DE2005231A1 - Process for vulcanizing large, flat rubber objects - Google Patents
Process for vulcanizing large, flat rubber objectsInfo
- Publication number
- DE2005231A1 DE2005231A1 DE19702005231 DE2005231A DE2005231A1 DE 2005231 A1 DE2005231 A1 DE 2005231A1 DE 19702005231 DE19702005231 DE 19702005231 DE 2005231 A DE2005231 A DE 2005231A DE 2005231 A1 DE2005231 A1 DE 2005231A1
- Authority
- DE
- Germany
- Prior art keywords
- mold release
- vulcanizing
- press
- release agent
- mold
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Description
Die Erfindung bezieht sich auf ein Verfahren zum Vulkanisieren von großflächigen Gummigegenständen, wie beispielsweise sogenannten Druckausgleichstüohern zur Verwendung in Etagenpressen, von Fördergurten und ähnlichen bandförmigen Gummigegenständen mit und/oder ohne Verstärkungseinlagen.The invention relates to a method for vulcanizing large-area rubber objects, such as so-called pressure compensation tubes for use in multi-stage presses, conveyor belts and similar band-shaped rubber objects with and / or without reinforcement inserts.
Die Vulkanisation derartiger Gummigegenstände wi#d entweder insbesondere bei größerer Längenausdehnung abschnittsweise vorgenommen oder der Gegenstand wird als solcher in einer seinen Abmessungen entsprechenden Form in einer Vulkanisierpresse vulkanisiert.The vulcanization of such rubber articles is either in particular in the case of a greater length expansion made in sections or the object is as such in a shape corresponding to its dimensions vulcanized in a vulcanizing press.
Bei diesem Vulkanisierverfahren treten in der Oberfläche des Gummigegenstandes nach der Vulkanisation oftmals Fehlstellen auf, die durch zwischen Formwand und Rohling eingeschlossene Luft verursacht werden und eine Nacharbeitung, sei es durch Abschleifen der Oberfläche, sei es durch Ausfüllung der Vertiefung mit Gummimasse,und Nachvulkanisation erforderlich machen.In this vulcanization process, defects often occur in the surface of the rubber article after vulcanization Trapped air in the mold wall and blank are caused and reworking, be it by grinding the surface, or by filling the recess with rubber compound, and post-vulcanization is required do.
Sie Lufteinschlüsse sind dadurch erklärbar, daß beim Schließen der Form bzw. Vulkanisierpresse an den Formwandungen bzw. Heizplatten stellenweise der Gummi sofort anhaftet und am Fließen gehindert wird. Biese Erscheinung tritt selbst bei sorgfältiger Anwendung von Formtrennmitteln der verschiedensten Art im Überschuß auf und ist in erster Linie dadurch erklärbar, daß sich kaum wahrnehmbare Verschmutzungen der Oberfläche auf die Benetzbarkeit mit den als Lösungen oder Dispersionen verwendeten Formtrennmitteln auswirken und an diesen Stellen beim Abtrocknen eine nicht auereichende Menge der Trennsubstanz verbleibt.The air inclusions can be explained by the fact that when the mold is closed or vulcanizing press on the mold walls or heating plates in places where the rubber immediately adheres and is prevented from flowing. This phenomenon occurs even with careful use of mold release agents of various kinds in excess and can primarily be explained by the fact that there is barely noticeable dirt on the surface affect the wettability with the mold release agents used as solutions or dispersions and at these points during drying Insufficient amount of the separating substance remains.
Durch die Oberflächenhaftung können in dem Gegenstand eingelagerte Gewebeeinlagen gegebenenfalls so stark verzogen werden, daß eine Falten-As a result of the surface adhesion, fabric inlays embedded in the object may be warped to such an extent that wrinkles
BAD - 2 - BATHROOM - 2 -
109834/0763109834/0763
bildung eintritt. DieserFaltenbildung konnte bisher erfolgreich nur dadurch begegenet werden, daß der gummierte Bandkern oder dgl. vor den Belegen in Hüll- bzw. Decksohichten vorvulkanieiert wird. Jeder zusätzliche Arbeitsschritt - sowohl eine nachträgliche Reparatur des Gumaigegenstandes wie auch das Vorvulkanieieren des Gewebekernes -aber kompliziert und verteuert den Produktionsgang des Artikels. Durch die Notwendigkeit einer Nachbehandlung der Formoberfläohe bzw. Halbplattenoberfläohen nach einen oder nur wenigen Vulkanisationzyklen mit Formtrennmittel wird insbesondere wegen der erforderlichen Trookenzeit auch die sogenannte Totzeit der Vorrichtungen vergrößert.education occurs. This wrinkling has only been successful so far be begegenet that the rubberized tape core or the like. Before the documents are pre-vulcanized in envelope or cover layers. Everyone additional work step - both a subsequent repair of the rubber article and the pre-vulcanization of the tissue core - but complicates and increases the cost of the production process of the article. Due to the need for post-treatment of the mold surface or half-plate surface after one or only a few vulcanization cycles with mold release agents, in particular because of the necessary Trooke time also increases the so-called dead time of the devices.
