JPH101571A - Agricultural polyolefin resin composition - Google Patents
Agricultural polyolefin resin compositionInfo
- Publication number
- JPH101571A JPH101571A JP8175519A JP17551996A JPH101571A JP H101571 A JPH101571 A JP H101571A JP 8175519 A JP8175519 A JP 8175519A JP 17551996 A JP17551996 A JP 17551996A JP H101571 A JPH101571 A JP H101571A
- Authority
- JP
- Japan
- Prior art keywords
- polyolefin resin
- resin composition
- nonionic surfactant
- agricultural
- fatty acid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、農業用ポリオレフ
ィン系樹脂組成物、更に詳しくは、防曇性を阻害するこ
となく透明性及びブルーム白化性を改良した防曇性農業
用ポリオレフィン系樹脂組成物に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a polyolefin resin composition for agricultural use, and more particularly, to an anti-fogging agricultural polyolefin resin composition having improved transparency and bloom whitening without impairing the anti-fogging property. About.
【０００２】[0002]
【従来の技術】合成樹脂は、その優れた性質のために現
在広い分野で使用されている。しかし、元来合成樹脂表
面は疎水性であるため、形成された製品を使用すると
き、温度や湿度などの条件によっては、水滴が製品表面
に付着し種々の不都合が引き起こされる。例えば、合成
樹脂製フィルムを農業用ハウス又はトンネル栽培などに
利用する場合、地表或いは作物から蒸発した水分が微細
な水滴としてフィルム内表面に付着し、太陽光線の透過
を悪くし、作物の成育を遅らせたり、水滴が作物に落下
することで病害の発生原因となったりする。2. Description of the Related Art Synthetic resins are currently used in a wide variety of fields due to their excellent properties. However, since the synthetic resin surface is originally hydrophobic, when using the formed product, depending on conditions such as temperature and humidity, water droplets adhere to the product surface, causing various inconveniences. For example, when a synthetic resin film is used for an agricultural house or tunnel cultivation, moisture evaporated from the surface or the crop adheres to the inner surface of the film as fine water droplets, impairs the penetration of sunlight, and grows the crop. Delays and drops of water falling on crops can cause disease.
【０００３】上記のような欠点を改良する技術として、
合成樹脂に防曇剤を練り込む方法が知られている。防曇
剤としては、例えば、ソルビタン、ソルビトール、グリ
セリン、ポリグリセリン、ポリエチレングリコール、ポ
リプロピレングリコール、トリメチロールプロパン、ペ
ンタエリスリトールなどの高級脂肪酸エステル、及びこ
れらの高級脂肪酸エステルにアルキレンオキサドを付加
した非イオン系界面活性剤、その他の広範な界面活性剤
が用いられている。[0003] As a technique for improving the above disadvantages,
A method of kneading an antifogging agent into a synthetic resin is known. Examples of anti-fog agents include, for example, higher fatty acid esters such as sorbitan, sorbitol, glycerin, polyglycerin, polyethylene glycol, polypropylene glycol, trimethylolpropane, and pentaerythritol, and nonionic compounds obtained by adding alkylene oxide to these higher fatty acid esters. Based surfactants and a wide variety of other surfactants have been used.
【０００４】しかしながら、これらの防曇剤は樹脂の種
類によって、フィルム表面にブルーム白化し、フィルム
の透明性を阻害している場合がある。この現象はポリオ
レフィン系樹脂、例えばポリエチレン、エチレン−α−
オレフィン共重合体、エチレン−酢酸ビニル共重合体等
の樹脂でこの傾向が強い。この現象を抑えるため、液状
防曇剤を使用したり、防曇剤の添加量を減らすという措
置を講じると、狙いとする防曇性が低下し好ましくな
い。[0004] However, depending on the type of the resin, these antifogging agents may cause whitening of the bloom on the film surface and hinder the transparency of the film. This phenomenon is caused by polyolefin resin, for example, polyethylene, ethylene-α-
This tendency is strong in resins such as olefin copolymers and ethylene-vinyl acetate copolymers. In order to suppress this phenomenon, it is not preferable to use a liquid anti-fogging agent or take measures to reduce the amount of the anti-fogging agent, because the intended anti-fogging property is lowered.
