KR870009036A - 펄라이트 함량이 높은 주철의 제조공정 - Google Patents

펄라이트 함량이 높은 주철의 제조공정 Download PDF

Info

Publication number
KR870009036A
KR870009036A KR870002274A KR870002274A KR870009036A KR 870009036 A KR870009036 A KR 870009036A KR 870002274 A KR870002274 A KR 870002274A KR 870002274 A KR870002274 A KR 870002274A KR 870009036 A KR870009036 A KR 870009036A
Authority
KR
South Korea
Prior art keywords
pearlite
stabilizer
cast iron
casing
content according
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
KR870002274A
Other languages
English (en)
Other versions
KR910001353B1 (ko
Inventor
이포 헤니치
Original Assignee
마리안네 스치라귀, 루돌프 링크
게오르그 피셔 악티엔 게젤샤프트
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 마리안네 스치라귀, 루돌프 링크, 게오르그 피셔 악티엔 게젤샤프트 filed Critical 마리안네 스치라귀, 루돌프 링크
Publication of KR870009036A publication Critical patent/KR870009036A/ko
Application granted granted Critical
Publication of KR910001353B1 publication Critical patent/KR910001353B1/ko
Expired legal-status Critical Current

Abstract

내용 없음

Description

펄라이트 함량이 높은 주철의 제조공정
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음

Claims (20)

  1. 펄라이트 함량이 높은 주철의 제조를 위해 용기에서 주철융체를 제조하고, 상기 융체를 주조주형에 이동하며, 이동하는 동안에 펄라이트 안정화제를 상기 융체에 첨가하는 것을 특징으로 하는 펄라이트 함량이 높은 주철의 제조공정.
  2. 제 1항에 있어서, 상기 펄라이트 안정화제가 상기 융체의 주입흐름에 첨가되는 것을 특징으로 하는 펄라이트 함량이 높은 주철의 제조공정.
  3. 제 1항에 있어서, 상기 펄라이트 안정화제가 주석을 구성함을 특징으로 하는 펄라이트 함량이 높은 주철의 제조공정.
  4. 제 1항에 있어서, 상기 펄라이트 안정화제가 안티몬을 구성함을 특징으로 하는 펄라이트 함량이 높은 주철의 제조공정.
  5. 제 1항에 있어서, 상기 펄라이트 안정화제가 펄라이트 안정화물질과 접종제를 구성함을 특징으로 하는 펄라이트 함량이 높은 주철의 제조공정.
  6. 제 1항에 있어서, 상기 펄라이트 안정화제가 와이어형상임을 특징으로 하는 펄라이트 함량이 높은 주철의 제조공정.
  7. 제 1항에 있어서, 상기 펄라이트 안정화제가 분말형상임을 특징으로 하는 펄라이트 함량이 높은 주철의 제조공정.
  8. 제 1항에 있어서, 상기 펄라이트 안정화제가 금속 또는 비금속으로 된 케이싱으로 둘러싸인 분말상의 펄라이트 안정화물질을 구성하는 와이어형상임을 특징으로 하는 펄라이트 함량이 높은 주철의 제조공정.
  9. 제 1항에 있어서, 상기 펄라이트 안정화제가 금속 또는 비금속으로 된 케이싱으로 둘러싸인 분말상의 펄라이트 안정화물질과 접종제를 구성하는 와이어형상임을 특징으로 하는 펄라이트 함량이 높은 주철의 제조공정.
  10. 제 1항에 있어서, 상기 펄라이트 안정화제가 펄라이트 안정화제로 된 케이싱으로 둘러싸인 접종제를 구성함을 특징으로 하는 펄라이트 함량이 높은 주철의 제조공정.
  11. 제 1항에 있어서, 상기 펄라이트 안정화제가 케이싱과 케이싱에 층으로 인가된 펄라이트 안정화물질로 둘러싸인 분말상의 접종제를 구성함을 특징으로 하는 펄라이트 함량이 높은 주철의 제조공정.
  12. 제 1항에 있어서, 상기 펄라이트 안정화제가 분말상의 접종제에 매립된 와이어형상의 펄라이트 안정화물질을 구성하고, 상기 분말이 케이싱으로 둘러싸여 있음을 특징으로 하는 펄라이트 함량이 높은 주철의 제조공정.
  13. 제 1항에 있어서, 상기 펄라이트 함량이 높은 주철이 GG,GGG, 또는 GGV주철을 구성함을 특징으로 하는 펄라이트 함량이 높은 주철의 제조공정.
  14. 펄라이트 함량이 높은 주철의 제조를 위해 용기에서 주철융체를 제조하고, 상기 융체를 주조주형에 이동하며, 이동하는 동안에 펄라이트 안정화제를 상기 융체에 첨가하고, 상기 펄라이트 안정화제가 주석과 안티몬으로 구성된 군에서 선택됨을 특징으로 하는 펄라이트 함량이 높은 주철의 제조공정.
  15. 제 13항에 있어서, 상기 펄라이트 안정화제가 상기 융체의 주입흐름에 첨가되는 것을 특징으로 하는 펄라이트 함량이 높은 주철의 제조공정.
  16. 케이싱으로 둘러싸인 분말상의 펄라이트 안정화물질을 구성하고, 상기 펄라이트 안정화물질이 주석과 안티몬으로 구성된 군에서 선택됨을 특징으로 하는 와이어형상의 펄라이트 안정화제.
  17. 제 16항에 있어서, 상기 케이싱으로 둘러 사인 분말상의 접종제를 더 구성함을 특징으로 하는 와이어형상의 펄라이트 안정화제.
  18. 주석과 안티몬으로 구성된 군에서 선택한 펄라이트 안정화물질로 만든 케이싱으로 둘러싸인 분말상의 접종제를 구성함을 특징으로 하는 와이어형상의 펄라이트 안정화제.
  19. 케이싱으로 둘러싸인 분말상의 접종제와 상기 케이싱에 층으로서 인가된 펄라이트 안정화물질을 구성하고, 상기 펄라이트 안정화물질이 주석과 안티몬으로 군에서 선택됨을 특징으로 하는 와이어형상의 펄라이트 안정화제.
  20. 케이싱으로 둘러싸인 분말상 접종제에 매립된 와이어형상의 펄라이트 안정화물질을 구성하고, 상기 펄라이트 안정화물질이 주석과 안티몬으로 구성된 군에서 선택됨을 특징으로 하는 와이어형상의 펄라이트 안정화제.
    ※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.
KR1019870002274A 1986-03-20 1987-03-13 펄라이트 함량이 높은 주철의 제조방법 Expired KR910001353B1 (ko)