Die Erfindung hat sich die Aufgabe gestellt, die genannten Fehler-W quellen beim Vulkanisieren großflächiger Gummigegenstände, insbesondere von Druckausgleichstüchern, Förderbändern, Antriebsriemen und dgl. möglichst weitgehend auszuschalten und die Oberflächengüte dieser Artikel zu verbessern.The invention has the task of which mentioned error W swell during vulcanization of large rubber objects, especially of pressure equalization towels, etc.. As far as possible off conveyor belts, drive belts and and improve the surface quality of these products.
Die Aufgabe wird erfindungsgemäS durch die Verwendung von mikroporösen Trägerstoffen für die Formtrennmittel gelöst, die für die Dauer der Vulkanisation zwischen Gummi- und Formenoberfläche angeordnet werden.The object is achieved according to the invention through the use of microporous carrier materials for the mold release agents, which last for the duration the vulcanization between the rubber and mold surface.
Als Trägerstoffe für die Formtrennmittel können blatt- oder folienförmige Stoffe z. B. Papiere verschiedener Art verwendet werden, die sich durch eine besondere Mikroporosität auszeichnen. Als besonders geeignet hat sich mit Polysyloxanen imprägniertes Pergamentpapier erwiesen, da dieses selbst im oberen Bereich der bis zu etwa 160° C ansteigenden Vulkanisationstemperaturen auch unter dem gleichzeitigen Einfluß der in den Gummimischungen enthaltenen Chemikalien nicht nennenswert angegriffen wird und infolgedessen mehrmals verwendet werden kann. Aber auch auf Kunststoffbasis aufgebaute, mikroporöse Folien, die zu den verwendeten Formtrennmitteln eine ausreichende Affinität besitzen, können im erfindungsgemäßen Sinne verwendet werden.As a carrier for the mold release agent sheet or film-like substances such. B. papers of various types are used, the are characterized by a special microporosity. Parchment paper impregnated with polysyloxanes has proven to be particularly suitable proven, as this even in the upper range of up to about 160 ° C increasing vulcanization temperatures also under the simultaneous Influence of the chemicals contained in the rubber compounds is not noticeably attacked and is consequently used several times can be. But also based on plastic, microporous Films which have sufficient affinity for the mold release agents used can be used in the context of the invention.
BAD ORIGiNALORIGINAL BATHROOM
- 5 -.lQ9.flL3LA/076 3- 5 -.lQ9.flL3LA / 076 3
Neben den bereite genannten, als Formtrennmittel bevorzugt verwendeten Polysyloxanen, die gewöhnlich als Silikonöle bezeichnet werden, insbesondere den Methylpolysyloxanen, können auch andere an eich bekannte Formtrennmittel in Form von Lösungen oder Dispersionen für die Imprägnierung der Trägerstoffe verwendet werden. Als solche Formtrennmittel seien beispielsweise genannt Polyäthylenwachse, Poly glykole oder dgl.In addition to those already mentioned, they are preferably used as mold release agents Polysyloxanes, commonly referred to as silicone oils, in particular the methylpolysyloxanes, others known in the art can also be used Mold release agents in the form of solutions or dispersions for impregnation the carrier materials are used. Such mold release agents are, for example, polyethylene waxes, poly glycols or the like.
Sie Trägerfolie läßt sich durch Tränken, Tauchen oder dgl. wesentlich gleichmäßiger mit den Formtrennmitteln imprägnieren als dies bei der Beschichtung der in der Segel metallischen Formwände oder Pressenplatten möglich ist, so daß Unregelmäßigkeiten in der Beschichtung, die wohl für das Auftreten von Fehlstellen in der Oberfläche des Gegenstandes verantwortlich sind, vermieden werden. Sie Mikroporosität der Trägerfolie andererseits stellt eine ausreichende Abführung von in der Oberfläche des Rohlinge beim Schließen der Vorrichtung eingeschlossener Luft sicher. Gleichzeitig wird beim Auftreten von Dickentoleranzen im Rohling ein schubarmer Ausgleich erzielt, der eine Faltenbildung des Gewebekernes im Rohling vermeidet. Durch die vorteilhaften Wirkungen wird einerseits somit der Vulkanisationszyklus wesentlich verkürzt, da das Auftrocknen des Formtrennmittels an einen anderen Ort verlegt wird, andererseits aber wird auch das Auftreten von Fehlstellen infolge von Lufteinsiuüssen und eine Faltenbildung der im zu vulkanisierenden .Körper enthaltenen Verstärkungseinlagen vermieden.The carrier film can be impregnated with the mold release agents much more evenly by soaking, dipping or the like than is possible when coating the metal mold walls or press plates in the sail, so that irregularities in the coating, which are probably responsible for the occurrence of imperfections in the surface responsible for the item. The microporosity of the carrier film, on the other hand, ensures sufficient removal of air trapped in the surface of the blank when the device is closed. At the same time, when thickness tolerances occur in the blank, a low-thrust compensation is achieved, which prevents the tissue core from wrinkling in the blank. Due to the advantageous effects, the vulcanization cycle is on the one hand significantly shortened, since the drying of the mold release agent is relocated to another location, but on the other hand the occurrence of imperfections due to air infiltration and wrinkling of the reinforcement inserts contained in the body to be vulcanized is avoided.
Die Oberfläche der in erfindungsgemäßer Weise vulkanisierten Gummigegenstände erscheint infolge der auf ihr vom Trennmittelträger abgezeichneten Mikroporen mattglänzend bis matt. Die mit bloßem Auge kaum in Erscheinung tretende Rauheit der Oberfläche verringert den Schlupf auf Antriebselementen ohne andererseits zu verstärkten Verschmutzungen des Gegenstandes im Betrieb AnIaB zu geben.The surface of the rubber articles vulcanized in accordance with the invention appears matt-glossy to matt as a result of the micropores marked on it by the release agent carrier. Hardly with the naked eye The appearance of roughness on the surface reduces the slippage on drive elements without, on the other hand, increasing contamination to give the object in the company AnIaB.
Die zu vulkanisierenden Rohlinge können ohne Schwierigkeiten mit den Trägerstoffen für die Formtrennmittel umhüllt werden; so ist es beispielsweise möglich, die Trägerbahnen beim abschnittsweisen Vorschub von langgestreckten Gegenständen, wie Förderbändern und dgl. in der erforderlichen Breite von Rollen ablaufen zu lassen oder sie als endlose Bänder auszubilden. The blanks to be vulcanized can be used without difficulty with the Carriers for the mold release agents are coated; that's how it is, for example possible, the carrier webs in the sectional feed of elongated objects, such as conveyor belts and the like. In the to run the required width of rolls or to train them as endless belts.
109834/0763109834/0763
Sie Erfindung wird schematisch in der Zeiohnung in einer Einrichtung zum selbsttätigen Vulkanisieren von Fördergurten als Ausführungsbeispiel dargestellt.The invention is shown schematically in the drawing in a facility shown as an exemplary embodiment for the automatic vulcanization of conveyor belts.
Fig. 2 eine Einzelheit aus Fig. 1 in vergrößertem Maßstab im Schnitt.FIG. 2 shows a detail from FIG. 1 on an enlarged scale in section.
Sie dargestellte Einrichtung enthält als wesentlichen Bestandteil eine Vulkanisierpresse 1 mit zwei beheizten Druckplatten, der feststehenden Unterplatte 2 und der auf- und abbeweglichen Kante 3, zwischen denen der Gurtrohling unter Einwirkung von Druck und Wärme fertigvulkanisiert wird. Zur seitlichen Begrenzung des von den Druckplatten 2, 3 gebildeten Pressenraumes sind in üblicher Weise sogenannte Beilegestangen 6 (Fig. 2) vorgesehen. Die Beilegestangen sind in Pfeilrichtung auf der Unterplatte 2 gleitend beweglich und können durch nicht weiter dargestellte Arbeitszylinder oder anderen Kraftmittel an die Seitenkanten des Fördergurtes angedrückt werden.The device shown contains a vulcanizing press 1 with two heated pressure plates, the fixed lower plate 2 and the up and down edge 3, between which the belt blank is fully vulcanized under the action of pressure and heat. For the lateral delimitation of the press space formed by the printing plates 2, 3, so-called attachment rods 6 (FIG. 2) are provided in the usual way. The support rods are slidably movable in the direction of the arrow on the lower plate 2 and can be pressed against the side edges of the conveyor belt by working cylinders (not shown) or other power means.
Für die Zuführungsmöglichkeiten des in diesem Falle als Trennmittel verwendeten silikonisierten Papiers sind in Fig. 1 zwei Aueführungsformen schematisch dargestellt.Two embodiments are shown in FIG. 1 for the supply options for the siliconized paper used as a release agent in this case shown schematically.
