CN104556958A - 一种抗裂防渗加气砌块及其制备方法 - Google Patents
一种抗裂防渗加气砌块及其制备方法 Download PDFInfo
- Publication number
- CN104556958A CN104556958A CN201410792172.7A CN201410792172A CN104556958A CN 104556958 A CN104556958 A CN 104556958A CN 201410792172 A CN201410792172 A CN 201410792172A CN 104556958 A CN104556958 A CN 104556958A
- Authority
- CN
- China
- Prior art keywords
- parts
- aluminium powder
- powder
- sodium
- modified aluminium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种抗裂防渗加气砌块及其制备方法，其由以下重量份的原料制成：硅灰石34-48、黄泥粉16-24、白云石27-35、粉煤灰？21-29、废砂浆14-22、高炉矿渣10-15、玉米糊精粉4-6、葡萄糖酸钙？3-5、硅藻土12-16、剑麻短纤维5-10、硼酸镁晶须4-8、石油沥青2-3、硬脂酸锌1-2、油酸铝1-2、聚丙烯酸钠3-6、改性铝粉？0.5-1。本发明加气砌块不仅具有优异的耐水性和抗渗性，还具有较高的抗压强度和抗弯折强度，使用寿命长，应用范围广，市场前景广阔。
Description
技术领域
本发明涉及一种抗裂防渗加气砌块及其制备方法，属于建筑材料领域。
背景技术
加气砌块是以硅质材料（砂、粉煤灰及含硅尾矿等）和钙质材料（石灰、水泥等）为主要原料，掺加发气剂（铝粉），经加水搅拌，由化学反应形成孔隙，通过浇注成型、预养切割、蒸压养护等工艺过程制成的多孔硅酸盐制品。加气砌块具有质轻、保温隔热、可加工性好、原料来源广、生产效率高、生产能耗低等特点，广泛应用于工业和民用建筑的承重或围护、填充等，受到世界各国的普遍重视，成为许多国家大力推广和发展的优选建筑材料。随着我国建筑行业的快速发展，对加气砌块的抗裂、防渗等性能要求越来越高，然而传统加气砌块的抗裂防渗性能已无法满足市场需求，因此，急需开发一种抗裂防渗加气砌块。
发明内容
本发明的目的在于提供一种抗裂防渗加气砌块及其制备方法。
为实现上述目的，本发明采用如下技术方案：
一种抗裂防渗加气砌块，由以下重量份的原料制成：硅灰石34-48、黄泥粉16-24、白云石27-35、粉煤灰 21-29、废砂浆 14-22、高炉矿渣10-15、玉米糊精粉 4-6、葡萄糖酸钙 3-5、硅藻土12-16、剑麻短纤维5-10、硼酸镁晶须4-8、石油沥青2-3、硬脂酸锌1-2、油酸铝1-2、聚丙烯酸钠 3-6、改性铝粉 0.5-1；
所述改性铝粉的制备方法如下：（a）、取以下重量份的原料：活性铝粉60-80、亚甲基二萘磺酸钠3-6、椰油酰胺丙基甜菜碱2-4、十四烷基二甲基氧化胺1.5-2.5、十二烷基苯磺酸钠4.5-6.5、月桂酰二乙醇胺4-7、松香酸钠5-8、鲸蜡硬脂基葡糖苷2-4、茶皂素1-3；（b）、取铝粉加适量的水，搅拌制成浓度为50-60%的浆液，然后加入亚甲基二萘磺酸钠、椰油酰胺丙基甜菜碱、十四烷基二甲基氧化胺和十二烷基苯磺酸钠，在50-80r/min的转速下搅拌1-2h，抽滤，烘干；（c）、取1/3-1/2量的上述烘干的铝粉与月桂酰二乙醇胺、茶皂素混合，在40-60r/min的转速下搅拌2-3h，得改性铝粉A；（d）、取余下的铝粉与松香酸钠、鲸蜡硬脂基葡糖苷混合，在30-50r/min的转速下搅拌3-4h，得改性铝粉B；（e）、将改性铝粉A和改性铝粉B混合均匀，即得所需的改性铝粉。
上述改性铝粉采用传统铝粉与月桂酰二乙醇胺、松香酸钠、鲸蜡硬脂基葡糖苷、茶皂素等多种原料复合，能显著增加料浆稠度,大幅度提高铝粉的发气效率，有效解决了传统铝粉发气剂发气效率低的缺点。
一种抗裂防渗加气砌块的制备方法，由下列步骤组成：
（1）取硅灰石、白云石、高炉矿渣混合均匀，粉碎，过250-300目筛，加水使得混合料的含水量控制在45-50%，然后加入葡萄糖酸钙、聚丙烯酸钠、油酸铝，900-1400rpm研磨8-12min后加入黄泥粉、粉煤灰、废砂浆、玉米糊精粉、硅藻土、剑麻短纤维、硼酸镁晶须、石油沥青、硬脂酸锌，搅拌均匀后再调整混合料的含水量至65-75%，1000-1500rpm搅拌2-5min；
（2）将改性铝粉加入步骤（1）制得的浆料中，搅拌均匀后在50-60℃温度下发泡30-40min；
（3）将步骤（2）得到的发泡浆料注入成型模具中，自然养护35-45h，拆模，得生坯；
