DE19719442A1

DE19719442A1 - Glued wood plate

Info

Publication number: DE19719442A1
Application number: DE1997119442
Authority: DE
Inventors: Michael Haug
Original assignee: SCHMUCK SUSANNE
Current assignee: SCHMUCK SUSANNE
Priority date: 1997-05-07
Filing date: 1997-05-07
Publication date: 1998-11-12
Anticipated expiration: 2017-05-08
Also published as: DE19719442C2

Abstract

A multi-layered plate consists of two or more glued wooden plates located alternatingly crossways over one another and turned through 90 degrees. With this type of plate also an additional cover veneer is applied to the lower and/or upper side of the plate. To produce the plate, the small bars and/or strips are provided with glue on one side and by means of a frame press via a negative form and through a positive form are pressed together in wave-formation. The pressed material is held under tension until the glue hardens. After hardening, the predetermined wave shape no longer warps due to the inherent tension of the pressed-together small bars and strips.

Description

Diese Erfindung bezieht sich auf die Bereitstellung einer neuen verwindungssteifen Leimholzplatte, die als Tischlerplatte, Stab-, Stäbchen- oder Mehrschichtplatte und sonstigen Konstruktionsleimhölzern eine vielseitige Verwendung finden kann.This invention relates to the provision of a new torsionally rigid Glued wood board, which is used as a block board, rod, stick or multi-layer board and others Construction glue can find a versatile use.

Herkömmliche Leimholzplatten aus Holz werden nach dem Stand der Technik dadurch bereitgestellt, daß der Fachmann Holzplatten aus geraden Stäben bzw. geraden Leisten durch eine sogenannte "gerade Verleimung" der einzelnen Schichten herstellt.Conventional glued wood panels made of wood are thereby according to the state of the art provided that the expert through wooden panels from straight bars or straight strips produces a so-called "straight gluing" of the individual layers.

Diese Leimholzplatten haben jedoch im allgemeinen den Nachteil, daß ihre Verwindungssteifigkeit und Durchbiegestabilität gering ist. Nach dem Stand der Technik hat man bislang versucht, diesen Nachteil dadurch zu verbessern, indem man an der Unter- und Oberseite der Leimholzplatte diese mit einer zusätzlichen Sperrschicht versah. Jedoch hat auch dieses Herstellungsverfahren den Nachteil, daß die so verleimte und verstärkte Platte sich dennoch mit der Zeit verziehen kann. Aus diesem Grunde müssen derartige Leimholzplatten gerade stehend oder liegend gelagert werden, damit sich das Material nicht bereits bei der Lagerung verzieht.However, these glued wood boards generally have the disadvantage that their Torsional rigidity and deflection stability is low. According to the state of the art So far, attempts have been made to improve this disadvantage by working on the lower and The top of the glued wood panel provided an additional barrier layer. However, too this manufacturing process has the disadvantage that the so glued and reinforced plate can still warp over time. For this reason, such glued wood panels stored upright or lying down, so that the material is not already in the Storage warps.

Der Erfindung liegt somit die Aufgabe zugrunde, eine Leimholzplatte zur Verfügung zu stellen, die eine bessere Materialstabilität, höhere Materialsteifigkeit in allen Richtungen und extrem geringen Verzug der Platte bereitstellt. Ferner stellt die Erfindung eine wirtschaftlich kostengünstigere Alternative für beispielsweise den Einsatz von hochwertigen Multiplexplatten bereit.The invention is therefore based on the object of providing a glued wood panel, which have better material stability, higher material rigidity in all directions and extreme provides slight warpage of the plate. Furthermore, the invention provides an economical cheaper alternative for example for the use of high quality multiplex panels ready.

