GB1034094A - Self-lubricating article and means for its manufacture - Google Patents
Self-lubricating article and means for its manufactureInfo
- Publication number
- GB1034094A GB1034094A GB11926/63A GB1192663A GB1034094A GB 1034094 A GB1034094 A GB 1034094A GB 11926/63 A GB11926/63 A GB 11926/63A GB 1192663 A GB1192663 A GB 1192663A GB 1034094 A GB1034094 A GB 1034094A
- Authority
- GB
- United Kingdom
- Prior art keywords
- degraded
- temperature
- ptfe
- hours
- mixture
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Abstract
1,034,094. Bearings. POLYMER CORPORATION. March 26, 1963 [April 13, 1962], No. 11926/63. Heading F2A. [Also in Division H2] A self-lubricated article, such as a bearing or a brush for an electric motor, comprises a sintered metal and thermally degraded polytetrafluoroethylene contained in the interstices of the sintered metal. The thermally degraded PTFE is prepared by heating the resin to a temperature between 1000 and 1500 F. for a period up to one half-hour and allowing the resulting liquid to cool to room temperature. The degraded material is ground to a convenient particle size and reheated to a temperature between 600 and 800 F. to oxidize any free carbonaceous material and to volatilize any low boiling materials. As an alternative to cooling to room temperature, the degraded material may be cooled to a temperature of 600 to 800 F. which is maintained for an adequate time to obtain the same result. The degraded PTFE is milled until it will pass an 80-mesh screen and mixed with finely divided silver and cadmium oxide. After milling the mixture for about three hours and passing it through a 325- mesh screen, slugs of inch diameter and length are pressed from it at a pressure of about 25 tons per square inch before sintering for two hours at 720 F. The PTFE constitutes 9À6% of the volume of the mixture and the silver and cadmium oxide 79À5 and 10À9% respectively.
Applications Claiming Priority (1)
| Application Number | Priority Date | Filing Date | Title |
|---|---|---|---|
| US18718362A | 1962-04-13 | 1962-04-13 |
Publications (1)
| Publication Number | Publication Date |
|---|---|
| GB1034094A true GB1034094A (en) | 1966-06-29 |
Family
ID=22687930
Family Applications (1)
| Application Number | Title | Priority Date | Filing Date |
|---|---|---|---|
| GB11926/63A Expired GB1034094A (en) | 1962-04-13 | 1963-03-26 | Self-lubricating article and means for its manufacture |
Country Status (5)
| Country | Link |
|---|---|
| CH (1) | CH418738A (en) |
| DE (1) | DE1246255B (en) |
| FR (1) | FR1355167A (en) |
| GB (1) | GB1034094A (en) |
| SE (1) | SE307016B (en) |
Families Citing this family (5)
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| GB1599399A (en) * | 1977-05-13 | 1981-09-30 | Johnson Matthey Co Ltd | Production of metallic articles |
| DE2948485C2 (en) * | 1979-12-01 | 1993-10-28 | Scharwaechter Gmbh Co Kg | Door stops for vehicle doors |
| JP2907999B2 (en) * | 1990-11-16 | 1999-06-21 | 日立粉末冶金株式会社 | High temperature sintered plain bearings |
| US5207513A (en) * | 1990-11-30 | 1993-05-04 | Ntn Corporation | Rolling bearing with solid lubricant |
| DE4412715C1 (en) * | 1994-04-13 | 1995-08-17 | Degussa | Noble metal material free from allergenic heavy metal for making jewellery |
Family Cites Families (1)
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| DE962561C (en) * | 1949-01-11 | 1957-05-23 | Glacier Co Ltd | Plain bearing made of at least porous metal on the surface, which contains a friction-reducing substance |
-
1963
- 1963-03-26 GB GB11926/63A patent/GB1034094A/en not_active Expired
- 1963-04-08 SE SE3851/63A patent/SE307016B/xx unknown
- 1963-04-11 CH CH466763A patent/CH418738A/en unknown
- 1963-04-11 FR FR931319A patent/FR1355167A/en not_active Expired
- 1963-04-13 DE DEP31584A patent/DE1246255B/en active Pending
Also Published As
| Publication number | Publication date |
|---|---|
| CH418738A (en) | 1966-08-15 |
| SE307016B (en) | 1968-12-16 |
| DE1246255B (en) | 1967-08-03 |
| FR1355167A (en) | 1964-03-13 |
Similar Documents
| Publication | Publication Date | Title |
|---|---|---|
| GB1037306A (en) | Electrically conductive tetrafluoroethylene polymer tubing and method for producing same | |
| ATE82012T1 (en) | SUPPORT ARTICLES MADE FROM GRAPHITE OCCUPATIONAL COMPOUNDS. | |
| GB1427070A (en) | Iron or steel powder containing phsophorus | |
| GB1034094A (en) | Self-lubricating article and means for its manufacture | |
| US2964476A (en) | Process for producing a metal-lubricant | |
| GB1309559A (en) | Bearing compositions | |
| US3630968A (en) | Oxide having the structural formula (la1-xcax)cro3 where x is between .01 and .15 and a method for producing the same | |
| CN102703161A (en) | Self-lubricating copper-Ti3SiC2-NbSe2 composite material and preparation method thereof | |
| GB1145387A (en) | Sintered silver-copper contact material | |
| US2379232A (en) | Metallic compositions containing bismuth | |
| GB561165A (en) | Improvements in or relating to bearings | |
| US3273977A (en) | Bearing of sintered metal containing interstitial solid lubricant | |
| GB892350A (en) | Plain bearings | |
| JPS5655439A (en) | Conductive resin composition | |
| GB1043918A (en) | Electrical contacts | |
| GB1151355A (en) | Improvements in and relating to Bearings for Rotatable Shafts and the like | |
| GB1279293A (en) | Improvements in or relating to powdered metal composites and method of making the same | |
| GB1137427A (en) | Improvements in or relating to superconducting alloys and their manufacture | |
| GB1186671A (en) | Lubricating Compositions | |
| Tang | The energy gap of the lower band of superconducting niobium at T= 0° K | |
| GB892846A (en) | Improvements in and relating to powdered metal moulding | |
| JPS54108150A (en) | Combination of slide parts material | |
| GB988184A (en) | Electric resistor film and its manufacturing process | |
| JPS5611951A (en) | Aromatic polyamide composition | |
| JPS53146903A (en) | Preparation of wear-resisting sintered alloy of iron base |