RU2482095C1

RU2482095C1 - Ceramic mixture for making floor tiles (versions)

Info

Publication number: RU2482095C1
Application number: RU2012101190/03A
Authority: RU
Inventors: Юлия Алексеевна Щепочкина
Original assignee: Юлия Алексеевна Щепочкина
Priority date: 2012-01-12
Filing date: 2012-01-12
Publication date: 2013-05-20

Abstract

FIELD: chemistry.

SUBSTANCE: invention relates to compositions of ceramic mixtures which can be used in making floor tiles. The ceramic mixture for making floor tiles contains the following components, wt %: clay 52.7-54.7; pegmatite 27.0-31.0; andesite 8.0-12.0; quartz sand 6.0-8.0; carboxymethyl cellulose 0.1-0.2; glycerol 0.1-0.2. In an alternative version of the invention, the ceramic mixture contains, wt %: clay 52.7-54.7; pegmatite 27.0-31.0; andesite 8.0-12.0; zircon 6.0-8.0; carboxymethyl cellulose 0.1-0.2; glycerol 0.1-0.2.

EFFECT: high scratch resistance of articles made from the ceramic mixture.

2 tbl

Description

Изобретение относится к области технологии силикатов и касается составов керамических масс, которые могут быть использованы для изготовления напольной плитки.The invention relates to the field of technology of silicates and relates to compositions of ceramic masses that can be used for the manufacture of floor tiles.

Известная керамическая масса, содержащая, мас.%: глину 45,0-90,0; андезит 0,5-30,0; пегматит 0-25,0 [1].Known ceramic mass containing, wt.%: Clay 45.0-90.0; andesite 0.5-30.0; pegmatitis 0-25.0 [1].

Задача изобретения состоит в повышении стойкости к истиранию изделий, полученных из керамической массы.The objective of the invention is to increase the abrasion resistance of products obtained from ceramic mass.

Технический результат достигается тем, что керамическая масса для изготовления напольной плитки, включающая глину, пегматит, андезит, дополнительно содержит кварцевый песок, карбоксиметилцеллюлозу и глицерин, при следующем соотношении компонентов, мас.%: глина 52,7-54,7; пегматит 27,0-31,0; андезит 8,0-12,0; кварцевый песок 6,0-8,0; карбоксиметилцеллюлоза 0,1-0,2; глицерин 0,1-0,2.The technical result is achieved by the fact that the ceramic mass for the manufacture of floor tiles, including clay, pegmatite, andesite, additionally contains quartz sand, carboxymethyl cellulose and glycerin, with the following ratio of components, wt.%: Clay 52.7-54.7; pegmatitis 27.0-31.0; andesite 8.0-12.0; silica sand 6.0-8.0; carboxymethyl cellulose 0.1-0.2; glycerol 0.1-0.2.

Технический результат достигается также тем, что керамическая масса для изготовлений напольной плитки, включающая глину, пегматит, андезит, отличается тем, что дополнительно содержит циркон, карбоксиметилцеллюлозу и глицерин при следующем соотношении компонентов, мас.%: глина 52,7-54,7; пегматит 27,0-31,0; андезит 8,0-12,0; циркон 6,0-8,0; карооксиметилцеллюлоза 0,1-0,2; глицерин 0,1-0,2.The technical result is also achieved in that the ceramic mass for the manufacture of floor tiles, including clay, pegmatite, andesite, is characterized in that it additionally contains zircon, carboxymethyl cellulose and glycerin in the following ratio of components, wt.%: Clay 52.7-54.7; pegmatitis 27.0-31.0; andesite 8.0-12.0; zircon 6.0-8.0; carboxymethyl cellulose 0.1-0.2; glycerol 0.1-0.2.

В таблицах приведены составы керамической массы для изготовления напольной плитки.The tables show the composition of the ceramic mass for the manufacture of floor tiles.

Таблица 1Table 1 КомпонентыComponents Состав, мас%Composition, wt% 1one 22 33 ГлинаClay 54,754.7 53,753.7 52,752.7 ПегматитPegmatite 27,027.0 29,029.0 31,031,0 АндезитAndesite 12,012.0 10,010.0 8,08.0 Кварцевый песокQuartz sand 6,06.0 7,07.0 8,08.0 КарбоксиметилцеллюлозаCarboxymethyl cellulose 0,10.1 0,150.15 0,20.2 Кварцевый песокQuartz sand 0,20.2 0,150.15 0,10.1 Истираемость, г/см² Abrasion, g / cm ² ~0,01~ 0.01 ~0,01~ 0.01 ~0,01~ 0.01

Таблица 2table 2 КомпонентыComponents Состав, мас%Composition, wt% 1one 22 33 ГлинаClay 54,754.7 53,753.7 52,752.7 ПегматитPegmatite 27,027.0 29,029.0 31,031,0 АндезитAndesite 12,012.0 10,010.0 8,08.0 Кварцевый песокQuartz sand 6,06.0 7,07.0 8,08.0 КарбоксиметилцеллюлозаCarboxymethyl cellulose 0,10.1 0,150.15 0,20.2 ЦирконZircon 0,20.2 0,120.12 0,10.1 Истираемость, г/см² Abrasion, g / cm ² ~0,01~ 0.01 ~0,01~ 0.01 ~0,01~ 0.01

В составе керамической массы используют любые качественные беложгущиеся глины.As part of the ceramic mass, any high-quality white-burning clay is used.

Компоненты дозируют в требуемых количествах, по отдельности размалывают (до прохождения через сетку 008), смешивают и готовят керамическую массу с влажностью 9-13%, из которой прессуют плитку полусухим способом. Плитку обжигают при температуре 1250-1280°C.The components are dosed in the required quantities, individually milled (before passing through the mesh 008), mixed and a ceramic mass with a moisture content of 9-13% is prepared, from which the tile is pressed semi-dry. The tile is fired at a temperature of 1250-1280 ° C.

Источники информацииInformation sources

1. BG 104264, 2001.1. BG 104264, 2001.

Claims

1. Ceramic mass for the manufacture of floor tiles, including clay, pegmatite, andesite, characterized in that it further comprises quartz sand, carboxymethyl cellulose and glycerin in the following ratio, wt.%:
clay 52.7-54.7 pegmatite 27.0-31.0 andesite 8.0-12.0 quartz sand 6.0-8.0 carboxymethyl cellulose 0.1-0.2 glycerol 0.1-0.2

2. Ceramic mass for the manufacture of floor tiles, including clay, pegmatite, andesite, characterized in that it further comprises zircon, carboxymethyl cellulose and glycerin in the following ratio, wt.%:
clay 52.7-54.7 pegmatite 27.0-31.0 andesite 8.0-12.0 zircon 6.0-8.0 carboxymethyl cellulose 0.1-0.2 glycerol 0.1-0.2