RU2008107689A - ARMORED HEAT RESISTANT WELDABLE MARTENSITY STEEL - Google Patents
ARMORED HEAT RESISTANT WELDABLE MARTENSITY STEEL Download PDFInfo
- Publication number
- RU2008107689A RU2008107689A RU2008107689/02A RU2008107689A RU2008107689A RU 2008107689 A RU2008107689 A RU 2008107689A RU 2008107689/02 A RU2008107689/02 A RU 2008107689/02A RU 2008107689 A RU2008107689 A RU 2008107689A RU 2008107689 A RU2008107689 A RU 2008107689A
- Authority
- RU
- Russia
- Prior art keywords
- molybdenum
- manganese
- phosphorus
- sulfur
- nickel
- Prior art date
Abstract
1. Броневая термостойкая свариваемая мартенситная сталь, содержащая углерод, кремний, марганец, хром, никель, молибден, серу, фосфор и железо, отличающаяся тем, что она дополнительно содержит кобальт и медь при следующем соотношении содержаний компонентов, мас.%: ! Углерод0,001-0,41Кремний0,1-2,6Марганец0,1-1,8Хром0,1-8,6Никель0,1-1,9Молибден0,1-0,6Кобальт0,05-4,6Медь0,1-1,9СераНе более 0,004ФосфорНе более 0,008ЖелезоОстальное ! 2. Броневая термостойкая свариваемая мартенситная сталь по п.1, отличающаяся тем, что при содержании углерода не более 0,15%, она имеет следующее соотношение компонентов, мас.%: ! Кремний0,1-0,8Марганец0,6-1,8Хром0,6-8,6Никель1,2-1,9Молибден0,3-0,6Кобальт0,05-1,9Медь0,9-1,9СераНе более 0,004ФосфорНе более 0,008ЖелезоОстальное ! 3. Броневая термостойкая свариваемая мартенситная сталь по п.1, отличающаяся тем, что при содержании углерода более 0,15%, она имеет следующее соотношение компонентов, мас.%: ! Кремний0,6-2,6Марганец0,1-0,7Хром0,1-0,5Никель0,1-1,6Молибден0,1-0,3КобальтНе менее 2,0Медь0,1-0,8СераНе более 0,004ФосфорНе более 0,008ЖелезоОстальное1. Armored heat-resistant welded martensitic steel containing carbon, silicon, manganese, chromium, nickel, molybdenum, sulfur, phosphorus and iron, characterized in that it additionally contains cobalt and copper in the following ratio of components, wt.%:! Carbon 0.001-0.41 Silicon 0.1-2.6 Manganese 0.1-1.8 Chrome 0.1-8.6 Nickel 0.1-1.9 Molybdenum 0.1-0.6 Cobalt 0.05-4.6 Copper 0.1-1.9 Sulfur Not more than 0.004 Phosphorus Not more than 0.008 Iron 2. Armored heat-resistant welded martensitic steel according to claim 1, characterized in that when the carbon content is not more than 0.15%, it has the following ratio of components, wt.%:! Silicon 0.1-0.8 Manganese 0.6-1.8 Chromium 0.6-8.6 Nickel 1.2-1.9 Molybdenum 0.3-0.6 Cobalt 0.05-1.9 Copper 0.9-1.9 Sulfur Not more than 0.004 Phosphorus Not more than 0.008 Iron Remaining! 3. Armored heat-resistant welded martensitic steel according to claim 1, characterized in that when the carbon content is more than 0.15%, it has the following ratio of components, wt.%:! Silicon 0.6-2.6 Manganese 0.1-0.7 Chromium 0.1-0.5 Nickel 0.1-1.6 Molybdenum 0.1-0.3 Cobalt Not less than 2.0 Copper 0.1-0.8 Sulfur Not more than 0.004 Phosphorus Not more than 0.008 Iron Other
Claims (3)