DE1054885B - Process for the production of a laminated aluminum foil with a grease-proof, thermoplastic coating - Google Patents
Process for the production of a laminated aluminum foil with a grease-proof, thermoplastic coatingInfo
- Publication number
- DE1054885B DE1054885B DEA21094A DEA0021094A DE1054885B DE 1054885 B DE1054885 B DE 1054885B DE A21094 A DEA21094 A DE A21094A DE A0021094 A DEA0021094 A DE A0021094A DE 1054885 B DE1054885 B DE 1054885B
- Authority
- DE
- Germany
- Prior art keywords
- aluminum foil
- parts
- grease
- proof
- paper
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Description
DEUTSCHESGERMAN
kl. 75 c 5/06kl. 75 c 5/06
INTERNAT. KL. B 44 dINTERNAT. KL. B 44 d
PATENTAMTPATENT OFFICE
A 21094 IVc/75 cA 21094 IVc / 75 c
ANMELDETAG: 7. SEPTEMBER 1954REGISTRATION DATE: SEPTEMBER 7, 1954
BEKANNTMACHUNG
DER ANMELDUNG
UND AUSGABE DER
AUSLEGESCHRIFT: 9. A P R I L 1 9 5 9NOTICE
THE REGISTRATION
AND ISSUE OF THE
EDITORIAL: 9 APRIL 1 9 5 9
Eine mit einem thermoplastischen Kunststoff lackierte Aluminium-Folie genügt bezüglich Fettdichtigkeit den normalen Ansprüchen bei der Verpackung von kochfertigen Suppen u. dgl., auch wenn zwischen Aluminium-Folie und Überzug aus thermoplastischem Kunststoff eine Lage aus wasserdampfdurchlässigem Papier angeordnet ist, wobei die Papierseite dem Inhalt zugekehrt ist. Gegenüber Füllgütern mit hohen und bzw. oder leicht flüssigen Fettanteilen genügt jedoch eine solche Aluminium-Folie nicht in jeder Hinsicht. So kann z. B. bei Beuteln, die aus diesem Material gefertigt sind und eine kochfertige Suppe mit Hühnerfettanteil enthalten, das Fett durch die Heißklebestelle hindurchdringen und häßliche Flecken in der Pappschachtel, in der die Beutel gelagert und transportiert werden, verursachen, was den Eindruck hervorrufen kann, daß ein erheblicher Teil des Fettgehaltes der Suppe verlorengegangen sei oder tatsächlich auf einen spürbaren Fettverlust schließen läßt.An aluminum foil coated with a thermoplastic is sufficient in terms of grease tightness normal requirements for the packaging of ready-to-cook soups and the like, even if between aluminum foil and a layer of water-vapor-permeable paper is arranged in a thermoplastic plastic coating, with the paper side facing the content. Compared to filling goods with high and / or slightly liquid However, such an aluminum foil is not sufficient for fat content in every respect. So z. B. in bags that are made of this material and contain a ready-to-cook soup with chicken fat, the fat through the hot glue line penetrate and ugly stains in the cardboard box in which the bags are stored and are transported, cause what can give the impression that a significant part of the fat content the soup has been lost or actually suggests a noticeable loss of fat.
Liegt eine papierkaschierte Aluminium-Folie vor, die auf der Papierseite mit einem einfachen Überzug aus thermoplastischem Kunststoff versehen ist, kann das Füllgut in Verpackungen, die aus diesem Material hergestellt sind, unansehnlich wirkende Fettflecken im Papier hervorrufen, die besonders stark in Erscheinung treten, weil dann an den fettigen Stellen die Aluminium-Folie durchscheint.If there is a paper-laminated aluminum foil, which is covered on the paper side with a simple coating thermoplastic material is provided, the filling material can be packaged in packaging made from this material cause unsightly-looking grease stains in the paper, which are particularly noticeable step, because then the aluminum foil will shine through at the greasy areas.
Die vorliegende Erfindung bezieht sich nun auf ein Verfahren zur Herstellung einer kaschierten Aluminium-Folie mit fettdichter, thermoplastischer Beschichtung.The present invention now relates to a method for producing a laminated aluminum foil with grease-proof, thermoplastic coating.
