treatment, plasma treatment, and Itro treatment. Particularly preferred is corona treatment.
  • reactive functional groups such as carbonyl group or amino group, are generated on the surface of the polarizer to improve close adhesion of the polarizer to the adhesive layer.
  • the treatment allows to remove foreign substances on the surface, or relieve irregularities in the surface by ashing effect, so that a polarizing film excellent in external appearance properties can be produced.
  • the polarizer and the transparent protective film are bonded to each other.
  • the bonding between the polarizer and the transparent protective film may be attained, using, for example, a roll laminator.
  • an active energy ray is radiated to the workpiece from the polarizer surface side thereof or the transparent protective film surface side thereof to cure the curable resin composition.
  • the polarizer and the transparent protective film are caused to adhere to each other.
  • the thickness of the adhesive layer made from the curable resin composition is preferably from 0.01 to 3.0 ⁇ m. If the thickness of the adhesive layer is too small, the adhesive layer is short in cohesive strength to be unfavorably lowered in peel strength. If the thickness of the adhesive layer is too large, the polarizing film is easily caused therein when stress is applied to a cross section of the polarizing film, so that so that a peel defect is unfavorably generated therein by impact.
  • the thickness of the adhesive layer is more preferably from 0.1 to 2.5 ⁇ m, most preferably from 0.5 to 1.5 ⁇ m.
  • the curable resin composition used in the present invention is preferably used as an active-energy-ray-curable resin composition.
  • the active-energy-ray-curable resin composition is usable in an electron beam curable, ultraviolet curable or visible ray curable form.
  • the form of the curable resin composition is preferably a visible-ray-curable resin composition from the viewpoint of the producibility of polarizing films.
  • an active energy ray such as an electron beam, an ultraviolet ray or a visible ray
  • a direction along which the active energy ray (which is, for example, an electron beam, an ultraviolet ray or a visible ray) is radiated may foe any appropriate radiating direction.
  • the active energy ray is radiated from the transparent protective film side of the workpiece. If the active energy ray is radiated from the polarizer side thereof, the polarizer may be unfavorably deteriorated by the active energy ray (which is, for example, an electron beam, an ultraviolet ray or a visible ray).
  • conditions for radiating an electron beam may be arbitrarily-selected appropriate conditions as far as the conditions are conditions under which the active-energy-ray-curable resin composition is curable.
  • the accelerating voltage is preferably from 5 to 300 kV, more preferably from 10 to 250 kV. If the accelerating voltage is less than 5 kV, the electron beam may not reach the adhesive so that the adhesive may not be unfavorably cured sufficiently. If the accelerating voltage is more than 300 kV, the penetrating power of the beam into a sample is too strong, so that the beam may unfavorably damage its transparent protective film or polarizer.
  • the radiation ray quantity thereof is from 5 to 100 kGy, more preferably from 10 to 75 kGy. If the radiation ray quantity is less than 5 kGy, the adhesive is insufficiently cured. If the quantity is more than 100 kGy, the transparent protective film or the polarizer is damaged, so that the polarizing film is lowered in mechanical strength or yellowed not to gain predetermined optical properties.
  • the electron beam radiation is usually performed in an inert gas. If necessary, the radiation maybe performed in the atmospheric air or under conditions that a small amount of oxygen is introduced into an inert gas.
  • An appropriate introduction of oxygen dares to cause oxygen blocking in a surface of the transparent protective film onto which the electron beam is to be initially radiated, so that the beam can be prevented from damaging the transparent protective film to radiate the electron beam effectively only to the adhesive although this matter depends on the material of the transparent protective film.
  • active energy rays rays including visible rays having wavelengths ranging from 380 to 450 nm, particularly, active energy rays in which the radiation quantity of visible rays having wavelengths ranging from 380 to 450 nm is the largest.
  • the transparent protective film When a transparent protective film to which ultraviolet ray absorbing power is given (ultraviolet non-transmissible type transparent, protective film) is used about ultraviolet curability or visible ray curability, the transparent protective film absorbs light rays having wavelengths shorter than about 380 nm; thus, the light rays having wavelengths shorter than 380 nm do not reach the active-energy-ray-curable resin composition not to contribute to a polymerization reaction of the composition. Furthermore, the light rays having wavelengths shorter than 380 nm, which are absorbed by the transparent protective film, are converted to heat, so that the transparent protective film itself generates heat. The heat causes defects of the polarizing film, such as a curling or wrinkles of the film.
  • ultraviolet curability or visible ray curability it is preferred to use, as an active energy ray generating device, a device which does not emit light rays shorter than 380 nm. More specifically, a device in which the ratio of the integrated illuminance of light rays having a wavelength range from 380 to 440 mm to that of light rays having a wavelength range from 250 to 370 nm is preferably from 100/0 to 100/50, more preferably from 100/0 to 100/40.
  • a gallium sealed metal halide lamp or an LED light source emitting light rays having a wavelength range from 380 to 440 nm.
  • a light source including ultraviolet rays and visible rays is usable, examples of which include a low pressure mercury lamp, a middle pressure mercury lamp, a high pressure mercury lamp, a super high pressure mercury lamp, an incandescent lamp, a xenon lamp, a halogen lamp, a carbon arc light, a metal halide lamp, a fluorescent lamp, a tungsten lamp, a gallium lamp, an excimer laser, and sunlight. It is allowable to use light rays about which a bandpass filter is used to block ultraviolet rays having wavelengths shorter than 380 nm.
  • an active energy ray obtained by using a gallium sealed metal halide lamp and further passing light therefrom through a bandpass filter which can block light rays having wavelengths shorter than 380 nm, or use an active energy ray having a wavelength of 405 nm, which is obtained by using an LED light source.
  • the composition is heated preferably to 40° C. or higher, more preferably to 50° C. or higher. It is also preferred to heat the active-energy-ray-curable resin composition after the radiation of ultraviolet rays or visible rays (heating after radiation) thereto. In this case, the composition is heated preferably to 40° C. or higher, more preferably to 50° C. or higher.
  • the active-energy-ray-curable resin composition used in the present invention is favorably usable, particularly, when an adhesive layer is formed for causing a polarizer to adhere to a transparent protective film about which the transmittance of light rays having a wavelength of 365 nm is less than 5%.
  • the active-energy-ray-curable resin composition according to the invention may include a photopolymerization initiator of the general formula (3); in this case, by radiating ultraviolet rays to the composition across the transparent protective film having UV absorbing power, the composition can be cured to form the adhesive layer.
  • a photopolymerization initiator of the general formula (3) in this case, by radiating ultraviolet rays to the composition across the transparent protective film having UV absorbing power, the composition can be cured to form the adhesive layer.
  • transparent protective film having UV absorbing power means a transparent protective film about which the transmittance of a light ray having a wavelength of 380 nm is less than 10%.
