NL8203164A - PLATE OF PLASTER CARDBOARD. - Google Patents
PLATE OF PLASTER CARDBOARD. Download PDFInfo
- Publication number
- NL8203164A NL8203164A NL8203164A NL8203164A NL8203164A NL 8203164 A NL8203164 A NL 8203164A NL 8203164 A NL8203164 A NL 8203164A NL 8203164 A NL8203164 A NL 8203164A NL 8203164 A NL8203164 A NL 8203164A
- Authority
- NL
- Netherlands
- Prior art keywords
- gypsum
- plate according
- mixture
- inert filler
- semi
- Prior art date
Description
-1- 22614/Vk/mb-1- 22614 / Vk / mb
Korte aanduiding: Plaat van gipskarton.Short designation: Plasterboard board.
De uitvinding heeft betrekking op een plaat van gipskarton vervaardigd uit halfhydraat gips en andere toevoegstoffen.The invention relates to a plasterboard board made from semi-hydrate gypsum and other additives.
5 Het is bekend om gips met diverse stoffen te mengen, waar- bij deze stoffen zuivere vulstoffen zijn of zelf~bardende of verstevi-gende eigenschappen hebben, waarbij in het begin gips als halfhydraat of als halfhydraat mengsel of anhydriet aanwezig kan zijn. aIt is known to mix gypsum with various substances, wherein these substances are pure fillers or have self-balancing or firming properties, in the beginning gypsum may be present as a semi-hydrate or as a semi-hydrate mixture or anhydrite. a
Zo is het bijvoorbeeld bekend om bij het vervaardigen van 10 vloerplaten uit anhydriet, deze stof voor of tijdens de voorbewerking te vervangen door bepaalde organische produkten die door polymerisatie, condensatie of dergelijke tot een kunststofmassa verharden. Deze zelf-hardende mengsels maken echter een verdere verwerking nodig en maken in het algemeen het produkt duurder. In plaats van de dure· organische 15 produkten gebruikt men bij platen voor vloeren ook zand, kwartsmeel, houtmeel, diatomeeenaarde, kalksteenmeel en krijt, waarbij echter een verlaging van de drukvastheid optreedt, zodat men extra lagen moet op-brengen om deze nadelen op te heffen zoals beschreven in het Duitse octrooischrift 825.521.For example, it is known, when manufacturing floor plates from anhydrite, to replace this material before or during the pre-treatment by certain organic products which harden into a plastic mass by polymerization, condensation or the like. However, these self-curing mixtures require further processing and generally make the product more expensive. Instead of the expensive organic products, sanding boards for floors also use sand, quartz flour, wood flour, diatomaceous earth, limestone flour and chalk, but a reduction in the compressive strength occurs, so that additional layers have to be applied to overcome these disadvantages. lifting as described in German Patent 825,521.
20 Verder is het bekend uit het Duitse octrooischrift 03.655 om platen uit gips te verbeteren door hieraan vezelvormige bestanddelen toe te voegen, waarbij aan gips bovendien nog cement kan worden toege-voegd.It is furthermore known from German patent specification 03.655 to improve gypsum plates by adding fibrous constituents thereto, while cement can additionally be added to gypsum.
Uit het Duitse octrooischrift 1258323 is de bereiding 25 bekend van platen uit gipskarton voor de bouwindustrie, waarbij men het gebruik van calciumsulfaatdihydraat afkomstig uit de bereiding van fosforzuur wil verbeteren doordat men het industriele gips brandt op een wijze zoals gebeurt bij de bereiding van halfhydraat uit natuurlijk gips en bij de verwerking hiervan tot een gipsmengsel de pH op een be-30 paalde wijze instelt.German patent 1258323 discloses the preparation of plasterboard boards for the construction industry, in which the use of calcium sulphate dihydrate from the preparation of phosphoric acid is to be improved by burning the industrial gypsum in the manner that is done in the preparation of semi-hydrate from natural gypsum and when processing it into a gypsum mixture adjusts the pH in a certain way.
