RU2018112714A - Зимние шины - Google Patents
Зимние шины Download PDFInfo
- Publication number
- RU2018112714A RU2018112714A RU2018112714A RU2018112714A RU2018112714A RU 2018112714 A RU2018112714 A RU 2018112714A RU 2018112714 A RU2018112714 A RU 2018112714A RU 2018112714 A RU2018112714 A RU 2018112714A RU 2018112714 A RU2018112714 A RU 2018112714A
- Authority
- RU
- Russia
- Prior art keywords
- phr
- mol
- polymer
- composition according
- resins
- Prior art date
Links
- 239000000203 mixture Substances 0.000 claims 20
- 229920000642 polymer Polymers 0.000 claims 19
- 239000007788 liquid Substances 0.000 claims 11
- 239000011347 resin Substances 0.000 claims 10
- 229920005989 resin Polymers 0.000 claims 10
- 239000005062 Polybutadiene Substances 0.000 claims 9
- 230000009477 glass transition Effects 0.000 claims 7
- 239000002174 Styrene-butadiene Substances 0.000 claims 6
- 229920002857 polybutadiene Polymers 0.000 claims 6
- 229920001195 polyisoprene Polymers 0.000 claims 6
- 229920003048 styrene butadiene rubber Polymers 0.000 claims 6
- 239000005011 phenolic resin Substances 0.000 claims 4
- 238000004073 vulcanization Methods 0.000 claims 4
- PPBRXRYQALVLMV-UHFFFAOYSA-N Styrene Chemical compound C=CC1=CC=CC=C1 PPBRXRYQALVLMV-UHFFFAOYSA-N 0.000 claims 3
- 125000000217 alkyl group Chemical group 0.000 claims 3
- 125000003118 aryl group Chemical group 0.000 claims 3
- MTAZNLWOLGHBHU-UHFFFAOYSA-N butadiene-styrene rubber Chemical compound C=CC=C.C=CC1=CC=CC=C1 MTAZNLWOLGHBHU-UHFFFAOYSA-N 0.000 claims 3
- 150000001993 dienes Chemical class 0.000 claims 3
- 239000007787 solid Substances 0.000 claims 3
- 239000011115 styrene butadiene Substances 0.000 claims 3
- 244000043261 Hevea brasiliensis Species 0.000 claims 2
- 239000013032 Hydrocarbon resin Substances 0.000 claims 2
- 239000003795 chemical substances by application Substances 0.000 claims 2
- 229920001577 copolymer Polymers 0.000 claims 2
- 229920006270 hydrocarbon resin Polymers 0.000 claims 2
- XMGQYMWWDOXHJM-UHFFFAOYSA-N limonene Chemical compound CC(=C)C1CCC(C)=CC1 XMGQYMWWDOXHJM-UHFFFAOYSA-N 0.000 claims 2
- 239000000178 monomer Substances 0.000 claims 2
- 229920003052 natural elastomer Polymers 0.000 claims 2
- 239000000025 natural resin Substances 0.000 claims 2
- 229920001194 natural rubber Polymers 0.000 claims 2
- 229920001568 phenolic resin Polymers 0.000 claims 2
- 239000012763 reinforcing filler Substances 0.000 claims 2
- GRWFGVWFFZKLTI-UHFFFAOYSA-N α-pinene Chemical compound CC1=CCC2C(C)(C)C1C2 GRWFGVWFFZKLTI-UHFFFAOYSA-N 0.000 claims 2
- WTARULDDTDQWMU-RKDXNWHRSA-N (+)-β-pinene Chemical compound C1[C@H]2C(C)(C)[C@@H]1CCC2=C WTARULDDTDQWMU-RKDXNWHRSA-N 0.000 claims 1
- WTARULDDTDQWMU-IUCAKERBSA-N (-)-Nopinene Natural products C1[C@@H]2C(C)(C)[C@H]1CCC2=C WTARULDDTDQWMU-IUCAKERBSA-N 0.000 claims 1
- CBXRMKZFYQISIV-UHFFFAOYSA-N 1-n,1-n,1-n',1-n',2-n,2-n,2-n',2-n'-octamethylethene-1,1,2,2-tetramine Chemical compound CN(C)C(N(C)C)=C(N(C)C)N(C)C CBXRMKZFYQISIV-UHFFFAOYSA-N 0.000 claims 1
- GRWFGVWFFZKLTI-IUCAKERBSA-N 1S,5S-(-)-alpha-Pinene Natural products CC1=CC[C@@H]2C(C)(C)[C@H]1C2 GRWFGVWFFZKLTI-IUCAKERBSA-N 0.000 claims 1
- PJEKFSKIOOHJNR-UHFFFAOYSA-N 1h-indene;styrene Chemical compound C=CC1=CC=CC=C1.C1=CC=C2CC=CC2=C1 PJEKFSKIOOHJNR-UHFFFAOYSA-N 0.000 claims 1
- RSWGJHLUYNHPMX-UHFFFAOYSA-N Abietic-Saeure Natural products C12CCC(C(C)C)=CC2=CCC2C1(C)CCCC2(C)C(O)=O RSWGJHLUYNHPMX-UHFFFAOYSA-N 0.000 claims 1
- ISWSIDIOOBJBQZ-UHFFFAOYSA-N Phenol Chemical compound OC1=CC=CC=C1 ISWSIDIOOBJBQZ-UHFFFAOYSA-N 0.000 claims 1
- WTARULDDTDQWMU-UHFFFAOYSA-N Pseudopinene Natural products C1C2C(C)(C)C1CCC2=C WTARULDDTDQWMU-UHFFFAOYSA-N 0.000 claims 1
- KHPCPRHQVVSZAH-HUOMCSJISA-N Rosin Natural products O(C/C=C/c1ccccc1)[C@H]1[C@H](O)[C@@H](O)[C@@H](O)[C@@H](CO)O1 KHPCPRHQVVSZAH-HUOMCSJISA-N 0.000 claims 1
- 230000003213 activating effect Effects 0.000 claims 1
- 229920006271 aliphatic hydrocarbon resin Polymers 0.000 claims 1
- -1 alkyl phenol-formaldehyde Chemical compound 0.000 claims 1
- XCPQUQHBVVXMRQ-UHFFFAOYSA-N alpha-Fenchene Natural products C1CC2C(=C)CC1C2(C)C XCPQUQHBVVXMRQ-UHFFFAOYSA-N 0.000 claims 1
- MVNCAPSFBDBCGF-UHFFFAOYSA-N alpha-pinene Natural products CC1=CCC23C1CC2C3(C)C MVNCAPSFBDBCGF-UHFFFAOYSA-N 0.000 claims 1
- 229930006722 beta-pinene Natural products 0.000 claims 1
- 239000011230 binding agent Substances 0.000 claims 1
- 229920001971 elastomer Polymers 0.000 claims 1
- LCWMKIHBLJLORW-UHFFFAOYSA-N gamma-carene Natural products C1CC(=C)CC2C(C)(C)C21 LCWMKIHBLJLORW-UHFFFAOYSA-N 0.000 claims 1
- 235000001510 limonene Nutrition 0.000 claims 1
- 229940087305 limonene Drugs 0.000 claims 1
- 150000003097 polyterpenes Chemical class 0.000 claims 1
- 239000005060 rubber Substances 0.000 claims 1
- 238000007789 sealing Methods 0.000 claims 1
- 150000003505 terpenes Chemical class 0.000 claims 1
- 235000007586 terpenes Nutrition 0.000 claims 1
- KHPCPRHQVVSZAH-UHFFFAOYSA-N trans-cinnamyl beta-D-glucopyranoside Natural products OC1C(O)C(O)C(CO)OC1OCC=CC1=CC=CC=C1 KHPCPRHQVVSZAH-UHFFFAOYSA-N 0.000 claims 1
- 229920002554 vinyl polymer Polymers 0.000 claims 1
Classifications
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
- C08L9/00—Compositions of homopolymers or copolymers of conjugated diene hydrocarbons
- C08L9/06—Copolymers with styrene
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
- B29B—PREPARATION OR PRETREATMENT OF THE MATERIAL TO BE SHAPED; MAKING GRANULES OR PREFORMS; RECOVERY OF PLASTICS OR OTHER CONSTITUENTS OF WASTE MATERIAL CONTAINING PLASTICS
- B29B7/00—Mixing; Kneading
- B29B7/02—Mixing; Kneading non-continuous, with mechanical mixing or kneading devices, i.e. batch type
- B29B7/06—Mixing; Kneading non-continuous, with mechanical mixing or kneading devices, i.e. batch type with movable mixing or kneading devices
- B29B7/10—Mixing; Kneading non-continuous, with mechanical mixing or kneading devices, i.e. batch type with movable mixing or kneading devices rotary
- B29B7/18—Mixing; Kneading non-continuous, with mechanical mixing or kneading devices, i.e. batch type with movable mixing or kneading devices rotary with more than one shaft
- B29B7/183—Mixing; Kneading non-continuous, with mechanical mixing or kneading devices, i.e. batch type with movable mixing or kneading devices rotary with more than one shaft having a casing closely surrounding the rotors, e.g. of Banbury type
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
- B29B—PREPARATION OR PRETREATMENT OF THE MATERIAL TO BE SHAPED; MAKING GRANULES OR PREFORMS; RECOVERY OF PLASTICS OR OTHER CONSTITUENTS OF WASTE MATERIAL CONTAINING PLASTICS
- B29B7/00—Mixing; Kneading
- B29B7/30—Mixing; Kneading continuous, with mechanical mixing or kneading devices
- B29B7/34—Mixing; Kneading continuous, with mechanical mixing or kneading devices with movable mixing or kneading devices
- B29B7/38—Mixing; Kneading continuous, with mechanical mixing or kneading devices with movable mixing or kneading devices rotary
- B29B7/46—Mixing; Kneading continuous, with mechanical mixing or kneading devices with movable mixing or kneading devices rotary with more than one shaft
- B29B7/48—Mixing; Kneading continuous, with mechanical mixing or kneading devices with movable mixing or kneading devices rotary with more than one shaft with intermeshing devices, e.g. screws
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
- B29B—PREPARATION OR PRETREATMENT OF THE MATERIAL TO BE SHAPED; MAKING GRANULES OR PREFORMS; RECOVERY OF PLASTICS OR OTHER CONSTITUENTS OF WASTE MATERIAL CONTAINING PLASTICS
- B29B7/00—Mixing; Kneading
- B29B7/30—Mixing; Kneading continuous, with mechanical mixing or kneading devices
- B29B7/34—Mixing; Kneading continuous, with mechanical mixing or kneading devices with movable mixing or kneading devices
- B29B7/38—Mixing; Kneading continuous, with mechanical mixing or kneading devices with movable mixing or kneading devices rotary
- B29B7/46—Mixing; Kneading continuous, with mechanical mixing or kneading devices with movable mixing or kneading devices rotary with more than one shaft
- B29B7/48—Mixing; Kneading continuous, with mechanical mixing or kneading devices with movable mixing or kneading devices rotary with more than one shaft with intermeshing devices, e.g. screws
- B29B7/485—Mixing; Kneading continuous, with mechanical mixing or kneading devices with movable mixing or kneading devices rotary with more than one shaft with intermeshing devices, e.g. screws with three or more shafts provided with screws
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
- B29B—PREPARATION OR PRETREATMENT OF THE MATERIAL TO BE SHAPED; MAKING GRANULES OR PREFORMS; RECOVERY OF PLASTICS OR OTHER CONSTITUENTS OF WASTE MATERIAL CONTAINING PLASTICS
- B29B7/00—Mixing; Kneading
- B29B7/30—Mixing; Kneading continuous, with mechanical mixing or kneading devices
- B29B7/58—Component parts, details or accessories; Auxiliary operations
- B29B7/60—Component parts, details or accessories; Auxiliary operations for feeding, e.g. end guides for the incoming material
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
- B29B—PREPARATION OR PRETREATMENT OF THE MATERIAL TO BE SHAPED; MAKING GRANULES OR PREFORMS; RECOVERY OF PLASTICS OR OTHER CONSTITUENTS OF WASTE MATERIAL CONTAINING PLASTICS
- B29B7/00—Mixing; Kneading
- B29B7/74—Mixing; Kneading using other mixers or combinations of mixers, e.g. of dissimilar mixers ; Plant
- B29B7/7461—Combinations of dissimilar mixers
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
- B29B—PREPARATION OR PRETREATMENT OF THE MATERIAL TO BE SHAPED; MAKING GRANULES OR PREFORMS; RECOVERY OF PLASTICS OR OTHER CONSTITUENTS OF WASTE MATERIAL CONTAINING PLASTICS
- B29B7/00—Mixing; Kneading
- B29B7/74—Mixing; Kneading using other mixers or combinations of mixers, e.g. of dissimilar mixers ; Plant
- B29B7/7476—Systems, i.e. flow charts or diagrams; Plants
- B29B7/7485—Systems, i.e. flow charts or diagrams; Plants with consecutive mixers, e.g. with premixing some of the components
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
- B29B—PREPARATION OR PRETREATMENT OF THE MATERIAL TO BE SHAPED; MAKING GRANULES OR PREFORMS; RECOVERY OF PLASTICS OR OTHER CONSTITUENTS OF WASTE MATERIAL CONTAINING PLASTICS
- B29B7/00—Mixing; Kneading
- B29B7/74—Mixing; Kneading using other mixers or combinations of mixers, e.g. of dissimilar mixers ; Plant
- B29B7/7476—Systems, i.e. flow charts or diagrams; Plants
- B29B7/7495—Systems, i.e. flow charts or diagrams; Plants for mixing rubber
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
- B29B—PREPARATION OR PRETREATMENT OF THE MATERIAL TO BE SHAPED; MAKING GRANULES OR PREFORMS; RECOVERY OF PLASTICS OR OTHER CONSTITUENTS OF WASTE MATERIAL CONTAINING PLASTICS
- B29B7/00—Mixing; Kneading
- B29B7/80—Component parts, details or accessories; Auxiliary operations
- B29B7/88—Adding charges, i.e. additives
- B29B7/90—Fillers or reinforcements, e.g. fibres
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B60—VEHICLES IN GENERAL
- B60C—VEHICLE TYRES; TYRE INFLATION; TYRE CHANGING; CONNECTING VALVES TO INFLATABLE ELASTIC BODIES IN GENERAL; DEVICES OR ARRANGEMENTS RELATED TO TYRES
- B60C1/00—Tyres characterised by the chemical composition or the physical arrangement or mixture of the composition
- B60C1/0016—Compositions of the tread
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
- C08L7/00—Compositions of natural rubber
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
- C08L9/00—Compositions of homopolymers or copolymers of conjugated diene hydrocarbons
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
- B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
- B29C48/00—Extrusion moulding, i.e. expressing the moulding material through a die or nozzle which imparts the desired form; Apparatus therefor
- B29C48/022—Extrusion moulding, i.e. expressing the moulding material through a die or nozzle which imparts the desired form; Apparatus therefor characterised by the choice of material
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
- B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
- B29C48/00—Extrusion moulding, i.e. expressing the moulding material through a die or nozzle which imparts the desired form; Apparatus therefor
- B29C48/25—Component parts, details or accessories; Auxiliary operations
- B29C48/285—Feeding the extrusion material to the extruder
- B29C48/288—Feeding the extrusion material to the extruder in solid form, e.g. powder or granules
- B29C48/2888—Feeding the extrusion material to the extruder in solid form, e.g. powder or granules in thread form or in strip form, e.g. rubber strips
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
- B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
- B29C48/00—Extrusion moulding, i.e. expressing the moulding material through a die or nozzle which imparts the desired form; Apparatus therefor
- B29C48/25—Component parts, details or accessories; Auxiliary operations
- B29C48/36—Means for plasticising or homogenising the moulding material or forcing it through the nozzle or die
- B29C48/375—Plasticisers, homogenisers or feeders comprising two or more stages
- B29C48/385—Plasticisers, homogenisers or feeders comprising two or more stages using two or more serially arranged screws in separate barrels
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
- B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
- B29C48/00—Extrusion moulding, i.e. expressing the moulding material through a die or nozzle which imparts the desired form; Apparatus therefor
- B29C48/25—Component parts, details or accessories; Auxiliary operations
- B29C48/36—Means for plasticising or homogenising the moulding material or forcing it through the nozzle or die
- B29C48/50—Details of extruders
- B29C48/76—Venting, drying means; Degassing means
- B29C48/765—Venting, drying means; Degassing means in the extruder apparatus
- B29C48/766—Venting, drying means; Degassing means in the extruder apparatus in screw extruders
- B29C48/767—Venting, drying means; Degassing means in the extruder apparatus in screw extruders through a degassing opening of a barrel
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
- C08K3/00—Use of inorganic substances as compounding ingredients
- C08K3/02—Elements
- C08K3/04—Carbon
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
- C08K3/00—Use of inorganic substances as compounding ingredients
- C08K3/34—Silicon-containing compounds
- C08K3/36—Silica
Landscapes
- Chemical & Material Sciences (AREA)
- Engineering & Computer Science (AREA)
- Mechanical Engineering (AREA)
- Health & Medical Sciences (AREA)
- Chemical Kinetics & Catalysis (AREA)
- Medicinal Chemistry (AREA)
- Polymers & Plastics (AREA)
- Organic Chemistry (AREA)
- Compositions Of Macromolecular Compounds (AREA)
- Tires In General (AREA)
Claims (44)
1. Вулканизуемая эластомерная композиция для зимних шин, включающая в свой состав, по меньшей мере,
одно количество Х, равное, по меньшей мере, 1 phr (массовых частей на 100 массовых частей каучука), по меньшей мере, одного жидкого полимера (А), выбранного из жидкого полибутадиена, жидкого полиизопрена и/или их смесей,
одно количество Y, равное, по меньшей мере, 4 phr, по меньшей мере, одной смолы (В),
100 phr смеси твердых диеновых эластомерных полимеров (D),
где упомянутая смесь (D) содержит:
от 0 до 95 phr, предпочтительно от 20 до 95 phr, по меньшей мере, одного стирол-бутадиенового полимера (SBR),
от 0 до 95 phr, предпочтительно от 0 до 60 phr, по меньшей мере, одного полибутадиенового полимера (BR), и
от 5 до 100 phr, предпочтительно от 5 до 80 phr, по меньшей мере, одного полиизопренового полимера (IR), по меньшей мере, 10 phr, по меньшей мере, одного армирующего наполнителя (Е), и
0,05 phr, по меньшей мере, одного вулканизирующего агента (F).
2. Композиция по п. 1, включающая в свой состав, по меньшей мере
одно количество X, по меньшей мере, одного жидкого полимера (A), составляющее, по меньшей мере, 3 phr или 5 phr или 10 phr или 15 phr или 20 phr; и/или менее 70 phr, или менее 60 phr, или менее 50 phr; и/или составляющее от 1 до 70 phr или от 3 до 70 phr или от 5 до 60 phr или от 5 до 50 phr или от 5 до 40 phr или от 5 до 30 phr; и/или
одно количество Y, по меньшей мере, одной смолы (B), составляющее, по меньшей мере, 5 phr или 7 phr или 11 phr; и/или менее 40 phr или 30 phr или 25 phr или 20 phr или 15 phr; и/или составляющее от 4 до 40 phr или от 4 до 30 phr или от 4 до 25 phr или от 5 до 30 phr или от 5 до 25 phr или от 5 до 20 phr или от 5 до 15 phr или от 11 до 40 phr или от 11 до 30 phr или от 11 до 25 phr или от 11 до 20 phr или от 11 до 15 phr; и/или
возможно, одно количество Z, по меньшей мере, одного пластифицирующего масла (C), составляющее, по меньшей мере, 1 phr или 5 phr или 10 phr; и/или менее 70 phr или 60 phr или 50 phr; и/или составляющее от 0 до 70 phr или от 0 до 60 phr или от 0 до 50 phr или от 5 до 70 phr или от 10 до 60 phr или от 15 до 50 phr, и/или
по меньшей мере, 20 phr или 30 или 40 phr или 50 phr; и/или не более 150 phr или 140 phr или 130 phr или 120 phr или 110 phr или 100 phr; и/или составляющее от 10 до 150 phr или от 30 до 120 phr или от 50 до 120 phr или от 70 до 110 phr или от 80 до 100 phr, по меньшей мере, одного армирующего наполнителя (E).
3. Композиция по п. 1 или 2, включающая в свой состав одно количество Y, по меньшей мере, одной смолы (B), составляющее, по меньшей мере, 11 phr.
4. Композиция по любому из предшествующих пунктов, где
упомянутый жидкий полимер (А) характеризуется среднемассовой молекулярной массой (
) не более 80000 г/моль, и/или температурой стеклования (Tg) ниже 0°С, предпочтительно среднемассовой молекулярной массой (), составляющей от 500 до 80000 г/моль, более предпочтительно от 500 до 60000 г/моль, и/или температурой стеклования (Tg), находящейся в диапазоне от -105°С до 0°С, более предпочтительно от -100°С до -50°С;
упомянутая смола (В) характеризуется среднемассовой молекулярной массой (), составляющей от 200 до 3000 г/моль, предпочтительно от 500 до 3000 г/моль, и/или температурой стеклования (Tg) выше 0°С, предпочтительно выше 25°С, и/или температурой размягчения (Tm) выше 25°С, предпочтительно находящейся в диапазоне от 50 до 160°С или от 80°С до 140°С, в случае жидкой смолы (В), ниже 25°С, предпочтительно ниже 0°С, ниже -10°С, или ниже -25°С.
5. Композиция по любому из предшествующих пунктов, где, по меньшей мере, один жидкий полимер (А) выбирают из числа
жидких полибутадиеновых полимеров, характеризующихся посредством (), составляющей от 500 до 30000 г/моль, предпочтительно от 1000 до 20000 г/моль, и/или температурой стеклования (Tg) от -105°С до 0°С, предпочтительно от -95°С до -50°С; и/или
жидких полиизопреновых полимеров, характеризующихся посредством (), составляющей от 3000 до 80000 г/моль, предпочтительно от 10000 до 60000 г/моль, и/или температурой стеклования (Tg), находящейся в диапазоне от -70°С до -30°С.
6. Композиция по любому из предшествующих пунктов, где, по меньшей мере, одну смолу (В) выбирают из числа
углеводородных смол, предпочтительно из числа углеводородных смол, полученных из кумарон-инденовых, стирол-инденовых, стирол-алкилстирольных, и алифатических углеводородных смол, предпочтительно имеющих среднемассовую молекулярную массу, составляющую от 500 до 3000 г/моль, более предпочтительно от 700 до 1500 г/моль; и/или
фенольных смол, предпочтительно из числа смол основе алкилфенол-формальдегида, алкилфенольных смол, модифицированных канифолью, смол на основе алкилфенол-ацетилена, модифицированных алкилфенольных смол и смол на основе терпен-фенола; и/или
природных смол, предпочтительно из числа политерпеновых природных смол, выбранных из числа гомо- или сополимеров альфа-пинена, бета-пинена, лимонена, и винилароматических мономеров (стирола) и/или ароматических мономеров (фенола), предпочтительно имеющих температуру стеклования (Tg) выше 25°С, и/или температуру размягчения (Tm), находящуюся в диапазоне от 50°С до 150°С, и/или среднемассовую молекулярную массу, составляющую от 500 до 3000 г/моль; и/или природных смол на основе канифоли.
7. Композиция по любому из предшествующих пунктов, дополнительно включающая в свой состав, по меньшей мере, одно пластифицирующее масло (С), предпочтительно характеризующееся среднемассовой молекулярной массой () не выше 600 г/моль, или, в случае пластифицирующего масла класса RAE (Остаточный ароматический экстракт), среднемассовой молекулярной массой, составляющей от 400 до 10000 г/моль, и/или температурой стеклования (Tg) ниже -30°C.
8. Композиция по любому из предшествующих пунктов, где, по меньшей мере, один жидкий полимер (А) представляет собой жидкий полибутадиен, и/или, по меньшей мере, одна смола (В) представляет собой терпен/стирольный сополимер, и/или возможное, по меньшей мере, одно пластифицирующее масло (С) представляет собой масло TDAE (очищенный дистиллированный ароматический экстракт).
9. Композиция по любому из предшествующих пунктов, где смесь (D) твердых диеновых эластомерных полимеров включает в свой состав
от 40 до 90 phr, по меньшей мере, одного стирол-бутадиенового полимера (SBR),
от 0 до 50 phr, по меньшей мере, одного полибутадиенового полимера (BR), и
от 10 до 60 phr, по меньшей мере, одного полиизопренового полимера (IR), или
от 0 до 50 phr, по меньшей мере, одного стирол-бутадиенового полимера (SBR),
от 30 до 80 phr, по меньшей мере, одного полибутадиенового полимера (BR), и
от 20 до 70 phr, по меньшей мере, одного полиизопренового полимера (IR).
10. Композиция по любому из предшествующих пунктов, где упомянутый твердый диеновый эластомерный полиизопреновый полимер (IR) представляет собой натуральный каучук (NR).
11. Композиция по любому из предшествующих пунктов, дополнительно включающая в свой состав
от 0,5 до 10 phr, по меньшей мере, одного активирующего агента для вулканизации; и/или
от 0,05 до 10 phr, по меньшей мере, одного ускорителя для вулканизации; и/или
от 0,05 до 2 phr, по меньшей мере, одного замедлителя для вулканизации; и/или
от 0,1 до 20 phr, по меньшей мере, одного связывающего агента (G).
12. Элемент для зимних шин, включающий в себя эластомерную композицию, полученную с использованием вулканизуемой эластомерной композиции по любому из предшествующих пп. 1-11.
13. Зимняя шина для транспортных средств, включающая элемент шины, содержащий вулканизованную эластомерную композицию, полученную в результате вулканизации вулканизуемой эластомерной композиции по любому из пп. 1-11.
14. Элемент по п. 12 или шина по п. 13, где упомянутый элемент не является крайним в направлении вовнутрь слоем (герметизирующим слоем).
15. Элемент по п. 12 или 14 или шина по п. 13 или 14, где упомянутый элемент представляет собой протекторный браслет.