CN102786232A - 一种多介质陶瓷低辐射镀膜玻璃 - Google Patents
一种多介质陶瓷低辐射镀膜玻璃 Download PDFInfo
- Publication number
- CN102786232A CN102786232A CN2012103242747A CN201210324274A CN102786232A CN 102786232 A CN102786232 A CN 102786232A CN 2012103242747 A CN2012103242747 A CN 2012103242747A CN 201210324274 A CN201210324274 A CN 201210324274A CN 102786232 A CN102786232 A CN 102786232A
- Authority
- CN
- China
- Prior art keywords
- zinc oxide
- eradiation
- coated glass
- layer
- thickness
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种多介质陶瓷低辐射镀膜玻璃，其在玻璃原片的表面从下至上依次设置氧化钛层、氧化锌铝陶瓷层Ⅰ、银膜层、氧化锌铝陶瓷层Ⅱ、氧化锌铝陶瓷层Ⅲ和氧化锡层。本发明提供的多介质陶瓷低辐射镀膜玻璃，与现有技术相比具有以下优点：由于各玻璃膜层采用独特的排列顺序，更重要的是采用多层氧化锌铝陶瓷材料作为阻挡层保护银层，且每层氧化锌铝陶瓷材料分别在不同的条件下制作而成，从而具有耐磨、耐酸碱性，高可见光透射率，隔热，低辐射率，使用寿命长等优点。
Description
技术领域
本发明涉及玻璃领域，尤其涉及一种多介质陶瓷低辐射镀膜玻璃。
背景技术
目前，作为建筑用节能玻璃，低辐射中空玻璃已被广泛使用。但目前高透产品已经跟不上建筑镀膜的要求，特别是热学性能要求。其中影响玻璃热学性能的主要是镀膜玻璃的辐射率。由于现今的环境越来越恶劣，大气及雨水有些带酸性，减少了玻璃的使用寿命。
发明内容
发明目的：本发明的目的是为了解决现有技术的不足，提供一种耐磨、耐酸碱性的多介质陶瓷低辐射镀膜玻璃。
技术方案：为了实现以上目的，本发明所述的一种在玻璃原片的表面从下至上依次设置氧化钛层、氧化锌铝陶瓷层Ⅰ、银膜层、氧化锌铝陶瓷层Ⅱ、氧化锌铝陶瓷层Ⅲ和氧化锡层。
作为优选，所述的氧化钛层的厚度为10～20nm；氧化锌铝层Ⅰ的厚度为5～12nm；银膜层的厚度为10～16nm；氧化锌铝层Ⅱ的厚度为4～8nm；氧化锌铝层Ⅲ的厚度为6～12nm；氧化锡层的厚度为25～38nm。
作为进一步优选，所述玻璃原片的厚度为4mm、5mm、6mm、8mm、10mm或12mm。
有益效果：本发明提供的多介质陶瓷低辐射镀膜玻璃，与现有技术相比具有以下优点：由于各玻璃膜层采用独特的排列顺序，更重要的是采用多层氧化锌铝陶瓷材料作为阻挡层保护银层，且每层氧化锌铝陶瓷材料分别在不同的条件下制作而成，从而具有耐磨、耐酸碱性，高可见光透射率，隔热，低辐射率，使用寿命长等优点。
附图说明
图1为本发明的结构示意图。
具体实施方式
下面结合附图和具体实施例，进一步阐明本发明。
如图1所示的多介质陶瓷低辐射镀膜玻璃，在玻璃原片1的表面从下至上依次设置氧化钛层2、氧化锌铝陶瓷层Ⅰ3、银膜层4、氧化锌铝陶瓷层Ⅱ5、氧化锌铝陶瓷层Ⅲ6和氧化锡层7。
所述多介质陶瓷低辐射镀膜玻璃的各个膜层的制作参数如下表所示：
上述实施例只为说明本发明的技术构思及特点，其目的是让熟悉该技术领域的技术人员能够了解本发明的内容并据以实施，并不能以此来限制本发明的保护范围。凡根据本发明精神实质所作出的等同变换或修饰，都应涵盖在本发明的保护范围之内。
Claims (3)
1.一种多介质陶瓷低辐射镀膜玻璃，其特征在于：在玻璃原片（1）的表面从下至上依次设置氧化钛层（2）、氧化锌铝陶瓷层Ⅰ（3）、银膜层（4）、氧化锌铝陶瓷层Ⅱ（5）、氧化锌铝陶瓷层Ⅲ（6）和氧化锡层（7）。
2.根据权利要求1所述的多介质陶瓷低辐射镀膜玻璃，其特征在于：所述的氧化钛层（2）的厚度为10～20nm；氧化锌铝层Ⅰ的厚度为5～12nm；银膜层（4）的厚度为10～16nm；氧化锌铝层Ⅱ（5）的厚度为4～8nm；氧化锌铝层Ⅲ（6）的厚度为6～12nm；氧化锡层（7）的厚度为25～38nm。
3. 根据权利要求1和2所述的一种多介质陶瓷低辐射镀膜玻璃，其特征在于：所述玻璃原片（1）的厚度为4mm、5mm、6mm、8mm、10mm或12mm。