Das erfindungsgemäße Verfahren zeichnet sich dadurch aus, daß auf die Papierseite einer mit Papier kaschierten Aluminium-Folie zuerst ein fettunlöslicher, thermoplastischer Kunststoff als wäßrige Dispersion oder wäßrige Lösung und dann ein fettunlöslicher, thermoplastischer Kunststoff als Lösung in einem organischen Lösungsmittel aufgebracht wird. Bei diesem Vorgehen können auch Aluminium-Folien verwendet werden, die mit einem wasserdampfdurchlässigerl Papier kaschiert sind.The method according to the invention is characterized in that one laminated with paper on the paper side Aluminum foil first a fat-insoluble, thermoplastic material as an aqueous dispersion or aqueous solution and then a fat-insoluble, thermoplastic plastic as a solution in an organic Solvent is applied. In this procedure, aluminum foils can also be used, which Laminated with a water vapor permeable paper are.
: Es. hat sich überraschenderweise gezeigt, daß eine solche thermoplastische Mehrfachbeschichtung in hohem Maße fettdicht ist, und zwar in viel höherem Maße als eine doppelte Beschichtung mit einem nur als Dispersion oder wäßrige Lösung oder nur als Lösung in einem organischen Lösungsmittel aufgetragenen thermoplastischen Kunststoff.: It. has surprisingly been shown that such a thermoplastic multiple coating in high Is grease-proof to a degree, and to a much greater extent than a double coating with one only as a dispersion or aqueous solution or thermoplastic applied only as a solution in an organic solvent Plastic.
Es ist zwar bekannt, beim Aufbringen festhaftender Schutzschichten auf glatte Flächen oder bei der Lackierung von Konservendosen zum Zwecke des Korrosionsschutzes mehrere Schichten von Kunststoffen gelöst oder dispergiert in verschiedenen Lösungsmitteln aufzubringen. Problemstellung und Arbeitsweise sind dabei jedoch grundsätzlich verschieden vom vorliegenden Verfahren zur Herstellung von fettdichten Aluminium-Folien, bei Verfahren zur HerstellungIt is known when applying firmly adhering protective layers to smooth surfaces or when painting Several layers of plastics have been removed or removed from food cans for the purpose of corrosion protection to be applied dispersed in various solvents. However, the problem and the way of working are included fundamentally different from the present process for the production of greaseproof aluminum foils Method of manufacture
einer kaschierten Aluminium-Foliea laminated aluminum foil
mit fettdichter, thermoplastischerwith grease-proof, thermoplastic
BeschichtungCoating
Anmelder:Applicant:
Aluminium-Walzwerke Singen G.m.b.H., Singen (Hohentwiel)Aluminum rolling mills Singen G.m.b.H., Singen (Hohentwiel)
Dipl.-Chem. Dr. phil. Karl BroockmannDipl.-Chem. Dr. phil. Karl Broockmann
und Dipl.-Ing. Rolf Schnell, Singen (Hohentwiel), sind als Erfinder genannt wordenand Dipl.-Ing. Rolf Schnell, Singen (Hohentwiel), have been named as the inventor
dem die Kunststoffschichten auf die Papierseite einer kaschierten Metallfolie aufgetragen werden.where the plastic layers are applied to the paper side of a laminated metal foil.
Gute Ergebnisse zeitigt das vorliegende Verfahren bei Verwendung einer ungefähr 50%igen Kunststoffdispersion. Es ist vorteilhaft, dieser Dispersion ein Mittel zuzugeben, welches das Zusammenkleben der Folienlagen nach einem Aufrollen vor dem zweiten Kunststoffauftrag verhindert. In Frage kommt hierfür z. B. Stärke- und bzw. oder Dextrinleim zusammen mit hochdisperser Kieselsäure. Solche Mittel sind dem Lackfachmann bekannt. An Stelle von Kieselsäure lassen sich unter anderem auch Bentonit, China-Clay, Tonerdehydrat oder andere inerte Pulver verwenden. Die Gesamtheit dieser Zusätze, als feste Substanzen gerechnet, soll nicht mehr als 50 Gewichtsprozent, vorzugsweise nicht mehr als 15 Gewichtsprozent, des Kunststoffanteiles der Dispersion oder der wäßrigen Lösung betragen.The present method produces good results when using an approximately 50% plastic dispersion. It is advantageous to add an agent to this dispersion which prevents the film layers from sticking together prevented after rolling up before the second application of plastic. For this purpose comes z. B. Strength and or or dextrin glue together with highly dispersed silica. Such means are known to the paint expert. Instead of silica, bentonite, china clay, alumina hydrate or others can also be used use inert powders. The total of these additives, calculated as solid substances, should not exceed 50 percent by weight, preferably not more than 15 percent by weight, of the plastic content of the dispersion or the aqueous solution.
Auch der Kunststofflösung in organischen Lösungsmitteln können inerte Pigmente zugesetzt werden.Inert pigments can also be added to the plastic solution in organic solvents.
Eine mit der Mehrfachbeschichtung versehene papierkaschierte Aluminium-Folie ist geschmeidiger als eine ebenso starke, mit Hilfe von Leim oder Lack pergamentkaschierte Aluminium-Folie und wirtschaftlicher als zwei aufeinandergeklebte Aluminium-Folien mit oder ohne Papierzwischenschicht und als eine mit Kunststoff-Folie kaschierte Aluminium-Folie. Eine solche papierkaschierte Aluminium-Folie mit Mehrfachbeschichtung auf der Papierseite eignet sich insbesondere für Beutelpackungen, die ein Füllgut mit hohem und bzw. oder leicht flüssigem Fettanteil, wie gewisse kochfertige Suppen und Suppositorien, enthalten. Eine solche Folie eignet sich auch zur Verpackung von Fetten.A paper-laminated aluminum foil provided with the multiple coating is more flexible than one equally strong, parchment-laminated aluminum foil with the help of glue or varnish and more economical than two Aluminum foils glued to one another with or without a paper intermediate layer and as one with a plastic foil laminated aluminum foil. Such a paper-laminated aluminum foil with multiple coating on the The paper side is particularly suitable for pouch packs that have a high and / or slightly liquid content Contain fat content, such as certain ready-to-cook soups and suppositories. Such a film is also suitable for Packaging of fats.
809 789/294809 789/294
Auf die Papierseitc einer mittels Lackes, Kunstharzdispersion oder Leimes papierkaschierten Aluminium-Folie wird folgende wäßrige Kunststoffdispersion im Anschwcmm.ycrfah.ren aufgebracht:On the paper side with a varnish, synthetic resin dispersion or glue paper-laminated aluminum foil is the following aqueous plastic dispersion in the Anschwcmm.ycrfah.ren applied:
a) 50°/oigc Dispersion eines Mischpolymerisates aus \'inylchlorida) 50 ° / o igc dispersion of a copolymer of \ 'inylchlorid
und Vinylacetat 62 (Gewichts-)Teileand vinyl acetate 62 parts (by weight)
50%igc Dispersion von Polyacrylsäureester 2 Teile50% igc dispersion of polyacrylic acid ester 2 parts
15°/oigcr Stärkeleim 20 TeUe15 ° / o IGCR starch 20 TeUe
Wasser 15 TeileWater 15 parts
hochdisperse Kieselsäure 1 Teilhighly disperse silica 1 part
Diese Dispersionsmischung wird in einer solchen Menge aufgebracht, daß eine Trockenfilmschicht von 3 bis 20 g/m2 entsteht.This dispersion mixture is applied in such an amount that a dry film layer of 3 to 20 g / m 2 is formed.
Die zweite, darübcrzulegende Lackschicht besteht aus:The second layer of varnish to be placed on top consists of:
b) Mischpolimerisat aus Vinylchlorid und Vinylacetat mit 10 bis 15 °/0 b) mixed polymers of vinyl chloride and vinyl acetate with 10 to 15 ° / 0
Acetatanteil 20 (Gewichts-)TeileAcetate content 20 parts (by weight)
Mischpolymerisat aus A'inylchlorid und Vinylacetat mit 30 bisCopolymer of a'inyl chloride and vinyl acetate with 30 to
50°/0 Acetatanteil 10 Teile50 ° / 0 acetate content 10 parts
Äthylacetat 50 TeileEthyl acetate 50 parts
Butylacetat 20 TeileButyl acetate 20 parts
Titandioxyd 5 bis 15 TeileTitanium dioxide 5 to 15 parts
Dieser zweite Lackauftrag soll in einer solchen Menge auf die erste Lackschicht gegeben werden, daß eine Trockcnfilmschicht von 3 bis 20 g/m2 entsteht. Auch dieser zweite thermoplastische Kunststoff-Film wird im Anschwcmmvcrfahrcn aufgebracht.This second application of lacquer should be applied to the first layer of lacquer in such an amount that a dry film layer of 3 to 20 g / m 2 is formed. This second thermoplastic plastic film is also applied using the precoating process.
Auf die Papicrscite einer mittels Lackes, Kunstharzdispersion oder Leimes papierkaschierten Aluminium-Folie wird folgende wäßrige Kunststoffdispersion im Anschwcmmvcrfahrcn aufgebracht:On the papicrscite of an aluminum foil laminated with paper using varnish, synthetic resin dispersion or glue the following aqueous plastic dispersion is applied in a precoating process:
a) 50%igc wäßrige Polyvinylacctat-a) 50% aqueous polyvinyl acetate
dispcrsion 80 (Gewichts-)Teiledispersion 80 parts (by weight)
30%igcr Dcxtrinleim 10 Teile30% dcxtrin glue 10 parts
Wasser 9 TeileWater 9 parts
hochdispersc Kieselsäure 1 Teilhighly dispersed silica 1 part
Diese Dispersionsmischung wird in einer solchen Menge aufgebracht, daß eine Trockenfilmschicht von 3 bis 20 g/m2 entsteht.This dispersion mixture is applied in such an amount that a dry film layer of 3 to 20 g / m 2 is formed.
Die zweite, darüberzulegende Lackschicht besteht beispielsweise aus:The second layer of lacquer to be overlaid exists, for example the end:
b) Polyvinylacetat 30 (Gewichts-)Teileb) polyvinyl acetate 30 parts (by weight)
Äthylacetat 34 TeileEthyl acetate 34 parts
Toluol 10 TeileToluene 10 parts
Butylacetat 10 TeileButyl acetate 10 parts
Butanol 10 TeileButanol 10 parts
Dibutylphthalat 6 TeileDibutyl phthalate 6 parts
Titandioxyd 5 bis 15 TeileTitanium dioxide 5 to 15 parts
Dieser zweite Lackauftrag soll in einer solchen MengeThis second coat of paint should be in such an amount
auf die erste Lackschicht gegeben werden, daß eine Trockenfilmschicht von 3 bis 20 g/m2 entsteht. Auch dieser zweite thermoplastische Kunststoff-Film wird im Anschwemmverfahren aufgebracht.be applied to the first layer of lacquer that a dry film layer of 3 to 20 g / m 2 is formed. This second thermoplastic plastic film is also applied using the precoating process.
Auf die Papierseite einer mittels Lackes, Kunstharzdispersion oder Leimes papierkaschierten Aluminium-Folie wird folgende wäßrige Kunststofflösung im Anschwemmverfahren aufgebracht:On the paper side of an aluminum foil laminated with paper using varnish, synthetic resin dispersion or glue the following aqueous plastic solution is applied using the precoat method:
a) 20°/0ige wäßrige Lösung von Polyvinylalkohol 79 (Gewichts-)Teilea) 20 ° / 0 aqueous solution of polyvinyl alcohol 79 (by weight) of
15°/oiger Stärkeleim 20 Teile15 ° / o sodium starch 20 parts
1^ hochdisperse Kieselsäure 1 Teil 1 ^ highly disperse silica 1 part
Diese wäßrige Kunststofflösung wird in einer solchen Menge aufgebracht, daß eine Trockenfilmschicht von bis 12 g/m2 entsteht.This aqueous plastic solution is applied in such an amount that a dry film layer of up to 12 g / m 2 is formed.
Die zweite, darüberzulegende Lackschicht besteht beispielsweise aus:The second layer of varnish to be overlaid consists, for example, of:
b) Mischpolymerisat aus Vinylchlorid, Vinylacetat und Maleinsäure
oder Acrylsäure oder Vinyl-b) Copolymer of vinyl chloride, vinyl acetate and maleic acid
or acrylic acid or vinyl
alkohol 20 (Gewichts-)Teilealcohol 20 parts (by weight)
Mischpolymerisat aus Vinylchlorid und Vinylacetat 10 TeileCopolymer of vinyl chloride and vinyl acetate 10 parts
■Methyläthylketon 30 Teile■ methyl ethyl ketone 30 parts
Methylisobutylketon 20 TeileMethyl isobutyl ketone 20 parts
Butylacetat 10 TeileButyl acetate 10 parts
Toluol 10 TeileToluene 10 parts
Titandioxyd 5 bis 15 TeileTitanium dioxide 5 to 15 parts
Dieser zweite Lackauftrag soll in einer solchen Menge auf die erste Lackschicht gegeben werden, daß eine Trockenfilmschicht von 3 bis 20 g/m2 entsteht. Auch dieser zweite thermoplastische Kunststoff-Film wird im Anschwemm verfahr en aufgebracht.This second application of lacquer should be applied to the first lacquer layer in such an amount that a dry film layer of 3 to 20 g / m 2 is formed. This second thermoplastic plastic film is also applied using the precoating method.
Claims (1)
Schweizerische Patentschrift Nr. 298 999;
Auszüge deutscher Patentanmeldungen, Vol. 8, S. 627: Sch 126774 IVd.Considered publications:
Swiss Patent No. 298 999;
Excerpts from German patent applications, Vol. 8, p. 627: Sch 126774 IVd.