JPH04236300A - プランジャー装置用粉末潤滑剤 - Google Patents

プランジャー装置用粉末潤滑剤

Info

Publication number
JPH04236300A
JPH04236300A JP3018450A JP1845091A JPH04236300A JP H04236300 A JPH04236300 A JP H04236300A JP 3018450 A JP3018450 A JP 3018450A JP 1845091 A JP1845091 A JP 1845091A JP H04236300 A JPH04236300 A JP H04236300A
Authority
JP
Japan
Prior art keywords
lubricant
compound
powder
base material
plunger
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP3018450A
Other languages
English (en)
Inventor
Takashi Hanano
花野　孝
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Hanano Shoji KK
Original Assignee
Hanano Shoji KK
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Hanano Shoji KK filed Critical Hanano Shoji KK
Priority to JP3018450A priority Critical patent/JPH04236300A/ja
Priority to US07/675,767 priority patent/US5154839A/en
Priority to KR9105008A priority patent/KR930011934B1/ko
Priority to GB9107005A priority patent/GB2251862B/en
Priority to CA002040372A priority patent/CA2040372C/en
Priority to DE4112408A priority patent/DE4112408C2/de
Publication of JPH04236300A publication Critical patent/JPH04236300A/ja
Priority to HK110695A priority patent/HK110695A/xx
Pending legal-status Critical Current

