DD209656A5

DD209656A5 - METHOD FOR THE COMBINED TREATMENT OF PIG SHELLS

Info

Publication number: DD209656A5
Application number: DD24990383A
Authority: DD
Inventors: Jozsef Bakan; Tamas Klinger; Eszter Nagy; Laszlo Devai; Pal Jani; Istvan Bieli; Terez Weiss
Original assignee: Pecsi Boergyar
Priority date: 1982-04-26
Filing date: 1983-04-15
Publication date: 1984-05-16
Also published as: YU83583A; HU187688B

Abstract

VERFAHREN ZUR KOMBINIERTEN GERBUNG VON SCHWEINSHAEUTEN, GEKENNZEICHNET DADURCH, DASS MAN DIE ZUR GERBUNG VORBEREITETE BLOESSE NACH DER BEHANDLUNG MIT DEM PICKEL MIT 2 BIS 4 VOL.-% KALIUMALUMINIUMSULFAT, BEZOGEN AUF DIE ROHHAUT, DANACH DURCH STUFENWEISE ZUGABE V. NATRIUMCARBONAT BEI ERHOEHUNG D. PH-WERTES BEHANDELT, D. MIT KALIUMALUMINIUMSULFAT BEHANDELTE HAUT M. WAEESSRIGER FORMALDEHYDLOESUNG IN AEHNLICHER MENGE GERBT, AM ENDE D. GERBUNG D. PH-WERT AUF 6,5 BIS 7,5 EINSTELLT, DANACH D. VORBEHANDELTE HAUT M. EINER CHROMBRUEHE, D. ZWECKMAESSIG EINE BASITAET VON 30 BIS 40 % U. EINE KONZENTRATION V. 120 BIS 200 G/L AUFWEIST, UNTER ANWENDG. EINER DICARBONSAEURE NACHGERBT U. GEWUENSCHTENFALLS D. WAEHREDER MECHANISCHEN VORGAENGE ERHALTENE ABFALLHAUT EINER WAESSRIG-PEROXYDISCHEN ODER SAUER-PEROXYDISCHEN BEHANDLUND UNTERWIRFT.PROCEDURE FOR THE COMBINED TREATMENT OF PIGSHAUT, CHARACTERIZED BY THE PREPARATION OF THE PREPARED BLOUSE AFTER TREATMENT WITH THE PICKLE OF 2 TO 4% VOLTAGE OF CALIUM ALUMINIUM SULPHATE, RELATED TO RAW SKIN, THEN BY STEP BY STEP INCREASE V. SODIUM CARBONATE ON EARLY EXTRACTION D. PH - TREATED D. CALIUM ALUMINIUM SULFATE TREATED SKIN M. THOROUGHLY FORMALDEHYDE SOLUTION STENNED IN SIMILAR AMOUNT, AT END D. TREATMENT D. PH VALUE SETTING TO 6.5-7.5, AFTER D. PREPARED SKIN M. OF CHROMBRUHE, D PERMANENTLY A BASITAET OF 30 TO 40% AND A CONCENTRATION V. 120 TO 200 G / L WILL APPLY, UNDER APPLICATION. A DICARBONE ACID AFFORDED AND DESIRED, D. THE WEAVE OF A WAESSRIG-PEROXYDIC OR OXYGEN-PEROXYDIC TREATMENT UNDER CONSTRUCTION, DUE TO THE MECHANICAL PROCESS.

Description

15 513 5515 513 55

24 9-9 0 3 324 9-9 0 3 3

Verfahren zur kombinierten Gerbung von SchweinshäutenMethod for the combined tanning of pig skins

Field of application of the invention:

Die Erfindung betrif££ein Verfahren zur kombinierten Gerbung von Schweinshäuten. , ' > . The invention relates to a method for the combined tanning of pigskins. , '>.

Characteristic of the known technical solutions:

Es ist bekannt, daß bei der Gerbung von Häuten, wie Schweins häuten, hauptsächlich die Chromgerbung angewandt wirdIt is known that in the tanning of hides such as pork skins, the chrome tanning is mainly used

Während der Chromgerbung wird die Blöße mit Säuren und ' Entquellungsmitteln (Pickeln) auf säuer eingestellt und danach wird mit basischem Chromsulfat gegerbt. Während der Chromgerbung wird die Haut geschmeidig sein, und es können starke, außerordentlich dauerhafte, gegen kaltes und warmes Wasser beständige Fertigleder hergestellt werden. During chrome tanning, the puff is acidified with acids and de-scaling agents (pimples) and then tanned with basic chromium sulfate. During the chrome tanning, the skin will be supple, and strong, extremely durable finished leather resistant to cold and warm water can be produced.