  • the method for giving UV absorbing power to a transparent protective film may be a method of incorporating an ultraviolet absorbent into the transparent protective film, or a method of laminating a surface treatment layer containing an ultraviolet absorbent onto a surface of the transparent protective film.
  • ultraviolet absorbent examples include oxybenzophenone-based compounds, benzotriazole-based compounds, salicylate-based compounds, benzophenone-based compounds, cyanoacrylate-based compounds, nickel complex salt type compounds, and triazine-based compounds, which are known in the prior art.
  • the active-energy-ray-curable resin composition is irradiated with an active energy ray (such as an electron beam, a ultraviolet ray or a visible ray) to be cured to form an adhesive layer.
  • an active energy ray such as an electron beam, a ultraviolet ray or a visible ray
  • a direction along which, the active energy ray (which is, for example, an electron beam, an ultraviolet ray or a visible ray) is radiated may be any appropriate radiating direction.
  • the active energy ray is radiated from the transparent protective film side of the resultant workpiece. If the active energy ray is radiated from the polarizer side thereof, the polarizer may be unfavorably deteriorated by the active energy ray (which is, for example, an electron beam, an ultraviolet ray or a visible ray).
  • the line speed which depends on the curing period of the curable resin composition, is preferably from 1 to 500 m/min., more preferably from 5 to 300 m/min., even more preferably from 10 to 100 m/min. If the line speed is too small, the producing system is small in producing performance, or the transparent protective, film is excessively damaged, so that no polarizing film that can endure an endurance test or the like can be produced. If the line speed is too large, the adhesive resin composition is insufficiently cured so that the composition may not gain a target adhesion.
  • a polarizer and a transparent protective film are caused to adhere onto each other to interpose, therebetween, a second adhesive layer constituted by a cured product layer of the above-mentioned active-energy-ray-curable resin composition.
  • a second adhesion-improving layer may be disposed between the transparent protective film and the adhesive layer.
  • the second adhesion-improving layer can be formed, using a resin that may be of various types. This resin has, for example, a polyester, polyether, polycarbonate, polyurethane, silicone type, polyamide, polyimide or polyvinyl alcohol skeleton. These polymeric resins may be used singly or in any combination of two or more thereof.
  • a different additive may be added thereto.
  • the following may be further used: a tackifier, a ultraviolet absorbent, an antioxidant, a heat-resistant stabilizer, and other stabilizers.
  • the second adhesion-improving layer is beforehand laid on the transparent protective film, and then the second adhesion-improving layer side of the transparent protective film, and the polarizer are caused to adhere to each other through the adhesive layer.
  • the formation of the second adhesion-improving layer is attained by using a known technique to apply a forming-material for the second adhesion-improving layer onto the transparent protective film, and drying the resultant.
  • the forming-material for the second adhesion-improving layer is usually prepared in the form of a solution in which the material is diluted into an appropriate concentration, considering the thickness of the dried forming-material, the smoothness of the applying, and others.
  • the thickness of the dried second adhesion-improving layer is from 0.01 to 5 ⁇ m, more preferably from 0.02 to 2 ⁇ m, even more preferably from 0.05 to 1 ⁇ m.
  • Plural second adhesion-improving layers may be laid. In this case also, the total thickness of the second adhesion-improving layers is preferably set into any one of these ranges.
  • the polarizer is not particularly limited, and may be of various types.
  • the polarizer is, for example, a polarizer yielded by causing a dichroic material such as iodine or dichroic dye to be adsorbed into a hydrophilic polymeric film, such as a polyvinyl alcohol-based film, a partially-formal-converted polyvinyl alcohol-based film or an ethylene/vinyl acetate copolymer-based partially-saponified film, and then stretching the resultant uniaxially; or a polyene aligned film made of, for example, a polyvinyl alcohol dehydrated product or a polyvinyl chloride de-hydrochloride-treated product.
  • a dichroic material such as iodine or dichroic dye
  • a polarizer composed of a polyvinyl alcohol-based film and a dichroic substance such as iodine.
  • the thickness of such a polarizer is preferably from 2 to 30 ⁇ m, more preferably for 4 to 20 ⁇ m, most preferably from 5 to 15 ⁇ m. If the thickness of the polarizer is small, the polarizer is unfavorably lowered in optical endurance. If the thickness of the polarizer is large, the polarizer becomes large in dimension change at a high temperature and high humidity, so that inconveniences such as display unevenness are unfavorably generated.
  • the polarizer in which a polyvinyl alcohol-based film that has been dyed with iodine has uniaxially stretched can be produced, for example, by immersing a polyvinyl alcohol into an aqueous solution of iodine to be dyed, and then stretching the resultant film into a length 3 to 7 times the original length of this film.
  • the stretched film may be immersed into an aqueous solution of, for example, boric acid or potassium iodide.
  • the polyvinyl alcohol-based film may be immersed into water as required to be cleaned with water.
  • the cleaning of the polyvinyl alcohol-based film with water allows to clean stains and a blocking-preventing agent on surfaces of the polyvinyl alcohol-based film, and further produce an advantageous effect of swelling the polyvinyl alcohol-based film to prevent unevenness of the dyeing, and any other unevenness.
  • the stretching may be performed after the dyeing with iodine or while the dyeing is performed. Alternatively, after the stretching, the dyeing with iodine may be performed. The stretching may be performed in an aqueous solution of, for example, boric acid or potassium iodide, or in a water bath.
  • the active-energy-ray-curable resin composition used in the present invention can remarkably produce the advantageous effect thereof (that the resultant layer satisfies optical endurance in a severe environment at a high temperature and high humidity).
  • the polarizer the thickness of which is 10 ⁇ m or less, is more largely affected by water than any polarizer having a thickness more than 10 ⁇ m. Consequently, the former is insufficient in optical endurance in an environment at a high temperature and high humidity to be easily raised in transmittance or lowered in polarization degree.
  • the thickness of the polarizer is preferably from 1 to 7 ⁇ m from the viewpoint of making the polarizing film thinner.
  • Such a thin polarizer is small in thickness unevenness, excellent in perceptibility, and small in dimension change. Furthermore, favorably, this thin polarizer also makes the polarizing film small in thickness.
  • Typical examples of the thin polarizer include thin polarizing membranes described in JP-A-51-069644, JP-A-2000-338329, WO 2010/100917 pamphlet, and specifications of PCX/JP2010/001460 and Japanese Patent Applications No. 2010-269002 and No. 2010-263692.
  • These thin polarizing membranes can each be yielded by a producing method including the step of stretching a polyvinyl alcohol-based resin (hereinafter referred to also as a PVA-based resin) and a resin substrate for stretching in a laminate state, and the step of dyeing the laminate.
  • This producing method allows to draw the laminate, even when the PVA-based resin layer is thin, without causing inconveniences, such as breaking by the stretching, on the basis of the supporting of the PVA-based resin layer on the resin substrate for stretching.
  • the thin polarizing membranes are preferably polarizing membranes each yielded by the following producing method, out of producing methods including the step of stretching a PVA-based resin and a resin substrate in a laminate state, and the step of dyeing the laminate, since the laminate can be stretched into a high draw ratio to improve the resultant in polarizing performance: a producing method including the step of stretching the laminate in an aqueous solution of boric acid, as is described in a pamphlet of WO 2010/100917, or a specification of PCT/JP2010/001460 or Japanese Patent Application No. 2010-263002 or 2010-263632.