（4）将步骤（3）得到的生坯在温度为60-70℃、压力为0.4-0.7MPa的条件下蒸汽养护16-22h，即得加气砌块成品。
本发明的有益效果：
本发明加气砌块不仅具有优异的耐水性和抗渗性，还具有较高的抗压强度和抗弯折强度，使用寿命长，应用范围广，市场前景广阔。
具体实施方式
一种抗裂防渗加气砌块，由以下重量（kg）的原料制成：硅灰石42、黄泥粉22、白云石30、粉煤灰 25、废砂浆 18、高炉矿渣12、玉米糊精粉 5、葡萄糖酸钙 4、硅藻土14、剑麻短纤维7、硼酸镁晶须6、石油沥青2.5、硬脂酸锌1.5、油酸铝1、聚丙烯酸钠 4.5、改性铝粉 0.8；
所述改性铝粉的制备方法如下：（a）、取以下重量（kg)的原料：活性铝粉80、亚甲基二萘磺酸钠6、椰油酰胺丙基甜菜碱4、十四烷基二甲基氧化胺2.5、十二烷基苯磺酸钠-6.5、月桂酰二乙醇胺7、松香酸钠8、鲸蜡硬脂基葡糖苷4、茶皂素3；（b）、取铝粉加适量的水，搅拌制成浓度为60%的浆液，然后加入亚甲基二萘磺酸钠、椰油酰胺丙基甜菜碱、十四烷基二甲基氧化胺和十二烷基苯磺酸钠，在80r/min的转速下搅拌1h，抽滤，烘干；（c）、取1/2量的上述烘干的铝粉与月桂酰二乙醇胺、茶皂素混合，在60r/min的转速下搅拌2h，得改性铝粉A；（d）、取余下的铝粉与松香酸钠、鲸蜡硬脂基葡糖苷混合，在50r/min的转速下搅拌3h，得改性铝粉B；（e）、将改性铝粉A和改性铝粉B混合均匀，即得所需的改性铝粉。
一种抗裂防渗加气砌块的制备方法，由下列步骤组成：
（1）取硅灰石、白云石、高炉矿渣混合均匀，粉碎，过300目筛，加水使得混合料的含水量控制在50%，然后加入葡萄糖酸钙、聚丙烯酸钠、油酸铝，1400rpm研磨8min后加入黄泥粉、粉煤灰、废砂浆、玉米糊精粉、硅藻土、剑麻短纤维、硼酸镁晶须、石油沥青、硬脂酸锌，搅拌均匀后再调整混合料的含水量至75%，1500rpm搅拌3min；
（2）将改性铝粉加入步骤（1）制得的浆料中，搅拌均匀后在60℃温度下发泡30min；
（3）将步骤（2）得到的发泡浆料注入成型模具中，自然养护45h，拆模，得生坯；
（4）将步骤（3）得到的生坯在温度为70℃、压力为0.7MPa的条件下蒸汽养护16h，即得加气砌块成品。
上述实施例制得的加气砌块的的主要性能检测见下表：
| 项目 | 单位 | 检测结果 |
| 常温耐压强度 | Mpa | 5.7 |
| 干燥收缩值 | mm/m | 0.4 |
| 导热系数 | W/m.K | 0.16 |
| 吸水率 | % | 1.5 |
Claims (2)
1.一种抗裂防渗加气砌块，其特征在于，由以下重量份的原料制成：硅灰石34-48、黄泥粉16-24、白云石27-35、粉煤灰 21-29、废砂浆 14-22、高炉矿渣10-15、玉米糊精粉 4-6、葡萄糖酸钙 3-5、硅藻土12-16、剑麻短纤维5-10、硼酸镁晶须4-8、石油沥青2-3、硬脂酸锌1-2、油酸铝1-2、聚丙烯酸钠 3-6、改性铝粉 0.5-1；
所述改性铝粉的制备方法如下：（a）、取以下重量份的原料：活性铝粉60-80、亚甲基二萘磺酸钠3-6、椰油酰胺丙基甜菜碱2-4、十四烷基二甲基氧化胺1.5-2.5、十二烷基苯磺酸钠4.5-6.5、月桂酰二乙醇胺4-7、松香酸钠5-8、鲸蜡硬脂基葡糖苷2-4、茶皂素1-3；（b）、取铝粉加适量的水，搅拌制成浓度为50-60%的浆液，然后加入亚甲基二萘磺酸钠、椰油酰胺丙基甜菜碱、十四烷基二甲基氧化胺和十二烷基苯磺酸钠，在50-80r/min的转速下搅拌1-2h，抽滤，烘干；（c）、取1/3-1/2量的上述烘干的铝粉与月桂酰二乙醇胺、茶皂素混合，在40-60r/min的转速下搅拌2-3h，得改性铝粉A；（d）、取余下的铝粉与松香酸钠、鲸蜡硬脂基葡糖苷混合，在30-50r/min的转速下搅拌3-4h，得改性铝粉B；（e）、将改性铝粉A和改性铝粉B混合均匀，即得所需的改性铝粉。
2.根据权利要求1所述的抗裂防渗加气砌块的制备方法，其特征在于，由下列步骤组成：
（1）取硅灰石、白云石、高炉矿渣混合均匀，粉碎，过250-300目筛，加水使得混合料的含水量控制在45-50%，然后加入葡萄糖酸钙、聚丙烯酸钠、油酸铝，900-1400rpm研磨8-12min后加入黄泥粉、粉煤灰、废砂浆、玉米糊精粉、硅藻土、剑麻短纤维、硼酸镁晶须、石油沥青、硬脂酸锌，搅拌均匀后再调整混合料的含水量至65-75%，1000-1500rpm搅拌2-5min；
（2）将改性铝粉加入步骤（1）制得的浆料中，搅拌均匀后在50-60℃温度下发泡30-40min；
（3）将步骤（2）得到的发泡浆料注入成型模具中，自然养护35-45h，拆模，得生坯；
（4）将步骤（3）得到的生坯在温度为60-70℃、压力为0.4-0.7MPa的条件下蒸汽养护16-22h，即得加气砌块成品。