Ook is het bekend om ter verbetering van de eigenschappen van de platen van gipskarton vooral een waterige en gietbare gipsmassa te bereiden en daarmee een betere verbinding van het halfhydraat mengsel met karton te bereiken waarbij karton als natte vezellaag in de vorm 35 van een natte laag wordt gebruikt en met het gipsmengsel in.verbinding wordt gebracht zodat ook karton in de vorm van een vezelachtige materiaal-band wordt toegevoerd.It is also known to, in order to improve the properties of the plasterboard panels, mainly prepare an aqueous and pourable gypsum mass and thereby achieve a better connection of the semi-hydrate mixture with cardboard, whereby cardboard is used as wet fiber layer in the form of a wet layer. and is brought into contact with the gypsum mixture so that cardboard in the form of a fibrous material belt is also supplied.
8203164 % \ -2- 22614/Vk/mb8203164% \ -2- 22614 / Vk / mb
Bij het vervaardigen van gipsplaten die voorzien zijn van een papieren laag waarbij de gipskern zetmeel bevat, die ten minste op den kant met een papieren deklaag is voorzien, waarbij tussen de gipskern en de deklaag van papier een laag is aangebracht bestaande uit een 5 uitgeharde verknoopte organische waterstofpolysiloxaanverbinding, is het bekend om een tussenlaag toe te passen bereid uit een uitgeharde, waterafstotende organische siliciumverbinding die uit een epoxysilicium, een gepolymeriseerde silaan of een gepolymeriseerd additieprodukt van waterstofsilicium en een vetzure ester bestaat. Deze maatregelen hebben 10 tot doel om de hechting van karton op dekern van gips te verbeteren, het gehalte aan zetmeel in gips te verlagen en de stevigheid hiervan te verbeteren, zoals beschreven in het Duitse octrooischrift 1646797.In the manufacture of gypsum boards which are provided with a paper layer, wherein the gypsum core contains starch, which is at least on the side provided with a paper coating, wherein a layer consisting of a hardened cross-linked is applied between the gypsum core and the covering layer of paper. organic hydrogen polysiloxane compound, it is known to use an intermediate layer prepared from a cured, water-repellent organic silicon compound consisting of an epoxy silicon, a polymerized silane or a polymerized addition product of hydrogen silicon and a fatty acid ester. The purpose of these measures is to improve the adhesion of cardboard to the gypsum core, to decrease the starch content in gypsum and to improve its firmness, as described in German patent 1646797.
Ook heeft men voorgesteld om platen te vervaardigen uit een mengsel van aarde, zand en natriumhydroxide onder toepassing van 15 warmte en druk om zodoende op een rationele wijze platen te vervaardigen die slechts £en hardingstrap omvatten en een hoge stevigheid hebben (Duits Auslegeschrift 2500151),It has also been proposed to prepare plates from a mixture of soil, sand and sodium hydroxide using heat and pressure to thereby rationally produce plates that comprise only one curing step and have a high strength (German Auslegeschrift 2500151),
Ten slotte kan nog worden gewezen op het Duitse Auslege-schrift 2546181, betrekking hebbende op het vervaardigen van bouwelementen, 20 waarbij het gipsmengsel wordt verschuimd, en waarbij in het gipswater-mengsel in aanwezigheid van schuim-stabiliserende toevoegstoffen iso-cyanaatverbindingen en/of polyurethaan-vooraddukt uit overvloedige iso-cyanaatverbindingen met polyester en/of polyether en/of met aminover-bindingen worden gedispergeerd. Men wil zodoende een langzaam verschuir 25 men onder vorming van een lage schuimdruk bereiken en zodoende een langere open verwerkingsduur verkrijgen voor het vervaardigen van het bouwelement, bijvoorbeeld voor het vervaardigen van sandwichplaten.Finally, reference should also be made to German Auslege script 2546181, relating to the production of building elements, in which the gypsum mixture is foamed, and in which the gypsum water mixture in the presence of foam-stabilizing additives contains iso-cyanate compounds and / or polyurethane -adducts are dispersed from abundant isocyanate compounds with polyester and / or polyether and / or with amino compounds. Thus, it is desired to achieve a slow shifting with the formation of a low foam pressure and thus obtain a longer open processing time for manufacturing the building element, for example for manufacturing sandwich plates.
