DE10120313A1 - Rectangular assembly block for sanitary installations consists of expanded glass granulate which is provided with a bonding agent and is pressed into a required shape

Info

Publication number: DE10120313A1
Application number: DE10120313A
Authority: DE
Original assignee: WASSER GERAETE GmbH
Current assignee: WASSER GERAETE GmbH
Priority date: 2000-06-10
Filing date: 2001-04-26
Publication date: 2001-12-13
Also published as: DE20010444U1

Abstract

The rectangular assembly block (1) for sanitary installations is characterized by the fact that it consists of expanded glass granulate which is provided with a bonding agent and is pressed into a required shape.

Description

Die Erfindung betrifft einen quaderförmigen Montageblock für die Sanitärinstallation, wobei in den Montageblock mindestens ein Leitungsabschnitt eingebettet ist, der mit seinen Enden stirnseitig aus dem Montageblock vorragt, und in den Leitungsabschnitt jeweils Armaturen integriert sind, insbesondere eine Absperrarmatur und ein Zählerunterteil, wobei die Anschlüsse für die Armaturen durch frontseitige Aussparungen des Montageblocks zugänglich sind und das Material des Montageblocks alle Leitungsabschnitte und Armaturen umgibt und die Außenfläche des Montageblocks bildet.The invention relates to a cuboid mounting block for the sanitary installation, being in the assembly block at least one line section is embedded, the with its ends at the front from the assembly block protrudes, and fittings in the line section are integrated, in particular a shut-off valve and a lower part of the counter, the connections for the Fittings through recesses on the front of the Mounting blocks are accessible and the material of the Assembly blocks all line sections and fittings surrounds and forms the outer surface of the mounting block.

Montageblöcke dieser Art sind im Stand der Technik vielfältig bekannt, wozu beispielsweise auf die EP 0 853 753 B1 verwiesen wird. Die dort beschriebenen Montagebausteine werden aus Polyurethanschaum (2- Komponenten-Material) hergestellt. Solches Material ist hinsichtlich des Herstellungsaufwandes relativ aufwendig, da das Schaummaterial in einer geschlossenen Form geschäumt werden muss und die Form entsprechende Verklammerungen oder Verspannungen aufweisen muss, um die Form während des Schäumvorganges geschlossen zu halten. Zudem ist bei dem angegebenen Material nachteilig, dass dieses Material nur begrenzt temperaturbeständig ist, so dass dieses Material und damit der komplette Montageblock nicht schwer entflammbar ist und somit für bestimmte Bedingungen, in denen eine schwere Entflammbarkeit oder sogar eine sehr schwere Entflammbarkeit erforderlich ist, unbrauchbar ist. Desweiteren ist bei dem angegebenen Material nachteilig, dass es beim Verputzen des Montageblockes nach dessen Installation in dem entsprechenden Bauwerk häufig zu Abrissen zwischen dem Putz und dem Montageblock kommt, da das Verputzmaterial keinen festen Halt auf dem PU-Material findet.Mounting blocks of this type are state of the art widely known, for example on EP 0 853 753 B1 is referred. The ones described there Assembly blocks are made of polyurethane foam (2- Component material). Such material is relative to the manufacturing effort complex, because the foam material in a closed Form must be foamed and the form corresponding Must have brackets or tension to the mold closed during the foaming process hold. In addition, with the specified material disadvantageous that this material is limited is temperature resistant, so this material and so that the complete assembly block is not difficult is flammable and therefore for certain conditions, in which are highly flammable or even very flame retardancy is required, unusable is. Furthermore, with the specified material disadvantageous that it is when plastering the mounting block after its installation in the corresponding structure often between the plaster and the Assembly block comes because the plastering material is not a solid Holds on the PU material.

Ausgehend von diesem Stand der Technik liegt der Erfindung die Aufgabe zugrunde, einen Montageblock gattungsgemäßer Art zu schaffen, der äußerst beständig gegen aggressive Medien ist, der mindestens schwer entflammbar, vorzugsweise sehr schwer entflammbar ist, der einfach und kostengünstig gefertigt werden kann und bei dessen Herstellung auf einfache und preiswert zu erhaltende Rohstoffe zurückgegriffen werden kann.Based on this state of the art Invention the task of an assembly block to create generic type that is extremely durable against aggressive media is at least difficult flammable, preferably very flame retardant, that can be manufactured easily and inexpensively and in its manufacture to simple and inexpensive too conserving raw materials can be used.

