JP2001288415A - Water-based matte coating composition and matte coating method - Google Patents
Water-based matte coating composition and matte coating methodInfo
- Publication number
- JP2001288415A JP2001288415A JP2000102662A JP2000102662A JP2001288415A JP 2001288415 A JP2001288415 A JP 2001288415A JP 2000102662 A JP2000102662 A JP 2000102662A JP 2000102662 A JP2000102662 A JP 2000102662A JP 2001288415 A JP2001288415 A JP 2001288415A
- Authority
- JP
- Japan
- Prior art keywords
- water
- matte coating
- coating composition
- wax
- stone
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、生産効率がよく、
安価で、人や環境に優しい水系艶消しコーティング組成
物と、艶消し風合いを要求される下地面、特に打ち放し
コンクリート面や石材調仕上面及び改修時の磁器タイル
面などに透明性、耐水性、防水性、耐候性に優れ、また
カビや藻などによる汚染防止性に優れた処理面を付与す
ることができる艶消しコーティング方法に関する。TECHNICAL FIELD The present invention has a high production efficiency,
An inexpensive, water-based matte coating composition that is friendly to people and the environment, and the transparency, water resistance, and the like on the ground surface, which is required to have a matte texture, especially on the exposed concrete surface, the stone preparation surface, and the porcelain tile surface during renovation. The present invention relates to a matte coating method capable of providing a treated surface excellent in waterproofness and weather resistance and excellent in prevention of contamination by mold and algae.
【０００２】[0002]
【従来の技術】従来、打ち放しコンクリートや、石材調
仕上面の艶消し用の上塗材として用いる艶消しコーティ
ング組成物は溶剤系が多く使用されている。最近におい
ては環境問題や、安全性などの面から水系化が進み、溶
剤をできるだけ使用しない水系コーティング組成物が強
く望まれるようになっている。この水系コーティング組
成物は合成樹脂エマルションや水溶性樹脂と、艶消し剤
としてシリカ粉末や合成樹脂ビーズ等の微粒子材料によ
り構成されている。2. Description of the Related Art Conventionally, solvent-based matting coating compositions for use as bare coating materials for bare concrete and matting of stone-prepared upper surfaces are often used. In recent years, water-based coatings have been promoted from the viewpoints of environmental problems and safety, and a water-based coating composition using as little solvent as possible has been strongly desired. This aqueous coating composition is composed of a synthetic resin emulsion or a water-soluble resin, and a fine particle material such as silica powder or synthetic resin beads as a matting agent.
【０００３】[0003]
【発明が解決しようとする課題】ところが、シリカ粉末
を含有したコーティング組成物を使用すると、透明性が
悪く下地の外観を大きく損ねたり、光沢が若干残る傾向
がある。また、合成樹脂ビーズを含有したコーティング
組成物では貯蔵安定性が悪く、ビーズが沈降する傾向が
あり、さらにはコストが高い等の問題がある。However, when a coating composition containing a silica powder is used, transparency tends to be poor, and the appearance of a base material is greatly impaired, and gloss tends to remain. Further, a coating composition containing synthetic resin beads has problems such as poor storage stability, tendency of settling of beads, and high cost.
【０００４】[0004]
【課題を解決するための手段】通常、ワックスは従来よ
り広く艶出しのために使用されてきているが、本発明者
らは、溶剤系艶消しコーティング組成物の一部のものに
ワックスが含有されていることに着目した。ワックスは
透明性が高く、安価であるという魅力がある。しかしな
がら、ワックスは有機溶剤に対しては可溶であるが水に
対しては不溶であるため、合成樹脂エマルションや水溶
性樹脂への直接添加では混合が困難であった。本発明者
らは、ワックスと水を多量の分散剤等を用いることによ
り混合して水系艶消しコーティング組成物を得ている
が、耐水性が非常に悪く、建物外部への使用は困難であ
った。Means for Solving the Problems In general, wax has been widely used for polishing, but the present inventors have found that some of solvent-based matte coating compositions contain wax. We paid attention to that. Wax has high transparency and is inexpensive. However, since the wax is soluble in an organic solvent but insoluble in water, it is difficult to mix the wax by direct addition to a synthetic resin emulsion or a water-soluble resin. The present inventors have obtained a water-based matte coating composition by mixing wax and water by using a large amount of a dispersant or the like, but the water resistance is very poor, and it is difficult to use it outside a building. Was.
【０００５】本発明者らは、さらに研究を重ねた結果、
合成樹脂エマルション及び水溶性樹脂から選ばれる少な
くとも１種と、水に天然ワックス及び合成ワックスから
選ばれる少なくとも１種のワックスが分散しているワッ
クス分散液とを混合することにより、生産効率がよく、
安価で、人や環境に優しく、さらには、艶消し風合いを
要求される下地面、特に打ち放しコンクリート面や石材
調仕上面、及び改修が必要とされる磁器タイル面等の上
塗材として、透明性、耐水性、防水性、耐候性に優れ、
カビや藻等による汚染防止性に優れた処理面を付与する
ことができる艶消しコーティング組成物が得られること
の知見を得て本発明を完成させた。本発明は、以下の各
発明を包含する。[0005] As a result of further studies, the present inventors have found that
By mixing at least one selected from a synthetic resin emulsion and a water-soluble resin and a wax dispersion in which at least one wax selected from a natural wax and a synthetic wax is dispersed in water, production efficiency is improved,
Inexpensive, friendly to humans and the environment, and as a topcoat material such as a ground surface that requires a matte texture, especially a bare concrete surface and a stone preparation surface, and a porcelain tile surface that needs renovation, transparency Excellent in water resistance, waterproofness, and weather resistance,
The present invention was completed based on the finding that a matte coating composition capable of providing a treated surface excellent in the prevention of mold and algae contamination was obtained. The present invention includes the following inventions.
【０００６】(1) 合成樹脂エマルション及び水溶性樹脂
から選ばれる少なくとも１種と、水に天然ワックス及び
合成ワックスから選ばれる少なくとも１種のワックスが
分散しているワックス分散液とを含有することを特徴と
する、水系艶消しコーティング組成物。(1) It is required that at least one selected from a synthetic resin emulsion and a water-soluble resin and a wax dispersion in which at least one wax selected from a natural wax and a synthetic wax is dispersed in water. A water-based matte coating composition characterized by the following:
【０００７】(2) 合成樹脂エマルション及び水溶性樹脂
から選ばれる少なくとも１種と、水に天然ワックス及び
合成ワックスから選ばれる少なくとも１種のワックスが
分散しているワックス分散液とを含有することを特徴と
する、打ち放しコンクリート面、石材調仕上面及び磁器
タイル面等の上塗材用の水系艶消しコーティング組成
物。(2) At least one selected from a synthetic resin emulsion and a water-soluble resin, and a wax dispersion in which at least one wax selected from a natural wax and a synthetic wax is dispersed in water. A water-based matte coating composition for an overcoating material, such as a bare concrete surface, a stone material preparation surface, and a porcelain tile surface.