  • the thin polarizing membranes are in particular preferably thin polarizing membranes each yielded by a producing method including the step of stretching the laminate supplementally in the air before the stretching in the aqueous solution of boric acid, as is described in a specification of Japanese Patent Application No. 2010-269002 or 2010-263692.
  • the polarizer generally has reactive functional groups such as hydroxyl, carbonyl and amino groups. Accordingly, about an adhesion improvement-treated polarizer in which a polarizer having, on surfaces thereof, at least reactive functional groups has, on at least one of the surfaces, a compound represented by the general formula (1), particularly, about an adhesion-improving layer attached polarizer in which an adhesion-improving layer including a compound represented by the general formula (1) is formed, close adhesion between its adhesive layer and the polarizer is improved, so that the polarizing film is favorably improved, particularly, in adhesion therein.
  • a transparent film corresponding to the second resin film is, for example, a transparent protective film or a retardation film.
  • the transparent protective film is preferably a film excellent in transparency, mechanical strength, thermal stability, water blocking performance, isotropy and others.
  • a material therefor include polyester-based polymers, such as polyethylene terephthalate and polyethylene naphthalate, cellulose-based polymers such as diacetylcellulose and triacetylcellulose, acrylic polymers such as polymethyl methacrylate, styrene-based polymers such as polystyrene and acrylonitrile/styrene copolymer (AS resin), and polycarbonate-based polymers.
  • polystyrene resin examples include polyethylene, polypropylene, polyolefins each having a cyclic or norbornene structure, polyolefin-based polymers such as ethylene/propylene copolymer, vinyl chloride polymers, amide-based polymers such as nylon and aromatic polyamide, imide polymers, sulfone-based polymers, polyethersulfone-based polymers, polyetheretherketone-based polymers, polyphenylene sulfide-based polymers, vinyl alcohol-based polymers, vinylidene chloride-based polymers, vinyl butyral-based polymers, arylate-based polymers, polyoxymethylene-based polymers, and epoxy-based polymers; and any blend composed of two or more of these polymers.
  • the transparent protective film may contain one or more appropriate additives selected at will.
  • the additive(s) include an ultraviolet absorbent, an antioxidant, a lubricant, a plasticizer, a release agent, a coloring preventive, a flame retardant, a nucleating agent, an antistatic agent, a pigment and a colorant.
  • the content of one or more of the above-mentioned thermoplastic resins in the transparent protective film is preferably from 50 to 100%, more preferably from 50 to 99%, even more preferably from 60 to 98%, in particular preferably from 70 to 97% by weight. If the content of the thermoplastic resin(s) in the transparent protective film is 50% or less by weight, it is feared that the transparent-protective film cannot sufficiently express, high transparency and other properties which the thermoplastic resin(s) originally has/have.
  • the transparent protective film may be a polymer film described in JP-A-2001-343529 (WO 01/37007), for example, a resin composition including a thermoplastic resin (A) having at a side chain thereof a substituted inside group and/or an unsubstituted imide group and a thermoplastic resin having at a side chain thereof a substituted phenyl and/or an unsubstituted phenyl, and a nitrile group.
  • a specific example thereof is a film of a resin composition including an alternating copolymer made from isobutylene and N-methylmaleimide, and acrylonitrile/styrene copolymer.
  • the film may be a film made of, for example, a blend extruded product of the resin composition.
  • a film is small in retardation, and small in photoelastic coefficient; thus, this film can solve inconveniences, such as an unevenness of the polarizing film that is based on strains in the film.
  • the film is small in water-vapor permeability to be excellent in humidity endurance.
  • the transparent protective film preferably has a water-vapor permeability of 156 g/m 2 /24-hours or less.
  • This structure makes water in the air difficult to enter the inside of the polarizing, film, so that the water content, by percentage in the polarizing film itself can be restrained from being changed. As a result, the polarizing film can be restrained from being curled or changed in dimension by a storage environment of the film.
  • the transparent protective film laid over one surface or each of both surfaces of the polarizer is preferably a film excellent, in transparency, mechanical strength, thermal stability, water blocking performance, isotropy and others; and is more preferably a material the water-vapor permeability of which is particularly 150 g/m 2 /24-hours or less, in particular preferably 120 g/m 2 /24-hours or less, more preferably from 5 to 70 g/m 2 /24-hours.
  • the water-vapor permeability is gained by a method described in the item EXAMPLES.
  • polyester resins such as polyethylene terephthalate and polyethylene naphthalate
  • polycarbonate resins such as polycarbonate resins; arylate-based resins; amide-based resins such as nylon and aromatic polyamide
  • polyolefin-based polymers such as polyethylene, polypropylene and ethylene/propylene copolymer, cyclic, olefin-based, resins, having a cyclic or norbornene structure, and (meth)acrylic resins; and mixtures each made of two or more of these resins.
  • preferred are polycarbonate resins, cyclic polyolefin-based resins and (meth)acrylic resins, and particularly preferred are cyclic polyolefin-based resins and (meth)acrylic resins.
  • the thickness of the transparent protective film may be appropriately decided, and is generally from about 5 to 100 ⁇ m, in particular preferably from 10 to 60 ⁇ m, more preferably from 13 to 40 ⁇ m from the viewpoint of the strength, the handleability and other workabilities of the film, thin-layer properties of the film, and other factors.
  • the transparent protective film is subjected to a surface-modifying treatment, such as corona treatment, plasma treatment, or saponifying treatment, to have reactive functional group, such as hydroxyl, carbonyl and amino groups.
  • a surface-modifying treatment such as corona treatment, plasma treatment, or saponifying treatment
  • reactive functional group such as hydroxyl, carbonyl and amino groups.
  • the method for bonding the polarizer and the protective film to each other may be a method using a roll laminator.
  • the method for laminating protective films, respectively, onto both surfaces of the polarizer is selected from a method of bonding the polarizer to one of the protective films, and then bonding the other protective film to the resultant, and a method of bonding the two protective films simultaneously to the polarizer.
  • Air bubbles involved between the polarizer and the protective films, which are generated at the time of the bonding, can be remarkably decreased by adopting the former method, that is, the method of bonding the polarizer to one of the protective films, and then bonding the other protective film to the resultant.
  • the former method is favorable.
  • the retardation film may be, for example, a retardation film having a front-face retardation of 40 nm or more and/or a thickness-direction retardation of 80 nm or more.
  • the front-face retardation and the thickness-direction retardation are usually controlled Into the range of 40 to 200 nm, and that of 80 to 300 nm, respectively.
  • the retardation, film is, for example, a birefringence film yielded by stretching a polymeric material uniaxially or biaxially, an aligned film of a liquid crystal polymer, or a product in which an aligned layer of a liquid crystal polymer is support on a film.
  • the thickness of the retardation film is not particularly limited, and is generally from about 20 to 150 ⁇ m.
  • the retardation film may be a reverse wavelength dispersion type retardation film satisfying the following expressions (1) to (3):
  • Re[450] and Re[550] are, respectively, an in-plane retardation value of the retardation film that, is measured at a wavelength of 450 nm at 23° C., and an in-plane retardation value of the retardation film that is measured at a wavelength of 550 nm at 23° C.;
  • ⁇ n is an in-plane birefringence “nx ⁇ ny” of the retardation film when the retardation film has a refractive index nx in a slow axis direction of the film, and has a refractive index ny in a fast axis direction of the film;
  • NZ is a ratio between “nx ⁇ nz”, which is a birefringence of the film in the thickness direction, and “nx ⁇ ny”, which is an in-plane birefringence of the film.
  • the laminated resin film is preferably a polarizing film.
  • the polarizing film may be a laminated optical film in which, a different optical film is laminated onto the polarizing film.
  • the optical film is not particularly limited, and examples thereof include a retardation film (examples thereof including 1 ⁇ 2 and 1 ⁇ 4 wavelength plates), a viewing angle compensation films, a brightness enhancement film, a reflector or an anti-transmissible plate, and other optical films that are each a film that may be used to form, for example, a liquid crystal display device. These optical films may each be used as a substrate film for an adhesion-improving layer attached substrate film in the present invention.
  • the optical film is subjected to a surface-modifying treatment to have reactive functional groups such as hydroxyl, carbonyl, and amino groups.
  • a surface-modifying treatment to have reactive functional groups such as hydroxyl, carbonyl, and amino groups.
  • a pressure-sensitive adhesive layer may be laid for bonding this polarizing film or optical film onto a different member such as a liquid crystal cell.
  • a pressure-sensitive adhesive agent which forms the pressure-sensitive adhesive layer is not particularly limited. This agent may be appropriately selected from the following, and then used: pressure-sensitive adhesive agents each containing, as a base polymer thereof, an acrylic polymer, silicone-based polymer, polyester, polyurethane, polyamide, polyether, fluorine-containing polymer, rubbery polymer, or some other polymer.
  • the pressure-sensitive adhesive agent is in particular preferably an acrylic pressure-sensitive adhesive, or any other pressure-sensitive adhesive that is excellent in optical transparency, and shows adherabilities of appropriate wettability, cohesive property and adhesion to be excellent in weather resistance, heat resistance and others.
  • Pressure-sensitive adhesive layers may be laid, as superimposed layers different from each other in, for example, composition or species, onto a single surface or each surface of the polarizing film or the optical film.
  • these layers may be different from each other in, for example, composition, species or thickness on the front and rear side of the film.
  • the thickness of (each of) the pressure-sensitive adhesive layer(s) may be appropriately decided in accordance with, for example, the use purpose and adhering strength thereof.
  • the thickness is generally from 1 to 500 ⁇ m, preferably from 1 to 200 ⁇ m, in particular preferably from 1 to 100 ⁇ m.
  • a separator is temporarily bonded to a naked surface of the pressure-sensitive adhesive layer to cover the surface in order to attain the prevention of the pollution of the surface, and other purposes until this layer is put into practical use. This coverage allows to prevent a person or object from contacting the pressure-sensitive adhesive layer in an ordinarily handled state thereof.
  • the separator may be an appropriate separator according to conventional techniques except the above-mentioned thickness conditions, for example, a plastic film, a rubber sheet, a paper, cloth or nonwoven cloth piece, a net, a foamed sheet or a metal foil piece; a laminated body of such flat pieces; or a product in which such a flat piece is optionally subjected to coating treatment with an appropriate release agent, such as a silicone type, long-chain alkyl type or fluorine-containing type agent, or molybdenum sulfide.
  • an appropriate release agent such as a silicone type, long-chain alkyl type or fluorine-containing type agent, or molybdenum sulfide.
  • the polarizing film or laminated polarizing film of the present invention is preferably usable to form various devices such as a liquid crystal display device.
  • the formation of the liquid crystal display device may be attained in accordance with the prior art.
  • any liquid crystal display device is generally formed, for example, by: fabricating appropriately a liquid crystal cell and a polarizing film or laminated optical film, and further optional constituent parts such as an optional lighting system; and then integrating a driving circuit into the resultant.
  • the method for the formation is not particularly limited except, the use of the polarizing film or laminated optical film according to the invention.
  • the method is substantially according to the prior art.
  • the liquid crystal cell may be also of any type, such as a TN type, STN type or ⁇ type.
  • An appropriate liquid crystal display device may be formed, examples thereof including liquid crystal display device in which a polarizing film or laminated optical film is arranged onto one of both sides of a liquid crystal cell or each of both the sides, and a liquid crystal display device in which a backlight or reflector is used as a lighting system.
  • any polarizing film or laminated optical film according to the present invention can be set onto the one side of the liquid crystal cell, or each of both the sides thereof.
  • polarizing films or laminated optical films of the invention are set up, respectively, on both the sides, these may be the same as or different from each other.
  • one or more appropriate components may be further arranged, at one or more appropriate positions of the device, in the form of one or two or more layers of the component (s).
  • the component(s) include a diffusion plate, an anti-glare layer, an anti-reflection film, a protective plate, a prism array, a lens array sheet, a light diffusion plate, and a backlight.
  • a 45- ⁇ m-thickness film of a polyvinyl alcohol having an average polymerization degree of 2400 and a saponification degree of 99.5% by mole was immersed in hot water of 30° C. temperature for 60 seconds to be swollen.
  • the film was stretched in an aqueous solution of a boric acid that had a temperature of 65° C. to give a total stretch ratio of 6.
  • the film was dried in an oven of 40° C. temperature for 3 minutes. In this way, each polyvinyl alcohol-based polarizer (thickness: 18 ⁇ m) was yielded.
  • Each protective film A A biaxial kneader was used to mix 100 parts by weight of an imidated MS resin described in Production Example 1 in JF-A-2010-284840 with 0.62 parts by weight of a triazine-based ultraviolet absorbent (trade name: T 712, manufactured by Adeka Corp.) at 220° C. to produce resin pellets.
  • the resultant resin pellets were dried at 100.5 kPa and 100° C. for 12 hours, and a uniaxial extruder was then used to extrude the pellets through a T die at a dice temperature of 270° C. to be shaped into the form of a film (thickness: 160 ⁇ m). Furthermore, this film was stretched, into the transporting direction thereof in an atmosphere of 150° C.
  • Each protective film B Each 60- ⁇ m-thickness triacetylcellulose film (FUJTTACK TG6GUL, manufactured by Fujifilm Corp.) was used.
  • Each protective film C Each 50- ⁇ m-thickness cyclic olefin polymer film (COP) (ZB-12, manufactured by Zeon Corp.) was used.
  • COP cyclic olefin polymer film
  • visible rays As active energy rays, visible rays (gallium sealed metal halide lamp) were used. Radiating device: Light HAMMER 10, manufactured by Fusion UV Systems, Inc. Bulb: V bulb. Peak irradiance: 1600 mW/cm 2 . Integrated radiated-light quantity: 1000/mJ/cm 2 (wavelengths: 380 to 440 nm). The irradiance of the visible rays was measured, using a Sola-Check system manufactured by Solatell Ltd.