Die Unterplatte 2 ist mit einer Bahn silikonisierten Papiers 8 belegt, das über eine Umlenkrolle 7 von einer Vorratsrolle 11 abgezogen wird und nach Verlassen der Presse über eine Umlenkrolle 9 auf einer Aufwickelrolle 12 wieder aufgewickelt wird.The lower plate 2 is covered with a sheet of siliconized paper 8, which is drawn off from a supply roll 11 via a deflection roller 7 and, after leaving the press, is wound up again on a winding roller 12 via a deflection roller 9.
An der beweglich angeordneten Pressenoberplatte 3 ist ein endloses Band silikonisierten Papiers 4 über Umlenkrollen 7a, 9a, 10 und 10a geführt.On the movably arranged press top plate 3 is an endless Tape of siliconized paper 4 guided over pulleys 7a, 9a, 10 and 10a.
Im geschlossenen Zustand der Presse tritt unter vorgegebenem Preßdruck bei der eingestellten Temperatur die Vulkanisation des gegebenenfalls Verstärkungseinlagen 5a enthaltenden Gurtrohlings 5 ein. Hierbei dringtIn the closed state of the press occurs under a predetermined pressure at the set temperature the vulcanization of the possibly Reinforcing inserts 5a containing belt blank 5 a. Here penetrates
109834/0763 - 5 -109834/0763 - 5 -
-l·-l ·
in geringem Umfange die zu vulkanisierende Gummimischung in die Mikroporen des Trennmittelträgers ein, während gleichzeitig etwa eingeschlossene Luft durch sie hindurchgedrückt wird und zwischen Pressenplatten und Oberfläche und der Unterseite des Trennmittelträgerβ abgeführt wird. Wird die Presse nach dem Vulkanisieren geöffnet und der Rohling um einen bestimmten Längenbetrag vorwärtsbewegt, so nimmt dieser in gleichem Maße den Formtrennmittelträger bei seiner Vorwärtsbewegung mit, so daß die neu in den Pressenzwischenraum eingeführte Oberfläche des Gurtrohlings 5 gleichzeitig von der ebenfalls mitgeführten Trennmittelfolie abgedeckt wird. Bei Verwendung von endlosen Bändern, wie an der Pressenplatte 3 dargestellt, tritt ein inzwischen abgekühltes Folienstück mit der Oberfläche in Kontakt, während bei der Anordnung, wie sie im Zusammenhang mit der Unterplatte 2 dargestellt ist, ein frisches Stück von der Vorratsrolle abgezogen und in die Presse eingeführt wird.to a small extent the rubber compound to be vulcanized into the micropores of the release agent carrier, while at the same time approximately trapped Air is forced through it and discharged between the press plates and the surface and the underside of the release agent carrierβ will. If the press is opened after vulcanization and the blank is moved forward by a certain amount of length, then this takes place to the same extent the mold release agent carrier as it moves forward with, so that the newly introduced surface of the belt blank 5 in the press space at the same time of the also carried along Release film is covered. When using endless belts, as shown on the press platen 3, occurs that has meanwhile cooled down Foil piece in contact with the surface, while in the arrangement as shown in connection with the lower plate 2, a fresh piece is withdrawn from the supply roll and inserted into the press.
Die gute Biegsamkeit des gemäß der Erfindung bevorzugt verwendeten Pergamentpapiers als Folienträger ermöglicht es auch, wie im Schema der Fig. 2 dargestellt ist, die untere Trägerbahn 8 mit Hilfe der Beilegestangen 6 an die Seitenkanten des Gurtes 5 anzudrücken, so daß sich im Verein mit der ebenfalls breiteren oberen Bahn 8 eine allseitige Umhüllung des Rohlings ergibt.The good flexibility of the one preferably used according to the invention Parchment paper as a film carrier also allows, as shown in the diagram of FIG. 2, the lower carrier web 8 with the help of Attachment rods 6 to press against the side edges of the belt 5, so that in association with the also wider upper web 8 a encasing the blank on all sides results.
Es ist auch möglich und liegt im Rahmen der Erfindung, durch geeignete Antriebselemente die Aufwickelrolle 12 bzw. eine oder mehrere der Umlenkrollen 9a» 10 nach dem Öffnen der Presse zum Zwecke des Vorechubs des Trennmittelträgers anzutreiben und auf diese Weise die Zuführung von abgekühlten bzw. frischen Trennmittelfolien sicherzustellen. It is also possible and lies within the scope of the invention by suitable means Drive elements the winding roller 12 or one or more of the deflection rollers 9a »10 after opening the press for the purpose of To drive the advance of the release agent carrier and in this way ensure the supply of cooled or fresh release agent foils.
109834/0763109834/0763
Claims (3)