Obwohl die Chromgerbung viele Vorteile aufweist, ist ihre Verwendung mit gewissen Nachteilen verbunden. Infolge dieser Nachteile müssen zum Vernichten der Abwasser und derAlthough chrome tanning has many advantages, its use has certain disadvantages. As a result of these disadvantages have to destroy the sewage and the

Schmutzstoffe aufwendige Verfahren angewandt werden. Der Wirkstoff der Chromgerbung, d.h. der Gr ^ -ion-Gehalt der angewandten Lohen, darf in den Abwässern nur beschränkt enthalten sein, da der zugelassene Chromgehalt, je nach den verschiedenen Vorschriften,' nur 1 bis 10 mg/1 betragen darf» Ähnliche;;,Probleme treten bei der Vernichtung der anderen Abfälle_s z.B. der Spaltabfälle auf, die nach der Chromgerbung der Häute während der mechanischen Vorgänge entstehen. Die während der mechanischen Vorgänge entstandenen Abfälle besitzen einen relativ großen Gehalt an nützlichem Eiweiß, das jedoch infolge des Chromgehaltes industriell nicht genutzt werden kann. Der bei der Chromgerbung auftretende Abfall ist außerordentlich groß, bezogenContaminants consuming procedures are applied. The active substance of chrome tanning, that is to say the green oil content of the lozenges applied, may not be present in the effluent only to a limited extent since the chromium content authorized may be 'only 1 to 10 mg / 1, depending on the various requirements';;, Problems occur in the destruction of other waste _s, for example, the gap wastes that arise after the chrome tanning of the skins during the mechanical processes. The wastes generated during the mechanical processes have a relatively high content of useful protein, which, however, can not be used industrially due to the chromium content. The occurring in chrome tanning waste is extremely large, based

auf 1 t Schweinsrohhaut entstehen 1 rar benutzte Lohe mit einem Cr₂O-.--Gehalt von 1 bis 8 g/l, sowie 150 bis 200 kg Hautabfälle.on 1 t pig skin arise 1 scar used Lohe with a Cr ₂ O.-content of 1 to 8 g / l, and 150 to 200 kg of skin waste.

Es wurden viele Versuche zur Beseitigung der bekannten Machteile der Chromgerbung bzw» zur Vorgerbung ohne Chromgerbung, sowie zur Entchromung der chromhaltigen Abfälle und für deren weitere Nutzung durchgeführt. Pur die Vorgerbung können Aluminiumsulfat, pflanzliche Gerbmittel(Mimose, Kastanienbaumextrakt, usw.), Alaungerbung oder Formaldehydger-bimg angewandt werden« Diese Verfahren werden aber - im Vergleich, zu der Chromgerbung - in der Industrie wegen der qualitativen lachteile der Fertigleder nur sehr selten angewendet. Ein weiteres Problem ergibt sich aus der Vernichtung der chromhaltigen Abfälle, was mit einem großen Aufwand verbunden ist»There have been many attempts to eliminate the known Mach parts of chrome tanning or »Vorgerbung without chrome tanning, as well as for chromium-containing waste chromium waste and their further use. For example, aluminum sulfate, vegetable tanning agents (mimosa, chestnut tree extract, etc.), alaungerbung or formaldehyde fermentation can be used for the pretreatment. "However, in comparison with chrome tanning, these processes are rarely used in industry because of the qualitative disadvantages of finished leather , Another problem arises from the destruction of waste containing chromium, which is very costly »

Ziel der Erfindung ist es_s die Mängel des Standes der Technik zu beseitigen»The aim of the invention is to eliminate _s the shortcomings of the prior art "

Explanation of the essence of the invention:

Es wurde gefunden, daß durch eine Aluminiumformaidehydgerbung von Schweinshäuten nach der mechanischen Bearbeitung im gesamten Querschnitt der Haut eine gute Gerbmittelbindung erreicht werden kann. Außerdem entsprechen die Eigenschaften der so erhaltenen Fertigleder den Eigenschaften der durch Chromgerbung hergestellten Leder· Ferner kann der nach der Vorgerbung während der mechanischen Bearbeitung entstandene Abfall in eine solche Form gebracht werden, daß er in der Landwirtschaft als Roheiweiß ausgenutzt werden kann.It has been found that a good tanning agent binding can be achieved by aluminum formaldehyde tanning of pig skins after mechanical working in the entire cross-section of the skin. In addition, the properties of the finished leathers thus obtained correspond to the properties of the leathers prepared by chrome tanning. Further, the post-tanning waste produced during the mechanical working can be shaped such that it can be utilized in agriculture as raw protein.

Das Wesen des jsrfindungsgemäßen Verfahrens zur kombinierten Gerbung von Schweinshäuten besteht darin, daß man die zur Gerbung vorbereitete Blöße nach der Behandlung mit dem Pickel mit 2 bis 4 Vol.-% Kaliumaluminiumsulfat, bezogen auf die Rohhaut j danach durch stufenweise Zugabe von Natriumcarbonat mit Erhöhung des pH-Wertes behandelt, sodann die mit Kaliumaluminiumsulfat behandelte Haut mit einer wäßrigen Formaldehydlösung in ähnlicher Menge gerbt und am Ende der Gerbung den pH-Wert auf 6,5 bis 7,5 einstellt. Sodann wird die vorbehandelte Haut mit einer Chrombrühe, die zweckmäßig eine Basizität von 30 bis 40 % und eine Konzentration von 120 bis 200 g/l aufweist, unter Anwendung einer Dicarbonsäure nachgegerbt und gewünsentenfalls die während der mechanischen Bearbeitung erhaltene Abfallhaut einer wäßrig-peroxydischen oder sauer-peroxydischen Behandlung unterwirft.The essence of the method according to the invention for the combined tanning of pigskins consists in treating the teas prepared for tanning with 2 to 4% by volume of potassium aluminum sulphate, based on the rawhide, by stepwise addition of sodium carbonate with an increase of Then the potassium aluminum sulfate treated skin is tanned with an aqueous solution of formaldehyde in a similar amount and at the end of the tanning, the pH is adjusted to 6.5 to 7.5. Then, the pretreated skin is retanned with a chromium broth having a basicity of from 30 to 40 % and a concentration of from 120 to 200 g / l using a dicarboxylic acid and, if desired, the greasy skin obtained during the mechanical working of an aqueous-peroxidic or acidic subject to peroxidic treatment.

Vor der Behandlung mit Kaliumaluminiumsulfat wird die Haut vorzugsweise mit elektrolytbeständigem, anionischem, lederschmierendem Licker und einem Dispergiermittel behandelt. Das lederschmierende Licker kann eine in der Lederindustrie gebräuchliche, bei einem pH-Wert von 2 bis 4 stabile anionische Lederschmiere sein. Solche Lederschmie-Prior to treatment with potassium aluminum sulfate, the skin is preferably treated with electrolyte-resistant, anionic, leather-lubricating licker and a dispersant. The leather-lubricating licker may be an anionic leather smear used in the leather industry and stable at a pH of 2 to 4. Such leather

ren sind z.B. Sultosol C (Produkt der Firma Busetti) oder Salco AL (Produkt der Firma Salara Oil). Als Dispergiermittel können Fettsäuresulfonate, sulfonierte Fettsäurederivate, wie Tergolix A (Produkt der Firma Sandoz) oder ein ethoxyliertes oberflächenaktives Gemisch, wie Lutensol AP-10 (Produkt der Firma BASF) bzw. Lutensol AP-6 verwendet v/erden. Der AlgO-j-Gehalt des verwendeten Kaliumaluminiumsulfats (Alauns) beträgt 10,8 Vol.-%, d.h. bei der Verwendung von 3 Vol.-% Kaliumaluminiumsulfat, bezogen auf die Rohhaut, beträgt der A^O^-Gehalt 32,4 Vol.-SS. Die Haut wird mit dem Kaliumaluminiumsulfat 20 bis 40 Minuten lang behandelt. Die stufenweise Alkalisierung der Haut erfolgt mit 1,5 bis 2,0 VoI,-^ Natriumcarbonatlösung. Die Behandlung mit Formaldehyd wird vorzugsweise in zwei Schritten durchgeführt, danach wird der vorgeschriebene pH-Wert der Haut mit Efatriumbicarbonat eingestellt.They are e.g. Sultosol C (product of the company Busetti) or Salco AL (product of the company Salara Oil). As dispersants fatty acid sulfonates, sulfonated fatty acid derivatives such as Tergolix A (product of the company Sandoz) or an ethoxylated surface-active mixture, such as Lutensol AP-10 (product of BASF) or Lutensol AP-6 can be used. The AlgO-j content of the potassium aluminum sulfate (alum) used is 10.8% by volume, i. when using 3% by volume of potassium aluminum sulfate, based on the rawhide, the A ^ O ^ content is 32.4% by volume. The skin is treated with the potassium aluminum sulfate for 20 to 40 minutes. The stepwise alkalization of the skin is carried out with 1.5 to 2.0% solution of sodium carbonate. The treatment with formaldehyde is preferably carried out in two steps, after which the prescribed pH of the skin is adjusted with efatrium bicarbonate.