Uit de bovenvermelde stand van de techniek blijkt dat bij het vervaardigen van bouwelementen in de vorm van platen merte vul-30 stoffen, vanwege hetzuivere ballastkarakter en de onvoldoende zijnde eigen hardingseigenschappen als nadelig zijn beschouwd, terwijl de stevigheid en de eenheid van het produkt worden verzwakt. Ook blijkt uit deze stand van de techniek dat men bijna altijd heeft geprobeerd om plaat-vormige bouwelementen te vervaardigen uit gips door menging van zelf-35 hardende organische kunststoffen en deze te verbeteren zelfs bij ge-schuimde of schuimvormige produkten, of door onder mengen toevoegen van vezelvormig materiaal of door een bepaalde voorbewerking en verwerking van de halfhydraatgips.The above-mentioned prior art shows that in the manufacture of building elements in the form of plates, fillers are considered to be disadvantageous due to the pure ballast character and the insufficient self-hardening properties, while the firmness and the unity of the product are weakened. . It also appears from this prior art that almost always attempts have been made to produce plaster board-shaped building elements by mixing and improving self-hardening organic plastics even with foamed or foamed products, or by adding with mixing of fibrous material or by a certain pre-processing and processing of the semi-hydrate gypsum.
8203164 -3- 22614/Vk/mb8203164 -3- 22614 / Vk / mb
Uit Ullmann, Enzyklopadie der technischen Chemie, derde uitgave, band 8, biz. 124, blijkt bijvoorbeeld dat inerte toevoegstoffen de verknoping van de gipskristalletjes storen en dat de stevigheid hiervan evenredig met de concentratie wordt verlaagd. Bij de toevoeging 5 van zandin een hoeveelheid tot 6 gew.delen per gew.deel pleister daalt de stevigheid onder droge omstandigheden tot 1/6-1/7.From Ullmann, Enzyklopadie der technicalen Chemie, third edition, volume 8, biz. 124, it appears, for example, that inert additives interfere with the cross-linking of the gypsum crystals and that their firmness is reduced in proportion to the concentration. When sand is added in an amount of up to 6 parts by weight per part by weight of plaster, the firmness drops to 1 / 6-1 / 7 under dry conditions.
Bovendien zijn gipsmengsels bekend die als vulmassa of * smeermassa worden toegepast, die met m water oplosbare cellulosederivaten en vulstoffen worden gemengd of met bijvoorbeeld een kleigel in een hoe-10 veelheid tot 5 gew.%. Dergelijke massa's worden echter toegepast als pleister- of mortelmassa, maar niet voor het vervaardigen van plaat-vormige bouwelementen (zie Duits Auslegeschrift 2540954 en Duits Offen-legungsschrift 2165221).In addition, gypsum mixtures are known which are used as filler or lubricant, which are mixed with water-soluble cellulose derivatives and fillers or, for example, with a clay gel in an amount of up to 5% by weight. However, such masses are used as plaster or mortar compound, but not for the manufacture of plate-shaped building elements (see German Auslegeschrift 2540954 and German Offenlegungsschrift 2165221).
Verder heeft men geprobeerd om de eigenschappen van gips 15 of van gipsbouwstof daardoor te verbeteren dat men bepaalde brand-, ops lag-, of maalbewerkingen toepaste om aan gips bepaalde eigenschappen te geven met betrekking tot de hardingseigenschappen en de stevigheid.Furthermore, attempts have been made to improve the properties of gypsum 15 or of gypsum building material by applying certain burning, storage or grinding operations to give gypsum certain properties with regard to the curing properties and the strength.
Men had in de gipstechnologie, vooral bij het vervaardigen van platen, de opvatting dat gips indien mogelijk zuiver moest zijn, en 20 daarora zijn ook de.vele in de literatuur bekende voorstellen gedaan om bijvoorbeeld industrieel gips op bijzondere wijze verder te verwerken, in overeenstemming met de verwerking van natuurlijk gipsgesteente .In gypsum technology, especially in the manufacture of plates, the idea was that gypsum should be pure if possible, and for this reason many proposals known in the literature have been made to further process industrial gypsum in a special way, in accordance with with the processing of natural gypsum rock.