【０００５】[0005]
【発明が解決しようとする課題】本発明は、上記した防
曇性合成樹脂において、防曇性を阻害することなく防曇
剤によるブルーム白化現象を解決した防曇性農業用ポリ
オレフィン系樹脂組成物を提供することを目的とする。DISCLOSURE OF THE INVENTION The present invention relates to an anti-fogging agricultural polyolefin resin composition in which the above-mentioned anti-fogging synthetic resin has solved the bloom whitening phenomenon caused by the anti-fogging agent without impairing the anti-fogging property. The purpose is to provide.
【０００６】[0006]
【課題を解決するための手段】本発明者らは、防曇性農
業用ポリオレフィン系樹脂組成物に関わる上記問題点を
解決すべく鋭意検討を行った結果、農業用ポリオレフィ
ン系樹脂用防曇剤として用いられている界面活性剤の中
の非イオン系界面活性剤と、従来農業用ポリオレフィン
系樹脂組成物として使用例のないアルキルスルホン酸塩
を配合することにより、防曇性を低下させることなく防
曇剤によるブルーム白化現象を改良できることを発見し
本発明の完成に至ったものである。Means for Solving the Problems The present inventors have conducted intensive studies to solve the above problems relating to the anti-fog agricultural polyolefin resin composition, and as a result, have found that the anti-fog agent for agricultural polyolefin resin. By blending a nonionic surfactant among the surfactants used as an alkyl sulfonate, which is not conventionally used as a polyolefin resin composition for agricultural use, without lowering the antifogging property The inventors have found that the bloom whitening phenomenon caused by the antifogging agent can be improved, and have completed the present invention.
【０００７】即ち、本発明に係る農業用ポリオレフィン
系樹脂組成物は、ポリオレフィン系樹脂１００重量部
に対して、非イオン系界面活性剤０．５〜５．０重量部
とアルキルスルホン酸塩０．０５〜０．２５重量部を添
加してなること、非イオン系界面活性剤がソルビタ
ン、ソルビトール、グリセリン、ポリグリセリン、ポリ
エチレングリコール、ポリプロピレングリコール、トリ
メチロールプロパン、ペンタエリスリトールなどの炭素
数８〜２２の高級脂肪酸エステル、及びこれらの高級脂
肪酸エステルにアルキレンオキサイドを付加した非イオ
ン系界面活性剤であること、ポリオレフィン系樹脂が
ポリエチレン、エチレン−α−オレフィン共重合体、エ
チレン−酢酸ビニル共重合体であること、をそれぞれ特
徴とする。That is, the agricultural polyolefin resin composition according to the present invention comprises 0.5 to 5.0 parts by weight of a nonionic surfactant and 0.5 parts by weight of an alkyl sulfonate per 100 parts by weight of the polyolefin resin. 0.5 to 0.25 parts by weight, and the nonionic surfactant has a carbon number of 8 to 22 such as sorbitan, sorbitol, glycerin, polyglycerin, polyethylene glycol, polypropylene glycol, trimethylolpropane, and pentaerythritol. A higher fatty acid ester, and a nonionic surfactant obtained by adding an alkylene oxide to these higher fatty acid esters, and the polyolefin resin is polyethylene, an ethylene-α-olefin copolymer, or an ethylene-vinyl acetate copolymer. , Respectively.
