US20110039109A1 - Activator for epoxy resin compositions - Google Patents

Activator for epoxy resin compositions Download PDF

Info

Publication number
US20110039109A1
US20110039109A1 US12/988,917 US98891709A US2011039109A1 US 20110039109 A1 US20110039109 A1 US 20110039109A1 US 98891709 A US98891709 A US 98891709A US 2011039109 A1 US2011039109 A1 US 2011039109A1
Authority
US
United States
Prior art keywords
group
epoxy resin
heat
formula
activator
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US12/988,917
Other languages
English (en)
Inventor
Karsten Frick
Ulrich Gerber
Juergen Finter
Andreas Kramer
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Sika Technology AG
Original Assignee
Sika Technology AG
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from EP08155487A external-priority patent/EP2113525A1/de
Priority claimed from CH17232008A external-priority patent/CH699848A2/de
Application filed by Sika Technology AG filed Critical Sika Technology AG
Assigned to SIKA TECHNOLOGY AG reassignment SIKA TECHNOLOGY AG ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: GERBER, ULRICH, FRICK, KARSTEN, FINTER, JUERGEN, KRAMER, ANDREAS
Publication of US20110039109A1 publication Critical patent/US20110039109A1/en
Abandoned legal-status Critical Current

Links

Classifications

    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
    • C08G65/00—Macromolecular compounds obtained by reactions forming an ether link in the main chain of the macromolecule
    • C08G65/02—Macromolecular compounds obtained by reactions forming an ether link in the main chain of the macromolecule from cyclic ethers by opening of the heterocyclic ring
    • C08G65/26—Macromolecular compounds obtained by reactions forming an ether link in the main chain of the macromolecule from cyclic ethers by opening of the heterocyclic ring from cyclic ethers and other compounds
    • C08G65/2642—Macromolecular compounds obtained by reactions forming an ether link in the main chain of the macromolecule from cyclic ethers by opening of the heterocyclic ring from cyclic ethers and other compounds characterised by the catalyst used
    • C08G65/2669—Non-metals or compounds thereof
    • C08G65/2672—Nitrogen or compounds thereof
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
    • C08G18/00—Polymeric products of isocyanates or isothiocyanates
    • C08G18/06—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen
    • C08G18/28—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen characterised by the compounds used containing active hydrogen
    • C08G18/30—Low-molecular-weight compounds
    • C08G18/38—Low-molecular-weight compounds having heteroatoms other than oxygen
    • C08G18/3819—Low-molecular-weight compounds having heteroatoms other than oxygen having nitrogen
    • C08G18/3842—Low-molecular-weight compounds having heteroatoms other than oxygen having nitrogen containing heterocyclic rings having at least one nitrogen atom in the ring
    • C08G18/3848—Low-molecular-weight compounds having heteroatoms other than oxygen having nitrogen containing heterocyclic rings having at least one nitrogen atom in the ring containing two nitrogen atoms in the ring
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
    • C08G59/00—Polycondensates containing more than one epoxy group per molecule; Macromolecules obtained by polymerising compounds containing more than one epoxy group per molecule using curing agents or catalysts which react with the epoxy groups
    • C08G59/18—Macromolecules obtained by polymerising compounds containing more than one epoxy group per molecule using curing agents or catalysts which react with the epoxy groups ; e.g. general methods of curing
    • C08G59/68—Macromolecules obtained by polymerising compounds containing more than one epoxy group per molecule using curing agents or catalysts which react with the epoxy groups ; e.g. general methods of curing characterised by the catalysts used
    • C08G59/686—Macromolecules obtained by polymerising compounds containing more than one epoxy group per molecule using curing agents or catalysts which react with the epoxy groups ; e.g. general methods of curing characterised by the catalysts used containing nitrogen
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/31504—Composite [nonstructural laminate]
    • Y10T428/31511—Of epoxy ether
    • Y10T428/31515—As intermediate layer

