CN108245701A - 一种卫生用品用植物芦荟提取物凝胶材料的制备工艺 - Google Patents
一种卫生用品用植物芦荟提取物凝胶材料的制备工艺 Download PDFInfo
- Publication number
- CN108245701A CN108245701A CN201810058239.2A CN201810058239A CN108245701A CN 108245701 A CN108245701 A CN 108245701A CN 201810058239 A CN201810058239 A CN 201810058239A CN 108245701 A CN108245701 A CN 108245701A
- Authority
- CN
- China
- Prior art keywords
- parts
- rubber material
- gel rubber
- extracting solution
- nano
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种卫生用品用植物芦荟提取物凝胶材料的制备工艺，凝胶材料组分按重量份数包括卡波姆5‑12份、琼脂糖8‑20份、大豆低聚糖4‑12份、γ‑环糊精2‑6份、纳米二氧化钛1‑4份、纳米二氧化锆3‑9份、聚合物多元醇10‑20份、芦荟提取液5‑15份、薄荷提取液4‑12份、益母草提取液8‑18份，本发明制备工艺简单，制得的凝胶材料具备较高的孔隙率、透气性和吸水膨胀率，同时还具有抑菌抗菌性能，适用于一次性卫生用品。
Description
技术领域
本发明涉及凝胶材料制备技术领域，具体为一种卫生用品用植物芦荟提取物凝胶材料的制备工艺。
背景技术
一次性卫生用品，包括卫生巾、纸尿裤、卫生护垫、失禁垫等材料，尤其要求材料具有良好的透气性、清爽性、舒适性、吸水性等。目前的此类卫生用品普遍存在的问题是：因产品导热系数低，人体局部热量疏通不畅，造成局部闷热、红肿、红疹、发炎等症状，不能给人体带来良好的使用体感。有部分一次性卫生产品采用薄荷等冷感物质，由于导热系数过高，造成人体局部过凉，妇女、儿童、老弱使用会造成身体不适，抵抗力减弱。
目前，采用凝胶材料的卫生用品使用一端时间后其导热能力就会变差，导致其冰凉程度降低，大大影响了其舒适性，而且其容易滋生细菌。
发明内容
本发明的目的在于提供一种卫生用品用植物芦荟提取物凝胶材料的制备工艺，以解决上述背景技术中提出的问题。
为实现上述目的，本发明提供如下技术方案：一种卫生用品用植物芦荟提取物凝胶材料,凝胶材料组分按重量份数包括卡波姆5-12份、琼脂糖8-20份、大豆低聚糖4-12份、γ- 环糊精2-6份、纳米二氧化钛1-4份、纳米二氧化锆3-9份、聚合物多元醇10-20份、芦荟提取液5-15份、薄荷提取液4-12份、益母草提取液8-18份。
优选的，凝胶材料组分优选的成分配比包括卡波姆9份、琼脂糖14份、大豆低聚糖8份、γ- 环糊精4份、纳米二氧化钛3份、纳米二氧化锆6份、聚合物多元醇15份、芦荟提取液10份、薄荷提取液8份、益母草提取液13份。
优选的，其制备工艺包括以下步骤：
A、将卡波姆、琼脂糖、大豆低聚糖、γ- 环糊精、纳米二氧化钛、纳米二氧化锆、聚合物多元醇充分混合后加入磁力搅拌机中搅拌，搅拌速率为200-400转/分，时间为20min-30min，得到混合物A；
B、将芦荟提取液、薄荷提取液、益母草提取液混合后加入水浴锅中水浴加热，得到混合物B；
C、将混合物A加入混合物B中，充分混合后在常温下静置15min，再进行剪切处理，剪切处理时间为 10min，剪切处理转速为 1000-2500转/分；最后将剪切后的材料放置在常温下30min，即得到凝胶材料。
优选的，所述步骤B中水浴加热温度为55℃-70℃，加热时间为15min-25min。
与现有技术相比，本发明的有益效果是：本发明制备工艺简单，制得的凝胶材料具备较高的孔隙率、透气性和吸水膨胀率，同时还具有抑菌抗菌性能，适用于一次性卫生用品；其中，本发明中添加的纳米二氧化钛和纳米二氧化锆具有优异的抗菌性能；此外，本发明采用的制备工艺操作简单，成本低，能够防止有效成分流失，同时还能够提高凝胶材料的韧性和抗拉伸性能。
具体实施方式
下面对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
本发明提供如下技术方案：一种卫生用品用植物芦荟提取物凝胶材料,凝胶材料组分按重量份数包括卡波姆5-12份、琼脂糖8-20份、大豆低聚糖4-12份、γ- 环糊精2-6份、纳米二氧化钛1-4份、纳米二氧化锆3-9份、聚合物多元醇10-20份、芦荟提取液5-15份、薄荷提取液4-12份、益母草提取液8-18份。
实施例一：
凝胶材料组分按重量份数包括卡波姆5份、琼脂糖8份、大豆低聚糖4份、γ- 环糊精2份、纳米二氧化钛1份、纳米二氧化锆3份、聚合物多元醇10份、芦荟提取液5份、薄荷提取液4份、益母草提取液8份。
本实施例的制备工艺包括以下步骤：
A、将卡波姆、琼脂糖、大豆低聚糖、γ- 环糊精、纳米二氧化钛、纳米二氧化锆、聚合物多元醇充分混合后加入磁力搅拌机中搅拌，搅拌速率为200转/分，时间为20min，得到混合物A；
B、将芦荟提取液、薄荷提取液、益母草提取液混合后加入水浴锅中水浴加热，得到混合物B；
C、将混合物A加入混合物B中，充分混合后在常温下静置15min，再进行剪切处理，剪切处理时间为 10min，剪切处理转速为 1000转/分；最后将剪切后的材料放置在常温下30min，即得到凝胶材料。
本实施例中，步骤B中水浴加热温度为55℃，加热时间为15min。
实施例二：
凝胶材料组分按重量份数包括卡波姆12份、琼脂糖20份、大豆低聚糖12份、γ- 环糊精6份、纳米二氧化钛4份、纳米二氧化锆9份、聚合物多元醇20份、芦荟提取液15份、薄荷提取液12份、益母草提取液18份。
本实施例的制备工艺包括以下步骤：
A、将卡波姆、琼脂糖、大豆低聚糖、γ- 环糊精、纳米二氧化钛、纳米二氧化锆、聚合物多元醇充分混合后加入磁力搅拌机中搅拌，搅拌速率为400转/分，时间为30min，得到混合物A；
B、将芦荟提取液、薄荷提取液、益母草提取液混合后加入水浴锅中水浴加热，得到混合物B；
C、将混合物A加入混合物B中，充分混合后在常温下静置15min，再进行剪切处理，剪切处理时间为 10min，剪切处理转速为 2500转/分；最后将剪切后的材料放置在常温下30min，即得到凝胶材料。
本实施例中，步骤B中水浴加热温度为70℃，加热时间为25min。
实施例三：
凝胶材料组分按重量份数包括卡波姆7份、琼脂糖9份、大豆低聚糖6份、γ- 环糊精3份、纳米二氧化钛2份、纳米二氧化锆5份、聚合物多元醇12份、芦荟提取液7份、薄荷提取液6份、益母草提取液9份。
本实施例的制备工艺包括以下步骤：
A、将卡波姆、琼脂糖、大豆低聚糖、γ- 环糊精、纳米二氧化钛、纳米二氧化锆、聚合物多元醇充分混合后加入磁力搅拌机中搅拌，搅拌速率为250转/分，时间为22min，得到混合物A；
B、将芦荟提取液、薄荷提取液、益母草提取液混合后加入水浴锅中水浴加热，得到混合物B；
C、将混合物A加入混合物B中，充分混合后在常温下静置15min，再进行剪切处理，剪切处理时间为 10min，剪切处理转速为 1300转/分；最后将剪切后的材料放置在常温下30min，即得到凝胶材料。
本实施例中，步骤B中水浴加热温度为58℃，加热时间为17min。
实施例四：
凝胶材料组分按重量份数包括卡波姆10份、琼脂糖18份、大豆低聚糖10份、γ- 环糊精6份、纳米二氧化钛3份、纳米二氧化锆7份、聚合物多元醇16份、芦荟提取液12份、薄荷提取液10份、益母草提取液15份。
本实施例的制备工艺包括以下步骤：
A、将卡波姆、琼脂糖、大豆低聚糖、γ- 环糊精、纳米二氧化钛、纳米二氧化锆、聚合物多元醇充分混合后加入磁力搅拌机中搅拌，搅拌速率为380转/分，时间为26min，得到混合物A；
B、将芦荟提取液、薄荷提取液、益母草提取液混合后加入水浴锅中水浴加热，得到混合物B；
C、将混合物A加入混合物B中，充分混合后在常温下静置15min，再进行剪切处理，剪切处理时间为 10min，剪切处理转速为 2000转/分；最后将剪切后的材料放置在常温下30min，即得到凝胶材料。
本实施例中，步骤B中水浴加热温度为66℃，加热时间为22min。
实施例五：
凝胶材料组分按重量份数包括卡波姆9份、琼脂糖14份、大豆低聚糖8份、γ- 环糊精4份、纳米二氧化钛3份、纳米二氧化锆6份、聚合物多元醇15份、芦荟提取液10份、薄荷提取液8份、益母草提取液13份。
本实施例的制备工艺包括以下步骤：
A、将卡波姆、琼脂糖、大豆低聚糖、γ- 环糊精、纳米二氧化钛、纳米二氧化锆、聚合物多元醇充分混合后加入磁力搅拌机中搅拌，搅拌速率为300转/分，时间为25min，得到混合物A；
B、将芦荟提取液、薄荷提取液、益母草提取液混合后加入水浴锅中水浴加热，得到混合物B；
C、将混合物A加入混合物B中，充分混合后在常温下静置15min，再进行剪切处理，剪切处理时间为 10min，剪切处理转速为 1800转/分；最后将剪切后的材料放置在常温下30min，即得到凝胶材料。
本实施例中，步骤B中水浴加热温度为61℃，加热时间为20min。
实验例：
采用本发明各实施例制得的凝胶材料进行抗拉伸强度和除菌率实验，得到数据如下表：
| 抗拉伸强度（MPA） | 除菌率（%） | |
| 实施例一 | 0.82 | 92.8 |
| 实施例二 | 0.82 | 92.6 |
| 实施例三 | 0.80 | 93.1 |
| 实施例四 | 0.84 | 92.7 |
| 实施例五 | 0.88 | 93.8 |
本发明制备工艺简单，制得的凝胶材料具备较高的孔隙率、透气性和吸水膨胀率，同时还具有抑菌抗菌性能，适用于一次性卫生用品；其中，本发明中添加的纳米二氧化钛和纳米二氧化锆具有优异的抗菌性能；此外，本发明采用的制备工艺操作简单，成本低，能够防止有效成分流失，同时还能够提高凝胶材料的韧性和抗拉伸性能。
尽管已经示出和描述了本发明的实施例，对于本领域的普通技术人员而言，可以理解在不脱离本发明的原理和精神的情况下可以对这些实施例进行多种变化、修改、替换和变型，本发明的范围由所附权利要求及其等同物限定。
Claims (4)
1.一种卫生用品用植物芦荟提取物凝胶材料,其特征在于：凝胶材料组分按重量份数包括卡波姆5-12份、琼脂糖8-20份、大豆低聚糖4-12份、γ- 环糊精2-6份、纳米二氧化钛1-4份、纳米二氧化锆3-9份、聚合物多元醇10-20份、芦荟提取液5-15份、薄荷提取液4-12份、益母草提取液8-18份。
2.根据权利要求1所述的一种卫生用品用植物芦荟提取物凝胶材料,其特征在于：凝胶材料组分优选的成分配比包括卡波姆9份、琼脂糖14份、大豆低聚糖8份、γ- 环糊精4份、纳米二氧化钛3份、纳米二氧化锆6份、聚合物多元醇15份、芦荟提取液10份、薄荷提取液8份、益母草提取液13份。
3.实现权利要求1所述的一种卫生用品用植物芦荟提取物凝胶材料的制备工艺,其特征在于：其制备工艺包括以下步骤：
A、将卡波姆、琼脂糖、大豆低聚糖、γ- 环糊精、纳米二氧化钛、纳米二氧化锆、聚合物多元醇充分混合后加入磁力搅拌机中搅拌，搅拌速率为200-400转/分，时间为20min-30min，得到混合物A；
B、将芦荟提取液、薄荷提取液、益母草提取液混合后加入水浴锅中水浴加热，得到混合物B；
C、将混合物A加入混合物B中，充分混合后在常温下静置15min，再进行剪切处理，剪切处理时间为 10min，剪切处理转速为 1000-2500转/分；最后将剪切后的材料放置在常温下30min，即得到凝胶材料。
4.根据权利要求3所述的一种卫生用品用植物芦荟提取物凝胶材料的制备工艺,其特征在于：所述步骤B中水浴加热温度为55℃-70℃，加热时间为15min-25min。