CN104828961A - 工业污水处理剂 - Google Patents
工业污水处理剂 Download PDFInfo
- Publication number
- CN104828961A CN104828961A CN201510256013.XA CN201510256013A CN104828961A CN 104828961 A CN104828961 A CN 104828961A CN 201510256013 A CN201510256013 A CN 201510256013A CN 104828961 A CN104828961 A CN 104828961A
- Authority
- CN
- China
- Prior art keywords
- parts
- treating agent
- stirrer
- industrial sewage
- sewage treating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种工业污水处理剂，该工业污水处理剂由以下质量份数的组分组成，茴香醛20～40份、硼酸钠20～40份、蒙脱土10～30份、葡萄糖酸钠15～30份、乙酸锌40～60份、安息香二乙醚10～20份、活性硅藻土20～40份、二甲基二烯丙基氯化铵5～15份、三乙酸铵10～30份和去离子水50～100份。该发明中的污水处理剂，反应速度快，过程中无有毒有害气体产生；反应后的生成物稳定，不会再分解成有毒物质；高效、无毒，反应前后对人体安全，对设备无腐蚀；使用方法简便不改动工艺流程，无需增加设备和附加材料，污水处理效果明显，使用方便。
Description
技术领域
本发明涉及一种工业污水处理剂，属于污水处理技术领域。
背景技术
当前，环境保护已成为世界关注的问题，工业污水的排放要求严格，国家采取了
相应的强制措施，寻求一种有效的污水处理剂，能够使污水处理后能达到污水排放要求，是众多企业急需解决的难题。污水处理技术对节水、节能等问题具有十分重要的作用，但同时污水处理药剂的使用过程中也给环境造成一定的影响。科学利用水处理药剂可有效防腐蚀和防止结垢，从而提高设备及水的利用率而达到节约水源和能源的目的。
发明内容
本发明的目的在于提供一种工业污水处理剂及其制备方法，该污水处理剂高效、无毒，对设备无腐蚀，该污水处理剂的制备方法简单。
为了实现上述目的，本发明的技术方案如下。
一种工业污水处理剂，由以下质量份数的组分组成，茴香醛20～40份、硼酸钠20～40份、蒙脱土10～30份、葡萄糖酸钠15～30份、乙酸锌40～60份、安息香二乙醚10～20份、活性硅藻土20～40份、二甲基二烯丙基氯化铵5～15份、三乙酸铵10～30份和去离子水50～100份。
本发明所述的工业污水处理剂的制备方法，采用如下步骤：
（1）按照上述质量份数量取原材料，清洗处理物料混合制备搅拌机，加入二次去离子水；
（2）将硼酸钠、活性硅藻土和二甲基二烯丙基氯化铵缓慢加入物料混合制备搅拌机内，记录搅拌时间，从开启物料混合制备搅拌机到投料结束所需时间为10～20分钟；
（3）将茴香醛、安息香二乙醚和三乙酸铵缓慢加入物料混合制备搅拌机内搅拌；
（4）常压下缓慢投入原料蒙脱土，温度小于70℃，直至加料结束，整个过程在60分钟内完成；
（5）常压下缓慢投入葡萄糖酸钠和乙酸锌，温度小于60℃，直至加料结束，整个过程在60分钟内完成，pH控制在6～8之间，停止物料混合制备搅拌机，即得本品。
本发明中，茴香醛具有持久的山楂香气，在山楂花、葵花、紫丁香香精中作主体香料；在铃兰香精中作香剂；在桂花香精中作修饰剂，也可用于日用香精和食品香精。硼酸钠主要用于玻璃和搪瓷工业中，可增强玻璃的紫外线透射率，提高玻璃的透明度和耐热性能，使瓷釉不易脱落且具有光泽。此外，在有色金属焊接，丝、毛织品洗涤，延迟橡胶硫化速度,织物防水、木材防腐,医用消毒以及制革、造纸等方面也有应用。硼酸可改善玻璃制品的耐热和透明性能，能提高机械强度，缩短熔融时间，主要用于制造无碱玻璃、玻璃纤维。此外，还可作防腐消毒剂、熏蒸剂、皮革后处理剂等，也可用于制造防火材料、肥皂、硼钢、陶瓷釉药、染料、颜料。蒙脱土是一类由纳米厚度的表面带负电的硅酸盐片层，依靠层间的静电作用而堆积在一起构成的土状矿物，其晶体结构中的晶胞是由两层硅氧四面体中间夹一层铝氧八面体构成。具有独特的一维层状纳米结构和阳离子交换性特性，从而赋予蒙脱土诸多改性的可能和应用领域的扩大。经改性的蒙脱土具有很强的吸附能力，良好的分散性能。葡萄糖酸钠阻垢能力强：对钙，镁，铁盐具有很强的络合能力，所以阻垢能力很强，特别对Fe3+有极好的螯合作用，甚至在全PH范围内部有作用。安息香乙醚可作光敏剂，主要用于印刷工业制感光树脂板，在涂料工业中配制溶液时用作光敏剂起光固化作用。用于紫外线固化涂料、油墨、胶粘剂等。乙酸锌用于制锌盐、液用作媒染剂、木材防腐剂、试剂等。硅藻土具有孔隙度大、吸收性强、化学性质稳定、耐磨、耐热等特点，能为涂料提供优异的表面性能，增容，增稠以及提高附着力。二甲基二烯丙基氯化铵为高纯度、聚合级、季胺盐、高电荷密度的阳离子单体，含微量氯化钠和其他杂质。在水处理过程中可用于脱色、絮凝和净化，高效而无毒。三乙醇胺的碱性比氨弱，具有叔胺和醇的性质。与有机酸反应低温时生成盐，高温时生成酯。与多种金属生成2～4个配位体的螯合物。
该发明的有益效果在于：该发明中的污水处理剂，反应速度快，过程中无有毒有害气体产生；反应后的生成物稳定，不会再分解成有毒物质；高效、无毒，反应前后对人体安全，对设备无腐蚀；使用方法简便不改动工艺流程，无需增加设备和附加材料，污水处理效果明显，使用方便。
具体实施方式
下面结合实施例对本发明的具体实施方式进行描述，以便更好的理解本发明。
实施例1
本实施例中的工业污水处理剂，由以下质量份数的组分组成，茴香醛20份、硼酸钠20份、蒙脱土10份、葡萄糖酸钠15份、乙酸锌40份、安息香二乙醚10份、活性硅藻土20份、二甲基二烯丙基氯化铵5份、三乙酸铵10份和去离子水50份。
本实施例所述的工业污水处理剂的制备方法，采用如下步骤：
（1）按照上述质量份数量取原材料，清洗处理物料混合制备搅拌机，加入二次去离子水；
（2）将硼酸钠、活性硅藻土和二甲基二烯丙基氯化铵缓慢加入物料混合制备搅拌机内，记录搅拌时间，从开启物料混合制备搅拌机到投料结束所需时间为10分钟；
（3）将茴香醛、安息香二乙醚和三乙酸铵缓慢加入物料混合制备搅拌机内搅拌；
（4）常压下缓慢投入原料蒙脱土，温度小于70℃，直至加料结束，整个过程在60分钟内完成；
（5）常压下缓慢投入葡萄糖酸钠和乙酸锌，温度小于60℃，直至加料结束，整个过程在60分钟内完成，pH控制在6左右，停止物料混合制备搅拌机，即得本品。
利用本实施例中的污水处理剂，分别针对处理前的废水和和处理后固液分离出的清水检测COD、BOD、和SS(水质中的悬浮物)，并检测总氮、总磷和氨氮含量，结果如下：
COD和BOD分别由初始的12000mg/L和3790mg/L下降到1250mg/L和280mg/L；SS由初始的3486mg/L下降到360mg/L；总氮含量由78.5mg/L下降至30mg/L，总磷含量由12.1mg/L下降至1.8mg/L，氨氮含量由16.6mg/L下降至8.5mg/L。
表观效果测定：处理前废水色度为2200倍，处理后的清水色度小于35倍；相比于处理前废水，处理后的清水的恶臭气味明显减轻；处理前废水色度为120倍，处理后的清水色度下降到26倍；处理前废水浊度为268NTU，处理后的清水浊度下降到24NTU。
实施例2
本实施例中的工业污水处理剂，由以下质量份数的组分组成，茴香醛30份、硼酸钠30份、蒙脱土20份、葡萄糖酸钠18份、乙酸锌50份、安息香二乙醚15份、活性硅藻土30份、二甲基二烯丙基氯化铵10份、三乙酸铵20份和去离子水80份。
本发明所述的工业污水处理剂的制备方法，采用如下步骤：
（1）按照上述质量份数量取原材料，清洗处理物料混合制备搅拌机，加入二次去离子水；
（2）将硼酸钠、活性硅藻土和二甲基二烯丙基氯化铵缓慢加入物料混合制备搅拌机内，记录搅拌时间，从开启物料混合制备搅拌机到投料结束所需时间为15分钟；
（3）将茴香醛、安息香二乙醚和三乙酸铵缓慢加入物料混合制备搅拌机内搅拌；
（4）常压下缓慢投入原料蒙脱土，温度小于70℃，直至加料结束，整个过程在60分钟内完成；
（5）常压下缓慢投入葡萄糖酸钠和乙酸锌，温度小于60℃，直至加料结束，整个过程在60分钟内完成，pH控制在7左右，停止物料混合制备搅拌机，即得本品。
利用本实施例中的污水处理剂，分别针对处理前的废水和和处理后固液分离出的清水检测COD、BOD、和SS(水质中的悬浮物)，并检测总氮、总磷和氨氮含量，结果如下：
COD和BOD分别由初始的11000mg/L和3390mg/L下降到1200mg/L和220mg/L；SS由初始的3666mg/L下降到355mg/L；总氮含量79.5mg/L下降至27mg/L，总磷含量由11.8mg/L下降至1.8mg/L，氨氮含量由27.6mg/L下降至10.5mg/L。
表观效果测定：处理前废水色度为2200倍，处理后的清水色度小于45倍；相比于处理前废水，处理后的清水的恶臭气味明显减轻；处理前废水色度为115倍，处理后的清水色度下降到28倍；处理前废水浊度为278NTU，处理后的清水浊度下降到48NTU。
实施例3
本实施例中的工业污水处理剂，由以下质量份数的组分组成，茴香醛40份、硼酸钠40份、蒙脱土30份、葡萄糖酸钠30份、乙酸锌60份、安息香二乙醚20份、活性硅藻土40份、二甲基二烯丙基氯化铵15份、三乙酸铵30份和去离子水100份。
本发明所述的工业污水处理剂的制备方法，采用如下步骤：
（1）按照上述质量份数量取原材料，清洗处理物料混合制备搅拌机，加入二次去离子水；
（2）将硼酸钠、活性硅藻土和二甲基二烯丙基氯化铵缓慢加入物料混合制备搅拌机内，记录搅拌时间，从开启物料混合制备搅拌机到投料结束所需时间为20分钟；
（3）将茴香醛、安息香二乙醚和三乙酸铵缓慢加入物料混合制备搅拌机内搅拌；
（4）常压下缓慢投入原料蒙脱土，温度小于70℃，直至加料结束，整个过程在60分钟内完成；
（5）常压下缓慢投入葡萄糖酸钠和乙酸锌，温度小于60℃，直至加料结束，整个过程在60分钟内完成，pH控制在8左右，停止物料混合制备搅拌机，即得本品。
利用本实施例中的污水处理剂，分别针对处理前的废水和和处理后固液分离出的清水检测COD、BOD、和SS(水质中的悬浮物)，并检测总氮、总磷和氨氮含量，结果如下：
COD和BOD分别由初始的13000mg/L和3890mg/L下降到1020mg/L和270mg/L；SS由初始的3696mg/L下降到350mg/L；总氮含量由65.5mg/L下降至24mg/L，总磷含量由18.1mg/L下降至3.8mg/L，氨氮含量由18.6mg/L下降至7.3mg/L。
表观效果测定：处理前废水色度为2400倍，处理后的清水色度小于34倍；相比于处理前废水，处理后的清水的恶臭气味明显减轻；处理前废水色度为135倍，处理后的清水色度下降到25倍；处理前废水浊度为468NTU，处理后的清水浊度下降到58NTU。
以上所述是本发明的优选实施方式，应当指出，对于本技术领域的普通技术人员来说，在不脱离本发明原理的前提下，还可以做出若干改进和润饰，这些改进和润饰也视为本发明的保护范围。
Claims (2)
1.一种工业污水处理剂，其特征在于：由以下质量份数的组分组成，茴香醛20～40份、硼酸钠20～40份、蒙脱土10～30份、葡萄糖酸钠15～30份、乙酸锌40～60份、安息香二乙醚10～20份、活性硅藻土20～40份、二甲基二烯丙基氯化铵5～15份、三乙酸铵10～30份和去离子水50～100份。
2.根据权利要求1所述的工业污水处理剂，其特征在于：其制备方法采用如下步骤：
（1）按照上述质量份数量取原材料，清洗处理物料混合制备搅拌机，加入二次去离子水；
（2）将硼酸钠、活性硅藻土和二甲基二烯丙基氯化铵缓慢加入物料混合制备搅拌机内，记录搅拌时间，从开启物料混合制备搅拌机到投料结束所需时间约为10～20分钟；
（3）将茴香醛、安息香二乙醚和三乙酸铵缓慢加入物料混合制备搅拌机内搅拌；
（4）常压下缓慢投入原料蒙脱土，温度约小于70℃，直至加料结束，整个过程在约60分钟内完成；
（5）常压下缓慢投入葡萄糖酸钠和乙酸锌，温度约小于60℃，直至加料结束，整个过程在60分钟内完成，pH控制在约6～8之间，停止物料混合制备搅拌机，即得本品。