Die Erfindung beruht auf der Erkenntnis, daß bei der kombinierten Gerbung der Schweinshäute die gleichen Vorteile wie bei der Chromgerbung erreicht werden können, wenn die vorgeschriebenen Behandlungen durchgeführt werden. Die Bindung der Gerbmittel wird erheblich verbessert, da die Bindung des Kaliumaluminiumsulfats während der Gerbung durch die Erhöhung der Basizität erreicht werden kann. Während der danach erfolgenden Formaldehydbehandlung erfolgt die Aldehydbindung bei einem optimalen pH-Wert, und durch die Erhöhung des pH-Wertes wird die Haut stufenweise und in vollem Maße durchgegerbt. Wie Untersuchungen gezeigt haben, beträgt der AlgOo-Gehalt der auegenutzten Lohe 40 bis 60 mg/1, d.h. die gesamte Aluminiumausnutzung beträgt 95 bis 97 %· Der Aldehydgehalt der benutzten Lohe beträgt 2,1 bis 2,6 g/l, dies entspricht einer Aldehydbindung von 52 bis 60 %. Die vorgegerbten Schweinshäute sind bei 80 ⁰C kochfest, bei 85 ⁰C variiert die Kochfestigkeit zwischen 85 und 92 %, die Häute werden jedoch nicht härter sein.The invention is based on the recognition that in the combined tanning of the pigskins, the same advantages as in chrome tanning can be achieved when the prescribed treatments are carried out. The binding of the tanning agents is considerably improved because the binding of the potassium aluminum sulfate during tanning can be achieved by increasing the basicity. During the subsequent formaldehyde treatment, the aldehyde binding occurs at an optimum pH, and by increasing the pH, the skin is gradually and fully tanned. The results show that the AlgOo content of the used Lohe is 40 to 60 mg / l, ie the total aluminum utilization is 95 to 97 % · The aldehyde content of the used Lohe is 2.1 to 2.6 g / l, which corresponds to one Aldehyde binding from 52 to 60 %. The Pretanned Pig skins are washed at 80 ⁰ C, at 85 ⁰ C, the cooking resistance varies between 85 and 92%, the skins are not to be harder.

Wenn die vorgegerbte Haut mit Chromlohe nachgegerbt wird, entsprechen die Eigenschaften des erhaltenen Fertigleders in ihrer Qualität der von chromgegerbtem Leder.When the pre-tanned skin is retanned with Chromlohe, the properties of the finished leather obtained are similar in quality to that of chrome-tanned leather.

Die Vorteile des erfindungsgemäßen Verfahrens sind zusammengefaßt die folgenden:The advantages of the method according to the invention are summarized the following:

- Die Verschmutzung der Umwelt kann erheblich vermindert werden, da sich bei der Vorgerbung chromfreies Abwasser bildet. Die Menge des sich bei den nachchromierten Häuten gebildeten Wassers beträgt nur 20 % der gewöhnlich angewandten Lohen, da die Konzentration der Cr -ionen nur auf das FaIζengewicht eingestellt werden muß.- The pollution of the environment can be significantly reduced, as formed in the pre-tanning chrome-free wastewater. The amount of water formed in the post-churned hides is only 20 % of the commonly used powders, since the concentration of the Cr ions must be adjusted only to the solid weight.

- Der Chromaufwand beträgt 1/4 der Menge des Chromaufwandes der gewöhnlichen Chromgerbung auch in dem Fall, daß die gesamte Produktion nachchromiert wird.- The chrome cost is 1/4 of the amount of chromium of the ordinary chrome tanning even in the case that the entire production is nachchromiert.

- Krach der Vorgerbung entstehen 15 bis 20 % chromfreie Falzenschnitzel und Abfälle, bezogen auf das Volumen der Rohhaut, diese Können benutzbar gemacht oder ohne Probleme vernichtet werden.- Crashing of the pretanning results in 15 to 20 % chromium-free fold chips and waste, based on the volume of the raw hide, these skills can be made usable or destroyed without problems.

- Zur Aluminiumformaidehidgerbung können die Maschinen und Vorrichtungen der normalen Lederherstellung verwendet werden, die gesamte Produktion kann je nach den Marktanforderungen wirtschaftlich geändert werden.For the aluminum mold aid tanning the machines and devices of the normal leather production can be used, the whole production can be changed economically according to the market requirements.

Embodiments;

Das erfindungsgemäße Verfahren wird durch die nachfolgenden Beispiele näher erläutert.The process of the invention is further illustrated by the following examples.

example 1

Aluminiumformaldehydgerbung von SchweinehäutenAluminum formaldehyde tanning of pig skins

Die Rohhaut wird wie gewöhnlich geäschert und entfettet, danach werden nach der Beizung die folgenden Operationen bezogen auf das Volumen der Rohhaut - durchgeführt:The rawhide is, as usual, limed and degreased, after which the following operations on the volume of the rawhide are carried out after staining:

1. Waschen mit Wasser mit einer Temperatur von 30 ⁰C Die Brühe wird entfernt1. Washing with water at a temperature of 30 ^° C. The broth is removed

Temperatur von 30 ⁰C 15 Minuten DrehungTemperature of 30 ⁰ C 15 minutes rotation

2. 30 % Wasser mit einer Temperatur von 30 ⁰C .2. 30 % water with a temperature of 30 ⁰ C.

4· % Natriumchlorid (technisches) 5 Minuten Drehung4 % sodium chloride (technical) 5 minutes rotation

3. 1j2 % Ameisensäure 90 Minuten Drehung Die Brühe wird entfernt3. 1 % 2 % formic acid 90 minutes rotation The broth is removed

4. 200 % Wasser mit einer Temperatur von 30 ⁰C 8 % Natriumchlorid (technisches) 1 Minute Drehung4. 200 % water with a temperature of 30 ⁰ C 8 % sodium chloride (technical) 1 minute rotation

5. 1 % Sultosol C5. 1 % Sultosol C

0,5 % Tergolix A₅ 30 Minuten Drehung0.5% Tergolix A ₅ 30 minutes of rotation

6. 3 % Kaliumaluminiumsulfat ' 30 Minuten Drehung6. 3 % potassium aluminum sulfate '30 minutes rotation

7. 1,5 % Natriumformiat 30 Minuten Drehung7. 1.5 % sodium formate for 30 minutes

8. 0,5 % Natriumcarbonat 30 Minuten Drehung8. 0.5 % sodium carbonate 30 minutes rotation

9. 0,5 % Natriumcarbonat 30 Minuten Drehung9. 0.5 % sodium carbonate 30 minutes rotation

10. 0,8 % Natriumcarbonat 60 Minuten Drehung10. 0.8 % sodium carbonate 60 minutes rotation

11. 1 % Formaldehyd (technisches,11. 1 % formaldehyde (technical,

40 ^Siges) 10 Minuten Drehung40 ^ Siges) 10 minutes rotation

12. 2 % Formaldehyd 50 Minuten Drehung 13· 0,5 % Natriumbicarbonat 20 Minuten Drehung12. 2% formaldehyde 50 minutes of rotation 13 x 0.5 % sodium bicarbonate 20 minutes of rotation

14. 0,5 % Matriumbicarbonat 30 Minuten Drehung14. 0.5 % Matrium bicarbonate 30 minutes rotation

15. 0,3 % Natriumbicarbonat 60 Minuten Drehung15. 0.3 % sodium bicarbonate 60 minutes rotation

Die Haut wird in der Lohe 4 bis 5 Stunden lang stehengelassen, der pH-Wert der Lohe und der Haut wird am Ende der Gerbung auf 6,5 bis 7,5 eingestellt.The skin is allowed to stand in the Lohe for 4 to 5 hours, the pH of the Lohe and the skin is adjusted to 6.5 to 7.5 at the end of the tanning.

Hach der Gerbung werden die mechanischen Operationen durchgeführt. Die Häute werden 1 Stunde lang gealtert, danach werden die Häute gespaltet, gefalzt bzw. rundgezwickt, entsprechend den Fertigprodukten. Die erhaltenen Schweinsleder sind bei 80 ⁰C kochfest, ihre mechanische Bearbeitbarkeit entspricht den Forderungen, und sie können gelagert werden.After the tanning the mechanical operations are carried out. The skins are aged for 1 hour, after which the skins are split, folded or zwgezwickt, according to the finished products. The pigskin obtained are resistant to boiling at 80 ⁰ C, their mechanical workability meets the requirements, and they can be stored.

Example 2

Nachchromierung von vorgegerbten HäutenNachchromierung of pre-tanned hides

Die gemäß Beispiel 1 vorgegerbten Schweinsblankhäute werden den folgenden Operationen, bezogen auf 0,7 bis 0,8 mm gefalztes Gewicht, unterworfen (die Reagenzien werden auf das gefalzte Volumen zugegeben):The pretanned pork skins according to Example 1 are subjected to the following operations, based on 0.7 to 0.8 mm folded weight (the reagents are added to the folded volume):

1. 100 % Wasser mit .einer Temperatur von 20 ⁰C 0,9 % Schwefelsäure (technisches) 15 Minuten Drehung1. 100 % water with .A temperature of 20 ⁰ C 0.9 % sulfuric acid (technical) 15 minutes of rotation

UJ .JYY .J

2. 0,9 ^ Schwefelsäure (technisches) 60 Minuten Drehung2. 0.9 ^ sulfuric acid (technical) 60 minutes rotation

3. 1 $ Natriuffiformiat3. 1 $ Natriuffiformiat

4. 6 % Chrombrühe (Basizität Cr₂O₃-Gehalt 180 g/l)4. 6 % chromium broth (basicity Cr ₂ O ₃ content 180 g / l)

5. 5 % Chrombrühe (Zusammensetzung wie oben)5. 5 % chromium broth (composition as above)

6. 1 % Adipinsäurenatriumsalz6. 1 % adipic acid sodium salt

7. 150 % Wasser mit einer Temperatur von 60 ⁰C7. 150% water with a temperature of 60 ⁰ C.

8. 0,2 % Natriumcarbonat 9 · 0,3% Natriumcarbonat 10. 0,3 % Natriumcarbonat8. 0.2% sodium carbonate 9 x 0.3% sodium carbonate 10. 0.3 % sodium carbonate

20 Minuten Drehung20 minutes of rotation

60 Minuten Drehung60 minutes of rotation

30 Minuten Drehung 10 Minuten Drehung 10 Minut en Drehung 90 Minuten Drehung30 minutes of rotation 10 minutes of rotation 10 minutes of rotation 90 minutes of rotation

Die Brühe wird abgelassen. Die Kochfestigkeit der erhaltenen Haut beträgt bei 100 ⁰C 100 %. The broth is drained. The cooking strength of the skin obtained is 100 % at 100 ⁰ C.

Die während der Nachbehandlung erhaltene Chrombrühe weist einen Cr^O.-Gehalt von 0,2 bis 1,3 g/l auf, dies entspricht einer Chromaufnahme von 80 bis 97 %.The chromium broth obtained during the aftertreatment has a Cr.sub.2 O content of 0.2 to 1.3 g / l, which corresponds to a chromium uptake of 80 to 97%.

Durch die Naehchromierung können verschiedene Schweinsleder-Fertigprodukte mit chromgegerbten Eigenschaften - einbegriffen die Schweinsspalte, welche nach der Vorgerbung während der mechanischen Operationen entstehen - hergestellt werden. Nach der Nachbehandlung werden die Häute in Abhängigkeit von den herzustellenden Fertigprodukten nachgegerbt, gefettet, gefärbt bzw. ausgerüstet.Naochromatization makes it possible to produce various pigskin finished products with chrome-tanned properties, including the pig's paw, which are produced after pre-tanning during mechanical operations. After the aftertreatment, the hides are retanned, greased, dyed or finished depending on the finished products to be produced.

Beispiel ? ^:; ' : : ;:; . . .' "" ' -'.'..,.'' Example? ^:; '::;:; , ,. '""' - .., '''.'.

Behandlung der Abfälle, die bei dem Umschneiden entstehen (Spalte und Palzenschnitzel)Treatment of waste generated during cutting (column and chipboard)

Zu den während der mechanischen Operationen entstandenen Abfällen werden die folgenden Reagenzien, bezogen auf das Volumen der Abfälle, zugegeben, und die folgenden Operationen werden durchgeführt:To the wastes generated during the mechanical operations, the following reagents are added based on the volume of the wastes, and the following operations are performed:

150 % Wasser bei 100 ⁰C + 1 Stunde Drehung150 % water at 100 ^° C + 1 hour of rotation

10 % Wasserstoffperoxyd (technisches, 40 &Lges) 3 Stunden Drehung10 % hydrogen peroxide (technical, 40 & Lges) 3 hours of rotation

Die zerkleinerten Abfälle lösen sich bei der Behandlung auf, danach wird unter Stehen ein niederschlag der hauptsächlich Aluminium enthält, ausgefallen.The shredded waste dissolves during treatment, after which a precipitate containing mainly aluminum precipitates.

Das obige Verfahren wird in saurem Medium folgenderweise durchgeführt:The above procedure is carried out in an acidic medium as follows:

150 $5 Wasser mit einer Temperatur von 60 ⁰C 15 % Schwefelsäure (technisches)150 $ 5 water with a temperature of 60 ⁰ C 15 % sulfuric acid (technical)

10 % Wasserstoffperoxyd (technisches) 1 Stunde Drehung +10 % Wasserstoffperoxyd (technisches) 5 Stunden Drehung +15 % Hatriumhydroxyd (festes) 30 Minuten Drehung10 % hydrogen peroxide (technical) 1 hour of rotation +10% hydrogen peroxide (technical) 5 hours of rotation +15 % of sodium hydroxide (solid) 30 minutes of rotation

Der pH-Wert der Lösung wird am Ende neutral eingestellt. Die erhaltene Lösung enthält Kollagen und die Produkte der saueren Hydrolyse und kann zur Fütterung von Tieren (Eiweißersatz) benutzt werden.The pH of the solution is finally adjusted to neutral. The resulting solution contains collagen and the products of acid hydrolysis and can be used to feed animals (protein substitute).

Claims

/ 4y ^ UJ s -ίο. Invention entitled;

1. A method for the combined tanning of pigskins, characterized in that the tanning prepared for the tanning after treatment with the pimple with 2 to 4 ¹ VoL-JS potassium aluminum sulfate, based on the rawhide, then by gradual addition of sodium carbonate behaiidelt treated Treated skin with aqueous solution of Pormaldehydlösung, at the end of the tanning, the pH to 6.5 to 7.5 sets, then the pretreated skin with a chrome broth, the expedient basicity of 30 to 40 % and a concentration of 120 to 200 g / retanning with the use of a dicarboxylic acid and, if desired, subjecting the refuse skin obtained during the mechanical processes to an aqueous-peroxidic or acid-peroxidic treatment.

2. The method according to item 1, characterized in that the skin is treated before the aluminum treatment with an electrolyte-resistant, anionic, leather-lubricating Licker and a dispersant.

3.. Method according to item 1, characterized in that

as potassium aluminum sulfate a reagent with about 10% by volume AlgO content is used ·

4 * Process according to item 1 or 3 », characterized in that the rawhide is treated with potassium aluminum sulphate for 20 to 40 minutes.

5. The method according to any one of items 1 to 4 », characterized in that the skin is gradually alkalized after the aluminum treatment with 1.5.bis 2.0 vol .- % sodium carbonate.

-y

6. The method according to item 1, characterized in that is used as the aqueous formaldehyde about 40% technical grade formaldehyde.

7. The method according to item 1, characterized in that the formaldehyde-treated skin is gradually neutralized with Katriumbiearbonat.

8. The method according to item 1, characterized in that the waste skins, based on their volume, with 150 vol .- $ water at the boiling point, then treated with 10 vol .- # hydrogen peroxide or in the presence of sulfuric acid with hydrogen peroxide at about 60 ⁰ C. whereupon the pH of the resulting solution is adjusted to neutral.