Zur Lösung dieser Aufgabe wird vorgeschlagen, dass der Montageblock aus Blähglasgranulat, welches mit Bindemittel verpresst ist, besteht.To solve this problem, it is proposed that the Mounting block made of expanded glass granules, which with Binder is pressed.

Blähglasgranulat ist an sich im Stand der Technik bekannt. Ein zum erfindungsgemäßen Zweck besonders geeignetes Material ist beispielsweise in der DE 43 42 996 C2 beschrieben.Expanded glass granulate is in itself state of the art known. A particularly for the purpose of the invention Suitable material is, for example, in DE 43 42 996 C2 described.

Durch die erfindungsgemäße Ausbildung wird ein Montageblock geschaffen, der hinsichtlich des Herstellungsmaterials schwer entflammbar ist und ggf. sogar sehr schwer entflammbar ist, so dass er der Brandklasse B1 entspricht. Die Herstellung eines solchen Montageblocks ist äußerst einfach zu bewerkstelligen. Zudem kann als Grundmaterial für die Herstellung Blähglasgranulat verwendet werden, welches aus Altglas recycelt ist. Das Herstellungsmaterial ist somit äußerst kostengünstig zu erhalten. Als Bindemittel können geeignete chemische Bindemittel oder auch Klebstoffe eingesetzt werden. Insgesamt wird ein Montageblock zur Verfügung gestellt, der äußerst formstabil ist und den Einsatzzwecken in jeglicher Weise hervorragend genügt. Dabei ist besonders vorteilhaft, dass durch die Ausbildung aus Blähglasgranulat eine körnige bis rauhe Oberflächenstruktur des Montageblockes erreicht ist, so dass das anschließende Verputzen des Montageblockes, wenn dieser gebäudeseitig installiert ist, ohne Probleme zu vollziehen ist, da das Putzmaterial eine ausgezeichnete Verbindung mit dem Werkstoff des Montageblockes eingeht.The training according to the invention is a Assembly block created, the regarding Manufacturing material is flame retardant and possibly is even very flame retardant, making it the Fire class B1 corresponds. The making of one Assembly blocks are extremely easy to do. It can also be used as a base material for manufacturing Expanded glass granulate can be used, which is made from waste glass is recycled. The manufacturing material is therefore extremely to get inexpensive. Can as a binder suitable chemical binders or adhesives be used. Overall, one assembly block is used Provided that is extremely stable and the Purpose in any way is perfectly sufficient. It is particularly advantageous that the Formation from expanded glass granules a granular to rough Surface structure of the mounting block is reached, so that the subsequent plastering of the assembly block, if this is installed on the building side, without problems is to be carried out because the cleaning material is a excellent connection with the material of the Assembly block received.

Der erfindungsgemäße Montageblock ist nahezu unverrottbar und weist äußerst geringes Gewicht auf. Zudem ist der Montageblock in einfacher Weise wieder zu recyceln.The assembly block according to the invention is almost rot-proof and extremely light. In addition, the assembly block is closed again in a simple manner recycle.

Eine bevorzugte Weiterbildung wird darin gesehen, dass der Montageblock aus einer Mischung von Blähglasgranulat mit folgenden Bestandteilen besteht:
Blähglasgranulat Körnung 0,2 bis 0,5 mm,
Blähglasgranulat Körnung 0,5 bis 1,0 mm.A preferred further development is seen in the fact that the assembly block consists of a mixture of expanded glass granulate with the following components:
Expanded glass granules grain size 0.2 to 0.5 mm,
Expanded glass granulate grain size 0.5 to 1.0 mm.

Vorzugsweise wird Blähglasgranulat einer Körnung von 0,2 bis 0,5 mm mit solchem Material von einer Körnung mit 0,5 bis 1,0 mm in gleichen Teilen homogen vermischt und mit dem entsprechenden Bindemittel oder Klebmittel ebenso homogen vermischt. Durch Pressen und Erhitzen in einer entsprechenden Form kann der Montageblock in einfacher Weise gefertigt werden, wobei die entsprechenden Armaturen und Leitungsabschnitte in die Form eingelegt werden können, ebenso wie Befestigungselemente, die in den Montageblock integriert werden können, um diesen in einfacher Weise an bestehenden Installationen befestigen zu können.Expanded glass granules with a grain size of 0.2 are preferred up to 0.5 mm with such material with a grain size 0.5 to 1.0 mm homogeneously mixed in equal parts and with the appropriate binder or adhesive mixed equally homogeneously. By pressing and heating in the mounting block can have a corresponding shape in are manufactured in a simple manner, the corresponding fittings and pipe sections in the Form can be inserted, as well Fastening elements integrated in the assembly block can be made to do this in a simple manner to be able to fix existing installations.

Bevorzugt ist dabei vorgesehen, dass das Blähglasgranulat aus einer homogenen Mischung in gleichen Teilen der angegebenen Körnung besteht.It is preferably provided that the Expanded glass granulate from a homogeneous mixture in equal parts of the specified grain size.

Desweiteren ist bevorzugt vorgesehen, dass das Bindemittel bis zu 15 Masse-% enthalten ist.Furthermore, it is preferably provided that the Binder up to 15 mass% is included.

Auch ist bevorzugt, dass mindestens 8 Masse-% Bindemittel enthalten sind.It is also preferred that at least 8% by mass Binders are included.

Zudem kann bevorzugt sein, dass als Bindemittel Polyurethan, Epoxidharz, Latex oder eine Mischung daraus vorgesehen ist.It may also be preferred that as a binder Polyurethane, epoxy, latex or a mixture of these is provided.

Besonders bevorzugt ist vorgesehen, dass das Blähglasgranulat eine vorwiegend geschlossenporige Oberfläche und im Kern Poren im Durchmesserbereich von 0,0001 bis 0,5 mm aufweist.It is particularly preferably provided that the Expanded glass granules are mainly closed-pore Surface and in the core pores in the diameter range of 0.0001 to 0.5 mm.

Ein Verfahren zur Herstellung eines Montageblockes nach einem der Ansprüche 1 bis 7 ist durch folgende Verfahrensschritte gekennzeichnet:
die Leitungsabschnitte mit integrierten Armaturen werden in eine Pressform eingelegt und lagerichtig gehalten,
Blähglasgranulat wird aus unterschiedlicher Körnung gleichmäßig gemischt und mit chemischem Bindemittel versetzt,
das so gemischte Material wird in die Pressform eingefüllt,
anschließend wird die Pressform geschlossen und das Material verpresst,
nach dem Verpressen wird die Pressform geöffnet und der Montageblock entnommen.A method for producing an assembly block according to one of claims 1 to 7 is characterized by the following method steps:
the pipe sections with integrated fittings are placed in a press mold and held in the correct position,
Expanded glass granulate is mixed evenly from different grain sizes and mixed with chemical binder,
the material mixed in this way is filled into the mold,
then the mold is closed and the material is pressed,
after pressing, the mold is opened and the assembly block removed.

Dabei ist bevorzugt vorgesehen, dass die Verpressung unter gegenüber Raumtemperatur erhöhter Temperatur erfolgt.It is preferably provided that the compression under elevated temperature compared to room temperature he follows.

Die Aussparungen im Montageblock können durch den Einsatz von topfartigen Hülsen oder dergleichen hergestellt werden, so dass die Aussparungen frei von Blähglasgranulat bleiben.The cutouts in the assembly block can be made through the Use of pot-like sleeves or the like are made so that the recesses are free of Expandable glass granules remain.

Die Erfindung ist nachstehend anhand eines schematisierten Ausführungsbeispieles beschrieben.The invention is based on a Schematic embodiment described.

In der Zeichnung ist ein quaderförmiger Montageblock 1 gezeigt, der für die Sanitärinstallation dient. In den Montageblock sind vorzugsweise mittig zwischen dessen Vorder- und Rückseite Leitungsabschnitte 2 eingebettet, die zu Armaturensträngen gehören, die parallel zueinander im Montageblock angeordnet sind. Jeder Leitungsabschnitt 2 ragt oberseitig und unterseitig stirnseitig aus dem Montageblock hervor und weist Anschlüsse auf, beispielsweise Schraubanschlüsse oder auch Lötanschlüsse. Auch eine Verklebung der Anschlüsse mit entsprechenden Anschlußleitungen ist möglich. Zudem sind in die Leitungsabschnitte Armaturen 3, 4 integriert, deren Anschlüsse durch frontseitige Aussparungen des Montageblocks 1 zugänglich sind, so dass entsprechende Anschlußarmaturen angeschlossen werden können. Das Material des Montageblocks 1 umgibt alle Leitungsabschnitte 2 sowie darin eingebettete Armaturen mit Ausnahme der entsprechenden Ausschnitte, wobei das Material gleichzeitig die Außenfläche des Montageblocks bildet. Dieser ist also nicht zusätzlich mit einem Gehäuse oder dergleichen umgeben.In the drawing, a cuboid mounting block 1 is shown, which is used for the sanitary installation. In the assembly block, line sections 2 are preferably embedded centrally between its front and rear sides, which belong to armature strings which are arranged parallel to one another in the assembly block. Each line section 2 protrudes from the mounting block on the top and bottom sides and has connections, for example screw connections or solder connections. It is also possible to glue the connections to the corresponding connecting lines. In addition, fittings 3 , 4 are integrated in the line sections, the connections of which are accessible through cutouts on the front of the mounting block 1 , so that corresponding connecting fittings can be connected. The material of the assembly block 1 surrounds all line sections 2 and fittings embedded therein with the exception of the corresponding cutouts, the material simultaneously forming the outer surface of the assembly block. So this is not additionally surrounded by a housing or the like.

Erfindungsgemäß besteht der Montageblock 1 aus Blähglasgranulat, welches mit Bindemittel versetzt und verpresst ist. Vorzugsweise kann in einen solchen Montageblock 1 die Integration von zwei parallelen Leitungssträngen 3 nebst Armaturenanschlüssen 3, 4 vorgesehen sein. Dabei ist mittig des Montageblocks 1 eine Trennfuge 5 vorgesehen, so dass der Montageblock 1 auch in zwei gleiche Teile zerlegbar ist, die jeweils nur einen Leitungsstrang 2 mit Armaturen 3, 4 aufweisen.According to the invention, the assembly block 1 consists of expanded glass granulate, which is mixed with binder and pressed. In such an assembly block 1, the integration of two parallel line strands 3 together with valve connections 3 , 4 can preferably be provided. A separating joint 5 is provided in the middle of the assembly block 1 , so that the assembly block 1 can also be dismantled into two identical parts, each of which has only one cable run 2 with fittings 3 , 4 .

Vorzugsweise ist der Montageblock 1 aus einer Mischung von Blähglasgranulat mit folgenden Bestandteilen gefertigt:
Blähglasgranulat mit der Körnung 0,2 bis 0,5 mm,
Blähglasgranulat mit einer Körnung von 0,5 bis 1,0 mm.The assembly block 1 is preferably made from a mixture of expanded glass granulate with the following components:
Expanded glass granules with a grain size of 0.2 to 0.5 mm,
Expanded glass granules with a grain size of 0.5 to 1.0 mm.

Dabei sind die angegebenen Materialien mit der unterschiedlichen Körnung zu einer homogenen Mischung aus gleichen Teilen der angegebenen Körnung vermischt. Das Bindemittel kann wenigstens 8 Masse-% bis zu 15 Masse-% eingesetzt werden, wobei als Bindemittel beliebige geeignete Stoffe in Betracht kommen. Vorzugsweise kann Polyurethan, Epoxidharz, Latex oder eine Mischung daraus vorgesehen sein. Das Blähglasgranulat weist eine vorwiegend geschlossenporige Oberfläche und im Kern Poren im Durchmesserbereich von 0,0001 bis 0,5 mm auf. Der derart ausgebildete Montageblock 1 ist relativ leichtgewichtig und unverrottbar. Das Material ist wieder recycelbar. Das Material kann eine gute Bindung zu Putzmaterial eingehen. Zudem ist das Material schwer entflammbar und bei Einsatz von entsprechendem Binde- oder Klebmittel sogar sehr schwer entflammbar, so dass er der Brandklasse B2 oder sogar der Brandklasse B1 unterliegt. Aufgrund der entsprechenden Ausbildung ist der Montageblock 1 nur gering wärmeleitfähig, also im Wesentlichen isolierend. Dabei ist der Montageblock 1 äußerst druckfest. Zur Herstellung eines solchen Montageblockes können die zueinander parallelen Leitungsabschnitte 2 samt integrierten Armaturenteilen 3, 4 lagerichtig in eine Form eingelegt und auf Abstand gehalten werden, wobei zudem noch Befestigungselemente 6, beispielsweise in Form von Gewindehülsen, in die Form eingelegt und gehalten werden können. Anschließend wird das Gemisch aus Blähglasgranulat unterschiedlicher Körnung und Bindemittel oder Klebmittel in die Form eingebracht. Nachfolgend kann die Pressform mit einer entsprechenden Platte oder mit einer Platte, die Formteile trägt, die die Ausnehmungen im Bereich 3, 4 begrenzen, geschlossen werden und das Material vorzugsweise unter Temperatureinwirkung verpresst werden. Anschließend kann der fertige Montageblock 1 aus der Form entnommen werden, wenn die Form geöffnet ist.The specified materials with the different grain sizes are mixed to form a homogeneous mixture of equal parts of the specified grain size. The binder can be used at least 8% by mass up to 15% by mass, any suitable substances being considered as binders. Polyurethane, epoxy resin, latex or a mixture thereof can preferably be provided. The expanded glass granulate has a predominantly closed-pore surface and the core has pores in the diameter range from 0.0001 to 0.5 mm. The assembly block 1 designed in this way is relatively light-weight and rot-proof. The material is recyclable again. The material can form a good bond with the cleaning material. In addition, the material is flame retardant and even very flame retardant when using the appropriate binder or adhesive, so that it is subject to fire class B2 or even fire class B1. Due to the appropriate design, the mounting block 1 is only slightly thermally conductive, that is to say essentially insulating. The mounting block 1 is extremely pressure-resistant. To produce such an assembly block, the mutually parallel line sections 2 together with integrated armature parts 3 , 4 can be inserted in the correct position in a mold and kept at a distance, and fastening elements 6 , for example in the form of threaded sleeves, can also be inserted and held in the mold. The mixture of expanded glass granules of different grain sizes and binders or adhesives is then introduced into the mold. Subsequently, the mold can be closed with a corresponding plate or with a plate that carries molded parts that delimit the recesses in the area 3 , 4 , and the material is preferably pressed under the influence of temperature. The finished assembly block 1 can then be removed from the mold when the mold is open.

Die Erfindung ist nicht auf das Ausführungsbeispiel beschränkt, sondern im Rahmen der Offenbarung vielfach variabel.The invention is not based on the embodiment limited, but often within the scope of the disclosure variable.

Alle neuen, in der Beschreibung und/oder Zeichnung offenbarten Einzel- und Kombinationsmerkmale werden als erfindungswesentlich angesehen.All new, in the description and / or drawing disclosed individual and combination features are considered viewed essential to the invention.

Claims

1.Rectangular mounting block ( 1 ) for the sanitary installation, at least one pipe section ( 2 ) is embedded in the mounting block ( 1 ), the ends of which protrude from the mounting block ( 1 ) at the front, and fittings () in the pipe section ( 2 ) 3 , 4 ) are integrated, in particular a shut-off valve and a lower part of the meter, the connections for the valves being accessible through cutouts on the front of the mounting block ( 1 ) and the material of the mounting block ( 1 ) all line sections ( 2 ) and fittings ( 3 , 4 ) surrounds and forms the outer surface of the assembly block ( 1 ), characterized in that the assembly block ( 1 ) consists of expanded glass granulate, which is pressed with binder.

2. Assembly block according to claim 1, characterized in that the assembly block ( 1 ) consists of a mixture of expanded glass granules with the following components:
Expanded glass granules grain size 0.2 to 0.5 mm,
Expanded glass granulate grain size 0.5 to 1.0 mm.

3. Assembly block according to claim 2, characterized in that the expanded glass granulate from a homogeneous mixture consists of equal parts of the specified grit.

4. Mounting block according to one of claims 1 to 3, characterized in that the binder up to 15 mass% is included.

5. Mounting block according to one of claims 1 to 4, characterized in that at least 8% by mass Binders are included.

6. assembly block according to one of claims 1 to 5, characterized in that as a binder Polyurethane, epoxy, latex or a mixture from it is provided.

7. Mounting block according to one of claims 1 to 6, characterized in that the expanded glass granules a predominantly closed-pore surface and in the core Pores in the diameter range from 0.0001 to 0.5 mm having.

8. A method for producing an assembly block according to one of claims 1 to 7, characterized by the following method steps:
the pipe sections with integrated fittings are placed in a press mold and held in the correct position,
Expanded glass granulate is mixed evenly from different grain sizes and mixed with chemical binder,
the material mixed in this way is filled into the mold,
then the mold is closed and the material is pressed,
after pressing, the mold is opened and the assembly block removed.

9. The method according to claim 8, characterized in that the compression below versus room temperature elevated temperature.