CN107828183A - 一种改性脲醛模塑料及其制备方法 - Google Patents
一种改性脲醛模塑料及其制备方法 Download PDFInfo
- Publication number
- CN107828183A CN107828183A CN201711128211.3A CN201711128211A CN107828183A CN 107828183 A CN107828183 A CN 107828183A CN 201711128211 A CN201711128211 A CN 201711128211A CN 107828183 A CN107828183 A CN 107828183A
- Authority
- CN
- China
- Prior art keywords
- formaldehyde
- moulding compound
- preparation
- urea
- modified urea
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及改性聚合物技术领域，具体地说，涉及一种改性脲醛模塑料及其制备方法，包括如下重量百分比的各种组分：脲甲醛模塑料60‑80％；三聚氰胺甲醛模塑料15‑25％。本发明中的改性脲醛模塑料具有优良的耐热性，可在160℃下连续150小时加热不开裂、不变形，不仅能保持原有塑料的外观且保持尺寸的稳定性和其它机型性能，制备方法简单实用，适合大规模工业化生产。
Description
技术领域
本发明涉及改性聚合物技术领域，具体地说，涉及一种改性脲醛模塑料及其制备方法。
背景技术
三聚氰胺甲醛模塑料是由三聚氰胺甲醛树脂为基础，添加填料、脱模剂、颜料、固化剂和脱模剂，并采用一定的工艺制成，其色彩鲜艳、外表光滑、无臭无味，具有较高的热变形温度、阻燃、自熄、耐电弧、制品尺寸稳定及耐水等优点，因而广泛用于电子、电器、汽车以及日常用具。
然而在使用常规的脲醛树脂模塑料加工低压电器接插件时，通常加工的温度超过180℃，在这种高温的条件下长时间加工，常规的脲醛模塑料会出现开裂、变形等现象，降低了低压电器接插件的加工效率，产生大量不合格产品。鉴于此，我们提出一种改性脲醛模塑料及其制备方法。
发明内容
本发明的内容是提供一种改性脲醛模塑料及其制备方法，其能够克服现有技术的某种或某些缺陷。
根据本发明的一种改性脲醛模塑料及其制备方法，包括如下重量百分比的各种组分：脲甲醛模塑料60-80％；三聚氰胺甲醛模塑料15-25％。
作为优选，所述脲甲醛模塑料包括如下重量百分比的各种组分：苯胺甲醛树脂20-30％；脲醛树脂25-35％；木浆10-15％；无机填料2-4％；颜料2-4％；固化剂0.5-2％；增塑剂2-8％；脱模剂0.5-3％。
作为优选，所述三聚氰胺甲醛模塑料包括如下重量百比的各种组分：三聚氰胺甲醛树脂40-50％；木浆20-30％；无机填料2-3％；颜料2-3％；固化剂2-5％；增塑剂3-4％；脱模剂1-1.5％。
作为优选，所述改性脲醛模塑料包括如下重量百分比的各种组分：脲甲醛模塑料65％；三聚氰胺甲醛模塑料20％。
作为优选，所述脲甲醛模塑料包括如下重量百分比的各种组分：苯胺甲醛树脂25％；脲醛树脂30％；木浆12％；无机填料3％；颜料3％；固化剂1％；增塑剂5％；脱模剂2％.