Die in Anlage beigefügten Zeichnungen verdeutlichen beispielhaft den Gegenstand der Erfindung, wobei The attached drawings illustrate the subject of the example Invention, being

Fig. 1 eine Leimholzplatte mit wellenförmig verleimten Stäben darstellt,Is Fig. 1 is a glued laminated timber with wavy glued rods,

Fig. 2 eine Leimholzplatte gemäß Fig. 1 ist, jedoch mit zusätzlich versehenem Deckfurnier auf der Unter- und Oberseite der Platte, FIG. 2 is a glued wood panel according to FIG. 1, but with an additional top veneer on the top and bottom of the panel,

Fig. 3 eine Leimholzplatte mit jeweils quer übereinandergelegten, wellenförmigen, verleimten Stäbchenfurnieren bzw. Stäben zeigt, Fig. 3 shows a glued laminated timber, each transverse superimposed wave-shaped, laminated veneer strips or rods,

Fig. 4 Stäbchen bzw. Leisten als Ausgangsmaterial vor der Pressung darstellt und Fig. 4 represents rods or strips as the starting material before pressing and

Fig. 5 die für die Verwendung beispielhaft gewellten Stäbchen bzw. Leisten während des Preßvorgangs zeigt. Fig. 5 shows the example of corrugated rods or strips during the pressing process.

Fig. 6 eine Leimholzplatte gem. Fig. 3 zeigt, jedoch zusätzlich mit Sperrfurnier. Fig. 6 is a glued wood panel. Fig. 3 shows, but additionally with a veneer.

Im allgemeinen werden die erfindungsgemäß beanspruchten Platten wie folgt hergestellt:In general, the plates claimed according to the invention are produced as follows:

Je nach gewünschter Materialstärke und Biegung der zu erzielenden Welle werden die in Fig. 4 gezeigten Stäbchen bzw. Leisten in der jeweils erforderlichen Stärke und Länge verwendet. Diese Stäbchen bzw. Leisten werden einseitig mit entsprechendem Leim versehen, und mittels einer dem Fachmann bekannten Rahmenpresse über eine Negativform durch eine Positivform, wie in Fig. 5 gezeigt, zusammengepreßt. Das dabei gepreßte Material wird so lange unter Spannung gehalten, bis der Leim vollständig ausgebärtet ist. Nach Aushärtung bzw. Trocknung des Leims steht die Platte in Folge der Leimfixierung unter Eigenspannung und kann sich in Folge der Eigenspannung und der ihr vorgegebenen Wellenform nicht mehr verziehen, da diese Kräfte zur Kompensation gelangen.Depending on the desired material thickness and curvature of the shaft to be achieved, the rods or strips shown in FIG. 4 are used in the thickness and length required in each case. These rods or strips are provided with appropriate glue on one side and pressed together by means of a frame press known to the person skilled in the art via a negative mold by a positive mold, as shown in FIG. 5. The pressed material is kept under tension until the glue has completely hardened. After the glue has hardened or dried, the plate is under internal stress as a result of the glue fixation and can no longer warp as a result of the internal stress and the predetermined waveform, since these forces are compensated.

Erfindungsgemäß wird der Fachmann hierbei beachten, daß man bei der Herstellung je nach Größe der Leimholzplatten die Starke der Stäbe bzw. Stäbchen bzw. Furniere, die Wellenhöhe und Wellenlänge anzupassen hat. Dementsprechend wurde aufgefunden, daß je kleiner die herzustellenden Leimholzplatten sind, desto kleiner sollte die Wellenhöhe und Wellenlänge sein bzw. desto dünner müssen die verwendeten Stäbe bzw. Stäbchen oder Furniere sein. According to the invention, the person skilled in the art will note that depending on the manufacture Size of the glued wood panels, the thickness of the rods or chopsticks or veneers, the wave height and adjust wavelength. Accordingly, it has been found that the smaller the to be produced, the smaller the wave height and wavelength should be or the thinner the rods or chopsticks or veneers used.

Das hier beschriebene Herstellungsverfahren ist dazu geeignet, Platten einzeln oder endlos herzustellen. Ferner kann je nach der gewünschten Materialstärke und der Biegung die entsprechende Wellenform bzw. Stäbchenform ausgewählt werden. Die fertige Platte kann nach Austrocknung des Leims bzw. seiner Aushärtung kalibriert werden, so daß die Oberfläche glatt ist.The manufacturing process described here is suitable for making plates individually or endlessly to manufacture. Furthermore, depending on the desired material thickness and the bend appropriate waveform or rod shape can be selected. The finished plate can calibrated after the glue has dried or hardened, so that the surface is smooth.

Als besondere Ausführungsform kann erfindungsgemäß die so hergestellte Platte je nach Bedarf und Anwendungszweck, wie beispielhaft in Fig. 3 gezeigt, nun um vorzugsweise 90° gedreht werden und dann mit einer oder mehreren Platten zu 2- oder Mehrschichtplatten, die jeweils quer übereinandergelegt und verleimt werden, versehen werden.As a special embodiment, according to the invention, the panel produced in this way can, depending on need and application, as shown by way of example in FIG. 3, now preferably be rotated by 90 ° and then with one or more panels to form 2 or multi-layer panels, which are in each case placed across one another and glued , are provided.

Ferner kann man aus dem so hergestellten Rohmaterial einzelne Furnierschichten schälen oder schneiden und wie oben beschrieben quer in 2- oder Mehrschichten zu Furnierplatten weiter verarbeiten.Furthermore, individual veneer layers can be peeled or made from the raw material thus produced cut and crosswise in 2 or more layers to veneer panels as described above to process.

Dieses Herstellungsverfahren ist äußerst flexibel, da die Wellenfrequenz und Amplitude der wellenförmig quer übereinandergelegten Schichten (vgl. Fig. 3) variabel ist. Wellenfrequenz und Amplitude richten sich vielmehr nach der jeweils erforderlichen Elastizität des Materials, der Stärke der Leisten und der Größe der zu verwendenden Werkstoffe.This manufacturing process is extremely flexible, since the wave frequency and amplitude of the wave-like layers (see FIG. 3) superimposed on one another are variable. Rather, the wave frequency and amplitude depend on the required elasticity of the material, the thickness of the strips and the size of the materials to be used.

Der Fachmann wird in Kenntnis dieser Erfindung sich auch anderer Werkstoffe als Ausgangsmaterial bedienen, die in Folge ihrer Eigenspannung für den erfindungsgemäßen Zweck geeignet sind.In the knowledge of this invention, the person skilled in the art will also consider materials other than Serve starting material, which is due to their inherent tension for the invention Purpose.

Die in Fig. 2 gezeigte Leimholzplatte ist im besonderen Maße geeignet, nicht anfällig gegen Verwindungssteifigkeit zu sein bzw. eine extrem hohe Durchbiegestabilität zu haben. Bei entsprechendem Bedarf wird der Fachmann nach Durchführung des allgemeinen Herstellungsverfahrens an der oberen und unteren Seite der Platte ein zusätzliches Deckfurnier auf die Platte auflegen.The glued wood panel shown in Fig. 2 is particularly suitable not to be susceptible to torsional rigidity or to have an extremely high deflection stability. If necessary, the person skilled in the art will place an additional cover veneer on the top and bottom of the board after carrying out the general manufacturing process.

Claims

1. glued wood panel comprising wavy glued rods or strips.

2. glued wood panel according to claim 1, with an additionally provided cover veneer on the Bottom and / or top of the glued wood panel is applied.

3. Multi-layer glued wood board with at least 2 or more glued wood boards according to claim 1, the individual glued wood panels alternately lying one above the other by 90 degrees applied rotated.

4. multilayer glued wood panel according to claim 3, with an additional provided Cover veneer on the bottom and / or top of the multilayer glued wood panel is applied.

5. A method for producing a glued wood panel according to claim 1, wherein the rods and / or strips are provided on one side with appropriate glue, by means of a Frame press over a negative shape by a positive shape wavy are pressed together, then the pressed material is kept under tension until the glue has hardened, whereby the predetermined waveform after hardening no longer in the form of the internal stress of the compressed rods or strips warps.