【０００８】[0008]
【発明の実施の形態】本発明に係る防曇性農業用ポリオ
レフィン系樹脂組成物は、ポリエチレン、エチレン−α
−オレフィン共重合体、エチレン−酢酸ビニル共重合体
等のポリオレフィン系樹脂１００重量部に対して、非イ
オン系界面活性剤、即ちソルビタン、ソルビトール、グ
リセリン、ポリグリセリン、ポリエチレングリコール、
ポリプロピレングリコール、トリメチロールプロパン、
ペンタエリスリトールなどの炭素数８〜２２の高級脂肪
酸エステル、及びこれらの高級脂肪酸エステルにアルキ
レンオキサイドを付加した物質を０．５〜５．０重量部
と、アルキルスルホン酸塩０．０５〜０．２５重量部を
添加したものである。アルキルスルホン酸塩としては、
炭素数８〜２０のアルキルスルホン酸のナトリウム、カ
リウム、アンモニウムなどの塩が好ましく用いられる。
尚、本発明の非イオン系界面活性剤は、従来知られた化
合物を特別の制限なく用いることができ、具体例として
は、特公昭５９−３５５７３号第９欄に記載のものなど
を挙げることができる。DETAILED DESCRIPTION OF THE INVENTION The antifogging agricultural polyolefin resin composition according to the present invention comprises polyethylene, ethylene-α.
-Olefin copolymer, 100 parts by weight of a polyolefin resin such as an ethylene-vinyl acetate copolymer, a nonionic surfactant, namely, sorbitan, sorbitol, glycerin, polyglycerin, polyethylene glycol,
Polypropylene glycol, trimethylolpropane,
0.5 to 5.0 parts by weight of a higher fatty acid ester having 8 to 22 carbon atoms such as pentaerythritol, and a substance obtained by adding an alkylene oxide to the higher fatty acid ester; Parts by weight are added. As alkyl sulfonates,
Salts of sodium, potassium, ammonium and the like of alkyl sulfonic acids having 8 to 20 carbon atoms are preferably used.
As the nonionic surfactant of the present invention, conventionally known compounds can be used without any particular limitation. Specific examples include those described in column 9 of JP-B-59-35573. Can be.
【０００９】非イオン系界面活性剤とアルキルスルホン
酸塩の添加量が上記した範囲未満では防曇効果が不十分
であったり、ブルーム白化性を改良することができず、
また、上記した範囲を超える量では経済的ではなく、フ
ィルムが白化したりする。If the amounts of the nonionic surfactant and the alkyl sulfonate are less than the above ranges, the antifogging effect is insufficient or the bloom whitening property cannot be improved.
If the amount exceeds the above range, it is not economical and the film is whitened.
【００１０】尚、本発明のポリオレフィン系樹脂として
は、具体的には低密度、中密度又は高密度ポリエチレン
等のポリエチレン類、例えばエチレン２５〜４５モル％
を含むエチレン−酢酸ビニル共重合体（ケン化度９０％
以上のものがよい）等のオレフィン−ビニルアルコール
系共重合体、エチレン−α−オレフィン共重合体等を挙
げることができ、またアイオノマー樹脂等にも適用する
ことができる。As the polyolefin resin of the present invention, specifically, polyethylenes such as low density, medium density or high density polyethylene, for example, 25 to 45 mol% of ethylene
Ethylene-vinyl acetate copolymer containing 90% saponification degree
Olefin-vinyl alcohol-based copolymers, ethylene-α-olefin copolymers, and the like, and also applicable to ionomer resins and the like.
【００１１】尚また、本発明に係る農業用ポリオレフィ
ン系樹脂組成物では、上記した防曇剤の外に酸化防止剤
（例えば、フェノール系化合物）、紫外線吸収剤（例え
ばベンゾフェノン系、ベンゾトリアゾール系化合物）、
光安定剤（例えばヒンダードアミン系化合物）、光透過
性向上剤（例えばβ−ジケトン化合物）、可塑剤（例え
ば、グリセリン、エチレングリコール、トリエチレング
リコール、ソルビトール等の分子量２５０以下の低分子
量多価アルコールやフタル酸エステル等）、滑剤、熱安
定剤、帶電防止剤、顔料、染料などの種々の目的の添加
剤を単独で又は併用することは何ら差し支えない。これ
らの例としては特開昭５５−８６７５０号、同５８−８
２７５４号、特公昭６３−６５０２６号などに記載され
た各種化合物が挙げられる。In the agricultural polyolefin resin composition according to the present invention, an antioxidant (eg, a phenolic compound) and an ultraviolet absorber (eg, a benzophenone-based or benzotriazole-based compound) are provided in addition to the above-described anti-fogging agent. ),
Light stabilizers (eg, hindered amine compounds), light transmittance improvers (eg, β-diketone compounds), plasticizers (eg, glycerin, ethylene glycol, triethylene glycol, low molecular weight polyhydric alcohols having a molecular weight of 250 or less such as sorbitol, and the like) Various additives such as phthalic acid esters, lubricants, heat stabilizers, antistatic agents, pigments and dyes may be used alone or in combination. Examples thereof are described in JP-A-55-86750 and JP-A-58-8.
2754, and various compounds described in JP-B-63-65026.
【００１２】更に、本発明の目的を損なわない範囲で、
本発明外の界面活性剤を併用してもよい。更にまた、本
発明に係る農業用ポリオレフィン系樹脂組成物をフィル
ムとした場合の当該フィルムの厚みについては特別の制
限がない。Further, within a range not to impair the object of the present invention,
A surfactant other than the present invention may be used in combination. Furthermore, when the agricultural polyolefin resin composition according to the present invention is used as a film, there is no particular limitation on the thickness of the film.
【００１３】[0013]
【実施例】次に実施例により本発明を説明するが、本発
明に係る防曇性農業用ポリオレフィン系樹脂組成物は、
これらの実施例に限定されるものではない。尚、実施例
の説明において「部」とは「重量部」を意味する。The present invention will now be described by way of examples. The antifogging agricultural polyolefin resin composition according to the present invention comprises:
It is not limited to these examples. In the description of the embodiments, “parts” means “parts by weight”.
【００１４】次の配合の防曇剤部分に本発明品と比較品
をそれぞれ加えたフィルムを作成し防曇性及びブルーム
白化性を評価した。Films were prepared by adding the product of the present invention and the comparative product to the antifogging agent portion of the following formulation, and the antifogging property and the bloom whitening property were evaluated.
【００１５】 配合処方 ＥＶＡ（三菱油化社製 Ｖ４０１Ｈ） １００部 防曇剤 １部 防曇剤としては、実施例１〜５の製剤及び比較例１〜５
の化合物を用いた。これらの防曇剤の内容を表１に示
す。Formulation Formulation EVA (V401H manufactured by Mitsubishi Yuka Co., Ltd.) 100 parts Antifogging agent 1 part As the antifogging agent, the preparations of Examples 1 to 5 and Comparative Examples 1 to 5
Was used. Table 1 shows the contents of these antifogging agents.
【００１６】[0016]
【表１】 [Table 1]
【００１７】アルキルスルホン酸ナトリウムは、東邦化
学工業株式会社製アンステックスＨＴ−１００を用い
た。As the sodium alkyl sulfonate, Anstex HT-100 manufactured by Toho Chemical Industry Co., Ltd. was used.
【００１８】（評価方法） 低温防曇性： １００ｍｌのビーカーに２０℃の水を満
たし、フィルムを張り、輪ゴムで固定したものを０℃の
恒温室に入れ、水滴の着き具合を◎、○、△、×、××
の５点法で評価。◎は表面が均一に濡れ水滴を全く認め
ない状態。××は、全面に小さな水滴が付着している状
態。○〜△〜×はそれぞれの中間の状態。(Evaluation method) Low-temperature antifogging property: A 100 ml beaker was filled with water at 20 ° C, a film was stretched, and a film fixed with a rubber band was placed in a constant temperature room at 0 ° C. △, ×, XX
Of the five-point method. ◎ indicates that the surface was uniformly wet and no water droplets were observed. XX indicates a state in which small water droplets adhere to the entire surface. ○ ~ △ ~ × are intermediate states of each.
【００１９】高温防曇性： ５００ｍｌのマヨネーズ瓶
に水を満たしフィルムを張り、輪ゴムで固定したものを
５０℃の恒温水槽に入れて放置し、経時的に水滴のつき
具合を上記と同様の５点法で評価。High temperature anti-fog property: A 500 ml mayonnaise bottle was filled with water, covered with a film, fixed with a rubber band, placed in a constant temperature water bath at 50 ° C. and allowed to stand. Evaluated by the point method.
【００２０】ブルーム白化性： フィルムを３０℃、３
０日間保存した時のフィルム表面の白化性を上記と同様
の５点法で評価。Bloom whitening: The film was heated at 30 ° C. for 3 hours.
The whitening property of the film surface when stored for 0 days was evaluated by the same 5-point method as described above.
【００２１】評価結果： 表１に示した配合処方におけ
る結果を表２に示す。Evaluation results: Table 2 shows the results of the formulation shown in Table 1.
【００２２】[0022]
【表２】 [Table 2]
【００２３】表２の結果から明らかなように、本発明品
を用いたフィルムは防曇剤によるブルーム白化がなく、
防曇性も優れていた。As is clear from the results in Table 2, the film using the product of the present invention was free from bloom whitening due to the antifoggant,
The antifogging property was also excellent.
【００２４】[0024]
【発明の効果】本発明に係る農業用ポリオレフィン系樹
脂組成物により農業用フィルムを形成すれば、防曇性を
阻害することなく防曇剤によるブルーム白化現象を防止
することができ頭記した課題が解決される。According to the present invention, when an agricultural film is formed from the agricultural polyolefin resin composition according to the present invention, the blooming phenomenon caused by the antifogging agent can be prevented without inhibiting the antifogging property. Is resolved.
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.6 識別記号 庁内整理番号 ＦＩ 技術表示箇所 Ｃ０８Ｋ 5/42 ＫＦＧ Ｃ０８Ｋ 5/42 ＫＦＧ ──────────────────────────────────────────────────続 き Continued on the front page (51) Int.Cl. 6 Identification code Agency reference number FI Technical display location C08K 5/42 KFG C08K 5/42 KFG
Claims (3)
て、非イオン系界面活性剤０．５〜５．０重量部とアル
キルスルホン酸塩０．０５〜０．２５重量部を添加して
なることを特徴とする農業用ポリオレフィン系樹脂組成
物。(1) To 100 parts by weight of a polyolefin resin, 0.5 to 5.0 parts by weight of a nonionic surfactant and 0.05 to 0.25 parts by weight of an alkyl sulfonate are added. A polyolefin resin composition for agricultural use characterized by the following.
ビトール、グリセリン、ポリグリセリン、ポリエチレン
グリコール、ポリプロピレングリコール、トリメチロー
ルプロパン、ペンタエリスリトールなどの炭素数８〜２
２の高級脂肪酸エステル、及びこれらの高級脂肪酸エス
テルにアルキレンオキサイドを付加した非イオン系界面
活性剤であることを特徴とする請求項１に記載の農業用
ポリオレフィン系樹脂組成物。2. The nonionic surfactant has a carbon number of 8 to 2 such as sorbitan, sorbitol, glycerin, polyglycerin, polyethylene glycol, polypropylene glycol, trimethylolpropane and pentaerythritol.
2. The agricultural polyolefin resin composition according to claim 1, which is a higher fatty acid ester of No. 2, and a nonionic surfactant obtained by adding an alkylene oxide to these higher fatty acid esters.
チレン−α−オレフィン共重合体、エチレン−酢酸ビニ
ル共重合体である請求項１記載の農業用ポリオレフィン
系樹脂組成物。3. The agricultural polyolefin resin composition according to claim 1, wherein the polyolefin resin is polyethylene, ethylene-α-olefin copolymer or ethylene-vinyl acetate copolymer.