Vooral bij de toepassing van gips voor het vervaardigen van platen nit gipskarton heeft de mening zich gevormd dat gips zuiver moet zijn om 25 niet alleen een goede verbinding met karton te verkrijgen, maar ook met betrekking tot de secundaire xivloeden op de plaat van gipskarton zoals met betrekking tot de vochtigheid of de verfbaarheid van karton, met betrekking tot het doorslaan van naar buiten komende chemische verbindin-gen of met betrekking tot de corosieve werking van de in de gipskem aan-30 wezige bevestigingsmiddelen, bijvoorbeeld een ijzeren spijker.Particularly in the use of gypsum for the manufacture of sheets of gypsum board, the opinion has developed that gypsum must be pure in order to obtain a good connection not only with cardboard, but also with regard to the secondary effects on the gypsum board plate such as with with regard to the moisture or paintability of cardboard, with regard to the penetration of outgoing chemical compounds or with regard to the corosive action of the fasteners present in the gypsum core, for instance an iron nail.
Bovendien is het in deze samenhang vermeldenswaard dat een zo zuiver mogelijke halfhydraatgips niet alleen slechts zeer arbeids-intensief te verkrijgen is, maar ook dat dit produkt zeer veel energie vereist, en bovendien niet onbeperkt voor de aannemer of een andere 35 gebruiker ter beschikking staat.In addition, it is worth noting in this context that the purest possible semi-hydrate gypsum is not only very labor-intensive to obtain, but also that this product requires a great deal of energy and is moreover not available indefinitely to the contractor or other user.
De doelstelling van de onderhavige uitvinding is daarom een plaatvormig bouwelement te verkrijgen, vooral een plaat uit gipskarton, dat met betrekking tot de kwaliteit hiervan en met betrekking tot de 8203164 -4- 22614/Vk/mb algemene kwaliteit en de stevigheid en verwerkbaarheid praktisch niet van normale, uit zuivere gips vervaardigdei platen uit gipskarton is te onderscheiden, maar dat op een aanzienlijker milieuvriendelijke en energiebesparende wijze is te vervaardigen.The object of the present invention is therefore to obtain a plate-shaped building element, in particular a plasterboard board, which with regard to its quality and with regard to the 8203164 -4-22614 / Vk / mb general quality and the firmness and workability practically do not plates made of plasterboard made from pure plaster can be distinguished, but can be produced in a more environmentally friendly and energy-saving manner.
5 Deze doelstelling wordt bereikt door het toepassen van een plaat van gipskarton volgens de uitvinding en deze wordt hierdoor gekenraerkt, dat de gipsen kern ook tot 50 gew,% berekend op gips, inerte vulstof bevat, waarbij de vulstof volgens een zeefcurve zodanig is samen-gesteld, dat deze een dichte kogelpakking heeft, vergelijkbaar met de 10 op zich bekende Fuller-curve.This object is achieved by using a plasterboard board according to the invention and it is characterized in that the gypsum core also contains up to 50% by weight, based on gypsum, inert filler, the filler being so arranged according to a sieve curve. provided that it has a dense ball packing, comparable to the 10 per se known Fuller curve.
Deze zeefcurve van de inerte vulstof ligt in het gebied van 0 tot 3 mm, bij voorkeur echter in het gebied van 0 tot 1,5 mm, en in het bijzonder in het gebied van 0 tot 0,5 mm. Het is een voordeel wanneer het gehalte aan grotere korrels niet te hoog is.This sieve curve of the inert filler is in the range from 0 to 3 mm, but preferably in the range from 0 to 1.5 mm, and in particular in the range from 0 to 0.5 mm. It is an advantage when the content of larger grains is not too high.
15 Als inerte vulstof wordt bij voorkeur kalksteen en dolomiet- gesteente toegepast, maar ook anhydriet en/of zand. Het mengsel volgens de uitvinding wordt volgens een op zich bekende wijze bereid en ook volgens een op zich bekende wijze met water tot een overeenkomstig, verwerkbaar gipsmengsel gemengd, welk mengsel de gebruikelijke en in 20 de Industrie voor het vervaardigen van platen uit gipskarton bekende en toegepaste toevoegstoffen bevat zoals vertragers, versnellers en dergelijke.Limestone and dolomite rock are preferably used as the inert filler, but also anhydrite and / or sand. The mixture according to the invention is prepared in a manner known per se and also in a manner known per se mixed with water to form a corresponding, processable gypsum mixture, which mixture is known and used in the industry for the production of plasterboard panels. contains additives such as retarders, accelerators and the like.