作为优选，所述三聚氰胺甲醛模塑料包括如下重量百比的各种组分：三聚氰胺甲醛树脂45％；木浆25％；无机填料2.5％；颜料2.5％；固化剂2.5％；增塑剂3.5％；脱模剂1％。
作为优选，所述无机填料选自硅微粉、滑石粉或玻璃微珠中的任意一种或几种的组合物。
作为优选，所述增塑剂选自葡萄糖苷或ACR中的任意一种或者两者的组合物。
作为优选，所述固化剂选自SE、GW和UP中的任意一种或者几种的组合物。所述脱模剂选自硬脂酸锌或硬脂酸钙中的任意一种或者两者的组合物。
作为优选，所述改性脲醛模塑料及其制备方法，包括以下步骤：
1)按配方量将制备好的苯胺甲醛树脂和脲醛树脂加入捏合机中，然后加入配方量所述的木浆、无机填料、颜料、固化剂与脱模剂，在夹套蒸汽加热下真空脱水，温度控制在50℃，加热时间为55分钟，然后关闭蒸汽，物料冷却至45℃以下，即得脲醛模塑料浆料；
2)将步骤1)所述的脲醛模塑料浆料送入干燥器，控制各节热风温度在90℃，时间为130分钟，最后一节冷却至35℃以下，得到含水量低于3％的脲醛模塑料；
3)将步骤2)所得的脲醛模塑料按配方的重量比粉碎进入球磨机球磨2.5小时，然后按配方的重量比投入已制备好的三聚氰胺甲醛模塑料，一起再球磨3小时后出料分离，细粉成半成品，粗粉集中再球磨后，均摊入以后的球磨；
4)将经步骤3)混合的模塑料投入造粒机中造粒，然后经筛粒、分离得到一定粒度范围的颗粒状改性脲醛模塑料及其制备方法包装为成品，细粉再回到球磨进行循环利用。
与现有技术相比，本发明的有益效果：使用了苯胺甲醛树脂、脲醛树脂、三聚氰胺甲醛树脂及耐热的无机填料来提高脲醛树脂的耐热性，选用的无机填料为高熔点的白色粉末及实心玻璃微珠，具有较高的白度，膨胀系数低，酸值略偏于弱碱性，通过处理与树脂交联，由于三聚氰胺与甲醛反应生成三聚氰胺甲醛树脂，在耐热性、耐水性上均优于脲醛树脂，而且有效降低脲醛树脂中残留的甲醛，明显降低改性脲醛模塑料中所含游离醛，改善后加工的环境条件，因此，经过上述改性的脲醛树脂具有优良的耐热性，可在150℃下连续168小时加热不开裂、不变形，不仅能保持原有塑料的外观且保持尺寸的稳定性和其它机型性能，制备方法简单实用，适合大规模工业化生产。
具体实施方式
为进一步了解本发明的内容，结合实施例对本发明作详细描述。应当理解的是，实施例仅仅是对本发明进行解释而并非限定。
本实施例提供了一种改性脲醛模塑料及其制备方法，其由重量百分比为以下的组分组成：
一种改性脲醛模塑料及其制备方法，包括如下重量百分比的各种组分：脲甲醛模塑料60-80％；三聚氰胺甲醛模塑料15-25％。
本实施例中，所述脲甲醛模塑料包括如下重量百分比的各种组分：苯胺甲醛树脂20-30％；脲醛树脂25-35％；木浆10-15％；无机填料2-4％；颜料2-4％；固化剂0.5-2％；增塑剂2-8％；脱模剂0.5-3％。
本实施例中，所述三聚氰胺甲醛模塑料包括如下重量百比的各种组分：三聚氰胺甲醛树脂40-50％；木浆20-30％；无机填料2-3％；颜料2-3％；固化剂2-5％；增塑剂3-4％；脱模剂1-1.5％。
本实施例中，所述改性脲醛模塑料包括如下重量百分比的各种组分：脲甲醛模塑料65％；三聚氰胺甲醛模塑料20％。
本实施例中，所述脲甲醛模塑料包括如下重量百分比的各种组分：苯胺甲醛树脂25％；脲醛树脂30％；木浆12％；无机填料3％；颜料3％；固化剂1％；增塑剂5％；脱模剂2％.
本实施例中，所述三聚氰胺甲醛模塑料包括如下重量百比的各种组分：三聚氰胺甲醛树脂45％；木浆25％；无机填料2.5％；颜料2.5％；固化剂2.5％；增塑剂3.5％；脱模剂1％。
本实施例中，所述无机填料选自硅微粉、滑石粉或玻璃微珠中的任意一种或几种的组合物。
本实施例中，所述增塑剂选自葡萄糖苷或ACR中的任意一种或者两者的组合物。
本实施例中，所述固化剂选自SE、GW和UP中的任意一种或者几种的组合物。所述脱模剂选自硬脂酸锌或硬脂酸钙中的任意一种或者两者的组合物。
本实施例中，所述改性脲醛模塑料及其制备方法，包括以下步骤：
3)按配方量将制备好的苯胺甲醛树脂和脲醛树脂加入捏合机中，然后加入配方量所述的木浆、无机填料、颜料、固化剂与脱模剂，在夹套蒸汽加热下真空脱水，温度控制在50℃，加热时间为55分钟，然后关闭蒸汽，物料冷却至45℃以下，即得脲醛模塑料浆料；
4)将步骤1)所述的脲醛模塑料浆料送入干燥器，控制各节热风温度在90℃，时间为130分钟，最后一节冷却至35℃以下，得到含水量低于3％的脲醛模塑料；
3)将步骤2)所得的脲醛模塑料按配方的重量比粉碎进入球磨机球磨2.5小时，然后按配方的重量比投入已制备好的三聚氰胺甲醛模塑料，一起再球磨3小时后出料分离，细粉成半成品，粗粉集中再球磨后，均摊入以后的球磨；
4)将经步骤3)混合的模塑料投入造粒机中造粒，然后经筛粒、分离得到一定粒度范围的颗粒状改性脲醛模塑料及其制备方法包装为成品，细粉再回到球磨进行循环利用。
将实施例中所得的改性脲醛模塑料进行耐热性测试，实验结果如下：
| 实验项目 | 实施例 |
| 160℃烘箱连续烘烤150小时 | 不开裂不起泡不变形 |
| 绝缘电阻Ω | ≥1x1012 |
| 弯曲强度(MPa) | 97 |
通过上表可以发现，本实施例的改性脲醛模塑料为最佳实施例。
以上示意性地对本发明及其实施方式进行了描述，该描述没有限制性。所以，如果本领域的普通技术人员受其启示，在不脱离本发明创造宗旨的情况下，不经创造性地设计出与该技术方案相似的方案及实施例，均应属于本发明的保护范围。
Claims (10)
1.一种改性脲醛模塑料及其制备方法，其特征在于，包括如下重量百分比的各种组分：脲甲醛模塑料60-80％；三聚氰胺甲醛模塑料15-25％。
2.如权利要求1所述的改性脲醛模塑料及其制备方法，其特征在于，所述脲甲醛模塑料包括如下重量百分比的各种组分：苯胺甲醛树脂20-30％；脲醛树脂25-35％；木浆10-15％；无机填料2-4％；颜料2-4％；固化剂0.5-2％；增塑剂2-8％；脱模剂0.5-3％。
3.如权利要求1所述的改性脲醛模塑料及其制备方法，其特征在于，所述三聚氰胺甲醛模塑料包括如下重量百比的各种组分：三聚氰胺甲醛树脂40-50％；木浆20-30％；无机填料2-3％；颜料2-3％；固化剂2-5％；增塑剂3-4％；脱模剂1-1.5％。
4.如权利要求1所述的改性脲醛模塑料及其制备方法，其特征在于，所述改性脲醛模塑料包括如下重量百分比的各种组分：脲甲醛模塑料65％；三聚氰胺甲醛模塑料20％。
5.如权利要求2所述的改性脲醛模塑料及其制备方法，其特征在于，所述脲甲醛模塑料包括如下重量百分比的各种组分：苯胺甲醛树脂25％；脲醛树脂30％；木浆12％；无机填料3％；颜料3％；固化剂1％；增塑剂5％；脱模剂2％。
6.如权利要求3所述的改性脲醛模塑料及其制备方法，其特征在于，所述三聚氰胺甲醛模塑料包括如下重量百比的各种组分：三聚氰胺甲醛树脂45％；木浆25％；无机填料2.5％；颜料2.5％；固化剂2.5％；增塑剂3.5％；脱模剂1％。
7.如权利要求2-6任一项所述的改性脲醛模塑料及其制备方法，其特征在于：所述无机填料选自硅微粉、滑石粉或玻璃微珠中的任意一种或几种的组合物。
8.如权利要求2-6任一项所述的改性脲醛模塑料及其制备方法，其特征在于:所述增塑剂选自葡萄糖苷或ACR中的任意一种或者两者的组合物。
9.如权利要求2-6任一项所述的改性脲醛模塑料及其制备方法，其特征在于,所述固化剂选自SE、GW和UP中的任意一种或者几种的组合物。所述脱模剂选自硬脂酸锌或硬脂酸钙中的任意一种或者两者的组合物。
10.如权利要求2-6任一项所述的改性脲醛模塑料及其制备方法的制备方法，其特征在于，包括以下步骤：
1)按配方量将制备好的苯胺甲醛树脂和脲醛树脂加入捏合机中，然后加入配方量所述的木浆、无机填料、颜料、固化剂与脱模剂，在夹套蒸汽加热下真空脱水，温度控制在50℃，加热时间为55分钟，然后关闭蒸汽，物料冷却至45℃以下，即得脲醛模塑料浆料；
2)将步骤1)所述的脲醛模塑料浆料送入干燥器，控制各节热风温度在90℃，时间为130分钟，最后一节冷却至35℃以下，得到含水量低于3％的脲醛模塑料；
3)将步骤2)所得的脲醛模塑料按配方的重量比粉碎进入球磨机球磨2.5小时，然后按配方的重量比投入已制备好的三聚氰胺甲醛模塑料，一起再球磨3小时后出料分离，细粉成半成品，粗粉集中再球磨后，均摊入以后的球磨；
4)将经步骤3)混合的模塑料投入造粒机中造粒，然后经筛粒、分离得到一定粒度范围的颗粒状改性脲醛模塑料及其制备方法包装为成品，细粉再回到球磨进行循环利用。