DE19649306C2 - Keramische Einbettmasse zum Herstellen von Gußformen - Google Patents
Keramische Einbettmasse zum Herstellen von GußformenInfo
- Publication number
- DE19649306C2 DE19649306C2 DE1996149306 DE19649306A DE19649306C2 DE 19649306 C2 DE19649306 C2 DE 19649306C2 DE 1996149306 DE1996149306 DE 1996149306 DE 19649306 A DE19649306 A DE 19649306A DE 19649306 C2 DE19649306 C2 DE 19649306C2
- Authority
- DE
- Germany
- Prior art keywords
- investment
- weight
- material according
- ceramic
- investment material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
Die vorliegende Erfindung betrifft eine keramische Einbettmasse auf Basis von Calciumoxid
zum Herstellen von Feingußformen für Titan, Zirkonium und andere Metalle und deren
Legierungen, die im flüssigen Zustand hoch aggressive Schmelzen bilden.
In der Medizintechnik und dabei insbesondere in der Dentaltechnik haben sich Titan und
seine Legierungen als Implantat- und Prothetikwerkstoff erfolgreich durchgesetzt. Es ist
auch aufgrund seiner Biokompatibilität, Korrosionsbeständigkeit und guten mechanischen
Eigenschaften ein nahezu idealer Werkstoff für den dentalen Zahnersatz. Diesen Vorteilen
steht in der Gußtechnik jedoch die hohe Reaktivität der Titanschmelze entgegen, die ein
Hindernis für weitere Verbreitung der Technologie ist.
Die üblichen Einbettmassen für die Herstellung der Gußformen sind für den Titanguß
ausnahmslos ungeeignet, weil sie wenig widerstandsfähige Materialien wie Quarz bzw.
Silikate, Phosphate usw. enthalten. Nach dem Eingießen des Titans in eine solche Form
kommt es zur starken Reaktion der Metallschmelze mit der keramischen Formmasse und
zusätzlich zur Aufhärtung und Versprödung der Titangußoberfläche durch die
Sauerstoffaufnahme. Diese sog. alpha-case wird bis zu 0,5 mm dick und muß nachher
entfernt werden. Damit wird die Geometrie des Gußstückes geändert bzw., bei dünnen
Wandstärken, das Gußstück unbrauchbar gemacht.
Eine Einbettmasse für diese Anwendung wird in der EP 0 503 626 A1 vorgestellt. Sie enthält
40-60% Zirkonoxid, eventuell auch Aluminiumoxid oder Magnesiumoxid. Die hiermit erzielte
Verbesserung ist aber nur gering, weil weiterhin mindestens 40% der Einbettmasse aus
Phosphat-Binder und Quarz bestehen, die mit der Titanschmelze heftig reagieren. Ähnliche
Einbettmassen mit einem Phosphat-Binder werden auch in EP 0 433 546 A1, DE 40 19 818
A1, oder DE 35 42 921 A1 beschrieben. Den Anforderungen der dentalen Titanguß
technologie entsprechen besser keramische Einbettmassen, die auf Quarz, Silikate bzw.
Phosphate großenteils verzichten, zugunsten thermodynamisch stabileren Rohstoffe. Eine
solche Einbettmasse ist aus DE 38 25 250 C2 bekannt. Sie basiert auf Aluminiumoxid und
Magnesiumoxid, mit Magnesiumacetat als Binder, alternativ mit kolloidalem SiO2 bzw.
Ethylsilikat. Diese und der hohe Anteil an feinerem Aluminiumoxid (20 bis über 40%), das
nicht ausreichend widerstandsfähig ist, führen jedoch auch hier zur schwachen Reaktion mit
der Titanschmelze. Letztlich wird in EP 0 733 419 A1 eine andere Einbettmasse auf Basis
von Zirkoniumoxid (bzw. Calciumzirkonat) und Magnesiumoxid mit einem Zirkonatbinder
vorgeschlagen. Der Nachteil ist das hohe Gewicht und der Rohstoffpreis der ZrO2-haltigen
Einbettmassen. Die Gußform aus einer solchen Einbettmasse muß vor dem Guß auf unter
500°C abgekühlt werden, weil bekanntlich das Zirkonoxid nur unter 500°C der Titan
schmelze widersteht. Zusätzlich dazu kommt es in Gußformen nach den beiden letztlich
genannten Schriften auch bei niedriger Gußtemperatur zur nachteiligen Aufnahme der Zr-
bzw. Al-Ionen in die Gußoberfläche (Lenz, Dietz: Quintessenz Zahntech 21(1995) 633-645).
Dies ist bei Magnesiumoxid oder Calciumoxid nicht der Fall.
Dem Einsatz von Calciumoxid, einem der thermodynamisch stabilsten oxidischen Rohstoffe
für diese Anwendung, steht jedoch seine heftige Reaktion mit Wasser gegenüber (Löschen
von Kalk) die sehr gefährlich ist (Augen, Haut). Zudem ist es hoch feuchtigkeitsempfindlich.
Das macht die Anwendung in wasserhaltigen Einbettmassen praktisch unmöglich (DE 40 19 818 A1).
Aus diesem Grund wird das Calciumoxid nur in nichthärtenden Schlickergemischen des
Typs CaO-Öl/Kerosin verarbeitet (EP 0 233 478).
Die technische Lösung der geschilderten Probleme ist nicht nur für die dentale
Titangußtechnik interessant, sondern auch für die Herstellung von Schmuck, Uhrenteilen und
allgemeine in der industriellen Titanfeingußfertigung.
Der vorliegenden Erfindung liegt die Aufgabe zugrunde, eine keramische Einbettmasse zu
entwickeln, welche die vorstehend genannten Mängel nicht aufweist. Die aus einer solchen
Einbettmasse hergestellte Gußform soll der aggressiven Metallschmelze auch bei höheren
Temperaturen weitgehend widerstehen, so daß die Reaktion mit der Schmelze völlig
unterbunden wird und die Aufhärtung und Aufnahme der Zr- bzw. Al-Ionen in die Oberfläche
auf ein mögliches Minimum reduziert wird.
Diese Aufgabe wird erfindungsgemäß mit einer keramischen Einbettmasse gelöst, die als
Hauptbestandteil 30-40% Calciumoxid in einer deaktivierten Form enthält
(Elektroschmelzprodukt, bzw. totgebrannt), oder 30-65% eines Gemisches aus demselben
Calciumoxid und Calciumzirkonat, mit höchstens 40% Calciumoxid. Als Bindemittel wird
0,1-4% wasserlösliches Calciumsalz einer organischer Säure zugegeben. Weiterhin enthält
die Einbettmasse 15-20% Aluminiumoxid, zusammen mit 0,001-0,1% Aluminiumpulver als
Härtemittel und 10-15% Magnesiumoxid für die nötige thermische Expansion. Als
Anmischflüssigkeit wird Wasser, oder eine wässrige Lösung benutzt. Nach dem Anmischen
entsteht eine knetbare fließfähige Masse, die selbständig zum niedrigporösen, festen
keramischen Körper abbindet.
Dieser Problemlösung liegt die Erkenntnis zugrunde, daß sich das Calciumoxid durch
spezielle Behandlung deaktivieren läßt. Zu dieser weniger üblichen Form des Calciumoxids
gehören sog. Elektroschmelzprodukte, oder durch thermische Behandlung entstandenes
"totgebranntes" Calciumoxid. Diese Produkte besitzen nicht die bekannte Aggressivität des
gebrannten Kalkes, sind nicht hydroskopisch und lassen sich problemlos mit Wasser
anmischen.
In einer derart hergestellten Einbettmasse lassen sich einwandfreie Feingußteile aus Titan
und anderen reaktiven Metallen und dessen Legierungen je nach Bedarf bei
unterschiedlichen Temperaturen schaffen. Die Gußstücke haften nicht an der keramischen
Gußform und können leicht entfernt werden. Die so freigelegte Metallgußoberfläche hat
einen sauberen metallischen Glanz ohne, bzw. mit nur einem Bruchteil der sonst üblichen
alpha-case, so daß sie nicht nachgearbeitet werden muß. Mit der erfindungsgemäßen
Einbettmasse ist auch die Aufnahme der Fremdionen in die Oberfläche des Gußstückes
weitgehend unterbunden, weil die Einbettmasse zu hohem Teil aus Calciumoxid und
Magnesiumoxid besteht.
Calciumoxid wird vorzugsweise als Elektroschmelzprodukt gewählt, oder in einer anderen
deaktivierten Form (sog. totgebrannt), als grobes Pulver oder Sand in einer Korngröße
bis höchstens 250 µm. Die optimale Menge liegt bei 30-40%. (Unter % werden
ausschließlich Gewichtsprozente verstanden.) Geringere Mengen führen zu nachteilig
schlechteren Gußergebnissen, größere Mengen dagegen zum nicht optimalen Verhalten
der Einbettmasse. Es ist ebenfalls möglich, zusätzlich zum Calciumoxid das Calciumzirkonat
anzuwenden. Die optimale Menge liegt dann bei 30-65% (mit höchstens 40% CaO).
Als Bindemittel wird ein wasserlösliches Calciumsalz einer organischer Säure in einer Menge
von 0,1-4% verwendet, wie z. B. Calcium-Ligninsulfonat oder Calcium-Formiat. Bei hohen
Temperaturen verbrennen sie zu CaO. Es ist auch möglich, zusätzlich ein oder mehrere
andere verbrennbare Binder einzusetzen, wie z. B. Cellulosederivate, Polysaccharide, oder
Polyvinylalkohol.
Zum Aushärten wird vorzugsweise 15-20% hochreaktives Aluminiumoxid in einer Korngröße
bis 20 µm benutzt, in Kombination mit metallischem Aluminiumpulver (0,001-0,1%). Feines
metallisches Aluminium besitzt die Eigenschaft, schon bei Raumtemperatur mit Wasser zu
reagieren nach
2Al + 3H2O → Al2O3 + 3H2
In leicht alkalischem Medium, wie dies in dem beschriebenen Einbettmassenschlicker der
Fall ist, beginnt die Reaktion und damit die Festigung erst nach einigen Minuten, so daß
genug Zeit für die plastische Verarbeitung des Schlickers bleibt. Die restliche Wassermenge
wird vom reaktiven Aluminiumoxid aufgenommen. Damit läßt sich innerhalb einer bis weniger
Stunden die Gußform ausreichend aushärten. Eine geringere Menge von Al und Al2O3 als
vorzugsweise genannt führt nachteilig zu längeren Aushärtezeiten, größere Menge dagegen
zur schlechteren Verarbeitung und Fließfähigkeit des Schlickers.
Die Kontraktion der Metallschmelze beim Erstarren in der Gußform wird üblicherweise beim
dentalen Metallguß mit einer entsprechenden vorherigen Volumenexpansion der Gußform
ausgeglichen. Zu diesem Zweck enthält die beschriebene Einbettmasse vorzugsweise
10-15% eines feinen (1-40 µm) Magnesiumoxides. Dieser Zusatz führt beim Brand bei
Temperaturen über 900°C zur Bildung von MgAl2O4 und zu einer Volumenzunahme. Eine
andere Menge an reaktivem MgO außerhalb der erwähnten Grenzen führt zu nicht
optimalen Expansionswerten.
Zusätzlich zu den genannten Bestandteilen kann die Einbettmasse bis zu 25% einer groben
Fraktion (Korngröße 150-600 µm) eines vorher genannten keramischen Rohstoffes
enthalten. Gröbere Sande in dieser Korngröße sind reaktionsträge, nicht plastisch
anmischbar, mit der Tendenz zum Entmischen und können deshalb nicht die Funktionen
der vorher beschriebenen feineren Pulver ersetzen. Sie sind lediglich als Füllstoffe
zuzumischen, um die Gasdurchlässigkeit der gebrannten keramischen Gußform dem
Gasdruck der benutzten Gußanlage anzupassen.
In einer Menge bis zu 6% können dem Pulver oder der Anmischflüssigkeit ebenfalls
Zusätze zugemischt werden, die die Fließfähigkeit, Plastizität, oder andere Eigenschaften
der Einbettmasse verbessern.
Nachfolgend soll erläutert werden, wie die praktische Herstellung der Gußform bei
Verwendung der beschriebenen Einbettmasse für den Titanguß realisiert wird.
Die Einbettmasse besteht aus Pulver und wasserhaltiger Anmischflüssigkeit. Beide
Komponenten werden zuerst im Verhältnis 100 g Pulver mit 12-14 ml Anmischflüssigkeit zur
knetbaren Masse angerührt und schließlich im Vakuummischer zum homogenen plastischen
Schlicker 30 Sec. lang angemischt. Danach wird das fertige Wachsmodell eingebettet. Die
Verarbeitungszeit beträgt ca. 5 Min., später beginnt eine langsame Versteifung des
Schlickers, bis in etwa 2 Stunden die Gußform eine ausreichende Härte erreicht. Dann wird
sie in einen kalten, oder bereits auf bis zu 300°C vorgeheizten Brennofen eingebracht. Mit
einer Geschwindigkeit bis zu 10°C/Min. wird die Endtemperatur von etwa 1000°C (±40°C)
erreicht. Bei der Temperatur wird die Gußform 1 Stunde an Luft gebrannt. Danach wird der
Brennofen auf die gewünschte Gußtemperatur abgekühlt. Diese sollte mindestens 20 Min.
gehalten werden, um eine gleichmäßige Temperaturverteilung in der Gußform zu erreichen.
Schließlich wird die Gußform aus dem Brennofen entnommen und in der Gußanlage mit
Titan gegossen.
Claims (6)
1. Keramische Einbettmasse zur Herstellung von Gußformen für Gußteile aus Titan,
Zirkonium und anderen Metallen und deren Legierungen, die im flüssigen Zustand
aggressive Schmelzen bilden, welche hauptsächlich aus einem keramischen,
thermodynamisch stabilen Hauptbestandteil und einem Bindemittel besteht, dadurch
gekennzeichnet, daß sie als keramischen, thermodynamisch stabilen Hauptbestandteil
30-40 Gew.-% deaktiviertes Calciumoxid (Elektroschmelzprodukt, totgebranntes
Calciumoxid), oder 30-65 Gew.-% eines Gemisches aus Calciumoxid und
Calciumzirkonat (CaZrO3) mit höchstens 40 Gew.-% Calciumoxid enthält und als
Bindemittel 0,1-4 Gew.-% eines wasserlöslichen Calciumsalzes einer organischer Säure
vorgesehen ist.
2. Einbettmasse nach Anspruch 1 dadurch gekennzeichnet, daß sie zusätzlich 15-20
Gew.-% Aluminiumoxid (Al2O3) und 0,001-0,1 Gew.-% metallisches Aluminiumpulver
(Al) enthält.
3. Einbettmasse nach Ansprüchen 1 bis 2 dadurch gekennzeichnet, daß sie zusätzlich
10-15 Gew.-% Magnesiumoxid (MgO) enthält.
4. Einbettmasse nach Ansprüchen 1 bis 3 dadurch gekennzeichnet, daß sie zusätzlich bis
zu 25 Gew.-% einer Fraktion der Korngröße von 150 µm bis 600 µm eines in
Ansprüchen 1 bis 3 genannten keramischen Rohstoffes enthalten kann.
5. Einbettmasse nach Ansprüchen 1 bis 4 dadurch gekennzeichnet, daß sie zusätzlich bis
zu 6 Gew.-% verbrennbare, oder thermodynamisch stabile Zusätze enthalten kann, die
die Verarbeitungseigenschaften der Einbettmasse verbessern.
6. Einbettmasse nach Ansprüchen 1 bis 5 dadurch gekennzeichnet, daß sie zusätzlich ein
oder mehrere wasserlösliche verbrennbare Bindemittel, insbesondere Cellulosederivate,
Polysaccharide, oder Polyvinylalkohol enthalten kann.