DE339950C - Process for the extraction of vanadium from iron ores or mixtures of such ores with other ores - Google Patents
Process for the extraction of vanadium from iron ores or mixtures of such ores with other oresInfo
- Publication number
- DE339950C DE339950C DE1919339950D DE339950DD DE339950C DE 339950 C DE339950 C DE 339950C DE 1919339950 D DE1919339950 D DE 1919339950D DE 339950D D DE339950D D DE 339950DD DE 339950 C DE339950 C DE 339950C
- Authority
- DE
- Germany
- Prior art keywords
- ores
- vanadium
- iron
- slag
- ore
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Description
Verfahren zur Gewinnung von Vanadin aus Eisenerzen oder Gennischen solcher Erze mit anderen Erzen. Gegenstand der Erfindung ist ein Verfahren zur Gewinnung von Vanaldin aus Eisenerzen, welches eine Kostenersparnis herbeiführt und die Ausbeute an Vanadin steigert. Durch die Erfindung wird die Verwendung von Vanadin bei der Stahlerzeugung und zu anderen Zwecken gefördert.Process for the extraction of vanadium from iron ores or genniches such ores with other ores. The invention relates to a method of extraction of vanaldine from iron ores, which brings about a cost saving and the yield increases in vanadium. The invention makes the use of vanadium in the Steelmaking and other purposes.
Die Erfindung besteht darin, daß durch Schmelzen vanadinhaltiger Eisenerze oder Gemische solcher Erze mit anderem Material mit Kohle older anderen Reduktionsmitteln unter Zusatz eines Flußmittels ein das Vanadin ider Erze- vollständig oder nahezu vollständig enthaltendes Roheisen erzeugt wird.The invention consists in that iron ores containing vanadium are melted or mixtures of such ores with other material with coal or other reducing agents with the addition of a flux, the vanadium ore is completely or almost completely completely containing pig iron is produced.
Die Erfirndung kann beispielsweise ein der Weise ausgeführt werden, @daß vanadinhaltige Eisenerze, z. B. titanhaltige Magneteisenerze, welche Vanadin oder Vanad-in und' Chrom enthalten, meinem elektrischen Ofen, einem Hochofen oder einem anderen geeigneten Ofen mit .Kohle in geeigneter Form oder einem anderen Reduktionsmittel und Kieselsäure in der Form von Sanidt oder Silikateisenerz geschmolzen werden, wobei das Vanadin vollständig oder zum weitaus größten Teile nicht in die beim Schmelzen gebildete Schlacke, sondern in das erzeugte Roheisen übergeht.The invention can for example be carried out in such a way @ that iron ores containing vanadium, e.g. B. titanium-containing magnetic iron ores, which vanadium or vanad-contained in and 'chrome, my electric furnace, or a blast furnace another suitable furnace with charcoal in a suitable form or another reducing agent and silica in the form of sanidt or silicate iron ore are melted, with the vanadium completely or by far the largest part not being incorporated into the melting process formed slag, but passes into the pig iron produced.
Das vanadi:nhaltige Roheisen wird !dann in einen anderen Ofen, beispielsweise :in einen Herdflammofen ad-,er elektrischen Ofen gebracht und dort entkohlt, wobei die gesamte oder nahezu gesamte Menge des Vanadins in die dabei entstehende Schlacke übergeführt wird.The pig iron containing vanadium is then placed in another furnace, for example : ad- in a hearth furnace, he placed an electric furnace and decarburized there, whereby all or almost all of the amount of vanadium in the resulting slag is convicted.
Die vanadinhaltige Schlacke wird dann mit frischem Erz gemischt zur Beschickung des zuerst benutzten Ofens verwendet. In diesem vereinigt sich das in -dem neu zugeführten Erz enthaltene Vanadin mit dem aus der zuerst verarbeiteten Erzmenge gewonnenen Vanadin, welches bei dem neuen Schmelzprozeß wieder frei wird und Idas gesamte Vanad:n geht in das bei dem zweiten Prozeß erzeugte Roheisen über.The vanadium-containing slag is then mixed with fresh ore to produce Load of the oven used first. In this the in -the newly supplied ore contained vanadium with that from the first processed Amount of ore recovered vanadium, which is released again in the new smelting process and Ida's entire vanad: n goes into the pig iron produced in the second process.
Wenn es notwendig ist, ,den Vanadi.ngehalt des Roheisens noch weiter zu steigern, so wird das in idem zweiten Schmelzprozeß gebildete Roheisen, wie vorstehend beschrieben, in einem Herdflammofen oder einem anderen Ofen entkohlt und die dabei gebildete Schlacke, welche entsprechend reicher an Vana-dmn ist, als die zuerst erzeugte, in der beschriebenen Weise mit frischem Erze zusammengebracht. Dieses Verfahren kann beliebig oft wiederholt werden, bis der gewünschte Vanadingehalt des Roheisens erreicht ist.If necessary, increase the vanadium content of the pig iron even further to increase, the pig iron formed in the second smelting process becomes as above described, decarburized in a hearth furnace or another furnace and the thereby formed slag, which is correspondingly richer in Vana-dmn than the first produced, brought together with fresh ore in the manner described. This The procedure can be repeated as often as required until the desired vanadium content is obtained of pig iron is reached.
