CN104387903A - 一种环氧聚酯水性涂料及其制备方法 - Google Patents
一种环氧聚酯水性涂料及其制备方法 Download PDFInfo
- Publication number
- CN104387903A CN104387903A CN201410621311.XA CN201410621311A CN104387903A CN 104387903 A CN104387903 A CN 104387903A CN 201410621311 A CN201410621311 A CN 201410621311A CN 104387903 A CN104387903 A CN 104387903A
- Authority
- CN
- China
- Prior art keywords
- parts
- epoxy polyester
- water
- epoxy
- raw material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种环氧聚酯水性涂料，涉及建筑装饰材料技术领域，由以下组分的原料组成：环氧聚酯树脂30-40份、触变剂5-6份、氨基树脂10-20份、甲基溶纤剂7-8份、颜料6-8份、促进剂2-3份、蒸馏水15-25份。本发明的有益效果是：本发明制备方便简单，原料易得，设备投资少，便于操作，制备的环氧聚酯水性涂料，环保无污染，纯度高，附着力强，使用效果明显，安全可靠。
Description
技术领域
本发明涉及建筑装饰材料技术领域，具体涉及一种环氧聚酯水性涂料及其制备方法。
背景技术
涂料是一种能牢固覆盖在物体表面，起保护、装饰、标志和其他特殊用途的化学混合物涂料，包含更多的科技成分，在现代科技和工业领域应用广泛。但是涂料有一些顺口习惯性称呼还是保留下来，如乳胶漆、底漆、面漆等。一般而言，涂料就是能够涂覆在被涂物件表面并能形成牢固附着的连续薄膜的材料。它既可以是无机的，如电镀铜，电镀镍，电镀锌等。也可以是有机的，如大多数的有机高分子材料，有机高分子材料构成了当今涂料市场主要部分，油漆的种类繁多，不同的领域所使用的油漆，种类也不尽相同，水性涂料是相对使用比较广泛的油漆，产量需求比较大，但是市面上的地坪漆工艺配方还是相对比较传统，并不能符合目前市面的需求。
发明内容
本发明所要解决的技术问题在于提供一种无毒无害，环保健康，制备工艺简单的环氧聚酯水性涂料及其制备方法。
本发明所要解决的技术问题采用以下技术方案来实现：
一种环氧聚酯水性涂料，其特征在于，由以下组分的原料组成：
环氧聚酯树脂30-40份、触变剂5-6份、氨基树脂10-20份、甲基溶纤剂7-8份、颜料6-8份、促进剂2-3份、蒸馏水15-25份。
各原料的优选分量为：
环氧聚酯树脂35份、触变剂5.5份、氨基树脂15份、甲基溶纤剂7.5份、颜料7份、促进剂2.5份、蒸馏水20份。
所述的环氧聚酯树脂包括的原料有：多元醇20-30份、多元酸35-45份、二甲苯10-20份、乙二醇醚80-120份、环氧树脂100-200份，去离子水100-150份；
制备方法为：选用一反应釜，将多元醇，多元酸和二甲苯加入其中，升温至150-220℃，进行搅拌，当酸值达到10-50mgKOH/g后，加入环氧树脂和乙二醇醚，进行改性反应后，加入去离子水搅拌均匀后，出料、过滤即可。
所述的触变剂为膨润土，所述的促进剂为三乙醇胺，所述的颜料为钛白粉。
本发明的另一目的是制备本发明环氧聚酯水性涂料的制备方法，其特征在于：包括以下工艺步骤，
a、选用一洁净的调漆罐，将原料中的环氧聚酯树脂、甲基溶纤剂、蒸馏水、颜料、促进剂全部加入其中，搅拌均匀；
b、待上述步骤a搅拌结束后，将原料中的触变剂和氨基树脂加入其中，搅拌均匀后，全部投入砂磨机中进行砂磨至颗粒细度为30-40um后即可出料，包装入库。
本发明的有益效果是：本发明制备方便简单，原料易得，设备投资少，便于操作，制备的环氧聚酯水性涂料，环保无污染，纯度高，附着力强，使用效果明显，安全可靠。
具体实施方式
为了使本发明实现的技术手段、创作特征、达成目的与功效易于明白了解，下面结合具体实施例，进一步阐述本发明。
实施例1
一种环氧聚酯水性涂料，由以下组分的原料组成：
环氧聚酯树脂30kg、膨润土5kg、氨基树脂10kg、甲基溶纤剂7kg、钛白粉6kg、三乙醇胺2kg、蒸馏水15kg。
所述的环氧聚酯树脂包括的原料有：多元醇20kg、多元酸35kg、二甲苯10kg、乙二醇醚80kg、环氧树脂100kg，去离子水100kg；
制备方法为：选用一反应釜，将多元醇，多元酸和二甲苯加入其中，升温至150-220℃，进行搅拌，当酸值达到10-50mgKOH/g后，加入环氧树脂和乙二醇醚，进行改性反应后，加入去离子水搅拌均匀后，出料、过滤即可。
本发明的另一目的是制备本发明环氧聚酯水性涂料的制备方法，包括以下工艺步骤，
a、选用一洁净的调漆罐，将原料中的环氧聚酯树脂、甲基溶纤剂、蒸馏水、钛白粉、三乙醇胺全部加入其中，搅拌均匀；
b、待上述步骤a搅拌结束后，将原料中的膨润土和氨基树脂加入其中，搅拌均匀后，全部投入砂磨机中进行砂磨至颗粒细度为30-40um后即可出料，包装入库。
实施例2
一种环氧聚酯水性涂料，由以下组分的原料组成：
环氧聚酯树脂35kg、膨润土5.5kg、氨基树脂15kg、甲基溶纤剂7.5kg、钛白粉7kg、三乙醇胺2.5kg、蒸馏水20kg。
所述的环氧聚酯树脂包括的原料有：多元醇25kg、多元酸40kg、二甲苯15kg、乙二醇醚100kg、环氧树脂150kg，去离子水125kg；
制备方法为：选用一反应釜，将多元醇，多元酸和二甲苯加入其中，升温至150-220℃，进行搅拌，当酸值达到10-50mgKOH/g后，加入环氧树脂和乙二醇醚，进行改性反应后，加入去离子水搅拌均匀后，出料、过滤即可。
本发明的另一目的是制备本发明环氧聚酯水性涂料的制备方法，包括以下工艺步骤，
a、选用一洁净的调漆罐，将原料中的环氧聚酯树脂、甲基溶纤剂、蒸馏水、钛白粉、三乙醇胺全部加入其中，搅拌均匀；
b、待上述步骤a搅拌结束后，将原料中的膨润土和氨基树脂加入其中，搅拌均匀后，全部投入砂磨机中进行砂磨至颗粒细度为30-40um后即可出料，包装入库。
以上显示和描述了本发明的基本原理和主要特征和本发明的优点。本行业的技术人员应该了解，本发明不受上述实施例的限制，上述实施例和说明书中描述的只是说明本发明的原理，在不脱离本发明精神和范围的前提下，本发明还会有各种变化和改进，这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界定。
Claims (5)
1.一种环氧聚酯水性涂料，其特征在于，由以下组分的原料组成：
环氧聚酯树脂30-40份、触变剂5-6份、氨基树脂10-20份、甲基溶纤剂7-8份、颜料6-8份、促进剂2-3份、蒸馏水15-25份。
2.根据权利要求1所述的环氧聚酯水性涂料，其特征在于：各原料的优选分量为：环氧聚酯树脂35份、触变剂5.5份、氨基树脂15份、甲基溶纤剂7.5份、颜料7份、促进剂2.5份、蒸馏水20份。
3.根据权利要求1所述的环氧聚酯水性涂料，其特征在于：所述的环氧聚酯树脂包括的原料有：多元醇20-30份、多元酸35-45份、二甲苯10-20份、乙二醇醚80-120份、环氧树脂100-200份，去离子水100-150份；
制备方法为：选用一反应釜，将多元醇，多元酸和二甲苯加入其中，升温至150-220℃，进行搅拌，当酸值达到10-50mgKOH/g后，加入环氧树脂和乙二醇醚，进行改性反应后，加入去离子水搅拌均匀后，出料、过滤即可。
4.根据权利要求1所述的环氧聚酯水性涂料，其特征在于：所述的触变剂为膨润土，所述的促进剂为三乙醇胺，所述的颜料为钛白粉。
5.制备权利要求1或2所述的环氧聚酯水性涂料，其特征在于：包括以下步骤，
a、选用一洁净的调漆罐，将原料中的环氧聚酯树脂、甲基溶纤剂、蒸馏水、颜料、促进剂全部加入其中，搅拌均匀；
b、待上述步骤a搅拌结束后，将原料中的触变剂和氨基树脂加入其中，搅拌均匀后，全部投入砂磨机中进行砂磨至颗粒细度为30-40um后即可出料，包装入库。