【０００８】(3) 前記ワックス分散液は、ポリエチレン
分散液であることを特徴とする、(1)項又は(2) 項に記
載の水系艶消しコーティング組成物。 (4) 前記水系艶消しコーティング組成物は、該組成物に
おける全固形分中の固形分の５０〜９０重量％を占める
割合の前記合成樹脂エマルション及び水溶性樹脂から選
ばれる少なくとも１種と、該組成物における全固形分中
の固形分の１０〜５０重量％を占める割合の前記ワック
ス分散液とを含有することを特徴とする、(1) 項〜(3)
項のいずれか１項に記載の水系艶消しコーティング組成
物。(3) The water-based matte coating composition according to the above (1) or (2), wherein the wax dispersion is a polyethylene dispersion. (4) The water-based matte coating composition comprises at least one selected from the synthetic resin emulsion and a water-soluble resin in a proportion occupying 50 to 90% by weight of solids in total solids in the composition; (1) to (3), wherein the composition contains the wax dispersion in a proportion of 10 to 50% by weight of the solid content in the total solid content of the composition.
Item 10. The water-based matte coating composition according to any one of the above items.
【０００９】(5) 前記水系艶消しコーティング組成物
は、該組成物における全固形分中の固形分の６０〜８０
重量％を占める割合の前記合成樹脂エマルション及び水
溶性樹脂から選ばれる少なくとも１種と、該組成物にお
ける全固形分中の固形分の２０〜４０重量％を占める割
合の前記ワックス分散液とを含有することを特徴とす
る、(1) 項〜(3) 項のいずれか１項に記載の水系艶消し
コーティング組成物。(5) The water-based matte coating composition has a solid content of 60 to 80 in the total solid content in the composition.
At least one selected from the group consisting of the synthetic resin emulsion and the water-soluble resin in a proportion of 20% by weight, and the wax dispersion in a proportion of 20 to 40% by weight of solids in the total solids in the composition. The water-based matte coating composition according to any one of items (1) to (3), wherein:
【００１０】(6) 前記(1) 項〜(5) 項のいずれか１項に
記載の水系艶消しコーティング組成物を艶消し風合いを
要求される下地面に塗布することを特徴とする艶消しコ
ーティング方法。(6) Matting characterized by applying the water-based matte coating composition according to any one of the above items (1) to (5) to a base surface requiring a matte texture. Coating method.
【００１１】(7) 前記(1) 項〜(5) 項のいずれか１項に
記載の水系艶消しコーティング組成物を打ち放しコンク
リート面、石材調仕上面又は磁器タイル面に塗布するこ
とを特徴とする、艶消しコーティング方法。(7) The water-based matte coating composition according to any one of the above items (1) to (5) is exposed and applied to a concrete surface, a stone preparation surface, or a porcelain tile surface. , Matte coating method.
【００１２】(8) 前記打ち放しコンクリート面に前記水
系艶消しコーティング組成物の付着力向上及び／又はコ
ンクリートのアルカリによる変質防止の機能を有する下
塗材を塗布し、その下塗材上に前記水系艶消しコーティ
ング組成物を塗布することを特徴とする、(7) 項記載の
打ち放しコンクリート面の艶消しコーティング方法。(8) An undercoat material having a function of improving the adhesion of the aqueous mat coating composition and / or preventing deterioration of the concrete due to alkali is applied to the exposed concrete surface, and the aqueous mat is applied on the undercoat material. The matte coating method for a bare concrete surface according to item (7), which comprises applying a coating composition.
【００１３】(9) 前記石材調仕上面は、天然石粉砕骨
材、寒水石、硅砂、着色骨材等と合成樹脂の混合物を単
色又は複数種の単色を組み合わせて製造されている御影
石調、インド砂岩調等の天然石調の風合いを有する石材
調仕上面であることを特徴とする、(6) 項又は(7) 項に
記載の石材調仕上面の艶消しコーティング方法。(9) The stone-prepared upper surface is made of a mixture of a crushed natural stone aggregate, cold water stone, silica sand, a colored aggregate or the like and a synthetic resin in a single color or a combination of a plurality of types of single colors. The matte coating method for a stone-finished upper surface according to the above mode (6) or (7), wherein the surface is a stone-finished upper surface having a natural stone-like texture such as sandstone.
【００１４】(10)前記磁器タイル面に、前記水系艶消し
コーティング組成物の付着力向上機能を有する下塗材を
塗布し、その下塗材上に前記水系艶消しコーティング組
成物を塗布することを特徴とする(6) 項又は(7) 項に記
載の艶消しコーティング方法。(10) An undercoat material having a function of improving the adhesion of the water-based matte coating composition is applied to the porcelain tile surface, and the water-based matte coating composition is applied on the undercoat material. The matte coating method according to the above (6) or (7).
【００１５】[0015]
【発明の実施の形態】本発明の水系艶消しコーティング
組成物は、基本的には、合成樹脂エマルション及び水溶
性樹脂から選ばれる少なくとも１種と、水に天然ワック
ス及び合成ワックスから選ばれる少なくとも１種のワッ
クスが分散しているワックス分散液とを配合した構成を
有することを特徴とするものである。BEST MODE FOR CARRYING OUT THE INVENTION The water-based matte coating composition of the present invention basically comprises at least one selected from a synthetic resin emulsion and a water-soluble resin, and at least one water selected from a natural wax and a synthetic wax. It is characterized by having a configuration in which a wax dispersion in which a kind of wax is dispersed is blended.
【００１６】前記合成樹脂エマルションとしては、従
来、内外部用水系コーティング材の主原料として用いら
れている、ガラス転移温度が−２０〜８０℃、好ましく
は０〜４０℃である合成樹脂を使用することができ、例
示すれば、アクリル酸エステル樹脂、スチレン−アクリ
ル酸エステル共重合樹脂、アクリルウレタン樹脂、ウレ
タン樹脂、アクリルシリコーン樹脂、フッ素樹脂等が挙
げられる。また、水溶性樹脂としては、内部用水系コー
ティング材の主原料として用いられている、ガラス転移
温度が−２０〜８０℃、好ましくは０〜４０℃である合
成樹脂を使用することができ、例えば、アクリル酸エス
テル樹脂、スチレン−アクリス酸エステル共重合樹脂、
アクリルウレタン樹脂、ウレタン樹脂、アクリルシリコ
ーン樹脂、フッ素樹脂等が挙げられる。このような合成
樹脂エマルションや水溶性樹脂の配合割合は、水系艶消
しコーティング組成物の全固形分中、固形分として１０
〜９０重量％を占める範囲であり、好ましくは５０〜９
０重量％を占める範囲である。As the synthetic resin emulsion, there is used a synthetic resin having a glass transition temperature of -20 to 80 ° C., preferably 0 to 40 ° C., which is conventionally used as a main raw material of a water-based coating material for internal and external use. Examples thereof include acrylate resin, styrene-acrylate copolymer resin, acrylic urethane resin, urethane resin, acrylic silicone resin, and fluororesin. Further, as the water-soluble resin, a synthetic resin having a glass transition temperature of −20 to 80 ° C., preferably 0 to 40 ° C., which is used as a main raw material of an internal water-based coating material, can be used. , Acrylate resin, styrene-acrylic acid ester copolymer resin,
Acrylic urethane resin, urethane resin, acrylic silicone resin, fluororesin and the like can be mentioned. The mixing ratio of such a synthetic resin emulsion or water-soluble resin is 10% as a solid content in the total solid content of the water-based matte coating composition.