  • a curable resin composition was prepared which included the following in this curable resin composition, the total proportion of which was 100% by weight: 10% by weight of hydroxyethylacrylamide (manufactured by Kojin Co., Ltd.); 30% by weight of acryloylmorpholine (manufactured by Kojin Co., Ltd.); 45% by weight of 1,9-nonanediol diacrylate (manufactured by Kyoeisha Chemical Co., Ltd.); 10% by weight of a product ARUFRON UP1190 (acrylic oligomer yielded by polymerizing (meth)acrylic monomers, this product being manufactured by Toagosei Co., Ltd.); 3% by weight, of a product.
  • IRGACURE 907 polymerization initiator, manufactured by the company BASF
  • KAYACURE DETX-S polymerization initiator, manufactured by Nippon Kayaku Co., Ltd.
  • An adhesion-improving composition (A) used in each of Examples 1 to 18 and Comparative Examples 1 to 5 was yielded by mixing individual components with each other in accordance with a blend table described in Table 1.
  • Compounds blended into the adhesion-improving composition (A) are as follows:
  • 3-Acrylamidephenylboric acid compound represented by the general formula (1) (manufactured by Junsei Chemical Co., Ltd.),
  • 3-Methacrylamidephenylboric acid compound represented by the general formula (1): (manufactured by Junsei Chemical Co., Ltd.),
  • OLFIN EXP4200 leveling agent: (manufactured by Nissin Chemical Industry Co., Ltd.),
  • ARON A-104 (binder component): acrylic resin (solid content: 40%) (manufactured by Toagosei Co., Ltd.), and
  • JC-25 (binder component): polyvinyl, alcohol resin (manufactured by Japan VAM & Poval Co., Ltd.).
  • the above-mentioned visible rays were radiated onto both surfaces of the workpiece from the bonded transparent protective film sides (both sides) thereof to cure the active energy ray curable adhesive.
  • the workpiece was dried by hot wind at 70° C. for 3 minutes to yield a polarizing film having, on both sides thereof, the transparent protective films, respectively.
  • the line speed for the bonding was 25 m/min.
  • the polarizing film yielded in each of the examples was cat into pieces each having a size of 200 mm in a direction in parallel with the stretched direction of the polarizer, and 20 mm in an direction orthogonal thereto.
  • a utility knife was cut into between one of the transparent protective films and the polarizer of one of the pieces, and into between the other side transparent protective film and the polarizer of another of the pieces.
  • Each of the resultant polarizing films was bonded to a glass plate.
  • a machine Tensilon was used to peel off the transparent protective film and the polarizer from each other into 90-degree directions at a peel rate of 10 m/min. The peel strength thereof was measured.
  • an infrared absorption spectrum of each of the resultant peel surfaces was measured, using an ATR method. The peel interface was then evaluated in accordance with the following criterion:
  • a and D each mean that the adhering strength is not less than the cohesive strength of the film so that the adhering strength is very good.
  • B and C each mean that the transparent-protective-film/adhesive-layer (adhesive-layer/polarizer) interface is insufficient in adhering strength (or poor in adhering strength).
  • the adhering strength is judged to be good (circular mark); when the polarizing film falls under A and B (simultaneous generation of “cohesive fracture of the transparent protective film” and “interfacial fracture between the transparent protective film and the adhesive layer”) or under A and C (simultaneous generation of “cohesive fracture of the transparent protective film” and “interfacial fracture between the adhesive layer and the polarizer”), the adhering strength is judged to be acceptable (triangular mark); or when the polarizing film falls under B or C, the adhering strength is judged to foe bad (cross mark).
  • the polarizing film yielded in each of the examples was cut into pieces each having a size of 200 mm in a direction in parallel with the stretched direction of the polarizer, and 20 mm in a direction orthogonal thereto.
  • the polarizing films were immersed in pure water of 23° C. temperature for 24 hours, and then taken out.
  • the polarizing films were wiped with a dried cloth, and then a utility knife was cut into between one of the transparent protective films and the polarizer of one of the pieces, and into between the other side transparent protective film and the polarizer of another of the pieces.
  • Each of the resultant polarizing films was bonded to a glass plate.
  • a machine Tensilon was used to peel off the transparent protective film and the polarizer from each other into 90-degree directions at a peel rate of 10 m/min. The peel strength thereof was measured. Moreover, after the peeling, an infrared absorption spectrum of each of the resultant peel surfaces was measured, using an ATR method. The peel interface was then evaluated in accordance with the same criterion as in the adhering strength test. This evaluation was made within one minute after the time when the polarizing film was taken out from the pure water.
  • the polarizing film yielded in each of the examples was cut into pieces each having a size of 200 mm in a direction in parallel with the stretched direction of the polarizer, and 20 mm in an direction orthogonal thereto.
  • the polarizing films were immersed in pure water of 23° C. temperature for 48 hours, and then taken out.
  • the polarizing films were wiped with a dried cloth, and then a utility knife was cut into between one of the transparent protective films and the polarizer of one of the pieces, and into between the other side transparent protective film and the polarizer of another of the pieces.
  • Each of the resultant polarizing films was bonded to a glass plate.
  • a machine Tensilon was used to peel off the transparent protective film and the polarizer from each other into 90-degree directions at a peel rate of 10 m/min. The peel strength thereof was measured. Moreover, after the peeling, an infrared absorption spectrum of each of the resultant peel surfaces was measured, using an ATR method. The peel interface was then evaluated in accordance with the same criterion as in the adhering strength test. This evaluation was made within one minute after the time when the polarizing film was taken out from the pure water.
  • An adhesion-improving composition (A) used in each of Example 19 and Comparative Examples 6 to 8 was yielded by mixing individual components with each other in accordance with a blend table described in Table 4.
  • composition (A) used in each of Example 19 and Comparative Examples 6 to 8, which is described in Table 4 was applied onto both surfaces of any one of the above-mentioned polarizers, using a wire bar (manufactured by a company limited Dai-Ichi Rika; No. 2), The resultant was wind-dried at 60° C. for one minute to remove the solvent therein to produce an adhesion-improving-layer-attached polarizer. Next, each of two of the transparent protective films C was subjected to corona treatment, and the corona-treated surface of the film was coated with the composition (A) used in used in each of Example 19 and Comparative Examples 6 to 8, which is described in Table 3. The resultants were then dried at 60° C.
  • adhesion-improving-layer-attached protective films C were produced.
  • the above-mentioned curable resin composition was applied onto adhesion surfaces of the adhesion-improving-layer-attached polarizer and each of the adhesion-improving-layer-attached protective films C, so as to give each thickness of 0.7 ⁇ m, using an MCB coater (manufactured by FUJI KIKAI KOGYO Co., Ltd) (cell shape: honeycomb, the number of gravure lines: 1000 lines/inch, and rotating speed: 140% of line speed). A rolling device was then used to cause the protective films to bond onto both surfaces of the polarizer, respectively.
  • the above-mentioned visible rays were radiated onto both surfaces of the workpiece from the bonded transparent protective film sides (both sides) thereof to cure the active energy ray curable adhesive.
  • the workpiece was dried by hot wind at 70° C. for 3 minutes to yield a polarizing film having, on both sides thereof, the transparent protective films, respectively.
  • the line speed for the bonding was 25 m/min.