Abstract

(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。

Description

【発明の詳細な説明】
【０００１】
【産業上の利用分野】本発明は、ダイカスト作業におい
て用いるダイカスト装置のプランジャー装置のプランジ
ャーチップ表面やスリーブ内面に吹付けて用いる潤滑剤
に関するものである。
【０００２】
【従来の技術】図１に示すように、プランジャー装置１
は、ダイカスト作業において金型内に溶湯を注入するた
めの装置であり、固定側金型２内に連通するスリーブ１
１と、スリーブ１１内を摺動してスリーブ１１内に給湯
口１１ａから供給された溶湯を金型内に押出すプランジ
ャーチップ１２とで構成されている。なお３は移動側金
型である。
【０００３】ところでダイカスト法は高精度の鋳造品を
連続して且つ大量に製造できるので、自動車、電気機器
、家庭用品、建材等の各種部品の製造に多く利用されて
いる。そしてこのダイカスト法においては、プランジャ
ー装置により、溶融金属即ち溶湯を高速で成形型の金型
内に押込んでいる。このとき、スリーブ内のプランジャ
ーチップの摺動を円滑に行なわせ且つ摩耗を防止するた
めに、プランジャー装置用潤滑剤が用いられている。
【０００４】プランジャー装置用潤滑剤は一般に油性潤
滑剤と水溶性潤滑剤に大別される。両潤滑剤は共に鉱物
油、天然油脂、ワックス、合成潤滑油等を基材とし、油
性潤滑剤にあってはこれに極圧性付与剤、摩耗防止剤が
添加され、水溶性潤滑剤にあっては水、界面活性剤が添
加されてなるものである。
【０００５】
【発明が解決しようとする問題点】ところで近年ダイカ
スト技術の進歩、合金の進歩等に合せてコスト低減、不
良率低減、軽量化等を中心としたダイカスト製品の高品
質化が要望されるようになってきた。そして従来のプラ
ンジャー装置用潤滑剤ではそのような要望を満足させら
れなくなってきた。
【０００６】即ち油性潤滑剤及び水溶性潤滑剤では共に
、発生するガスに起因して製品内部に欠陥が生じ、この
ため例えば軽量化に伴う耐圧強度を阻害したり、より高
速化する作業サイクルに対応できないという問題があっ
た。また水溶性潤滑剤においては、水残りに起因して製
品内部に欠陥が生じる可能性が高いという問題があり、
更には使用後の水質汚濁防止のために廃水処理を必要と
しそのための設備投資等の諸経費を必要とするという問
題があった。また油性潤滑剤においては、発煙、火災の
危険性が高く、安全性に問題があり、更には作業環境を
汚染するという問題があった。そこで新しい形態のプラ
ンジャー装置用潤滑剤が強く望まれるようになってきた
。
【０００７】本発明は以上のような点に鑑みて鋭意研究
し各種の系統的実験を行なった結果なされたもので、ダ
イカスト法においてより高品質の鋳造品を環境を悪化さ
せることなく且つ作業性良く得るために用いられるプラ
ンジャー装置用潤滑剤、即ち具体的には製品内部欠陥の
発生を確実に防止でき、火災等の危険や環境汚染を防止
でき、更にはプランジャーチップの摺動を円滑にして作
業性を向上できるプランジャー装置用粉末潤滑剤を提供
することを目的とする。
【０００８】
【問題点を解決するための手段】本発明のプランジャー
装置用粉末潤滑剤は、固体で潤滑剤として用いられる無
機化合物からなる粉末状又は顆粒状の潤滑剤基材と、潤
滑剤基材に付着性を付与する有機化合物とを混合してな
る潤滑剤であって、両者とも粉末状又は顆粒状の形態を
有し、又は潤滑剤基材が有機化合物により被覆された形
態を有することを特徴とするものである。このような潤
滑剤は、図１に示すように、プランジャーチップ１２表
面や給湯口１１ａを通してスリーブ１１内面に、通常の
スプレー方式や静電式スプレー方式により噴霧して用い
られる。なお４は噴霧するためのノズルである。
【０００９】本発明の最大の特徴は、潤滑剤基材が粉末
状又は顆粒状の形態を有することである。
【００１０】そして有機化合物の無機化合物に対する含
有割合は、０．１〜５０重量％の範囲から選択するのが
有効である。０．１重量％より小さいと無機化合物のプ
ランジャーチップ表面やスリーブ内面に対する付着効果
が充分には得られず、５０重量％より大きいとガスの発
生により製品内部欠陥を生じる恐れがあるからである。
【００１１】本発明で用い得る潤滑剤基材は、固体で潤
滑剤として用いられる無機化合物であれば特に制限はな
い。一般には窒化ホウ素、フッ化物、タルク、雲母、金
属酸化物、窒化ケイ素、ホウ素化合物、硫黄化合物、リ
ン化合物が好ましく用いられるが、その他従来から潤滑
剤として用いられている公知の固体潤滑剤、例えばグラ
ファイト、二硫化モリブデン等も用いることができる。 そしてこれらの無機化合物は粉末状又は顆粒状の形態で
、その１種類のみが、又は２種類以上が組合せて用いら
れる。
【００１２】また本発明で用い得る有機化合物は、上述
のような無機化合物に付着性、転着性を付与する性質を
有するものであれば、特に制限はない。一般には金属石
鹸、高分子化合物、及び液体状又はペースト状の化合物
をサイクロデキストリン化合物により粉末状又は顆粒状
としたものが好ましく用いられる。金属石鹸としてはカ
ルボン酸骨格にナトリウム、カルシウム、アルミニウム
、バリウム、リチウム、カリウム、マグネシウム、又は
亜鉛を付加してなるものが、また高分子化合物としては
ポリエチレン、ポリプロピレン、エポキシ樹脂、ケイ素
樹脂、天然ワックス、フェノール樹脂、アクリル樹脂、
アルキッド樹脂、ポリウレタン樹脂、又はポリスチレン
樹脂が、また液体状又はペースト状の化合物としては、