To 90% by weight, preferably 50 to 9% by weight.
The range occupying 0% by weight.
【００１７】前記ワックス分散液としては、カルナウバ
ワックス、ライスワックス、木ろう等の天然ワックスの
分散液、又は、パラフィンワックス、ポリエチレンワッ
クス、ポリプロピレンワックス等の合成ワックスの分散
液が挙げられるが、コストが安く、耐候性が良いことか
らポリエチレンワックス分散液が好ましい。ワックス分
散液中には耐水性が保持できる量であれば少量の分散剤
が含まれていてもよい。また、ワックスの水への濡れ性
を向上させるために少量の水溶性溶剤を用いてあっても
よい。水系艶消しコーティング組成物中におけるワック
ス分散液の配合割合は、該組成物の全固形分中、固形分
として１０〜５０重量％を占める範囲であり、好ましく
は２０〜４０重量％となる範囲である。Examples of the wax dispersion include a dispersion of a natural wax such as carnauba wax, rice wax, and wax, or a dispersion of a synthetic wax such as paraffin wax, polyethylene wax, and polypropylene wax. However, polyethylene wax dispersions are preferred because they are inexpensive and have good weather resistance. A small amount of a dispersant may be included in the wax dispersion as long as water resistance can be maintained. Further, a small amount of a water-soluble solvent may be used in order to improve the wettability of the wax with water. The mixing ratio of the wax dispersion in the water-based matte coating composition is in the range of occupying 10 to 50% by weight, preferably 20 to 40% by weight as a solid content in the total solid content of the composition. is there.
【００１８】水系艶消しコーティング組成物中におい
て、合成樹脂エマルションの固形分が６０〜８０重量％
で、ワックス分散液の固形分が２０〜４０重量％である
水系艶消しコーティング組成物が、その光沢、耐候性、
耐水白化性等の性能が安定しているので好ましい。In the aqueous matte coating composition, the solid content of the synthetic resin emulsion is 60 to 80% by weight.
The water-based matte coating composition having a wax dispersion having a solid content of 20 to 40% by weight has a gloss, weather resistance,
It is preferable because the performance such as water whitening resistance is stable.
【００１９】本発明の水系艶消しコーティング組成物中
には、前記合成樹脂エマルション及び水溶性樹脂から選
ばれる少なくとも１種とワックス分散液の他に、通常、
この種の水系艶消しコーティング組成物に使用される添
加剤も適宜使用できる。そのような添加剤としては、増
粘剤、分散剤、ｐＨ調整剤、消泡剤の他に、成膜助剤、
凍結安定剤、防腐剤、防黴剤、防藻剤などを使用するこ
とができる。また、水系艶消しコーティング組成物は、
これが有する特性を害さない範囲で、他の充填材、安定
剤等の公知の添加剤を配合することができる。In the water-based matte coating composition of the present invention, in addition to at least one selected from the synthetic resin emulsion and the water-soluble resin and a wax dispersion,
Additives used in this type of water-based matte coating composition can also be appropriately used. Such additives include a thickener, a dispersant, a pH adjuster, a defoaming agent, a film-forming auxiliary,
Freezing stabilizers, preservatives, fungicides, algicides and the like can be used. In addition, the water-based matte coating composition,
Known additives such as other fillers and stabilizers can be blended within a range that does not impair the properties possessed by this.
【００２０】本発明の水系艶消しコーティング組成物
は、つぎのように製造することができる。まず、可変変
速型撹拌機付容器に１〜３０重量％の水を投入する。必
要に応じて高速撹拌状態にして増粘剤、ｐＨ調整剤を添
加して増粘溶液を得る。つぎに、中速撹拌状態にしてこ
の増粘溶液に、合成樹脂エマルション及び／又は水溶性
樹脂を加え、さらに必要に応じて成膜助剤、凍結安定
剤、防腐剤、防黴剤、防藻剤等を加えて撹拌する。つぎ
にワックス分散液及び必要に応じて消泡剤を前記配合比
にて投入し、所定時間撹拌して本発明の水系艶消しコー
ティング組成物を得る。The aqueous matte coating composition of the present invention can be produced as follows. First, 1 to 30% by weight of water is charged into a variable-speed stirrer-equipped container. If necessary, a thickener and a pH adjuster are added under high-speed stirring to obtain a thickened solution. Next, a synthetic resin emulsion and / or a water-soluble resin are added to the thickened solution under a medium-speed stirring state, and if necessary, a film-forming aid, a freeze stabilizer, a preservative, a fungicide, an anti-algae. Add the agent and stir. Next, a wax dispersion and, if necessary, an antifoaming agent are added at the above-mentioned mixing ratio, and the mixture is stirred for a predetermined time to obtain an aqueous matte coating composition of the present invention.
【００２１】上記のように製造される本発明の水系艶消
しコーティング組成物は、打ち放しコンクリート下地面
に塗布することにより、下地面の色、風合いを損ねるこ
となく長期にわたり保護することができる。上記のよう
に保護処理できる下地面としては、打ち放しコンクリー
ト面、石材調仕上面、磁器タイル面、スレート面、サイ
ディングボード面、木部面、金属面等が挙げられる。The water-based matte coating composition of the present invention produced as described above can be protected for a long period of time without impairing the color and texture of the exposed surface by applying it to the exposed concrete surface. Examples of the ground surface that can be protected as described above include a bare concrete surface, a stone preparation surface, a porcelain tile surface, a slate surface, a siding board surface, a wood surface, and a metal surface.