Beim Schrnelze@ der Schlacke mit frischen Erzen kann auch chromhaltiges Erz und darauf eine entsprechende Menge des bei Bildung der Schlacke entstandenen kohlenstoffarni -,n Eisens oder anderen Eisens von gleicher Beschaffenheit zugesetzt werden.When the slag is shredded with fresh ores, chromium-containing Ore and then a corresponding amount of what was produced when the slag was formed carbonarni -, n iron or other iron of the same quality can be added.
Unterumständen ist es zweckmäßig, einen dritt.-n Ofen zu Hilfe zu nehmen, und in diesem die zunächst,-gebiläete vanadinhaltige Schlacke zusammen finit dem frischen Erz zu hehandeln, indem=" iiür' eine verhältnismäßig geringe Menge des letzteren zugesetzt wird.In some circumstances it is advisable to have a third oven to help take, and in this the initially, -gebiläete vanadium-containing slag together finite to deal with the fresh ore by = "for 'a comparatively small amount of the latter is added.
Um Stahl zu erzeugen, wird dem entkohlten Metall, welches in der beschriebenen Weise gewonnen wurde, von ,dem hoch vanadinhaltigen Roheisen so viel zugesetzt, daß der gewonnene Stahl den gewünschten Gehalt an Kohle, Vanadin und an 'deren Bestandteilen enthält. Falls einer oder mehrere der Bestandteile des Endproduktes in dem verwendeten Erz in zu geringer Menge -enthalten sind, wird bei -dem ersten Schmelzprozeß eine entsprechende lIen.ge -Erz mit dem fehlenden Bestandteil zugesetzt. Wenn z. B. -der Chromgehalt der Erze zu gering ist, so wird Chromeisenerz hinzugefügt, welches dem gebildeten Roheisen bzw. dem zur Stahlerzeugung benutzten kohlenstofireichen Material Aden gewünschten Chromgehalt gibt.To produce steel, the decarburized metal, which is described in the The way that so much was added to the pig iron, which has a high vanadium content, that the steel obtained has the desired content of coal, vanadium and their constituents contains. If one or more of the components of the final product are used in the Ore is contained in too small a quantity, becomes one in the first smelting process Corresponding lIen.ge ore with the missing component was added. If z. B. -der If the chromium content of the ores is too low, chromium iron ore is added to the pig iron formed or the carbon-rich material used for steel production Adenes the desired chromium content.
Bei den im vorstehenden beschriebenen Vorgängen verhalten sich leicht oxydierbdre Metalle, wie Mangan und Chrom, in @derselben Weise wie das Vanadin und werden in gleicherweise wie dieses gewonnen. Weniger leicht oxydierbare Metalle, wie Nickel und Kobalt bleiben bei der Entkohlung mit dem Eisen oder kohlenstoffarmen Stahl' vereinigt, und wenn sie nicht darin verbleiben sollen, so werden sie in diesem Stadium des Verfahrens ausgeschieden.The operations described above behave easily Oxidizable metals, such as manganese and chromium, in the same way as vanadium and are won in the same way as this. Less easily oxidizable metals, like nickel and cobalt in decarburization stay with the iron or low carbon Stahl 'united, and if they are not to remain in it, they become in this one Eliminated stage of the procedure.
Das beschriebene Verfahren zur Herstellung von Vanadinstahl kann in der Weise abgeändert werden, daß däs zuerst gewonnen.. vanadinhaltige Roheisen entweder für sich allein oder in Mischung mit einer entsprechenden Menge Eisen- oder Stahlschrott oder anderem in gewöh.nl,icher Weise gewonnenen Eisen 'oder Stahl entkohlt und in einem geeigneten Ofen, am besten in einem elektrischen Ofen zuerst oxydierend' und dann reduzierend gefrischt (refine) wird. Dabei gelangen Vanadin und andere Bestandteile, Welche zuerst oxydiert und von der Schlacke aufgenommen werden, während des Rediiktionsvorganges in :die Metallmasse.The process described for the manufacture of vanadium steel can be found in be modified in such a way that the first is extracted .. pig iron containing vanadium either on its own or mixed with a corresponding amount of iron or steel scrap or other iron or steel obtained in the usual way, decarburized and in a suitable furnace, preferably first oxidizing in an electric furnace 'and then it is refined in a reducing process. Vanadium and other components get there, Which are first oxidized and absorbed by the slag during the reduction process in: the metal mass.
Das zuletzt erwähnteVerfahren, metallische Bestandteile,von Stahl festzuhalten, ist bekannt und bildet keinen Teil der vorliegen-,den Erfindung. Diese besteht in der Hauptsache in der Gewinnung von Vanadin, welches sich in Eisenerzen findet, zusammen mit ,dem ihm in der Natur beigesellten Eisen in der Forin von vanadinbaltigem Roheisen als Zwischenprodukt oder Vanadinstahl als Endprodukt.The last mentioned process, metallic constituents, of steel Note is known and does not form part of the present invention. These consists mainly in the extraction of vanadium, which is found in iron ores finds, together with, the iron, which is naturally associated with it, in the form of vanadium Pig iron as an intermediate product or vanadium steel as an end product.
Claims (3)