CN201106735Y - 无溶剂环氧涂料补口的三层聚乙烯防腐管 - Google Patents

无溶剂环氧涂料补口的三层聚乙烯防腐管 Download PDF

Info

Publication number
CN201106735Y
CN201106735Y CNU2007201905660U CN200720190566U CN201106735Y CN 201106735 Y CN201106735 Y CN 201106735Y CN U2007201905660 U CNU2007201905660 U CN U2007201905660U CN 200720190566 U CN200720190566 U CN 200720190566U CN 201106735 Y CN201106735 Y CN 201106735Y
Authority
CN
China
Prior art keywords
layer
solvent
steel pipe
coating
free epoxy
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Lifetime
Application number
CNU2007201905660U
Other languages
English (en)
Inventor
解蓓蓓
徐忠萍
邵怀启
韩文礼
张其滨
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
China National Petroleum Corp
CNPC Engineering Technology Research Institute Co Ltd
Original Assignee
China National Petroleum Corp
CNPC Engineering Technology Research Institute Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by China National Petroleum Corp, CNPC Engineering Technology Research Institute Co Ltd filed Critical China National Petroleum Corp
Priority to CNU2007201905660U priority Critical patent/CN201106735Y/zh
Application granted granted Critical
Publication of CN201106735Y publication Critical patent/CN201106735Y/zh
Anticipated expiration legal-status Critical
Expired - Lifetime legal-status Critical Current

Abstract

本实用新型涉及一种无溶剂环氧涂料补口的三层聚乙烯防腐管，由钢管(1)、环氧粉末涂层(2)、胶粘剂层(3)、聚乙烯层(4)、无溶剂环氧涂层(5)、热收缩带层(6)构成，其特征在于：环氧粉末涂层(2)、胶粘剂层(3)、聚乙烯层(4)顺次涂覆在钢管(1)的外表面，无溶剂环氧涂层(5)涂覆在钢管(1)预留焊接段(7)焊接处钢管(8)表面，热收缩带层(6)包覆在无溶剂环氧涂层(5)外，在现场管线补口施工中采用无溶剂环氧涂层补口，无溶剂环氧涂层实干后与热收缩带的粘结力高，使补口处具有优良的密封性、防水性、防化学侵蚀性能，现场施工方便，保证补口质量，可用于输送油、气的防腐管线。