【００２２】本発明の艶消しコーティング組成物は、打
ち放しコンクリート面上に直接塗布するか、又は、打ち
放しコンクリート面に予めコーティング組成物の付着力
を向上させるか、又はコンクリートのアルカリによる変
質防止等の機能を有する下塗材（シーラー）を塗布し、
下塗材上に本発明の水系艶消しコーティング組成物を塗
布することによって、さらに長期にわたりコンクリート
面を保護することができる。The matte coating composition of the present invention may be applied directly to the exposed concrete surface, or may be used to improve the adhesion of the coating composition to the exposed concrete surface in advance, or to prevent alteration of the concrete by alkali. Apply a primer material (sealer) with a function,
By applying the water-based matte coating composition of the present invention on the undercoat material, the concrete surface can be protected for a longer period of time.
【００２３】上記のような下塗材、すなわちシーラーと
して使用できるものとしては、アクリル酸エステル樹脂
系、スチレン−アクリル酸エステル共重合樹脂系、アク
リルウレタン樹脂系、ウレタン樹脂系、アクリルシリコ
ーン樹脂系、シリコーン樹脂系、フッ素樹脂系の下塗材
が挙げられる。本発明の艶消しコーティング方法の場
合、濡れ色を防ぐためには水系シーラーを使うことが好
ましい。また、シーラー塗布前及び／又は浸透性吸水防
止材を使用するとコンクリートの中性化防止効果が向上
するのでさらに好ましい。The undercoating materials as described above, that is, those which can be used as sealers, include acrylate resin resins, styrene-acrylate copolymer resin resins, acrylic urethane resin resins, urethane resin resins, acrylic silicone resin resins, and silicone resins. Resin-based and fluororesin-based undercoat materials are exemplified. In the case of the matte coating method of the present invention, it is preferable to use an aqueous sealer in order to prevent a wet color. In addition, it is more preferable to use a water-absorbing preventive material before applying the sealer and / or because the effect of preventing carbonation of concrete is improved.
【００２４】また、浸透性吸水防止材の塗布後又はシー
ラー塗布後もしくは浸透性吸水防止材を塗布し、さらに
シーラー塗布した後にコンクリート近似色の中塗材（カ
ラークリヤー）を予め塗布することでより安定したコン
クリートの外観、風合いを維持することができる。この
ような中塗材すなわちカラークリヤーとしては、アクリ
ル酸エステル樹脂系、スチレン−アクリル酸エステル共
重合体樹脂系、アクリルウレタン樹脂系、ウレタン樹脂
系、アクリルシリコーン樹脂系、シリコーン樹脂系、ふ
っ素樹脂系などの樹脂に少量の二酸化チタン、少量のカ
ーボンブラック等の顔料が混合分散されているものが挙
げられる。[0024] Further, after applying the permeable water-absorbing preventive material or after applying the sealer or applying the permeable water-absorbing preventive material, and further applying the sealer, the intermediate coating material (color clear) of a color similar to concrete is applied in advance to make it more stable. The appearance and texture of the concrete can be maintained. As such an intermediate coating material, that is, a color clear, an acrylate resin, a styrene-acrylate copolymer resin, an acrylic urethane resin, a urethane resin, an acrylic silicone resin, a silicone resin, a fluororesin, etc. And a resin in which a small amount of pigment such as titanium dioxide and a small amount of carbon black is mixed and dispersed.
【００２５】本発明の水系艶消しコーティング組成物
は、石材調仕上面の上塗材として塗布することにより、
石材調の外観、風合いを損ねることなく、長期にわたり
石材調仕上げ面を保護することができる。The water-based matte coating composition of the present invention is applied as a top coating material on a stone-prepared upper surface,
The stone-finished surface can be protected for a long time without impairing the stone-like appearance and texture.
【００２６】本発明の水系艶消しコーティング組成物
は、磁器タイル面上に直接塗布することにより、長期に
わたり磁器タイル面を保護することができる。また、磁
器タイル面に予めコーティング組成物の付着力向上機能
を有する下塗材を塗布し、下塗材上に本発明の水系艶消
しコーティング組成物を塗布することによって、さらに
長期にわたって磁器タイル面及び目地モルタルを保護す
ることができる。The water-based matte coating composition of the present invention can protect a porcelain tile surface for a long period of time by directly applying it on the porcelain tile surface. Further, by applying an undercoating material having a function of improving the adhesive force of the coating composition on the porcelain tile surface in advance and applying the water-based matte coating composition of the present invention on the undercoating material, the porcelain tile surface and the joint for a longer period of time. Mortar can be protected.
【００２７】このような下塗材、すなわちシーラーとし
て使用できるものとしては、アクリル酸エステル樹脂
系、スチレン−アクリル酸エステル共重合樹脂系、アク
リルウレタン樹脂系、ウレタン樹脂系、アクリルシリコ
ーン樹脂系、シリコーン樹脂系、フッ素樹脂系の下塗材
が挙げられる。また、シーラー塗布前及び／又は後に浸
透性吸水防止材を使用すると、磁器タイルの目地モルタ
ルの中性化防止効果が向上するので好ましい。[0027] Such undercoat materials, that is, those which can be used as sealers, include acrylic resin resins, styrene-acrylic acid ester copolymer resins, acrylic urethane resins, urethane resins, acrylic silicone resins, and silicone resins. And fluororesin-based undercoat materials. It is preferable to use a permeable water absorption preventing material before and / or after the application of the sealer because the effect of preventing the neutralization of the joint mortar of the porcelain tile is improved.
【００２８】[0028]
【実施例】以下、実施例に基づいて本発明をさらに具体
的に説明するが、本発明は、発明の要旨を逸脱しない限
りにおいてこれらの実施例に限定されるものではない。EXAMPLES Hereinafter, the present invention will be described more specifically with reference to examples, but the present invention is not limited to these examples without departing from the gist of the invention.
【００２９】実施例１ 可変変速型撹拌機付容器に、６．７重量％の水を入れて
低速撹拌状態で撹拌しながら増粘剤（商品名「プライマ
ルＴＴ−６１５」ロームアンドハース社）０．２重量％
を添加して１分間撹拌して溶解させる。つぎに、容器内
を中速状態にし、得られた増粘剤水溶液に樹脂固形分４
２重量％のアクリルシリコーン合成樹脂エマルション
（商品名「ポリデュレックスＧ−６１３」旭化成工業社
製）を６７重量％、成膜助剤（商品名「エチレングリコ
ールモノブチルエーテル」和光純薬工業社製）６重量％
を投入して３分間撹拌して均一混合する。つぎに、固形
分４０％平均粒子径約５μｍのポリエチレンワックス分
散液（商品名「ハイディスパーＡ−１１０」岐阜セラッ
ク製造所社製）２０重量％、消泡剤（商品名「アデカネ
ートＢ−１９０」旭電化工業社製）０．１重量％を投入
し、２分間撹拌して水系艶消しコーティング組成物を得
た。Example 1 A thickener (trade name "Primal TT-615", Rohm and Haas Co.) was placed in a variable-speed stirrer-equipped container equipped with 6.7% by weight of water while stirring at a low speed. .2% by weight
And stir for 1 minute to dissolve. Next, the inside of the container was set to a medium-speed state, and a resin solid content of 4 was added to the obtained thickener aqueous solution.
67% by weight of 2% by weight of an acrylic silicone synthetic resin emulsion (trade name "Polydurex G-613" manufactured by Asahi Kasei Kogyo Co., Ltd.) and a film forming aid (trade name "ethylene glycol monobutyl ether" manufactured by Wako Pure Chemical Industries) 6 weight%
And stirred for 3 minutes to mix uniformly. Next, a polyethylene wax dispersion having a solid content of 40% and an average particle diameter of about 5 μm (trade name “HIDISPER A-110” manufactured by Gifu Shellac Mfg. Co., Ltd.) 20% by weight, an antifoaming agent (trade name “Adecanate B-190”) 0.1% by weight (manufactured by Asahi Denka Kogyo KK) was added and stirred for 2 minutes to obtain an aqueous matte coating composition.
【００３０】実施例２ 水８．７重量％、合成樹脂エマルションとして樹脂固形
分４３重量％のスチレン−アクリル共重合体樹脂エマル
ション（商品名「アクリセットＥＸ−３５」日本触媒社
製）６５重量％を使用する以外は、実施例１と同様の方
法により水系艶消しコーティング組成物を得た。Example 2 8.7% by weight of water, 65% by weight of a styrene-acrylic copolymer resin emulsion (trade name: "ACRESET EX-35" manufactured by Nippon Shokubai Co., Ltd.) having a resin solid content of 43% by weight as a synthetic resin emulsion A water-based matte coating composition was obtained in the same manner as in Example 1 except for using.
【００３１】実施例３ 水１８．７重量％、ワックス分散液としてポリエチレン
ワックス分散液（商品名「ハイディスパーＡ−１１０」
岐阜セラック製造所社製）１０重量％とする以外は、実
施例２と同様の方法により水系艶消しコーティング組成
物を得た。Example 3 18.7% by weight of water, polyethylene wax dispersion as a wax dispersion (trade name "High Disper A-110")
A water-based matte coating composition was obtained in the same manner as in Example 2 except that the content was 10% by weight (manufactured by Gifu Shellac Manufacturing Co., Ltd.).
【００３２】実施例４ 水１．７重量％、ワックス分散液としてポリエチレンワ
ックス分散液（商品名「ハイディスパーＡ−１１０」岐
阜セラック製造所社製）２７重量％とする以外は、実施
例２と同様の方法により水系艶消しコーティング組成物
を得た。Example 4 The procedure of Example 2 was repeated except that 1.7% by weight of water and 27% by weight of a polyethylene wax dispersion (trade name “Hi-Disper A-110” manufactured by Gifu Shellac Mfg. Co., Ltd.) were used as the wax dispersion. A water-based matte coating composition was obtained in the same manner.
【００３３】実施例５ 水３．７重量％、合成樹脂エマルションとして、（商品
名「アクリセットＥＸ−３５」日本触媒社製）６０重量
％、ワックス分散液として固形分２７％平均粒子径約８
μｍのライスワックス分散液（商品名「ハイディスパー
Ａ−６３７」岐阜セラック製造所社製）３０重量％とす
る以外は、実施例２と同様の方法により水系艶消しコー
ティング組成物を得た。Example 5 3.7% by weight of water, 60% by weight as a synthetic resin emulsion (trade name "Acreset EX-35" manufactured by Nippon Shokubai Co., Ltd.), 27% solid content as a wax dispersion, and an average particle diameter of about 8
A water-based matte coating composition was obtained in the same manner as in Example 2, except that the thickness was 30% by weight of a μm rice wax dispersion (trade name “High Disper A-637” manufactured by Gifu Shellac Manufacturing Co., Ltd.).
【００３４】実施例６ 水９．７重量％、合成樹脂エマルションに代えて、樹脂
固形分４０重量％の水溶性樹脂（商品名「Ｆ−５２」星
光化学工業社製）７０重量％、成膜助剤（商品名「エチ
レングリコールモノブチルエーテル」和光純薬工業社
製）を０重量％とする以外は、実施例２と同様の方法に
より水系艶消しコーティング組成物を得た。Example 6 In place of 9.7% by weight of water and a synthetic resin emulsion, 70% by weight of a water-soluble resin having a resin solid content of 40% by weight (trade name: "F-52", manufactured by Hoshiko Chemical Co., Ltd.), film formation An aqueous matte coating composition was obtained in the same manner as in Example 2, except that the auxiliary agent (trade name “ethylene glycol monobutyl ether” manufactured by Wako Pure Chemical Industries, Ltd.) was 0% by weight.
【００３５】比較例１ 可変変速型撹拌機付容器に１７．６重量％の水を入れて
低速撹拌状態で撹拌しながら増粘剤（商品名「プライマ
ルＴＴ−６１５」ロームアンドハース社）０．２重量
％、分散剤（商品名「エマルゲン９５０」花王社製）１
重量％を添加して５分間撹拌し、つぎに高速撹拌状態と
してアクリルビーズ（商品名「エポスターＭＡ１００
６」日本触媒工業社製）８重量％、消泡剤（商品名「ア
デカネートＢ−１９０」旭電化工業社製）０．１重量％
を投入し、１０分間高速撹拌を続けてよく分散混合して
ミルベースを得た。つぎに、容器内を中速撹拌状態を
し、得られたミルベースに、アクリルシリコーン合成樹
脂エマルション（商品名「ポリデュレックスＧ−６１
３」旭化成工業社製）６７重量％、成膜助剤（商品名
「エチレングリコールモノブチルエーテル」和光純薬工
業社製）６重量％、消泡剤（商品名「アデカネートＢ−
１９０」旭電化工業社製）０．１重量％を投入して２分
間撹拌した。得られた組成物を１００メッシュのフィル
ターで濾過して均一分散液としての水系艶消しコーティ
ング組成物を得た。COMPARATIVE EXAMPLE 1 A thickener (trade name "Primal TT-615", Rohm and Haas Co.) was placed in a variable-speed stirrer-equipped container with 17.6% by weight of water and stirred under low-speed stirring. 2% by weight, dispersant (trade name "Emulgen 950" manufactured by Kao Corporation) 1
% By weight, followed by stirring for 5 minutes, and then a high-speed stirring state of acrylic beads (trade name “Eposter MA100
6) Nippon Shokubai Kogyo Co., Ltd.) 8% by weight, defoamer (trade name "Adecanate B-190" manufactured by Asahi Denka Kogyo KK) 0.1% by weight
Was added, and high-speed stirring was continued for 10 minutes to thoroughly disperse and mix to obtain a mill base. Next, the inside of the container was stirred at a medium speed, and an acrylic silicone synthetic resin emulsion (trade name: Polydurex G-61) was added to the obtained mill base.
3) 67% by weight of Asahi Kasei Kogyo Co., Ltd., 6% by weight of a film-forming aid (trade name "ethylene glycol monobutyl ether" manufactured by Wako Pure Chemical Industries, Ltd.), and a defoaming agent (trade name "Adecanate B-
190 "(manufactured by Asahi Denka Kogyo Co., Ltd.) and 0.1% by weight were added and stirred for 2 minutes. The resulting composition was filtered through a 100-mesh filter to obtain a water-based matte coating composition as a uniform dispersion.
【００３６】比較例２ 水１９．６重量％、合成樹脂エマルションとして（商品
名「アクリセットＥＸ−３５」日本触媒社製）６５重量
％を使用する以外は、比較例１と同様の方法により水系
艶消しコーティング組成物を得た。Comparative Example 2 An aqueous system was prepared in the same manner as in Comparative Example 1, except that 19.6% by weight of water and 65% by weight of a synthetic resin emulsion (trade name "Acreset EX-35" manufactured by Nippon Shokubai Co., Ltd.) were used. A matte coating composition was obtained.
【００３７】比較例３ 可変変速型撹拌機付容器に１８．６重量％の水を入れて
低速撹拌状態で撹拌しながら増粘剤（商品名「プライマ
ルＴＴ−６１５」ロームアンドハース社）０．２重量
％、分散剤（商品名「エマルゲン９５０」花王社製）２
重量％を添加して５分間撹拌し、つぎに高速撹拌状態と
してシリカ粉末（商品名「サイリシア４４６」富士シリ
シア化学社製）８重量％、消泡剤（商品名「アデカネー
トＢ−１９０」旭電化工業社製）０．１重量％を投入
し、３０分間高速撹拌を続けてよく分散混合してミルベ
ースを得た。つぎに、容器内を中速撹拌状態をし、得ら
れたミルベースに、スチレン−アクリル共重合体合成樹
脂エマルション（商品名「アクリセットＥＸ−３５」日
本触媒社製）６５重量％、成膜助剤（商品名「エチレン
グリコールモノブチルエーテル」和光純薬工業社製）６
重量％、消泡剤（商品名「アデカネートＢ−１９０」旭
電化工業社製）０．１重量％を投入して２分間撹拌し
た。得られた組成物を１００メッシュのフィルターで濾
過して均一分散液としての水系艶消しコーティング組成
物を得た。Comparative Example 3 Thickener (trade name "Primal TT-615", Rohm and Haas Co.) was added to a variable-speed stirrer-equipped container with 18.6% by weight of water and stirred under low-speed stirring. 2% by weight, dispersant (trade name “Emulgen 950” manufactured by Kao Corporation) 2
% Of silica powder (trade name "Sylysia 446" manufactured by Fuji Silysia Chemical Ltd.) and 8% by weight of a defoaming agent (trade name "Adecanate B-190" Asahi Denka) 0.1% by weight (manufactured by Kogyo Co., Ltd.) was added, and high-speed stirring was continued for 30 minutes to thoroughly disperse and mix to obtain a mill base. Next, the inside of the vessel was stirred at a medium speed, and 65% by weight of a styrene-acrylic copolymer synthetic resin emulsion (trade name "Acreset EX-35" manufactured by Nippon Shokubai Co., Ltd.) was added to the obtained mill base. Agent (trade name "ethylene glycol monobutyl ether" manufactured by Wako Pure Chemical Industries, Ltd.) 6
0.1% by weight of an antifoaming agent (trade name "Adecanate B-190" manufactured by Asahi Denka Kogyo Co., Ltd.) and stirred for 2 minutes. The resulting composition was filtered through a 100-mesh filter to obtain a water-based matte coating composition as a uniform dispersion.
【００３８】〈試験方法及び判定基準〉 １．生産効率： 水系艶消しコーティング組成物を１ｋ
ｇ製造するために撹拌した時間の合計で判定した。判定
基準はつぎのとおりである。 ○：１０分未満、△：１０分以上、２０分未満、×：２
０分以上 ２．艶消剤のコスト： 判定基準はつぎのとおりであ
る。 ○：安い、△：やや高い、×：高い ３．貯蔵安定性： 水系艶消しコーティング組成物を１
ｋｇ製造後、２０℃、７日間放置後の状態を目視にて確
認。 ○：異常なし、△：若干の沈降分離が認められる、×：
完全に分離している<Test Method and Criteria> 1. Production efficiency: 1k of water-based matte coating composition
g was determined based on the total time of stirring for production. The criteria are as follows. ：: less than 10 minutes, Δ: 10 minutes or more, less than 20 minutes, ×: 2
0 minutes or more Matting agent cost: The criteria are as follows. ○: cheap, △: slightly expensive, ×: high Storage stability: 1 aqueous matte coating composition
After the production of kg, the condition after standing at 20 ° C. for 7 days was visually checked. ：: No abnormality, △: Slight sedimentation separation observed, ×:
Completely separated
【００３９】４．透明性： 予めスレート板に下塗材と
してダイヤ目地用下塗材（ブラック：恒和化学工業社
製）、及び石材調仕上塗材（ダイヤアールストーン主材
Ａ−３２：恒和化学工業社製）を塗布し、２日間乾燥
後、ダイヤアールストーン主材Ａ−３２面の半面上に水
系艶消しコーティング組成物をスプレーガンにて１２０
ｇ／ｍ2・回で２回塗りし、常温乾燥した。乾燥後、コ
ーティングした面とコーティングしていない面との色差
を目視にて判定した。判定基準は以下のとおりである。 ○：コーティングしている面としていない面も差がない △：コーティングした面の方がやや白い ×：コーティングした面の方がかなり白い4. Transparency: An undercoating material for diamond joints (black: manufactured by Kowa Kagaku Kogyo Co., Ltd.) and a finishing material for stone preparation (diamond stone main material A-32: manufactured by Kowa Kagaku Kogyo Co., Ltd.) are used as undercoating materials on a slate plate in advance. After applying and drying for 2 days, a water-based matte coating composition was sprayed on a half surface of the A-32 main surface of the diamond R stone using a spray gun.
g / m 2 times twice and dried at room temperature. After drying, the color difference between the coated and uncoated surfaces was visually determined. The criteria are as follows. ○: No difference between coated and uncoated surfaces △: Coated surface is slightly white ×: Coated surface is fairly white
【００４０】５．光沢： 隠ぺい率試験紙（日本テスト
パネル社製）上に水系艶消しコーティング組成物を６ミ
ルのアプリケーターにて塗布し、常温乾燥した。乾燥
後、光沢計（日本電色工業社製）を使用し、６０°グロ
スを測定した。判定基準は以下のとおりである。 ○：１０未満、△：１０以上２０未満、×：２０以上5. Gloss: The water-based matte coating composition was applied on an opacity test paper (manufactured by Nippon Test Panel Co., Ltd.) using a 6-mil applicator and dried at room temperature. After drying, the gloss was measured at 60 ° using a gloss meter (manufactured by Nippon Denshoku Industries Co., Ltd.). The criteria are as follows. ：: less than 10, Δ: 10 or more and less than 20, X: 20 or more
【００４１】６．耐水白化性： 予め裏側面をエポキシ
系シール剤でシールしたスレート板に下塗材としてダイ
ヤ目地用下塗材（ブラック：恒和化学工業社製）及び石
材調仕上主材：ダイヤアールストーン主材（Ａ−３２：
恒和化学工業社製）を塗布し、２日間乾燥した。その石
材調主材面上に水系艶消しコーティング組成物をスプレ
ーガンにて１２０ｇ／ｍ2・回で２回塗りし、常温乾燥
した。１日乾燥後、速乾型塗料にて側面をシールして１
時間乾燥し、各試験体を約８０°に設置し、図１に示す
ように、上方から水温２０℃、６００ｍｍ／ｈｒの水を
シャワー状にて８時間散水した。散水終了直後の試験片
表面の状態を目視にて判定した。判定基準は以下のとお
りである。 ○：白化なし、△：薄く白化、×：白化6. Water whitening resistance: An undercoating material for diamond joints (Black: manufactured by Tsuneka Kagaku Kogyo Co., Ltd.) and a stone finishing material: Diamond Earlstone (A) -32:
Co., Ltd.) and dried for 2 days. The water-based matte coating composition was applied twice on the stone-like main material surface at 120 g / m 2 times with a spray gun and dried at room temperature. After drying for 1 day, seal the sides with quick-drying paint
After drying for a time, each specimen was placed at about 80 °, and as shown in FIG. 1, water at a water temperature of 20 ° C. and 600 mm / hr was sprinkled with a shower from above for 8 hours. The state of the test piece surface immediately after the end of watering was visually determined. The criteria are as follows. ：: No whitening, Δ: Light whitening, ×: Whitening
【００４２】７．耐候性： 予め裏側面をエポキシ系シ
ール剤でシールしたスレート板に耐候性の良い白塗料
（ダイヤパーマルＷ：恒和化学工業社製）を塗布した。
１日乾燥後、ダイヤパーマルＷ面上に水系艶消しコーテ
ィング組成物をスプレーガンにて１２０ｇ／ｍ2・回で
２回塗りし、常温乾燥した。１４日間養生後、各試験体
をサンシャインカーボンアーク灯式耐候性試験機（スガ
試験機社製）にて１０００時間照射した後、電子顕微鏡
( 日本電子社製) にて表面状態を確認した。判定基準は
以下のとおりである。 ○：劣化していない、△：やや劣化している、×：劣化
している7. Weather resistance: A white paint (Dia Palmer W: manufactured by Tsuneka Chemical Industry Co., Ltd.) having good weather resistance was applied to a slate plate whose back surface was previously sealed with an epoxy sealant.
After drying for one day, the water-based matte coating composition was applied twice on the surface of the diamond palmal W at a rate of 120 g / m 2 times with a spray gun, and dried at room temperature. After curing for 14 days, each specimen was irradiated with a sunshine carbon arc lamp type weather resistance tester (manufactured by Suga Test Instruments Co., Ltd.) for 1000 hours, and then electron microscope
(Manufactured by JEOL Ltd.) to confirm the surface condition. The criteria are as follows. ：: not deteriorated, や: slightly deteriorated, ×: deteriorated
【００４３】８．付着性−１：舗道ブロックに水系艶消
しコーティング組成物をスプレーガンにて１２０ｇ／ｍ
2・回で２回塗りし、常温乾燥した。１４日間養生後、
塗膜をカッターにて２５マスの碁盤目状（１マス２ｍｍ
四方）にカットし、カットした部分にセロハン粘着テー
プを貼り付け、上方に剥がして舗道ブロック面に残って
いる塗膜のマス目を数える。判定基準はつぎのとおりで
ある。 ○：２１マス以上、△：１６〜２０マス、×：１５マス
以下8. Adhesion-1: 120 g / m2 of water-based matte coating composition on pavement block with spray gun
It was applied twice in two times and dried at room temperature. After curing for 14 days,
The coating film is cut in a grid of 25 squares with a cutter (1 square 2 mm
Cut into four sides), affix cellophane adhesive tape to the cut part, peel off upward and count the number of squares of the coating film remaining on the pavement block surface. The criteria are as follows. ○: 21 or more squares, Δ: 16 to 20 squares, ×: 15 or less squares
【００４４】９．付着性−２：艶有り磁器タイル〔プレ
ーンプラス：（株）ＩＮＡＸ製〕に下塗材（ダイヤロー
レルＰＳシーラーＳ：恒和化学工業社製）を塗布し、１
時間乾燥後、水系艶消しコーティング組成物をスプレー
ガンにて１２０ｇ／ｍ2・回で２回塗りし、常温乾燥し
た。１４日間養生後、塗膜をカッターにて２５マスの碁
盤目状（１マス２ｍｍ四方）にカットし、カットした部
分にセロハン粘着テープを貼り付け、上方に剥がして磁
器タイル面に残っている塗膜のマス目を数える。判定基
準はつぎのとおりである。 ○：２１マス以上、△：１６〜２０マス、×：１５マス
以下9. Adhesion-2: An undercoat material (Dia Laurel PS Sealer S: manufactured by Tsuneka Chemical Industry Co., Ltd.) was applied to a glossy porcelain tile [Plain Plus: manufactured by INAX Corporation]
After drying for an hour, the aqueous matte coating composition was applied twice with a spray gun at 120 g / m 2 times and dried at room temperature. After curing for 14 days, the coating film was cut into a grid of 25 squares (1 square 2 mm square) with a cutter, a cellophane adhesive tape was applied to the cut portion, and the coating was peeled upward and remained on the porcelain tile surface. Count the squares of the membrane. The criteria are as follows. ○: 21 or more squares, Δ: 16 to 20 squares, ×: 15 or less squares
【００４５】表１に、前記実施例及び比較例の９種類の
水系艶消しコーティング組成物の配合処方とそれらの試
験結果を示す。Table 1 shows the formulations of the nine water-based matte coating compositions of the above Examples and Comparative Examples and the test results thereof.
【００４６】[0046]
【表１】 [Table 1]
【００４７】[0047]
【発明の効果】表１から明らかなように、本発明の水系
艶消しコーティング組成物を塗布して形成した塗膜は、
透明性、耐水性、防水性、耐候性に優れていることか
ら、本発明の水系艶消しコーティング組成物は、艶消し
風合いを要求される下地面、特に打ち放しコンクリート
面や石材調仕上面の上塗材として、また、磁器タイル面
の改修時の保護剤などのための上塗材として有用であ
る。また、本発明の水系艶消しコーティング組成物は、
人や環境に優しく、建物外装だけでなく内装仕上材とし
てや改装用としても適用できる。さらに、生産効率がよ
く、安価であることから、現在のニーズの１つとして考
えられる。As is clear from Table 1, the coating film formed by applying the water-based matte coating composition of the present invention is as follows.
Because of its excellent transparency, water resistance, waterproofness, and weather resistance, the water-based matte coating composition of the present invention can be used to coat a base surface requiring a matte texture, particularly a bare concrete surface or a stone-prepared top surface. It is useful as a material and as an overcoating material for a protective agent or the like when renovating a porcelain tile surface. Further, the water-based matte coating composition of the present invention,
It is friendly to people and the environment, and can be applied not only to building exteriors but also to interior finishing materials and renovations. Furthermore, it is considered as one of the current needs because of good production efficiency and low cost.
【図１】散水試験装置モデル図である。FIG. 1 is a model diagram of a watering test device.
フロントページの続き (51)Int.Cl.7 識別記号 ＦＩ テーマコート゛(参考） Ｂ０５Ｄ 7/24 ３０２ Ｂ０５Ｄ 7/24 ３０２Ｇ Ｃ０９Ｄ 5/00 Ｃ０９Ｄ 5/00 Ｆ 5/02 5/02 123/06 123/06 191/06 191/06 (72)発明者 小沢 公男 東京都大田区北糀谷１−９−13 恒和化学 工業株式会社中央研究所内 Ｆターム(参考） 4D075 CA32 CA38 CB02 CB06 DB12 DB14 DC01 EA06 EA07 EA13 EA37 EB13 4J038 BA212 CB022 CC061 CD091 CG141 CJ281 CJ291 DG001 HA156 MA08 MA10 NA01 NA03 NA04 NA05 NA26 PB05 PC04 PC08 Continued on the front page (51) Int.Cl. 7 Identification symbol FI Theme coat II (reference) B05D 7/24 302 B05D 7/24 302G C09D 5/00 C09D 5/00 F 5/02 5/02 123/06 123 / 06 191/06 191/06 (72) Inventor Kimio Ozawa 1-9-13 Kita-Kojiya, Ota-ku, Tokyo Kowa Kagaku Kogyo Co., Ltd. F-term (reference) 4D075 CA32 CA38 CB02 CB06 DB12 DB14 DC01 EA06 EA07 EA13 EA37 EB13 4J038 BA212 CB022 CC061 CD091 CG141 CJ281 CJ291 DG001 HA156 MA08 MA10 NA01 NA03 NA04 NA05 NA26 PB05 PC04 PC08
Claims (8)
ら選ばれる少なくとも１種と、水に天然ワックス及び合
成ワックスから選ばれる少なくとも１種のワックスが分
散しているワックス分散液とを含有することを特徴とす
る、水系艶消しコーティング組成物。1. A composition comprising at least one selected from a synthetic resin emulsion and a water-soluble resin, and a wax dispersion in which at least one wax selected from a natural wax and a synthetic wax is dispersed in water. , A water-based matte coating composition.
ら選ばれる少なくとも１種と、水に天然ワックス及び合
成ワックスから選ばれる少なくとも１種のワックスが分
散しているワックス分散液とを含有することを特徴とす
る、打ち放しコンクリート面用、石材調仕上面用又は磁
器タイル面用の水系艶消しコーティング組成物。2. A composition comprising at least one selected from a synthetic resin emulsion and a water-soluble resin, and a wax dispersion in which at least one wax selected from a natural wax and a synthetic wax is dispersed in water. A water-based matte coating composition for a bare concrete surface, a stone preparation surface, or a porcelain tile surface.
散液であることを特徴とする、請求項１又は２に記載の
水系艶消しコーティング組成物。3. The aqueous matte coating composition according to claim 1, wherein the wax dispersion is a polyethylene dispersion.
全固形分中の固形分の５０〜９０重量％を占める割合の
前記合成樹脂エマルション及び水溶性樹脂から選ばれる
少なくとも１種と、該組成物における全固形分中の固形
分の１０〜５０重量％を占める割合の前記ワックス分散
液とを含有することを特徴とする、請求項１〜３のいず
れか１項に記載の水系艶消しコーティング組成物。4. The water-based matte coating composition according to claim 1,
At least one selected from the synthetic resin emulsion and the water-soluble resin in a proportion occupying 50 to 90% by weight of solids in total solids, and 10 to 50% by weight of solids in total solids in the composition; The water-based matte coating composition according to any one of claims 1 to 3, wherein the wax-based dispersion composition contains a proportion of the wax dispersion.
の水系艶消しコーティング組成物を、艶消し風合いを要
求される下地面に塗布することを特徴とする艶消しコー
ティング方法。5. A matte coating method comprising applying the water-based matte coating composition according to any one of claims 1 to 4 to a base surface requiring a matte texture.
打ち放しコンクリート面、石材調仕上面又は磁器タイル
面であることを特徴とする、請求項５記載の艶消しコー
ティング方法。6. The matte coating method according to claim 5, wherein the ground surface requiring the matte texture is a bare concrete surface, a stone material preparation upper surface, or a porcelain tile surface.
前記水系艶消しコーティング組成物の付着力向上及び／
又はコンクリートのアルカリによる変質防止の機能を有
する下塗材を塗布し、その下塗材上に前記水系艶消しコ
ーティング組成物を塗布することを特徴とする請求項５
又は６に記載の艶消しコーティング方法。7. An improvement in adhesion of the water-based matte coating composition to a base surface requiring the matte texture and / or
Alternatively, an undercoating material having a function of preventing deterioration of concrete due to alkali is applied, and the water-based matte coating composition is applied on the undercoating material.
Or the matte coating method according to 6.
寒水石、硅砂、着色骨材等と合成樹脂の混合物を単色又
は複数種の単色を組み合わせて製造されている御影石
調、インド砂岩調等の天然石調の風合いを有する石材調
仕上面であることを特徴とする、請求項５〜７のいずれ
か１項に記載の艶消しコーティング方法。8. The stone preparation surface is a crushed natural stone aggregate,
It must be a stone-finished surface with a natural stone-like texture, such as granite-like or Indian sandstone-like, which is manufactured by mixing a single color or a mixture of multiple types of synthetic resin with a mixture of synthetic minerals, such as dolomite, silica sand, colored aggregate, etc. The matte coating method according to any one of claims 5 to 7, wherein the matte coating method is characterized in that: