KR101700640B1 - Manufacturing Method for Multi-Color Aqueous Paint Composition, Multi-Color Aqueous Paint Composition thereof and Coating Method Using the Same - Google Patents
Manufacturing Method for Multi-Color Aqueous Paint Composition, Multi-Color Aqueous Paint Composition thereof and Coating Method Using the Same Download PDFInfo
- Publication number
- KR101700640B1 KR101700640B1 KR1020160122137A KR20160122137A KR101700640B1 KR 101700640 B1 KR101700640 B1 KR 101700640B1 KR 1020160122137 A KR1020160122137 A KR 1020160122137A KR 20160122137 A KR20160122137 A KR 20160122137A KR 101700640 B1 KR101700640 B1 KR 101700640B1
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- water
- paint
- pigment
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
본 발명은 수성 다채 무늬 도료 조성물의 제조방법 및 그 수성 다채 무늬 도료 조성물과 이를 이용한 천연석 입체 무늬 도장방법에 관한 것으로서, 본 발명에 따른 수성 다채 무늬 도료 조성물의 제조방법은 합성 실리카 증점제와 수용성 입자 침강 방지제와 물을 혼합하여 제조되는 수상 겔 50.0~60.0중량%에 수용성 다채 무늬 도료 입자 형성용 페이스트와 안료 페이스트를 혼합하여 제조되는 천연석 칼라 도료 40.0~50.0중량%를 혼합하고, 상하 이동하는 메시 망을 이용하여 천연석 칼라 도료가 3~8mm의 크기를 가지도록 절단하여 분산시키는 것으로 구성되며, 본 발명에 따르면 다양한 종류의 아름다운 색상과 무늬를 지니는 천연 화강석 또는 대리석과 같은 고급스러운 패턴과 질감을 다양한 자유도로 경제적 및 효율적으로 연출할 수가 있음과 아울러, 통상적인 도장 장치를 이용하여 간단하고 용이하게 도장할 수가 있고, 높은 저장 안정성과 부착력을 지니며, 수성제품유기 용제의 함량이 낮아 인체 유해성이 적고 보다 친환경적이다.The present invention relates to a process for producing an aqueous color pattern coating composition, a water-based colorful pattern coating composition and a natural stone three-dimensional pattern coating method using the same, 40.0 to 50.0% by weight of a natural stone color paint prepared by mixing a water-soluble coloring agent particle-forming paste and a pigment paste in an amount of 50.0 to 60.0% by weight of an aqueous gel prepared by mixing an inhibitor and water, The granite color paint is cut and dispersed to have a size of 3 to 8 mm. According to the present invention, it is possible to produce a luxurious pattern and texture such as natural granite or marble having various kinds of beautiful colors and patterns, Economically and efficiently. In addition, And a number of simple and easily painted by using a coating device, said Genie high storage stability and adhesive strength, low hazard body the content of the water-based product the organic solvent is less than environmentally friendly.
Description
본 발명은 수성 다채 무늬 도료 조성물의 제조방법 및 그 수성 다채 무늬 도료 조성물과 이를 이용한 천연석 입체 무늬 도장방법에 관한 것이며, 더욱 상세하게는 다양한 종류의 아름다운 색상과 무늬를 지니는 천연 화강석 또는 대리석과 같은 고급스러운 패턴과 질감을 경제적 및 효율적으로 연출할 수가 있음과 아울러, 통상적인 도장 장치를 이용하여 간단하고 용이하게 도장할 수가 있고, 높은 저장 안정성과 부착력을 지니며, 수성제품유기 용제의 함량이 낮아 인체 유해성이 적어 친환경적인 수성 다채 무늬 도료 조성물의 제조방법 및 그 수성 다채 무늬 도료 조성물과 이를 이용한 천연석 입체 무늬 도장방법에 관한 것이다.The present invention relates to a process for producing an aqueous multicolor paint composition, an aqueous multicolor paint composition and a method for coating a natural stone multicolor pattern using the same, and more particularly, to a process for producing a watercolor multicolor paint composition using natural granite or marble It is possible to economically and efficiently produce a desired pattern and texture and can easily and easily paint using a conventional coating device and has a high storage stability and adhesion ability and has a low content of an aqueous organic solvent, This invention relates to a process for producing an environmentally friendly aqueous multicolor paint composition and an aqueous multicolor paint composition and a method for coating natural stone multicolor using the same.
일반적으로 건축물에 품격 있는 고급스러운 멋을 부여할 목적으로 건축물의 고급 내장 및/또는 외장 마감재로서 고가의 천연 대리석이나 화강석 등이 널리 사용되어 왔으며, 이러한 천연 대리석이나 화강석은 다양한 종류의 아름다운 색상과 무늬패턴을 보유하므로 높은 장식성과 고품격감을 가지는 분위기를 연출한다.In general, expensive natural marble or granite has been widely used as an interior decoration and / or an exterior finish of a building for the purpose of giving a luxurious style to a building. Such natural marble or granite has various kinds of beautiful colors and patterns So that it creates an atmosphere with high ornamental quality and high quality feeling.
그러나 천연 대리석이나 화강석을 이용한 건축물의 내장 및/또는 외장 마감은 재료 자체가 고가일 뿐만 아니라 중량물이므로 운송 및 시공 비용이 많이 소요된다는 문제점이 있다.However, the interior and / or exterior finishing of buildings using natural marble or granite is not only expensive but also heavy, which requires a lot of transportation and construction costs.
따라서 종래로부터 건축물의 내장 및/또는 외장 마감 장식성을 높이기 위한 경제적인 방안의 하나로서, 천연 대리석이나 화강석과 같은 아름답고 자연스러운 색상 및 문양과 질감을 나타낼 수 있는 수중유적형, 수중수적형, 또는 에멀전 수적형의 다양한 다채 무늬 도료가 제안되어 왔다.Accordingly, as one of the economical measures for enhancing the decorative property of the built-in and / or exterior finish of a building, there has been proposed an artificial marble, granite, A variety of colorful patterned paints have been proposed.
일반적으로 다채 무늬 도료는 수용액 중에 유성 도료를 입자 상태로 분산시켜 놓은 도료를 일컬으며, 다양한 색상의 유성 입자를 하나의 수용액 중에 분산시킨 것으로서, 통상적으로 수용액:유성 입자의 비율이 중량비 4:6~6:4의 범위로 제조되며, 다채 무늬 도료에서 소지(素地) 은폐력을 발휘하는 것은 유성 입자이므로 도장 면적 범위는 유성 입자의 혼입량에 의존적이다.In general, a multi-pattern paint is a paint in which the oil-based paint is dispersed in the form of particles in an aqueous solution. Oil-based particles of various colors are dispersed in one aqueous solution. Usually, the ratio of aqueous solution: 6: 4, and the coating area range depends on the amount of the oily particles to be mixed because the oily particles exhibit the hiding power in the color pattern paint.
여기서, 수중유적형 다채 무늬 도료는 외부상인 수성졸에 내부상인 유기용제를 분산시켜 제조되며, 유기용제를 상당량 포함하므로 휘발성 유기 화합물로 인하여 인체에 유해하고, 작업성 및 저장성과 부착력이 열등하다는 단점이 있다.Here, the underwater type multi-pattern paint is produced by dispersing the organic solvent in the aqueous phase, which is an external phase, and contains a considerable amount of organic solvent, which is harmful to the human body due to volatile organic compounds, .
상기한 수중유적형 다채 무늬 도료의 단점을 해소하고자 에멀젼 수적형 다채 무늬 도료가 제안되었으며, 외부상으로서의 에멀젼화된 졸에 내부상으로서의 수성겔을 분산시켜 제조되는 에멀젼 수적형 다채 무늬 도료는 휘발성 유기 화합물 함량이 적어 인체에 덜 유해하고 저장성이 우수하다는 장점은 있으나, 도장을 위해서는 특수건인 더블 노즐건을 이용하여 도장하여야 하고 점도 조절이 곤란하여 일정한 무늬 패턴을 형성하기 곤란하다는 문제점이 있다.In order to overcome the disadvantages of the above-mentioned underwater type multi-patterned paint, an emulsion watercolor pattern paint has been proposed. An emulsion watercolor pattern paint prepared by dispersing an aqueous gel as an internal phase on an emulsified sol as an external phase has a volatile organic It is less harmful to the human body and has excellent storage stability. However, it is difficult to control the viscosity by using a double nozzle gun which is a special gun for painting, and it is difficult to form a uniform pattern pattern.
상기한 에멀젼 수적형 다채 무늬 도료의 전형적인 예로서는 한국 공개특허공보 제10-2005-24076호(2005.03.10. 공개)를 들 수 있으며, 상기한 종래 기술은 물에 셀룰로오스계 증점제, 분산제, 고분자 안료 분산제, TiO2, 마이카(Mica), 탄산칼슘(CaCO3), 클레이(clay), 에멀젼 수지로서의 아크릴-스티렌 에멀젼, 우레탄 증점제, 클레이계 증점제, 응착제, 소포제, pH 조절제, 방부제 및 방균제를 혼합하여 수성겔상의 내부상 조성물을 제조하고, 물에 pH 조절제, 합성 크레이 미네랄, 증점제, 우레탄 증점제, 황산 바륨, 카복실레이티드 스티렌 아크릴레이트 코폴리머, 방부제, 부틸 벤질 프탈레이트 및 소포제를 혼합하여 에멀젼화된 졸상의 외부상 조성물을 제조하며, 이와는 별도로 안료와 프로필렌글리콜, 물, 분산제, 소포제, 평활제 및 침강방지제를 혼합하여 고농도 착색제를 제조한 다음, 상기 내부상 조성물과 외부상 조성물 및 고농도 착색제를 일정 비율로 혼합하여 얻어지는 에멀젼 수적형 다채 무늬 도료 조성물을 제안하고 있다.A typical example of the aforementioned emulsion watercolor type color pattern paint is Korean Patent Laid-Open Publication No. 10-2005-24076 (published on March 10, 2005). The above-mentioned prior art is a method of dispersing a water- , A mixture of an acrylic-styrene emulsion as a emulsion resin, a urethane thickener, a clay thickener, a binder, a defoaming agent, a pH adjuster, a preservative and a disinfectant as TiO 2 , Mica, CaCO 3 , clay, To prepare an aqueous composition in the form of an aqueous gel and mixing the water with a pH adjusting agent, a synthetic crayminer, a thickener, a urethane thickener, a barium sulphate, a carboxylated styrene acrylate copolymer, an antiseptic, a butylbenzyl phthalate and a defoamer to form an emulsified Separately, a pigment is mixed with propylene glycol, water, a dispersing agent, an antifoaming agent, a smoothing agent and an anti-settling agent to prepare a high-concentration It proposes a a method of preparing a developer, and then, the inner portion and the composition outside the composition and the water droplet-shaped patterns varied emulsion coating composition obtained by mixing the high-concentration coloring agent at a constant rate.
그러나 이러한 에멀젼 수적형 다채 무늬 도료는 스프레이 작업을 통한 도막 형성 시 입자의 발달(development) 한계로 인하여 통상 무늬 크기가 3mm 이하에 불과하여 무늬 크기 5~10mm 범위의 화강석 질감을 가지는 도막을 얻기 곤란하다는 문제점이 있음과 아울러, 내부상과 외부상을 혼합한 후 고농도 착색제를 첨가하여 스프레이 도장으로 무늬를 형성하는 과정에서 수직 흐름성과 같은 도장작업성을 고려하여 점도를 높일 경우 무늬 입자가 지나치게 작게 형성되어 화강암의 자연스러운 질감을 얻을 수 없고, 역으로 화강암의 자연스러운 질감을 살리기 위해 에멀젼 수적형 다채 무늬 도료의 점도를 낮출 경우 현장 도장 작업 시 도료의 흐름성이 지나치게 높아져서 도막 품질이 열등하게 된다는 문제점이 있다.However, it is difficult to obtain a coating film having a granite texture in a pattern size of 5 to 10 mm because the size of the emulsion watercolor pattern paint is usually 3 mm or less due to the development limit of the particles during the formation of the coating film through spraying In addition, when the viscosity is increased in consideration of coating workability such as vertical flowability in the process of forming a pattern by spraying painting by adding a high-concentration coloring agent after mixing the inner and outer phases, the grain particles are formed too small The natural texture of the granite can not be obtained. In contrast, when the viscosity of the emulsion watercolor pattern paint is lowered in order to utilize the natural texture of the granite, there is a problem that the flowability of the paint is excessively increased at the site coating operation and the quality of the coating film is inferior.
상기한 바와 같은 종래의 문제점을 해소하기 종래의 방안으로서, 본 출원인에 의한 한국 등록특허공보 제10-0741480호(2007.07.13. 등록)는 외부상으로서의 수성졸에 내부상으로서의 수성겔을 분산시켜 제조되는 수중수적형 다채 무늬 도료를 제안한 바 있으나, 경시(經時) 안정성이 열등하여 수상 삼투압에 의한 무늬 뭉침 현상으로 인하여 도장 현장에서 다량(도료의 10~50%)의 물로 희석하여 도장하여야 한다는 문제점이 있음과 아울러, 물로 희석 시 형성된 무늬가 잘게 부서지는 외에, 부착성이 열등하여 도막이 피도물로부터 박리되거나 도장 후 시간 경과에 따라 부착력이 저하되어 도막이 피도물에서 박리될 염려가 있다는 문제점이 있다.As a conventional method for solving the conventional problems as described above, Korean Patent Registration No. 10-0741480 (registered on July 13, 2007) by the present applicant discloses a method in which an aqueous gel as an internal phase is dispersed in an aqueous phase as an external phase But it has to be diluted with a large amount of water (10 ~ 50% of the paint) due to the accumulation of texture due to water osmotic pressure due to inferior stability over time In addition to the problem that the pattern formed upon dilution with water is finely crushed, there is a problem that the adhesion is inferior and the coating film is peeled off from the coating film or the adhesion force is decreased with time after coating, so that the coating film may peel off from the coating film.
또한, 한국 등록특허공보 제10-1004657호(2010.12.22. 등록)는 건축 내장재용 도료에 관련하여 천연 화강석 또는 대리석 무늬를 쉽고 자연스럽게 제조 및 도포할 수 있는 수용성 천연 화강석 또는 대리석 무늬 도료 조성물 도장 방법을 제안한 바 있으나, 부착력이 낮아 입체 무늬 칼라 입자가 피도물로부터 탈락되기 쉽다는 문제점이 있다.Also, Korean Patent Registration No. 10-1004657 (registered on December 22, 2010) discloses a water-soluble natural granite or marble pattern paint composition coating method capable of easily and naturally producing and coating natural granite or marble pattern However, there is a problem in that the adhesion force is so low that the three-dimensional patterned color particles are easily separated from the substrate.
또한 본 출원인에 의한 한국 등록특허공보 제10-108951호(2011.11.28. 등록)는 헥토라이트를 이용한 천연 화강석 또는 대리석 다채 입체 무늬 도료 조성물 및 이의 제조방법을 개시(開示)하고 있으나, 천연석 패턴 및 질감이 충분히 만족스러운 정도는 못되었으며, 부착성이 열등하여 접착력 보완제를 첨가하여야만 한다는 문제점이 있었다.Korean Patent Registration No. 10-108951 (registered on November 28, 2011) by the present applicant discloses a natural granite or marble variety stereographic painting composition using hectorite and a method for producing the same, The texture is not satisfactory enough, and the adhesive property is inferior, so that the adhesive strength compensating agent must be added.
한편, 수중수적형 다채 무늬 도료는 , 휘발성 유기 화합물로 인한 인체 유해성이 낮고 환경친화적이라는 장점을 가지나, 작업성 및 저장성과 부착력은 상대적으로 열등하다는 문제점이 있다.On the other hand, the underwater waterborne type color pattern paint has the advantages of low human harmfulness due to volatile organic compounds and environmental friendliness, but it has a problem that workability, storage and adhesion are relatively inferior.
따라서 본 발명의 첫 번째 목적은 다양한 종류의 아름다운 색상과 무늬를 지니는 천연 화강석 또는 대리석과 같은 고급스러운 패턴과 질감을 경제적 및 효율적으로 연출할 수가 있는 수성 다채 무늬 도료 조성물의 제조방법을 제공하기 위한 것이다.Accordingly, it is a first object of the present invention to provide a method for producing a water-based colorful pattern coating composition which can produce a luxurious pattern and texture such as natural granite or marble having various kinds of beautiful colors and patterns economically and efficiently.
본 발명의 두 번째 목적은 상기한 첫 번째 목적에 더하여, 통상적인 도장 장치를 이용하여 간단하고 용이하게 도장할 수가 있는 수성 다채 무늬 도료 조성물의 제조방법을 제공하기 위한 것이다.A second object of the present invention is to provide a method for producing an aqueous multicolor paint composition which is simple and easy to paint using a conventional coating apparatus, in addition to the above-mentioned first object.
본 발명의 세 번째 목적은 상기한 제반 목적에 더하여 높은 저장 안정성과 부착력을 지니며, 유기 용제의 함량이 낮아 인체 유해성이 거의 없고 친환경적인 수성 다채 무늬 도료 조성물의 제조방법을 제공하기 위한 것이다.A third object of the present invention is to provide a method for producing a water-based multicolor paint composition which has high storage stability and adhesion, low organic solvent content, and is environmentally friendly, in addition to the aforementioned objects.
본 발명의 네 번째 목적은 상기한 제조방법에 따른 수성 다채 무늬 도료 조성물을 제공하기 위한 것이다.A fourth object of the present invention is to provide an aqueous color pattern coating composition according to the above-mentioned production method.
본 발명의 다섯 번째 목적은 상기한 네 번째 목적에 따른 수성 다채 무늬도료 조성물을 이용한 효과적인 천연석 입체 무늬 도장방법을 제공하기 위한 것이다.A fifth object of the present invention is to provide an effective method of coating a natural stone three-dimensional pattern using the water-based colorful pattern coating composition according to the fourth object.
상기한 첫 번째 내지 세 번째 목적을 원활히 달성하기 위한 본 발명의 바람직한 일 양태에 따르면, (A) (a) 피로인산소다 1.0~2.0중량%와, 소포제 0.01~0.2중량%와, 합성실리카 10.0~20.0중량%와, 잔부가 물로 구성되는 합성 실리카 증점제 15.0~25.0중량%와, (b) 침강방지제로서의 잔탄검 1.5~5.0중량%와, 잔부가 물로 구성되는 수용성 입자 침강 방지제 10.0~25.0중량%와, (c) 물 50~75중량%를 혼합하는 수상 겔 제조 단계와; (B) (a) 피로인산소다 1.0~2.0중량%와 소포제 0.01~0.2중량%와 합성실리카 10.0~20.0중량%와 잔부가 물로 구성되는 합성 실리카 증점제 5.0~10.0중량%와, 셀룰로오스계 증점제 1.0~3.0중량%와, 우레탄계 증점제 1.0~5.0중량%와, 분산제 0.1~2.0중량%와, 소포제 0.2~2.0중량%와, 탄산칼슘 10.0~20.0중량%와, 실란계 발수제 0.1~5.0중량%와, 아크릴 에멀전 또는 아크릴-스티렌 에멀전 35.0~55.0중량%와, 아크릴 에멀전 조도막제 0.1~5.0중량%와, 잔부가 물로 구성되는 수용성 다채 무늬 도료 입자 형성용 페이스트 85~95중량%와, (b) 피로인산소다 1.0~2.0중량%와 소포제 0.01~0.2중량%와 합성실리카 10.0~20.0중량%와 잔부가 물로 구성되는 합성 실리카 증점제 1.0~10.0중량%와, 분산제 1.0~5.0중량%와, 소포제 0.2~2.0중량%와, 안료 60.0~72.0중량%와, 잔부가 물로 구성되는 안료 페이스트 5~15중량%를 혼합하는 천연석 칼라 도료 제조 단계와; (C) 상기한 수상 겔 50.0~60.0중량%에 천연석 칼라 도료 40.0~50.0중량%를 혼합하고 메시 망을 상하로 이동시켜 천연석 칼라 도료가 3~8mm의 크기를 가지도록 절단하여 분산시키는 입자 형성 단계로 구성되는 수성 다채 무늬 도료 조성물의 제조방법이 제공된다.(A) 1.0 to 2.0% by weight of sodium pyrophosphate, 0.01 to 0.2% by weight of an antifoaming agent, and 10 to 20% by weight of synthetic silica. (B) 1.5 to 5.0% by weight of xanthan gum as an anti-settling agent and 10 to 25.0% by weight of a water-soluble anti-settling agent comprising water as the balance, , (c) 50 to 75% by weight of water; (B) a synthetic silica thickener comprising 1.0 to 2.0% by weight of sodium pyrophosphate, 0.01 to 0.2% by weight of defoamer, 10.0 to 20.0% by weight of synthetic silica and the balance of water, 5.0 to 10.0% by weight of a synthetic silica thickener, Based surfactant, 1.0 to 5.0% by weight of a urethane-based thickener, 0.1 to 2.0% by weight of a dispersant, 0.2 to 2.0% by weight of a defoaming agent, 10.0 to 20.0% by weight of calcium carbonate, 0.1 to 5.0% (B) 85 to 95% by weight of a water-soluble multicolor paint particle-forming paste composed of 35.0 to 55.0% by weight of an emulsion or an acryl-styrene emulsion, 0.1 to 5.0% by weight of an acrylic emulsion paint film, 1.0 to 5.0% by weight of a dispersing agent, 0.2 to 2.0% by weight of a defoaming agent, 1.0 to 5.0% by weight of an antifoaming agent, 0.01 to 0.2% by weight of an antifoaming agent, 10.0 to 20.0% by weight of a synthetic silica, % Of a pigment, 60.0 to 72.0% by weight of a pigment, and 5 to 15% Color paint manufacturing step; (C) Particle-forming step of mixing 50.0 to 60.0% by weight of the above-mentioned water-based gel with 40.0 to 50.0% by weight of a natural stone color coating material and moving the mesh screen up and down to cut and disperse the natural stone color coating material so as to have a size of 3-8 mm ≪ / RTI > is provided.
여기서, 상기한 안료는 백색의 이산화티탄, 산화철 황색, 산화철 적색, 산화철 흑색, 또는 이들의 임의의 조합일 수 있다.Here, the pigment may be white titanium dioxide, iron oxide yellow, iron oxide red, iron oxide black, or any combination thereof.
상기한 수상 겔 및 천연석 칼라 도료는 각각 방부제를 1~5중량% 더 포함할 수 있다.The water-soluble gel and the natural stone color paint may further contain 1 to 5% by weight of a preservative.
한편, 상기한 안료 페이스트는 냉동 안정제를 1.0~5.0중량% 더 포함할 수 있다.On the other hand, the pigment paste may further contain 1.0 to 5.0% by weight of a freezing stabilizer.
또한 상기한 수용성 다채 무늬 도료 조성물에는 pH 조절제로서 인산 완충액을 첨가할 수도 있다.In addition, a phosphate buffer solution may be added to the water-soluble multicolored paint composition as a pH adjusting agent.
상기한 네 번째 목적을 원활히 달성하기 위한 본 발명의 바람직한 일 양태에 따르면, 전술한 제조방법에 의하여 제조되는 수성 다채 무늬 도료 조성물이 제공된다.According to a preferred embodiment of the present invention for achieving the fourth object, there is provided an aqueous colored pattern coating composition produced by the above-mentioned production method.
상기한 다섯 번째 목적을 원활히 달성하기 위한 본 발명의 바람직한 일 양태에 따르면, (A) 소지(素地: substrate)의 바탕면에 아크릴 에멀전 또는 아크릴-스티렌 에멀전 하도 도장을 수행하는 단계; (B) 탄산칼슘과 규사 및 안료와 셀룰로오스 증점제를 포함하는 아크릴-스티렌 에멀전 도료를 천연석 표면과 유사한 질감을 가지도록 스프레이하여 중상도 볼륨 도장을 수행하는 단계; 및 (C) 상기한 제6항에 따른 수성 다채 무늬 도료 조성물을 스프레이하여 상도 다채 무늬 도장을 수행하는 단계를 포함하는 천연석 입체 무늬 도장방법이 제공된다.According to a preferred embodiment of the present invention, there is provided a method of manufacturing a semiconductor device, comprising the steps of: (A) performing an acrylic emulsion or acrylic-styrene emulsion undercoating on a substrate; (B) spraying an acrylic-styrene emulsion paint containing calcium carbonate, silica and a pigment and a cellulose thickener so as to have a texture similar to a natural stone surface, thereby performing a heavy phase volume coating; And (C) spraying the water-based multicolor paint composition according to the sixth aspect of the present invention to perform topographic patterning.
상기한 상도 다채 무늬 도장 위에 투명 상도 또는 투명 무광 상도 도장을 더욱 수행할 수도 있음은 물론이다.It is needless to say that a transparent topcoat or a transparent non-transparent topcoat may be further applied on the above-mentioned upper-order colorful pattern coating.
또한 상기한 하도 도장과 중상도 볼륨 도장 사이에 안료를 포함하는 아크릴-스티렌 에멀전 도료를 이용한 중도 도장을 수행할 수도 있다.Also, intermediate painting using an acrylic-styrene emulsion paint including a pigment may be performed between the undercoating and the medium-volume paint.
한편, 상기한 소지는 콘크리트, 합판, 석고 보드, 또는 아크릴판일 수 있다.Meanwhile, the substrate may be concrete, plywood, gypsum board, or acrylic plate.
본 발명에 따른 수성 다채 무늬 도료 조성물의 제조방법 및 그 수성 다채 무늬 도료 조성물과 이를 이용한 천연석 입체 무늬 도장방법에 의하면, 다양한 종류의 아름다운 색상과 무늬를 지니는 천연 화강석 또는 대리석과 같은 고급스러운 패턴과 질감을 다양한 표현 자유도로 경제적 및 효율적으로 연출할 수가 있음과 아울러, 통상적인 도장 장치를 이용하여 간단하고 용이하게 도장할 수가 있고, 높은 저장 안정성과 부착력을 지니며, 수성제품유기 용제의 함량이 낮아 인체 유해성이 적어 친환경적이다.According to the process for producing an aqueous multicolor paint composition according to the present invention and its water-based multicolor paint composition and a method for coating a natural stone three-dimensional pattern using the same, a luxurious pattern and texture such as natural granite or marble having various kinds of beautiful colors and patterns Can be applied economically and efficiently with various freedom of expression, and can be painted simply and easily by using a conventional coating device, has high storage stability and adhesion, has a low content of aqueous organic solvent, This is eco-friendly.
도 1은 석고 보드 소지에 대한 하도 도장 상태도이다.
도 2는 도 1의 하도 처리 석고 보드에 대한 중도 도장 상태도이다.
도 3은 도 2의 중도 처리 석고 보드에 대한 중상도 볼륨 도장 상태도이다.
도 4는 도 3의 중상도 볼륨 도장 처리 석고 보드에 대한 상도 다채 무늬 도장 상태도이다.BRIEF DESCRIPTION OF THE DRAWINGS Fig. 1 is a bottom view of a gypsum board. Fig.
Fig. 2 is an intermediate painting state diagram of the gypsum board of Fig. 1; Fig.
3 is a sagittal volume painting state of the gypsum board of FIG. 2; FIG.
Fig. 4 is a state diagram showing a top-and-bottom pattern coating on the gypsum board treated with the heavy-duty volume paint shown in Fig. 3;
이하, 본 발명에 대하여 상세히 설명하기로 한다.Hereinafter, the present invention will be described in detail.
먼저, 본 발명에 따른 수성 다채 무늬 도료 조성물의 제조방법은 하기의 단계로 구성된다.First, a method for producing an aqueous color pattern coating composition according to the present invention comprises the following steps.
(A) 수상 겔 제조 단계:(A) Preparation of water gel:
수상 겔은 후술하는 천연석 칼라 도료와 혼합되어 도료 및 도막의 안정화와 도장 작업성을 향상시킬 목적으로 사용되며, 상기한 수상 겔은 합성(무정형) 실리카 증점제와 수용성 입자 침강 방지제와 물의 혼합물로 구성된다.The water-soluble gel is used for the purpose of stabilizing the coating material and coating film and improving the workability of painting by mixing with a natural stone color coating material to be described later. The water-based gel is composed of a synthetic (amorphous) silica thickener and a mixture of water- .
본 발명에 있어서 수상 겔은In the present invention, the water-
(a) 합성 실리카 증점제의 제조(a) Preparation of synthetic silica thickener
피로인산소다(tetrasodium pyrophosphate) 1.0~2.0중량%와, 소포제 0.01~0.2중량%와, 합성실리카 10.0~20.0중량%와, 선택적 성분으로서의 방부제 1.0~3.0중량%와, 잔부가 물로 구성된다.1.0 to 2.0% by weight of tetrasodium pyrophosphate, 0.01 to 0.2% by weight of an antifoaming agent, 10.0 to 20.0% by weight of synthetic silica, 1.0 to 3.0% by weight of an antiseptic as an optional ingredient, and the balance of water.
한편, 본 발명에서 수상 겔은 후술하는 2가지 색상 이상의 천연석 칼라 도료를 첨가하여 혼합할 때 서로 다른 색상의 천연석 칼라 도료가 서로 용해 및 혼합되지 않도록 작용하는 불용성 용매로서, 일정한 속도로 균일하게 휘저으면 천연석 칼라 도료가 다채색의 입자상으로 형성함과 동시에 이를 유지시키는 역할을 하며, 상기한 피로인산소다는 수중에서 가수분해 되어 제2 피로인산나트륨으로 되며 합성 실리카 증점제 중의 양이온과 착염을 형성하여 수용액의 겔화를 제어하여 점도를 일정하게 제어하여 천연석 칼라 도료의 무늬 형성 및 유지에 중요한 작용을 함과 아울러, pH 조절제로서 본 발명에 따른 도료 조성물의 저장 안정성 향상에 기여한다.Meanwhile, in the present invention, the water-swellable gel is an insoluble solvent which prevents the natural stone color paints of different colors from dissolving and mixing with each other when the natural stone color paints of two or more colors described later are added and mixed, The natural stone color paint forms a multicolor particle shape and maintains it. The above-mentioned sodium pyrophosphate is hydrolyzed in water to become a second sodium pyrophosphate and forms a complex with the cation in the synthetic silica thickener to form an aqueous solution Controlling the gelation and controlling the viscosity to be constant, it plays an important role in the pattern formation and maintenance of the natural stone color paint, and contributes to the improvement of the storage stability of the paint composition according to the present invention as a pH adjusting agent.
피로인산소다의 첨가량이 1.0중량% 미만에서는 점도가 지나치게 높아질 우려가 있으며 역으로 2.0중량%를 초과하면 점도가 지나치게 낮아질 우려가 있으므로, 점도의 최적한 제어를 위해서는 전술한 범위로 첨가하는 것이 바람직하다.If the amount of sodium pyrophosphate added is less than 1.0% by weight, the viscosity may excessively increase. Conversely, if it exceeds 2.0% by weight, the viscosity may be excessively lowered. Therefore, in order to optimally control the viscosity, .
상기한 소포제로서는 통상적인 실리콘 에멀전이나 계면활성제 또는 고급 알코올이 사용될 수 있다.As the antifoaming agent, a conventional silicone emulsion, a surfactant, or a higher alcohol may be used.
또한 방부제는 유기성분의 부패 및 도막의 붕괴를 막아주는 역할을 하며 당업계 공지의 것을 임의로 선택하여 사용할 수 있다.The preservative also serves to prevent the decay of the organic components and the collapse of the coating film, and any of those well known in the art can be selected and used.
상기한 합성 실리카는 증점제로서 작용하여 점도를 증가시켜 흐름성을 방지하며 안용의 침강 방지와 도장 작업성을 원활히 하기 것으로서, 첨가량이 10중량% 미만인 경우에는 흐름성이 지나치게 증가될 우려가 있고 20중량%를 초과하면 도장 작업성이 열등해질 우려가 있어 바람직하지 못하다.The above synthetic silica acts as a thickener to increase the viscosity to prevent flowability and to prevent sedimentation of the interior and to smooth the painting workability. When the amount of the synthetic silica is less than 10% by weight, the flowability may be excessively increased. %, The paint workability may be inferior, which is not preferable.
상기한 합성 실리카 증점제는 합성 실리카의 용해 속도를 높이기 위하여 약 60~85℃의 물에 피로인산소다와 소포제 및 방부제를 혼합하고 150~300rpm으로 저속 교반하여 혼합한 후, 합성실리카를 소량씩 투입하면서 700~1,000rpm으로 고속 교반하여 완전히 용해시켜 제조한다.In order to increase the dissolution rate of the synthetic silica, the synthetic silica thickener is mixed with sodium pyrophosphate, defoamer and preservative at about 60 to 85 ° C, mixed at a low speed of 150 to 300 rpm and then mixed with a small amount of synthetic silica And the mixture is stirred at 700 to 1,000 rpm at high speed to dissolve completely.
(b) 수용성 입자 침강 방지제의 제조(b) Preparation of water-soluble anti-settling agent
침강방지제로서의 잔탄검 1.5~5.0중량%와, 선택적 성분으로서의 방부제 0.1~2.0중량%와, 잔부가 물로 구성된다.1.5 to 5.0% by weight of xanthan gum as an anti-settling agent, 0.1 to 2.0% by weight of a preservative as an optional component, and the balance of water.
상기한 침강방지제는 도료 중의 안료가 저장 중에 침강하여 케이크상이 되는 것을 방지하기 위하여 사용되며 1.5중량% 미만에서는 침강 방지 효과가 만족스럽지 못하게 될 우려가 있고 역으로 5.0중량%를 초과하면 도막의 물성에 악영향을 초래할 우려가 있으므로 바람직하지 못하다.The anti-settling agent is used to prevent the pigment in the paint from precipitating during storage and becoming a cake. When the content of the anti-settling agent is less than 1.5% by weight, the effect of preventing sedimentation may be unsatisfactory. Conversely, if it exceeds 5.0% It is undesirable because it may cause adverse effects.
상기한 잔탄검 외에도 스테아린산 알루미늄, 유기클레이, 폴리아마이드, 왁스 등도 사용 가능하다.In addition to the above-mentioned xanthan gum, aluminum stearate, organic clay, polyamide, wax and the like can also be used.
상기한 수용성 입자 침강 방지제는 50~60℃의 물을 100~300rpm으로 저속 교반하면서 잔탄검을 소량씩 투입하여 모두 투입한 후, 방부제를 첨가하고, 700~1,000rpm으로 고속 회전시켜 잔탄검을 완전히 용해시켜 제조한다.The above water-soluble anti-settling agent is added with a small amount of xanthan gum while slowly stirring water at 50 to 60 ° C at a rate of 100 to 300 rpm, adding a preservative, and rotating at a high speed of 700 to 1,000 rpm to completely dissolve the xanthan gum .
(c) 수상 겔의 제조(c) Preparation of water-phase gel
상기한 합성 실리카 증점제 15.0~25.0중량%와 상기한 수용성 입자 침강 방지제 10.0~25.0중량%와 물 50~75중량%를 혼합하여 수상 겔을 제조한다.15.0 to 25.0% by weight of the above-mentioned synthetic silica thickener, 10.0 to 25.0% by weight of the water-soluble anti-settling agent and 50 to 75% by weight of water are mixed to prepare an aqueous gel.
수상 겔에 있어서, 상기한 합성 실리카 증점제의 첨가량이 15.0중량% 미만인 경우에는 증점 효과가 충분치 못하게 될 우려가 있으며 역으로 25중량%를 초과하면 도장 작업성이 열등하게 우려가 있고, 상기한 수용성 입자 침강 방지제의 첨가량이 10.0중량% 미만인 경우에는 안료의 케이크화가 발생할 우려가 있으며 역으로 25중량%를 초과하면 도막의 물리적 특성이 저하될 우려가 있으므로 역시 바람직하지 못하다.If the addition amount of the synthetic silica thickening agent is less than 15.0% by weight in the water-based gel, the thickening effect may be insufficient. Conversely, if it exceeds 25% by weight, If the addition amount of the anti-settling agent is less than 10.0% by weight, the pigment may be caked. Conversely, if it exceeds 25% by weight, the physical properties of the coating film may be deteriorated.
상기한 수상 겔은 물을 100~300rpm으로 저속 교반하면서 상기한 합성 실리카 증점제를 투입하여 완전히 용해시킨 다음, 상기한 수용성 입자 침강 방지제를 투입하여 교반하면서 용해시켜 제조한다.The above water-soluble gel is prepared by completely dissolving the above-mentioned synthetic silica thickening agent while stirring at a low speed of 100 to 300 rpm with water, and then adding the above-mentioned water-soluble anti-settling agent and dissolving with stirring.
(B) 천연석 칼라 도료 제조 단계:(B) Natural Stone Color Paint Manufacturing Step:
천연석 칼라 도료는 하기하는 수용성 다채 무늬 도료 입자 형성용 페이스트와 적어도 2종의 선택된 칼라의 안료 페이스트의 혼합물로 구성된다.The natural stone color paint is composed of a mixture of the following water-soluble colorful pattern particle-forming paste and at least two selected color pigment pastes.
(a) 수용성 다채 무늬 도료 입자 형성용 페이스트의 제조(a) Production of water-soluble multicolor paint particle-forming paste
수용성 다채 무늬 도료 입자 형성용 페이스트는, 피로인산소다 1.0~2.0중량%와 소포제 0.01~0.2중량%와 합성실리카 10.0~20.0중량%와 잔부가 물로 구성되는 전술한 바와 같은 합성 실리카 증점제 5.0~10.0중량%와, 셀룰로오스계 증점제 1.0~3.0중량%와, 분산제 0.1~2.0중량%와, 선택적 성분으로서의 방부제 0.2~2.0중량%와, 소포제 0.2~2.0중량%와, 약 350 메시 정도의 탄산칼슘 10.0~20.0중량%와, 아크릴 에멀전 또는 아크릴-스티렌 에멀전 35.0~55.0중량%와, 실란계 발수제 0.1~5.0중량%와, 아크릴 에멀전 조도막제 0.1~5.0중량%와, 우레탄계 증점제 1.0~5.0중량%와, 잔부가 물로 구성된다.The water-soluble colorful pattern paint particle-forming paste is prepared by mixing 1.0 to 2.0% by weight of sodium pyrophosphate, 0.01 to 0.2% by weight of defoamer, 10.0 to 20.0% by weight of synthetic silica and the balance of synthetic silica thickener 5.0 to 10.0 weight 0.2 to 2.0% by weight of a defoamer, 0.2 to 2.0% by weight of a defoaming agent, and 10.0 to 20.0% by weight of a calcium carbonate-based thickener in an amount of 1.0 to 3.0% by weight, a dispersant in an amount of 0.1 to 2.0% % Based on the weight of the acrylic emulsion, 0.1 to 5.0% by weight of the acrylic emulsion coating composition, 1.0 to 5.0% by weight of the urethane based thickener, Additive.
본 발명에 있어서는 수용성 다채 무늬 도료 입자 형성용 페이스트의 제조에 상기한 합성 실리카 증점제 외에, 셀룰로오스계 증점제와 우레탄계 증점제가 함께 사용되며, 이들 증점제는 점도를 일정하게 유지하여 천연석 칼라 도료의 일정한 크기의 칼라 입자 형성과 안정성 유지에 중요한 역할을 하며, 각 증점제의 서로 다른 특징의 상호 보완과 아울러, 비용 절감을 위하여 다양한 증점제를 혼합 사용한다.In the present invention, in addition to the above-mentioned synthetic silica thickening agent, a cellulose type thickening agent and a urethane type thickening agent are used together in the production of a paste for forming a water-soluble colorful pattern paint particle. These thickening agents maintain a constant viscosity, It plays an important role in the formation of particles and stability. In addition to complementing the different characteristics of each thickener, various thickeners are mixed for cost reduction.
상기한 셀룰로오스계 증점제와 우레탄계 증점제의 첨가량이 각각 1중량% 미만인 경우에는 수용성 다채 무늬 도료 입자 형성용 페이스트의 점도가 지나치게 낮아져서 무늬 형성 후 무늬가 풀어지거나 도장 시 도료가 흘러내릴 염려가 있으며, 역으로 각각 3.0중량% 및 5.0중량%를 초과하면 점도가 지나치게 높아져 무늬의 분산성이 열등해지거나 스프레이 도장시 작업성이 열등하게 될 우려가 있다.When the addition amounts of the cellulose type thickening agent and the urethane type thickening agent are each less than 1% by weight, the viscosity of the water-soluble coloring agent particle-forming paste becomes too low and the pattern may be loosened after the pattern formation or the paint may flow down during coating If it exceeds 3.0% by weight and 5.0% by weight, respectively, the viscosity becomes too high, so that the dispersibility of the pattern may be inferior or the workability may be inferior at the time of spray coating.
탄산칼슘은 본 발명에 따른 도료 조성물에서 안료 페이스트에는 없는 체질 안료를 수용성 다채 무늬 도료 입자 형성용 페이스트에 사용한 것으로, 10.0 중량% 미만을 사용하면 체질 효과가 열등하게 될 우려가 있고, 역으로 20.0 중량%를 초과하면 다른 주요 성분의 첨가량을 제한하게 되므로, 상기한 범위 내에서 사용하는 것이 바람직하다.Calcium carbonate is used in the paint composition according to the present invention for the water-soluble coloring paint particle-forming paste which is not contained in the pigment paste. If less than 10.0% by weight is used, the constitutional effect may be inferior. In contrast, %, The amount of other main components to be added is restricted, and therefore, it is preferable to use it within the above-mentioned range.
아크릴 에멀전 또는 아크릴-스티렌 에멀전은 도막 형성제로서 35중량% 미만에서는 도막 형성에 문제점이 생길 수 있으며, 역으로 55중량%를 초과하여 사용하면 다른 주요 성분의 첨가량을 제한하게 되므로, 상기한 범위 내에서 사용하는 것이 바람직하다.If the acrylic emulsion or the acryl-styrene emulsion is used as a film-forming agent at less than 35% by weight, problems may arise in forming a coating film. If the acrylic emulsion or acryl-styrene emulsion is used in an amount exceeding 55% by weight, .
또한 아크릴 에멀전 조도막제는 가소제로서 수용성 다채 무늬 도료 입자 형성용 페이스트에 가소성을 제공하는 도막 형성 보조제로 사용되며, 0.1중량% 미만을 사용하면 상술한 효과가 미미하여 도장 후 형성된 도막에 크랙(crack)이 발생할 우려가 있고, 역으로 5.0중량%를 초과하여 사용하면 사용량 증가에 따른 효과가 미미하므로 바람직하지 못하다.In addition, the acrylic emulsion paint film is used as a film forming aid to provide plasticity to the water-soluble multicolor paint particle-forming paste as a plasticizer. When less than 0.1% by weight is used, the above-mentioned effect is insufficient, , And conversely, if it is used in an amount exceeding 5.0 wt%, the effect of increasing the amount of use is insignificant.
그 외, 방부제, 소포제, 분산제 및, 실란계 발수제는 당업계 공지의 것을 임의로 사용할 수 있으며, 전체 도료 조성물의 함량을 고려하여 당업자가 상기한 범위 내에서 적절히 사용할 수 있다.In addition, antiseptics, antifoaming agents, dispersing agents, and silane-based water repellents can be arbitrarily used in the art, and those skilled in the art can appropriately use them within the above-mentioned ranges in consideration of the content of the entire coating composition.
상기한 수용성 다채 무늬 도료 입자 형성용 페이스트의 제조는, 물을 700~1,000rpm으로 고속 회전 교반하면서, 상기한 성분들을 순차적으로 투입하여 분산시켜 제조한다.The above water-soluble multicolor paint particle-forming paste is prepared by sequentially adding and dispersing the above-mentioned components while stirring and rotating the water at 700 to 1,000 rpm at a high speed.
(b) 안료 페이스트의 제조(b) Production of pigment paste
안료 페이스트는, 피로인산소다 1.0~2.0중량%와 소포제 0.01~0.2중량%와 합성실리카 10.0~20.0중량%와 잔부가 물로 구성되는 전술한 바와 같은 합성 실리카 증점제 1.0~10.0중량%와, 분산제 1.0~5.0중량%와, 선택적 성분으로서의 방부제 0.2~2.0중량%와, 소포제 0.2~2.0중량%와, 냉동 안정제 1.0~5.0중량%와, 안료 60.0~72.0중량%와, 잔부가 물로 구성된다.The pigment paste is prepared by mixing 1.0 to 2.0% by weight of sodium pyrophosphate, 0.01 to 0.2% by weight of defoamer, 10.0 to 20.0% by weight of synthetic silica and 1.0 to 10.0% by weight of a synthetic silica thickener as described above, 0.2 to 2.0% by weight of a defoamer, 1.0 to 5.0% by weight of a freezing stabilizer, 60.0 to 72.0% by weight of a pigment, and the balance of water.
위 성분 중 냉동 안정제, 즉 동결융해안정제는 물을 다량 함유하는 수성 도료를 저온 보관 시 동결현상의 발생으로 에멀전이 파괴되지 않도록 하는 역할을 하며, 에틸렌글리콜, 디에틸렌 글리콜 등과 같은 당업계 공지의 것들을 상기한 범위 내에서 적절히 사용할 수 있다.Among the above components, the cryoprotectant, that is, the cryoprotectant stabilizer, plays a role of preventing the emulsion from being destroyed by the occurrence of the freezing phenomenon when the water-based paint containing a large amount of water is stored at a low temperature and includes those known in the art such as ethylene glycol and diethylene glycol It can be suitably used within the above-mentioned range.
상기한 안료는 백색의 이산화티탄(TiO2), 산화철 황색, 산화철 적색, 산화철 흑색일 수 있으며, 사용하고자 하는 색상의 소정의 조합에 따라 각각의 안료 페이스트 제조된다.The above-mentioned pigments may be white titanium dioxide (TiO 2 ), iron oxide yellow, iron oxide red, iron oxide black, and each pigment paste is produced according to a predetermined combination of colors to be used.
상기한 산화철(산화제이철: Fe2O3) 안료는 철강이나 도금 공업 분야의 폐액 중의 황산철을 원료로 하여 제조되며 입자의 크기, 혼입물의 종류, 결정격자의 완전성 정도 등에 따라 황색, 갈색, 적색, 흑색 등을 나타내며, 이들은 모두 상업적으로 입수 가능하다.The above-mentioned iron oxide (ferric oxide: Fe 2 O 3 ) pigment is produced by using iron sulfate as a raw material in a waste solution of steel or plating industry and has a yellow, brown and red color depending on the particle size, the kind of the mixture, , Black, and the like, all of which are commercially available.
상기한 안료의 첨가량이 60중량% 미만인 경우에는 천연석 입자 무늬의 재현성이 충분히 만족스럽지 못하게 될 우려가 있으며, 역으로 72중량%를 초과하면 침강에 의한 케이크화 우려가 있으므로 역시 바람직하지 못하다.If the added amount of the pigment is less than 60% by weight, the reproducibility of the natural stone particle pattern may not be sufficiently satisfactory. Conversely, if it exceeds 72% by weight, caking may occur due to sedimentation.
상기한 안료 페이스트의 제조는 물에 합성 실리카 증점제, 분산제, 방부제, 소포제, 냉동 안정제를 투입하여 100~300rpm으로 저속 교반하면서, 안료를 서서히 투입하고, 투입 완료 후에는 1,000~1,600rpm으로 고속 교반하여 철저히 혼합한다.The above pigment paste is prepared by slowly adding a synthetic silica thickening agent, a dispersant, a preservative, a defoaming agent and a freezing stabilizer to water and slowly stirring the mixture at 100 to 300 rpm while slowly stirring the pigment at 1,000 to 1,600 rpm Mix thoroughly.
(c) 천연석 칼라 도료의 제조(c) Production of natural stone color paints
수용성 다채 무늬 도료 입자 형성용 페이스트 85~95중량%와, 의도하는 조색에 따라 서로 다른 안료가 포함된 안료 페이스트를 적어도 2종 이상으로 합계 5~15중량%를 혼합하여 천연석 칼라 도료를 제조한다.85 to 95% by weight of a paste for water-soluble colorful pattern paint particles and 5 to 15% by weight in total of at least two kinds of pigment pastes containing different pigments according to intended coloring are mixed to prepare a natural stone color paint.
본 발명에 있어서, 수용성 다채 무늬 도료 입자 형성용 페이스트의 첨가량이 85중량% 미만인 경우에는 도막 형성이 불충분하게 되거나 형성된 도막의 물성이 저하될 우려가 있어 바람직하지 못하며, 역으로 95중량%를 초과하면 선명한 천연석 색상 패턴을 얻지 못하게 될 우려가 있으므로 역시 바람직하지 못하다.In the present invention, when the amount of the water-soluble multicolor paint particle-forming paste to be added is less than 85% by weight, formation of the coating film may be insufficient or the physical properties of the formed coating film may be deteriorated. Conversely, It is also undesirable because there is a possibility that a vivid natural stone color pattern may not be obtained.
또한 안료 페이스트의 첨가량이 5중량% 미만인 경우에는 앞서 언급한 바와 같이 선명한 천연석 색상 패턴을 얻지 못하게 될 우려가 있고, 역으로 15중량%를 초과하는 경우에는 도막 형성 성분의 첨가량 저하로 인하여 도막 형성이 불충분하게 되거나 형성된 도막의 물성이 저하될 우려가 있어 바람직하지 못하다.When the addition amount of the pigment paste is less than 5% by weight, there is a possibility that a clear natural stone color pattern may not be obtained as mentioned above. Conversely, when the addition amount exceeds 15% by weight, There is a possibility that the coating film becomes insufficient or the physical properties of the formed coating film are lowered.
(C) 입자 형성 단계:(C) Particle formation step:
상기한 수상 겔 50.0~60.0중량%에 천연석 칼라 도료 40.0~50.0중량%를 혼합하고 피아노선 등으로 제작된 메시 망을 상하로 이동시키는 것에 의해 천연석의 색상 평균 입자 크기와 유사한 3~8mm의 평균 입자 크기의 천연석 칼라 도료가 되도록 절단하여 분산시킨다.By mixing 40.0 ~ 50.0% by weight of a natural stone color paint with 50.0 ~ 60.0% by weight of the above water gel, and moving a mesh net made of piano wire or the like up and down, an average particle size of 3-8 mm Size natural stone color paint.
상기한 수상 겔의 첨가량이 60.0중량%를 초과하거나 천연석 칼라 도료의 첨가량이 40.0중량% 미만인 경우에는 착색성이 충분히 만족스럽지 못하게 되어 천연 대리석이나 화강석과 같은 자연스러운 색상 및 무늬 패턴을 얻지 못하게 될 우려가 있고, 역으로 상기한 수상 겔의 첨가량이 50.0중량% 미만이거나 천연석 칼라 도료의 첨가량이 50.0중량%를 초과할 경우에는 도막의 물리적 특성 및 도막 부착성과 도료의 저장 안정성이 열등하게 될 우려가 있으므로 역시 바람직하지 못하다.If the addition amount of the water-soluble gel is more than 60.0% by weight or the amount of the natural stone color coating is less than 40.0% by weight, the coloring property is not sufficiently satisfactory, and natural color or pattern pattern such as natural marble or granite may not be obtained Conversely, when the amount of the above-mentioned water-based gel is less than 50.0% by weight or when the amount of the natural stone color coating is more than 50.0% by weight, the physical properties of the coating film, the coating film adhesion and the storage stability of the coating may be inferior, I can not.
한편, 본 발명에 있어서는 pH 조절제로서 인산을 0.5 내지 5% 수용액으로 하여 본 발명에 따른 수성 다채 무늬 도료 조성물에 첨가할 수 있다.Meanwhile, in the present invention, it is possible to add to the water-based multicolor paint composition according to the present invention by using 0.5-5% aqueous solution of phosphoric acid as a pH adjusting agent.
이하, 본 발명에 따른 수성 다채 무늬 도료 조성물의 제조방법에 의하여 제조되는 수성 다채 무늬 도료 조성물을 이용한 천연석 입체 무늬 도장방법에 대하여 설명하기로 한다.Hereinafter, a method for coating a natural stone three-dimensional pattern using the water-based multicolor paint composition produced by the method for producing an aqueous multicolor paint composition according to the present invention will be described.
본 발명에 따른 천연석 입체 무늬 도장방법은 하기의 단계를 포함한다.The method for coating a natural stone three-dimensional pattern according to the present invention includes the following steps.
(A) 하도 도장 단계:(A) Undercoating Step:
콘크리트, 합판, 원목, 칩보드, 섬유보드, 석고보드, 아크릴판, 유리 등과 같은 소지(素地)의 바탕면에 아크릴 에멀전 또는 아크릴-스티렌 에멀전 하도를 붓이나 롤러, 또는 스프레이건을 이용하여 도장한다.Acrylic emulsion or acrylic-styrene emulsion paints are applied to the surface of substrates such as concrete, plywood, wood, chip board, fiber board, gypsum board, acrylic plate, glass, etc. using brush, roller or spray gun .
이때 우수한 은폐력을 나타낼 수 있도록 표현하고자 하는 대상 천연석에 가장 많은 주된 칼라의 색상으로 바탕면을 도장한다(도 1 참조).In order to exhibit excellent hiding power, the base surface is painted with the color of the main color most corresponding to the natural stone to be expressed (see FIG. 1).
상기한 하도 도료의 예로서는, 아크릴 에멀전 또는 아크릴-스티렌 에멀전 40~50 중량%와, 방부제 0.1~2.0중량%와, 소포제 0.1~2.0중량%와, 잔부가 물로 이루어지는 하도를 들 수 있다.Examples of the undercoat paint include 40 to 50% by weight of an acrylic emulsion or an acryl-styrene emulsion, 0.1 to 2.0% by weight of an antiseptic agent, 0.1 to 2.0% by weight of an antifoaming agent, and the remainder is water.
(B) 중상도 볼륨 도장 단계:(B) Medium level volume painting step:
탄산칼슘과 규사 및 안료와 셀룰로오스 증점제를 포함하는 아크릴-스티렌 에멀전 도료를 천연석 표면과 유사한 질감과 볼륨(엠보싱)을 가지도록 하도 위에 스프레이하여 중상도 볼륨 도장을 수행한다(도 3 참조).The acrylic-styrene emulsion paint containing calcium carbonate, silica sand, pigment and cellulose thickener is sprayed on the undercoat so as to have a texture and volume (embossing) similar to the surface of the natural stone, and a heavy phase volume coating is performed (see FIG.
중상도 볼륨 도장의 색상은 우수한 은폐력을 나타낼 수 있도록 표현하고자 하는 대상 천연석에 가장 많은 주된 칼라의 색상으로 하는 것이 바람직하다.It is preferable that the color of the medium-phase volume paint is the color of the main color most corresponding to the natural stone to be expressed in order to exhibit excellent hiding power.
중상도 볼륨 도료의 예로서는, 분산제 0.2~4.0중량%와, 방부제 0.1~2.0중량%와, 셀로루오스 증점제 0.05~0.5중량%와, 아크릴-스티렌 에멀전 15.0~20.0중량%와, 소포제 0.1~2.0중량%와, 콜로이드상 클레이 0.1~2.0중량%와, 고비점 솔벤트 0.1~2.0중량%와, 냉동안정제 0.1~3.0중량%와, 백색 체질 안료(TiO2) 2.0~8.0중량%와, 탄산칼슘(150~250 메시) 25.0~30.0중량%와, 규사(80~150메쉬) 25.0~40.0중량%와, 아크릴-스티렌 에멀전 피막형성제 0.2~3.0중량%와, 아크릴계 증점제(고형분 함량 33%) 0.2~2.0중량%와 잔부가 물로 구성되는 것을 들 수 있으며, 결과물은 고점도 반죽 상태의 도료이다.Examples of the medium-phase volume coating include a coating composition containing 0.2 to 4.0% by weight of a dispersing agent, 0.1 to 2.0% by weight of a preservative, 0.05 to 0.5% by weight of a cellulosic thickener, 15.0 to 20.0% by weight of an acryl-styrene emulsion, 0.1 to 2.0% by weight of a colloidal phase clay, 0.1 to 2.0% by weight of a high boiling point solvent, 0.1 to 3.0% by weight of a refrigerating stabilizer, 2.0 to 8.0% by weight of a white coloring pigment (TiO 2 ) Styrene emulsion film-forming agent 0.2 to 3.0% by weight, an acrylic thickener (solid content 33%) 0.2 to 2.0% by weight, And the remainder is composed of water and the resultant product is a high viscosity kneaded paint.
(C) 상도 다채 무늬 도장 단계:(C) Top-of-the-
천연석을 예컨대 50mm x 50mm 면적을 선택하고 각각의 색상을 육안으로 세어 분포도를 측정 결정한다.Natural stone is selected, for example, 50 mm x 50 mm, and each color is visually counted to determine the distribution.
상기와 같이 결정된 분포도에 따라 적어도 2종 이상의 색상으로 된 안료 페이스트를 선택하여 수용성 다채 무늬 도료 입자 형성용 페이스트와 혼합 조색한, 본 발명에 따른 수성 다채 무늬 도료 조성물의 제조방법에 의하여 제조되는 수성 다채 무늬 도료 조성물을 압송건이나 스프레이건을 이용하여 도장하며, 상하 좌우로 빠짐없이 전면 도장한다(도 4 참조).The aqueous pigment mixture prepared by the method of producing an aqueous color pattern paint composition according to the present invention in which pigment paste having at least two kinds of colors is selected according to the distribution chart thus determined and mixed with the paste for forming water- The pattern paint composition is applied by using a press-feeding gun or a spray gun, and is entirely coated on the upper and lower sides (see FIG. 4).
한편, 필요하다면 선택적으로, 상기한 하도 도장과 중상도 볼륨 도장 사이에 하도와 동일한 색상의 안료를 포함하되 탄산칼슘 및/또는 규사를 포함하지 않으며 중상도 볼륨 도료에 비하여 낮은 점도로 제조된 유사한 성분으로 된 아크릴-스티렌 에멀전 도료를 이용한 중도 도장을 수행할 수도 있음은 물론이다(도 2 참조).On the other hand, if desired, optionally a similar component which contains pigments of the same color as the undercoat between the undercoat and medium-high-volume paint, but which does not contain calcium carbonate and / or silica, Styrene emulsion paints (see Fig. 2).
또한 필요하다면 선택적으로, 상도 다채 무늬 도장 위에 투명 상도 또는 투명 무광 상도 도장을 더욱 수행할 수도 있으며, 이 또한 본 발명의 영역 내이다.Optionally, if desired, a transparent topcoat or a clear topcoat may also be applied on top of the top colorful pattern, which is also within the scope of the present invention.
투명 상도 도료의 예로서는, 아크릴 에멀전 50.0~70.0중량%와, 냉동안정제 1.0~5.0중량%와, 소포제 0.2~2.0중량%와, 방부제 0.1~2.0중량%와, 우레탄계 증점제 0.1~2.0중량%와, 아크릴 에멀전 조도막제 0.2~4.0중량%와 잔부가 물인 것을 들 수 있다.Examples of the transparent top coating include an acrylic emulsion of 50.0 to 70.0 wt%, a freezing stabilizer of 1.0 to 5.0 wt%, an antifoaming agent of 0.2 to 2.0 wt%, a preservative of 0.1 to 2.0 wt%, a urethane-based thickener of 0.1 to 2.0 wt% 0.2 to 4.0% by weight of the emulsion paint film and the balance thereof.
또한 투명 무광 도료의 예로서는, 아크릴 에멀전 40.0~60.0중량%와, 냉동안정제 1.0~5.0중량%와, 방부제 0.1~2.0중량%와, 소포제 0.1~2.0중량%와, 우레탄계 증점제 0.1~2.0중량%와, 아크릴 에멀전 조도막제 0.2~4.0중량%와, 무광제로서의 실리카(500~1000㎛) 4.0~10.0중량%와, 분산제 0.2~2.0중량%와, 잔부가 물로 구성되는 것일 수 있으며, 물에 분산제와 소포제를 투입하여 교반하면서 실리카를 소량씩 투입하고 1~2시간 고속(700~1200rpm) 교반하고, 분산이 완료되면 아크릴에멀전 및 다른 원료를 투입하여 제조할 수 있다.
Examples of the transparent matting paints include an acrylic emulsion of 40.0 to 60.0 wt%, a freezing stabilizer of 1.0 to 5.0 wt%, a preservative of 0.1 to 2.0 wt%, an antifoaming agent of 0.1 to 2.0 wt%, a urethane-based thickener of 0.1 to 2.0 wt% 0.2 to 4.0% by weight of an acrylic emulsion coating composition, 4.0 to 10.0% by weight of silica (500 to 1000 μm) as a matting agent, 0.2 to 2.0% by weight of a dispersing agent and the balance of water, The antifoaming agent is added, and a small amount of silica is added thereto while stirring. The mixture is stirred at high speed (700 to 1200 rpm) for 1 to 2 hours, and after the dispersion is completed, acrylic emulsion and other raw materials can be added.
이하, 실시예 및 도장예를 통하여 본 발명을 더욱 상세히 설명하기로 하나, 이는 본 발명을 예증하기 위한 것일 뿐 본 발명을 제한하고자 하는 것은 아니다.
EXAMPLES Hereinafter, the present invention will be described in more detail with reference to examples and coating examples, but the present invention is not limited thereto.
실시예 1:
Example 1:
하기와 같은 조성 및 조성비와 배합 방법으로 수성 다채 무늬 도료 조성물을 제조하였다.
An aqueous color pattern coating composition was prepared by the following composition and composition ratio and mixing method.
(1) 수상 겔의 제조:
(1) Preparation of a water gel:
1) 합성 실리카 증점제의 제조 1) Preparation of synthetic silica thickener
81.4중량%의 60~85℃의 물에 피로인산소다 1.5중량%, 소포제(NXZ) 0.1중량%, 방부제(100LA) 2.0중량%를 혼합하고 250rpm으로 교반하여 용해시켰다. 이어서, 합성실리카(LAPONATE) 15중량%를 소량씩 투입하면서 850rpm으로 고속 교반하여 용해시켜, 합성 실리카 증점제를 제조하였다.
1.5% by weight of sodium pyrophosphate, 0.1% by weight of an antifoaming agent (NXZ) and 2.0% by weight of an antiseptic agent (100LA) were mixed in 81.4% by weight of water at 60 to 85 ° C and dissolved by stirring at 250 rpm. Subsequently, 15 wt% of synthetic silica (LAPONATE) was added at a high speed with stirring at 850 rpm while dissolving in small amounts to prepare a synthetic silica thickener.
2) 수용성 입자 침강 방지제의 제조2) Preparation of water-soluble anti-settling agent
96.0중량%의 50~60℃의 물을 250rpm으로 교반하면서 침강방지제로서의 잔탄검 3.0중량%를 교반기로 교반하면서 소량씩 투입하고 투입 완료 후 방부제(100LA) 1.0중량%를 투입하고 850rpm으로 고속 교반하여 용해시켜, 수용성 입자 침강 방지제를 제조하였다.
While 96.0 wt% of water at 50 to 60 캜 was stirred at 250 rpm, 3.0 wt% of xanthan gum as an anti-settling agent was added in small portions while stirring with a stirrer. After completion of the addition, 1.0 wt% of preservative (100LA) was added and stirred at 850 rpm To prepare a water-soluble anti-settling agent.
3) 수상 겔의 제조3) Preparation of water-soluble gel
68.0중량%의 물을 250rpm으로 교반하면서 합성 실리카 증점제 20.0중량%를 투입하여 완전히 용해시킨 후, 수용성 입자 침강 방지제 20.0중량%를 투입하여 교반하여 용해시키고, 방부제(100LA) 2.0중량%를 첨가하여 용해시켜, 수상 겔을 제조하였다.
20.0% by weight of a synthetic silica thickener was completely dissolved by adding 68.0% by weight of water with stirring at 250 rpm, 20.0% by weight of a water-soluble anti-settling agent was added thereto and stirred to dissolve, and 2.0% by weight of a preservative (100LA) To prepare a water gel.
(2) 천역석 칼라 도료의 제조:
(2) Preparation of Thinner Color Coating Material:
1) 수용성 다채 무늬 도료 입자 형성용 페이스트의 제조1) Preparation of paste for forming water-soluble multicolor paint particles
물 19중량%를 850rpm으로 고속교반하면서, 앞에서와 동일한 성분 및 성분비로 동일하게 제조한 합성실리카 증점제 8.0중량%와, 셀룰로오스 증점제(Bermocol 451FQ) 2.0중량%와, 분산제(N44S) 1.0중량%와, 방부제(100LA) 1.0중량%와, 소포제(NXZ) 1.0중량%와, 탄산칼슘(325메쉬) 15.0중량%와, 고형분 함량 46%의 아크릴-스티렌 에멀전 45.0중량%와, 실란계 발수제 2.0중량%와, 아크릴 에멀전 조도막제(TEXANOL) 3.0중량%와, 우레탄계증점제(622N) 3.0중량%를 순서대로 투입하여 고속 분산시켜 수용성 다채 무늬 도료 입자 형성용 페이스트를 제조하였다.
8.0 wt% of a synthetic silica thickener, 2.0 wt% of a cellulose thickener (Bermocol 451FQ), 1.0 wt% of a dispersing agent (N44S), and 10 wt% of a dispersing agent (N44S) were mixed at a high speed with stirring at 850 rpm, 1.0% by weight of an antiseptic agent (NXZ), 15.0% by weight of calcium carbonate (325 mesh), 45.0% by weight of an acryl-styrene emulsion having a solid content of 46%, 2.0% by weight of a silane- 3.0% by weight of an acrylic emulsion paint film forming agent (TEXANOL) and 3.0% by weight of a urethane-based thickener (622N) were put in order and dispersed at high speed to prepare a water-soluble multicolor paint particle-forming paste.
2) 백색 안료 페이스트(1)의 제조2) Preparation of white pigment paste (1)
물 22.0중량%를 250rpm으로 교반하면서, 앞에서와 동일한 성분 및 성분비로 동일하게 제조한 합성 실리카 증점제 5.0중량%와, 분산제(N44S) 3.0중량%와, 방부제(100LA) 1.0중량%와, 소포제(NXZ) 1.0중량%와, 냉동안정제(E.G) 3.0중량%를 투입하여 용해시킨 후, 이산화티탄 백색 안료(TiO2) 65.0중량%를 서서히 투입하면서 1200rpm으로 고속 교반하여, 백색 안료 페이스트(1)을 제조하였다.
5.0 wt% of a synthetic silica thickener prepared in the same manner as in the foregoing with the same composition as in the foregoing, 3.0 wt% of a dispersing agent (N44S), 1.0 wt% of a preservative (100LA) and a defoaming agent (NXZ ) Was added and dissolved in 3.0 wt% of a freezing stabilizer (EG), and the mixture was stirred at 1200 rpm at a high speed while gradually adding 65.0 wt% of a titanium dioxide white pigment (TiO 2 ) to prepare a white pigment paste (1) Respectively.
3) 흑색 안료 페이스트(2)의 제조3) Production of black pigment paste (2)
안료 페이스트 1의 제조에서, 물을 30중량% 사용하고 이산화티탄 백색 안료(TiO2) 대신에 산화철 흑색 안료(Fe2O3) 57.0중량%를 사용한 것을 제외하고는 동일한 방법 및 절차로 흑색 안료 페이스트(2)를 제조하였다.
In the same manner as in the production of the pigment paste 1, except that 30% by weight of water was used and 57.0% by weight of iron oxide black pigment (Fe 2 O 3 ) was used instead of the titanium dioxide white pigment (TiO 2 ) (2).
4) 천연석 칼라 도료의 제조:4) Preparation of natural stone color paint:
상기한 수용성 다채 무늬 도료 입자 형성용 페이스트 안료 90중량%에 상기한 백색 안료 페이스트(1) 2중량%와 상기한 흑색 안료 페이스트(2) 8중량%를 혼합하여 천연석 칼라 도료를 제조하였다.
2% by weight of the white pigment paste (1) and 8% by weight of the above-mentioned black pigment paste (2) were mixed with 90% by weight of the paste for water-soluble colorful pattern paint particles.
(3) 수성 다채 무늬 도료 조성물의 제조 및 칼라 입자 형성:
(3) Preparation of aqueous color pattern coating composition and color particle formation:
앞서 제조한 수상겔 50.0중량%와 앞서 제조한 천연석 칼라 도료 50.0중량%를 50.0% by weight of the previously prepared water gel and 50.0% by weight of the natural stone color paint prepared above
혼합하여 수성 다채 무늬 도료 조성물을 제조하였다. 이어서, 메시 망을 상하로 이동시켜 백색 및 흑색의 천연석 칼라 도료가 3~8mm의 크기를 가지도록 절단된 상태로 분산시켜 칼라 입자를 형성하였다.
Were mixed to prepare an aqueous multicolor paint composition. Then, the mesh net was moved up and down to disperse the white and black natural stone color paints in a cut state so as to have a size of 3 to 8 mm to form color particles.
실시예 2:
Example 2:
상기한 실시예 1의 (2), 2) 및 3)의 백색 안료 페이스트(1) 및 흑색 안료 페이스트(2)의 제조 외에, 흑색 안료 페이스트(2)에서의 산화철 흑색 안료(Fe2O3) 57.0중량% 대신에 산화철 황색 안료(Fe2O3) 57.0중량%를 사용하여 황색 안료 페이스트(3)을 더 제조하고, 상기한 수용성 다채 무늬 도료 입자 형성용 페이스트 안료 90중량%에 상기한 백색 안료 페이스트(1) 1중량%와 상기한 흑색 안료 페이스트(2) 1중량%와 상기한 황색 안료 페이스트(3) 8중량%를 혼합하여 천연석 칼라 도료를 제조한 것을 제외하고는 동일한 절차 및 방법에 의하여 수성 다채 무늬 도료 조성물을 제조하고, 마찬가지 방법으로 칼라 입자를 형성하였다.
(Fe 2 O 3 ) in the black pigment paste 2 in addition to the production of the white pigment paste 1 and the black pigment paste 2 in Examples 1 (2), 2) and 3 ) A yellow pigment paste (3) was further prepared by using 57.0 wt% of iron oxide yellow pigment (Fe 2 O 3 ) instead of 57.0 wt%. To the above-mentioned water-soluble colorful pattern paint particle-forming paste pigment 90 wt% Except that 1 mass% of the paste (1), 1 mass% of the black pigment paste (2) and 8 mass% of the yellow pigment paste (3) were mixed to prepare a natural stone color paint. An aqueous multicolor paint composition was prepared and color particles were formed in the same manner.
실시예 3:
Example 3:
상기한 실시예 1의 (2), 3)의 흑색 안료 페이스트(2)의 제조에 있어, 산화철 흑색 안료(Fe2O3) 57.0중량% 대신에 산화철 황색 안료(Fe2O3) 57.0중량%를 사용하여 황색 안료 페이스트(3)을 제조하고, 상기한 수용성 다채 무늬 도료 입자 형성용 페이스트 안료 90중량%에 상기한 황색 안료 페이스트(3) 8중량%와 상기한 백색 안료 페이스트(1) 2중량%를 혼합하여 천연석 칼라 도료를 제조한 것을 제외하고는 동일한 절차 및 방법에 의하여 수성 다채 무늬 도료 조성물을 제조하고, 마찬가지 방법으로 칼라 입자를 형성하였다.
57.0 wt% of iron oxide yellow pigment (Fe 2 O 3 ) was used instead of 57.0 wt% of iron oxide black pigment (Fe 2 O 3 ) in the production of the black pigment paste (2) of (2) , Yellow pigment paste 3 was prepared. To 90 wt% of the paste for water-soluble colorful pattern paint particles, 8 wt% of the yellow pigment paste 3 and 2 wt% of the white pigment paste 1 % To prepare a natural stone color coating composition. The same procedure and the same procedure were followed to prepare an aqueous color pattern coating composition, and color particles were formed in the same manner.
도장예:
Coating Example:
30x60x2.5cm 치수의 석고 보드 시편을 준비하였다.A gypsum board specimen of size 30x60x2.5 cm was prepared.
상기한 석고 보드 시편 상에, 고형분 함량 45%의 아크릴-스티렌 에멀전 45중량%와, 물 63중량%와, 방부제(procel XL-2) 1.0중량%와, 소포제(NXZ) 1.0중량%로 이루어지는 하도 도료를 붓으로 도포하고 경화시켜 하도를 형성함으로써 소지의 바탕면을 은폐하였다(도 1 참조).The above-mentioned gypsum board specimen was coated with 45% by weight of acrylic-styrene emulsion having a solid content of 45% by weight, 63% by weight of water, 1.0% by weight of preservative (procel XL-2) and 1.0% by weight of defoamer The paint was applied with a brush and cured to form a primer, thereby hiding the base surface of the primer (see Fig. 1).
이어서, 분산제 3.0중량%와, 방부제 1.0중량%와, 셀로루오스 증점제 0.3중량%와, 아크릴-스티렌 에멀전 18.0중량%와, 소포제 1.0중량%와, 콜로이드상 클레이 1.0중량%와, 고비점 솔벤트 1.0중량%와, 냉동안정제 2.0중량%와, 백색 체질 안료(TiO2) 5.0중량%와, 아크릴-스티렌 에멀전 피막형성제 2.0중량%와, 아크릴계 증점제(고형분 함량 33%) 1.0중량%와 잔부가 물로 구성되는 중도를 스프레이건을 이용하여 스프레이하여 소지의 바탕면을 더욱 은폐하였다(도 2 참조).Then, a mixture of 3.0 wt% of dispersant, 1.0 wt% of preservative, 0.3 wt% of cellulosic thickener, 18.0 wt% of acryl-styrene emulsion, 1.0 wt% of defoamer, 1.0 wt% of colloidal clay, , 2.0 wt% of a cryoprene stabilizer, 5.0 wt% of a white extender pigment (TiO 2 ), 2.0 wt% of an acryl-styrene emulsion film former, 1.0 wt% of an acrylic thickener (solid content 33% The intermediate surface of the substrate was sprayed using a spray gun to further conceal the substrate surface (see FIG. 2).
그 후, 분산제 3.0중량%와, 방부제 1.0중량%와, 셀로루오스 증점제 0.3중량%와, 아크릴-스티렌 에멀전 18.0중량%와, 소포제 1.0중량%와, 콜로이드상 클레이 1.0중량%와, 고비점 솔벤트 1.0중량%와, 냉동안정제 2.0중량%와, 백색 체질 안료(TiO2) 5.0중량%와, 탄산칼슘(150~250 메시) 25.0중량%와, 규사(80~150메쉬) 30.0중량%와, 아크릴-스티렌 에멀전 피막형성제 2.0중량%와, 아크릴계 증점제(고형분 함량 33%) 1.0중량%와 잔부가 물로 구성되는 고점도 반죽 상태의 중상도 볼륨 도료를 나팔 건을 이용하여 스프레이하고 경화시켜 천연석의 표면 바탕 질감의 예비 처리를 하였다(도 3 참조).Thereafter, 3.0 wt% of dispersant, 1.0 wt% of preservative, 0.3 wt% of cellulosic thickener, 18.0 wt% of acryl-styrene emulsion, 1.0 wt% of defoamer, 1.0 wt% of colloidal clay, and with 1.0% by weight, freeze stabilizer, 2.0 wt.%, white extender pigment (TiO 2) 5.0% by weight, calcium (150 to 250 mesh) 25.0% by weight and a silica (80 to 150 mesh) 30.0% by weight, acrylic - a high viscosity kneaded medium volume paint of 2.0% by weight of a styrene emulsion film former and 1.0% by weight of an acrylic thickener (solids content 33%) and the remainder water was sprayed and cured using a trumpet gun to produce a surface of natural stone (See Fig. 3).
이어서, 실시예 2의 수성 다채 무늬 도료 조성물을 메시 망을 상하 이동시켜 백색, 흑색, 황색의 천연석 칼라 도료가 3~8mm의 크기를 가지도록 절단된 상태로 분산 유지된 칼라 입자를 형성하였으며, 압송 건을 이용하여 스프레이 도장하여 천연 화강석과 유사한 표면 질감 및 패턴과 색상을 지니는 상도 다채 무늬 도장 처리를 수행하였다(도 4 참조).Then, the water-based multicolor paint composition of Example 2 was vertically moved by a mesh net to form color particles dispersed and retained in a state of being cut so that white, black and yellow natural stone color paints had a size of 3 to 8 mm, Spray painting was performed using a gun to perform a top-color pattern painting process having a surface texture and pattern and color similar to those of natural granite (see FIG. 4).
여기서 필요하다면 상도 투명 보호 처리 또는 상도 투명 무광 보호 처리를 수행할 수 있음은 물론이다.
It is needless to say that the top transparent protection treatment or the top clear transparent mat protection treatment can be performed if necessary.
이상, 본 발명에 관하여 상세히 설명하였으나, 본 발명은 이에 한정되는 것은 아니며, 당업자라면 이로부터 다양한 변화 및 수정이 가능함은 물론이나, 이 또한 본 발명의 영역 내이다.
Although the present invention has been described in detail, the present invention is not limited thereto, and various changes and modifications may be made by those skilled in the art.
Claims (10)
(A) (a) 피로인산소다 1.0~2.0중량%와, 소포제 0.01~0.2중량%와, 합성실리카 10.0~20.0중량%와, 잔부가 물로 구성되는 합성 실리카 증점제 15.0~25.0중량%와, (b) 침강방지제로서의 잔탄검 1.5~5.0중량%와, 잔부가 물로 구성되는 수용성 입자 침강 방지제 10.0~25.0중량%와, (c) 물 50~75중량%를 혼합하는 수상 겔 제조 단계와;
(B) (a) 피로인산소다 1.0~2.0중량%와 소포제 0.01~0.2중량%와 합성실리카 10.0~20.0중량%와 잔부가 물로 구성되는 합성 실리카 증점제 5.0~10.0중량%와, 셀룰로오스계 증점제 1.0~3.0중량%와, 우레탄계 증점제 1.0~5.0중량%와, 분산제 0.1~2.0중량%와, 소포제 0.2~2.0중량%와, 탄산칼슘 10.0~20.0중량%와, 실란계 발수제 0.1~5.0중량%와, 아크릴 에멀전 또는 아크릴-스티렌 에멀전 35.0~55.0중량%와, 아크릴 에멀전 조도막제 0.1~5.0중량%와, 잔부가 물로 구성되는 수용성 다채 무늬 도료 입자 형성용 페이스트 85~95중량%와, (b) 피로인산소다 1.0~2.0중량%와 소포제 0.01~0.2중량%와 합성실리카 10.0~20.0중량%와 잔부가 물로 구성되는 합성 실리카 증점제 1.0~10.0중량%와, 분산제 1.0~5.0중량%와, 소포제 0.2~2.0중량%와, 안료 60.0~72.0중량%와, 잔부가 물로 구성되는 안료 페이스트 5~15중량%를 혼합하는 천연석 칼라 도료 제조 단계와;
(C) 상기한 수상 겔 50.0~60.0중량%에 천연석 칼라 도료 40.0~50.0중량%를 혼합하고 메시 망을 상하로 이동시켜 천연석 칼라 도료가 3~8mm의 크기를 가지도록 절단하여 분산시키는 입자 형성 단계.A process for preparing an aqueous colored paint composition comprising the steps of:
(A) a synthetic silica thickener comprising 1.0 to 2.0% by weight of sodium pyrophosphate, 0.01 to 0.2% by weight of defoamer, 10.0 to 20.0% by weight of synthetic silica, 15.0 to 25.0% ) An aqueous gel preparation step of mixing 1.5 to 5.0% by weight of xanthan gum as an anti-settling agent, 10.0 to 25.0% by weight of a water-soluble anti-settling agent consisting of water and 50 to 75% by weight of water;
(B) a synthetic silica thickener comprising 1.0 to 2.0% by weight of sodium pyrophosphate, 0.01 to 0.2% by weight of defoamer, 10.0 to 20.0% by weight of synthetic silica and the balance of water, 5.0 to 10.0% by weight of a synthetic silica thickener, Based surfactant, 1.0 to 5.0% by weight of a urethane-based thickener, 0.1 to 2.0% by weight of a dispersant, 0.2 to 2.0% by weight of a defoaming agent, 10.0 to 20.0% by weight of calcium carbonate, 0.1 to 5.0% (B) 85 to 95% by weight of a water-soluble multicolor paint particle-forming paste composed of 35.0 to 55.0% by weight of an emulsion or an acryl-styrene emulsion, 0.1 to 5.0% by weight of an acrylic emulsion paint film, 1.0 to 5.0% by weight of a dispersing agent, 0.2 to 2.0% by weight of a defoaming agent, 1.0 to 5.0% by weight of an antifoaming agent, 0.01 to 0.2% by weight of an antifoaming agent, 10.0 to 20.0% by weight of a synthetic silica, % Of a pigment, 60.0 to 72.0% by weight of a pigment, and 5 to 15% Color paint manufacturing step;
(C) Particle-forming step of mixing 50.0 to 60.0% by weight of the above-mentioned water-based gel with 40.0 to 50.0% by weight of a natural stone color coating material and moving the mesh screen up and down to cut and disperse the natural stone color coating material so as to have a size of 3-8 mm .
(A) 소지(素地: substrate)의 바탕면에 아크릴 에멀전 또는 아크릴-스티렌 에멀전 하도 도장을 수행하는 단계;
(B) 탄산칼슘과 규사 및 안료와 셀룰로오스 증점제를 포함하는 아크릴-스티렌 에멀전 도료를 스프레이하여 중상도 볼륨 도장을 수행하는 단계;
(C) 상기한 제6항에 따른 수성 다채 무늬 도료 조성물을 스프레이하여 상도 다채 무늬 도장을 수행하는 단계.A natural stone three-dimensional patterning method comprising the steps of:
(A) performing an acrylic emulsion or acrylic-styrene emulsion undercoating on a substrate surface;
(B) spraying an acrylic-styrene emulsion paint containing calcium carbonate, silica and a pigment and a cellulose thickener to perform a heavy phase volume coating;
(C) spraying the aqueous multi-pattern paint composition according to the above-mentioned (6) above to perform topographic patterning.
The method according to claim 7, wherein the substrate is a concrete, a plywood, a gypsum board, or an acrylic plate.