Landscapes

  • Chemical & Material Sciences (AREA)
  • Physics & Mathematics (AREA)
  • Organic Chemistry (AREA)
  • Optics & Photonics (AREA)
  • General Physics & Mathematics (AREA)
  • Life Sciences & Earth Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Wood Science & Technology (AREA)
  • Materials Engineering (AREA)
  • Nonlinear Science (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Mathematical Physics (AREA)
  • Crystallography & Structural Chemistry (AREA)
  • Medicinal Chemistry (AREA)
  • Health & Medical Sciences (AREA)
  • Polymers & Plastics (AREA)
  • Polarising Elements (AREA)
  • Adhesives Or Adhesive Processes (AREA)
  • Laminated Bodies (AREA)
  • Paints Or Removers (AREA)
  • Application Of Or Painting With Fluid Materials (AREA)
  • Compositions Of Macromolecular Compounds (AREA)
  • Devices For Indicating Variable Information By Combining Individual Elements (AREA)
  • Liquid Crystal (AREA)
US16/301,207 2016-05-17 2017-05-16 Laminated resin film, method for producing same, laminated optical film, image display device, and adhesion improvement-treated resin film Abandoned US20190137675A1 (en)

Applications Claiming Priority (5)

Application Number Priority Date Filing Date Title
JP2016-099139 2016-05-17
JP2016099138 2016-05-17
JP2016-099138 2016-05-17
JP2016099139 2016-05-17
PCT/JP2017/018421 WO2017199979A1 (ja) 2016-05-17 2017-05-16 積層樹脂フィルムおよびその製造方法、積層光学フィルム、画像表示装置ならびに易接着処理樹脂フィルム

Publications (1)

Publication Number Publication Date
US20190137675A1 true US20190137675A1 (en) 2019-05-09

Family

ID=60325202

Family Applications (2)

Application Number Title Priority Date Filing Date
US16/301,207 Abandoned US20190137675A1 (en) 2016-05-17 2017-05-16 Laminated resin film, method for producing same, laminated optical film, image display device, and adhesion improvement-treated resin film
US16/301,158 Expired - Fee Related US11061175B2 (en) 2016-05-17 2017-05-16 Polarizing film, method for producing same, optical film, image display device, and adhesion improvement-treated polarizer

Family Applications After (1)

Application Number Title Priority Date Filing Date
US16/301,158 Expired - Fee Related US11061175B2 (en) 2016-05-17 2017-05-16 Polarizing film, method for producing same, optical film, image display device, and adhesion improvement-treated polarizer

Country Status (6)

Country Link
US (2) US20190137675A1 (zh)
JP (4) JP7071786B2 (zh)
KR (2) KR20190006477A (zh)
CN (2) CN109073812A (zh)
TW (2) TWI777952B (zh)
WO (2) WO2017199979A1 (zh)

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
GB2616111B (en) * 2021-12-27 2024-11-20 Lg Display Co Ltd Adhesive material and display apparatus
US12359099B2 (en) 2019-07-30 2025-07-15 Nitto Denko Corporation Pressure-sensitive adhesive composition, pressure-sensitive adhesive layer, and pressure-sensitive adhesive sheet

