DE1267161B - Feuerfeste Massen - Google Patents

Feuerfeste Massen

Info

Publication number
DE1267161B
DE1267161B DEF44648A DEF0044648A DE1267161B DE 1267161 B DE1267161 B DE 1267161B DE F44648 A DEF44648 A DE F44648A DE F0044648 A DEF0044648 A DE F0044648A DE 1267161 B DE1267161 B DE 1267161B
Authority
DE
Germany
Prior art keywords
polyphosphoric acid
masses
percent
refractory masses
binder
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
DEF44648A
Other languages
English (en)
Inventor
Dr Albert Hloch
Dr Rudolf Kohlhaas
Dipl-Ing Nikolay Medie
Dr Helmut Neises
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Hoechst AG
Original Assignee
Hoechst AG
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Hoechst AG filed Critical Hoechst AG
Priority to DEF44648A priority Critical patent/DE1267161B/de
Priority to LU49837D priority patent/LU49837A1/xx
Priority to US508101A priority patent/US3345192A/en
Priority to NL656515761A priority patent/NL150090B/xx
Priority to FR41397A priority patent/FR1459532A/fr
Priority to BE673497D priority patent/BE673497A/xx
Publication of DE1267161B publication Critical patent/DE1267161B/de
Withdrawn legal-status Critical Current

Description

  • Feuerfeste Massen Gegenstand der Erfindung sind feuerfeste Massen mit erhöhter Grünfestigkeit und verkürzter Abbindezeit.
  • Als Kitte, Mörtel und Stampfmassen für feuerfeste Auskleidungen und Ausmauerungen werden zunehmend Massen verwendet, die aus einem hochschmelzenden Füllstoff, beispielsweise Schamotte, einer reaktionsfähigen Aluminiumverbindung, beispielsweise Mullit, Korund, Bauxit, Hydrargillit, Kaolin, und einer Lösung eines sauren Aluminiumphosphats bestehen, wobei das saure Aluminiumphosphat durch Reaktion mit der reaktionsfähigen Aluminiumverbindung das Abbinden der Massen bewirkt. Solche Massen zeichnen sich durch hohe Feuerfestigkeit aus und können je nach Feuerfestigkeit der Füllstoffe im Dauerbetrieb mit Temperaturen bis etwa 1600°C belastet werden. Nachteilig sind die geringe Grünfestigkeit und die lange Abbindezeit solcher Massen, die ein zügiges Arbeiten, etwa beim Ausmauern von Öfen, sehr erschweren. Durch Zusatz wasserlöslicher Fluoride, insbesondere von Ammoniumiluorid, konnte die Abbindezeit verkürzt werden, allerdings auf Kosten der mechanischen Eigenschaften.
  • Aus der USA.-Patentschrift 2 852 401 ist es bekannt, in feuerfesten Massen aus einem hochschmelzenden Füllstoff, einer reaktionsfähigen Aluminiumverbindung und einem sauren Bindemittel als Bindemittel Polyphosphorsäure zu verwenden. Diese Massen binden rascher ab und erreichen wesentlich höhere Grünfestigkeiten als solche, die z. B. o-Phosphorsäure als Bindemittel enthalten.
  • Es wurde nun gefunden, daß bei feuerfesten Massen aus einem hochschmelzenden Füllstoff' einer reaktionsfähigen Aluminiumverbindung und Polyphosphorsäure als Bindemittel die Abbindezeit verkürzt und die Grünfestigkeit erheblich gesteigert werden kann. Solche Massen bestehen aus einem hochschmelzenden Füllstoff', einer reaktionsfähigen Aluminiumverbindung und Polyphosphorsäure mit einem Gehalt an P205 von mindestens 80 °/o als Bindemittel, wobei der Gehalt der Gesamtmasse an Polyphosphorsäure 3 bis 15 Gewichtsprozent und das Verhältnis A1203: P205 1 : 1,4 bis 1 : 4 beträgt, und enthalten gemäß der Erfindung 0,5 bis 3 Gewichtsprozent Aluminiumfluorid, bezogen auf die Gesamtmasse.
  • Die verbesserte Wirkung des Zusatzes von Aluminiumfluorid gemäß der Erfindung ist besonders deshalb überraschend, weil die bisher bekannten Fluoridzusätze sich nachteilig auf die mechanischen Eigenschaften auswirkten und weil ein Zusatz von Aluminiumfluorid praktisch wirkungslos bleibt, wenn als Bindemittel nicht Polyphosphorsäure verwendet wird. Als reaktionsfähige Aluminiumverbindungen eignen sich in erster Linie wohlbekannte Tonerdehydratgele. Sie werden üblicherweise im Gemisch mit plastischen Tonen verwendet, wobei die plastischen Tone ebenfalls teilweise als reaktionsfähige Aluminiumverbindungen anzusehen sind.
  • Beispiel Für die Vergleichsversuche wurden folgende Materialien verwendet: Schamottemehl (40 bis 410/, AI203, Korngröße 0 bis 0,3 mm), Plastischer Ton (Geisenheim, 17 °/o A1203), Tonerdehydratgel (HZS04, 49 °/o A1203), o-Phosphorsäure (58 °/o P205), Polyphosphorsäure (840/" P205), AlF, - 3 H20 technisch.
  • Die Zusammensetzung der Massen ist aus der Tabelle ersichtlich.
    Ver- Ver- Ver- Ver-
    Material such 1 such 2 such 3 such 4
    °/o °/o °/o °@o
    Phosphorsäure
    58 °/o P205 ...... - 8,5 - 11,5
    Polyphosphorsäure
    84 °/o P205 ...... 6,0 - 8,0 -
    Tonerdegel
    49 °/o AI203 ..... 2,5 2,5 3,5 3,5
    Aluminiumfluorid
    AIF3 - 3 11,0 .... - - 2,0 2,0
    Geisenheimer Ton . . 20,0 20,0 15,0 15,0
    Schamotte ......... 71,5 69,0 71,5 68,0
    Die relative P206- und A1203-Menge sowie das A1203: P206-Verhältnis wurden gleich eingestellt.
  • Das Schaubild zeigt, daß die längste Abbindezeit und die geringste Grünfestigkeit mit o-Phosphorsäure erhalten wird (Versuch 2). Ein Zusatz von Aluminiumfluorid (Versuch 4) ändert daran praktisch nichts. Bei Verwendung von Polyphosphorsäure als Bindemittel (Versuch 1) binden die Massen rascher ab und erreichen vor allem schon wesentlich höhere Grünfestigkeiten. Setzt man nun Aluminiumfluorid zu, so steigt die Festigkeit unerwartet schnell an (Versuch 3). Die grüne Zugfestigkeit erreicht nach kurzer Zeit Werte, die über der Zugfestigkeit der feuerfesten Steine liegen.

Claims (1)

  1. Patentanspruch: Feuerfeste Massen, bestehend aus einem hochschmelzenden Füllstoff, einer reaktionsfähigen Aluminiumverbindung und Polyphosphorsäure mit einem Gehalt an P206 von mindestens 800o als Bindemittel, wobei der Gehalt der Gesamtmasse an Polyphosphorsäure 3 bis 15 Gewichtsprozent, bezogen auf das Verhältnis A1203: P206 in der Gesamtmasse 1: 1,4 bis 1: 4, beträgt, d a d u r c h gekennzeichnet, daß die Masse, bezogen auf die Gesamtmischung, 0,5 bis 3 Gewichtsprozent Aluminiumfluorid enthält. In Betracht gezogene Druckschriften: Deutsche Auslegeschrift Nr. 1063 513; USA.-Patentschriften Nr. 2 852 401, 2 866 714; K i n g e r y, »Fundamental Study of Phosphate Bonding in Refractories« in Journal of the Amer. Cer. Soc., 1950, S. 239 bis 241; »Briek and Clay Record«, August 1950, New Bonds for Refractories.
DEF44648A 1964-12-09 1964-12-09 Feuerfeste Massen Withdrawn DE1267161B (de)