CN102621811B - 一种应用于面板结构的可显影感光性树脂组成物 - Google Patents
一种应用于面板结构的可显影感光性树脂组成物 Download PDFInfo
- Publication number
- CN102621811B CN102621811B CN201110033452.6A CN201110033452A CN102621811B CN 102621811 B CN102621811 B CN 102621811B CN 201110033452 A CN201110033452 A CN 201110033452A CN 102621811 B CN102621811 B CN 102621811B
- Authority
- CN
- China
- Prior art keywords
- resin composition
- photosensitive resin
- monomer
- lower section
- oxygen ethylene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明一种应用于面板结构的可显影感光性树脂组成物,为一种可显影感光性树脂组成物，其含有树脂、感光起始剂、单体、溶剂、白色颜料及分散剂；其中，该白色颜料在该感光性树脂组成物中为20~45wt%，使该感光性树脂组成物呈现出白色外观颜色，由该感光性树脂组成物设置于一透光基板其中一表面周缘，而形成具有白色装饰边框作用的面板结构，可应用于触控面板或平面显示器等相关产品中。
Description
技术领域
本发明有关可显影感光性树脂组成物的组成，旨在提供一种可显影感光性树脂组成物可应用于触控面板或平面显示器等相关产品中，可有别以往外观颜色受限于黑色或深色的缺失，藉以提升产品外观搭配性。
背景技术
触控面板目前已被广泛应用在行动电话手机、数字相机以及卫星导航器等一般的消费性电子商品上，用以改善使用介面，提升输入效率；通常，触控面板是透明且被配置于这些电子商品的显示屏前使用，让使用者可依据显示屏上指示讯息以进行交互式输入操作，进而大幅改善人与机器之间沟通介面的亲善性。典型的触控面板构造将一触控感应器绝缘的设置在一顶板与一基板之间，然后在迭层板的周缘部位设有线路，用以将触控感应器上的触控讯号传送到一讯号处理电路；较早的时候，触控面板与显示屏的组装方式，大多利用一罩框压制于触控面板表面玻璃的四周边缘，而将触控面板固设于显示屏前方使用，而该罩框除了用以固定面板的目的之外，亦具有保护触控面板表面玻璃周边线路以及美化安装结构的效能。
然此种习知的触控面板组装结构常会衍生诸多缺失，例如，罩框的设置会在表面玻璃形成高低不平的表面，会破坏产品造型的平整性，而且作框内的板面清洁擦拭时，容易使灰尘污垢卡入罩框与触控面板表面玻璃之间的缝隙中，除了产生清洁不干净的卫生问题之外，灰尘污垢在框缘缝隙的填塞累积，也非常容易导致触控面板发生误动作，而且触控面板边缘部位的线路结构通常较为脆弱，受到尘垢填塞物的累积挤压极易侧成损伤，导致传讯不良的现象，此外填塞在框缘缝隙的污垢会破坏外壳与触控面板之间的密接性，影响防水防尘效果，甚至造成内部电器组件的损坏。
另种习知的触控面板亦可于表面玻璃加贴一装饰层，该装饰层一般多使用深色非导电材料所组成的框体结构，用以遮饰表面玻璃下方周边线路，同时做到全平面的触控面板；惟，利用黏贴方式的制作工序繁杂，生产时造成误差的机会也会提升，且该装饰层大多为黑色或银色，虽然提升其产品的质感，但却也使其外观颜色受限制而不具变化性。
发明内容
有鉴于此，本发明旨在提供一种可应用于触控面板或平面显示器等相关产品中，以提升产品外观搭配性。
为达上述目的，本发明的感光性树脂组成物，含有树脂、感光起始剂、单体、溶剂、白色颜料及分散剂；其中，该白色颜料在该感光性树脂组成物中为20~ 45wt%，使该感光性树脂组成物呈现出白色外观颜色。
本发明可应用于触控面板或平面显示器等相关产品中，其中，该感光性树脂组成物可设置于一透光基板其中一表面周缘，而形成具有白色装饰边框作用的面板结构，且亦可对下方周缘部位的线路层形成遮蔽作用。
附图说明
图1为本发明中面板的结构示意图。
图号说明：面板结构1；透光基板11；下表面111；白色边框层12；线路13。
具体实施方式
本发明的感光性树脂组成物，含有15~35wt%的树脂、0.5~10wt%的感光起始剂、0~20wt%的单体、25~50wt%的溶剂、20~45wt%的白色颜料及1~5wt%的分散剂。
其中：该树脂可以为含羧酸基(COOH)的聚合物或共聚物，如可包含但不限于压克力树脂、压克力-环氧树脂、压克力-美耐皿树脂、压克力-苯乙烯树脂、苯酚-酚醛树脂，或以上树脂的混合。因白色颜料比重较高，较易有沉淀的产生，故树脂分子量需大于8000，树脂分子量8000以上搭配适当比例，可减缓白色原料沉淀速度。但另一方面若分子量过大则有操作不易的问题，故分子量要求在100,000以下为佳，更好则在20,000-70,000范围。
该感光起始剂的功能在于感光特性、解析能力，其可包含但不限于肟酯系化合物、苯乙酮系化合物、二苯甲酮系化合物或二咪唑系化合物，或以上感光起始剂的混合。
该单体的功能在于提供较佳的附着性、显影性、解析能力等，可包含但不限于多官能的丙烯酸酯单体、非水溶性单体或水溶性单体，该多官能的丙烯酸酯单体可以为三甲基丙烷三丙烯酸酯、三丙烯乙二醇双丙烯酸酯、1,6 己二醇双丙烯酸酯；而该非水溶性单体可以为戊赤藻糖醇三丙烯酸酯、三甲基醚丙烷三丙烯酸酯、三甲基醚丙烷三甲基丙烯酸酯、三,二-乙醇异氰酸酯三丙烯酸酯、二，三甲醇丙烷四丙烯酸酯、二异戊四醇五丙烯酸酯、五丙烯酸酯、四乙酸异戊四醇、六乙酸二己四醇、六乙酸二异戊四醇，或为多官能基单体、树状/多丛蔟丙烯酸酯寡体、多丛蔟聚醚丙烯酸酯、氨甲酸乙酯；而该水溶性单体则可为聚氧乙烯和聚氧丙烯的单体，其可为二-(二-氧乙烯氧乙烯)乙烯基丙烯酸酯、十五聚氧乙烯三甲醇丙烷三丙烯酸酯、三十个氧乙烯二,二-双对酚甲烷二丙烯酸酯、三十个氧乙烯二,二-双对酚甲烷二甲基丙烯酸酯、二十个氧乙烯三甲醇丙烷三丙烯酸酯、十五个氧乙烯三甲醇丙烷三丙烯酸酯、甲基氧五百五十个氧乙烯单甲基丙烯酸酯、二百个氧乙烯二丙烯酸酯、四百个氧乙烯二丙烯酸酯、四百个氧乙烯二甲基丙烯酸酯、六百个氧乙烯二丙烯酸酯、六百个氧乙烯二甲基丙烯酸酯、聚氧丙烯单甲基丙烯酸酯；亦或者可添加两种以上单体混合成共单体。
该白色颜料包含但不限于可为二氧化钛 (titanium dioxide)、 碳酸铅(Whitelead)、氧化锌(Zinc oxide)、 硫化锌(Zinc sulphide)、 锌钡白(lithopone)或氧化锑(Antimony oxide)；为达遮蔽效果该白色颜料需要达感光性树脂组成物20％以上，来达到遮蔽效果，超过45%则有显影不良的情形产生。而该溶剂作为调整黏度用，其可以为丙二醇单甲基醚醋酸酯；该感光性树脂组成物可进一步添加适量添加剂，例如可以为界面活性剂。
整体感光性树脂组成物因添加有白色颜料，故呈现出白色外观颜色，亦可进一步添加另一其它颜料，如添加 Blue Pigment 15而呈现蓝色、添加Pigment Green 7而呈现绿色，或添加其它色粉而达到想要的色彩。
而本发明的感光性树脂组成物可应用于触控面板或平面显示器等相关产品中，其于一透光基板经由旋转涂布(spin coating)步骤，将本发明的感光性树脂组成物涂布于该透光基板上表面，再依序经由真空干燥(vacuum dry)、预烤(pre-baking)、曝光(exposure)、显影(developing)、硬烤(post baking)等步骤，使该透光基板11下表面111周缘处形成有白色边框层12，如图1所示，形成面板结构1，该透光基板下表面可进一步结合有触控组件，而形成触控面板，例如该透光基板11相对于该感光性树脂组成物所形成的白色边框层12处可进一步设有复数线路13，做为触控讯号的导通，而该白色边框层12恰可完全遮蔽周缘部位的线路13，据此确保触控面板的平整性，并兼具保护触控面板周边线路的功效，且本发明所应用的触控面板或平面显示器等相关产品外观，可有别以往外观颜色受限于黑色或深色的缺失，可大为提升产品外观搭配性。
具体的实施例如下所述，然而，并非以此局限本发明。
感光性树脂组成物采用以下的组成，如表1及表2所列。
表1 感旋光性树脂组成物的组成。
表2 感光性树脂组成物的组成.
测试方法如下。
1. 沉淀观察。
将实施例与比较例进行光学浓度(Optical Density)量测(取样品上层1/3处)，量测日为配制后首日与配制后7日，期间保持样品于室温静置测试。并以波长380nm-780nm 照射各样品比较OD值的差异。
OD值差=∣(第七日OD值-首日OD值)/ 首日OD值∣*100%
2. 观察遮蔽效果(相同膜厚下)。
感光性树脂组成物配制后首日，将金属线路个别置于涂有实施例与比较例的感光性树脂组成物的玻璃片下，进行遮蔽观察，观察涂有感光性树脂组成物的玻璃片下的金属线路是否可见，各实施例与比较例的遮蔽性测试结果表3所示。
| 实施例1 | 实施例2 | 实施例3 | 实施例4 | 比较例1 | 比较例2 | |
| OD值差 | 0.53％ | 0.62％ | 0.85％ | 0.71％ | 3.25％ | 0.58％ |
| 遮蔽性 | ◎ | ◎ | ◎ | ◎ | ◎ | ○ |
◎ 好 ○普通。
表3 测试结果。
如表3可知，各实施例与比较例中OD值的差异以比较例1的数值较大，表示使用分子量5000的压克力树脂，其沉淀现象较为明显，而比较例2中白色颜料的含量低于20 wt%，在遮蔽性的比较中，以比较例2的遮蔽性相对较差，故比较例1及比较例2的组成物成分及比例不适用于本发明的发明目的，而实施例1~4的组成物成分及比例则为本发明的较佳实施例。
Claims (8)
1.一种适用于涂布于一透光基板其中一表面周缘而形成面板结构以对下方线路层形成遮蔽作用的可显影感光性树脂组成物，其特征在于，该感光性树脂组成物含有15~35wt%的树脂、0.5~10wt%的感光起始剂、0~20wt%的单体、25~50wt%的溶剂、20~45wt%的白色颜料及1~5wt%的分散剂；
其中该树脂包含压克力树脂，且该树脂分子量在8000-100,000的范围内。
2.如权利要求1所述的适用于涂布于一透光基板其中一表面周缘而形成面板结构以对下方线路层形成遮蔽作用的可显影感光性树脂组成物，其特征在于，该树脂含压克力酸。
3.如权利要求1所述的适用于涂布于一透光基板其中一表面周缘而形成面板结构以对下方线路层形成遮蔽作用的可显影感光性树脂组成物，其特征在于，该感光起始剂包含肟酯系化合物、苯乙酮系化合物、二苯甲酮系化合物或二咪唑系化合物，或以上感光起始剂的混合。
4.如权利要求1所述的适用于涂布于一透光基板其中一表面周缘而形成面板结构以对下方线路层形成遮蔽作用的可显影感光性树脂组成物，其特征在于，该单体包含多官能的丙烯酸酯单体、非水溶性单体或水溶性单体；该多官能的丙烯酸酯单体为三甲基丙烷三丙烯酸酯、三丙烯乙二醇双丙烯酸酯、或1,6 己二醇双丙烯酸酯；该非水溶性单体为戊赤藻糖醇三丙烯酸酯、三甲基醚丙烷三丙烯酸酯、三甲基醚丙烷三甲基丙烯酸酯、三,二-乙醇异氰酸酯三丙烯酸酯、二，三甲醇丙烷四丙烯酸酯、二异戊四醇五丙烯酸酯、五丙烯酸酯、四乙酸异戊四醇、六乙酸二己四醇、六乙酸二异戊四醇，或为多官能基单体、树状/多丛蔟丙烯酸酯寡体、多丛蔟聚醚丙烯酸酯、氨甲酸乙酯；该水溶性单体为聚氧乙烯和聚氧丙烯的单体，其为二-(二-氧乙烯氧乙烯)乙烯基丙烯酸酯、十五聚氧乙烯三甲醇丙烷三丙烯酸酯、三十个氧乙烯二,二-双对酚甲烷二丙烯酸酯、三十个氧乙烯二,二-双对酚甲烷 二甲基丙烯酸酯、二十个氧乙烯三甲醇丙烷三丙烯酸酯、十五个氧乙烯三甲醇丙烷三丙烯酸酯、甲基氧五百五十个氧乙烯单甲基丙烯酸酯、二百个氧乙烯二丙烯酸酯、四百个氧乙烯二丙烯酸酯、四百个氧乙烯二甲基丙烯酸酯、六百个氧乙烯二丙烯酸酯、六百个氧乙烯二甲基丙烯酸酯、或聚氧丙烯单甲基丙烯酸酯；亦或者该单体为包含该多官能的丙烯酸酯单体、该非水溶性单体或该水溶性单体的两种以上的混合。
5.如权利要求1所述的适用于涂布于一透光基板其中一表面周缘而形成面板结构以对下方线路层形成遮蔽作用的可显影感光性树脂组成物，其特征在于，该溶剂为丙二醇单甲基醚醋酸酯。
6.如权利要求1至5任一所述的适用于涂布于一透光基板其中一表面周缘而形成面板结构以对下方线路层形成遮蔽作用的可显影感光性树脂组成物，其特征在于，该白色颜料包含二氧化钛、碳酸铅、氧化锌、硫化锌、 锌钡白或氧化锑。
7.如权利要求6所述的适用于涂布于一透光基板其中一表面周缘而形成面板结构以对下方线路层形成遮蔽作用的可显影感光性树脂组成物，其特征在于，该感光性树脂组成物进一步添加另一颜料。
8.如权利要求1至5任一所述的适用于涂布于一透光基板其中一表面周缘而形成面板结构以对下方线路层形成遮蔽作用的可显影感光性树脂组成物，其特征在于，该树脂分子量在20,000-70,000的范围内。