Families Citing this family (19)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP6560999B2 (ja) 2016-03-09 2019-08-14 日東電工株式会社 硬化性樹脂組成物、偏光フィルムおよびその製造方法、光学フィルムならびに画像表示装置
WO2019163749A1 (ja) * 2018-02-26 2019-08-29 日東電工株式会社 偏光フィルムおよびその製造方法、光学フィルム、ならびに画像表示装置
JP7288306B2 (ja) * 2018-02-26 2023-06-07 日東電工株式会社 偏光フィルムおよびその製造方法、光学フィルム、ならびに画像表示装置
JP7137900B2 (ja) * 2018-02-26 2022-09-15 日東電工株式会社 活性エネルギー線硬化型接着剤組成物、偏光フィルムおよびその製造方法、光学フィルム、ならびに画像表示装置
CN111954833B (zh) * 2018-03-30 2022-07-12 Ａｇｃ株式会社 光学滤波器
US20220057557A1 (en) * 2018-12-17 2022-02-24 Nitto Denko Corporation Optical film with adhesive layer, image display panel and image display device
JP7370709B2 (ja) * 2019-01-28 2023-10-30 日東電工株式会社 積層体、光学フィルム、ならびに画像表示装置およびその製造方法
JP7265882B2 (ja) * 2019-02-26 2023-04-27 日東電工株式会社 偏光フィルムの製造方法、易接着層付偏光子、偏光フィルム、光学フィルム、および画像表示装置
WO2020174787A1 (ja) * 2019-02-28 2020-09-03 日東電工株式会社 偏光子保護用樹脂組成物および該組成物から形成された保護層を備える偏光板
JP7311291B2 (ja) 2019-03-28 2023-07-19 日東電工株式会社 偏光フィルムの製造方法
JP7219137B2 (ja) 2019-03-28 2023-02-07 日東電工株式会社 偏光フィルムの製造方法
JP2021009231A (ja) * 2019-07-01 2021-01-28 日東電工株式会社 偏光フィルム及びその製造方法、光学フィルム、並びに画像表示装置
CN110437739B (zh) * 2019-07-15 2021-02-19 淮阴工学院 环氧复合涂料及其制备方法
JP7305473B2 (ja) * 2019-07-18 2023-07-10 日東電工株式会社 偏光フィルムの製造方法及び偏光フィルムの製造装置
JP7336319B2 (ja) * 2019-09-04 2023-08-31 日東電工株式会社 偏光フィルムの製造方法
KR102850911B1 (ko) 2019-11-19 2025-08-26 닛토덴코 가부시키가이샤 광학 적층체의 제조 방법, 접착제 도공 장치 및 광학 적층체의 제조 장치
JP7398964B2 (ja) * 2020-01-10 2023-12-15 日東電工株式会社 偏光フィルムの製造方法
JP7617731B2 (ja) * 2020-12-04 2025-01-20 日東電工株式会社 偏光フィルム用接着剤組成物、偏光フィルム、光学フィルム、および画像表示装置
JP2023169633A (ja) * 2022-05-17 2023-11-30 住友化学株式会社 光学積層体

Family Cites Families (34)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2001296427A (ja) 2000-04-17 2001-10-26 Nitto Denko Corp 偏光板の製造方法及び液晶表示装置
JP3733418B2 (ja) 2001-04-16 2006-01-11 シャープ株式会社 粘接着シート、積層シート及び液晶表示装置
JP3785355B2 (ja) * 2001-11-30 2006-06-14 シャープ株式会社 光送受信モジュールおよび電子機器
JP4007502B2 (ja) 2002-02-01 2007-11-14 日東電工株式会社 粘着型光学フィルムおよび画像表示装置
CN1659457A (zh) * 2002-06-11 2005-08-24 日东电工株式会社 偏振片、偏振片用胶粘剂、光学薄膜及图像显示装置
JP4433145B2 (ja) 2003-02-12 2010-03-17 日東電工株式会社 光学部材用粘着剤組成物、光学部材用粘着剤層、粘着型光学部材および画像表示装置
JP4827369B2 (ja) 2003-08-28 2011-11-30 住友化学株式会社 偏光板の製造方法
JP4583982B2 (ja) * 2004-03-23 2010-11-17 日東電工株式会社 偏光板、光学フィルムおよび画像表示装置
WO2006054438A1 (ja) * 2004-11-18 2006-05-26 Nitto Denko Corporation 偏光板およびそれを用いた画像表示装置
US20090059369A1 (en) * 2005-03-31 2009-03-05 Nippon Shokubai Co., Ltd. Polarizer protective film, polarizing plate, and image display apparatus
JP2007316366A (ja) * 2006-05-26 2007-12-06 Nippon Shokubai Co Ltd 偏光子保護フィルム、偏光板、および画像表示装置
JP5051696B2 (ja) * 2007-04-06 2012-10-17 住友化学株式会社 偏光板
US20090017298A1 (en) 2007-07-11 2009-01-15 Nitto Denko Corporation Adhesive composition, adhesive optical film and image display device
JP5250307B2 (ja) 2007-07-11 2013-07-31 日東電工株式会社 粘着型光学フィルムおよび画像表示装置
US7906216B2 (en) * 2007-09-28 2011-03-15 Nitto Denko Corporation Polarizing plate, manufacturing method therefor, optical film and image display
JP5591477B2 (ja) * 2008-03-13 2014-09-17 日東電工株式会社 光学部材用粘着剤組成物、光学部材用粘着剤層、粘着型光学部材、透明導電性積層体、タッチパネルおよび画像表示装置
JP4901978B2 (ja) * 2010-05-31 2012-03-21 住友化学株式会社 延伸フィルム、偏光性延伸フィルムおよび偏光板の製造方法
JP5426505B2 (ja) 2010-08-31 2014-02-26 日東電工株式会社 活性エネルギー線硬化型樹脂組成物、接着剤層、偏光板、光学フィルムおよび画像表示装置
JP6293422B2 (ja) * 2013-05-01 2018-03-14 日東電工株式会社 偏光板、その製造方法、光学フィルムおよび画像表示装置
KR102159761B1 (ko) 2013-08-12 2020-09-24 미쯔비시 케미컬 주식회사 접착제 조성물, 편광판용 접착제 조성물, 편광판용 접착제, 및 이를 사용하여 이루어진 편광판
WO2015053359A1 (ja) * 2013-10-09 2015-04-16 富士フイルム株式会社 偏光板、画像表示装置
JP6191427B2 (ja) 2013-12-05 2017-09-06 東洋インキＳｃホールディングス株式会社 活性エネルギー線重合性樹脂組成物及び積層体
JP6488125B2 (ja) 2013-12-26 2019-03-20 日東電工株式会社 積層偏光フィルム、その製造方法、積層光学フィルムおよび画像表示装置
WO2015098734A1 (ja) 2013-12-26 2015-07-02 住友化学株式会社 偏光子、ならびに、この偏光子を備える偏光板および偏光性積層フィルム
JP6186011B2 (ja) 2014-01-23 2017-08-23 富士フイルム株式会社 偏光板および画像表示装置
JP6670236B2 (ja) * 2014-06-30 2020-03-18 株式会社カネカ 光学用樹脂組成物およびフィルム
WO2016010031A1 (ja) * 2014-07-16 2016-01-21 日東電工株式会社 偏光フィルムおよびその製造方法
US10247979B2 (en) * 2014-09-30 2019-04-02 Nitto Denko Corporation Polarizing film, pressure-sensitive-adhesive-layer-attached polarizing film, and image display device
KR102121279B1 (ko) * 2014-11-06 2020-06-10 동우 화인켐 주식회사 편광자의 제조방법
JP6689103B2 (ja) * 2015-03-12 2020-04-28 日東電工株式会社 偏光フィルムおよびその製造方法、光学フィルムならびに画像表示装置
WO2016143885A1 (ja) 2015-03-12 2016-09-15 日東電工株式会社 偏光フィルムおよびその製造方法、光学フィルムならびに画像表示装置
JP6709060B2 (ja) * 2016-02-03 2020-06-10 日東電工株式会社 硬化性樹脂組成物
JP6560999B2 (ja) * 2016-03-09 2019-08-14 日東電工株式会社 硬化性樹脂組成物、偏光フィルムおよびその製造方法、光学フィルムならびに画像表示装置
JP6868345B2 (ja) * 2016-04-22 2021-05-12 日東電工株式会社 硬化性樹脂組成物、偏光フィルムおよびその製造方法、光学フィルムならびに画像表示装置

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US12359099B2 (en) 2019-07-30 2025-07-15 Nitto Denko Corporation Pressure-sensitive adhesive composition, pressure-sensitive adhesive layer, and pressure-sensitive adhesive sheet
GB2616111B (en) * 2021-12-27 2024-11-20 Lg Display Co Ltd Adhesive material and display apparatus

Also Published As

Publication number Publication date
JPWO2017199979A1 (ja) 2019-03-14
CN109073812A (zh) 2018-12-21
TW201806769A (zh) 2018-03-01
JP7071786B2 (ja) 2022-05-19
US20190293851A1 (en) 2019-09-26
CN109073817B (zh) 2021-12-21
TWI719207B (zh) 2021-02-21
KR20190006477A (ko) 2019-01-18
KR102324305B1 (ko) 2021-11-09
JP2022043088A (ja) 2022-03-15
JP2022062073A (ja) 2022-04-19
JPWO2017199978A1 (ja) 2019-03-14
CN109073817A (zh) 2018-12-21
TWI777952B (zh) 2022-09-21
TW201743086A (zh) 2017-12-16
WO2017199979A1 (ja) 2017-11-23
KR20190007410A (ko) 2019-01-22
JP7278075B2 (ja) 2023-05-19
US11061175B2 (en) 2021-07-13
WO2017199978A1 (ja) 2017-11-23

Similar Documents

Publication Publication Date Title
US11061175B2 (en) Polarizing film, method for producing same, optical film, image display device, and adhesion improvement-treated polarizer
JP6936355B2 (ja) 偏光フィルムおよびその製造方法、光学フィルムならびに画像表示装置
US10899946B2 (en) Curable resin composition, polarizing film and production process therefor, optical film, and image display device
US10696877B2 (en) Curable resin composition, polarizing film and method for manufacture thereof, optical film, and image display device
KR102261968B1 (ko) 점착층 부착 편광 필름 및 그 점착층 부착 편광 필름의 제조 방법
WO2016143435A1 (ja) 架橋剤および硬化性樹脂組成物、偏光フィルムおよびその製造方法、光学フィルムならびに画像表示装置
US20190031794A1 (en) Curable resin composition
WO2016143885A1 (ja) 偏光フィルムおよびその製造方法、光学フィルムならびに画像表示装置
JP6535797B2 (ja) 偏光フィルム用接着剤組成物、偏光フィルム、光学フィルムおよび画像表示装置
US20190055432A1 (en) Curing type adhesive composition for polarizing film and manufacturing method therefor, polarizing film and manufacturing method therefor, optical film and image display device
WO2017010225A1 (ja) 偏光フィルム用硬化型接着剤組成物、偏光フィルムおよびその製造方法、光学フィルムならびに画像表示装置
US20200056051A1 (en) Curable resin composition for optical films, optical film and method for producing same
WO2020039896A1 (ja) 偏光子、偏光フィルム、光学フィルム、ならびに画像表示装置
WO2017010224A1 (ja) 偏光フィルム用硬化型接着剤組成物、偏光フィルムおよびその製造方法、光学フィルムならびに画像表示装置
WO2020039895A1 (ja) 偏光子、偏光フィルム、光学フィルム、ならびに画像表示装置
JP6712846B2 (ja) 偏光フィルム用硬化型接着剤組成物、偏光フィルムおよびその製造方法、光学フィルムならびに画像表示装置
KR102909325B1 (ko) 편광 필름의 제조 방법
US20210132274A1 (en) Curable resin composition for polarizing films, polarizing film and method for producing same
US11046719B2 (en) Organic metal compound-containing composition
WO2018008443A1 (ja) 粘着層付き偏光フィルムおよび該粘着層付き偏光フィルムの製造方法
WO2016152564A1 (ja) 偏光フィルム用硬化型接着剤組成物、偏光フィルムおよびその製造方法、光学フィルムならびに画像表示装置
WO2020039894A1 (ja) 偏光子、偏光フィルム、光学フィルム、ならびに画像表示装置

Legal Events

Date Code Title Description
AS Assignment

Owner name: NITTO DENKO CORPORATION, JAPAN

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:KANNO, RYO;SAITO, TAKESHI;YAMASAKI, TATSUYA;AND OTHERS;SIGNING DATES FROM 20180613 TO 20180615;REEL/FRAME:047489/0347

STPP Information on status: patent application and granting procedure in general

Free format text: DOCKETED NEW CASE - READY FOR EXAMINATION

STPP Information on status: patent application and granting procedure in general

Free format text: NON FINAL ACTION MAILED

STCB Information on status: application discontinuation

Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION