DE1112892B - Photosensitive material for diazotype and process for its manufacture - Google Patents
Photosensitive material for diazotype and process for its manufactureInfo
- Publication number
- DE1112892B DE1112892B DER24462A DER0024462A DE1112892B DE 1112892 B DE1112892 B DE 1112892B DE R24462 A DER24462 A DE R24462A DE R0024462 A DER0024462 A DE R0024462A DE 1112892 B DE1112892 B DE 1112892B
- Authority
- DE
- Germany
- Prior art keywords
- aminoplasts
- auxiliary layers
- alcohols
- diazo
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Description
Für weite Anwendungsbereiche eines Reproduktionsmaterials für die Diazotypie ist seine Maßbeständigkeit von fundamentaler Bedeutung. Besonders wichtig für den technischen Gebrauch ist die dauernde Erhaltung der Maßbeständigkeit des Materials bei der Lagerung. So ist z. B. für die Reproduktion von Karten und Plänen, für die Vervielfältigung von für kartographische Zwecke geeigneten Luftbildaufnahmen und für die Wiedergabe besonders exakter Zeichnungen eine hohe Maßbeständigkeit des Kopiermaterials unerläßlich. Hierbei darf dasselbe bei Schwankung der atmosphärischen Bedingungen sich nur ganz unwesentlich sowohl in der Länge als auch in der Breite ändern.For a wide range of applications of a reproduction material for the diazotype is its dimensional stability of fundamental importance. Permanent is particularly important for technical use Maintaining the dimensional stability of the material during storage. So is z. B. for the reproduction of Maps and plans for the reproduction of aerial photographs suitable for cartographic purposes and a high dimensional stability of the copy material for the reproduction of particularly exact drawings indispensable. The same can happen with fluctuations in the atmospheric conditions change only insignificantly both in length and in width.
Mit der Maßbeständigkeit muß vorteilhaft eine so hohe mechanische Festigkeit verbunden sein, daß keine Beschädigung in den Belichtungs- und Entwicklungsmaschinen eintritt. Auch ist die Möglichkeit wiederholten Gebrauchs der fertigen Reproduktionen als Mutterpausen erstrebenswert. Daher sind Einreißfestigkeit, Elastizität und thermische Stabilität bei maßbeständigem Reproduktionsmaterial außerdem auch sehr wesentlich.Such a high mechanical strength must advantageously be associated with the dimensional stability that no damage occurs in the exposure and development machines. There is also the possibility repeated use of the finished reproductions as mother pauses is desirable. Therefore tear resistance, In addition, elasticity and thermal stability with dimensionally stable reproduction material also very essential.
Die Verwendung solchen Materials für die Diazotypie verlangt außerdem eine ausreichende Beständigkeit gegenüber auf 50 bis 80° C erwärmtem, wasserdampfhaltigem, gasförmigem Ammoniak, wie er üblicherweise in den heute gebräuchlichen Entwicklungsmaschinen der Diazotypie zur Hervorrufung des Farbstoffbildes verwendet wird. Stoffe, die diese Beständigkeit gegenüber erwärmtem, wasserdampfhaltigem, gasförmigem Ammoniak nicht besitzen, sind als Kopiermaterial in der Diazotypie nicht geeignet.The use of such material for the diazotype also requires sufficient durability compared to gaseous ammonia heated to 50 to 80 ° C, such as him usually in the developing machines of the diazotype used today to produce the Dye image is used. Substances that have this resistance to heated, steam-containing, do not have gaseous ammonia, are not suitable as copying material in the diazotype.
Für die Herstellung von maßbeständigen Bildträgern für die Diazotypie, welche die vorerwähnten Eigenschaften in genügendem Maße aufweisen, wurden bisher schon die verschiedensten Stoffe vorgeschlagen, ohne daß es bisher gelungen ist, sowohl in ökonomischer als auch in technischer Hinsicht eine befriedigende Lösung zu erzielen.For the production of dimensionally stable image carriers for the diazotype, which the aforementioned Have sufficient properties, a wide variety of substances have been proposed so far, without having succeeded so far, both economically and technically to achieve a satisfactory solution.
Cellulosepapiere sind nicht geeignet, da sich ihre Abmessungen in Abhängigkeit von der Luftfeuchtigkeit ändern. Aber auch Folien aus Estern der Cellulose sind auch dann nicht verwendbar, wenn diesen z. B. Weichmacher zur Verbesserung der Elastizität und anderer Eigenschaften zugesetzt werden. Filme und Folien aus Nitrocellulose sind nicht lichtbeständig und scheiden wegen ihrer sehr schnellen und intensiven Vergilbung für das in der Diazotypie gebräuchlicheDurchleuchtungsverfahrenaus. Folien aus Mischpolymerisaten von Vinylchlorid mit anderen ungesättigten Verbindungen sind nur unvollständig durchCellulose papers are not suitable because their dimensions depend on the humidity change. But films made from esters of cellulose cannot be used even if these z. B. Plasticizers can be added to improve elasticity and other properties. Movies and films made of nitrocellulose are not lightfast and separate because of their very fast and intense Yellowing for the fluoroscopic procedure commonly used in diazotype. Films made from copolymers of vinyl chloride with other unsaturated compounds are only incompletely through
Lichtempfindliches MaterialPhotosensitive material
für die Diazotypie und Verfahrenfor the diazotype and procedure
zu seiner Herstellungfor its manufacture
Anmelder:Applicant:
Renker-Belipa G. m. b. H.,
Lendersdorf-Krauthausen bei Düren (RhId.)Renker-Belipa G. mb H.,
Lendersdorf-Krauthausen near Düren (RhId.)
Dr. rer. nat. Horst KoscheDr. rer. nat. Horst Kosche
und Dr.-Ing. Hermann Winzer, Düren (RhId.),and Dr.-Ing. Hermann Winzer, Düren (RhId.),
sind als Erfinder genannt wordenhave been named as inventors
Tusche beschriftbar sowie für die technische Handhabung zu spröde. Die polymeren Ester der Terephthalsäure mit Glykolen sind als Folien durchaus maßbeständig, jedoch ist es infolge des schlechten Haftens von aufzutragenden Schichten schwierig, sie lichtempfindlich zu präparieren. Weitere Nachteile sind der hohe Preis dieser Folien wie die schwierige Beschriftbarkeit derselben mit Tusche.Ink can be written on as well as for technical handling too brittle. The polymeric esters of terephthalic acid with glycols are quite suitable as films dimensionally stable, but it is difficult to make them due to the poor adhesion of layers to be applied to prepare light-sensitive. Other disadvantages are the high price of these foils as well as the difficult one Can be written on with ink.
Aus der deutschen Patentschrift 734 457 sind bereits Filme, Platten oder Gewebe aus Superpolyamiden bekannt, die, durch Aufbringen oder Einlagerung einer lichtempfindlichen Diazopräparation in die Oberfläche derselben lichtempfindlich gemacht, als Reproduktionsmaterial für die Diazotypie Verwendung finden können. Indessen sind Superpolyamide nicht maßbeständig, auch dann nicht, wenn auf der lichtempfindlichen Schicht eine weitere Schutzschicht angebracht wird, weil Superpolyamide aus der Atmosphäre bis zu 8% Wasser aufnehmen können und dieses Wasser je nach Temperatur und Luftfeuchtigkeit wieder abgeben.German Patent 734 457 already discloses films, plates or fabrics made from superpolyamides known that, by applying or storing a light-sensitive diazo preparation sensitized into the surface of the same, as a reproduction material for the diazotype use can find. However, super polyamides are not dimensionally stable, even if Another protective layer is applied to the photosensitive layer because super polyamides can absorb up to 8% water from the atmosphere and this water depending on the temperature and Release humidity again.
Es wurde nun überraschenderweise gefunden, daß sich Folien aus Polycarbonaten besonders vorteilhaft als Träger für lichtempfindliche Schichten für die Diazotypie mit hoher Maßbeständigkeit und vorzüglicher mechanischer Festigkeit eignen, wenn sie mit zur Aufnahme der lichtempfindlichen Präparation geeigneten Hilfsschichten versehen werden.It has now surprisingly been found that films made from polycarbonates are particularly advantageous as a support for light-sensitive layers for the diazo type with high dimensional stability and excellent mechanical strength are suitable if they are suitable for holding the light-sensitive preparation Auxiliary layers are provided.
109 678/194109 678/194
Unter lichtempfindlichem Diazotypiematerial wer- material nicht verwendet. Es bestand daher auch
den im Sinne der Erfindung Materialien verstanden, keine Klarheit darüber, welche Stoffe oder Stoffkombei
denen die Herstellung eines Farbstoffbildes mit binationen bei dem bisher unbekannten Folien-Hilfe
von lichtempfindlichen Diazoniumverbindungen material eventuell geeignet sein könnten, auf der
oder solchen Vorprodukten erfolgt, die beim Beiich- 5 Polycarbonatfolie fest verankerte und auch gegen
tungsvorgang kupplungsfähige Diazoniumverbindun- mechanische Beanspruchung genügend widerstandsgen
ergeben oder nach Belichtung mit sich selbst fähige Hilfsschichten zu bilden. Diese Hilfsschichten
kuppeln. Dieses Material unterscheidet sich in Her- sind von denen, die zur Verankerung photographistellung
und Arbeitsweise grundsätzlich von dem scher Halogensilberemulsionen dienen, dadurch unterüblichen »photographischen« Material, welches stets io schieden, daß die Halogensilberemulsion während des
die Anwesenheit einer Halogensilberemulsion in Entwicklungsprozesses durch starke Feuchtigkeitswenigstens
einem Verfahrensschritt beim Bildaufbau aufnahme in einen gequollenen Zustand versetzt wird,
fordert. Daher liegt photographisches Material mit während dieser Vorgang bei Diazotypiematerial,
lichtempfindlichen Silbersalzen außerhalb des Be- welches mit gasförmigem Ammoniak entwickelt wird,
reichs der Erfindung. 15 nicht auftritt. Es waren also bei der Auswahl von Unter Polycarbonaten werden nach H. Schnell, Hilfsschichten neue, bisher nicht bekannte Wege zu
»Polycarbonate, eine Gruppe neuartiger thermo- beschreiten. Dazu kam noch, daß diese Hilfsschichten
plastischer Kunststoff« (Angew. Chemie, 68, S. 633 bis im besonderen die Aufnahme der ganz oder teilweise
640 [1956]), nämlich die hochpolymeren Ester der aus einer wäßrigen Lösung bestehenden lichtempfind-Kohlensäure,
verstanden. Insbesondere werden die 20 liehen Diazopräparation in genügender Konzentration
auf Basis von Di-(monooxaryl)-alkanen, beispiels- ermöglichen und zudem noch mit Tusche beschreibweise
von 4,4'-Di-(monooxaryl)-alkanen hergestellten bar und retuschierfähig sein sollten. Endlich durften
Polycarbonate zur Fertigung von Folien verwendet. sich diese Hilfsschichten bei der Einwirkung wasser-Diese,
aber auch andere, maßbeständige Folien er- dampfhaltigen, gasförmigen Ammoniaks ebenso wie
gebenden Polycarbonate eignen sich im Sinne der Er- 25 beim Durchlauf durch die heißen Beliehtungsmaschifindung
als Träger für Diazotypie-Reproduktions- nen von der Polycarbonatfolie nicht ablösen,
material. Es wurde nun gefunden, daß sich Polyamide und/ Es ist dabei zu berücksichtigen, daß gemäß oder vornehmlich verätherte und/oder plastifizierte
H. Schnell (a.a.O.) Polycarbonate als nicht be- Aminoplaste besonders für die Herstellung solcher
ständig gegen Ammoniak bezeichnet werden, während 30 für die Aufnahme lichtempfindlicher Diazopräparaeine
Beständigkeit gegen schwache Alkalien, wie Na- tionen geeigneter Hilfsschichten auf Polycarbonattriumcarbonat-
und Natriumbicarbonatlösungen, vor- folien eignen.Material is not used under light-sensitive diazotype material. There was therefore also the materials understood in the sense of the invention, no clarity as to which substances or combinations of substances on which the production of a dye image with combinations in the previously unknown film aid of light-sensitive diazonium compounds could possibly be suitable on which or such precursors takes place, the diazonium compounds, which are firmly anchored in the case of the Beiich- 5 polycarbonate film and can also be coupled against the process, are sufficiently resistant to mechanical stress or to form auxiliary layers capable of self-exposure after exposure. These auxiliary layers couple. This material differs in terms of its characteristics from those that are used for anchoring the photographing and working method in principle from the shear halogen silver emulsions, in that sub-standard "photographic" material, which always distinguishes the halogen silver emulsion during the development process due to the presence of a halogen silver emulsion at least due to strong moisture a process step during image formation is placed in a swollen state, demands. Therefore, photographic material with silver salts sensitive to light during this process in the case of diazotype material, which is developed with gaseous ammonia, is within the scope of the invention. 15 does not occur. In the selection of polycarbonates, according to H. Schnell, auxiliary layers were treading new, hitherto unknown ways to »polycarbonates, a group of new types of thermal. In addition, these auxiliary layers understood plastic plastic "(Angew. Chemie, 68, p. 633 to in particular the inclusion of all or part of 640 [1956]), namely the high-polymer esters of photosensitive carbonic acid consisting of an aqueous solution . In particular, the 20 borrowed diazo preparations in a sufficient concentration based on di- (monooxaryl) alkanes will, for example, enable and, in addition, they should also be able to be produced and retouched using Indian ink describing 4,4'-di (monooxaryl) alkanes. Polycarbonates were finally allowed to be used to manufacture foils. These auxiliary layers when exposed to water, but also other dimensionally stable foils containing vapor-containing, gaseous ammonia as well as giving polycarbonates, are suitable in the sense of the invention as carriers for diazotype reproductions of the machine when they pass through the hot exposure machine Do not peel off the polycarbonate film,
material. It has now been found that polyamides and / It should be taken into account that according to or primarily etherified and / or plasticized H. Schnell (loc. Cit.) Polycarbonates are not considered to be aminoplasts, especially for the production of such, constantly against ammonia, during 30 Suitable for the inclusion of light-sensitive diazo preparations, resistance to weak alkalis, such as suitable auxiliary layers on polycarbonate trium carbonate and sodium bicarbonate solutions.
handen ist. Da im allgemeinen photographische Ent- Das erfindungsgemäße Verfahren betrifft also die wickler im schwach sauren oder schwach alkalischen Herstellung eines lichtempfindlichen, maßbeständigen Bereich angewendet werden, war es keinesfalls vor- 35 Reproduktionsmaterials für die Diazotypie, welches auszusehen, daß diese Folien, die der Einwirkung als Träger eine Polycarbonatfolie besitzt, die mit zur photographischer Entwickler widerstehen, auch bei Aufnahme der lichtempfindlichen Diazopräparation Verwendung im erfindungsgemäßen Verfahren gegen geeigneten Hilfsschichten aus Polyamiden und/oder die Einwirkung von heißen Ammoniakdämpfen be- verätherten und/oder plastifizierten Aminoplasten verständig sind. 40 sehen ist und mit einer Diazopräparation licht-hand is. Since generally photographic de- The process according to the invention relates to the winder in weakly acidic or weakly alkaline production of a light-sensitive, dimensionally stable Area, it was by no means before reproductive material for the diazotype which look that these films, the action as a support has a polycarbonate film that is used for resist photographic developers, even when taking up the light-sensitive diazo preparation Use in the process according to the invention against suitable auxiliary layers made of polyamides and / or understand the action of hot ammonia vapors etherified and / or plasticized aminoplasts are. 40 can be seen and with a diazo preparation light-
Wird eine Polycarbonatfolie, beispielsweise eine empfindlich gemacht wird.If a polycarbonate sheet, for example one, is made sensitive.
Folie vom Typus »Lonza« 0,1 mm stark, einseitig Unter einer »Diazopräparation« wird das in die mattiert, in eine Ammoniakatmosphäre eingebracht, Hilfsschicht eingelagerte oder auf dieselbe aufgedie in einem Exsikkator unter Atmosphärendruck tragene Diazopräparat verstanden, welches, in Wasser durch Verdampfen von 24%igem wäßrigem Ammo- 45 und/oder einem anderen Lösungsmittel gelöst, lichtniak bei Zimmertemperatur hergestellt worden war, empfindliche kupplungsfähige Diazoniumverbindunso wird sie bereits nach lstündiger Einwirkung so gen, gegebenenfalls auch Kupplungskomponenten stark angegriffen, daß sie beim Berühren infolge ihrer neben Hilfsstoffen, wie anorganische oder organische Sprödigkeit in kleine Teile zerbricht, während nach Säuren, Oxydationsinhibitoren, Metallsalze, Stoffe zur 15stündiger Einwirkung unter den gleichen Bedingun- 50 Erhöhung der Lichtbeständigkeit der Farbstoffe, Antigen die Polycarbonatfolie zu einer teilweise mikro- statika sowie Entwicklungsbeschleuniger oder Entkristallinen schmierigen Masse zerfließt. wicklungshomogenisatoren u. dgl., in derartigen Kon-Es war daher in höchstem Maße überraschend und zentrationen enthält, daß sich nach Belichtung und keinesfalls vorauszusehen, daß diese Polycarbonat- Entwicklung ein deutlich erkennbares Farbstoffbild folie den mehrmaligen Durchgang durch die ge- 55 ergibt.Foil of the »Lonza« type, 0.1 mm thick, one-sided. This is incorporated into the matted, introduced into an ammonia atmosphere, auxiliary layer embedded or applied to the same Understood diazo preparation carried in a desiccator under atmospheric pressure, which, in water dissolved by evaporation of 24% aqueous Ammo-45 and / or another solvent, lichtniak had been produced at room temperature, sensitive couplable diazonium compounds it becomes so after an hour's exposure, if necessary also coupling components strongly attacked that they are touched as a result of their addition to auxiliaries, such as inorganic or organic Brittleness breaks down into small parts, while after acids, oxidation inhibitors, metal salts, substances for 15 hours exposure under the same conditions. 50 Increase in the light resistance of the dyes, antigen the polycarbonate film to a partially micro-static as well as development accelerator or decrystalline greasy mass dissolves. winding homogenizers and the like, in such Kon-Es was therefore extremely surprising and contains centrations that after exposure and under no circumstances can it be foreseen that this polycarbonate development will produce a clearly recognizable dye image slide the repeated passage through the ge 55 results.
bräuchlichen, für die sogenannte Trockenentwicklung Bekanntermaßen wird die lichtempfindliche Diazogeeigneten Entwicklungsmaschinen der Diazotypie, präparation bei anderem, nicht aus Polycarbonaten in denen sich bis 8O0C erwärmter, wasserdampf- bestehendem Folienmaterial mit Hilfe solcher Lösungshaltiger, gasförmiger Ammoniak befindet, bei nor- mittel vorgenommen, die während der kurzen Aufmaler Durchlaufgeschwindigkeit und in einem zur 60 tragszeit das Folienmaterial etwas anlösen oder quel-Bilderzeugung ausreichenden Zeitraum übersteht und len. Da die Diazoniumverbindungen sich bei längerer sich dabei nicht oder nur unwesentlich in ihren Di- Trocknung bei 100° C im Luftstrom zersetzen, ist es mensionen und Festigkeitseigenschaften verändert. nicht möglich, eine zur vollständigen Vertreibung der Dieser überraschende Befund erlaubt die Verwendung Lösungsmittel notwendige Verweilzeit im Trockenvon Polycarbonatfolie zur Herstellung von maßbe- 65 kanal einzuhalten.bräuchlichen, for the so-called dry development is well known, the photosensitive Diazogeeigneten processors of diazotype, preparation-for others, not of polycarbonates in which to 8O 0 C heated, water vapor existing film material by means of such Lösungshaltiger, gaseous ammonia is, made in normal medium, which survives and len during the short run-through speed and in a period of time sufficient to dissolve the film material or to generate swelling images. Since the diazonium compounds do not decompose or decompose only insignificantly in their dehydration at 100 ° C. in the air stream, the dimensions and strength properties are changed. This surprising finding allows the use of solvents to maintain the necessary residence time in the drying of polycarbonate film for the production of dimensional ducts.
ständigem Reproduktionsmaterial für die Diazotypie. Bei Anwendung dieser bekannten Arbeitsweise entFolien aus Polycarbonaten wurden bisher als Träger steht daher ein Reproduktionsmaterial, welches Restfür maßbeständiges lichtempfindliches Diazotypie- betrage des Lösungsmittels festhält, die ihrerseits nunpermanent reproduction material for the diazotype. When using this known working method, remove foils So far, polycarbonates have been used as a carrier as a reproduction material, which remains for dimensionally stable light-sensitive diazotype amount of the solvent, which in turn now
in der Folie als leichtflüchtige Weichmacher wirken. Daher schrumpft das so hergestellte Reproduktionsmaterial bei längerer Lagerung, vornehmlich nach der Bildherstellung, unter Abgabe des Lösungsmittels. Diese Arbeitsweise mit die Folie quellenden und lösenden Lösungsmitteln bei Anwesenheit von Diazoniumverbindungen gestattet es daher nicht, ein maßbeständiges Reproduktionsmaterial für die Diazotypie herzustellen.act as volatile plasticizers in the film. Therefore, the reproduction material produced in this way will shrink after prolonged storage, especially after Image production, with release of the solvent. This way of working with the film swelling and Solvents in the presence of diazonium compounds therefore does not allow a dimensionally stable To produce reproduction material for the diazotype.
Zur Herstellung der erforderlichen Hilfsschichten auf den erfindungsgemäß verwendeten Polycarbonatfolien sind Polyamide besonders geeignet. Sie zeichnen sich durch gute Haftung auf der Polycarbonatfolie, gute Elastizität sowie durch ein günstiges Aufnahmevermögen für die Diazopräparation aus.To produce the necessary auxiliary layers on the polycarbonate films used according to the invention polyamides are particularly suitable. They are characterized by good adhesion to the polycarbonate film, good elasticity and good absorption capacity for diazo preparation.
Unter Polyamiden werden in diesem Zusammenhang die von A. Hopff, A. Müller und F. Wenger in »Die Polyamide« (Springer, 1954) beschriebenen Kondensationsprodukte verstanden. Von diesen sind diejenigen für das erfindungsgemäße Verfahren besonders wertvoll, die eine erhöhte Löslichkeit in Alkoholen mit niederen und mittleren Molekulargewichten besitzen und bei geringem Wasserzusatz zu diesen Lösungen noch nicht ausfallen. Als besonders geeignet für das erfindungsgemäße Verfahren wurden die Handelsprodukte »Ultramid IC« [Wz.] und »UltramidoA« [Wz.] gefunden. Es ist weiterhin zweckmäßig, den Polyamiden verträgliche Weichmacher, wie beispielsweise p-Oxy-2-äthylhexylbenzoat, im Mengenverhältnis von 5 bis 40%, vorzugsweise 5 bis 25% (bezogen auf die Polyamide), zuzusetzen.In this context, polyamides are those of A. Hopff, A. Müller and F. Wenger understood in "Die Polyamides" (Springer, 1954) described condensation products. Of these those for the process according to the invention are particularly valuable which have increased solubility in Have alcohols with low and medium molecular weights and with little added water these solutions do not yet fail. Have been found to be particularly suitable for the method according to the invention the commercial products “Ultramid IC” [watermark] and “UltramidoA” [watermark] found. It is still appropriate plasticizers compatible with the polyamides, such as p-oxy-2-ethylhexyl benzoate, in a proportion of 5 to 40%, preferably 5 to 25% (based on the polyamides) to be added.
Die Feuchtigkeitsaufnahme der aus Polyamiden gebildeten dünnen Hilfsschichten läßt sich in weitem Maße vermindern, wenn diesen vornehmlich mit Alkoholen verätherte Aminoplaste in einem Mengenverhältnis von 5 bis 60%, vorzugsweise 5 bis 20% (bezogen auf die Polyamidmenge), zugesetzt werden.The moisture absorption of the thin auxiliary layers formed from polyamides can be varied Reduce dimensions if these aminoplasts, which are primarily etherified with alcohols, are in a proportion from 5 to 60%, preferably 5 to 20% (based on the amount of polyamide) are added.
Es wurde weiterhin gefunden, daß auch Aminoplaste allein zur Ausbildung von Hilfsschichten auf Polycarbonatfolie sich eignen. Aminoplaste, vornehmlich ihre mit Alkoholen verätherten oder plastifizierten Abkömmlinge, wurden schon verschiedentlich für die Aufnahme von Diazopräparaten vorgeschlagen. Es war aber in dem erfindungsgemäßen Verfahren nicht vorauszusehen, daß die vornehmlich mit Alkoholen verätherten und/oder mit Polyestern oder Alkydharzen elastifizierten Aminoplaste zur Ausbildung einer festen Hilfsschicht nun gerade auf Polycarbonatfolie geeignet sind. Es kann vorteilhaft sein, den Aminoplasten weitere Hilfsstoffe, wie beispielsweise Äthylcellulose, in Mengen von 10 bis 60% (bezogen auf Aminoplaste) und/oder verträgliche Weichmachungsmittel, wie beispielsweise Kondensationsprodukte aus Phthalsäure und Glykolen, zuzusetzen.It has also been found that aminoplasts are also used solely to form auxiliary layers Polycarbonate sheets are suitable. Aminoplasts, especially those that have been etherified or plasticized with alcohols Descendants have already been proposed on various occasions for the inclusion of diazo preparations. In the process according to the invention, however, it could not be foreseen that the predominantly aminoplasts etherified with alcohols and / or elasticized with polyesters or alkyd resins for Formation of a solid auxiliary layer are now just suitable on polycarbonate film. It can be beneficial be, the aminoplasts other auxiliaries, such as ethyl cellulose, in amounts of 10 to 60% (based on aminoplasts) and / or compatible plasticizers, such as condensation products from phthalic acid and glycols.
Unter Aminoplasten werden die in Ullmann, »Encyclopädie der technischen Chemie«, 3. Band, S. 475 bis 496 [1953], beschriebenen Kondensationsprodukte verstanden. Für das erfindungsgemäße Verfahren sind besonders diejenigen Aminoplaste wertvoll, bei denen das Kondensationsprodukt aus der Stickstoffverbindung und dem Aldehyd mit Alkoholen, vorzugsweise aliphatischen Alkoholen, und/oder mit Alkydharzen oder Polyestern elastifiziert ist. Besonders die mit Polyestern oder Alkydharzen plastifizierten, gegebenenfalls verätherten Aminoplaste zeichnen sich durch eine gesteigerte Haftfestigkeit auf der Polycarbonatfolie aus, wenn sie während des Trocknungsprozesses unter Zusatz von löslichen, die Folie nicht angreifenden säurebildenden Stoffen, vorzugsweise Phosphorsäure, gehärtet werden.Aminoplasts are those in Ullmann, "Encyclopadie der technischen Chemie", Volume 3, P. 475 to 496 [1953], understood condensation products described. For the method according to the invention those aminoplasts are particularly valuable in which the condensation product from the Nitrogen compound and the aldehyde with alcohols, preferably aliphatic alcohols, and / or is elasticized with alkyd resins or polyesters. Especially those plasticized with polyesters or alkyd resins, optionally etherified aminoplasts are characterized by an increased adhesive strength the polycarbonate film, if it is during the drying process with the addition of soluble, the Foil non-corrosive acid-forming substances, preferably phosphoric acid, are cured.
Zur Erhöhung des Glanzes einer aus Aminoplasten bestehenden Hilfsschicht und zur Verbesserung ihrer Aufnahmefähigkeit für die Diazopräparation ist es vorteilhaft, diese Schicht nach der Aufbringung auf die Polycarbonatfolie nur bis zur Klebfreiheit zu trocknen, aber nicht vollständig auszukondensieren. DieTo increase the gloss of an auxiliary layer consisting of aminoplasts and to improve it Ability to absorb the diazo preparation, it is advantageous to dry this layer after application to the polycarbonate film only until it is tack-free, but not condense out completely. the
ίο Schlußkondensation erfolgt dann nach der Sensibilisierung durch die im Diazopräparat enthaltenen, Wasserstoffionen bildenden Stoffe bei der Trocknung des auf die Hilfsschicht aufgetragenen Diazopräparats. Die Aufnahmefähigkeit der aus Aminoplasten, besonders aus ihren mit Alkoholen verätherten und/oder plastifizierten Typen, bestehenden Hilfsschicht für die Diazopräparation läßt sich noch steigern, wenn der beispielsweise in wäßrigem Alkohol gelösten Diazopräparation vornehmlich nichtplastifizierte, mit Alkoholen verätherte, geringfügig wasserverträgliche Aminoplaste zugesetzt werden.ίο Final condensation then takes place after the sensitization due to the substances in the diazo preparation that form hydrogen ions during drying of the diazo preparation applied to the auxiliary layer. The absorption capacity of aminoplasts, especially from their etherified and / or plasticized types, existing auxiliary layer for the Diazo preparation can be increased if, for example, the diazo preparation dissolved in aqueous alcohol mainly non-plasticized, etherified with alcohol, slightly water-compatible Aminoplasts are added.
Wird für bestimmte Zwecke eine glänzend glatte Oberfläche des Diazotypie-Reproduktionsmaterials mit einem Träger aus Polycarbonatfolie nicht gewünscht, so ist der Zusatz feindisperser Kieselsäure, vorzugsweise z. B. das Handelsprodukt »Aerosil«, zum Diazopräparat in Mengen von 0,1 bis 5% wertvoll. Used to create a glossy, smooth surface on the diazo type reproduction material for specific purposes with a carrier made of polycarbonate film is not desired, the addition of finely divided silica is preferably e.g. B. the commercial product "Aerosil", valuable for the diazo preparation in amounts of 0.1 to 5%.
Die vornehmlich in Alkoholen oder in leichtflüchtigen, die Polycarbonatfolie nicht oder nur in geringem Maße angreifenden Lösungsmitteln, gegebenenfalls unter Zusatz von Wasser gelösten, die Hilfsschichten bildenden, vorstehend beschriebenen Substanzen werden z. B. mit einer Anspülwalze auf die Folie aufgetragen und vorzugsweise mit einer Luftbürste abgestrichen. Auch mit dosierenden Walzen arbeitende Lackiermaschinen sowie andere, mit Rakelvorrichtungen versehene Streichmaschinen sind verwendbar. Die mit der Hilfsschicht versehene Folie wird anschließend bis zur Klebfreiheit getrocknet, gegebenenfalls durch eine Kühlwalze zur Vermeidung thermoplastischen Klebens abgekühlt und aufgerollt, wobei besonders auf die restlose Vertreibung der Lösungsmittel zu achten ist.Those mainly in alcohols or in volatile ones, the polycarbonate film not or only to a small extent Dimensions of attacking solvents, optionally dissolved with the addition of water, the auxiliary layers forming substances described above are e.g. B. applied to the film with a rinsing roller and preferably wiped off with an air brush. Also working with dosing rollers Painting machines as well as other coating machines provided with doctor blade devices can be used. The film provided with the auxiliary layer is then dried until it is tack-free, if necessary cooled by a chill roll to avoid thermoplastic sticking and rolled up, whereby Pay particular attention to the complete expulsion of the solvents.
Auf diese Hilfsschicht wird anschließend die vornehmlich wäßrigen Alkohol als Lösungsmittel enthaltende Diazopräparation aufgetragen, kurzzeitig danach mit einer Luftbürste abgestrichen und getrocknet. Man erhält eine einseitig beschichtete lichtempfindliehe, durchsichtige, für die Diazotypie geeignete Polycarbonatfolie hoher Maßbeständigkeit, die eine vorzügliche Planlage besitzt.The predominantly aqueous alcohol as solvent is then applied to this auxiliary layer Diazo preparation applied, shortly afterwards wiped off with an air brush and dried. A light-sensitive, transparent polycarbonate film suitable for the diazo type is obtained, coated on one side high dimensional stability, which has an excellent flatness.
Es ist weiterhin auch möglich, beide Seiten der Polycarbonatfolie mit je einer Hilfsschicht zu versehen und lichtempfindlich zu präparieren. Dies Verfahren besitzt für weitere Reproduktionen besondere Vorteile, wenn auf der einen Seite der Folie ein gut deckendes Bild von geringer visueller Wahrnehmbarkeit und auf der anderen Seite ein gut visuell wahrnehmbares, dunkelgefärbtes Bild erzeugt wird. Auch ist es möglich, beide Seiten mit einer Hilfsschicht zu versehen, aber nur eine Seite lichtempfindlich zu präparieren, da hierbei eine besonders bei mechanisch empfindlichen Polycarbonatfolien zweckmäßige Schutzschicht auf der Rückseite aufgebracht wird, der gegebenenfalls zur Eliminierung schädlicher Ammoniakaufnahme saure Substanzen zugesetzt werden können.It is also possible to provide both sides of the polycarbonate film with an auxiliary layer each and to prepare light-sensitive. This method has particular advantages for further reproductions, if on one side of the film there is a well-covering image with little visual perceptibility and on the other hand, a well visually perceptible, dark-colored image is produced. Even it is possible to provide both sides with an auxiliary layer, but only one side is sensitive to light prepare, as this is particularly useful for mechanically sensitive polycarbonate films Protective layer is applied on the back, which may help eliminate harmful ammonia uptake acidic substances can be added.
Die nachfolgend angeführten Beispiele stellen besondere Ausführungsformen der Erfindung dar.The examples given below represent particular embodiments of the invention.
Prüfung auf MaßbeständigkeitCheck for dimensional stability
Klimatische
BedingungenClimatic
conditions
Zur Herstellung einer Hilfsschicht auf Polycarbonatfolie werden 15 Gewichtsteile eines Mischpolyamids, bestehend aus 3 Teilen adipinsaurem Hexamethylendiamin und 2 Teilen ε-Caprolactam (z. B. das Handelsprodukt »Ultramid 6 A« [Wz.]), in 150 Gewichtsteilen Äthanol und 8 Gewichtsteilen Wasser unter Zusatz von 5 Gewichtsteilen p-Oxy-2-äthylhexylbenzoat (als Handelsprodukt »Weichmacher 13«To produce an auxiliary layer on polycarbonate film, 15 parts by weight of a mixed polyamide, Consists of 3 parts of adipic acid hexamethylenediamine and 2 parts of ε-caprolactam (e.g. the Commercial product "Ultramid 6 A" [trademark]), in 150 parts by weight of ethanol and 8 parts by weight of water with the addition of 5 parts by weight of p-oxy-2-ethylhexyl benzoate (as a commercial product »plasticizer 13«
bezeichnet) durch mehrstündiges Sieden unter Rück- .15 „!^™„ ^™
flußkühlung gelöst. Die bei 50° C klare und niedrigviskose Lösung wird bei dieser Temperatur mit einer
Anspülwalze einseitig auf die matte Seite einer
0,1 mm starken, einseitig matten Polycarbonatfolie
aufgetragen, mit einer Luftbürste abgestrichen und bei 20 Trockenschrank 75° C im warmen Luftstrom unter Zuhilfenahme von
Infrarotstrahlung getrocknet. Es entsteht eine festhaftende, klar durchscheinende Schicht, die im Quadratmetergewicht
zwischen 1,5 und 7 g liegt.referred to) by boiling under reflux for several hours .15 "! ^ ™" ^ ™. The at 50 ° C clear and low-viscosity solution is at this temperature with a
Rinse roller on one side on the matte side of one
0.1 mm thick polycarbonate film, matt on one side
applied, wiped off with an air brush and heated at 75 ° C in a warm air stream with the aid of
Dried infrared radiation. The result is a firmly adhering, clear, translucent layer that weighs between 1.5 and 7 g per square meter.
Auf diese Hilfsschicht wird eine in 2 Volumteilen Isopropylalkohol und 1 Volumteil Wasser gelöste Diazopräparation aufgetragen, mit der Luftbürste abgestrichen und im Luftstrom bei 70° C bis zur Lösungsmittelfreiheit getrocknet.On top of this auxiliary layer is dissolved in 2 parts by volume of isopropyl alcohol and 1 part by volume of water Diazo preparation applied, wiped off with an air brush and in a stream of air at 70 ° C until solvent-free dried.
Versuchsbeginn ....Start of the experiment ....
Normalklima
65% relative Luftfeuchte (20° C).. Normal climate
65% relative humidity (20 ° C) ..
Trockenschrank
(40° C) Drying cabinet
(40 ° C)
nebligem Regenwetter mit Taubildung (Temperatur 8 bis 18° C) ..misty rainy weather with dew formation (temperature 8 to 18 ° C).
(100° C) Normalklima Verweilzeit in
Stunden(100 ° C) normal climate dwell time in
hours
Längelength
in mmin mm
nachafter
Prüfungtest
7,57.5
69
33669
336
1,2771.277
1,277
1,2771.277
1.277
1,2771.277
1,276
1,2761.276
1.276
LängenänderungChange in length
mmmmmm
1
01
0
15 Gewichtsteile eines Mischpolyamids, bestehend aus adipinsaurem Hexamethylendiamin, ε-Caprolactam und adipinsaurem 4,4'-Diaminodicyclohexylmethan im Verhältnis 1:1:1 (z. B. das Handelsprodukt15 parts by weight of a mixed polyamide, consisting of adipic acid hexamethylenediamine, ε-caprolactam and adipic acid 4,4'-diaminodicyclohexylmethane in a ratio of 1: 1: 1 (e.g. the commercial product
Das so erhaltene lichtempfindliche Reproduktions- 30 »Ultramid 1C« [WzJ), und 2 Gewichtsteile Benzolmaterial für die Diazotypie wird unter einer Vorlage sulfonsäuremonomethylamid (z. B. das Handelsprodukt »Weichmacher MMA«) werden in 180 Volumteilen Äthanol unter rückfließendem Sieden gelöst. Die bei Zimmertemperatur stabile Lösung wird bei 35 40° C mittels Anspülwalzen auf die Polycarbonatfolie aufgetragen, abgestrichen und im warmen Luftstrom bei 70 bis 120° C getrocknet. Auf die so hergestellte Haftschicht wird eine Diazopräparation, deren Lösungsmittel aus 2 Volumteilen Isopropanol und 1 Vo-Trägermaterials wurden je zehn Prüfstreifen in den 40 lumteil Wasser besteht, aufgetragen, mit der Luft-Abmessungen 50 mm in der Längsrichtung und 15 mm bürste abgestrichen und bei 70 bis 100° C kurzzeitigThe light-sensitive reproduction 30 "Ultramid 1C" [TM] thus obtained, and 2 parts by weight of benzene material For the diazotype, sulfonic acid monomethylamide (e.g. the commercial product "MMA plasticizers") are dissolved in 180 parts by volume of ethanol under refluxing. The solution, which is stable at room temperature, is applied to the polycarbonate film at 35 40 ° C. by means of flushing rollers applied, wiped off and dried in a stream of warm air at 70 to 120 ° C. On the one made in this way The adhesive layer is a diazo preparation, the solvent of which consists of 2 parts by volume of isopropanol and 1 volume of carrier material ten test strips in each of the 40 lum part of water were applied, with the air dimensions 50 mm lengthways and 15 mm brush and at 70 to 100 ° C briefly
getrocknet.dried.
Das so hergestellte maßbeständige Reproduktionsmaterial für die Diazotypie ist besonders dann für die Herstellung von Mutterpausen geeignet, wenn in der Diazopräparation Kupplungskomponenten verwendet werden, die ein stark deckendes gelbes oder braunes Bild ergeben.The dimensionally stable reproduction material for the diazotype produced in this way is particularly suitable for the Production of mother breaks suitable if coupling components are used in the diazo preparation which give a very opaque yellow or brown image.
30 Gewichtsteile eines in Butanol löslichen Mischpolyamids (z. B. das Handelsprodukt »Ultramid LR102« [Wz.]) werden in 200 Volumteilen Butanol unter rückfließendem Sieden gelöst. Diese Lösung wird dünn auf die matte Seite einer Polycarbonatfolie aufgetragen, dünn abgestrichen und bei 100 bis 125° C unter Zuhilfenahme von Ultrarotstrahlern im30 parts by weight of a mixed polyamide soluble in butanol (e.g. the commercial product »Ultramid LR102 «[Wz.]) Are dissolved in 200 parts by volume of butanol under refluxing. This solution is applied thinly to the matt side of a polycarbonate film, smeared thinly and at 100 to 125 ° C with the help of ultrared radiators im
in einer Kopiervorrichtung belichtet und anschließend in einer gebräuchlichen Entwicklungsmaschine für die sogenannte Trockenentwicklung mit 70° C warmem, wasserdampfhaltigem, gasförmigem Ammoniak in zweimaligem Durchgang durch die genannte Apparatur ausentwickelt.exposed in a copier and then exposed in a customary developing machine for the so-called dry development with 70 ° C warm, steam-containing, gaseous ammonia in two passes through the apparatus mentioned.
Von der so hergestellten lichtempfindlichen Polycarbonatfolie und von einer unbehandelten Folie desOf the photosensitive polycarbonate film produced in this way and of an untreated film of the
in der Querrichtung hergestellt und im Zugfestigkeitsversuch geprüft.manufactured in the transverse direction and tested in the tensile strength test.
ZugfestigkeitsprüfungTensile strength test
Polycarbonatfolie
»Lonza«, 0,1 mm,
einseitig matt ....Polycarbonate sheet
»Lonza«, 0.1 mm,
matt on one side ....
Lichtempfindliches
Reproduktionsmaterial mitTräger
aus vorstehender
Polycarbonatfolie
entsprechend Beispiel 1 hergestellt,
belichtet und zweimal entwickelt ..Photosensitive
Reproduction material with carrier
from the above
Polycarbonate sheet
manufactured according to example 1,
exposed and developed twice.
Beginnende Beginning
Dehnung
beistrain
at
Belastung
in kgload
in kg
10,010.0
10,010.0
Dehnung des Prüfkörpers 50mm=0.0/oExtension of the test body 50mm = 0. 0 / o
162162
156156
BruchlastBreaking load
nachafter
erfolgterdone
Dehnungstrain
in kgin kg
12,812.8
12,512.5
Die angegebenen Meßwerte sind Mittelwerte aus zehn Einzelmessungen.The stated measured values are mean values from ten individual measurements.
Luftstrom getrocknet.Airflow dried.
Die derartig hergestellte Hilfsschicht wird mit einer Diazopräparation, die Isopropanol und Butanol neben Wasser als Lösungsmittel enthält, lichtempfindlich gemacht und getrocknet.The auxiliary layer produced in this way is with a Diazo preparation, which contains isopropanol and butanol as a solvent in addition to water, made photosensitive and dried.
Zur Herstellung einer zur Aufnahme der lichtempfindlichen Diazopräparation geeigneten Hilfsschicht auf Polycarbonatfolie werden unter rückfließendem Sieden in 155 Volumteilen technischem Äthanol unterFor the production of an auxiliary layer suitable for receiving the light-sensitive diazo preparation on polycarbonate sheet under refluxing in 155 parts by volume of technical grade ethanol
Zusatz von 8,5 Volumteilen Wasser 15 Gewichtsteile eines Mischpolyamids, bestehend aus adipinsaurem Hexamethylendiamin und ε-Caprolactam im Verhältnis 3:2 (z. B. das Handelsprodukt »Ultramid 6 A« [Wz.]), und 5 Gewichtsteile p-Oxy-äthylhexalbenzoat (z. B. das Handelsprodukt »Weichmacher 13«) gelöst. Zu der abgekühlten Lösung werden unter Rühren 5 Gewichtsteile eines mit Butanol verätherten, aus Melamin und Formaldehyd bestehenden aminoplastbildenden Vorkondensats (z. B. das Handelsprodukt »Maprenal NP « [Wz.] in 6O°/oiger butylalkoholischer Lösung und 0,5 Volumteile konzentrierte Phosphorsäure zugesetzt.Addition of 8.5 parts by volume of water 15 parts by weight of a mixed polyamide consisting of adipic acid Hexamethylenediamine and ε-caprolactam in a ratio of 3: 2 (e.g. the commercial product »Ultramid 6 A« [Wz.]), And 5 parts by weight of p-oxy-ethylhexalbenzoate (e.g. the commercial product “Plasticizer 13”). Add to the cooled solution while stirring 5 parts by weight of an aminoplast-forming compound which is etherified with butanol and consists of melamine and formaldehyde Precondensate (e.g. the commercial product "Maprenal NP" [wat.] In 60% strength butyl alcoholic Solution and 0.5 parts by volume of concentrated phosphoric acid added.
Die so erhaltene Lösung wird dünn auf Polycarbonatfolie aufgetragen, abgestrichen und bei 100 bis 1200C im Trockenkanal so getrocknet, daß Klebfreiheit auftritt, die Schlußkondensation aber noch nicht erfolgt ist.The solution thus obtained is applied thinly to polycarbonate film, and so scraped dried at 100 to 120 0 C in a drying tunnel that non-tackiness occurs, the final condensation is not yet taken place.
Auf die so hergestellte Hilfsschicht wird eine in Alkoholen und Wasser gelöste Diazopräparation aufgetragen und bei 70 bis 100° C kurzzeitig getrocknet, wobei die Schlußkondensation des Aminoplastes alsbald oder nach längerer, z. B. 2- bis 3tätiger Lagerung eintritt.A diazo preparation dissolved in alcohols and water is applied to the auxiliary layer produced in this way and dried briefly at 70 to 100 ° C, with the final condensation of the aminoplast immediately or after a long time, e.g. B. 2- to 3-day storage occurs.
Derartig hergestelltes lichtempfindliches, maßbeständiges Reproduktionsmaterial für die Diazotypie zeichnet sich durch besonderen Oberflächenglanz auf der lichtempfindlich präparierten Schichtseite aus. Ist dieser Glanz nicht erwünscht, so werden der Diazopräparation 2 Gewichtsprozent feindisperse Kieselsäure zugesetzt.Photosensitive, dimensionally stable produced in this way Reproduction material for the diazotype is characterized by a special surface gloss the light-sensitive prepared side of the layer. If this gloss is not desired, the diazo preparation 2 percent by weight of finely divided silica was added.
Zur Herstellung einer zur Aufnahme der lichtempfindlichen Diazopräparation geeigneten Hilfsschicht auf Polycarbonatfolie werden 50 Gewichtsteile eines mit Alkydharzen elastifizierten Harnstoff-Formaldehydharzes (z. B. das Handelsprodukt »Plastopal AW« [Wz.]), öOgewichtsprozentig in Butanol, und 5 Gewichtsteile eines aus Phthalsäure und synthetischen Fettsäuren bestehenden lichtechten Alkydharzes (z. B. das Handelsprodukt »Alkydal RD« [Wz.]) in 200 Gewichtsteilen Äthanol gelöst und kurz vor der Verwendung 50 Gewichtsteile einer Härtelösung, bestehend aus 5gewichtsprozentiger äthylalkoholischer Salzsäure, zugesetzt. Diese Lösung wird mittels einer dosierenden Auftragsvorrichtung auf Polycarbonatfolie gestrichen und bei 100 bis 125° C im Luftstrom unter Zuhilfenahme von Infrarotstrahlern getrocknet. Auf diese Hilfsschicht wird eine Diazopräparation aufgetragen, bei der die zur Bilderzeugung notwendigen Substanzen in 75 Volumteilen Isopropanol und 25 Volumteilen Wasser gelöst sind und der weiterhin 7 Gewichtsteile eines öOgewichtsprozentig in Butanol gelösten, mit Alkoholen partiell verätherten, schnellhärtenden aminoplastbildenden Vorkondensats aus Melamin und Formaldehyd zugesetzt werden.For the production of an auxiliary layer suitable for receiving the light-sensitive diazo preparation 50 parts by weight of a urea-formaldehyde resin elasticized with alkyd resins are placed on polycarbonate film (e.g. the commercial product »Plastopal AW« [Wz.]), oil percent by weight in butanol, and 5 parts by weight of a lightfast alkyd resin composed of phthalic acid and synthetic fatty acids (For example, the commercial product "Alkydal RD" [Wz.]) dissolved in 200 parts by weight of ethanol and shortly before the Use 50 parts by weight of a hardening solution consisting of 5 percent by weight ethyl alcohol Hydrochloric acid, added. This solution is applied to polycarbonate film by means of a metering application device Painted and dried at 100 to 125 ° C in a stream of air with the aid of infrared heaters. A diazo preparation is applied to this auxiliary layer, in which the necessary for image generation Substances are dissolved in 75 parts by volume of isopropanol and 25 parts by volume of water and that continues 7 parts by weight of an oil percent by weight dissolved in butanol, partially etherified with alcohols, fast-hardening aminoplast-forming precondensate of melamine and formaldehyde are added.
Das entsprechend hergestellte maßbeständige lichtempfindliche Reproduktionsmaterial für die Diazotypie besitzt eine besonders harte und klare Oberfläche auf der Schichtseite.The appropriately produced dimensionally stable photosensitive reproduction material for the diazotype has a particularly hard and clear surface on the layer side.
In 185 Gewichtsteilen Äthanol werden 15 Gewichtsteile Äthylcellulose gelöst und zu dieser Lösung unter Rühren 50 Gewichtsteile eines mit Alkydharzen plastifizierten Harnstoffharzes (ζ. B. das Handelsprodukt »Plastopal AW« [Wz.]), öOgewichtsprozentig in Butanol, sowie 2 Gewichtsteile eines Kondensationsproduktes aus Phthalsäure und Glykol (z. B. das Handelsprodukt »Weichharz MM« [Wz.]) zugefügt. Vor der Verwendung werden dieser Lösung 15 Gewichtsteile einer Mischung aus 13 Gewichtsteilen Äthanol und 2 Gewichtsteilen wäßriger Salzsäure (d = 1,18) zugesetzt; dann wird mittels einer dosierenden Auftragsvorrichtung auf Polycarbonatfolie gestrichen und bei 70 bis 110° C im Luftstrom getrocknet. Es entsteht auf der Polycarbonatfolie eine festhaftende klare Zwischenschicht, die zur Aufnahme alkoholisch-wäßriger Diazopräparationen geeignet ist.15 parts by weight of ethyl cellulose are dissolved in 185 parts by weight of ethanol and, with stirring, 50 parts by weight of a urea resin plasticized with alkyd resins (ζ. B. the commercial product "Plastopal AW" [Wz.]), Oil percent in butanol, and 2 parts by weight of a condensation product of phthalic acid and glycol (e.g. the commercial product “Soft Resin MM” [Wz.]) was added. Before use, 15 parts by weight of a mixture of 13 parts by weight of ethanol and 2 parts by weight of aqueous hydrochloric acid (d = 1.18) are added to this solution; Then the polycarbonate film is painted on by means of a metering applicator and dried at 70 to 110 ° C. in a stream of air. A firmly adhering clear intermediate layer is formed on the polycarbonate film, which is suitable for absorbing alcoholic-aqueous diazo preparations.
Claims (8)
Deutsche Auslegeschriften Nr. 1001586, 1064 806.Considered publications:
German Auslegeschriften No. 1001586, 1064 806.