合成エステル類、天然油脂類、鉱物油類、シリコンオイ
ル、ポリフェニルエーテル、ポリアルキレングリコール
、又はエチレン−プロピレン共重合体が特に好ましく用
いられる。そしてこれらの有機化合物は、粉末状又は顆
粒状の形態で潤滑剤基材と混合され、又は加熱溶融され
た状態で潤滑剤基材と混合される。従って本発明の潤滑
剤は、潤滑剤基材と有機化合物の両方が粉末状又は顆粒
状の形態を有し、又は粉末状又は顆粒状の潤滑剤基材が
有機化合物により被覆された形態を有することとなる。 なお有機化合物は、上述した化合物の１種類のみが、又
は２種類以上が組合せて用いられる。金属石鹸と、高分
子化合物と、粉末化された液体状又はペースト状の化合
物とを組合せて用いてもよい。
【００１３】
【作用】本発明のプランジャー装置用粉末潤滑剤は少な
くとも潤滑剤基材が粉末状又は顆粒状の形態を有してい
るので、熱が加わっても反応しにくくガスを殆んど発生
しない。このため製品内部にガスに起因する巣が発生す
ることはない。また本発明の潤滑剤は無機化合物と有機
化合物とからなり水分や低分子量物質を含有してはいな
い。従って製品内部欠陥の発生は防止され、製品の品質
は向上する。
【００１４】また本発明の潤滑剤は粉末状又は顆粒状の
形態を有しており水分を含有してはいないので、水溶性
潤滑剤のように使用後に水質を汚染することはなく、油
性潤滑剤のように作業環境を汚染することもない。従っ
て廃水処理のための経費、環境悪化防止のための経費は
不要となる。更に本発明の潤滑剤は油性のものを含有し
てはいないので、発煙、火災の危険性はなく、安全性も
問題ない。
【００１５】更に本発明の潤滑剤は少なくとも潤滑剤基
材が粉末状又は顆粒状の形態を有しているので、潤滑剤
が付着されたプランジャーチップ表面やスリーブ内面で
はプランジャーチップとスリーブとの間が確実に少なく
とも潤滑剤基材の粉末又は顆粒の粒子径だけ隔てられる
こととなる。従ってプランジャーチップとスリーブとの
接触が防止され、摺動時における熔着、摩耗が防止され
、摺動運動が円滑となり、作業性が向上する。
【００１６】
【発明の効果】本発明によれば無機化合物からなる潤滑
剤基材と有機化合物との混合物からなるプランジャー装
置用粉末潤滑剤を、少なくとも潤滑剤基材が粉末状又は
顆粒状の形態を有するものとしたので、ダイカスト法に
より得られる例えばアルミニウム合金や亜鉛合金等の鋳
造品の内部欠陥の発生を確実に防止してその品質を向上
させることができ、しかもダイカスト法による鋳造をよ
り作業性良く行なわせることができ、更には使用中及び
使用後における環境の悪化を充分に防止することができ
る。
【００１７】特に有機化合物の無機化合物に対する含有
割合を０．１〜５０重量％の範囲とすることにより、得
られる鋳造品の品質をより良好なものにすることができ
る。更に無機化合物として、窒化ホウ素、フッ化物、タ
ルク、雲母、金属酸化物、窒化ケイ素、ホウ素化合物、
硫黄化合物、リン化合を、また有機化合物として、カル
ボン酸骨格にナトリウム、カルシウム、アルミニウム、
バリウム、リチウム、カリウム、マグネシウム、又は亜
鉛を付加してなる金属石鹸や、ポリエチレン、ポリプロ
ピレン、エポキシ樹脂、ケイ素樹脂、天然ワックス、フ
ェノール樹脂、アクリル樹脂、アルキッド樹脂、ポリウ
レタン樹脂、又はポリスチレン樹脂である高分子化合物
や、合成エステル類、天然油脂類、鉱物油類、シリコン
オイル、ポリフェニルエーテル、ポリアルキレングリコ
ール、又はエチレン−プロピレン共重合体である液体状
又はペースト状の化合物をサイクロデキストリン化合物
により粉末状又は顆粒状としたものを用いることにより
、上記効果をより良好に発揮することができる。そして
上記の無機化合物、有機化合物の内、それぞれ２種類以
上のものを組合せて用いることにより、各ダイカスト作
業においてより最適に用い得る潤滑剤を得ることができ
る。
【００１８】
【実施例】以下、本発明の実施例を示すが、本発明はこ
れに限定されるものではない。次に示す（Ａ）〜（Ｆ）
の潤滑剤を得、これらの潤滑剤を用いてダイカスト法に
よるアルミニウム合金の鋳造を行ない、［表］に示す各
項目について比較検討した。
【００１９】本発明の例である（Ａ）〜（Ｄ）の混合物
としては、用いる有機化合物を粉末状又は顆粒状の形態
で無機化合物に混合したものと、加熱溶融した状態で無
機化合物に混合したものとの両方を得、それぞれについ
て検討したが、結果は両者とも同じであった。なお（Ｄ
）の有機化合物としては、天然油脂をサイクロデキスト
リン化合物を用いて実験的手法で粉末化したものを用い
たが、他の各化合物は市販のものである。
【００２０】（Ａ）雲母（平均粒度６μ）９０部と、ポ
リエチレン１０部との混合物からなる本発明の第１の例
、 （Ｂ）窒化ホウ素１０部と、雲母６０部と、ステアリン
酸カルシウム３０部との混合物からなる本発明の第２の
例、 （Ｃ）タルク７０部と、窒化ケイ素１０部と、天然ワッ
クス１０部と、ステアリン酸亜鉛１０部との混合物から
なる本発明の第３の例、 （Ｄ）窒化ホウ素２０部と、タルク６０部と、ホウ酸ナ
トリウム５部と、粉末化天然油脂１５部との混合物から
なる本発明の第４の例、 （Ｅ）窒化ホウ素のみ（比較例１）、 （Ｆ）鉱物油、天然油、摩耗防止剤からなる市販のプラ
ンジャー装置用油性潤滑剤（比較例２）、
【図面の簡単な説明】
【図１】プランジャー装置に本発明の潤滑剤をスプレー
している状態を示す断面図である。
【符号の説明】
１　　プランジャー装置 ２　　固定側金型 ３　　移動側金型 ４　　ノズル １１　　スリーブ １１ａ　　給湯口 １２　　プランジャーチップ