Het is ook mogelijk om aan het mengsel korte vezels in de vorm van glasvezels toe te voegen volgens een op zich bekende wijze.It is also possible to add short fibers in the form of glass fibers to the mixture in a manner known per se.
25 Als vertragende stoffen kan men bijvoorbeeld een verbinding toevoegen die als vertragende stof bekend is, doch bovendien aan gips nog een bepaalde hydrofobe eigenschap geeft, bijvoorbeeld een vetzuur, zoals palmitine-, stearine- of oliezuur in de vorm van een dispersie in water of in de vorm van een in water oplosbaar zout van een dergelijk zuur, 30 bijvoorbeeld magnesiumstearaat.As retarding substances, it is possible to add, for example, a compound which is known as retarding material, but also gives gypsum a certain hydrophobic property, for example a fatty acid, such as palmitic, stearic or oleic acid in the form of a dispersion in water or in the form of a water-soluble salt of such an acid, for example magnesium stearate.
Het is uit experimenten gebleken dat een op een dergelijke wijze vervaardigde plaat ten opzichte van de bekende platen van deze soort slechts onaanzienlijke lagere stevigheden heeft, waarbij hier tegenover staat dat een verlaagd gebruik van halfhydraatgips wordt 35 verkregen en bij de verwerking aanzienlijke voordelen worden verkregen, bijvoorbeeld het lagere verbruik aan energie voor het drogen per plaat-eenheid, terwijl bijvoorbeeld bij een gebruikelijke plaat per vierkante meter 3,5 kg water,dat hierbij is toegepast,moet worden verdampt, terwijl 8203164 > — -5- 22614/Vk/mb bij de platen volgens de uitvinding het te verdampen gedeelte van water, afhankelijk van de hoeveelheid van de toegevoerde inerte stof nog slechts 2,0 tot 2,8 kg bedraagt. Als toevoegstoffen kan men ook een combinatie van stoffen kiezen, bijvoorbeeld gemalen kalksteen, zand en 5 anhydriet, waarbij alle drie de stoffen met betrekking tot de zeefcurve zodanig moeten worden gekozen dat ze samen een zo dicht mogelijke pakking geven die in overeenstemming is met de Fuller-curve. Ook kan men vliegas toevoegen en gebruiken zoals bijvoorbeeld kan worden ver-kregen bij de elektrische filters van energiecentrales, welke vliegas 10 als toevoegstof in deze samenhang kan worden toegepast.Experiments have shown that a plate manufactured in such a manner has only considerably lower strengths compared to the known plates of this kind, whereas, on the other hand, a reduced use of semi-hydrate gypsum is obtained and considerable advantages are obtained during processing, for example, the lower energy consumption for drying per plate unit, while, for example, in a conventional plate, 3.5 kg of water used per square meter must be evaporated, while 8203164> - -5- 22614 / Vk / mb in the plates according to the invention, the portion of water to be evaporated, depending on the amount of inert material supplied, is still only 2.0 to 2.8 kg. As additives one can also choose a combination of substances, for example ground limestone, sand and anhydrite, all three substances with regard to the sieve curve must be chosen so that together they give the closest possible packing that is in accordance with the Fuller -curve. Fly ash can also be added and used, as can be obtained, for example, with the electric filters of power plants, which fly ash 10 can be used as an additive in this context.
Uit het bovenvermelde zal het duidelijk zijn dat de plaat volgens de uitvinding met betrekking tot de fysische eigenschappen overeenkomt met de tot nu toe bekende plaat, maar dat voor het vervaar-digen hiervan aanzienlijk minder energie moet worden verbruikt voor het 15 branden van gips en voor het vervaardigen van de platen uit gipskarton, in vergelijking met de werkwijze voor het vervaardigen van de tot nu toe bekende platen uit gipskarton. Zodoende kan een aanzienlijke technische vooruitgang worden verkregen, vooral met betrekking tot het verbruik aan primaire energie en het verbruik van gips, 8203164From the above it will be clear that the plate according to the invention corresponds in terms of physical properties to the plate known so far, but that for producing it considerably less energy has to be consumed for the burning of plaster and for the production of the plasterboard boards, in comparison with the method of manufacturing the hitherto known plasterboard boards. This will allow significant technical progress to be made, especially with regard to primary energy consumption and gypsum consumption, 8203164
Claims (10)