CN105200603A - 一种芳族聚酰胺纤维雪尼尔纱线 - Google Patents
一种芳族聚酰胺纤维雪尼尔纱线 Download PDFInfo
- Publication number
- CN105200603A CN105200603A CN201410294003.0A CN201410294003A CN105200603A CN 105200603 A CN105200603 A CN 105200603A CN 201410294003 A CN201410294003 A CN 201410294003A CN 105200603 A CN105200603 A CN 105200603A
- Authority
- CN
- China
- Prior art keywords
- fiber
- fibre
- aramid
- chenille yarn
- yarn
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种芳族聚酰胺纤维雪尼尔纱线，包括芯线和羽纱两部分，所述羽纱的材质为芳族聚酰胺纤维或芳族聚酰胺纤维与石英玻璃纤维、高硅氧玻璃纤维、硅酸铝纤维、聚酰胺酰亚胺纤维、聚醚醚酮纤维、聚苯硫醚纤维、聚砜基酰胺纤维、聚对苯撑苯并双噁唑纤维、聚苯并咪唑纤维、聚四氟乙烯纤维、聚酰亚胺纤维、芳纶中的一种或多种的混合纱；所述的芯线为两根股线，芯线加捻后将羽纱夹在两根芯线中间。本发明有以下优点：芳族聚酰胺纤维纤维是一种纯无机纤维，具有耐高温，强力大、散热透气性好，抗霉防蛀，无静电，以及独特的抑制细菌生长和高效阻隔紫外线穿透的特性。
Description
技术领域
本发明专利涉及一种空气净化用纱线，具体涉及一种芳族聚酰胺纤维雪尼尔纱线。
背景技术
现有技术中的雪尼尔纱线其芯线是以腈纶纱为原料加捻而成，羽纱是以粘胶纱为原料切割成短羽而成，被广泛地应用于家纺及针织服装领域。采用普通的雪尼尔纱线织造的织物一般多取其装饰效果，其舒适性方面较差。很少用于空气过滤用途。
中国在经历了18世纪工业革命带来的“煤烟型污染”和19世纪石油和汽车工业带来的“光化学烟雾污染”之后，现代人正经历以具有中国特色的“严重PM2.5型雾霾大气环境污染”为标志的第三污染时期。现在人们所处的生活环境越来越恶劣，无尽的工业排放废气、随处可见的汽车尾气导致了日益严重的空气污染。雾霾天气、PM2.5已经向人们警示空气污染的严重影响。工业化的进程对空气过滤器的需求日趋严格，如医疗、卫生、食品、化工、电子等洁净车间，洁净厂房，实验室及洁净室，或者用于电子机械通信设备等的防尘。
空气过滤器一般分为初效空气过滤器、中效空气过滤器、高效空气过滤器及亚高效空气过滤器等型号。过滤材料有无纺布、尼龙网、活性炭过滤棉、金属孔网等，防护网有双面喷塑铁丝网和双面镀锌铁丝网。价廉、重量轻、通用性好、结构紧凑。过滤器材料选择一般都要考虑到空气过滤器的阻力和使用问题，以防空气悬浮颗粒给洁净区造成影响，并且保证过滤器使用寿命。
空气中颗粒物去除技术主要有机械过滤、吸附、静电除尘、负离子和等离子体法及静电驻极过滤等。机械过滤一般主要通过以下3种方式捕获微粒：直接拦截，惯性碰撞，布朗扩散机理，其对细小颗粒物收集效果好但风阻大，为了获得高的净化效率，滤芯需要致密并定期更换。吸附是利用材料的大表面积及多孔结构捕获颗粒污染物，很容易堵塞，用于气体污染物去除效果更显著；静电除尘是利用高压静电场使气体电离从而使尘粒带电吸附到电极上的收尘方法，其风阻虽小但对较大颗粒和纤维捕集效果差，会引起放电，且清洗麻烦费时，易产生臭氧，形成二次污染。负离子和等离子体法去除室内颗粒污染物的工作原理类似，都是通过使空气中的颗粒物带电，聚结形成较大颗粒而沉降，但颗粒物实际上并未移除，只是附着于附近的表面上，易导致再次扬尘。静电驻极过滤以3M“高效静电空气过滤网”为代表，采用突破性携带永久静电滤材，有效阻隔空气中大于0.1微米的颗粒污染物，如粉尘、毛屑、花粉、细菌等，同时超低阻抗确保空调稳定运行及制冷效果。此外，深度容尘设计确保使用寿命更长。在家庭及车载空调(如上汽、大众、通用等知名品牌畅销车型)以及一些商用建筑领域(如鸟巢、北京饭店、首都机场三期)得到广泛应用。传统的标准过滤介质能非常有效地去除10微米以上的颗粒物。当颗粒物的粒径除至5微米，2微米甚至亚微米的范围时，高效的机械式过滤系统就会变得比较昂贵，且风阻会显著增加。通过静电驻极空气过滤材料过滤，能以较低的能源消耗达到很高的捕获效率，同时兼具静电除尘低风阻的优点，但无需外接上万伏的电压，故不会产生臭氧，且由于其组成为聚丙烯材质，很方便抛弃处理。该类滤料对低温污染空气较有用，由于纤维材料自身的限制，高于130度的污染空气环境，该类材料不能使用。
涤纶针刺毡更具有先进功能的高效材质的过滤材料。一般的烟气温度不高于150℃，可选用涤纶针刺无纺布等变通滤材，但工业温度高于150℃以上，如化工，炭黑尾气，炼铁高炉煤气，水泥厂立窖尾气，电石厂窖炉尾气，铸造，炼钢烟气，沥青混凝土搅拌沥青烟气，焦化烟气，冶炼烟气等则选用芳族聚酰胺纤维滤袋。一是因为这些烟气粉尘因受比电阻限制不适合于电收尘收集，只能采用布袋收集；二是如需将含尘烟气温度降至150℃以下，投资较高或受场地限制；三是因为粉尘烟气温度中包含有硫的成分，具酸露点，含尘烟气只能在酸露点以上温度较高的状况下进行过滤分离等因素。
玻璃纤维针刺毡，可广泛适用于化工，钢铁，冶金，炭黑，发电，水泥等各种工业炉窑的高温烟气过滤。适用于脉冲清灰及较高速反吹清灰等各种袋式除尘器。玻璃纤维针刺毡是一种结构合理，性能较好的耐高温过滤材料。它不仅具有玻纤织物耐高温，耐腐蚀，尺寸稳定，伸长收缩率极小，强度高的优点，而且毡层纤维承单纤维，三维微孔结构，孔隙率高，对气体过滤阻力小，是一种较高速，高效的高温过滤材料。与其它耐高温化纤毡相比，具有价格低，耐温更高等特殊优点。但其运行阻力要高于一般化纤高温滤料，过滤精度略低。
针对高温污染空气，“微孔薄复合滤料”是目前在特定环境实用的空气过滤材料。“微孔薄复合滤料”是经聚四氟乙烯为原料，将其膨化为一种具有多微孔性的薄膜，将此薄膜用特殊工艺复合在各种织物或纸质基材上，使其成为一种新型的“微孔薄复合滤料”。这是一种理想的过滤材料，它具有聚四氟乙烯所固有的性能极佳的化学稳定性、表面极其光滑、极低的摩檫系数，耐高低温、不会老化、持久耐用消费品用，而且它亦具有多微孔性、透气性和憎水性。但该类滤料由于材料本身的问题，空气阻力巨大，价格高，限制了其推广应用。
发明内容
针对现有技术中存在的问题，本发明提供一种芳族聚酰胺纤维雪尼尔纱线，该纱线兼具高温空气过滤净化性能和装饰性。
为实现上述发明目的，本发明采用以下技术方案：
一种芳族聚酰胺纤维雪尼尔纱线，包括芯线和羽纱两部分，所述羽纱的材质为芳族聚酰胺纤维或芳族聚酰胺纤维与石英玻璃纤维、高硅氧玻璃纤维、硅酸铝纤维、聚酰胺酰亚胺纤维、聚醚醚酮纤维、聚苯硫醚纤维、聚砜基酰胺纤维、聚对苯撑苯并双噁唑纤维、聚苯并咪唑纤维、聚四氟乙烯纤维、聚酰亚胺纤维、芳纶中的一种或多种的混合纱；所述的芯线为两根股线，芯线加捻后将羽纱夹在两根芯线中间。
所述芯线的材质为石英玻璃纤维、高硅氧玻璃纤维、硅酸铝纤维、聚酰胺酰亚胺纤维、聚醚醚酮纤维、聚苯硫醚纤维、聚砜基酰胺纤维、聚对苯撑苯并双噁唑纤维、聚苯并咪唑纤维、聚四氟乙烯纤维、聚酰亚胺纤维、芳纶和玄武岩纤维中的一种或多种的混合。
所述芯线的单纤维截面为圆形、星形、桔瓣形。
所述芯线的材质为芳族聚酰胺纤维。
所述羽纱和/或芯线的表面具有热塑性、热固性熔胶的涂层。
所述芯线的细度为0.01-100Nm。
所述羽纱的细度为0.01-100Nm。
所述芯线的加捻捻度为10-1000捻/米。
所述羽纱的轴向密度为10-10000根/cm。
与现有技术相比，本发明有以下优点：①芳族聚酰胺纤维纤维是一种纯无机纤维，具有耐高温，强力大、散热透气性好，抗霉防蛀，无静电，以及独特的抑制细菌生长和高效阻隔紫外线穿透的特性；②芳族聚酰胺纤维纤维充当羽纱，制成的条干均匀、可纺性好、手感比较柔软的芳族聚酰胺纤维雪尼尔纱线，其制成的绒类织物和装饰织物，阻燃、透气性好；③相对同样密度的针刺滤布和滤袋，重量轻，滤效高，阻力小，其性能是传统利用玻璃纤维、化纤为原料制成的空气过滤材料所不能比拟的。
具体实施方式
实施例1
本实施例芳族聚酰胺纤维雪尼尔纱线，包括芯线和羽纱两部分，所述羽纱的材质为芳族聚酰胺纤维，羽纱的细度为21Nm；所述的芯线为两根股线，每根股线的细度为24Nm，芯线的材质为芳族聚酰胺纤维，芯线加捻后将羽纱夹在两根芯线中间，芯线的加捻捻度为590捻/米，羽纱的轴向密度为390根/cm。
本实施例芯线的表面涂覆有热固性聚酰亚胺熔胶的涂层。
实施例2
本实施例芳族聚酰胺纤维雪尼尔纱线，包括芯线和羽纱两部分，羽纱的材质为100Nm芳族聚酰胺纤维纱；芯线为两根0.01Nm芳族聚酰胺纤维股线，芯线加10捻/米将10000根/cm羽纱夹在两根芯线中间。
本实施例芯线的表面涂覆有热塑性聚乙烯熔胶的涂层。
实施例3
本实施例芳族聚酰胺纤维雪尼尔纱线，包括芯线和羽纱两部分，羽纱的材质为100Nm芳族聚酰胺纤维纱；芯线为两根100Nm芳族聚酰胺纤维股线，芯线加1000捻/米将10000根/cm羽纱夹在两根芯线中间。
本实施例芯线的表面涂覆有具有热塑性聚丙烯熔胶的涂层。
实施例4
本实施例芳族聚酰胺纤维雪尼尔纱线，包括芯线和羽纱两部分，羽纱的材质为芳族聚酰胺纤维与高硅氧玻璃纤维及硅酸铝纤维的混合纱线，该混合纱线的细度为10Nm，所述芯线的细度为5Nm，该芯线为两根由聚砜基酰胺纤维与聚对苯撑苯并双噁唑纤维组成的股线，芯线加捻后将羽纱夹在两根芯线中间，芯线的加捻捻度600捻/米，羽纱的轴向密度为800根/cm。
本实施例芯线和羽纱的表面均涂覆有热固性聚酰亚胺熔胶的涂层。
实施例5
本实施例芳族聚酰胺纤维雪尼尔纱线，包括芯线和羽纱两部分，羽纱的材质为芳族聚酰胺纤维与聚四氟乙烯纤维组成的混合纱线，该混合纱线的细度为0.01Nm，所述芯线的细度为0.01Nm，该芯线为两根聚对苯撑苯并双噁唑纤维股线，该芯线的截面为圆形，芯线加捻后将羽纱夹在两根芯线中间，芯线的加捻捻度10捻/米，羽纱的轴向密度为10根/cm。
本实施例芯线和羽纱的表面均涂覆有热固性聚酰亚胺熔胶的涂层。
此外，需要说明的是，本发明专利所属技术领域的技术人员可以对所描述的具体实施例做各种各样的修改或补充或采用类似的方式替代，只要不偏离本发明专利的结构或者超越本权利要求书所定义的范围，均应属于本发明专利的保护范围。
Claims (9)
1.一种芳族聚酰胺纤维雪尼尔纱线，包括芯线和羽纱两部分，其特征在于：所述羽纱的材质为芳族聚酰胺纤维或芳族聚酰胺纤维与石英玻璃纤维、高硅氧玻璃纤维、硅酸铝纤维、聚酰胺酰亚胺纤维、聚醚醚酮纤维、聚苯硫醚纤维、聚砜基酰胺纤维、聚对苯撑苯并双噁唑纤维、聚苯并咪唑纤维、聚四氟乙烯纤维、聚酰亚胺纤维、芳纶中的一种或多种的混合纱；所述的芯线为两根股线，芯线加捻后将羽纱夹在两根芯线中间。
2.根据权利要求1所述的芳族聚酰胺纤维雪尼尔纱线，其特征在于：所述芯线的材质为石英玻璃纤维、高硅氧玻璃纤维、硅酸铝纤维、聚酰胺酰亚胺纤维、聚醚醚酮纤维、聚苯硫醚纤维、聚砜基酰胺纤维、聚对苯撑苯并双噁唑纤维、聚苯并咪唑纤维、聚四氟乙烯纤维、聚酰亚胺纤维、芳纶和玄武岩纤维中的一种或多种的混合。
3.根据权利要求1所述的芳族聚酰胺纤维雪尼尔纱线，其特征在于：所述芯线的单纤维截面为圆形、星形、桔瓣形。
4.根据权利要求1所述的芳族聚酰胺纤维雪尼尔纱线，其特征在于：所述芯线的材质为芳族聚酰胺纤维。
5.根据权利要求1所述的芳族聚酰胺纤维雪尼尔纱线，其特征在于：所述羽纱和/或芯线的表面具有热塑性、热固性熔胶的涂层。
6.根据权利要求1所述的芳族聚酰胺纤维雪尼尔纱线，其特征在于：所述芯线的细度为0.01-100Nm。
7.根据权利要求1所述的芳族聚酰胺纤维雪尼尔纱线，其特征在于：所述羽纱的细度为0.01-100Nm。
8.根据权利要求1所述的芳族聚酰胺纤维雪尼尔纱线，其特征在于：所述芯线的加捻捻度为10-1000捻/米。
9.根据权利要求1-8任一所述的芳族聚酰胺纤维雪尼尔纱线，其特征在于：所述羽纱的轴向密度为10-10000根/cm。