Claims (7)

    【特許請求の範囲】
  1. 【請求項１】固体で潤滑剤として用いられる無機化合物
    からなる粉末状又は顆粒状の潤滑剤基材と、潤滑剤基材
    に付着性を付与する有機化合物とを混合してなる潤滑剤
    であって、両者とも粉末状又は顆粒状の形態を有し、又
    は潤滑剤基材が有機化合物により被覆された形態を有す
    ることを特徴とするプランジャー装置用粉末潤滑剤。
  2. 【請求項２】有機化合物を無機化合物に対して０．１〜
    ５０重量％の割合で含有した請求の範囲１項記載のプラ
    ンジャー装置用粉末潤滑剤。
  3. 【請求項３】無機化合物としては、窒化ホウ素、フッ化
    物、タルク、雲母、金属酸化物、窒化ケイ素、ホウ素化
    合物、硫黄化合物、リン化合物のうち、１種類以上が用
    いられる請求の範囲１項又は２項記載のプランジャー装
    置用粉末潤滑剤。
  4. 【請求項４】有機化合物としては、複数種類の金属石鹸
    、複数種類の高分子化合物、液体状又はペースト状の化
    合物をサイクロデキストリン化合物により粉末状又は顆
    粒状としたもののうち、１種類以上が用いられる請求の
    範囲１項ないし３項のいずれかに記載のプランジャー装
    置用粉末潤滑剤。
  5. 【請求項５】金属石鹸は、カルボン酸骨格にナトリウム
    、カルシウム、アルミニウム、バリウム、リチウム、カ
    リウム、マグネシウム、又は亜鉛を付加してなるもので
    ある請求の範囲４項記載のプランジャー装置用粉末潤滑
    剤。
  6. 【請求項６】高分子化合物は、ポリエチレン、ポリプロ
    ピレン、エポキシ樹脂、ケイ素樹脂、天然ワックス、フ
    ェノール樹脂、アクリル樹脂、アルキッド樹脂、ポリウ
    レタン樹脂、又はポリスチレン樹脂である請求の範囲４
    項又は５項記載のプランジャー装置用粉末潤滑剤。
  7. 【請求項７】液体状又はペースト状の化合物は、合成エ
    ステル類、天然油脂類、鉱物油類、シリコンオイル、ポ
    リフェニルエーテル、ポリアルキレングリコール、又は
    エチレン−プロピレン共重合体である請求の範囲４項な
    いし６項のいずれかに記載のプランジャー装置用粉末潤
    滑剤。
JP3018450A 1991-01-17 1991-01-17 プランジャー装置用粉末潤滑剤 Pending JPH04236300A (ja)