CN104817802B - A kind of high grip rubber soles and preparation method thereof - Google Patents
A kind of high grip rubber soles and preparation method thereof Download PDFInfo
- Publication number
- CN104817802B CN104817802B CN201510166165.0A CN201510166165A CN104817802B CN 104817802 B CN104817802 B CN 104817802B CN 201510166165 A CN201510166165 A CN 201510166165A CN 104817802 B CN104817802 B CN 104817802B
- Authority
- CN
- China
- Prior art keywords
- parts
- rubber
- high grip
- poly
- sulphur
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention relates to a kind of sole, a kind of rubber soles with high grip and preparation method thereof are provided, the composition of the high grip rubber soles includes natural rubber, poly-norbornene rubber, brombutyl, mineral oil, white carbon, age resistor, polyethylene glycol, silane coupler, Tissuemat E, zinc oxide, sulphur, vulcanization accelerator, above component material is removed into sulphur, sizing material beyond vulcanization accelerator is put into banburying in banbury, 115 120 degree of dumpings, room temperature is placed 24 hours, then kneaded in two-roll mill, and add the sulphur of precise, vulcanization accelerator, after mixing is uniform, with uniform sheet slice, material is finally cut into sole shape and is put into sulfidization molding in rubber boots mould, obtain high grip rubber soles.
Description
Technical field
The invention belongs to organic high molecular compound technical field, more particularly to a kind of high grip rubber soles and its system
Preparation Method.
Background technology
Poly-norbornene rubber, maintains and is all interfixed between twin nuclei, each two adjacent carbon atom, construction unit
In carbon atom activity it is difficult, therefore with higher glass transition temperature and heat decomposition temperature.Poly-norbornene rubber
Molecular structure is mutually tangled between the macromolecular that some segments rely on chemical bond linkage to get up, macromolecular chain, the presence of side chain
Exacerbate mutual entanglement.Certain deformation is produced under external periodic force effect, causes high polymer due to being tangled between strand
During stretching-retraction circulation needs to overcome the frictional resistance between a part of strand, this deformation to lag behind stress,
The form that mechanical energy is changed into heat energy is dissipated, and is further presented as with high coefficient of friction, i.e. high grip.
The content of the invention
It is an object of the invention to provide it is a kind of with earth-grasping force is good, high mechanical strength the features such as high grip rubber boots
Bottom, and prepare the preparation method of foregoing high grip rubber soles.
To achieve the above object, the present invention is adopted the following technical scheme that：A kind of high grip rubber soles, by component material
By natural rubber, poly-norbornene rubber, brombutyl, white carbon, mineral oil, zinc oxide, age resistor, polyethylene glycol,
Silane coupler, Tissuemat E, sulphur, vulcanization accelerator are prepared from.
Wherein：A kind of each component material of high grip rubber soles is expressed as by weight：
Further, the parts by weight of each component material are preferably：
Wherein, the poly-norbornene rubber is poly-norbornene rubber of the molecular weight in 2,000,000-500 ten thousand dalton.
Wherein, the brominated amount of the brombutyl is more than 1.5%.
A kind of preparation method for preparing foregoing high grip rubber soles, natural rubber, poly- drop are weighed according to formula rate
Norbornene rubber, brombutyl, white carbon, mineral oil, zinc oxide, age resistor, polyethylene glycol, silane coupler, poly- second
Alkene wax, sulphur, vulcanization accelerator, banburying in banbury is put into by sizing material of the component material in addition to sulphur, vulcanization accelerator,
110-120 degree dumpings, room temperature is placed 24 hours, is then kneaded in two-roll mill, and adds the sulphur of precise, vulcanization
Accelerator, after mixing is uniform, with uniform sheet slice, is finally cut into sole shape by material and is put into rubber boots mould and be sulfided into
Type, that is, obtain high grip rubber soles.
By taking preceding solution, the present invention has the advantages that：
1, significantly, it is superior to be embodied in anti-skid property of soles for the effects of high grip rubber soles of the present invention, dry type, wet
The on-slip coefficient of formula is up to 1.17,0.70 respectively, hence it is evident that better than the Antiskid sole of prior art.Because polynorbornene rubber
The distribution of trans base forms the high resistance of intermolecular movement in plastic structure, with high coefficient of friction.
2. the material of main part of high-damping expanded material of the present invention is poly-norbornene rubber, with surface porosity, extremely strong
The features such as absorption affinity and hydrocarbon have high affinity, can add substantial amounts of filling oil without influenceing other physical property, carry
High process operation performance, and reduce production cost.
Embodiment
In conjunction with specific embodiment, the present invention is further described.
Embodiment 1：
In the present embodiment, a kind of high grip rubber soles are made up of by weight following components：
Sizing material of the component material in addition to sulphur, vulcanization accelerator is put into banburying in banbury, 119 degree of dumpings, room temperature
Place 24 hours, then kneaded in two-roll mill, and add the sulphur of precise, vulcanization accelerator, after mixing is uniform,
With uniform sheet slice, material is finally cut into sole shape and is put into sulfidization molding in rubber boots mould, that is, obtains high grip rubber
Rubber sole.
A kind of above-mentioned high grip rubber soles prepared, density 1.08g/cm3, hardness A 62, DIN is wear-resisting
143mm3, tensile strength 18.2MPa, tearing strength 75N/mm, the half sole 1.01 smooth 1.17 of on-slip coefficient dry type heel 1.04, only
The sliding half sole 0.66 smooth 0.70 of coefficient wet type heel 0.66, the wet ice face of on-slip coefficient smooth 0.30.
Embodiment 2：
In the present embodiment, a kind of preparation method of high grip rubber soles substantially with the preparation method phase in embodiment 1
Together, except that：
55 parts of poly-norbornene rubber, 8 parts of brombutyl, 25 parts of white carbon, 25 parts of mineral oil, 2 parts of polyethylene glycol,
2 parts of silane coupler.
A kind of above-mentioned high grip rubber soles prepared, density 1.06g/cm3, hardness A 59, DIN is wear-resisting
167mm3, tensile strength 19.3MPa, tearing strength 79N/mm, the half sole 1.02 smooth 1.06 of on-slip coefficient dry type heel 1.02, only
The sliding half sole 0.62 smooth 0.65 of coefficient wet type heel 0.63, the wet ice face of on-slip coefficient smooth 0.24.
Embodiment 3：
In the present embodiment, a kind of preparation method of high grip rubber soles substantially with the preparation method phase in embodiment 1
Together, except that：
45 parts of poly-norbornene rubber, 12 parts of brombutyl, 35 parts of white carbon, 35 parts of mineral oil, polyethylene glycol 4
Part, 3 parts of silane coupler；Control is in 120 degree of dumpings.
A kind of above-mentioned high grip rubber soles prepared, density 1.16g/cm3, hardness A 69, DIN is wear-resisting
231mm3, tensile strength 15.8MPa, tearing strength 57N/mm, the half sole 0.91 smooth 0.96 of on-slip coefficient dry type heel 0.96, only
The sliding half sole 0.48 smooth 0.52 of coefficient wet type heel 0.49, the wet ice face of on-slip coefficient smooth 0.16.
Embodiment 4：
In the present embodiment, a kind of preparation method of high grip rubber soles substantially with the preparation method phase in embodiment 1
Together, except that：
40 parts of poly-norbornene rubber, 15 parts of brombutyl, 35 parts of white carbon, 25 parts of mineral oil.
A kind of above-mentioned high grip rubber soles prepared, density 1.19g/cm3, hardness A 65, DIN is wear-resisting
287mm3, tensile strength 14MPa, tearing strength 49N/mm, the half sole 0.84 smooth 0.88 of on-slip coefficient dry type heel 0.83, on-slip
The half sole 0.48 smooth 0.49 of coefficient wet type heel 0.47, the wet ice face of on-slip coefficient smooth 0.11.
After the data preparation of above-described embodiment 1~4, obtain such as table 1 below (note：Hardness is measured using GS-706G hardness
Examination, DIN it is wear-resisting according to GB/T 9867-2008 test, tensile strength according to GB/T 528-2009 test, tearing strength according to
GB/T 529-2008 test right-angle tearing test piece, and on-slip coefficient is according to TM144：2011 tests)：
The performance parameter table of comparisons of high grip rubber soles prepared by table 1, embodiment 1~4
In summary, according to high grip rubber soles made from the preparation method of the high grip rubber soles of the present invention
With earth-grasping force is good, high mechanical strength the features such as, be particularly suitable for applying in terms of sole.
Described above, only using the embodiment of this origination techniques content, any those skilled in the art use this wound
Make done modifications and changes, all belong to the scope of the claims of this creation opinion, and be not limited to those disclosed embodiments.
Claims (5)
1. a kind of high grip rubber soles, it is characterised in that be made up of following raw materials according：
15 parts of natural rubber
40-55 parts of poly-norbornene rubber
8-15 parts of brombutyl
25-35 parts of white carbon
25-35 parts of mineral oil
1-3 part of zinc oxide
1-2 part of age resistor
2-4 parts of polyethylene glycol
2-3 parts of silane coupler
2-3 parts of Tissuemat E
2-3 parts of sulphur
2-3 parts of vulcanization accelerator.
2. high grip rubber soles according to claim 1, it is characterised in that the parts by weight of each raw material are：
15 parts of natural rubber
50 parts of poly-norbornene rubber
10 parts of brombutyl
30 parts of white carbon
30 parts of mineral oil
1 part of zinc oxide
1.5 parts of age resistor
3 parts of polyethylene glycol
3 parts of silane coupler
2 parts of Tissuemat E
2 parts of sulphur
2.2 parts of vulcanization accelerator.
3. high grip rubber soles according to claim 1, it is characterised in that：Poly-norbornene rubber is that molecular weight exists
The poly-norbornene rubber of 2000000-500 ten thousand dalton.
4. high grip rubber soles according to claim 1, it is characterised in that：The brominated amount of the brombutyl is big
In 1.5%.
5. a kind of preparation method for preparing any high grip rubber soles of claim 1-4, it is characterised in that：First by day
Right rubber, poly-norbornene rubber, brombutyl, white carbon, mineral oil, zinc oxide, age resistor, polyethylene glycol, silane
Coupling agent, Tissuemat E are put into banburying in banbury, and 115-120 degree dumpings, room temperature is placed 24 hours, then in two-roll mill
Upper mixing, and the sulphur of precise, vulcanization accelerator are added, after mixing is uniform, with uniform sheet slice, finally material is cut out
Sulfidization molding in rubber boots mould is put into sole shape, that is, obtains high grip rubber soles.