Description

无溶剂环氧涂料补口的三层聚乙烯防腐管
技术领域
本实用新型涉及一种无溶剂环氧涂料补口的三层聚乙烯防腐管，可用于输送油、气的防腐管线。
背景技术
目前三层聚乙烯防腐管的补口底漆的主要作用是提高热收缩带的抗阴极剥离，其防腐蚀功能并不突出；而且底漆和热收缩带配套施工要求苛刻，烘烤粘结质量难以稳定，结果是收缩带一旦渗漏进水，钢管就没有任何屏障。而且采用的热收缩带的环氧底漆要求在涂刷底漆表干状态下包覆热收缩带，主要是目前的环氧底漆是基于表干状态下的反应活性与熔融状态下的热收缩带上的热熔胶发生反应，达到融合粘结的效果；而在实干后就不能与热熔胶产生有效的融合粘结，造成不合格的补口。
实用新型内容
本实用新型的目的是提供一种无溶剂环氧涂料补口的三层聚乙烯防腐管，无溶剂环氧涂层实干后与热收缩带的粘结力高，使补口处具有优良的密封性、防水性、防化学侵蚀性能，现场施工方便，保证补口质量。
本实用新型的所述的一种无溶剂环氧涂料补口的三层聚乙烯防腐管，由钢管1、环氧粉末涂层2、胶粘剂层3、聚乙烯层4、无溶剂环氧涂层5、热收缩带层6构成，环氧粉末涂层2、胶粘剂层3、聚乙烯层4顺次涂覆在钢管1的外表面，无溶剂环氧涂层5涂覆在钢管1预留焊接段7焊接处钢管8表面，热收缩带层6包覆在无溶剂环氧涂层5外。
其中钢管1长度8～24m、管外径273～1219mm、壁厚5～22mm，预留焊接段7两端各长150～200mm，环氧粉末涂层2的厚度为0.12～0.4mm、胶粘剂层3的厚度为0.17～0.4mm、聚乙烯层4的厚度为1.8～4.0mm，无溶剂环氧涂层5的厚度为0.15～0.25mm，热收缩带层6的厚度为2～4mm，热收缩带层6与聚乙烯层4的搭接长度为100～300mm。
较优的无溶剂环氧涂料补口的三层聚乙烯防腐管，其特征是钢管1长度12m、管外径1219mm、壁厚22mm，预留焊接段7两端各长150mm，环氧粉末涂层2的厚度为0.2mm、胶粘剂层3的厚度为0.23mm、聚乙烯层4的厚度为3.7mm，无溶剂环氧涂层5的厚度为0.2mm，热收缩带层6的厚度为2.5mm，热收缩带层6与聚乙烯层4的搭接长度为150mm。
本实用新型的无溶剂环氧涂料补口的三层聚乙烯防腐管制造过程如下：将钢管1的外表面喷砂除锈，预留出预留焊接段7，在钢管1的外表面涂覆环氧粉末涂层2、胶粘剂层3和聚乙烯层4，在现场管线连接施工时，将两根无溶剂环氧涂层补口的三层聚乙烯防腐管两端的预留焊接段连接焊接好后，然后进行补口施工。将焊接处钢管8表面的温度加热到40～50℃，对其进行全面喷砂除锈，使钢表面的处理等级达到Sa2.5级，然后使用空气吹扫的方法清除钢管表面的污物。将无溶剂环氧涂料均匀的涂刷在焊接处钢管8表面，使无溶剂环氧涂层5厚度达到0.2mm，将无溶剂环氧涂层5加热到70±5℃，加热10min后进行测厚和电火花检漏，确保达到要求厚度并且没有漏点后，安装热收缩带6。
本实用新型与现有技术相比的有益效果：
1、无溶剂环氧涂层补口的三层聚乙烯防腐管，生产工艺简单、现场补口施工方便。
2、采用无溶剂环氧涂层补口，无溶剂环氧涂层实干后与热收缩带的粘结力高，使补口处具有优良的密封性、防水性、防化学侵蚀性能，现场施工方便，保证补口质量，可用于输送油、气的防腐管线。
附图说明
图1是无溶剂环氧涂层补口的三层聚乙烯防腐管的纵向剖视图。图中：1-钢管；2-环氧粉末涂层；3-胶粘剂层；4-聚乙烯层；5-无溶剂环氧涂层；6-热收缩带层；7-预留焊接段；8-焊接处钢管。
具体实施方式
无溶剂环氧涂层补口的三层聚乙烯防腐管，钢管1长12m，管外径1219mm、壁厚22mm，环氧粉末涂层2的厚度为0.2mm、胶粘剂层3的厚度为0.23mm、聚乙烯层4的厚度为3.7mm，预留焊接段7两端各长150mm，在现场管线连接施工时，将两根无溶剂环氧涂层补口的三层聚乙烯防腐管两端的预留焊接段连接焊接好后，然后进行补口施工。将钢管焊接处8表面的温度加热到40～50℃，对其进行全面喷砂除锈，使钢表面的处理等级达到Sa2.5级，然后使用空气吹扫的方法清除钢管表面的污物。将无溶剂环氧涂料均匀的涂刷在钢管焊接处8表面，使无溶剂环氧涂层5厚度达到0.2mm，将无溶剂环氧涂层5加热到70±5℃，加热10min后进行测厚和电火花检漏，确保达到要求厚度并且没有漏点后，安装热收缩带6。试验结果表明，无溶剂环氧涂层与热收缩带的粘结力强，剥离强度达到了80N/cm以上，补口处有优良的密封性、防水性、防化学侵蚀性能。

Claims (2)

1、一种无溶剂环氧涂料补口的三层聚乙烯防腐管，由钢管(1)、环氧粉末涂层(2)、胶粘剂层(3)、聚乙烯层(4)、无溶剂环氧涂层(5)、热收缩带层(6)构成，其特征在于：环氧粉末涂层(2)、胶粘剂层(3)、聚乙烯层(4)顺次涂覆在钢管(1)的外表面，无溶剂环氧涂层(5)涂覆在钢管(1)预留焊接段(7)焊接处钢管(8)表面，热收缩带层(6)包覆在无溶剂环氧涂层(5)外。
2、根据权利要求1所述的无溶剂环氧涂料补口的三层聚乙烯防腐管，其特征在于：钢管(1)长度12m、管外径1219mm、壁厚22mm，预留焊接段(7)两端各长150mm，环氧粉末涂层(2)的厚度为0.2mm、胶粘剂层(3)的厚度为0.23mm、聚乙烯层(4)的厚度为3.7mm，无溶剂环氧涂层(5)的厚度为0.2mm，热收缩带层(6)的厚度为2.5mm，热收缩带层(6)与聚乙烯层(4)的搭接长度为150mm。
CNU2007201905660U 2007-12-04 2007-12-04 无溶剂环氧涂料补口的三层聚乙烯防腐管 Expired - Lifetime CN201106735Y (zh)