Definitions

  • the present invention relates to the field of heat-curing epoxy resin bodyshell adhesives.
  • Heat-curing epoxy resin compositions have been known for a long time.
  • An important application of heat-curing epoxy resin compositions is in vehicle assembly, in particular in bonding or in filling cavities in the bodyshell with foam material.
  • the body is heated in a CDC (cathodic dip coating) oven, whereby the heat-curing epoxy resin composition is also cured and optionally expanded into a foam.
  • the aim of the present invention is to provide novel activators for heat-curing epoxy resin compositions which are quite effective but nevertheless have good storage stability.
  • the activators exhibit excellent activation or acceleration of epoxy resin curing, even at relatively low temperatures. However, in addition they also exhibit excellent storage stability, so they can be added to epoxy resins with no problems and can be stored for long periods at temperatures below 50° C. It has furthermore been shown that these activators have very little or no negative effect on the mechanical properties of the cured epoxy resin compositions.
  • heat-curing epoxy resin compositions can therefore be prepared according to embodiments.
  • Embodiments also relate to a method for bonding, as well as a bonded article.
  • Embodiments may include an activator C for epoxy resin compositions.
  • This activator C has formula (I) or is a reaction product between a compound of formula (Ia) and an isocyanate or epoxide.
  • n stands for 1 or 2 or 3 or 4.
  • R 2 and R 3 each independently stand for H or OH or halogen or NH 2 or NHR 7 or N(R 7 ) 2 or for an alkoxy, alkyl, aryl, alkylaryl, or arylalkyl group, in particular with 1 to 10 C atoms, or else R 2 and R 3 together form an optionally substituted aliphatic or aromatic ring.
  • R 4 and R 5 either each independently stand for H or OH or else R 4 and R 5 together form an optionally substituted aliphatic or aromatic ring.
  • the alkoxy, alkyl, aryl, alkylaryl, or arylalkyl groups have between 1 and 10 C atoms, a C 4 to C 6 alkylene group is especially preferred.
  • R 1 furthermore stands either for an n-valent, optionally hetero atom-containing aliphatic, cycloaliphatic, or aromatic organic radical, or else R 1 stands for a radical of formula (II).
  • i and j and k each stand for a number from 0 to 10, provided that the sum of i and j is at least 2 and X stands for O or S or NR 7 .
  • Y stands for OR 7 or SR 7 or N(R 7 )(R 7′ ) or for a substituent of formula (III).
  • R 2′ and R 3′ again each independently stand either for H or OH or halogen or NH 2 or NHR 7 or N(R 7 ) 2 or for an alkoxy, alkyl, aryl, alkylaryl, or arylalkyl group, or else R 2′ together with R 3′ form an optionally substituted aliphatic or aromatic ring.
  • R 7 and R 7′ each independently stand for H or for an alkyl, cycloalkyl, aralkyl, or aryl group with 1 to 8 carbon atoms.
  • At least one of the radicals R 2 , R 3 , R 4 , and R 5 must be different from H and, if the radicals R 2′ and/or R 3′ are present, at least three of the radicals R 2 , R 2′ , R 3 , and R 3′ must be different from H.
  • R 1 preferably stands for a radical of formula (II).
  • an essential feature of the invention is that at least one of the radicals R 2 , R 3 , R 4 , and R 5 is different from H.
  • R 2 , R 3 , R 4 , and R 5 is different from H.
  • 1-methyl-2-phenylimidazoline, 1-isopropyl-2-phenylimidazoline, or 2-phenylimidazoline do not correspond to formula (I) and thus do not represent activators according to the invention.
  • the activator C in particular has formula (I-1) or (I-2).
  • g stands for 0 or 1 or 2 or 3 and h stands for 0 or 1 or 2.
  • R 2 and R 2′ stand in particular for OH, and R 3 and/or R 3′ stand in particular for OH, Cl, CH 3 , or OCH 3 .
  • R 2 and R 2′ each stand for OH, and R 3 and R 3′ each stand for Cl.
  • R 2 and R 2′ each stand for OH, and R 3 and R 3′ each stand for CH 3 .
  • R 2 and R 3 , or R 2 and R 3 are preferably meta to each other.
  • radicals R 2′ and/or R 3′ are present in the formula of the activator C, as is the case in formulas (I-1), (I-1′), and (I-2), it should be noted that it is firstly an essential feature of the invention that at least one of the radicals R 2 , R 3 , R 4 , and R 5 is different from H, and secondly that at least three of the radicals R 2 , R 2′ , R 3 , and R 3′ are different from H.
  • activators C of formula (I) can be synthesized from an acid methyl ester of formula (I-1a) and an amine.
  • activators C of formula (I-1) can be synthesized from the acid methyl ester of formula (I-1a) and/or (I-1a′) and a polyamine of formula (I-1b).
  • R 2 and/or R 2′ are ortho to the ester group.
  • the activators C of formula (I-2) can be synthesized from the acid methyl ester of formula (I-1a) and a polyamine of formula (I-2b). Here an intermediate of formula (I-2c) is formed, which can be converted to the activator of formula (I-2) by ring closure or condensation.
  • the activator C can be a reaction product between a compound of formula (Ia) and an isocyanate, in particular a monoisocyanate or diisocyanate.
  • the activator C in particular has at least one structural element of formula (Ia-1).
  • Suitable isocyanates are in particular monoisocyanates or diisocyanates. Especially suitable monoisocyanates are phenyl isocyanate, tolyl isocyanate, or toluoylsulfonyl monoisocyanate.
  • Suitable diisocyanates are aliphatic, cycloaliphatic, aromatic, or araliphatic diisocyanates, in particular methylene diphenyl diisocyanate (MDT), hexamethylene diisocyanate (HDD, toluene diisocyanate (TDI), tolidine diisocyanate (TODD, isophorone diisocyanate (1PDI), trimethyl hexamethylene diisocyanate (TMDD, 2,5- or 2,6-bis(isocyanatomethyl)bicyclo[2.2.1]heptane, 1,5-naphthalene diisocyanate (NDI), dicyclohexylmethyl diisocyanate (H 12 MDD, p-phenylene diisocyanate (PPDD, m-tetramethylxylylene diisocyanate (TMXDI), as well as dimers or trimers thereof.
  • MDT methylene diphenyl diisocyanate
  • HDD hex
  • HDI, IPDI, MDI, or TDI are preferred diisocyanates.
  • a preferred monoisocyanate or diisocyanate is selected from the group consisting of phenyl isocyanate, tolyl isocyanate, hexamethylene diisocyanate (HDI), isophorone diisocyanate (IPDD, methylene diphenyl diisocyanate (MDI), and toluene diisocyanate (TDI).
  • reaction of a compound of formula (Ia) with an isocyanate is carried out by a method familiar to the person skilled in the art of polyurethanes.
  • the activator C can be a reaction product between a compound of formula (Ia) and an epoxide, in particular a monoglycidyl ether or diglycidyl ether or triglycidyl ether.
  • the activator C in particular has at least one structural element of formula (Ia-2), in particular of formula (Ia-2′).
  • Suitable epoxides are in particular
  • Glycidyl ethers of monofunctional saturated or unsaturated, branched or unbranched, cyclic or open-chain C 4 -C 30 alcohols in particular selected from the group consisting of butyl glycidyl ether, hexyl glycidyl ether, 2-ethylhexyl glycidyl ether, allyl glycidyl ether, tetrahydrofurfuryl and furfuryl glycidyl ether, trimethoxysilylpropyl glycidyl ether (3-glycidyloxypropyltrimethoxysilane);
  • Glycidyl ethers of difunctional saturated or unsaturated, branched or unbranched, cyclic or open-chain C 2 -C 30 alcohols in particular selected from the group consisting of ethylene glycol glycidyl ether, butanediol glycidyl ether, hexanediol glycidyl ether, octanediol glycidyl ether, cyclohexane dimethanol diglycidyl ether, and neopentyl glycol diglycidyl ether;
  • Glycidyl ethers of trifunctional or polyfunctional, saturated or unsaturated, branched or unbranched, cyclic or open-chain alcohols such as epoxidized castor oil, epoxidized trimethylolpropane, epoxidized pentaerythrol, or polyglycidyl ethers of aliphatic polyols such as sorbitol, glycerol, or trimethylolpropane;
  • Glycidyl ethers of phenol compounds and aniline compounds in particular selected from the group consisting of phenyl glycidyl ether, cresyl glycidyl ether, p-tert-butyl phenyl glycidyl ether, nonylphenyl glycidyl ether, 3-n-pentadecenyl glycidyl ether (from cashew nutshell oil), N,N-diglycidyl aniline, and p-aminophenyl triglycidyl [ether];
  • Epoxidized amines such as N,N-diglycidyl cyclohexylamine
  • Epoxidized monocarboxylic acids or dicarboxylic acids in particular selected from the group consisting of neodecanoic acid glycidyl ester, methacrylic acid glycidyl ester, benzoic acid glycidyl ester, phthalic acid diglycidyl ester, tetra- and hexahydrophthalic acid diglycidyl ester, and diglycidyl esters of dimeric fatty acids, as well as terephthalic acid glycidyl ester and trimellitic acid glycidyl ester;
  • Epoxidized difunctional or trifunctional, low molecular weight or high molecular weight polyether polyols in particular polyethylene glycol diglycidyl ether or polypropylene glycol diglycidyl ether.
  • Epoxy resins such as are described as epoxy resin A as a component of heat-curing epoxy resin compositions, in particular diglycidyl ethers of bisphenol A and/or F.
  • Hexanediol diglycidyl ether, cresyl glycidyl ether, p-tert-butylphenyl glycidyl ether, polypropylene glycol diglycidyl ether, and polyethylene glycol diglycidyl ether are especially preferred.
  • reaction of a compound of formula (Ia) with an epoxide is carried out by a method familiar to the person skilled in the art of epoxy compounds.
  • an activator C is formed which has at least one free epoxy group.
  • the activator C in the heat-curing epoxy resin compositions described below can realize its activation function but ultimately is chemically bound to the epoxy resin matrix, whereby activator C is prevented from leaching out of the cured compound over time (in particular due to the influence of environmental factors such as heat, contamination by water or chemicals) and thus being released into the environment in contact with the cured composition.
  • the activator C should not have any primary or secondary amino groups. But if it nevertheless has such groups, this is not at all critical since, although when used in a heat-curing epoxy resin composition described below it does react with the epoxy resin, in this reaction just an optionally higher molecular weight reaction product is formed which likewise functions as an activator. It is also assumed that in this case, because of the epoxy to activator concentration ratio, a reaction product forms which, besides having the activating imidazoline structure, also has free epoxy groups, whereby such an activator is also chemically bound to the epoxy resin matrix, resulting in the advantages mentioned above.
  • the activators C result in very effective activation of curing of epoxy resins by heat.
  • the improved activation results in curing at lower temperature. In DSC, this is apparent in a shift of the reaction peak, or by a shift of the “onset point” to lower temperatures for the first heating of an epoxy resin mixture containing an activator C, compared with the corresponding composition without activator C.
  • Tg glass transition temperature
  • embodiments may relate to a heat-curing epoxy resin composition consisting of
  • the epoxy resin with more than one epoxy group per molecule on the average is preferably a liquid epoxy resin or a solid epoxy resin.
  • the term “solid epoxy resin” is very familiar to the person skilled in the art of epoxides, and is used in contrast to “liquid epoxy resins.”
  • the glass transition temperature of solid resins is above room temperature, i.e., at room temperature they can be broken up into free-flowing particles.
  • Preferred solid epoxy resins have formula (X):
  • substituents R′ and R′′ each independently stand for either H or CH 3 .
  • subscript s stands for a number >1.5, in particular a number from 2 to 12.
  • Such solid epoxy resins are commercially available, for example, from Dow or Huntsman or Hexion.
  • Preferred liquid epoxy resins have formula (XI):
  • substituents R′′ and R′′′ each independently stand for either H or CH 3 .
  • subscript r stands for a number from 0 to 1.
  • the subscript r preferably stands for a number less than 0.2.
  • Such epoxy resins are commercially available under the trade names EPN or ECN as well as TACTIX® from Huntsman or as the D.E.N.® product line from Dow Chemical.
  • Epoxy resin A preferably is a liquid epoxy resin of formula (XI).
  • the heat-curing epoxy resin composition contains at least one liquid epoxy resin of formula (XI) as well as at least one solid epoxy resin of formula (X).
  • the proportion of epoxy resin A is preferably 10-85 wt. %, in particular 15-70 wt. %, preferably 15-60 wt. %, based on the weight of the composition.
  • composition according to the invention additionally contains at least one curing agent B for epoxy resins which is activated at elevated temperature.
  • the curing agent is preferably selected from the group consisting of dicyanodiamide, guanamines, guanidines, aminoguanidines, and derivatives thereof.
  • Catalytically effective curing agents can also be used, such as substituted ureas such as, for example, 3-(3-chloro-4-methylphenyl)-1,1-dimethylurea (chlortoluron) or phenyl dimethylureas, in particular p-chlorophenyl-N,N-dimethylurea (monuron), 3-phenyl-1,1-dimethylurea (fenuron), 3,4-dichlorophenyl-N,N-dimethylurea (diuron), or N,N-dimethylurea.
  • substituted ureas such as, for example, 3-(3-chloro-4-methylphenyl)-1,1-dimethylurea (chlortoluron) or phenyl dimethylureas, in particular p-chlorophenyl-N,N-dimethylurea (monuron), 3-phenyl-1,1-dimethylurea (fenuron), 3,4
  • Curing agent B is preferably a curing agent selected from the group consisting of dicyanodiamide, guanamines, guanidines, aminoguanidines, and derivatives thereof; substituted ureas, in particular 3-(3-chloro-4-methylphenyl)-1,1-dimethylurea (chlortoluron) or phenyl dimethylureas, in particular p-chlorophenyl-N,N-dimethylurea (monuron), 3-phenyl-1,1-dimethylurea (fenuron), 3,4-dichlorophenyl-N,N-dimethylurea (diuron), N,N-dimethylurea, as well as imidazoles, imidazole salts, and amine complexes.
  • substituted ureas in particular 3-(3-chloro-4-methylphenyl)-1,1-dimethylurea (chlortoluron) or phenyl dimethylureas,
  • Dicyanodiamide is particularly preferred as curing agent B.
  • the total proportion of curing agent B is advantageously 1-10 wt. %, preferably 2-8 wt. %, based on the weight of the total composition.
  • the heat-curing epoxy resin composition can contain a thixotropic agent C [sic] based on a urea derivative.
  • the urea derivative is in particular a reaction product between an aromatic monomeric diisocyanate and an aliphatic amine compound. It is also quite possible to react more than one different monomeric diisocyanates with one or more aliphatic amine compounds, or to react a monomeric diisocyanate with more than one aliphatic amine compounds.
  • MDI 4,4′-diphenylmethylene diisocyanate
  • butylamine has proven to be particularly advantageous.
  • the urea derivative is preferably present in a carrier.
  • the carrier can be a plasticizer, in particular a phthalate or an adipate, preferably a diisodecylphthalate (DIDP) or dioctyladipate (DOA).
  • DIDP diisodecylphthalate
  • DOA dioctyladipate
  • the carrier can also be a non-diffusing carrier. This is preferred in order to ensure the least possible migration of the unreacted components after curing.
  • Blocked polyurethane prepolymers are preferred as the non-diffusing carrier.
  • the carrier is advantageously a blocked polyurethane prepolymer, in particular obtained by reaction of a trifunctional polyether polyol with IPDI, followed by blocking of the terminal isocyanate groups by ⁇ -caprolactam.
  • the total proportion of thixotropic agent C is advantageously 0-40 wt. %, preferably 5-25 wt. %, based on the weight of the total composition.
  • the ratio of the weight of the urea derivative to the weight of the optionally present carrier is preferably 2:98 to 50:50, in particular 5:95-25:75.
  • the heat-curing one-component epoxy resin composition additionally contains at least one other toughener D.
  • the additional toughener D can be solid or liquid.
  • the toughener D is in particular selected from the group consisting of blocked polyurethane polymers, liquid rubbers, epoxy resin-modified liquid rubbers, and core/shell polymers.
  • this toughener D may be a liquid rubber D1 which is an acrylonitrile/butadiene copolymer terminated by carboxyl groups or (meth)acrylate groups or epoxy groups, or is a derivative thereof.
  • liquid rubbers are commercially available, for example, under the name HYPRO® (formerly HYCAR®) CTBN and CTBNX and ETBN from Nanoresins AG, Germany or Emerald Performance Materials LLC.
  • Suitable derivatives are in particular elastomer-modified prepolymers having epoxy groups, such as are commercially marketed as the POLYDIS® product line, preferably from the POLYDIS® 36xx product line, by the Struktol Company (Schill & Seilacher Group, Germany) or as the Albipox product line (Nanoresins, Germany).
  • the toughener D may be a polyacrylate liquid rubber D2 that is completely miscible with liquid epoxy resins, and only separates into microdroplets during curing of the epoxy resin matrix.
  • polyacrylate liquid rubbers are available, for example, under the name 20208-XPA from Rohm and Haas.
  • mixtures of liquid rubbers can of course also be used, in particular mixtures of carboxyl-terminated or epoxy-terminated acrylonitrile/butadiene copolymers or derivatives thereof with epoxy-terminated polyurethane prepolymers.
  • the toughener D may be a solid toughener which is an organic ion-exchanged layered mineral DE1.
  • the ion-exchanged layered mineral DE1 can be either a cation-exchanged layered mineral DE1c or an anion-exchanged layered mineral DE1a.
  • the cation-exchanged layered mineral DE1c here is obtained from a layered mineral DE1′, in which at least some of the cations have been exchanged by organic cations.
  • a layered mineral DE1′ in which at least some of the cations have been exchanged by organic cations.
  • Examples of such cation-exchanged layered minerals DE1c are in particular those which are mentioned in U.S. Pat. No. 5,707,439 or in U.S. Pat. No. 6,197,849. The method for preparation of these cation-exchanged layered minerals DE1c is also described in those patents.
  • the layered mineral DE1′ is preferably a sheet silicate.
  • the layered mineral DE1′ is particularly preferably a phyllosilicate as described in U.S. Pat. No.
  • At least some of the cations of the layered mineral DE1′ are replaced by organic cations.
  • examples of such cations are n-octylammonium, trimethyldodecylammonium, dimethyldodecylammonium, or bis(hydroxyethyl)octadecylammonium or similar derivatives of amines that can be obtained from natural fats and oils; or guanidinium cations or amidinium cations; or cations of N-substituted derivatives of pyrrolidine, piperidine, piperazine, morpholine, thiomorpholine; or cations of 1,4-diazobicyclo[2.2.2]octane (DABCO) and 1-azobicyclo[2.2.2]octane; or cations of N-substituted derivatives of pyridine, pyrrole, imidazole, oxazole, pyrimidine, quinoline
  • cyclic amidinium cations are suitable, in particular those such as are disclosed in U.S. Pat. No. 6,197,849 in Column 3, Line 6 to Column 4, Line 67.
  • linear ammonium compounds cyclic ammonium compounds are distinguished by elevated thermal stability, since thermal Hofmann degradation cannot occur with them.
  • Preferred cation-exchanged layered minerals DE1c are familiar to the person skilled in the art under the term organoclay or nanoclay, and are commercially available, for example, under the group names TIXOGEL® or NANOFIL® (Süchemie), CLOISITE® (Southern Clay Products), or NANOMER® (Nanocor, Inc.), or GARAMITE® (Rockwood).
  • the anion-exchanged layered mineral DE1a here is obtained from a layered mineral DE1′′ in which at least some of the anions have been exchanged by organic anions.
  • An example of such an anion-exchanged layered mineral DE1a is a hydrotalcite DE1′′, in which at least some of the interlayer carbonate anions have been exchanged by organic anions.
  • composition it is also quite possible for the composition to simultaneously contain a cation-exchanged layered mineral DE1c and an anion-exchanged layered mineral DE1a.
  • the toughener D is a solid toughener which is a block copolymer DE2.
  • the block copolymer DE2 is obtained from an anionic or controlled free-radical polymerization of methacrylic acid ester with at least one other monomer having an olefinic double bond.
  • Particularly preferred as a monomer having an olefinic double bond is one in which the double bond is conjugated directly with a hetero atom or with at least one other double bond.
  • Particularly suitable monomers are selected from the group including styrene, butadiene, acrylonitrile, and vinyl acetate.
  • Acrylate/styrene/acrylonitrile (ASA) copolymers available, for example, under the name GELOY 1020 from GE Plastics, are preferred.
  • block copolymers DE2 are block copolymers derived from methacrylic acid methyl ester, styrene, and butadiene. Such block copolymers are available, for example, as triblock copolymers under the group name SBM from Arkema.
  • the toughener D may be a core/shell polymer DE3.
  • Core/shell polymers consist of an elastic core polymer and a rigid shell polymer.
  • Particularly suitable core/shell polymers consist of a core made from elastic acrylate or butadiene polymer which is enclosed in a rigid shell made from a rigid thermoplastic polymer. This core/shell structure is either formed spontaneously through separation of a block copolymer or is determined by latex polymerization or suspension polymerization followed by grafting.
  • Preferred core/shell polymers are “MBS polymers,” which are available under the trade names CLEARSTRENGTH® from Atofina, PARALOID® from Rohm and Haas, or F-351® from Zeon.
  • core/shell polymer particles that are already in the form of dried polymer latex.
  • core/shell polymer particles that are already in the form of dried polymer latex.
  • examples of these are GENIOPERL® M23A from Wacker with a polysiloxane core and an acrylate shell, radiation crosslinked rubber particles of the NEP series manufactured by Eliokem, or Nanoprene from Lanxess or Paraloid EXL from Rohm and Haas or Kane ACE MX-120 from Kaneka.
  • core/shell polymers are sold under the name ALBIDUR® by Nanoresins AG, Germany.
  • Nanoscale silicates in an epoxy matrix are also suitable, such as are sold under the trade name Nonopox from Nanoresins AG, Germany.
  • the toughener D may be a reaction product DE4 between carboxylated solid nitrile rubber and excess epoxy resin.
  • the toughener D may be a blocked polyurethane polymer of formula (IV).
  • n and m′ each stand for numbers between 0 and 8, provided that m+m′ stands for a number from 1 to 8.
  • Y 1 stands for a linear or branched polyurethane polymer PU1 terminated by m+m′ isocyanate groups, after removal of all terminal isocyanate groups.
  • Y 2 each independently stand for a blocking group which is cleaved at a temperature above 100° C.
  • Y 3 each independently stand for a group of formula (IV').
  • R 14 stands for an aliphatic, cycloaliphatic, aromatic, or araliphatic epoxy radical containing a primary or secondary hydroxyl group, after removal of the hydroxide and epoxide groups, and p stands for the numbers 1, 2, or 3.
  • aromatic radical means an aralkyl group, i.e., an alkyl group substituted by aryl groups (see Römpp, CD Römpp Chemie Lexikon [Römpp Chemistry Encyclopedia], Version 1, Stuttgart/New York, Georg Thieme Verlag, 1995).
  • Y 2 each independently stand in particular for substituents selected from the group consisting of
  • R 15 , R 16 , R 17 , and R 18 each independently stand for an alkyl or cycloalkyl or aralkyl or arylalkyl group, or else R 15 together with R 16 or R 17 together with R 18 forms part of a 4- to 7-membered ring, which is optionally substituted.
  • R 19 , R 19′ , and R 20 each independently stand for an alkyl or aralkyl or arylalkyl group or for an alkyloxy or aryloxy or aralkyloxy group, and R 11 stands for an alkyl group.
  • R 23 and R 24 each independently stand for an alkylene group with 2 to 5 C atoms, which optionally has double bonds or is substituted, or for a phenylene group or for a hydrogenated phenylene group, and R 25 , R 26 , and R 27 each independently stand for H or for an alkyl group or for an aryl group or an aralkyl group.
  • R 28 stands for an aralkyl group or for a mononuclear or polynuclear substituted or unsubstituted aromatic group, which optionally has aromatic hydroxyl groups.
  • Phenols or bisphenols, after removal of an hydroxyl group, are in particular firstly to be considered as R 28 .
  • Preferred examples of such phenols and bisphenols are in particular phenol, cresol, resorcinol, pyrocatechol, cardanol (3-pentadecenylphenol (from cashew nutshell oil)), nonylphenol, phenols reacted with styrene or dicyclopentadiene, bisphenol A, bisphenol F, and 2,2′-diallyl bisphenol A.
  • Hydroxybenzyl alcohol and benzyl alcohol, after removal of an hydroxyl group, are in particular secondly to be considered as R 28 .
  • R 15 , R 16 , R 17 , R 18 , R 19 , R 19′ , R 20 , R 21 , R 25 , R 26 , or R 27 stand for an alkyl group, the latter group is in particular a linear or branched C 1 -C 20 alkyl group.
  • R 15 , R 16 , R 17 , R 18 , R 19 , R 19′ , R 20 , R 25 , R 26 , or R 28 stand for an aralkyl group, the latter group is in particular an aromatic group bonded through methylene, in particular a benzyl group.
  • R 15 , R 16 , R 17 , R 18 , R 19 , R 19′ , or R 20 stand for an alkylaryl group, the latter is in particular a C 1 to C 20 alkylaryl group bonded through phenylene such as, for example, tolyl or xylyl.
  • radicals Y 2 are radicals selected from the group consisting of
  • the radical Y here stands for a saturated or olefinic unsaturated hydrocarbon radical with 1 to 20 C atoms, in particular with 1 to 15 C atoms. Allyl, methyl, nonyl, dodecyl or an unsaturated C 15 alkyl radical with 1 to 3 double bonds are particularly preferred.
  • the radical X stands for H or for an alkyl, aryl, aralkyl group, in particular for H or methyl.
  • the subscripts z′ and z′′ stand for the numbers 0, 1, 2, 3, 4, or 5, provided that the sum z′-z′′ stands for a number between 1 and 5.
  • m is different from 0.
  • the blocked polyurethane polymer of formula (IV) is synthesized from isocyanate group-terminated linear or branched polyurethane polymers PU1 and one or more isocyanate-reactive compounds Y 2 H and/or Y 3 H. If more than one such isocyanate-reactive compound is used, the reaction can be carried out sequentially or with a mixture of these compounds.
  • the reaction is carried out in such a way that the one or more isocyanate-reactive compounds Y 2 H and/or Y 3 H are used in stoichiometric amounts or in stoichiometric excess, in order to ensure that all the NCO groups are reacted.
  • the isocyanate-reactive compound Y 3 H is a monohydroxyl epoxy compound of formula (IVa).
  • reaction can be carried out sequentially or with a mixture of these compounds.
  • the monohydroxyl epoxy compound of formula (IVa) has 1, 2, or 3 epoxy groups.
  • the hydroxyl group of this monohydroxyl epoxy compound (IVa) can be a primary or a secondary hydroxyl group.
  • Such monohydroxyl epoxy compounds can, for example, be produced by reaction of polyols with epichlorohydrin. Depending on how the reaction is carried out, when polyfunctional alcohols are reacted with epichlorohydrin, the corresponding monohydroxyl epoxy compounds are also formed as byproducts in different concentrations. The latter can be isolated by means of conventional separation operations. Generally, however, it is sufficient to use the product mixture obtained in the polyol glycidylization reaction, consisting of the polyol reacted completely and partially to form the glycidyl ether.
  • hydroxyl-containing epoxides examples include butanediol monoglycidyl ethers (present in butanediol diglycidyl ethers), hexanediol monoglycidyl ethers (present in hexanediol diglycidyl ethers), cyclohexanedimethanol glycidyl ethers, trimethylolpropane diglycidyl ethers (present as a mixture in trimethylolpropane triglycidyl ethers), glycerol diglycidyl ethers (present as a mixture in glycerol triglycidyl ethers), pentaerythritol triglycidyl ethers (present as a mixture in pentaerythritol tetraglycidyl ethers). It is preferable to use trimethylolpropane diglycidyl ether, which occurs
  • hydroxyl-containing epoxides can also be used, in particular glycidol, 3-glycidyloxybenzyl alcohol, or hydroxymethyl cyclohexene oxide.
  • ⁇ -hydroxy ether of formula (IVb) which is present in a proportion up to 15% in commercially available liquid epoxy resins synthesized from bisphenol A (R ⁇ CH 3 ) and epichlorohydrin, as well as the corresponding ⁇ -hydroxy ethers of formula (IVb), which are formed when bisphenol F (R ⁇ H) or the mixture of bisphenol A and bisphenol F is reacted with epichlorohydrin.
  • distillation residues produced during manufacture of high-purity distilled liquid epoxy resins are also preferred.
  • Such distillation residues have an hydroxyl-containing epoxide concentration one to three times higher than in commercially available undistilled liquid epoxy resins.
  • very different epoxides with a ⁇ -hydroxy ether group synthesized by reaction of (poly)epoxides with a substoichiometric amount of monofunctional nucleophiles such as carboxylic acids, phenols, thiols, or secondary amines, can also be used.
  • a trivalent radical of the following formula is particularly preferred as the radical R 14 :
  • R stands for methyl or H.
  • the free primary or secondary OH functional group of the monohydroxyl epoxy compound of formula (IVa) allows for efficient reaction with terminal isocyanate groups of polymers, without needing to use unusual excesses of the epoxide component.
  • the polyurethane polymer PU1 on which Y 1 is based can be synthesized from at least one diisocyanate or triisocyanate and at least one polymer Q PM having terminal amino, thiol, or hydroxyl groups and/or one optionally substituted polyphenol Q PP .
  • Suitable diisocyanates are, for example, aliphatic, cycloaliphatic, aromatic, or araliphatic diisocyanates, in particular commercially available products such as methylene diphenyl diisocyanate (MDI), 1,4-butane diisocyanate, hexamethylene diisocyanate (HDD, toluene diisocyanate (TDI), tolidine diisocyanate (TODD, isophorone diisocyanate trimethyl hexamethylene diisocyanate (TMDI), 2,5- or 2,6-bis(isocyanatomethyl)bicyclo[2.2.1]heptane, 1,5-naphthalene diisocyanate (NDI), dicyclohexylmethyl diisocyanate (H 12 MDI), p-phenylene diisocyanate (PPDI), or in-tetramethylxylylene diisocyanate (TMXDI) as well as dimers thereof.
  • Suitable triisocyanates are, for example, trimers or biurets of aliphatic, cycloaliphatic, aromatic, or araliphatic diisocyanates, in particular the isocyanurates and biurets of the diisocyanates described in the previous paragraph.
  • Suitable polymers Q PM having terminal amino, thiol, or hydroxyl groups are in particular polymers Q PM having two or three terminal amino, thiol, or hydroxyl groups.
  • the polymers Q PM advantageously have a weight per equivalent of 300-6000, in particular 600-4000, preferably 700-2200 g/equivalent of NCO-reactive groups.
  • Suitable polymers Q PM are in particular polyoxyalkylene polyols, also called polyether polyols, hydroxy-terminated polybutadienepolyols, styrene/acrylonitrile grafted polyether polyols, polyhydroxy-terminated acrylonitrile/butadiene copolymers, polyester polyols, as well as polycarbonate polyols.
  • polyoxyalkylene polyols also called polyether polyols, hydroxy-terminated polybutadienepolyols, styrene/acrylonitrile grafted polyether polyols, polyhydroxy-terminated acrylonitrile/butadiene copolymers, polyester polyols, as well as polycarbonate polyols.
  • polyphenol Q PP Particularly suitable as the polyphenol Q PP are bisphenols, trisphenols, and tetraphenols. This means not only pure phenols but optionally also substituted phenols. The nature of the substitution can be quite diverse. In particular, this means a direct substitution on the aromatic ring to which the phenol OH group is bonded. By phenols furthermore is meant not only mononuclear aromatics but also polynuclear or condensed aromatics or heteroaromatics having phenol OH groups directly on the aromatic or heteroaromatic rings.
  • Bisphenols and trisphenols are especially suitable.
  • tougheners D optionally present in the composition are tougheners which are amphiphilic hydroxyl group-containing block copolymers, such as are marketed under the trade name FORTEGRA®, in particular FORTEGRA®100, by Dow Chemical, or their reaction products with polyisocyanates and optionally other isocyanate-reactive compounds.
  • Especially suitable as the toughener D optionally present in the composition are any of those disclosed in the following articles or patents, whose contents are incorporated here by reference: EP 0 308 664 A 1, in particular formula (I), especially page 5, Line 14 to page 13, Line 24; EP 0 338 985 A1, EP 0 353 190 A1, WO 00/20483 A1, in particular formula (I), especially page 8, Line 18 to page 12, Line 2; WO 01/94492 A1, in particular the reaction products denoted as D) and E), especially page 10, Line 15 to page 14, line 22; WO 03/078163 A1, in particular the acrylate-terminated polyurethane resin denoted as B), especially page 14, Line 6 to page 14, Line 35; WO 2005/007766 A1, in particular formula (I) or (II), especially page 4, Line 5 to page 11 up to Line 20; EP 1 728 825 A1, in particular formula (I), especially page 3, line 21 to page 4 up to Line 47; WO 2006/052726 A1, in particular the
  • the proportion of toughener D is advantageously used in an amount of 1-35 wt. %, in particular 1-25 wt. %, based on the weight of the composition.
  • the composition in addition contains at least one filler F.
  • the filler is preferably mica, talc, kaolin, wollastonite, feldspar, syenite, chlorite, bentonite, montmorillonite, calcium carbonate (precipitated or ground), dolomite, quartz, silicic acids (pyrogenic or precipitated), cristobalite, calcium oxide, aluminum hydroxide, magnesium oxide, hollow ceramic spheres, hollow glass spheres, hollow organic spheres, glass spheres, colored pigments.
  • the Filler F we mean both organic coated and uncoated commercially available forms familiar to the person skilled in the art.
  • alumoxanes such as, for example, are described in U.S. Pat. No. 6,322,890.
  • the total proportion of total filler F is advantageously 3-50 wt. %, preferably 5-35 wt. %, in particular 5-25 wt. %, based on the weight of the total composition.
  • the composition may contain a physical or chemical blowing agent, as is available, for example, under the trade name EXPANCEL® from Akzo Nobel, or CELOGEN® from Chemtura, or under the trade name LUVOPOR® from Lehmann & Voss.
  • the proportion of the blowing agent is advantageously 0.1-3 wt.-%, based on the weight of the composition.
  • the composition in addition may contain at least one epoxy group-containing reactive diluent G.
  • reactive diluents G are in particular:
  • Glycidyl ethers of monofunctional saturated or unsaturated, branched or unbranched, cyclic or open-chain C 4 -C 30 alcohols in particular selected from the group consisting of butyl glycidyl ether, hexyl glycidyl ether, 2-ethylhexyl glycidyl ether, allyl glycidyl ether, tetrahydrofurfuryl and furfuryl glycidyl ether, trimethoxysilylpropyl glycidyl ether (3-glycidyloxypropyltrimethoxysilane).
  • Glycidyl ethers of difunctional saturated or unsaturated, branched or unbranched, cyclic or open-chain C 2 -C 30 alcohols in particular selected from the group consisting of ethylene glycol glycidyl ether, butanediol glycidyl ether, hexanediol glycidyl ether, octanediol glycidyl ether, cyclohexane dimethanol diglycidyl ether, and neopentyl glycol diglycidyl ether.
  • Glycidyl ethers of trifunctional or polyfunctional, saturated or unsaturated, branched or unbranched, cyclic or open-chain alcohols such as epoxidized castor oil, epoxidized trimethylolpropane, epoxidized pentaerythrol, or polyglycidyl ethers of aliphatic polyols such as sorbitol, glycerol, or trimethylolpropane.
  • Glycidyl ethers of phenol compounds and aniline compounds in particular selected from the group consisting of phenyl glycidyl ether, cresyl glycidyl ether, p-tert-butyl phenyl glycidyl ether, nonylphenyl glycidyl ether, 3-n-pentadecenyl glycidyl ether (from cashew nutshell oil), N,N-diglycidyl aniline, and p-aminophenyl triglycidyl [ether].
  • Epoxidized amines such as N,N-diglycidyl cyclohexylamine.
  • Epoxidized monocarboxylic acids or dicarboxylic acids in particular selected from the group consisting of neodecanoic acid glycidyl ester, methacrylic acid glycidyl ester, benzoic acid glycidyl ester, phthalic acid diglycidyl ester, tetra- and hexahydrophthalic acid diglycidyl ester, and diglycidyl esters of dimeric fatty acids, as well as terephthalic acid glycidyl ester and trimellitic acid glycidyl ester.
  • Epoxidized difunctional or trifunctional, low molecular weight to high molecular weight polyether polyols in particular polyethylene glycol diglycidyl ether or polypropylene glycol diglycidyl ether.
  • Hexanediol diglycidyl ether, cresyl glycidyl ether, p-tert-butylphenyl glycidyl ether, polypropylene glycol diglycidyl ether, and polyethylene glycol diglycidyl ether are especially preferred.
  • the total proportion of epoxy group-containing reactive diluent G is advantageously 0.1-20 wt. %, preferably 1-8 wt. %, based on the weight of the total composition.
  • the composition can include other components, in particular catalysts, stabilizers, in particular heat and/or light stabilizers, thixotropic agents, plasticizers, solvents, mineral or organic fillers, blowing agents, dyes and pigments, corrosion inhibitors, surfactants, defoamers, and adhesion promoters.
  • Suitable plasticizers are in particular phenyl alkylsulfonic acid esters or N-butyl benzenesulfonamide, such as are commercially available as MESAMOLL® or Dellatol BBS from Bayer.
  • Suitable stabilizers are in particular optionally substituted phenols such as BHT or WINGSTAY® T (Elikem), sterically hindered amines, or N-oxyl compounds such as TEMPO (Evonik)
  • heat-curing epoxy resin compositions described are especially suitable as one-component adhesives.
  • Such a one-component adhesive has broad applications.
  • heat-curing one-component adhesives can be realized in particular that are distinguished by high impact strength both at elevated temperatures and especially at low temperatures, in particular between 0° C. and ⁇ 40° C.
  • Such adhesives are needed for bonding heat-stable materials.
  • “Heat-stable materials” means materials which for a cure temperature of 100° C.-220° C., preferably 120° C.-200° C., are shape-stable at least during the cure time.
  • the heat-stable materials in particular are metals and plastics such as ABS, polyimide, polyphenylene ethers, composite materials such as SMC, glass fiber reinforced unsaturated polyesters, epoxy or acrylate composites.
  • a preferred use is when at least one material is a metal.
  • a particularly preferred use is bonding of identical or different metals, in particular in bodyshells in the automobile industry.
  • Preferred metals are especially steel, in particular electrogalvanized steel, hot-dip galvanized steel, lubricated steel, Bonazinc-coated steel, and subsequently phosphatized steel as well as aluminum, in particular the types commonly used in automobile construction.
  • Such an adhesive in particular is first brought into contact with the materials to be bonded at a temperature between 10° C. and 80° C., in particular between 10° C. and 60° C., and is subsequently cured at a temperature of typically 100° C.-220° C., preferably 120°-200° C.
  • a further aspect of the present invention relates to a method for bonding heat-stable substrates, including the following steps:
  • Heating the composition to a temperature of 100° C.-220° C., in particular 140° C.-200° C., preferably between 160° C. and 190° C.
  • Substrate S2 here consists of material which is the same as or different from substrate S1.
  • Such a method for bonding heat-stable materials results in a bonded article.
  • Such an article is preferably a vehicle or part of a vehicle.
  • sealants or coatings can also be realized with a composition according to the invention.
  • the compositions according to the invention are not only suitable for automobile assembly but are also suitable for other areas of application. We should especially mention related applications in assembly of means of transportation such as ships, trucks, buses, or track vehicles, or in assembly of consumer goods such as, for example, washing machines.
  • the materials bonded by means of a composition according to the invention are used at temperatures between typically 120° C. and ⁇ 40° C., preferably between 100° C. and ⁇ 40° C., in particular between 80° C. and ⁇ 40° C.
  • Such an adhesive in particular is first brought into contact with the materials to be bonded at a temperature between 10° C. and 80° C., in particular between 10° C. and 60° C., and is subsequently cured at a temperature of typically 100° C.-220° C., preferably 120°-200° C.
  • a further aspect of the present invention relates to a method for bonding heat-stable substrates, including the following steps:
  • Heating the composition to a temperature of 100° C.-220° C., in particular 140° C.-200° C., preferably between 160° C. and 190° C.
  • Substrate 52 here consists of material which is the same as or different from substrate S1.
  • Such a method for bonding heat-stable materials results in a bonded article.
  • Such an article is preferably a vehicle or part of a vehicle.
  • sealants or coatings can also be realized with a composition according to the invention.
  • the compositions according to the invention are not only suitable for automobile assembly but are also suitable for other areas of application. We should especially mention related applications in assembly of means of transportation such as ships, trucks, buses, or track vehicles, or in assembly of consumer goods such as, for example, washing machines.
  • the materials bonded by means of a composition according to the invention are used at temperatures between typically 120° C. and 40° C., preferably between 100° C. and ⁇ 40° C., in particular between 80° C. and ⁇ 40° C.
  • thermosetting epoxy resin composition according to the invention is its use as a heat-curing one-component bodyshell adhesive in vehicle assembly or as stiffening material or as a foamable heat-curing composition for reinforcement in cavities of structural components and reinforcement elements.

Landscapes

  • Chemical & Material Sciences (AREA)
  • Health & Medical Sciences (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Medicinal Chemistry (AREA)
  • Polymers & Plastics (AREA)
  • Organic Chemistry (AREA)
  • Epoxy Resins (AREA)
  • Adhesives Or Adhesive Processes (AREA)
  • Polyurethanes Or Polyureas (AREA)
US12/988,917 2008-04-30 2009-04-30 Activator for epoxy resin compositions Abandoned US20110039109A1 (en)

Applications Claiming Priority (5)

Application Number Priority Date Filing Date Title
EP08155487A EP2113525A1 (de) 2008-04-30 2008-04-30 Aktivator für Epoxidharzzusammensetzungen
EP08155487.5 2008-04-30
CH17232008A CH699848A2 (de) 2008-11-04 2008-11-04 Aktivator für epoxidharzzusammensetzungen.
CH01723/08 2008-11-04
PCT/EP2009/055252 WO2009133168A1 (de) 2008-04-30 2009-04-30 Aktivator für epoxidharzzusammensetzungen

Related Parent Applications (1)

Application Number Title Priority Date Filing Date
PCT/EP2009/055252 A-371-Of-International WO2009133168A1 (de) 2008-04-30 2009-04-30 Aktivator für epoxidharzzusammensetzungen

Related Child Applications (1)

Application Number Title Priority Date Filing Date
US13/904,542 Continuation US8859695B2 (en) 2008-04-30 2013-05-29 Activator for epoxy resin compositions

Publications (1)

Publication Number Publication Date
US20110039109A1 true US20110039109A1 (en) 2011-02-17

Family

ID=40940157

Family Applications (2)

Application Number Title Priority Date Filing Date
US12/988,917 Abandoned US20110039109A1 (en) 2008-04-30 2009-04-30 Activator for epoxy resin compositions
US13/904,542 Active US8859695B2 (en) 2008-04-30 2013-05-29 Activator for epoxy resin compositions

Family Applications After (1)

Application Number Title Priority Date Filing Date
US13/904,542 Active US8859695B2 (en) 2008-04-30 2013-05-29 Activator for epoxy resin compositions

Country Status (6)

Country Link
US (2) US20110039109A1 (de)
EP (1) EP2274359B1 (de)
JP (1) JP5687187B2 (de)
CN (1) CN102015817B (de)
AT (1) ATE548405T1 (de)
WO (1) WO2009133168A1 (de)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20210198538A1 (en) * 2010-11-19 2021-07-01 Ppg Industries Ohio, Inc. Structural adhesive compositions

Families Citing this family (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP3339347A1 (de) * 2016-12-23 2018-06-27 Sika Technology Ag Hitzehärtende epoxidharzzusammensetzung enthaltend einen beschleuniger
EP3476882A1 (de) 2017-10-24 2019-05-01 Sika Technology Ag Hitzehärtende epoxidharzzusammensetzung mit hoher lagerstabilität

Citations (12)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US622890A (en) * 1899-04-11 Rolling gate
US4060655A (en) * 1974-02-02 1977-11-29 Hoechst Aktiengesellschaft Resin coated metal substrates
US4200725A (en) * 1977-07-01 1980-04-29 Chemische Werke Huls A.G. Method of producing blocked polyisocyanates by reaction of an imidazoline with an isocyanate
US4242248A (en) * 1977-10-05 1980-12-30 Chemische Werke Huls Ag Storage-stable baking lacquers prepared from polyisocyanates blocked with cyclic amidines
US4246394A (en) * 1975-09-20 1981-01-20 Veba-Chemie Aktiengesellschaft Process of hardening epoxy coating composition with dicyandiamide/imidazoline derivative
DE3004902A1 (de) * 1980-02-09 1981-08-20 Chemische Werke Hüls AG, 4370 Marl Formkoerper- und ueberzugsmassen
US4355008A (en) * 1981-04-20 1982-10-19 Reynolds Metals Company Chlorination process
US4997851A (en) * 1987-12-31 1991-03-05 Isaacs Charles E Antiviral and antibacterial activity of fatty acids and monoglycerides
US4997951A (en) * 1989-03-17 1991-03-05 Ciba-Geigy Corporation Imidazoline compounds
US5207439A (en) * 1992-02-21 1993-05-04 Magline, Inc. Improvements in hand trucks with pivotally connected, spreadable, wheel-supported, auxiliary support frames
US5719240A (en) * 1995-12-28 1998-02-17 Huels Aktiengesellschaft Compounds containing cyclic amidine and uretdione groups, a process for their preparation and the use thereof
US6197349B1 (en) * 1993-08-12 2001-03-06 Knoll Aktiengesellschaft Particles with modified physicochemical properties, their preparation and uses

Family Cites Families (35)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE2123033A1 (de) 1971-02-11 1972-08-24 Du Pont Epoxy haltige Polymermasse
DE2731335A1 (de) * 1977-07-12 1979-01-25 Veba Chemie Ag Verfahren zum verkleben von werkstoffen
DE2738270A1 (de) * 1977-08-25 1979-03-01 Veba Chemie Ag Pulverfoermige ueberzugsmittel und deren anwendung
DE2861691D1 (en) * 1977-08-25 1982-04-29 Huels Chemische Werke Ag Poudery coating composition
JPS6011561A (ja) * 1983-06-30 1985-01-21 Hitachi Chem Co Ltd 配線板用エポキシ樹脂ワニス
ES2025260B3 (es) 1987-08-26 1992-03-16 Ciba-Geigy Ag Resinas epoxidicas modificadas
EP0338985B1 (de) 1988-04-18 1994-05-18 Ciba-Geigy Ag Modifizierte Epoxidharze
ES2068911T3 (es) 1988-07-28 1995-05-01 Ciba Geigy Ag Combinaciones de flexibilizadores para resinas epoxi.
JP2786456B2 (ja) * 1988-09-14 1998-08-13 旭電化工業株式会社 硬化性エポキシ樹脂組成物
US5189118A (en) 1991-02-28 1993-02-23 Texaco Chemical Company Mixtures of 1-isopropyl-2-aryl imidazole and 1-isopropyl-2-aryl imidazoline as epoxy resin curatives
JPH0827402A (ja) * 1994-07-18 1996-01-30 Shikoku Chem Corp エポキシ樹脂粉体塗料組成物
US5530052A (en) 1995-04-03 1996-06-25 General Electric Company Layered minerals and compositions comprising the same
DE19627951A1 (de) * 1996-07-11 1998-01-15 Huels Chemische Werke Ag Pulverförmige Verbindungen, ein Verfahren zu ihrer Herstellung sowie deren Verwendung
JP3924875B2 (ja) * 1997-11-26 2007-06-06 東ソー株式会社 液状エポキシ樹脂組成物
JP2002504582A (ja) 1998-02-20 2002-02-12 バンティコ アクチエンゲゼルシャフト 親有機性フィロシリケート
US6322890B1 (en) 1998-03-30 2001-11-27 Wm. Marsh Rice University Supra-molecular alkylalumoxanes
DE19845607A1 (de) 1998-10-06 2000-04-20 Henkel Teroson Gmbh Schlagfeste Epoxidharz-Zusammensetzungen
JP2000226441A (ja) * 1999-02-08 2000-08-15 Tosoh Corp 液状エポキシ樹脂組成物
JP2000290257A (ja) * 1999-04-01 2000-10-17 Shikoku Chem Corp 新規イミダゾリン化合物およびイミダゾリン化合物を有効成分とするエポキシ樹脂硬化剤
JP2001098210A (ja) * 1999-09-30 2001-04-10 Shikoku Chem Corp エポキシ系粉体塗料組成物
DE50102330D1 (de) 2000-04-10 2004-06-24 Henkel Kgaa Schlagfeste epoxidharz-zusammensetzungen
EP1152019A1 (de) 2000-05-02 2001-11-07 Sika AG, vorm. Kaspar Winkler & Co. Thixotropiermittel
US20030192643A1 (en) 2002-03-15 2003-10-16 Rainer Schoenfeld Epoxy adhesive having improved impact resistance
EP1431325A1 (de) 2002-12-17 2004-06-23 Sika Technology AG Hitze-härtbare Epoxidharzzusammensetzung mit verbesserter Tieftemperatur-Schlagzähigkeit
EP2843022B1 (de) 2003-07-07 2020-12-16 Dow Global Technologies LLC Klebende Epoxidzusammensetzung und Verfahren zum Auftragen
EP1498441A1 (de) 2003-07-16 2005-01-19 Sika Technology AG Hitzehärtende Zusammensetzungen mit Tieftemperatur-Schlagzähigkeitsmodifikatoren
JP2005290150A (ja) * 2004-03-31 2005-10-20 Idemitsu Kosan Co Ltd アミド化合物及びその用途
JP4583373B2 (ja) * 2004-03-31 2010-11-17 旭化成イーマテリアルズ株式会社 エポキシ樹脂用硬化剤及びエポキシ樹脂組成物
KR101226379B1 (ko) 2004-11-10 2013-01-24 다우 글로벌 테크놀로지스 엘엘씨 양친매성 블록 공중합체-개질된 에폭시 수지 및 그로부터제조된 접착제
RU2387683C2 (ru) 2004-11-10 2010-04-27 Дау Глобал Текнолоджиз Инк. Эпоксидные смолы, упрочненные амфифильным блок-сополимером
DE602005020260D1 (de) 2005-06-02 2010-05-12 Dow Global Technologies Inc Schlagzähmodifizierter Strukturklebstoff auf Epoxid Basis
EP1754721A1 (de) 2005-08-16 2007-02-21 Sika Technology AG Aminogruppen-terminierte Zähigkeitsverbesserer und deren Folgeprodukte und Verwendungen
ATE534703T1 (de) 2005-08-24 2011-12-15 Henkel Kgaa Epoxidzusammensetzungen mit verbesserter schlagzähigkeit
KR101352811B1 (ko) 2006-07-31 2014-02-17 헨켈 아게 운트 코. 카게아아 경화성 에폭시 수지-기재 접착성 조성물
US7759435B2 (en) 2006-09-26 2010-07-20 Loctite (R&D) Limited Adducts and curable compositions using same

Patent Citations (12)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US622890A (en) * 1899-04-11 Rolling gate
US4060655A (en) * 1974-02-02 1977-11-29 Hoechst Aktiengesellschaft Resin coated metal substrates
US4246394A (en) * 1975-09-20 1981-01-20 Veba-Chemie Aktiengesellschaft Process of hardening epoxy coating composition with dicyandiamide/imidazoline derivative
US4200725A (en) * 1977-07-01 1980-04-29 Chemische Werke Huls A.G. Method of producing blocked polyisocyanates by reaction of an imidazoline with an isocyanate
US4242248A (en) * 1977-10-05 1980-12-30 Chemische Werke Huls Ag Storage-stable baking lacquers prepared from polyisocyanates blocked with cyclic amidines
DE3004902A1 (de) * 1980-02-09 1981-08-20 Chemische Werke Hüls AG, 4370 Marl Formkoerper- und ueberzugsmassen
US4355008A (en) * 1981-04-20 1982-10-19 Reynolds Metals Company Chlorination process
US4997851A (en) * 1987-12-31 1991-03-05 Isaacs Charles E Antiviral and antibacterial activity of fatty acids and monoglycerides
US4997951A (en) * 1989-03-17 1991-03-05 Ciba-Geigy Corporation Imidazoline compounds
US5207439A (en) * 1992-02-21 1993-05-04 Magline, Inc. Improvements in hand trucks with pivotally connected, spreadable, wheel-supported, auxiliary support frames
US6197349B1 (en) * 1993-08-12 2001-03-06 Knoll Aktiengesellschaft Particles with modified physicochemical properties, their preparation and uses
US5719240A (en) * 1995-12-28 1998-02-17 Huels Aktiengesellschaft Compounds containing cyclic amidine and uretdione groups, a process for their preparation and the use thereof

Non-Patent Citations (3)

* Cited by examiner, † Cited by third party
Title
HCAPLUS accession no. 1981:103366 for Marxer, U.S. Patent No. 4,292,429, September 29, 1981, four pages. *
HCAPLUS accession no. 1981:54758 for Dupin et al., Annali dell 'Universita di Ferrara, Sezione 5: Chemica Pura ed Applicata,Supplemento, 1980, two pages. *
HCAPLUS accession no. 2001:578925 for Wang et al., Zhongguo Fushi Yu Fanghu Xuebao, 2001, two pages. *

Cited By (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20210198538A1 (en) * 2010-11-19 2021-07-01 Ppg Industries Ohio, Inc. Structural adhesive compositions
US20220204823A1 (en) * 2010-11-19 2022-06-30 Ppg Industries Ohio, Inc. Structural adhesive compositions
US20220204822A1 (en) * 2010-11-19 2022-06-30 Ppg Industries Ohio, Inc. Structural adhesive compositions
US11629276B2 (en) * 2010-11-19 2023-04-18 Ppg Industries Ohio, Inc. Structural adhesive compositions
US12031064B2 (en) * 2010-11-19 2024-07-09 Ppg Industries Ohio, Inc. Structural adhesive compositions
US12043768B2 (en) * 2010-11-19 2024-07-23 Ppg Industries Ohio, Inc. Structural adhesive compositions
US12049574B2 (en) * 2010-11-19 2024-07-30 Ppg Industries Ohio, Inc. Structural adhesive compositions

Also Published As

Publication number Publication date
US20130253094A1 (en) 2013-09-26
CN102015817B (zh) 2014-08-20
EP2274359B1 (de) 2012-03-07
WO2009133168A1 (de) 2009-11-05
EP2274359A1 (de) 2011-01-19
CN102015817A (zh) 2011-04-13
JP2011518936A (ja) 2011-06-30
ATE548405T1 (de) 2012-03-15
US8859695B2 (en) 2014-10-14
JP5687187B2 (ja) 2015-03-18

Similar Documents

Publication Publication Date Title
US8608899B2 (en) Heat-curing epoxy resin composition comprising an accelerator having heteroatoms
JP6359041B2 (ja) 非芳香族尿素を反応促進剤として含む熱硬化性エポキシ樹脂組成物
US8829122B2 (en) Polyurethane polymer based on an amphiphilic block copolymer and its use as impact modifier
US8071217B2 (en) Heat-curable epoxy resin composition containing one blocked and one epoxide-terminated polyurethane prepolymer
US20110114257A1 (en) Reaction products based on amphiphilic block copolymers and their use as impact modifier
US8202920B2 (en) Heat-curable epoxy resin composition comprising a blocked polyurethane prepolymer
US8728271B2 (en) Silane/urea compound as a heat-activatable curing agent for epoxide resin compositions
US9012575B2 (en) Epoxy group-terminated polymers, the compositions thereof and the use thereof as impact resistance modifiers
US20100310878A1 (en) Wash-out resistant heat-curing epoxy resin adhesives
JP2011503315A5 (de)
US20110130479A1 (en) Adhesion promoter compounds for oiled steel
JP2018510933A (ja) Ｐｔｍｅｇ系ポリウレタン耐衝撃改良剤における向上した低温耐衝撃性
US20190055439A1 (en) Single-component thermosetting epoxy resin with improved adhesion
US8859695B2 (en) Activator for epoxy resin compositions
JP2011518936A5 (de)
EP2113525A1 (de) Aktivator für Epoxidharzzusammensetzungen

Legal Events

Date Code Title Description
AS Assignment

Owner name: SIKA TECHNOLOGY AG, SWITZERLAND

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:FRICK, KARSTEN;GERBER, ULRICH;FINTER, JUERGEN;AND OTHERS;SIGNING DATES FROM 20100908 TO 20100915;REEL/FRAME:025180/0218

STCB Information on status: application discontinuation

Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION